By W. Dresler

Design details of a 100 kVA DC electric-arc reduction furnace are described. The furnace is equipped with a 610 mm (24 inch) diameter graphite crucible hearth. A 76 mm (3 inch) diameter top graphite electrode is used as a cathode. The current passes through the bottom of the crucible and is carried to a bottom plate (the anode) by conductive magnesia carbon bricks. The furnace can be operated up to a maximum of 120 V, 1800 A, and presently 100 kW. The start-up operating experiences and metallurgical results of one reduction test with a Montana chromite containing 38% Cr2O3 are discussed.

Jan 1, 1994

By Xiang-ning Meng, Miao-yong Zhu

"A three-dimensional finite-element heat-transfer model is conducted to predict temperature of hot copper plate in a slab continuous casting mold and the effect of casting speed on temperature difference between copper plate and solidifying shell is simulated in combination with process data. The results show that centre temperature of hot copper surface at casting speed 1.8 m·min-1 and 2.0 m·min-1 are higher than that of 1.6 m·min-1 casting speed 4.7-5.2 °C and 11.2-12.2 °C respectively and temperature is not increased linearly with casting speed. Temperature difference in meniscus between mold and shell is influenced obviously by casting speed and increased 4.0- 6.0 °C with increment of casting speed 0.2 m·min-1• Fluctuation of temperature difference in meniscus is a main reason to deteriorate casting quality as increasing casting speed.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipates in primary cooling zone and mold becomes a critical component of caster to govern steel quality, meanwhile, thermal load on mold is increased constantly and environment is also more abominable since high productivity and quality are required and high-effective technologies are applied. So, an in-depth understanding of thermal behavior of mold at high casting speed is essential to design cooling structure and maintain casting stability. Many studies have been carried out to shed light on thermal behavior in mold. Chow et al. [l] applied a mathematical model to heat transfer in billet mold at a high casting speed to give a new taper in order to minimize mold-strand interaction. Thomas et al. [2] researched relation between mold geometry and temperature distribution based on a finite-element heat-transfer model. Lu et al. [3] indicated that slab mold temperature are mainly affected by thickness of copper plate and nickel layer by a heat transfer model. Samarasekera et al. [4, 5] researched temperature of copper plates for both billet and slab molds and effect of a large number of factors ranging from water quality to casting speed. Park and Thomas et al. [6, 7] developed a finite-element thermal-stress model to determine temperature and thermal distortion and stress in both thin and slab molds and O'Connor et al. [8] applied an elastic-plastic-creep finite-element model in a funnel shaped mold to achieve same goals. Cicutti et al. [9] evaluated heat transfer and temperature fluctuation in a slab mold and proposed an expression to predict global heat flux as a function of process parameters and an index to quantify thermal instability. All mentioned above shown that thermal behavior is not only important to casting stability, it is also premise to further understand mechanical behavior in mold."

Jan 1, 2011

By Nils Eivind Kamfjord, Roar Jensen, Ingeborg Solheim

"SINTEF has carried out several pilot scale silicon process experiments in the past, but always with an open off gas system. In order to test the possibilities in running a semi closed furnace operation, a new off gas hood has been designed and tested. The off gas hood is designed to collect all off gases to gain insight into the phase compositions in the off gas and at the same time have the opportunity to monitor and maintain the charging/stoking of the furnace. The furnace hood has regulation and control of the air inlet into the combustion zone in two different heights. The off gas temperature and composition was continuously monitored and analyzed during the experiment. In order to expand the knowledge on NOx- formation in silicon metal production, such information is vital.IntroductionBecause of the negative environmental impact, the attention towards all kinds of NOX emissions increases in Norway. The authorities’ demand towards better surveillance and control of emissions increases as well.Earlier and new industrial measurements in FeSi- and Si-metal furnaces reveal quite high NOX-emission. The measurements also show that the NOX formation (mainly as thermal NOX) is distinct connected to the formation of dust (SiO?SiO2) in the combustion chamber above the furnace surface, when the temperature is high and the access to N2/O2 is good. This means that stoking, charging and temperature straight above the furnace surface is important factors for the NOX formation."

Jan 1, 2012

By K. Sarveswara Rao

"Any innovative approach made in non-ferrous metallurgical industry centers upon developing new processes, saving materials, improving production quality, and bornagain materials. Aqueous processing is commonly used to treat lean grade or more complex ore bodies. Its sustenance largely depends on energy and environmental compliance including water and wastewater management. The present paper focuses the importance of using particle size distribution and surface area measurements during ammoniacal dissolution of a Cu-Pb-Zn sulphide bulk concentrate and with an overview of the effect of water salinity on the process chemistry and residue mineralogy. Accordingly, an effort is made here to discuss the emerging perspective and highlight the recent successes and trends in terms of energy savings in non-ferrous hydrometallurgy.IntroductionThe nature and structure of the global energy industry is likely to change significantly in the 21st Century. Rabago et al [1] have comprehensively discussed how the mining and minerals industries can adapt to the challenges and opportunities posed by trends and drivers in global energy use. According to the authors, the drivers of sustainability include water, efficient energy use, climate modification, transportation technologies and energy security. Sustainability and competitiveness for the minerals industry will depend on natural capitalism, resource efficiency, new processes, saving materials, improving production quality, born-again materials and the solutions economy. Based on this motivation, the theme of the present paper is centered upon applications as relevant to energy and sustainable development in non-ferrous hydrometallurgy."

Jan 1, 2009

By Denise C. R. Espinosa

Rechargeable lithium batteries are one of the most promISIng technology in battery development. Although Li ion batteries have been used as an alternative to the more polluting and less performing Ni-Cd batteries, Li ion batteries have limited life and their disposal is uncertain. It is imperative that valuables from wastes, such as lithium, should be recovered. The main objective of the present work was to characterize secondary lithium batteries for cellular phones. This was done using unit operations of mining processing, x-ray diffraction (XRD), chemical analyses and the rmogravimetric analysis (TG). The unit operations were hammer mill grinding, knife mill grinding, size separation and magnetic separation. After the hammer grinding process, the plastic cases were almost intact, however, they have released the cylindrical lithium batteries themselves and these parts correspond to 70% of the total battery weight.

Jan 1, 2001

By C. Hakan Gür

Optimization and control of the microstructure is important for improving the properties of steel components. Development of non-destructive techniques for microstructure characterization is a critical task. Magnetic Barkhausen Noise (MBN) technique is a promising and challenging non-destructive technique fo automated evaluation of microstructures in steel components in a fast and reliable manner. This paper presents the results of MBN measurements for microstructure characterization of the quenched and tempered steels.

Mar 1, 2017

By Katsuyoshi Kondoh

The synthesis processing of Mg2Si or Mg2Si/MgO at lower temperature from the elemental magnesium alloy powder/chips and Si or SiO2 powder mixture was established via the repeated plastic working (RPW) based on Powder Metallurgy (P/M) process. RPW is much effective on the mechanical breakage of MgO surface films, which prevent from the solid-state reaction between Mg and Si powder. The solid-state synthesized Mg2Si particle of 200nm-2JIm is extremely fine, compared to that via the conventional casting process, causing the coarse one of 50-100um. This is because of not coarsening during the solid-state synthesis of Mg2Si. By using in-situ forming process of Mg2Si via RPW and pre-heating before hot working such as extrusion and forging, the magnesium composite material with Mg2Si or Mg2Si/MgO dispersions was developed in employing Si or SiO2 particles, respectively. For example, when employing AZ31 chips as raw materials of the matrix, it has low density of 1.85g/cm) and extremely superior mechanical properties, such as tensile strength over 350MPa with 5-10% elongation and Young's modulus of 47-50GPa, to the conventional Mg-Al-Zn alloys. The Mg composite alloy wires and pipes were produced via the hot extrusion process in the manufacturing plant, and also showed excellent mechanical properties.

Jan 1, 2003

By S. G. Kumar

Experimental studies on high carbon steelmaking through LD Converter - Vacuum Arc Degassing - Bottom Pouring route to produce low oxygen steels were carried out. The results indicated that it is possible to produce steel with a total oxygen content of less than 15 ppm. Thermodynamic and mass balance calculations are made on low-carbon steels that are treated by a complex deoxidation practice based on primary deoxidation of aluminum, manganese and silicon additions; followed by secondary deoxidation of vacuum degassing with simultaneous additions of aluminum. The results showed that primary deoxidation is mainly due to aluminum and the effect of carbon under reduced pressures on deoxidation of molten steel that is already killed by aluminum is negligible. The effect of process parameters on total oxygen content of steel, like carbon content, slag composition and inert gas purging, are discussed.

Jan 1, 1994

By Emilia Visileanu, Eftalea Carpus

"Ecological economic policy shall be understood as the sum of political, economical and environmental measurements aimed at the entire economy dematerialization and the dematerialization shall be ""imposed"" since the designing stage of goods and services"". European textile and clothing industry with a long leading tradition in terms of innovation, fashion and creativity, continues to be one of Europe's major industrial sectors. Textile industry affects the environment by high consumption of water, energy and chemicals, as well as by the large amount of waste it generates as a result of using a large number of chemicals and technological processes.Textile waste prevention, reduction and ecological exploitation require the implementation of new management and education tools.Introduction“Europe must learn from the experience of global economic and financial crisis ""- this was the conclusion of the European Commission that has elaborated a ten-year strategy designed to reinvigorate the economy and make possible a growth which is ""intelligent, sustainable and favorable to inclusion"", by a better coordination of national and European policies.Adapting infrastructure and logistics that encourage the marketing of ""sustainable"", ""fair traded"" and ""green"" products as well as other special „green” products will facilitate the movement towards dematerialization and eco-efficiency among producers."

Jan 1, 2012

By D. I. Davidov, D. A. Shishkin, M. B. Rigmant, E. P. Romanov, N. N. Stepanova, N. V. Kazantseva

The Co-19 at.%Al-6 at.%W alloy was prepared by two methods of casting. We used arc melting under an argon atmosphere with casting into a copper water-cooled casting mold and induction melting furnace with casting into a ceramic Al2O3 mold. According to the X-ray and SEM analyses, phase compositions depend on the cooling rate of the ingot after melting. After arc melting, the cast alloy has a three-phase structure, consisting of  cobalt (FCC), intermetallic phases CoAl (B2) type, and Co3W (DO19) type. After the induction melting, the alloy has a three-phase structure, consisting of  cobalt (FCC), intermetallic phases CoAl (B2) type, and Co7W6 () type. All phases in the investigated ternary alloy at the room temperature are ferromagnetic. Curie temperatures of all obtained phases were defined. It is shown that the magnetic properties of the studied alloy are typical for soft magnetic materials.

Jan 1, 2015

By Yuanbo Zhang, FENG ZHOU, Guanghui Li, Zhengwei Yu, RuijunWang, Tao Jiang

Composite agglomeration process (CAP) of iron ore fines has been proved an effective route for ironmaking burden production, and is characterized by low the fuel consumption and high the productivity compared with the traditional sintering process. Sintering behavior of pelletizing feed in CAP has not been studied fully yet. In this study, individual pellet and simulated CAP cells were roasted under the simulated sintering conditions. The compressive strength, FeO content and microstructures of roasted samples were investigated. The results show that pelletizing feed either from magnetite ore hematite concentrate can be indurated under the conditions of conventional iron ore sintering. Hematite pelletizing feed has better sintering property than magnetite pelletizing feed. Pelletizing feed consolidation in CAP cells is identical to the individual pelletizing feed, but the strength of CAP cells is much higher than the individual pelletizing feed. Higher basicity in both pelletizing feed and matrix feed is beneficial to the strength of CAP cells. Individual strength of pelletizing feed is not the decisive factor in CAP as the pelletizing feed has been embedded into the matrix with high basicity and formed an organic whole. The main chemical compositions and basicity of pelletizing feed and basicity matching with matrix feed is important.

Jan 1, 2015

By Adrien Antenen, Didier Villette

CITRON has developed a new process for the recycling of hydroxide sludge, household batteries, catalysts, automobile shredding residues, grinding sludge and other metal containing organic and inorganic waste. A pilot plant with a capacity of 1,000 tons per year has started operations in April 1998. In August 1999, an industrial plant became operational with an initial treatment capacity of 23,000 tons.

Jan 1, 2000

By K. Noda

Tamano Smelter of Hibi Kyodo Smelting Co., Ltd. started its operation adopting the Flash Smelting Furnace with Furnace Electrodes (FSFE). Thereafter, it developed a coke combustion technology based on C() concentration control, which made possible a low cost and high productivity operation without using electrodes. However, increase of treated concentrates and upgrading of matte grade for production expansion started to cause difficulties in operation control with then existing operation control system. This paper outlines recent improvements for stable operation of the Tamano Type Flash Smelting Furnace (T-FSF), such as computer aided operation guide system.

Jan 1, 2001

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In order to produce good quality ammonium paratungstate, Sn needs be removed efficiently from the tungstate processing solution. The nascent hydrous ferric oxide has excellent adsorption ability and is often used as an adsorbent to remove metal ions from aqueous solution. In this paper, nascent hydrous ferric oxide is used to remove Sn from tungstate solution. Through experimental, the effects of pH value, reagent amount of adsorbent, reaction temperature and reaction time on the Sn removal are investigated. The study shows that 98% of Sn can be removed effectively from sodium tungstate solution and only 2% of W is lost during process under the conditions of pH 9~12, reagent amount of Fe addition 40 times Sn amount, reaction time 30min and room temperature. As the Fe addition reaches 90 times of Sn concentration in the ammonium tungstate solution, 99% of Sn is removed and APT with zero level purity national standard is obtained.

Jan 1, 2014

By P. T. Velu, R. G. Reddy

"The use of emf measurements to derive classical thermochemical data has been in use for many years. The reaction associated with electrochemical process is harnessed in a galvanic cell and energy involved measured in terms of electromotive force. The property requirements of sensor electrodes used differ for various aqueous, molten salt and solid electrolyte systems. The electrodes for molten salt electrolytes need special care for construction. This paper describes the studies carried out using an Ag/ AgCI reference electrode. This electrode was used to measure the solubility of compounds in molten salt electrolytes. The results obtained using this electrode are in excellent agreement with the values from chemical analysis method.I. IntroductionThe technique of obtaining a metal from its oxides by electrolysis is more than a century old process now. In these processes, it has been well established that for halide electrolytes, only the dissolved oxides are available for the dissociation at the electrode to release the metal during electrolysis. Therefore, the solubility of metallic oxides in the molten salt electrolytes is an important parameter which determines the economical and technical viability of these processes. The widely used molten salts systems in halides are fluorides and chlorides. The fluoride electrolyte system is used in our present study.The viability of obtaining aluminum alloys by in-situ electrochemical processing has been outlined in our earlier publications[1-8]. Studies on the solubility of various alloying element compounds is a part of our ongoing research efforts for the direct production of Al-Li alloys. As mentioned above, the solubility of lithium oxide and lithium carbonate compounds in molten fluoride electrolyte system have studied using EMF technique. The change in potential of the molten electrolyte was measured by a working electrode against the reference electrode with the addition of lithium compound."

Jan 1, 1997

By John A. Thorpe, Gary R. Maxwell, Kirk M. Schall, Kenneth A. Brunk

"Gold ores containing oxide and some sulfide copper minerals incur significant cost penalties when leached with cyanide, because 4-5 moles of cyanide are consumed for each mole of leached copper. This equates to ~4 kg of NaCN per kg of leached copper. Total cost of excess NaCN consumption plus CN destruction can exceed $4.00 per tonne of ore. AuGMENT Technologies has patents pending on a process that can 1) economically recover 70-80% of the cyanide that is fed to a mill, 2) produce salable copper cathodes, and 3) reduce the need for a cyanide destruction facility. Standard equipment for resin processing and electrowinning are used to recover the cyanide and produce the copper cathodes. Steps have been taken to determine: 1) how to develop the resin kinetics, 2) how much savings are incurred at a mill site, 3) how the novel 'electro-elution' circuit achieves efficient operation.IntroductionWhen gold ores containing nuisance copper are leached with cyanide, a significant cost penalty is incurred because 4-5 moles of cyanide are consumed for each mole of copper that leaches. This is equivalent to the use of -4 kg of NaCN per kg of copper that leaches. The total cost of excess NaCN consumption plus cyanide destruction can exceed $4.00 per tonne of ore.AuGMENT Technologies has a patent pending on a process that can 1) economically recover 70-80% of the cyanide that is fed to a mill, 2) produce salable copper cathodes, and 3) reduce the need for a cyanide destruction facility. This ACCS (Au-.C.u-.C.N Solution) Process Technology involves the novel application of copper cyanide chemistry. Standard resin processing and electrowinning equipment are used to recover the cyanide and produce the copper cathodes."

Jan 1, 1997

By S. Jolivet, A. Klöfverskjöld, P. Latostenmaa, B. P. Wilson, M. Lundström, P. Halli

Doré slag is secondary product of copper electrore fining anode slime treatment. The slag consists mainly of different slag formers, such as borax and silica based minerals together with soda and traces of sealing materials. However, Doré slag also contains metals present in the anode slime, such as Ag, Cu, Bi, Sb and Te. At some plants, slag cleaning has been conducted utilizing conventional grinding and flotation circuits in order to enrich the content of precious metals in the slag [1]. Nevertheless, the routine consideration of the slag as a secondary raw material has so far not been adopted on an industrial scale. The current study presents the preliminary results of the nitric acid and chloride leaching of antimony from Doré slag. Chemical and mineralogical analyses (SEM-EDS, AAS, XRD) were performed for the raw material, leaching residue, and leaching solution in order to ascertain the metal recovery and kinetics during leaching.

Mar 1, 2017

By O. A. Ogunseitan

The contamination of aquatic ecosystems by mercury wastes is one of the most serious forms of environmental pollution associated with the metal mining and electrochemical industries. The transformation of inorganic mercury to alkylated species is a reversible bacterially-mediated process. The production of methylated mercury is of ?major public health and eco-toxicological concern because these forms of mercury are highly toxic ?and they bioaccumulate in aquatic organisms. We determined the response of the genetic determinants of mei:cury transrormation by Pseudomonas species (that predominate in contaminated soils and sediments), to the concentration and species? or available mercurfiations. By combining selective isolation and gene. ?probe techniques, the intrinsic genetic potential for mercury detoxification in a contaminated environment ?can be estimated. We determined that genetic units required for mericury volatilization (merA ?for mercuric reductase) are naturally amplified in response to mercury. Mercury-resistant bacteria that tolerate up to 100 ug Hg(Il)/ml of medium contain about 10 times more DNA fragments encoding merA than in unadapted bacteria. The exposure of bacteria to methylated.Hg (10 ug/ml lake water) produced increases (up to 10 times) in .genetic units, and higher levels of genetic expression (up to 50 times) per ml of lake water for the mercury reductase system, than on-induced lake water. The findings suggest that in environments where methylated Hg may accumulate as a result of bacterial activity, the reverse reaction which leads to the removal of mercury through volatilization from the system, may be achieved by inducing genetic ?amplification and expression of the mercuric reductase gene system.

Jan 1, 1991

By Alireza Zakeri

To evaluate the behavior of minor elements in the copper smelting process, activities of silver, selenium and tellurium at minor concentration were determined at 1473 K within the miscibility gap of the Cu-S-Me (Me = Ag, Se, Te) and Cu-Fe-S-Me systems varied in Fe/Cu ratio. Phase relations between the immiscible metal and matte phases in the foregoing systems were first established by a quenching technique at 1473 K to supplement the activity measurement data. A Knudsen-effusion mass spectrometer, capable of handling complex gaseous systems and relatively small vapor pressures, was adopted for activity determination. Using a multiple Knudsen-cell, the ion intensity of minor element in the sample under study was measured simultaneously with that in a reference sample. Activity was obtained from the ratio between the measured ion intensities as well as the known activity value of the minor element in the reference sample. Limiting activity coefficients of the minor elements were correlated with composition of the matte. Based on the experimental results, the vaporization behavior of the minor elements has been discussed.

Jan 1, 1999

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999