Search Documents

By C. A. Heberlein

C. A. HEBERLEIN,* New York, N. Y.-The results stated by Rey and Brevers are so startling that they are of great interest, as the concentration of a low percentage of cinnabar by differential flotation yields a high-grade concentrate in the presence of either arsenical or iron pyrite. The authors say: "Cyanide can thus be used to depress arsenopyrite and make a good cinnabar-arsenopyrite separation. A cinnabarpyrite separation could probably be effected in the same way." Corrosive sublimate at the present price of mercury would be a very expensive reagent but the expense would be justifiable if a high rate of concentration could be obtained with a high extraction. On my request, special tests were made in the Punitaqui mill in Chile along the line suggested by the authors, without any improvement of either grade or extraction. As the recovery of the cinnabar in a complex sulphide of chalcopyrite and pyrite gave unsatisfactory results, I had tests made at the testing laboratory of the American Cyanamid Co. at Stamford, Conn. As these tests turned out to be highly satisfactory, not only at Stamford but later at the mine, they are presented here. [AMERICAN CYANAMID TEST FEED PER CENT Si02 66.54 A12032.08 CaO0.70 MgO 0.00 Alkalis1.78 Fe15.63 Cu0.44 S9.42 Hg0.45 OZ. PER TON Ag0.95 Au0.151 Screen Analysis of Tailings, Per Cent Plus650.0 Plus 1001.32 Plus 15020.75 Plus 20019.85 Minus 20058.08] The pulp had a density of 22 and a pH of 7.8. Total time of conditioning was one minute. The reagent added was Texas fuel oil, 0.116lb. Of 33.7 Bé. gravity containing 0.9 per cent sulphur. Frother, 0.062 lb. of No. 5 pine oil. Rate of concentration of mercury was 25.7: 1 [ ]

Jan 1, 1941

By M. E. Nicholson

The solid solubility of boron in iron has been determined by saturating iron with respect to FeyB at several temperatures from 870° to 1135 C. In alpha iron the maximum solubility was found to be 0.002 pct B and in gamma iron the solubility varied from 0.001 pct at 915°C to 0.020 pct B at 1165OC. The eutectic and peritectoid temperatures were found to be 1165° and 911 °C respectively and the gamma iron solidus was located approximately at 0.020 pct B. RECENT investigations of boron-treated steels', ' indicate that the solubility of boron in austenite is of the order of 0.003 pct at 900°C. This has led to the general belief that the solubility of boron in a and r iron is considerably less than that indicated by Wever and Muller." Therefore the solid solubilities of boron in a and r iron have been re-determined. The eutectic and peritectoid temperatures were also remeasured and the r-iron solidus was studied in some detail.* In 1929 Wever and Miiller investigated the phase equilibria of Fe-B alloys. Fig. 1 shows the solid solubility region of the Fe-B diagram based on their investigation. They found that boron lowered the A, transformation temperature to 1381 °C where saturated 6 solid solution "which must contain about 0.15 pct B" and "r solid solution containing about 0.10 pct B" are in equilibrium with liquid containing 1.9 pct B. At the eutectic temperature of 1174"C, 7 solid solution was found to contain "about 0.15 pct B." A peritectoid relation was found to exist between a and y iron with an invariant temperature at 915 "C, where the boron solubility in 7 iron was "about 0.10 pct B" and the solid solubility in a iron "did not exceed 0.15 pct B." Although most of their

Jan 1, 1955

By Russell B. Cornell, William B. Plank

AT the close of the academic year 1940-'41 the largest number of students ever recorded received their first or bachelor degree in the mineral technology schools of the United States. The total of men thus prepared to enter their professional careers in the mineral industries was 1601, a number nearly 12 per cent larger than two years ago and nearly 75 per cent larger than four years ago. Notwithstanding this increase in the number of graduates and as had been predicted in the preliminary report in February, there was a slight decrease in the total student population of the schools in both the United States and Canada. During the college year 1940-'41, 9133 students were enrolled in the 54 schools of the United States and 764 in six of the seven schools of Canada.

Jan 1, 1941

By Fred D. Gustafson

With the postwar emergency for new housing and for new industrial buildings, much research has been done on lightweight aggregates for use in concrete and plaster. The trend toward lighter weight aggregates to relieve the dead load on the higher, steel frame- work buildings started toward the end of the last century. Progressively the requirements be- came more stringent, crushed bank slag, weighing 80 lb per cu ft as com- pared to 100 lb for crushed rock, was supplemented in some sections by foamed slags and expanded shales weighing from 40 to 60 lb per cu ft. In other sections cinders were used weighing from 40 to 50 lb, including sand. Sections favored with more recent vulcanism turned to pumice weighing from 30 to 60 lb, whereas other localities made use of diatomite, from 28 to 40 lb. Exfoliated vermiculite weighing from only 6 to 10 lb per cu ft came into use. As the search for lighter weights in aggregates continued so did the search for other desirable properties such as nailability, ease of cutting or channeling, and good insulation to both sound and heat. This search eventually led to a widespread interest in the expansion of perlite, or similar volcanic glasses, with the result that in 1946, the Office of the Housing Expediter' listed eleven firms reporting the operation of processing plants either on pilot or commercial scale producing aggregates weighing from 2 to 16 lb per cu ft.

Jan 1, 1949

By Nicholas J. Grant, Ernest P. Abrahamson

IN recent work, Bloom and Grant' and Stein and IGrant' have indicated that a high temperature chromium phase exists. In the 68 pct Cr-Ni binary they found a eutectoid reaction, P chromium transforming to a chromium plus y nickel at 1215°C. Un-

Jan 1, 1957

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who called at the Institute headquarters during the period Oct. 10; 1916 to Nov. 10, 1916. Edwin C. Bloomfield, Montreal. Roy E. Hoffman, Hannibal Mo. A. H. Collbran, Seoul, Korea. E. C. Harder, Cienfuegos, Cuba. Eugene Coste, Calgary, Canada. B. Jaeger, London, England. Fred Crabtree, Pittsburgh, Pa. Herbert H. Lauer, Philadelphia, Pa. P. St. John Dixon, London, England. Frank C. Laurie, Los Angeles, Cal. A. E. Drucker, London, England. 0. T. Lempriere, Melbourne, Australia. F. N. Flynn, Clifton, Ariz. W. C. Phalen, Washington D. C. Justice Grugan, Edwards, N. Y. William H. Rea, Pittsburgh, Pa. Fred A. Hale, Jr., Goodsprings, Nev. Thor Warner, Kingman, Ariz. P. S. Haury, Seoul, Korea. Arthur P. Allen has resigned his position with the Calumet & Hecla and is now connected with the Highland Mining Co., Ashcroft, B. C., Canada. H. Foster Bain, editor of the Mining Magazine of London, has resigned his position.

Jan 12, 1916

By O. N. Carlson, W. M. Paulson

A phase diagram is proposed for the Y-C system based on the vesults of thermal analyses, microscopic obsevvations, and X-ray diffraction studies. Three intermediate phases occur in the system: a congru-ently melting fcc phase with a wide range of homogeneity about the composition Y2C, an intermediate solid-solution region between 55 and 58 at. pct C, and a bct dicarbide melting congruently at 2415°C. All three compounds undergo a phase transformation at elezlated temperatures. A continuous serzes of solzd solutions exists between the fcc phase and the high-temperature form of YC2 with a maximum in the solidus at 2000°C and 30 at. pct C and a minimum at 1805°C and 54 at. pct C. THIS investigation of the Y-C system was undertaken as part of a nuclear materials development program. Yttrium-base alloys are of interest as possible containers for liquid metals, and carbides are currently receiving increased attention as high-temperature materials for advanced reactors and other applications. Previous work on this system was limited in scope, and the results were somewhat inconclusive and at times contradictory. Spedding et al.&apos; reported the existence of a triyttrium carbide having an fcc structure with a wide range of homogeneity and Dean et a1.2 reported the existence of a rhombohedra1 phase having the stoichiometry of Y2C. Bachella et a1.3 observed that the latter was the result of ordering of carbon atoms in the fcc solid solution. The ordering range was placed at 800" to 1000°C. Vickery et a1.4 reported a high-melting compound which they identified as yttrium dicarbide, and Spedding and coworkers1 determined the structure of this phase as bct with lattice parameters a = 3.66 and c = 6.17A. Samsonov et al.5 reported the melting point of YC2 as 2300" * 50°C. Recently Bowman et a1.6 found a transformation in the dicarbide from the tetragonal to an fcc form at 1320 20°C. Samsonov and coworkers7 reported a monocarbide of yttrium melting at 1950" * 20°C and also a sesqui-carbide melting at 1800" * 50°C. The existence of the latter has also been indicated by others,1&apos;8 but neither compound has been definitely established. The Y-C phase diagram shown in Fig. 1 was proposed by Chubb and Keller8 in 1964 based on the data available at that time. The tentative nature of this diagram together with the uncertain status of the compounds indicated that additional work on this system was needed. EXPERIMENTAL PROCEDURE Yttrium metal of 99.9 pct purity was prepared for use in this study by the reduction of YCl, with calcium to form a sponge product.9 The major impurities in this material were as follows: 100 ppm C, 150 pprn H, 20 ppm N, 300 to 1000 ppm O, <20 ppm Ca, <100 ppm Cr, <80 ppm Cu, 150 ppm Fe, <30 pprn Mg, <400 ppm Ta, and <100 ppm Ti. Alloys were prepared by arc melting yttrium sponge together with pieces of high-purity graphite rod in a purified argon atmosphere. Homogeneity was insured by repeated melting, inverting the ingot between melts.

Jan 1, 1969

Executive ARTHUR S DWIGHT, Chairman B THAYER CHARLES F RAND P MATHEWSON J V W REYNDERS Membership WILLIAM H BASSETT, Chairman W Y WESTERVELT Vice-chairman P MATHEWSON H G MOULTON F T RUBIDGE Finance WALTER H ALDRIDGE, Chairman GEORGE D BARRON GALEN H CLEVENGER

Jan 1, 1923

By R. E. Hanneman, A. N. Mariano

In conjunction with the need for accurate volumetric data in the Fe-V system for subsequent use in calculating the high-pressure diagrams, room- and high-temperature X-ray diffraction measurements have been carried out. No previous measurements have been published on lattice parameters or volume changes associated with the a transformation for Fe-V alloys. The existing literature on lattice-parameter data for the a and s phases has been reviewed by pearson1 with considerable uncertainty indicated in the data. In order to obtain a good estimate of ?Va-? for thermodynamic calculations of the a D ?(bee D fee) phase stability, high-temperature vacuum X-ray diffraction measurements were made on an Fe-V alloy of 0.92 wt pet V. The term ?Va-? is the difference of molar volumes of the limiting solubilities of the a and y phases at any given temperature; these values can be calculated readily from the appropriate lattice-parameter data. The equipment used was a commercially available MRC (Materials Research Corp.) high-temperature X-ray camera which was fitted to a Norelco diffractometer

Jan 1, 1964

By J. C. Fisher, J. H. Hollomon

The fundamental problem concerning the fracture of both crystalline and noncrystalline solids is the divergence between the actua1 and the theorcticallY computed fracture stresses; the stress required for fracture, computed from the forces between atoms, is many times that actually observed with commcrcinlly available materials. Computatiolls have been made,,2 indicating that the theoretical fracture stress should be from 100 to 1000 times that actually observed. There are other incidental problems that have arisen, perhaps the most importallt of which is the problem of size effect often observed in the measurement of the fracture stress of non-metallic solids, such as glass. Another effect conccrns the relation between deformation and the stress required for fracture, Experiments recently made with pearlitic steels indicate that the tensile fracture stress increases with increasing tensile deformation and decreases with increasing prior com-pressive deformation, This marked ani-sotropy of the effect of deformation on the fracture stress is in contrast with the essential isotropy of the flow stress. Early experiments on rock salt crystals by Joffe, et al.3 have illustrated the effect of tensile strain in increasing the tensile stress required for fracture. A consistent theory must be constructed that will explain not only the divergence, of the measured fracture stress from the theoretical value, the size effect, and the ergence of deformation; but will also explain and predict the effects of combined stress, of temperature, of strain rate, and of metallurgical structure. With respect to this last variable, it has now been relatively well established that the carbide particle is the clement of structure controlling the fracture of steels. In steels carbide particles vary in shape from plates to spheroids. It has been found that not only docs the magnitude Of the Fracture stress depend upon the size and shape of these particles. but also its dcpendencc upon strain is affected by changes in &apos;hap&apos; an&apos; size Or the particles. The precipitate resulting from the age hardening Of duralumin also modifies the fracture stress of this alloy. Nonmetallic inclusions greatly lower the fracture stress of all metals. The magnitude of the lowering depends 0&apos; the size and shape of the included particles. In glass, the major source of the low fracture stress has been fairly conclusively demonstrate&apos; by Griffith4 &apos;0 arise from real flaws or cracks present in the material. He showed that the stress concentration at the end of a defect was of suficient magnitude to raise the stress at this location to a value comparable with the theoretical strength Of the material. If the cracks were reduced in size, Griffith showed that the observed fracture slrength the by virtue Of the decrease in stress concentration. He also pointed out that cracks disposed perpendicularly to the applied tensile stress would be more effective in lowering the fracture

Jan 1, 1947

By J. H. Hollomon, J. C. Fisher

The fundamental problem concerning the fracture of both crystalline and noncrystalline solids is the divergence between the actua1 and the theorcticallY computed fracture stresses; the stress required for fracture, computed from the forces between atoms, is many times that actually observed with commcrcinlly available materials. Computatiolls have been made,,2 indicating that the theoretical fracture stress should be from 100 to 1000 times that actually observed. There are other incidental problems that have arisen, perhaps the most importallt of which is the problem of size effect often observed in the measurement of the fracture stress of non-metallic solids, such as glass. Another effect conccrns the relation between deformation and the stress required for fracture, Experiments recently made with pearlitic steels indicate that the tensile fracture stress increases with increasing tensile deformation and decreases with increasing prior com-pressive deformation, This marked ani-sotropy of the effect of deformation on the fracture stress is in contrast with the essential isotropy of the flow stress. Early experiments on rock salt crystals by Joffe, et al.3 have illustrated the effect of tensile strain in increasing the tensile stress required for fracture. A consistent theory must be constructed that will explain not only the divergence, of the measured fracture stress from the theoretical value, the size effect, and the ergence of deformation; but will also explain and predict the effects of combined stress, of temperature, of strain rate, and of metallurgical structure. With respect to this last variable, it has now been relatively well established that the carbide particle is the clement of structure controlling the fracture of steels. In steels carbide particles vary in shape from plates to spheroids. It has been found that not only docs the magnitude Of the Fracture stress depend upon the size and shape of these particles. but also its dcpendencc upon strain is affected by changes in &apos;hap&apos; an&apos; size Or the particles. The precipitate resulting from the age hardening Of duralumin also modifies the fracture stress of this alloy. Nonmetallic inclusions greatly lower the fracture stress of all metals. The magnitude of the lowering depends 0&apos; the size and shape of the included particles. In glass, the major source of the low fracture stress has been fairly conclusively demonstrate&apos; by Griffith4 &apos;0 arise from real flaws or cracks present in the material. He showed that the stress concentration at the end of a defect was of suficient magnitude to raise the stress at this location to a value comparable with the theoretical strength Of the material. If the cracks were reduced in size, Griffith showed that the observed fracture slrength the by virtue Of the decrease in stress concentration. He also pointed out that cracks disposed perpendicularly to the applied tensile stress would be more effective in lowering the fracture

Jan 1, 1947

Executive ERLE V. DAVELER. Chair u W. B. HEROY PAUL D. MERICA JOHN M. LOVEJOY WILLIAM WRAITH Finance H. G. MOULTON, Chairman H. T. HAMILTON HENRY KRUMB Admissions JOHN L. CHRISTIE, Chairman GEORGE D. BARRON, Vice-Chairman FRED H. KAY PHILIP KRAFT H. Y. WALKER

Jan 1, 1938

R. W. NEWCOMB, New York, N. Y. (written discussion*).-0n page 1712, the middle paragraph states that, in industrial equipment, only the single-step method of automatic regulation has been applied. Quite recently, there has been developed an automatic temperature regulator, operating in conjunction with a pyrometer of the thermoelectric type, in which the control is a slow regulation, with a range capable of regulat-ing valves, dampers, rheostats, or any other rotatable member, through one or more complete revolutions. It can control two valves at the same time, with a fixed definite ratio between them. Aside from those conditions in which it is. necessary to control two valves with a definite ratio one to the other, the greatest advantage that this slow, even control will have over those controls that are either all on or all off, will be for use in connection with processes where a large temperature variation is required, extended over a considerable period of time; that is, where the temperature must be regulated along an in-creasing or decreasing time-temperature curve.

Jan 12, 1919

[Year of Election 1944. WALTER HULL ALDRIDGE New York, N. Y. 1946. PETER M. ANDERSON Johannesburg, South Africa 1946. CHARLES CAMSELL Ottawa, Ont., Canada 1946. CHARLES AUGUSTUS CARLOW Fife, Scotland 1946. CECIL DESCH London, England 1946. WILLIAM FRASER London, England 1922. FEDERICO GIOLITTI Torino, Italy]

Jan 1, 1946

By Robert M. Grogan, James C. Bradbury

The Illinois-Kentucky mining district has, since 1880, accounted for 80 per cent of all U.S. production of fluorspar. The ore deposits are of two types: vein deposits formed by fissure fillings along faults and bedding-replacement deposits formed by the replacement of strata at certain favored stratigraphic positions along minor faults and fractures. Fluorite is the chief valuable mineral in the deposits. Sphalerite and galena commonly are present in small amounts but, in some ore bodies, may form a substantial part of the valuable constituents of the ore. Calcite is the chief gangue mineral; quartz and barite Exposed strata range from Devonian are present in various amounts. through Pennsylvanian in age. Igneous intrusive rocks occur as mafic dikes and sills and intrusive breccia dikes and plugs. Structurally, the district is situated on a generally northwest- trending arch that has been sliced into a series of long, narrow blocks by normal faults that trend northeastward. The structural The localization of the ore deposits by faults and fractures, the association of fluorite mineralization with intrusive breccias, and various lines of petrographic and geochemical evidence indicate that the fluorite-zinc-lead deposits were epigenetic and deposited by solutions emanating from a deep alkalic magma.

Jan 1, 1968

By AIME

Burton J. Westman-Besides decreasing the diamond size, there appear to be two other approaches open to overcome excessive diamond loss and, more particularly, the rapid diamond polish that took place in this quartz-feldspar rock. First, however, a short discussion of the diamond characteristics should be made in order to discuss the situation more clearly. The West African diamonds which we can assume were used. for this drilling have two disadvantages when drilling hard, exceptionally fine-grained rocks. These are rapid polishing and, if .the bit isn&apos;t "drilled in" carefully, a tendency to damage, resulting in excessive diamond loss. The normal wear resistance of any diamond is inversely proportional to the compressive strength of the diamond, therefore only the highest grade, of diamonds free from insipient fractures should be employed. Using upwards of 90 diamonds per carat instead of the20 to 30 per carat not only decreases the total projected area of the cutting points but increases the stress per point which, in turn, causes greater depth of penetration into the rock. Considering this depth of penetration, therefore, suggests an approach other than increasing the, number of diamonds per carat and that is to decrease the actual number of diamond points (also the carat weight per bit) so that the penetrating force on an individual diamond is increased. This penetration increases the chipping or rock shearing action.

Jan 1, 1950

By Johannes Moeljono, Werner Wenzel, Heinrich Wilhelm Gudenhau

As an important mechanism for increasing production of the suction-draft-sinter process, it has been shown that gas permeability through the sinter layer plays an important role. Methods to increase production rates have been indicated and suggestions for carrying out the process have been made to improve the rate of production, reduce the fuel consumption, and at the same time obtain a uniform sinter. Laboratory experiments were conducted at the Institute for Ferrous Metallurgy of the Technical University at Aachen to illustrate these methods. Methods of Increasing Gas Penetration Through Sinter Layers The following are of fundamental importance in determining the process cycle during the sintering of iron ores: 1) Generation of maximum temperature, since its form and range determine sinter quality. 2) Propagation velocity of the temperature maximum which controls the attainable output. 3) The convective heat transfer which influences the velocity of travel of the temperature maximum.

Jan 1, 1974

By Paul R. Dingess, Edward H. Hare, Douglas C. Brockie

Mining in the Tri-State district of Missouri, Kansas, and Oklahoma has been nearly continuous from about 1848 until the present day, although the major activity was from about 1880 to 1955. The district, which has produced over $2 billion in zinc and lead concentrates, ranks as one of the greatest mining districts in the world. Unlike other Mississippi Valleytype deposits in the United States, which occur in Cambrian and Ordovician limestones and dolomites, the Tri-State district ores occur in Mississippian limestones containing abundant chert. Zinc is 5 to 6 times more abundant than lead. In the Picher Field, the principal sub-district which has accounted for 61 percent of the total district production, most of the ore has been mined from the single horizon, M bed. Most ore bodies, other than those of the "Sheet Ground" or blanket-type, are in large, essentially flat-lying breccia zones and have a definite mineral zonal pattern. An irregular, generally elongated central dolomitic core is surrounded progressively outward by the main ore run, the jasperoid zone, the muddy or shaly and bouldery zone, the sparry calcite limestone zone, and the fossiliferous, dominantly crinoidal, limestone zone. Some of the zones may be absent or nearly so and may overlap to some extent with an adjacent zone. Although the district has been studied by many authors, much controversy still exists about such items as genesis, paragenesis, and time of emplacement. These subjects are discussed in the paper.

Jan 1, 1968

NEW MEMBERS The following list comprises the names of those persons who became members during the period Oct. 10, 1918, to Nov. 9, 1918. ALLER, FRANK D., Copper Met., Ore Purchaser, American Smelt. & Refin. Co., 120 Broadway, New York, N. Y. AVÈRY, PAUL W., Met. Engr., Esperanza Min. Co., Apt. 8, El Oro, Mex., Mexico. BAKER, CHARLES A., Leaching Foreman, Copper Leaching Plant, Anaconda Copper Min. Co., Anaconda, Mont: BREED, CHARLES H Met., Crown Cork & Seal Co., Baltimore, Md. CHASE, R. L., Min. Engr 102S First National Bank Bldg., Denver, Colo. EICHELBERGER, FRANK, Vice-pres. and Engr., New York-Montana Testing & Engrg. Co., Helena, Mont. GESTER, G. C., Geol., Standard Oil Co. of Cal., 616 Standard Oil Bldg., San Francisco, Cal. GRIFFIN, JOHN, Mgr., Anthracite Territory, The Dorr Co., Board of Trade Bldg., Scranton, Pa. HAYNES, ELWOOD Pres., The Haynes Stellite Co., Kokomo, Indiana. Hsi, T. C:.. Sec&apos;y, Tayeh Iron & Steel Works, Tayeh, China. HYDE, AUSTIN T., Mgr., Keokuk Plant, River Smelt. & Refin. Co., 607 Franklin St., Keokuk, Iowa.

Jan 12, 1918

By F. F. Aplan

Mineral processing engineers have recorded an- other year of active research and development work. Most gratifying was the broadly based attendance at the Mineral Processing Fundamental (formerly Basic Science) Committee sessions at the 1968 Annual Meeting of the AIME. Because of the availability of good papers, the active discussion and the growing attendance, sessions have grown from one to three at the annual meeting. Prof. M. C. Fuerstenau of the University of Utah will chair the Mineral Processing Fundamentals Committee for the next two years and we may thus be assured of continued active leadership. The name change from "Basic Science Committee" to the more descriptive "Mineral Processing Fundamentals Committee" approved by the MBD executive council is a welcome improvement. Our profession continues to attract the interest and cooperation of those in other professional groups. The 1968 Engineering Foundation Particulate Matter Conference, under the chairmanship of John Karpinski of Bethlehem Steel, was devoted exclusively to comminution this year. It attracted conferees from five continents and served as a particularly stimulating source of interchange of knowledge from many technical fields. Next year&apos;s conference will be under the chairmanship of Professor L,. G. Austin of The Pennsylvania State University. This conference plus the Symposium on Wettability and Flotation to be held at the annual American Chemical Society meeting in Minneapolis in April indicates the success achieved in the inter-disciplinary approach to problems. Other evidence of this spirit of professional cooperation is the forth- coming book on Size Reduction edited by D. W. Fuerstenau. This is the outgrowth of an AIChE symposium on size reduction held in 1965.

Jan 2, 1969