Search Documents

By T. A. Chepushtanova, B. Mishra, E. O. Kilibayev, V. A. Luganov

"The paper contains the results of studying about modification of pyrite and arsenopyrite specific surface and porosity at their thermal decomposition. The studying of specific surface was carry out by B.E.T. – adsorption of nitrogen at his boiling-point. In our work were using the electron-microscopical, X-ray structure analysis and chemical analysis. There was established that the decomposition of pyrite and arsenopyrite accompany by increasing of pores volume from 0.303 · 10-3 to 1.23 · 10-3 at increasing of pyrite degree of decomposition about 41 % and then decrease about 0.131 · 10-3 m3/g at degree of decomposition near 100 %. The surface area of pores increase from 0.31 to 1.085 m2/g with following lowering due to enlargement and confluence of minor, small pores. Increasing of porosity accompany with increasing of particles windage that appear the result of heightened dust-furnace partially decomposing pyrite and arsenopyrite particles by air flow from furnace reaction zone. This explains heightened contention of sulfide sulfur in roast dust of sulfide concentrate. 1. INTRODUCTION As a result of ore base exhaustion of ferrous and nonferrous metallurgy at metallurgical treatment are involving more complicated and less qualitative ores. Magnetiting ores content considerable quantity of pyrite complicative the technology of iron extraction. At the same time the pyrite concentrates wining at dressing content different nonferrous metals in industrial quantities. Extracting ores of nonferrous metals are contenting considerable quantity of arsenic at the present time. Extraction of base metals from complicated raw materials demands new technologies. Arsenic contenting in ores is necessary to utilize (waste burial) in more ecological compatible form. Arsenic on acting metallurgical and chemical enterprises from technological cycle is withdrawing in the form of arsenate – arsenite cakes, burial of their may lead to seriously ecological problems as times goes by. In Kazakh National Technical University is carry out the cycle of researching by pyrite, arsenopyrite and arsenate – arsenite cakes treatment with the object of arsenic withdrawal in sulfide form – in more ecological and safe form and with the object of preparation of initial ore raw materials to following pyro- and hydrometallurgical treatment. As a result of sulfidizing of arsenate – arsenite cakes by pyrite are forming the volatile arsenic forms and pyrrhotite of variable structure."

Jan 1, 2008

By O. Ryosuke Suzuki

A new metallurgical process via sulfide is proposed: a sulfide is produced at a high temperature from its metallic oxide using gaseous CS2, and this sulfide is electrochemically reduced to its metallic state using molten salt. This combined process via sulfide is effective to obtain high purity of metallic powder, even if the metal in its oxide is strongly combined with oxygen. For example, it is not easy to reduce stable oxide TiO2, and only Ca can remove oxygen to form α-Ti. However, a fairly large amount of oxygen remains as Ti–O solid solution. Because the solubility of S in Ti is very small, this proposal was examined experimentally both on the conversion of TiO2 to TiS2 and on the successive reduction of TiS2 to Ti. TiO2 powder was exposed to CS2 gas flow at 1073 K, and the conversion to TiS2 was confirmed. TiS2 could be reduced to Ti powder either by calciothermic reduction or electrolysis in a CaCl2 melt. By Ca reduction at 1133 K in CaCl2 melt, sulfur concentration decreased to 0.03 mass%S when the amount greater than twice the stoichiometric calcium amount is added. By electrochemical reduction at 1173 K in CaCl2–CaS melt, S concentration significantly decreased to 0.01 mass% S when four times larger amount of electric charge was supplied.

By Ju Shao-hua

Although nowadays gold extraction methods are very abundant, none of them is satisfying, especially, in the field of heap leaching of low grade gold ore. The traditional heap leaching method of cyanide method plays an inglorious role of badly environmental pollution. In this paper, a bran-new and innoxious method of gold extraction system, metal-ammonium-chloride-ammonia (MACA), was proposed, and also analyzed both thermodynamically and practically. Thermodynamically, according to the principles of simultaneous chemical equilibrium and electronic charge neutrality, the thermodynamics of Au-NH4Cl-NH3-H2O system was studied by using the exponential computation method and through MATLAB programming, and the solid figure of its potential - c(NH4Cl) - c(NH4OH) was drawn. The results showed when the concentrate of ammonia is higher than 0.6 mol?L-1, fAu+/Au is only about -0.2 v. Practically, the leaching results of a cuprous gold ore showed that the extraction of gold can reach to 80% in this system. The preliminary results of reduction of the rich solution with copper and zinc powders showed that with deoxygenizing, the reduction effects were relatively good. These new findings and results have established a theoretical and practical base for developing a new process for heap leaching of low grade gold ores in this system. And the new process owns a series of merits such as, non-cyanogens, nontoxic, broader applicability.

Jan 1, 2006

By V. Baltazar

The behaviour of arsenic and antimony during copper electrorefining was studied in order to identify the conditions under which good quality copper cathodes could be produced from anodes with high levels of these impurities. Examination of the effect of current density over the range 21 to 37 mA/cm2 indicated that the relative amounts of As and Sb entering the electrolyte affected the onset of passivation. When the ratio of As/Sb entering the electrolyte was greater than 2, the anodes showed no sign of passivation even at the highest current density; when the ratio was less than 2, the anodes passivated at 37 mA/cm2. Cathode analyses showed that anodes with an As/Sb dissolution ratio less than 2.0 tend to produce cathodes of inferior quality even at normal current densities (25.7 mA/cm2). The criterion of a minimum As/Sb dissolution ratio of 2.0, and mathematical correlations for the distribution of As and Sb between the electrolyte and slime developed in a previous study, allow the calculation of the maximum allowable Sb level in en anode for a given As concentration. Analyses of plant data at the CCR Division of Noranda Inc. for the last four years of operation have demonstrated that the use of this as a quality control tool has allowed the quality of copper cathodes to be maintained despite a significant increase in the average Sb levels in anode receipts.

Jan 1, 1987

By G. G. Krishna Murthy

Interactions of wustite and hematite pellets with Fe-C melts were investigated experimentally by examining the effect of pellet size and bath temperature on the reduction rates of the pellets. Experiments were carried out in the temperature range 1473-1923 K. A flash X-ray equipment was used to obtain images of the melt surface during its reaction with an oxide pellet. The reduction rates were calculated using experimentally estimated time for complete reaction of a pellet, tR. The value of tR was determined employing gas mass flow rate, or pressure rise in the sealed furnace, versus time traces. The value of tR was the same for both wustite and hematite pellets of equal weight at or above 1723 K and it decreased with increasing melt temperature. But the reduction rate was substantially lower at temperatures below 1651 K, the melting point of wustite. The rates were defined as the rate of moles of oxygen removed from the pellet per unit area of bath free surface and it was found that the bath surface area affects the reduction rates. It was established that the overall reaction followed nth-order rate kinetics with the values of n falling between 0.3 and 0.4 for temperatures above the melting point of wustite. The apparent activation energy determined using the apparent rate constants obtained from the experimental data was 76.2 + 27.7 kJ/mol-O.

Jan 1, 1992

By Cao rong-jiang, Tang Xin-he

"In ordinary manufacture process of tungsten powder, a preferable intermediate product used is ammonium paratungstate (APT). The particle size of tungten powder made from it through W2OO58 is larger than 1. 0 um. In order to obtain ultrafine tungsten powder with narrow size distribution, a new type of tungstate, hydraziniull tungstate, was studied. Its formula is 5(N2H5)2O·12 WO.s , with tetragonal crystal structure of a=5.821 , c=18. 468. Three methods for preparing hydrazinium tungstate (ART) were set up and ART can be produced by current industrial APT process with little modification of operation and without any change of equipment.Under certain PH and operation condition of the solution from which ART was produced, an autoreduction of tungsten occured, which produced a lower valency tungstate with blue color when ART was heated at different temperatures, in N atmosphere, tungsten bronze, tetragonal W0290 and W02.7E could be obtained respectively. They all have the superiorities, in the production of tungsten powder, of superfine size and narrow size distribution [average size of 0.5um or even smaller.The rate of autoreduction of ART is very fast at elevated temperature. The reduction reaction, which gaves tetragonal WO290, could be handled smoothly without explosion. To research their behaviors at autoreduction temperatures and the products of autoreduction will be new advances of tungsten chemistry and may also serve tungsten industry with new processes and materials."

Jan 1, 1988

By T. Iriyama, Y. Fujita, R. Omatsuzawa, T. Nishio, N. Okochi

Sm-Fe-N hard magnetic materials are good candidates for high performance bonded magnets. Rapid-quenching method should be highly favorable for the fabrication of isotropic magnet powder with high coercivity. We report here the magnetic properties of Sm-Fe-N powders produced by a few kinds of rapid-quenching processes. Sm2Fe17 powders were prepared by gas-atomization (GA), rotating-disk atomization (RDA), or melt-spinning (MS) method. The Sm2Fe17 GA powder had dendritic solidification structure, while the RDA powder had micro crystalline structure with size of 3-5 µm. Coercivities (HcI) of their nitrides were 56 (for GA) and 217 ka/m (for RDA). The H cI of nitrided Sm2Fe17 MS powder with wheel velocity (V5) of 5-20 m/s, which had also microcrystalline structure, was 53 to 509 Wm. These coercivity values are not sufficient for bonded magnet applications. From the study of additive effects, it was found that C, C-Si, C-Ga, or C-Al addition decreased the crystal size of quenched Sm2Fe17 powder. Consequently, high coercivity was obtained; the HcI of nitrided Sm2Fe1C1Si1 MS powder with V5 of 10 m/s was 898 kA/m, and 708 kA/m for the nitrided Sm2Fe15C1Si1 RDA powder. The compression-molded bonded magnet made from Sm2Fe18Si0.1Nx MS powder showed a high (BH)max of 82.7 kJ/m3.

Jan 1, 2000

By Y. Iguchi, T. Narushima, T. Shiozawa, M. Maruyama, R. Arashi

"In situ observation system for thermal oxidation using Raman spectroscopy' was constructed, and oxide films formed on liquid pure Al and Al-Mg alloys (Mg contents = 1 and 4 mass%) were analyzed at room temperature to 1273 K in dry oxygen. In situ Raman spectra of the surface of a liquid Al-:-4mass%Mg indicated the formation of MgO • AlP3 (spinel) as oxidation products, while a -AlP3 and MgO • Alz03 (spinel) were observed on a liquid Al-1mass%Mg alloy. It was suggested that the formation of MgO film affected oxidation behavior of these alloys.IntroductionLiquid aluminum alloys are cast to ingots mainly by the continuous casting process. It is well-.known that surface cracks could be caused by oxide films formed on the surface of melt during continuous casting and defects due to the film. With regard to oxidation behavior of liquid aluminum alloys, many investigations l -s have been carried out from the view point of formation of ceramic metal composites(CMC) which are expected as cutting tools and structural materials 1.2. It is very important for reasonable continuous casting and CMC formation processes to elucidate oxidation behavior of melts.Oxidation behavior of materials generally depends on compositions and properties of oxide films formed on the surface. If in situ observations of oxide films are available during oxidation, evaluation of oxide films and interpretation of oxidation mechanism could be expected. Laser Raman spectroscopy is one of the most appropriate techniques for in situ observation of oxide films under various atmosphere at high temperatures. The authors have discussed the effects of atmospheres and sample compositions on oxide film formation mechanism on Fe-Si alloy6 and SiC-B4C composite7 on basis of an in situ observation by Raman spectroscopy. In spite of many previous studies, systematic and clear explanations have never been gotten on oxidation behavior of liquid aluminum alloys. And no in situ observation has been made except for transmission electron microscopy(TEM) and X-ray diffraction(XRD)."

Jan 1, 1996

By Jose Antonio Silva Souza, Emanuel Negrao Macedo, Iara Ferreira Santos, Otacilio Dias, Luis C. A. Venancio

"The Bayer process alumina production generates 0.7 to 2.0 ton of bauxite residue (BR) and an average of 1.0 ton of C02 per ton of alumina produced. The direct reaction of exhaust gases to reduce the alkalinity of the BR may allow a triple gain: improve the storage conditions, open a range of new applications for BR and sequester from 16 to 102 kg of C02 per ton of alumina. This paper shows the measurement of C02 captured during a pilot scale reaction of a suspension of BR in water with flue gas, produced from direct oil burning. Three different types of reactors were used: one spray tower and two packed columns. The inlet and exhaust gases were analyzed using electrochemical and non dispersive infrared sensors. The pH of the suspension was monitored during and after the reaction to evaluate the buffer effect.IntroductionAlumina is mainly produced from refining bauxite using the Bayer process. This process consists of extracting the aluminum oxide through its dissolution in caustic soda and the separation of insoluble residues. The remaining bauxite residue (BR) although not particularly toxic, poses risks to the environment due to the large volume and its reactivity. According to the latest technology it is stacked on sealed deposits specially constructed. To date the vast majority of the bauxite residue that has been produced was stored and were not incorporated into any existing production processes to significant amount with exception to some extent of the sintering process residue at Russia and China [l]. On the other hand, a strategic goal was set in 2010 by the Bauxite and Alumina Committee of the International Aluminium Institute (formed by the majority of the industries) to reuse 20% of BR in 2025 [2]. China has established the same objective for 2015[1].This paper is a sequel of two others presented at TMS 2010/2012 [3-4] and describes:• A pilot plant assembled for testing the carbonation process of BR with gaseous effluents similar of the refining process.• The methodology used to measure the amount of C02 captured during the carbonation process.• The results of the carbonation process, the C02 capture and the buffering effect of the pH.This process is studied in order to consume minimal power and use the effluent as efficiently as possible in different reactors from low cost to ultra high performance. The process is designed for minimizing the power consumption and equipment investment."

Jan 1, 2013

By B. Yawney

A copper-nickel sulfide concentrate was leached in water at about 2000C under oxygen pressures of about 0.35 MPa. Oxidation of sulfide to sulfate was virtually complete in about 30 minutes, resulting in greater than 95% copper and 98% nickel extractions. Leaching temperature was shown to be the most important factor affecting metal extractions. Measured rates of oxygen consumption were used to develop batch kinetic data. Mini-plant continuous pressure leaching tests agreed with batch leach results. A proposed overall flowsheet is briefly examined.

Jan 1, 1976

By Jianxun Song, Hongmin Zhu, Qiuyu Wang, Jungang Hou, Shuqiang Jiao, Xiaobo Zhu

This work presents the results of a study on the Ti3+/Ti2+ couple redox potentials vs. Cl–/Cl2 at the temperature range (673 to 1073 K) in fused LiCl-KCl eutectic by direct potentiometric method. Initial concentrations of TiClx in solvents did not exceed 5.0 mol%. Basic thermodynamic properties of the reactions TiCl2+1/2Cl2(g)=TiCl3 were calculated using the temperature dependencies of apparent standard potentials of the couples E* Ti3+ /Ti2+.

Jan 1, 2014

By R. G. Reddy

The oxidation kinetics of A13Ti intermetallics have been studied at the temperature range of 850°C to 100O0C in pure dry oxygen. The oxygen diffusion rates were investigated using TGA method. Parabolic rate constants were calculated. The oxidation scales were analyzed using SEM, EDS and X-ray diffraction. A continuous A120, scales with a little TiO2(rutile) were formed on the intermetallic surface. The A13Ti intermetallic exhibited excellent oxidation resistance among the Ti-Al base intermetallics.

Jan 1, 1997

By G. S. Rao

Levitated drops of Fe-18%Cr-2%C were reacted with oxygen-argon mixtures to study the reactions that occur in the AOD process, where the gases are injected into the melt and form bubbles. In the laboratory an argon-oxygen pulse, followed by pure argon, was flowed past the levitated drop to simulate the transient conditions in the gas phase as the bubbles rise in the melt. Oxide layers formed on the drops immediately when they came into contact with gas pulses containing 75% or more oxygen. Once the oxygen flow had ceased, the oxides reacted with the carbon in the drops to form CO gas and eventually disappeared. The de-carburization reaction occurred without oxide formation when the gas contained 50% oxygen or less. Melts that were sampled after EAF tapping, ready to be charged into the AOD, showed a higher tendency to oxide formation and consequent carbon boil than pure ternary Fe-18%Cr-2%C alloys made in the laboratory. The actual steel samples contained significant impurities, such as 0.25% Si and 0.56% Mn. A similar effect of oxide-forming impurities had been observed previously with binary Fe-C alloys. Movies were taken of the oxide formation and decomposition, and the results will be presented, along with data on the experimental conditions, including temperature and oxide compositions. The results are important because they give an insight into the reaction mechanisms in the AOD, which must be understood in order to improve and model the process.

Jan 1, 2006

By Lztok Peruš, Goran Kugler, Matevz Fazarinc, Milan Tercel

"Hot deformability of M42 tool steel additionally alloyed with cobalt and molybdenum was investigated. Hot-compression tests were carried out in the temperature range 850 °C -1200 °C, at strain rates range 0.001--6s-l up to strain of0.9. Field-emission scanning electron microscope and optical microscopy were used for characterization of microstructure of deformed samples, which revealed a very complex precipitation of carbides that strongly depends on the soaking temperature, the soaking time, the stress state, the deformation temperature as well as on the strain rate. Gathered data was used to calculate the processing parameters such as process maps, apparent activation energies and strain hardening exponents. For better understanding of thermodynamical properties of the studied steel a simultaneous thermal analysis was conducted. Furthermore the analysis of phase equilibrium was calculated using Thermo-Cale software. On the basis of these studies the optimal soaking temperature and process windows were determined.IntroductionHot workability ofledeburitic tool steels is important economic factor. This means that for each tool steel individuallysafe range of hot working parameters should be revealed. Publications in the literature with regard to the hot workability of tool steels are rare and therefore more information from this research area is desired.The relatively low hot workability of ledeburitic tool steels, i.e. steels in which the solidification is completed by a eutectic transformation of the residual interdendritic liquid to austenite and various alloy carbides (ledeburitic carbides), is usually characterized by the production of surface and internal cracks during the hot deformation."

Jan 1, 2013

By Brad Wahlquist

An ex-situ biological treatment system was implemented at a gold mine site in South Dakota. The system removes selenium and nitrate from a mixture of groundwater and surface water runoff at ambient water temperatures. The Applied Biosciences? system replaced a denitrification system that did not perform consistently, did not treat for selenium and required heating of the influent water. Installation was completed in phases starting with the selenium circuit being brought into operation in February, 2002 and the nitrate circuit in March, 2002. System design can accommodate average flows of 380 L/min (100 gallons/minute) and a maximum flow of 1,136 L/min (300 gallons/min). Four cells were designed to remove nitrate from approximately 30 mg/L to below 10 mg/L and two cells were designed to remove selenium from 0.01 mg/L and higher, to below 0.005 mg/L. No pretreatment is required to operate the system at ambient temperatures, which can fall as low as -12C in the winter, and treat water at temperatures ranging between 8C to 16C. Nutrient requirements are met using a sugar based nutrient mixture that includes a balanced C:N:P:S ratio, trace elements and vitamins. Since start up, the system has consistently been in compliance for nitrate and selenium, treating water to below detection limits for both contaminants. This paper discusses laboratory biotreatability testing of a system designed to remove selenium, arsenic, and nitrate and full-scale implementation and optimization of a system to remove nitrate and selenium.

Jan 1, 2003

By Zhiqian Zhang, Chao Wu, Chao Li, Hongxu Li, Chuanqi Jiao

"Many used electronic and optical products contain cerium of rare earth oxides, but it is difficult to recover such rare earth compounds by traditional metallurgy methods. The proposed supercritical water metallurgy is a novel way, perhaps it will be very helpful for rare element recycling, but the thermodynamic properties at such special systems is not clear. In the paper the H20-CeO-CeO2 and H2O-CeO2-Ce2O3 ternary system phase diagram were produced under the pressure of30MPa with different temperature of350°C, 375°C and 400°C. The stability existing area of possible cerium compounds and different ions like Ce2+,Ce3+,Ce4+,W,HO2-,0ff ,CeOH2+,CeO+ and CeO2· were determined.IntroductionCerium is an extensively used metal element playing an important role in the rare earth elements. CeO2 is an apparently simple binary oxide with cubic fluorite structure [l]. Ce0O gives rise to a range of important technological applications because of its oxygen storage capacity at moderate temperatures as below: CeO2=CeO2.x+ X/2O2 [2]. The oxygen storage phenomenon gives ceria important technological uses in different fields as automobile exhaust purification catalyst [3-4], fluorescent powder, ultraviolet absorption material [5], polishing powder, fuel cell materials [ 6], and gas sensors, etc. The excellent properties of CeO2 nano powder make its synthesis and preparation become one of the hot spots of world scientists study."

Jan 1, 2013

By Jeffrey Shepherd, Scott R. Smith, Eduard Guerra

"Electrochemical and spectroscopic evidence for the dissolution of a Au electrode by meso-2,3- dimercaptosuccinic acid (DMSA) from an acidic LiCl04 electrolyte is presented. Near the potential of zero charge, DMSA was determined to form a stable layer on the metal surface but at more anodic polarizations, DMSA was displaced from the metal through an oxidative process. The anodic displacement of the layer from the electrode resulted in a small amount of Au that was detected in the electrolyte using atomic absorption analysis. The extent of Au dissolution, was monitored while holding the potential of the electrode for 24 hours at the thermodynamic Eo/H,O in LiCl04 electrolytes containing 10 mM DMSA. This routine resulted in detectable quantities of a soluble Au-DMSA complex in the electrolyte and the greatest leaching was observed at a pH = 2.0. At room temperature, the leaching rate was stable at 10.9 µg cm·2 hr·' however, upon increasing the temperature to 50.0°C, the rate of Au dissolution increased yielding an average rate of extraction of 40.1 µg cm·2 hr- 1. Interestingly, after the first 12 hours of leaching at 50.0°C, the leaching current decreased dramatically suggesting surface passivation which prevented further Au extraction. The implications of this process in the industrial leaching of Au will be discussed.IntroductionThe use of cyanide in the industrial process of leaching Au from ores has raised concerns regarding both operational safety and environmental issues surrounding the disposal of spent leaching eftluents in tailings ponds. Depending on the chemical nature of the processed ore, the spent solutions that are released into the tailings ponds can contain toxic cyanide, either dissolved or complexed with different metals and may pose serious risk to wildlife as well as freshwater contamination to nearby water systems. Because of these issues, some recent studies have focused on the exploration of more environmentally-friendly molecules to selectively leach Au with appropriate kinetics. However, to effectively leach Au into an aqueous solution, a suitable ligand that reacts to form a stable chemical bond with Au is needed to form soluble Au complexes that can be later recovered [I]. Recently several sulfur bearing alternatives have been shown to leach significant quantities of Au in aqueous solutions. These include thiourea [2], thiocyanate [3], and thiosulphate [4]. However, alkylthiols are also known to quickly form a stable covalent Au-S bond [5], but have been relatively understudied in term of their ability to leach Au in solution, even though some short chain thiols are water soluble and relatively nontoxic."

Jan 1, 2012

By M. A. Aziz

The electrochemical performance of a series of carbon materials produced from coconut shells, which are very cheap and readily available in Bangladesh was investigated for their viability as anode materials in rechargeable lithium-ion batteries. X-ray diffraction technique was used to measure the interlayer spacing (d002) of the produced carbon materials. A number of half-cells were prepared with the produced carbon materials from coconut shell as working electrode and metallic lithium as counter electrode with 1MLiPF6 electrolyte in a mixture of ethylene carbonate and dimethyl carbonate. The discharge-charge profiles were measured for the different half-cells by using Arbin 24-channel Cyler. The value of interlayer spacing of the coconut-based carbon material was found to be 0.397 nm at 900°C, which is most suitable for lithium-ion insertion into the carbon structure without any expansion. The specific discharge capacity of carbon material from coconut shell heat treated to 900°C was found to be 1015.65 mAh/g. The coconut carbon material heat treated to 900°C delivered 335.22 mAh/g reversible capacity, which is comparable to the commercial carbon/graphite presently used in lithium-ion battery systems. The irreversible capacity loss and coulombic efficiency in 25th cycle of half-cell made with coconut carbon material were found to be 0.16% and 99.83% respectively. The carbon material produced from coconut shell can, therefore, be used as a potential anode for rechargeable lithium-ion batteries.

Jan 1, 2006

By K. Twite, K. Mujinga, J-M. Dereydt, P. Louis

"GECAMINES is a large mining concern and the world's leading cobalt producer having some of the richest cobalt deposits in the world. Cobalt is associated in the ore with copper as sulphides and oxides and in some locations with nickel too. Specific hydrometallurgical processes have been developed by GECAMINES which had done an important contribution to the development of the cobalt hydrometallurgy.In the Shituru plant, cobalt is obtained from an unique in-pulp electrolysis process, while in Lullu, cobalt is electrolyzed in a clear acidic solution giving a purer deposit. In the beginning of 1996 Shituru started the treatment of mixed Cu-Co-Ni Shinkolobwe hydrates obtained as by-product of an uranium solvent extraction plant. A typical analysis of this feedstock is: 2% Cu, 8% Co and 4% Ni.The nickel sulfide depolarized cementation process developed previously by GECAMINES was inefficient to treat such a high level of nickel contamination and it was decided to produce alloyed Cobalt-Nickel cathodes in the Shituru tankhouse.As anticipated from laboratory tests as previous studies and publications, a lower Ni/Co in the deposit was obtained compared to the Ni/Co ratio solution, despite the nickel reversible electrochemical potential is somewhat higher than the one of cobalt (-0.25 V vs -0.28 V).In this paper, the process flow-sheet and production data are given. Cobalt alloy with 5 - 20 % Ni was obtained at a production level of 300 t per month. The process developed is a new contribution to cobalt hydrometallurgy."

Jan 1, 1997

By H. Ipek

In this study the effects of interstitial ratios on k-feldspar samples were investigated. The k-feldspar samples were taken from Egypt using dry batch grinding conditions and a kinetic model. Three different mono size fractions (-3350+2360, -850+600 and -300+212 µm) were ground separately for 0.5, 1, 4, and 8 minutes and at four different interstitial ratios (125%, 100%, 75% and 50%) using a Bond mill with a mixture of five ball sizes. The mill used was at a size of 30.5 cm diameters, with 30.5 cm length, providing a total mill volume of 22272 cm3. The mill has a total mass consisting of 22648 g. steel ball mixtures of 38.10, 31.75, 25.40, 19.05 and 12.70mm diameters, occupying 22% of mill volume. The mill rotates at a speed of 70 rpm. The weights of the feed charges were 3000, 2000, 1000, and 500 g for 125%, 100%, 75% and 50% filling of the interstices of the balls respectively. The specific rate of breakage (Si) was determined from the top size fractions at different grinding times that were mentioned above and the model parameters were compared for the four different powder filling ratios (U). In many investigations, it has been found that an interstitial filling ratio of U = 0.6-1.1 is a good powder ball loading ratio to give an efficient breakage in a ball mill. In this study, it was found that U=1.25 is a good ratio for K-Feldspar.

Jan 1, 2006