By R. Taggart, R. H. Ericksen, D. H. Polonis

Transmission electron microscopy techniques hare been used to study the spontaneous marfensite phase that forms during the thinning of Ti-Cr alloys. The structure of this phase has been found to differ. from the hcp martensite and has been identified as a clisforted fcc lattice. The spordaneous marlensile in this system is interpreted as a metastable isomorph of the equilibriunz TiCr, phase. WHEN thin-foil specimens for transmission electron microscopy were prepared from metastable alloys of the Ti-Cr system, a spontaneous transformation occurred' when the foils contained the untrans-formed 0 phase or two-phase mixtures of the 0 and w phases. The purpose of this paper is to examine the relationship that exists between the crystal structure of the spontaneous product and that of the matrix. The differences between the martensite transformation that occurs in the bulk material and the spontaneous reaction that occurs during the preparation of thin foils are compared with the observations that have been reported for similar phenomena in a commercial titanium alloy.' A spontaneous reaction that exhibits characteristics similar to a martensite transformation has been reported to occur in thin foils prepared from the retained metastable structures of several alloy systems.1'3"7 ~ull~ observed such a spontaneous reaction in 0 brass and attributed the apparent increase in the martensite transformation temperature to a decrease in the non-chemical free energy associated with bulk strain energy. He also showed that the spontaneous product did not have a specific habit plane, but that its orientation relationships to the parent matrix were dependen on the thickness of the transforming region. It has also been pointed out by Breedis6 that in thin films the absence of the constraints imposed by a bulk matrix can cause different requirements for the martensite plate interface and lattice distortion which is reflected bv a dependence of the transformation mechanism on the specimen geometry. In the case of the spontaneous reaction reported for Au-Zn alloys7 a definite habit plane was determined and shown to correspond with the habit plane calculated on the basis of the Bowles and Mackenzie crystallographic theory of the martensite transformation.'- lo EXPERIMENTAL PROCEDURE A series of titanium alloys containing 5.5, 5.9, 6.4: 7.6, 8.0, 11.3, and 18.7 at. pct Cr were prepared from high-purity (iochrome) chromium and iodide-grade titanium by levitation melting. The experimental procedure used for sectioning the alloys and for thin-foil preparation has been reported in an earlier paper.' X-ray diffraction patterns were obtained using a 114-mm Debye-Scherrer camera and Cu-Ka radiation. In order to minimize fluorescent radiation from the specimen, a strip of aluminum foil 0.002 in. thick was placed in contact with the X-ray film. After a specimen was removed from the camera: an additional X-ray experiment was performed, to insure that no spurious lines were obtained due to the presence of the aluminum foil. The interstitial impurity analysis for the alloys used in this study was as follows: oxygen, 100 ppm: hydrogen, 30 ppm: nitrogen, 28 ppm. EXPERIMENTAL RESULTS Electron diffraction patterns were obtained from several individual crystals of the spontaneous marten-

Jan 1, 1970

By Bernt Ellingsaeter, Terkel Rosenqvist

IN the silicothermic reduction of magnesia, burned dolomite is treated with high grade ferrosilicon in an evacuated steel retort at temperatures between 1150° and 1200°C. The following reaction is assumed to occur MgO + CaO + 1/2 Si (Fe) - Mg(g) +- & Ca,SiO, + Fe with the equilibrium constant on the basis of thermodynamic data for the substances involved and assuming unit activity for all solid constituents, Kubaschewski and Evans' calculated the magnesium pressure as a function of temperature logp,, (mmHg) = 15.06-1.61 T- log T- 13,16O/T. Pidgeon and King," who measured the magnesium pressure by means of a flow method, found values about three times the calculated ones. This may be caused by uncertainties in the thermodynamic data, but may also be caused by the formation of other reaction products, such as Ca,SiO,, which is known to be the stable silicate in equilibrium with lime. Whatever the exact reaction may be, it is evident that as long as all other factors are maintained constant the magnesium pressure will vary with the silicon activity, viz: p,, = &,. (p,,) ", where (p,,)" is the magnesium pressure by the reduction with silicon of unit activity. In the present investigation, p,,, was therefore measured for various grades of ferrosilicon and their silicon activities were calculated. The experimental method was similar to that used by Pidgeon and King. Briquettes of burned dolomite and Fe-Si alloys were placed in a 1 in. heat resistant steel tube and were heated to 1200°C. By means of a flow of purified hydrogen, the magnesium vapor was swept into a condenser filled with steel wool. From the amounts of hydrogen used and magnesium condensed the magnesium partial pressure was calculated. First a tube of 28 pct Cr steel, and later a tube of Kanthal D (a ferrous alloy with 22.6 pct Cr, 2 pct Co, and 4.5 pct Al), was used as a heat resistant tube. The latter tube showed the best heat resistance. The dolomite used had the following composition: 43.6 pct MgO, 55.5 pct CaO, 0.2 pct K,O + NalO, 0.2 pct Fe,O,, and 0.3 pct insoluble. The ferrosilicons were prepared from 98 pct Si of technical grade (0.7 pct Al, 0.3 pct Ca, and 1 pct Fe) by melting with various amounts of electrolytic iron of high purity. The alloys thus obtained were analyzed on their iron and silicon contents, which added up to between 99 and 100 pct. The amounts of reactants were chosen so that there would always be an excess of the oxides, and the average decrease in silicon content during the experiments would be about 1 pct. Most of the reaction occurred in the part of the reaction mixture facing the gas flow. The change in the silicon concentration in the part facing the condenser was, therefore, negligible. To facilitate the reaction, about 1 pct fluorspar was added to the briquette mixture. Fluorspar does not enter the reaction, but is known to act as a

Jan 1, 1957

By M. J. Pool, P. J. Spencer

Using liquid tin as the solvent metal, the heats of solution of silver and gold in dilute Ag-Au-Sn alloys have been determined at 723°K by solution calorimetry. From the values obtained, the various enthalpy interaction coefficients in the liquid solutions have been calculated. The self-interaction coefficients Au and Ag values of 2413 and -6322 cal per g-atom in binary Au-Sn and Ag-Sn alloys, respectively. For an alloy containing 0.04 mole fraction Ag, Au is equal to 2443 cal per g-atom, and in an alloy containing 0.04 mole fraction Au, Ag has a value of —8883 cal per g-atom. Ag Au has been determined as —2650 cal per g-atom. ADDITION of a second solute to a dilute binary alloy may cause striking changes in the thermodynamic characteristics of the alloy. As yet, such influences cannot be reliably predicted and it is only by accumulation and critical assessment of data that definite patterns can be established. Solute interactions in dilute solutions were first treated mathematically by Wagner,1 who derived expressions for the Gibbs energy interaction coefficients. For an alloy consisting of. two dilute solutes, i and j, in a solvent s, these coefficients are given by: where yi is the activity coefficient of component i and x represents the mole fraction of solute or solvent. Other interaction coefficients have since been established in terms of the various partial molar thermodynamic properties of an alloy; the definitions of these are summarized in a recent paper by Lupis and Elliott.2 Mathematical and experimental studies of such coefficients have received much attention recently, providing a very useful theoretical background to an understanding of the nature of solute interactions taking place in dilute solutions. One of the definitions to arise from such work has been the extension of Wagner's treatment by Lupis and Elliott4 to include an enthalpy interaction coefficient, defined as. where ?Hi is the relative partial molar enthalpy of component i. ?Hi is related to the relative partial molar enthalpy at infinite dilution, ?Hio, and to the enthalpy interaction coefficients by the expression: Values of ?Hi can often be obtained with a high degree of accuracy by calorimetry, and, if the composition of the alloy is carefully controlled by making calculated solute additions throughout a series of measurements, application of Eq. [2] will enable reliable enthalpy interaction coefficients to be determined. Partial heats of solution must be investigated as a function of solute concentrations down to xi = 0, and, since ? values are obtained from the slope of mi plotted against x, great care must be taken to obtain precise data. The data for binary systems which are presently available often require extrapolation of ?Hi values from compositions as great as xi = 0.05 or even 0.1 to obtain limiting heats of solution. Reliable enthalpy interaction coefficients are thus impossible to obtain from published data for most of the alloy systems already investigated. The aim of the present work was to determine values of Au, Ag, Ag, and Au in the limit xsn -1 for the relatively simple Ag-Au-Sn system and from these results to gain some insight into the possible influence

Jan 1, 1969

By Paul Pietrokowsky

THE formation of intermediate phases in the solid state reaction of titanium with silicon, germanium. and tin (of subgroup 4B in the periodic table) was the subject of a recent paper.' Further investigation of the system Ti-Sn revealed the presence of a new compound on the titanium-rich side of this phase diagram. Metallographic evidence indicated that this new phase was situated very close to 75 atomic pct Ti. The present work is concerned with the crystal structure of the intermediate phase Ti3Sn. Iodide-process titanium metal, furnished by the New Jersey Zinc Co., was used in this investigation. The metallic tin was received in powder form from Charles Hardy Inc., New York; its purity was 99.80 pct. The titanium rod was machined into small cups 1 cm in diam and about 1.5 cm in height. The tin powder was compacted, melted, and then placed in the titanium cups and alloyed by electric arc melting in a helium atmosphere. The alloys, weighing approximately 8 g, were sealed in evacuated quartz tubes and homogenized at 1030°C for 5 days. This isothermal heat treatment was terminated by a water quench from the soaking temperature. Filings of the alloyed pellets were sealed in evacuated quartz bulbs and quenched from 1030°C into liquid argon. A 14.32 cm Debye Scherrer X-ray camera was used for the powder diffraction study. The copper radiation was filtered. X-ray diffraction data for the compound Ti3Sn are given in Table I. The data were indexed on the basis of a hexagonal lattice. Good agreement between observed and calculated values of the square of the reciprocal interplanar spacings was obtained with the following expression: (1/d)2 = 0.03810 (h2 + hk + k2) + 0.04410 (l2) Unit cell parameters were calculated by the method of least squares from the reflections (20.3), (22.2), (40.1), and (42.1); ao = 5.916 & 0.004A, co = 4.764 ± 0.004A, and co/ao = 0.805. The relatively small size of the unit cell allowed the unambiguous indexing of most of the reflections from planes of large spacing. An inspection of the assigned indices (Table I) reveals the absence of (hk.l) reflections when 1 2n. A systematic absence of this type leads to the space group C 6/mmc or one of its subgroups. Assuming, for a first approximation, a linear increase in the density of titanium with the addition of tin, it follows that there are two stoichiometric molecules of Ti3Sn per unit cell. The density calculated from X-ray measurements is 5.194 g cm-'. At this point it became clear that Ti3Sn might be isomorphous with Mg3Cd. The 6 Ti and 2 Sn atoms were placed in the following positions of space group D4 6h, C 6/mmc: 6Tiin (h): X 2X 1/4; 22;; 1/4;Xx 1/4;x2x3/4; 2x x 3/4; x x 4; with x = 516 2 Sn in (c): 1/3 2/3 1/4; 2/3 1/3 3/4.

Jan 1, 1953

By NILS DANIELSEN

THE name of Swedish charcoal iron will probably bring to the memory of many old consumers an extremely tough and ductile iron which was formerly used in considerable quantities for common blacksmith purposes. To-day very little of this iron goes to such kind of work. Swedish charcoal iron is merely a speciality which is chosen whenever its remark¬able properties can be utilized. By giving a rough sketch of the manufacturing process of Swedish charcoal iron, the character of the iron, its weak as well as its strong points will more easily be understood. Swedish charcoal iron is a wrought iron also known in the United States under the name of Norway iron and Swedish Lancashire iron. The name Norway iron seems to have been attached to the product for the reason that in the earlier days it was generally brought into the States by Norwegian ships. However no iron of this kind is now made in Norway. The reason for the name Swedish Lancashire iron is that the manufac¬turing process emanated from Lancashier in England, the method being generally adopted in Sweden in the years 1831-1850. Today this iron is, with the exception of one plant in the United States, made in no place in the world outside of Sweden.

Jan 1, 1924

By B. Fazan, O. D. Sherby, J. E. Dorn

McLean's technique was employed to determine the effect of temperature on the contribution of grain boundary shearing to the total creep strain in pure aluminum over the range of 610° to 747°K. The contribution of grain boundary shearing at the same stress was found to depend upon a temperature-compensated time, where the activation energy AH was practically identical with that for total high temperature creep. SEVERAL outstanding investigations by McLeanl-' have demonstrated that the total creep strain in polycrystalline aluminum at 473°K arises from microscopically detectable slip, subgrain tilting, and grain boundary shearing. Whereas microscopically detectable slip arises from dislocations that move out of the grains, subgrain tilting is due to entrapment of dislocations of like sign in subgrain bound-arles. Consequently, creep in polycrystalline aggregates appears to be the resultant of two mechanisms, namely, migration of dislocations and grain boundary shearing. This suggests that an appropriate law for creep should contain two additive terms ?1 = ?d + ?yb where the total creep strain, ?1, depends on the sums of the creep strains arising from motion of dislocations, ?d, and from grain boundary shearing, ?yb. But extensive investigations5 over wide ranges of alloys, grain sizes, temperatures, and stresses have shown that the total creep strain is quite accurately dependent on the single term functional relationship ?1 = f (?), s = constant where s is the stress (constant),* ? = te-?H/RT, t is the time under stress, AH is the activation energy, R is gas constant, and T is absolute temperature. Since Eq. 2 was found to be valid over those ranges where appreciable grain boundary shearing is observed, it appears probable that the activation energy for grain boundary shearing might be identical with the activation energy for migration of dislocations. Thus, under a given stress, it could be thought that where fd and fgb represent the appropriate functions for each mechanism of creep. The primary objective of this investigation was to obtain a direct check on the accuracy of this hypothesis. Experimental Procedure and Results Rolled aluminum sheet (99.987 pct Al), 0.100 in. thick, was used in this investigation. Creep specimens having a 0.25 in. wide, 3 in. long gage section were so machined that their axes were in the rolling direction. All specimens were annealed for 9 hr at 894°K before testing to produce a mean grain diameter of about 0.1 in. One face of each specimen was polished electrolytically in 10 pct HBF4. In order to permit accurate measurements of grain boundary shearing, the polished surface was lightly scribed with a ruling machine accurate to ±0.0001 in. to give a uniform grid of lines which were 0.01 in. apart. Although it was thought that surface working might modify the creep behavior in the vicinity of the scribed grid lines, this technique nonetheless was employed because such local differences in creep properties should not modify seriously the fractions of the total creep strain due to grain boundary shearing or to migration of dislocations. All creep tests were conducted under constant load with an initial stress of 250 psi. The specimen tem-

Jan 1, 1955

By FREDERICK LAISY

A NUMBER of new plants for the treatment of copper ores were completed or under construction during the year. Among these may be mentioned the plants of the International Nickel Co., those of the Hudson Bay Mining and Smelting Co. and of the Roan Antelope Copper Co. Three copper re- fineries have been constructed, one at El Paso, Tex., and the other two in Canada. Two more are projected, one in France and one in England. The International Nickel Co.'s plant consists of an 8000-ton concentrator and a smelting plant containing thirty 10-hearth Herreshoff roasting furnaces, five reverberatory furnaces, and eight Smith-Pierce converter5 . The smelting plant is estimated to have a capacity of 5000 tons of ore or concentrate per day. The roasters are superimposed on the reverbratory furnace plant. As a consequence of this arrangement, the furnace building is unusually high. being 183 ft. from yard level to highest roof elevation.

Jan 1, 1931

By R. W. Fountain, W. D. Forgeng, G. M. Faulring

Precipitation of the phase Co3Ti (Cu3Au type) from a Co-5 pct Ti a11oy has been investigated using single-crystal X-ray diffraction techniques. Oscillation and transmission Laue patterns of specimens aged for short-time periods at 600" C indicate the formation of titanium-rich and titanium-poor zones coherent with the {100} matrix planes. Longer aging times at 600° C establish that the equilibrium phase also forms on the {100} matrix planes as platelets. These observations are corroborated by electron metallography; electron diffraction studies show the phase Co3Ti to be ordered. A probable sequence of the precipitation reaction is discussed. A previous publication by two of the present authors reported on the phase relations and precipitation in Co-Ti alloys containing up to 30 pct Ti.1 The results of this investigation established the existence of a new face-centered cubic inter metallic phase, ranging in composition from about 17.0 to 21.7 pct Ti at temperatures below 1000° C The decomposition of the fcc supersaturated solid solution was studied employing hardness and electrical resistivity measurements. The changes in hardness upon precipitation in alloys containing 3, 6, and 9 pct* Ti were found to be associated with an initial increase in hardness followed by a plateau and then a second, more pronounced hardness increase. Investigation of this behavior by electrical resistivity measurements suggested that two different kinetic processes were involved, which, when interpreted in terms of the kinetic relation,2-4 indicated that initial precipitation was in the form of thin plates. On continued aging, the plates impinged during the growth process. The general features of these findings have been confirmed by Bibring and Manenc,5 while, in addition, they report the phase to be ordered. The present investigation was undertaken to provide more definite information on the structural relationships between the precipitate and the matrix. EXPERIMENTAL PROCEDURE Single crystals of a (20-5 pct Ti alloy were prepared from the melt employing the Bridgman technique. Poly crystalline rod, 1/2 in. in diam, prepared from vacuum-melted material, was machined to 3/8- in. diam to remove any surface contamination that may have resulted from hot-working. The crystals were grown under a purified hydrogen atmosphere in high-purity alumina crucibles heated by induction. Considerable difficulty was encountered in attempting to grow monocrystals because of the high melting point of the alloy and the high solute concentration. However, one crystal about 6 in. long was obtained which was essentially a single crystal except for one or two very small grains around the periphery. The as-grown crystal was solution heat-treated for 24 hr at 1200°Cin a purified argon atmosphere and water-quenched. One-quarter-in. slices were taken from each end of the solution heat-treated crystal for chemical analyses, and the remainder of the crystal was mounted and oriented by the back reflection Laue Method. The chemical analysis of the crystal was as follows: Pct Ti Pct 0 Pct C Pct N Pct H Pet CO 5.29 0.08 0.004 0.002 0.0003 Balance By proper tilting of the crystal, it was possible to obtain slices 1/32 in. thick of [loo] and [110] orientation. The solution heat-treated crystal slices were sealed in silica capsules for the aging treatments, with titanium sponge placed at one end of the capsule to act as a getter. All slices were water-quenched from the aging temperatures, the capsules being broken under the water to ensure a rapid quench. Thinning of the slices for transmission X-ray studies was accomplished by a combination of mechanical and electrolytic techniques, the final thickness being about 0.1 mm. Laue patterns of the solution heat-treated crystal indicated that no strain was introduced by the thinning technique. ELECTRON METALLOGRAPHY After X-ray examination, the structural changes attending the precipitation were followed by examination of direct carbon replicas of polished and etched surfaces of the single-crystal slices and extracted phases. The earliest indication of significant structural change was observed after aging at 600°C The structure of a heavily etched, solution-treated crystal is shown in Fig. l(a). Aside from the etch pit pattern, no regularity of background structure is observed. On the other hand, in the background of the specimen heated for 500 hr at 600°C, the etching pattern shows a directionality indicating the influence of minute precipitate particles, Fig. l(b). On electrolytic dissolution of this specimen in 10 pct HC1 in alcohol, a large volume of very small, flattened cubes

Jan 1, 1962

By C. L. Magee, H. W. Paxton

The effects of testing temperature, frorn 77" to 420" K, and volume fraction of martensite on the micro-plastic response of unaged Fe-31Ni martensite-austenite aggregates have been determined. The kinetics of the aging phenomena which lead to a decrease in the microplastic response were also characterized. These determinations, supplemented by other experimental results, show that at least two mechanisms of plastic deformation give rise to the apparent softness of the quenched structures. Only one of these mechanisms is fully discussed in this paper The transformation of retained austenite to martensite during the application of stress leads, in specified conditions, to large microplastic strains. This deformation behavior cannot be described by normal transformation plasticity theory but is shown to result from the fact that stress-assisted formation of martensite is a possible deformation mode. The present results and further considerations of previous work lead to the conclusion that it is unnecessary to postulate a special work-hardening mechanism to explain the mechanical properties of unaged martensite. It is now generally accepted that dislocation motion can occur in many solids at stresses very much below the L'macroscpic" yield stress, e.g., 0.1 pct offset. This phenomenon has been investigated by a variety of techniques including measurements of elastic limit,' effective static elastic modulus,~ and irreversible deformation following stressing at low levels.3"5 Of particular interest to the work to be described are exper -iments conducted on the deformation of martensite in attempts to decide whether freshly quenched ferrous martensites are "hard" or "soft".6 Muir, Averbach, and cohenl and McEvily, Ku, and ~ohnston' have shown that as-quenched ferrous rnartensites can be plastically deformed at relatively low stresses. A difference between these two sets of experiments exists in that some diffusion of carbon would take place before testing in the experiments of Muir et a1. because the plain Fe-C alloys which they have tested transform to martensite well above room temperature. McEvily et a1. examined Fe-Ni-C alloys with Ms of about -30"~ and tested the alloys directly after quenching to — 195" ~ —a technique which obviates any appreciable carbon diffusion. Unfortunately, a characteristic of the alloys which transform below room temperature is that they do not transform entirely to martensite. The results discussed below will show that, because the transformation of this retained austenite under stress leads to plastic deformation, one cannot investigate the properties of martensite by such experiments. The existence of a second deformation phenomenon, which is not caused by retained austenite, is also established in the present work. In line with a previous suggestion,' it is believed that the second microdefor-mation mode is principally due to the internal stresses generated by the formation of martensite. To avoid confusion in the present report, the evidence we have found for this interpretation will be discussed separately in a brief note.7 EXPERIMENTAL Materials. The alloys were induction-melted and cast under vacuum; the resulting compositions are given in Table I. The ingots were hot-swaged to 2-in.-diam bar and further cold-swaged and/or cold-rolled prior to specimen preparation. The standard tensile specimens were machined from sheet. The gage section was 0.05 by 0.2 by 5 in.; 0.75-in.-wide ends had 0.2 5-in. centered holes for pinloading. The three-point bend samples were 0.075-in. thick and 0.6 in. bide. The distance between the outer loading points was 5.5 in. In order to establish a standard starting condition, all specimens were quenched to 77°K prior to annealing in vacuo for austenitizing. The temperature of the austenitizing anneal was controlled to + 5"~. The testing and aging temperatures were maintained by various liquid baths (nitrogen, 77"~; freon, 130° to 200°K; acetone, 200 to 300°K; silicone oil, 300' to 450°K) to better than il°K. Strain Measurement. The results herein were derived from both uniaxial tension and three-point bending experiments. For bending tests, the stresses and strains reported are those corresponding to the maximum fiber values. Normally, because of the small strains involved, very sensitive strain measurements are necessary to make microplastic measurements. However, because of the magnitude of the dilatation and shear involved in the martensitic transformation, the requirements in the present experiments proved to be less rigorous. In most experiments the plastic strain was evaluated by measuring stress relaxation and modulus defects. In this method, specimens are loaded rapidly to some predetermined load on an In-

Jan 1, 1969

By R. W. Stormont, F. Wald

The phase diagram of the Pseudobinary section PbTe-Fe was determined. It was found to contain a monotectic and a eutectic reaction, the latter one taking place at 14 at. pct Fe and 875° * 5°C. The solid solubility of iron in PbTe was found to be 0.3 at. pct by electronmicroProbe analysis. No solubility of PbTe was detected in iron. Slight deviations from true pseudobinary behavior were found to occur in the range of - 5 to 10 at. pct Fe. In the course of a general investigation of reactions of various metals with lead and tin telluride,' the lead telluride-iron system was reinvestigated. It had been established much earlier than iron does not chemically react with lead telluride but forms a eutectic with a melting point of 879" The eutectic composition or other related information has never been reported, but for a number of years iron has been in general use for contacting of lead telluride and lead telluride alloys for thermoelectric applications. It seems therefore desirable to clarify the exact constitution of the system to furnish a base for the long-term evaluation of bonds made between lead telluride and iron either by pressure contacting or by brazing methods. I) EXPERIMENTAL METHODS Lead telluride-iron alloys were prepared in 10-g charges, using premelted lead telluride. This material was prepared from high-purity, semiconductor-grade lead and tellurium obtained from the American Smelting and Refining Co. and described as 99.999 pct pure. The iron used was "Armco" iron; the major impurities found here were 0.02 pct C, 0.018 pct Si, and 0.015 pct Cr. All remaining impurities were less than 0.01, the total of all impurities not exceeding 0.15 pct. Charges were prepared in closed quartz arnpoules which were evacuated and in some cases backfilled with high-purity argon to retard excessive lead telluride evaporation and deposition in slightly cooler parts of the ampoule. For high iron concentrations, this can lead to total separation of the constituents, since the vapor pressure and the sublimation rate of PbTe are quite high.4 Nevertheless, since the ampoules are closed, no change in overall composition was expected and the nominal composition of all alloys was assumed to be retained. X-ray diffraction analysis, thermal analysis, and microsections were used in the evaluation of the alloys. The nature of the system was such that X-ray diffraction was not particularly helpful. It merely served to establish that at all concentrations PbTe and a! iron were in equilibrium at room temperature. Thermal analysis was carried out by taking direct temperature vs time curves on a Sargent recorder where a width of 10 in. was kept as 1 or 0.5 mv by use of an automatic bucking voltage network. Quartz ampoules with minimized dead space, coated with boron nitride and fitted with a thermocouple reentrant, were used as containers for the charge. At high temperatures and over long periods of time, boron nitride reacts with iron. For the thermal analysis runs, however, this was not significant. More significant was the fact that the vapor pressure of PbTe at some of the meas -uring temperatures apparently exceeded I atrn quite considerably. This, in some cases, caused the slightly softened quartz tubes to blow out if great care was not taken to contain them and minimize time and temperatures used. As containers pure nickel tubes were used which also served to avoid temperature gradients in the quartz ampoule. Nevertheless, the experimental difficulties at high temperatures were severe and the monotectic temperature could therefore not be determined accurately. In general, the accuracy reached by the thermal analysis setup in this case is *4"C as determined with gold, silver, and tin, under the conditions of analysis here. Inherently, the apparatus is capable of reaching accuracies better than i 1°C. Also, difficulties were encountered in microsection-ing. They were related to polishing, since it is rather difficult to avoid pulling the iron out of the weak and brittle lead telluride matrix. It proved best to follow a procedure where, after grinding to 600 grit on carborundum paper, a polish with 6 p diamond was used on nylon cloth. Finally, #3 "Buehler" alumina and an automatic polisher were used for -5 min only, to avoid relief. The best etching results were achieved with

Jan 1, 1969

R. Schuhmann, Jr. (Purdue University)— Fulton and Chipman's results on rate of silica reduction from slags are analogous in many was to the results of Parlee, Seagle, and Schuhmann10 on rate of alumina reduction from alumina crucibles. Both investigations have given comparably low rates of reduction and slow approaches to equilibrium. Accordingly, we may hypothesize that the rate-determining step is the same in both kinds of experiments; that is, oxygen diffusion across the stagnant boundary layer on the liquid-metal side of the interface between the liquid metal and the oxide phase (slag or solid oxide). I suggest that silica reduction involves the following consecutive steps: I) At the slag-metal interface: SiO2(slag) Si+ 20 II) Transport of oxygen from slag-metal to gas-metal interface: a) diffusion across liquid-metal boundary layer at slag-metal interface. b) convection within the body of liquid metal. c) diffusion across boundary layer at metal-gas interface. 111) At the metal-gas interface: C +O- CO (gas) Iv) At the graphite-metal interface: C (graphite) -C At steelmaking temperatures it is reasonable to assume that equilibrium is attained in all three chemical reactions (I, 111, and IV) right at the respective interfaces. Convection within the stirred liquid metal (step IIb) is also rapid. Transport of Si and C should be orders of magnitude easier than transport of 0, because of the relatively high concentrations of Si and C. Accordingly, we might expect the overall reaction rate to be determined by boundary-layer diffusion of oxygen, either IIa or IIc. Fulton and Chipman's demonstration that bubbling CO through the system had no major effect on reaction rate indicates that IIc is not the slowest step. Therefore, it becomes logical to estimate the maximum rate for step IIa and to compare this theoretical estimate with Fulton and Chipman's experimental data. If oxygen diffusion across the liquid metal boundary layer at the slag metal interface (step IIa) is rate-determining, In this equation, dn sio, /dt is the rate of silica reduction in moles per sec,A is the area of slag-metal interface in sq cm, Do is the diffusivity of oxygen in sq cm per sec, 6, is the boundary layer thickness in cm, c,* is the oxygen concentration right at the slag-metal interface in moles per cubic cm, and co is the oxygen concentration in the body of the liquid metal, also in moles per cubic cm. Equilibrium data" on the silicon deoxidation reaction in liquid iron and steel at 1600°C indicate that the oxygen contents of the liquid metal in Fulton and Chipman's experiments at 1600°C probably fell in the range of 0.5 x10-3 x10-3wt pct. That is, the maximum conceivable value of co*-co for the system under consideration was on the order of 10"5 mole oxygen per cubic cm. On the basis of previously published data,1O,11 it is estimated that Do/0 will fall somewhere in the range from 10-3 to 10-1 cm per sec. The surface area A in Fulton and Chipman's experiments was approximately 20 sq cm, and the weight of metal involved was about 500 grams. Combination of all these figures with the above rate equation leads to an estimate that the rate of silica reduction should fall within the range from 0.002 to 0.2 wt pct Si per hr. This estimate is consistent with the experimental data. For example, Fulton and Chipman's Fig. 2 shows a change of about 0.3 pct Si in 10 hr, corresponding to an average rate of 0.03 pct per hr. According to the proposed hypothesis, increasing the temperature will increase the reaction rate ill two ways: 1) by increasing oxygen diffusivity and 2) by increasing the oxygen concentration (oxygen solubility) in the liquid metal. The combination of these two effects accounts for the high value of the observed activation energy. Summarizing, I propose that the rate of silica reduction, like that of the carbon-oxygen reaction, is diffusion controlled and that low oxygen concentration in the liquid metal is the major factor accounting for the very low observed rates of silica reduction. John Chipman (author's reply)—The authors thank Professor Schuhmann for his interesting contribution. His proposed explanation may well prove to be the correct one. There is clearly a need for much further experimental work on this problem, and further research is in progress.

Jan 1, 1961

By R. R. Vandervoort

The creep behavior of Nb(Cb), Ta, Mo, and W was determined under conditions of constant atomic dif-fzisivity, constant stress to elastic modulus ratio, and nearly equivalent grain size, and the steady-state creep rates obtained from these tests were correlated with calculated stacking fault energies for the metals. These results, in conjunction with similar data for several fccMetals,13 suggest that stacking fault energy may influence the creep strength ofbcc metals. The interrelationship between steady-state creep rate, subgrain size, and stacking fault energy was examined. It was found that the subgrain size for a given creep stress, increased as stacking fault energy increased, but that this relationship did not cormpletely account for the effect of stacking fault energy on creep rate. The crystallography and energetics of stacking fault formation in bcc metals has been discussed by a num-ber of authors,1-5 and impurity stabilized stacking faults on (112) planes have been observed in Nb,6,7 w,8,9 Fe,] and V" by transmission electron microscopy. However, a crucial question is whether or not stack-ing faults influence the mechanical strength of bcc metals. Potentially, stacking faults could increase strength by reducing the mobility of the partial dis-locations bounding the fault, by acting as barriers to slip dislocations, and by retarding the climb of dislo-cations during high-temperature deformation. The objective of this study was to seek a correlation be-tween creep strength and stacking fault energy for several bcc metals; namely, Nb, Ta, Mo, and W. The creep behavior of most polycrystalline metals and alloys at high temperatures and moderate stresses can be described by the following relation:11,12 im=Af(s) where i, = minimum creep rate, A = constant, j(s) = a function involving metallurgical structure, a = applied stress, E = average elastic modulus at the test tempera-ture, w = constant (equal to 5 for most pure metals), D = diffusion coefficient. One factor in the structure function F(s) which sig- R. R. VANDERVOORT, Member AlME is Research Metallurgist, Process and Materials Development Division, Chemistry Department, Lawrence Radiation Laboratory, University of California, Livermore, Calif. Manuscript submitted February 28, 1969. IMD nificantly affects the creep resistance of fcc metals is stacking fault energy, and creep rate has been shown to vary directly with stacking fault energy to the 3.5 power." In the latter investigation, four fcc metals of widely different stacking fault energies (Ag, Cu, Ni, and Al) were creep tested at a constant stress to modulus ratio of 1.21 x 10-4, at a constant diffusivity of 2.7 x 10-12 sq cm per sec, and at nearly equivalent grain sizes of about 0.7 mm. The creep data were then correlated with stacking fault energies. In the present study, a similar procedure was followed. All materials used in this work were consolidated by powder metallurgy techniques. Impurity contents in the as-received materials are listed in Table I. Chemical analyses showed that no measurable contamination of the test specimens occurred during pretest annealing treatments or creep testing. Specimens with a gage section 0.75 by 0.125 by 0.050 in. were creep tested in tension in a vacuum of less than 10-9 torr. Deformation at temperature was measured by tracking fiducial marks on the gage section of the specimen with an optical comparator. Optical deformation measurements also permitted observation of the macroscopic characteristics of the deformation Table I. Typical Specimen Impurity Content, ppm Nb Ta Mo W C 45 10 155 6 O 185 30 4 10 N 30 6 3 2 H 5 I 1 <1 als 3 10 2 15 Ca <5 I3 5 Cr 5 <3 10 <5 Cu 10 50 2 15 Fc 10 10 150 35 Ni 2 150 20 <5 Si <I0 1 3 <10 Ta 100 Ti 10 8 1 Zi 15 50 1 3 Table II. Test Conditions for Constant Stress-Modulus Ratio of 6 X 10.&apos; and Constant Diffusivity of 2.7 X 10-12 sq cm per see, and Grain Size Values for the Given Pretest Annealing Treatments Literature references Pretest Annealing for E and D Treatment Stress, Temperature, ___"&apos;Values__ Grain Tempera-Metal psi "C E D Size, mm ture, .C Time hr Nb 745 1525 14 15 to 17 0.83 1650 I Ta 1220 1770 18 19.20 O.91 1800 I Mo 1975 1630 18 21 0.77 2200 I W 2140 2265 18 22 040 2400 5

Jan 1, 1970

By R. G. Knickerbocker

A STURDY and consistent expansion of the metal industry occurred in 1947 exemplified by an increase of approximately 30 per cent in steel consumption over 1946. For this major reason, ferroalloy metals have seen their most useful and important peace-time year. The current domestic rate of consumption of high-grade ferroalloy ores, together with added consumption of new foreign producers as well as for eign nationals&apos; restrictions on high-grade exports, makes very evident the increasing difficulties of obtaining sufficient high-grade ores. This accentuates the need for new and less expensive methods of production of ferro-alloy metals of higher purity from lower-grade domestic resources. As an important factor in preparedness, procurement of these high-grade, -critical ferroalloy minerals and metals for our nation&apos;s stock piles is a most important task. Also, this stock-piling can be the means of supplying incentive for the industrial development of the new metallurgical processes and plants necessary for the recovery of ferroalloy metals from our domestic low-grade deposits.

Jan 1, 1948

By Zay Jeffries

OF the new production of non-ferrous metals in 1930 gold will rank first in value. We usually think of copper as the most important non-ferrous metal. The copper industry as a whole, that is, adding copper production to copper fabrication, is the largest non-ferrous metal industry. Prior to the world war; however, gold led in value of new metal produced. During the war copper passed gold in value, but gold regained its position during the 1921 depression. For the past several years copper has again passed gold, but in 1930 gold promises again to regain the lead. The gold producer has at times been called a social parasite, largely because we &apos; cannot eat or drink gold, or because we cannot use it for clothes or for the construction of buildings. Let us briefly examine this accusation.

Jan 1, 1930

By AIME AIME

DURING the morning session," on Feb. 17, papers were presented and discussed regarding a recent wire saw installation, cement rock quarry operations, hydration factors in gypsum deposits and the status of the phosphate industry of the West. Oliver Bolvles presided and there were about twenty-five members present. W. M. Weigel&apos;s paper (T. P. 262), "The Application of the Wire Saw in Marble Quarrying," was read by the author. He described the recent installation of the St. Clair Marble Co., near Guion, Ark. Since the use of the wire saw for quarrying is comparatively new and the fact that it has been almost entirely limited to slate quarries heretofore, ?he description and data given in this paper were of much interest.

Jan 1, 1930

"World Mining and Metals Technology" is the title of this year&apos;s SME-AIME Fall Meeting and Exhibit in Denver, Sept. 1-3, where a record number of exhibits are scheduled for display. The international theme is particularly appropriate, for in addition to the annual SME session, the Third MMIJ-AIME Joint Meeting will be held.

Jan 8, 1976

By R. Grierson, L. J. Bonis

The high-temperature Strength oF TD nickel has been observed to be dependent upon the previons thermal and mechanical history of the material. Variations in both the level and the anisotropy of strength have been observed. 01 this paper- these variations are correlated with the storing of annealing resistant elastic strain energy in the matrix of the TD nickel. An x-vay line -broadening tecknique is used to measure the maLrTis elastie strain. THE inclusion of a finely dispersed second phase into a ductile matrix has long been recognized as an extremely effective method of strengthening the matrix both at high and at low homologous temperatures. It has been found, however, that the factors which determine the high-temperature strength are not the same as those which are important at low temperatures. Below 0.5 Tm the size and distribution of the second phase particles are of prime importance in determining the strength,&apos;)&apos; while above this temperature the strength is mainly dependent upon the previous thermal and mechanical history of the alloy,3-7 This paper is primarily concerned with explaining the response of the high-temperature mechanical strength of one of these alloys (DuPont&apos;s TD nickel) to various thermo-mechanical treatments. It will be shown that this response is not associated with the occurrence of any form of dislocation substructure within the matrix of the alloy. It has been found, however, that a correlation does exist between the elastic strain level in the matrix and the previous thermomechanical history of the alloy and that the observed changes in elastic strain level parallel the measured changes in high-temperature strength. It therefore must be concluded that variations in high-temperature strength are a direct result of the variations in elastic strain level. MATERIAL TD nickel contains approximately 2 vol pct of Tho2 in an unalloyed nickel matrix. It is formed, as a powder, by a chemical technique and this powder is compacted to form ingots which are then extruded to give 21/2-in.-diam rod. Rod of smaller diameter is prepared from the as-extruded rod by swaging. In the studies reported in this paper, 1/2-in.-diam rod was used. This rod received an anneal of 1 hr at 1100°C prior to being used in any of these studies. EXPERIMENTAL TECHNIQUES Two methods were used to examine the structure of the nickel matrix of the TD nickel. These were: 1) transmission electron microscopy; 2) the analysis of the position and profile of X-ray diffraction lines obtained using the nickel matrix as the diffracting media. To prepare thin foils for electron-microscopical examination, slices of TD nickel approximately 0.050 in. thick were cut from the as-received 1/2-in.-diam rod. These were then chemically polished down to 0.045 in., rolled to 0.009 in., given a predetermined heat treatment, and thinned, using a modified Bollman technique, to provide the foils for observation. All observations were carried out at 100 kv, using a Hitachi HU-11 electron microscope. Specimens of the undeformed rod were prepared by grinding down the 0.050-in.-thick slices to approximately 0.015 in. and then thinning chemically and electrolytically to give the thin foils. The X-ray specimens were prepared by rolling 0.375-in.-thick rectangular blocks down to 0.075 in. The surfaces of the rolled material were ground flat, chemically polished to remove the layer disturbed by the grinding, and given a predetermined anneal in an inert atmosphere. They were then ground lightly to check their flatness and given a final chemical polish prior to being examined. The X-ray diffraction line profiles were measured using an automated Picker biplane diffractometer. A special specimen holder was built to allow a more accurate and reproducible positioning of the specimen. The line profiles were determined by carrying out intensity measurements at intervals of either 1/30 deg or 1/60 deg over a range of 3 deg on either side of the nickel peaks of interest. A piece of pure nickel which had been recrystallized to give a large grain size was used as a standard to give the X-ray line profile generated by a strain-free matrix. The analysis of the X-ray diffraction line profiles is a modification of that due initially to Warren and Aver-bach8and has been described elsewhere.3 This analysis gives a measurement of two parameters associated with the structure of the nickel matrix. These parameters are: 1) the size of the coherently diffracting domains within the nickel matrix; 2) the magnitude of the elastic strains in these domains. Both of these parameters are first determined in terms of a Fourier series. These series are obtained from other Fourier series which describe the measured profile of the X-ray diffraction lines. Thus, for both the coherently diffracting domain size and the elastic strain level, it is possible to plot Ft (the Fourier coefficient) against t (the term in the Fourier series), where t can be expressed in terms of a distance L and the Fourier coefficient Ft(S) (associated with elastic strain level) can be expressed in terms of the root mean square strain (e2)1/2. Thus a plot of (F 2)1/2 vs L can be obtained. Plots of this type are shown graphically in Figs. 6 and 8. Interpretation

Jan 1, 1968

By S. G. Cupschalk, F. A. Dahlman, J. J. Wert

Studies have been undertaken to determine the indicidual effects of particle size, degree of long-range ovder, antiphase domain size, and root mean square stran on the microhardness and yield strength of ordered alloys. Dnta have been analyzed for Cu3Pt initzally ordered to a value of 0.82 and after deformations of 1 and 6 pct. It was observed that deformation fleatly reduced the degree of long-range order. Furtherrnore, wztkin this range of relatively small deforntntlons, the average particle size changed very little while the antiphase domain size was greatly reduced. Smultaneosly, the mcrohardness changed by a factor of two durzng the deforrtation process. PREVIOUS studies have reported some of the effects of cold work on the broadening of X-ray diffraction peaks. These investigations were performed on powder and wire samples representing both ordered and disordered states; i.e., the specimens were initially studied in a severly cold-worked condition. By comparing the difference in line shape between the annealed and cold-worked peaks, fundamental information was obtained concerning particle size, strain distribution in different crystallographic directions, degree of long-range order, and change in antiphase domain size. Considerable theoretical work has been done concerning the analysis of diffraction data obtained from cold-worked metals. Stokes&apos; expressed the change in diffraction profiles in terms of Fourier coefficients. Much of the work in this area has been summarized by warren2 in an extensive review article concerning the analysis of plastic deformation by X-ray diffraction. Cohen and Bever3 applied these techniques in studying the effects of cold work on alloy systems exhibiting long-range order. They utilized the Fourier coefficients of fundamental peaks in conjunction with those of the superlattice peaks to determine the change in antiphase domain size. Little work of this nature has been reported for ordered systems that have undergone small degrees of plastic deformation. The purpose of this investiga-tion was to determine the effects of small deformations in such a material with respect to particle size, strain distribution in various crystallographic directions, antiphase domain size, degree of long-range order, and hardness. EXPERIMENTAL PROCEDURE CusPt was used for the initial investigation since the order-disorder transformation takes place with- out a change in crystal structure. The transformation is readily detectable via X-ray diffraction techniques due to the large difference in the scattering factors of copper and platinum. Additionally, the alloy is relatively low melting (approximately 1300°C) and is easily deformable in both the ordered and disordered states. 1) Specimen Preparation and Cold Working. A 100-g, 12-in. diam., cylindrical specimen of Cu3Pt was prepared by melting and casting 99.99 pct pure Cu and Pt i.n vacuo. Prior to any mechanical working, the material was homogenized in a vacuum for 60 hr at 100O0C, and surface defects were removed by machining to a depth of approximately 116 of an in. The material was then cold-rolled, with an intermediate anneal, into a strip approximately 12 in. wide by 14 in. thick. Straightening and flattening removed another 0.025 in. from the thickness. After a recrystallization treatment at 750°C for 30 min, the specimen was slow-cooled from 55OoC, at the rate of 6°C per hr, down to 150°C to induce superlattice formation. This treatment yielded an ASTM grain size of 7 and a degree of long-range order equal to 0.83 0.06. After obtaining X-ray and Knoop hardness data, the sample was cold-rolled approximately 0.75 pct in one pass through a hand-operated jewelers&apos; mill. X-ray and hardness data were again obtained and the specimen was reduced an additional 5.41 pct in a single pass through the mill. 2) X-Ray Measurements. The specimen was examined in the ordered condition and after the two degrees of cold working previously mentioned using a General Electric XRD-5 unit equipped with a spectrometer and scintillation counter. Using Mo-Ka radiation with a zirconium filter, six orders of the 100 reflection were obtained. It was anticipated that point counting would be necessary for an accurate determination of the low-intensity peaks and tails: however, it was demonstrated that, by using a scanning speed of 0.2 deg per min and the appropriate time constant, the recorded data were sufficiently accurate. Thus, for ease of experimental procedure, all peaks were recorded on chart paper. Specimen position in the holder was considered to be insignificant after making a series of measurements of the same peak area in different positions with respect to the beam. Since peak overlapping did occur at high values of 20, it was necessary to separate the peaks graphically prior to analyzing the data in order to minimize this source of error. The peak tails were also carefully drawn to obtain the best possible data. Fourier coefficients of the line profiles were calculated on an IBM 7072 computer, and graphical meth-ods2j3 were employed in analyzing the results. For this type of calculation, in which the line profile is represented by intensities taken at set intervals, the intervals selected must be sufficiently small to give an accurate representation of the line profile. It was decided that for 20 = 0.02 deg the line profiles were

Jan 1, 1967

By Carl Wagner

This paper contains solutions of the differential equation of diffusion in binary alloys if the diffusion coefficient is an exponential function of the concentration of one of the components. THE general differential equation for one-dimensional diffusion in a binary system can be written as: where c is the concentration of one of the two components in any suitable units; x, the distance from a reference plane; t, time; and D, the diffusion coefficient. Hartley and Crank&apos; have pointed out that eq 1 with conventional length units for measuring the distance x holds only if the alloy can be regarded as a rigid framework. In general, this is not the case, especially if the lattice parameter varies appreciably with composition. If a modified coordinate system is used instead of an orthodox system based on the centimeter a:: length unit, eq 52 is obtained, which has the same general form as eq 1 and is generally valid. The necessary transformations are presented in the appendix. If&apos; D is independent of concentration, analytical solutions of eq 1 are known for numerous boundary conditions. If D depends on concentration, solutions based on known analytical functions are not available. Among others, Boltzmann2 and Matano3 have shown that the concentration c depends only on (x/t1/2) in the case of diffusion between two semi- infinite spaces with uniform initial concentrations: c = c, for x < 0, t = 0, i.e., x/tl/2 = — x [21] c = c2 for x > 0, t = 0, i.e., x/tl/2 = + a Moreover, Boltzmann and Matano have shown how D may be calculated as a function of concentration over the whole range of composition from c -c, to c = c2 if c as a function of (x/t1/2) for the initial conditions stated in eq 2 has been determined experimentally. Thus, for instance, in principle, the diffusion coefficient in silver-gold alloys may be calculated as a function of concentration for the whole range of composition from only one diffusion experiment with a couple of pure silver and pure gold welded together. If the diffusion coefficient D as a function of concentration c is known, a solution of eq 1 for boundary conditions as stated in eq 2 with arbitrarily chosen values of c, and C2 may be wanted. For instance, if the diffusion coefficient in an alloy A-B as a function of concentration has been derived from an experiment with a diffusion couple involving 0 and 30 pct B as initial. concentrations, the calculation of the concentration distribution in a diffusion couple involving other initial concentrations, e.g., 5 and 20 pct B, may be desired. This problem may be solved by numerical or graphical integration of eq l. The solution of an ordinary differential equation of second order, which results from using (x/t1/2) as an independent variable, can be computed quite rapidly if two conditions for the same value of the independent variable are given. In eq 2, however, two conditions are given for two

Jan 1, 1953

By S. I. Liu

THE effects of strain histories, consisting of several prestrains in opposite directions, on the flow and fracturing characteristics of metals determined in a final test have been investigated previously.&apos;" Such strain histories vary from a single prestrain in tension or compression to the number of strain cycles leading to fatigue failure.&apos; Between these two limits, various strain histories could be visualized and some can be attained readily. One such example is a strain history consisting of a first prestrain in tension of various magnitudes and a second prestrain in compression also of various mag-nitude. In this investigation the strain history was extended to the combination of these two limits, i.e., a single prestrain in tension or compression followed by balanced strain cycles of a selected magnitude e, = k0.12. It was found in this case that only compressive initial prestrains could be investigated with sufficient accuracy.* Such strain histories can be considered also as (low cycle) fatigue tests of a metal subjected to various amounts of cold working. It appears from previous publications that cold working within a wide range of reductions usually raises the un-notched fatigue strength of many metals.&apos;-&apos; This effect, however, has been found to be inconsistent and sometimes reversed for other metals?.7 Furthermore, Ludwik reports that the yield strength of cold-worked specimens may be reduced by cyclic strains, while that of materials without cold work is generally increased in the initial cycles." " In addition to the above tests, a study was made of the effect of intermediate re-solution heat treatment on low cycle fatigue behavior. Such anneals should eliminate the strain hardening induced by the cyclic strains. As far as their effect on the fracture characteristics is concerned, a few previous tests seemed to indicate that the damage resulting from cyclic strains is retained only partially after heat treatment." A further investigation was made in which one specimen was subjected to repeated unbalanced tension cycles in which the strain interval was approximately $ 0.013. This repetition of plastic tension damages the material slightly. This result appears to confirm Ludwik&apos;s observations." " Commercial 3/4-in. rod of the aluminum alloy 24ST4 was selected for this investigation. The material was subjected to the following treatments before machining: 1—Re-solution treatment at 920" ± 10°F for 45 min, 2—water quench at room temperature, and 3—aging for four days at room tem-perature.? The treated material then was machined to desired specimen contour and tested. A coolant was used during machining to minimize any artificial aging effects of heating during machining. In some cases the 24ST4 specimens were reheat treated after having been strained. In these cases, the heat treatment was the same as the re-solution heat treatment described above. Procedure As shown in Fig. 1, threaded end specimens with a minimum diameter of 0.266 in. and a contour radius of 2 in. were used for prestraining to an axial compressive strain ranging from 6, = —0.10 to E, = —0.48. For large prestrains, two consecutive corn-

Jan 1, 1952