By John T. Eash, Clair Upthegrove

During recent years nickel has had an increasingly important role as an alloying element in the copper-tin bronzes. Nickel additions not only produce better casting alloys but also make alloys whose properties can be varied by precipitation hardening; thus leading to increased commercial application of copper-nickel-tin alloys. Recent investigations have indicated a decrease in the solubility of tin in the alpha phase as the annealing temperature is lowered and as the nickel content is increased within certain limits. A further change caused by the nickel additions is produced in the excess phase of the copper-tin bronzes. The alpha plus delta eutectoid is replaced by a clear precipitated constituent in the alloys containing up to 15 per cent tin and not less than 1 per cent nickel. This paper has a dual purpose. The first is to present a new determination of the alpha-phase boundary in alloys containing from 0 to 20 per cent nickel, together with the liquidus and solidus temperatures above that field. The second purpose is to give the equilibrium conditions existing in alloys exceeding the alpha phase containing up to 31 per cent tin and 5 per cent nickel, so that the disappearance of the alpha plus delta eutectoid constituent may be explained. After considering the earlier investigations of the related alloy systems and the experimental procedure used in this investigation, the alloys will be discussed in groups as separate quasibinary systems containing constant amounts of nickel. The systems considered contain 0, 1, 2, 3, 5, 10 and 20 per cent nickel. The straight copper-tin system was reinvesti-gated in order to establish a foundation on which to build the remaining material. The 1 per cent nickel alloys studied give the relations existing in the region of the eutectoid transformation between the copper-tin system and the 2 per cent nickel copper-tin system which has been investigated in detail. The thorough examination of the latter system was made since 2 per cent of nickel is representative of the commercial additions to the cast bronzes and also because it is sufficient to produce

Jan 1, 1933

By Herbert Hoover

YOUR committee asks that I speak today on the relations of the engineering profession to public affairs. That takes in a lot of ground. This being a cheerful occasion, I will assume that I should exclude the engineer's function as a taxpayer. This being a nonpartisan occasion, I will assume that I should not refer to his voting emotions in 1940. Perhaps what was in the minds of your committee was the application of engineering thought to the confusions of the times. That is also a lot of ground. I fear, however, its boundaries disappear in mirages and rainbows on all sides. Now any entry of the engineer into public affairs involves his breaking into the fields of the sociologists, the economists, and the politicians. However I don't know why, seeing the difficulties these professions are having, they should not welcome a little help.

Jan 1, 1939

One of the best known of the early mining districts of Nevada was that at Eureka, where gold was first produced in 1864. While the most productive period for the district was during the early 1900s, production was maintained until World War II. During this time it is said that the Eureka district produced as much as $200 million from over 3,200 km (2,000 miles) of tunnels and workings. The Windfall Mine was discovered in 1902; and a 100 ton cyanide plant was operated there during the periods 1907 to 1912 and 1932 to 1940. Since 1974, however, Windfall Venture has been operating a unique heap leaching facility on the site of the old Windfall Mine. Gold at the Windfall occurs primarily in the Cambrian Hamburg dolomite which has been "sanded" and in which the original cementing material has been destroyed. The gold is micron sized and is accompanied by anomalous amounts of arsenic and mercury; however, the ore is low in base metals which distinguishes it from the typical Eureka district ores. Mining the ore causes it to break down into very fine sizes, approximately 50% minus 150 microns (100 mesh). Conventional heap leaching by spraying proved to be impossible; and extensive test work on alternate methods, aided by the United States Bureau of Mines, was conducted using 9 m (30 ft) high columns and then large tonnage heaps. The leaching procedure adopted was to build 10.6 m (35 ft) high heaps on a 50 mm (2 in.) asphalt pad covered with a layer of gravel for drainage assisted by perforated pipe drains and gravel-packed sumps. A berm is constructed around the top of each pad and cyanide solution is allowed to “pond” on top of the heap. The resulting percolation is at the rate of 24 liters per sq m per hr (0.6 gal per sq ft per hr), a figure about 2.4 times the average used in other heap leaching operations. The dolomite furnishes its own protective alkalinity and no lime or caustic is used in the solution which contains 0.4 kg per mt (0.8 lb per st) of NaCN. Pregnant solution from the heaps averages about 0.7 g Au per mt (0.02 oz per st) with a cyanide content of about 0. 2 kg per mt (0.4 lb per st) and a pH of plus 9. Addition of NaCN brings the pH of the leach solution up to 11 to 12. Carbon adsorption of the gold was originally done in six enclosed columns mounted in a trailer but five conventional columns have been substituted as the size of the operations has increased. Carbon stripping is with hot caustic, cyanide and 10% ethanol solution. The

Jan 1, 1981

By J. W. Pugh, J. D. Nisbet

F. B. Foley—The use of data published by Wever and Jellinghaus in 1931 to fix boundaries of the sigma phase in the Fe-Cr system, in the face of the author's own references to the suggestions of Bradley and Goldschmidt, Aborn and Bain, and Hougardy that the phase is much more extensive, and the very much more accurate work, which weighs heavily in favor of these suggestions, of Cook and Jones, published in 1943 and evidently disregarded by the authors, makes their derived ternary diagram, especially fig. 15 for 400°C, quite inaccurate on the Fe-Cr side and affects the extent of phase boundaries in the most controversial and important part of this ternary system. In commercial Fe-Ni-Cr alloys the occurrence of sigma has been observed time and time again at lower chromium contents than that of the 24 pct Cr, 16 pct Ni, 60 pct Fe alloy which is the lowest permitted by fig. 15 of practically carbonless metal. Newel1 reports sigma in 27 pct Cr-Fe even with some carbon present to be one of the greatest detriments to its extensive application, whereas Pugh and Nisbet set a low limit of 36 pct Cr for sigma in the binary Fe-Cr system. J. J. Heger—The diagrams presented by the authors do not agree with observations made on commercial Fe-Cr and Fe-Cr-Ni alloys, nor do they agree with two recent investigations made on the Fe-Cr and the Fe-Cr-Fe systems. I refer first to the investigation made by Cook and Jones1' on the sigma region of the Fe-Cr system. On the basis of their results which were published in 1943, Cook and Jones established new boundary limits for the sigma and the alpha plus sigma regions. These new limits have been accepted and are incorporated in the Fe-Cr diagram that appears in the 1948 edition of the Metals Handbook. This diagram is shown here as fig. 34. As will be noted, the boundary limits of the alpha plus sigma region in this diagram extend to much lower chromium contents than do those in the diagram presented by the authors in fig. 2. These new limits indicate that sigma phase should form in an Fe-Cr alloy containing 26 pct Cr, and experience with commercial alloys confirms this finding. Indeed, recent studies on a commercial Fe-Cr alloy containing 17 pct Cr have shown sigma phase to be stable in this alloy at 550°C. I recognize that the authors' work did not include studies on the sigma region; however, I believe this is a serious omission because sigma phase may profoundly affect the physical properties of these alloys and should be evaluated in any investigation which attempts to relate physical properties to the equilibrium diagram. The second investigation to which I refer is that made on the Fe-Cr-Ni system by Rees, Burns, and Cook,'' who used pure alloys and employed heating 17 W. P. Rees, B. D. Burns, and A. 3. Cook: Journal Iron and Steel Institute. (July 1949) 162, Part 3. p. 325. times that extend to 200 days. These investigators published their results in July 1949 and from these results constructed isothermal sections at 800" and 650°C. The isothermal section at 650°C is shown here as fig. 35. This diagram indicates sigma phase should form in a pure 18 pct Cr-8 pct Ni alloy. Although sigma phase has not been observed after 10,000 hr at 1200°F in commercial 18-8 alloys containing carbon and nitrogen, it has been observed under the same conditions in 18-8 alloys modified with titanium and columbium, both of which serve to reduce the effect of carbon and nitrogen. This section and the one at 800°C suggest that the constant iron sections which are presented by the authors, should be considerably altered, if they are to represent an accurate picture of the system. A few of the suggested alterations are as follows: In fig. 9, the section at 50 pct Fe, the gamma plus sigma region should be widened, not narrowed at 800" and 650°C. In fig. 10, the section at 60 pct Fe, the gamma plus sigma region should be widened at 800° and 650°C. In fig. 11, the section at 70 pct Fe, an alpha plus sigma, an alpha plus gamma plus sigma, and a gamma plus sigma region should be added. In fig. 12, the section at 80 pct Fe, the alpha plus gamma region should be widened at 800°C. In fig. 13, the section at 90 pct Fe, the alpha plus gamma region should be widened at 650° and 800°C. Undoubtedly, the chief reason for the discrepancies between the authors' data and those of Rees, Burns, and Cook is that the authors did not employ long enough heating times to allow for transformation. In this connection, I wish to warn that transformations in these alloys, particularly transformations at temperatures below 800°C, are extremely sluggish and may require a year or more to approach completion. Therefore, unless extremely long heating times are employed or steps are taken to accelerate these transformations by such means as mechanical working, the results will not yield an accurate picture of the alloy system. Certainly, an accurate picture is needed for the development of better high-temperature materials. E. J. Dulis-The purpose of this work is not clear. If an improvement of the ternary equilibrium diagram of the Fe-Cr-Ni system was wanted, it seems logical that testing techniques superior to those previously used would be a prime requirement. To approach equilibrium in this system, long holding times are needed; a fact established long ago but apparently ignored by the present authors, who used the continuous heating and cooling tests in equilibrium studies. A publication on the same system by Bradley and Goldschmidt6 was criticized by Monypenny in a

Jan 1, 1951

By C. P. Proctor

WESTERN Pennsylvania, eastern Ohio, and Illinois are carrying out experiments wherein much more slate and other impurities are loaded with the coal in the mine and hauled to the surface preparation plant for removal. In general everything is sent to the cleaning plant although there may be some gobbing in the mine. No conclusions have been announced as to the effect of such a mining system on clean coal costs. Such factors as ability of the surface plant to handle the impurities, land and facilities for disposing of the impurities, and the transportation facilities underground should be considered.

Jan 1, 1942

By C. H. Li, S. H. Bendel, J. A. Sartell

Small additions of Mg to a 62 Cu-38 Ni alloy reduce the oxidation yates drastically between 500° and 850°C. Metallographic examination of the oxide scale disclosed a continuous network, identified by X-ray diffraction as (Ni, Mg)O solid solutions, located along the former alloy grain boundaries. This network acts as a barrier to diffusion. It is thought to result from the segregation of mg to the alloy grain boundaries. Oxidation occurs preferentially in these regions because of the presence of this more active element. To substantiate these ideas, homogenized alloys ulere oxidized. No oxide network was produced and oxidation rates were the same as for the parent 62 Cu-38 Ni alloy. An interesting aspect of the oxidation of the 62 Cu-38 Ni alloy previously described by the present authors, is the relationship between oxidation kinetics and changes in the microstructure of the oxide.' The oxide scale on these alloys consists of two layers: a thin layer of CuO outside a much thicker layer of Cu20 in which particles of NiO are dispersed. In addition, immediately beneath the oxide-metal interface there is an internally oxidized zone in which NiO particles are dispersed in a copper-rich alloy matrix. Experimental observations on the growth of the individual layers under isothermal conditions have led to the conclusion that the rate-determining step in the oxidation of this alloy is the diffusion of anions through the Cu20 layer. It has been found that this diffusion rate is increased by the recrystallization of the outer CuO layer. Willardson and Gorton have reported that the addition of magnesium to the 62 Cu-38 Ni alloy causes a decrease in the oxidation rate.2 The present investigation was undertaken in order to determine the mechanism by which magnesium additions improve the oxidation resistance of the 62 Cu-38 Ni alloy. EXPERIMENTAL PROCEDURE Fifty-gram ingots of Cu-Ni alloys were prepared by vacuum melting materials of 99.999+ pct purity. These ingots were then remelted in a He atmos- phere and magnesium added in the form of a previously prepared and analyzed Cu-Mg master alloy. This procedure was necessitated by the high reactivity of pure magnesium at high temperatures. The proportion of the alloying elements was adjusted so as to obtain alloys with the desired magnesium content while maintaining a Cu-Ni ratio of 62 :38 by weight. (All alloy compositions will be given in weight percent.) Since it was considered desirable to study the oxidation of only single-phase, solid-solution alloys, it was necessary first to determine the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy. A series of melts with various magnesium contents was made, homogenized by annealing for 48 hr at 975OC, then cooled in the furnace. Metallographic samples were prepared, etched in a potassium dichromate solution and examined at XI500 for the presence of a second phase. The alloys were then chemically analyzed and it was found that the approximate limit of solid solubility of magnesium in the 62 Cu-38 Ni alloy was 1 pct Mg. The ingots containing less than 1 pct Mg (0.19, 0.29, 0.58, and 0.87 pct Mg) were cold-rolled down to thicknesses suitable for oxidation experiments and specimens for gravimetric studies were cut to dimensions of 3.0 by 1.5 by 0.05 cm, specimens for inert marker studies, 0.6 by 0.6 by 0.17 cm. These were heat-treated in a protective atmosphere at a temperature (975" C) well above the oxidation temperatures and furnace-cooled to insure structural stability of the alloy during oxidation. Immediately prior to oxidation, the specimens were chemically cleaned by immersion for 1 min in a solution of 2 parts nitric acid, 1 part acetic

Jan 1, 1961

By Jun Hino, P. G. Shewmon, P. A. Beck

THE investigations of Crussard,' of Guinier and Tennevin,' and of Dunn and Daniels," indicate that the subgrains formed in a cold worked and annealed metal are capable of growing at each other's expense during annealing, if the temperature of annealing is sufficiently high and the time is long enough. The results of Dunn and Daniels are particularly convincing in showing that subgrain growth is essentially the result of the free surface energy associated with the subboundaries. In subgrain growth, as in ordinary grain growth, energy is gained as a result of the decrease in total subboundary surface area per unit volume. Recently, Wood and Scrutton4 found that the rate of subgrain growth upon annealing increased very considerably, if simultaneously a creep strain was applied to the specimen at a low strain rate. Working with 99.98 pct pure fine-grained aluminum, these investigators found that the continuous X-ray diffraction back-reflection rings of material strained at room temperature remained continuous after heating for ten days at 250 °C. However, when heated at the same temperature under a stress of 1000 psi even for only three days, the formerly continuous X-ray diffraction rings broke up into numerous dots, which were fairly clearly separated from each other. The continuous X-ray diffraction rings were interpreted as indications of a very small subgrain size, not resolved by the X-ray diffraction method used. The breaking up of the continuous X-ray diffraction ring during annealing under stress was taken as an indication of a great increase in subgrain size, so that the individual subgrains could then be resolved. The effect of simultaneous strain at a low strain rate in accelerating subgrain growth, discovered by Wood and Scrutton and designated by them as "cell growth," is of fundamental importance. The experiments described in this note were carried out in order to confirm Wood and Scrutton's results by direct metallographic observation. Also, information was sought as to the minimum creep strain necessary to produce this effect. A fine grained high purity aluminum strip was prepared by alternate 33 pct rolling and annealing treatments for 1 hr at 350°C. Specimens cut from this strip were subjected to a relatively fast creep strain of 7.2 pct in 3.5 min at 300°C under a constant load initially corresponding to 1185 psi. The subgrains set up were large enough (about 0.015 to 0.03 mm) to be clearly observed (Fig. 1) at X200 magnification with polarized light, after electrolytic polishing and anodic etching, producing a fine oxide film." The corresponding X-ray diffraction pattern is shown in Fig. la. After the fast creep strain treatment a portion of the specimen was subjected to a creep strain of 8.3 pct in 44 hr at 350°C under a constant load initially corresponding to 320 psi. Another portion, annealed under the same conditions, but not strained, served as control specimen. The subgrain size of a typical area of the specimen annealed under strain and of the one annealed without strain is shown in Figs. 2 and 3 (X-ray diffraction patterns, Figs. 2a and 3a). Annealing without strain produced clearly observable subgrain growth (subgrain size: about 0.03 to 0.05 mm). The effect of simultaneous strain was to increase greatly the rate of subgrain growth (resulting in a subgrain size of approximately 0.05 to 0.13 mm), in accordance with Wood and Scrutton. In another experiment, the effect of the amount of simultaneous strain was studied. The initial subgrain structure was set up by fast creep, as described previously. The specimen was then heated at 350 °C under a constant load initially corresponding to 320 psi, as above, for 2.2 hr (0.24 pct strain), and 8.8 hr (0.58 pct strain). Comparison with the corresponding unstrained control specimens by means of X-ray diffraction showed that 0.58 pct strain definitely had an effect, but the effect of 0.24 pct strain was doubtful.

Jan 1, 1953

By C. R. Ince

THE term "differential flotation" is used to denote a flotation operation in which separation is effected between two or more minerals of the same class; e. g., lead sulfide from zinc sulfide, pyrite from blende, chalcopyrite from pyrite, chalcopyrite from blende. At present, so far as published work shows, there seem to be two theories as to the mechanics of differential flotation. The earlier and more generally accepted theory is that the so-called depressing agents alter the surface of one or more of the sulfides in the ore, either by chemical action or adsorption, so that it is no longer amenable to flotation, but that these depressed sulfides can be revived, after the unaffected sulfide has been floated, by reagents which react chemically with the altered surface and make it amenable to flotation. More recently, Professor Taggart1 has advanced the theory that slime adsorption is an important factor in differential flotation. He believes that, with the proper use of a class of agents, which he calls .dispersion agents and which include practically all the depressing agents, one can cause the slime to adsorb differentially on sulfide surfaces. A gangue-slime coated sulfide surface will act as a gangue particle and will not float. If, subsequently, an agent that will remove the gangue-slime coating is added, the sulfide again assumes its original surface and can be floated as an ordinary sulfide. This-is the basis of the slime theory of differential flotation. Timber Butte mill at Butte, Mont., is a typical lead-zinc flotation concentrator. Neihart ore, chosen for investigation in this work, is one of the custom ores treated at that mill. Practice at Timber Butte mill in February, 1928, was as follows: A combined lead-zinc concentrate was first made using 0.2 lb. per ton on the ore of potassium xanthate and 0.03 lb. per ton of Cleveland Cliffs oil after 1.5 lb. per ton of lime and 1 lb. per ton of calcium chloride has been added just before the ball mill. The concentrate was then thickened to 70 per cent. solids. Potassium cyanide to the amount of 0.3 lb. per ton and zinc sulfate in the quantity of 0.5 lb. per ton were added to the thickened pulp and the whole

Jan 1, 1929

Domestic: Middle West-,11.. B. Newcombe Eastern District-J. French Robinson1 Kansas-Henry A. Ley 2 Oklahoma-Henry A. Ley 3 Texas, except Gulf Coast and Panhandle-M. G. Cheney 5 Texas Panhandle-W. E. Hubbard and H. E. Crum 6 Gulf Coast-L. P. Teas 7 South Arkansas, North Louisiana and Mississippi-H. K. Shearer 8 Foreign Mexico-V. R. Garfias and C. 0. Isakson 9 Canada-Line M. Farish 10 Venezuela-C. W. Hamilton 10 Colombia-J. T. Duce 12 Peru-O. B. Hopkins 12 Trindad-Williaim J. Millard 13 Dutch East Indies-Fred B. Ely 13 Rumania-I. I. Gardescu . .. . 14 India-Eric J. Bradshaw 14

Jan 1, 1931

By J. E. Miller, W. E. DeVaney, L. Stroud

During a recent phase study of a natural gas, two stable equilibrium liquid phases were observed at temperatures below —200°F and pressures above 200 psi. This paper reviews the published literature on the occurrence of multiple equilibrium liquid phases and presents analytical data for the vapor and two equilibrium liquid phases of the liquefied natural gas at five experimental conditions. In addition, data for 30 conditions of two-phase equilibria are included. INTRODUCTION The low-temperature phase behavior of gases, most of which contained helium, has been investigated in the laboratories of the Helium Activity for many years. Since 1952, experimental studies of these systems have been continuous as part of the research program at Amarillo, Tex. Because of their value to private industries interested in participating in the Helium Conservation Program, several "Open File" reports containing phase equilibria data for heliurn-bearing natural gases have already been released by the Helium Activity. A paper containing information on the general phase behavior, operating criteria and extensive vapor-liquid data for two helium-containing systems was recently published.2 Additional publications presenting experimental data on the phase relationships of various gas systems are now in process and will be available in the near future. PREVIOUS EXPERIMENTAL WORK Although the formation of multiple liquids has been reported for various systems, to our knowledge this paper is the only substantiated evidence of a vapor-liquid-liquid equilibria in a naturally occurring gas. In 1940, Vink, Ames, and others13 reported the presence of two liquid phases in a hydrocarbon system consisting of mixtures of crude oils, solvents and natural gas. Eilerts and co-workers; published data on the recombined fluids from a gas-condensate well. This condensed gas, containing approximately 76 per cent methane and 24 per cent ethane-plus, exhibited two distinct liquid phases. Weinaug and Bradley 14 observed "unusual" phase behavior in a reservoir mixture. These workers postulated that the anomalous phase behavior was due to the "imminent formation of a second liquid phase". Botkin, Reamer, Sage and Lacey 1 studied two California crude oils that exhibited multiple phases. Kohn and Kuratal0 recently reported two equilibrium liquid phases in the methane-hydrogen sulfide system. Roof and Crawfordl1 and Eakin, et a16 also have reported experiments with binary systems that formed two stable equilibrium liquid phases. APPARATUS AND PROCEDURE A U. S. Bureau of Mines Phase Equilibrium Apparatus was used in conducting this study. The apparatus and procedures employed in its operation have been previously described3 and will not be repeated in detail ill this report. Briefly, the apparatus consists of a windowed cell which can be maintained within ±0.5°F for temperatures between room temperature arid -320°F. Pressure within the cell can be maintained within 0.1 per cent of gauge reading up to 800 psig. Equilibrium vapor and liquid samples are obtained in special containers4 for analysis by a mass spectrometer. Although the accuracy of the analyzer is about ±0.1 mol per cent, the reproducibility of the phase-equilibrium apparatus is considered relatively poor. Values reported from methane and nitrogen are considered accurate to ±l.0 and ±0.6 mol per cent. Data for ethane-plus in the vapor are accurate within 0.2 mol per cent; liquid-phase data for this aggregate compolnent are accurate within 1.5 mol per cent. For helium in the vapor phase, the analytical data are accurate within 0.2 mol per cent; liquid-phase analyses for this component were obtained by the charcoal adsorption method described by Frost8 and are accurate within 0.006 mol per cent. All of these references to the accuracy of reported values are conservative estimates based upon a statistical treatment of reproducibility data obtained with the apparatus.

By Per Kofstad, Hallstein Kjöllesdal

The oxidation behavior of niobium (columbium) has been studied in the temperature range 500° to 1200°C and at oxygen pressures of 760,100, 10, 1, and 0.1 mm of Hg. The work comprises kinetic studies of the oxidation as well as structural investigations of the oxidized specimens by means of X-ray diffraction, electron diffraclion, electron microscopy, and metal1ographic techniques. The oxidation reaction has a highly irregular temperature dependence and is unusually sensitive to changes in the oxygen pressure. The complex oxidation behavior is suggested to be due to formation of different Nb2O5 modifications in different temperature regions. During oxidation oxygen is also dissolved in the metal. Formation of oxide whiskers take place on the oxide surface at temperatures above approximately 800°C. VARIOUS aspects of the oxidation of niobium have been studied.l-12 The investigations show that niobium has a complex oxidation behavior, and the oxidation

Jan 1, 1962

By J. C. Van de Water

In June the supply of M3 army demolition powder being used for mudcapping was depleted and we switched to 4 by 8, 60% Special Quarry Gelatin dynamite. This size cartridge has proved convenient, as a half stick will handle the average boulder. By keeping the gelatin in the paper while cutting it in two, there is little contact with the gelatin and therefore fewer headaches among the powdermen. To further help prevent the headache nuisance the men are furnished with plastic coated gloves. Boulder breaking costs as reported last year were $0.426 using M3. This year, 8180 boulders have been broken with M3 at a cost of $0.472 each and 7479 with 60% Quarry Gelatin at a cost of $0.660 each. This rise in cost is due entirely to the greater cost of the Gelatin as the method has not changed.

Jan 4, 1950

By J. L. Wyatt

THE strain sensitivity, K, a property of metals defined as the unit change in electrical resistance per unit strain, was measured for commercial purity titanium wire to determine its usefulness as a strain gage material. A Kelvin double bridge, accurate to 0.000001 ohm, was used to make measurements from 0 to 1 pct total strain. A positive value of 0.17 for K was found. This compares with 2.15 for constantan and 3.5 for cold-worked invar, two of the more common strain gage materials. The effect of temperature also was determined. It was found that a change in temperature of 30°F caused the same resistance change as 1 pct strain. It is therefore concluded that titanium would have utility as a strain gage only if the thermal fluctuations in the specimen could be controlled to a high degree and in applications of very large total strain.

Jan 1, 1953

By Myron Read

DURING the past 25 years, mining engineers have seen the development of a multitude of specialized engineering curricula in the mineral industry field. Bachelor degrees are now !ranted in the fields of mineral dressing petroleum engineering, geological engineering, fuel technology, and many others. These fields were all, previously considered to be part of a mining enginieer's work and elementary phases of them were included in mining engineering curricula. Their emergence has left some mining engineers with the fear that nothing will he left for a purely mining engineer to teach, or that mining engineering graduates will be unable to complete in any of these fields with the more specialized students and thus will have neatly restricted employment opportunies. A secondary reaction has been that if students who began to say that the pining engineering curriculum taught everything but mining, since so many of :he subjects that had always been udedAuded in the mining engineering curriculum now were fields in their own right.

Jan 1, 1946

By Adam L. Wesner, A. C. Richardson

This paper describes the development of a continuous float-and-sink process to produce coal low enough in ash content to be suitable for production of electrodes. The cleaned coal had a combined iron and silicon content of 0.239 pct. The efficiency of recovery was 84 pct. DURING World War I1 the demand for electrode carbon was greater than could be met by the supply of petroleum coke available for this use. It was believed that coke made from an extremely low-ash coal might be a suitable substitute for petroleum coke. Requirements for electrode carbon to be used for the production of aluminum are that the silicon plus iron content shall be not more than 0.14 pct of the coke. However, during the period when petroleum coke was in short supply, it appeared that relaxations of the specifications might be allowed to permit 0.4 pct iron plus silicon in the coke. For this work, the specifications were that the coal should contain less than 1 pct of ash, and the combined iron and silicon content of the coal should not exceed 0.28 pct. Heavy-liquid separations made on a number of coals showed that if certain size fractions of some coals Were separated at low specific gravities the resulting float products would meet the required specifications. The objective of this work was to develop a continuous, commercially feasible process for producing low-ash coal. After consideration of various processes, the method chosen was a float-and-sink separation using a solution of calcium chloride as the separating medium. Eagle Seam coal was used for the experiments. The —10 +35 mesh fraction was found to be the most promising feed for producing the low-ash content coal. A batch of 30 tons of — --in. coal was screened at 10 and 35 mesh; the yield of —10 +35 mesh was 20 pct of the feed. This fraction comprised the feed for the separation tests. In spite of the fact that this portion was screened a second time at 35 mesh, the coal still contained 16 pct that was finer than 35 mesh. Three-fourths of the undersize was in the —35 +48 mesh range. A representative portion of the —10 +35 mesh fraction was subjected to batch float-and-sink separations to determine the best gravity to be used in the continuous tests to obtain a high recovery of low-ash content coal. The heavy liquid used was a mixture of carbon tetrachloride and benzene which assured complete wetting of all of the particles. As usual in batch separations, adequate time was allowed for each separation so that even the near gravity particles had ample time to separate. The separations were made at increments of 0.01 sp gr from 1.25 to 1.28 and also at 1.32 and 1.59. Each specific-gravity increment was assayed for ash content. From these data it was concluded that 1.27 sp gr was best for the continuous separation of the coal. The products from the batch separation were composited into float 1.27 and sink 1.27 sp-gr fractions; these were assayed for ash, iron, and silicon. Table I shows the results of the batch separations. The composite float 1.27 fraction contained 66.04 pct of the total weight, and had an analysis of 0.79 pct ash, 0.073 pct iron, and 0.112 pct silicon, or 0.185 pct iron and silicon combined. These data are indicative of the results possible if a perfect separation is made at 1.27 sp gr under static conditions. Inasmuch as the method under investigation is a dynamic system these results could not be obtained. It remained to be determined, however, just how close to the theoretical results the actual continuous separation would be.

Jan 1, 1953

By Adam L. Wesner, A. C. Richardson

This paper describes the development of a continuous float-and-sink process to produce coal low enough in ash content to be suitable for production of electrodes. The cleaned coal had a combined iron and silicon content of 0.239 pct. The efficiency of recovery was 84 pct. DURING World War I1 the demand for electrode carbon was greater than could be met by the supply of petroleum coke available for this use. It was believed that coke made from an extremely low-ash coal might be a suitable substitute for petroleum coke. Requirements for electrode carbon to be used for the production of aluminum are that the silicon plus iron content shall be not more than 0.14 pct of the coke. However, during the period when petroleum coke was in short supply, it appeared that relaxations of the specifications might be allowed to permit 0.4 pct iron plus silicon in the coke. For this work, the specifications were that the coal should contain less than 1 pct of ash, and the combined iron and silicon content of the coal should not exceed 0.28 pct. Heavy-liquid separations made on a number of coals showed that if certain size fractions of some coals Were separated at low specific gravities the resulting float products would meet the required specifications. The objective of this work was to develop a continuous, commercially feasible process for producing low-ash coal. After consideration of various processes, the method chosen was a float-and-sink separation using a solution of calcium chloride as the separating medium. Eagle Seam coal was used for the experiments. The —10 +35 mesh fraction was found to be the most promising feed for producing the low-ash content coal. A batch of 30 tons of — --in. coal was screened at 10 and 35 mesh; the yield of —10 +35 mesh was 20 pct of the feed. This fraction comprised the feed for the separation tests. In spite of the fact that this portion was screened a second time at 35 mesh, the coal still contained 16 pct that was finer than 35 mesh. Three-fourths of the undersize was in the —35 +48 mesh range. A representative portion of the —10 +35 mesh fraction was subjected to batch float-and-sink separations to determine the best gravity to be used in the continuous tests to obtain a high recovery of low-ash content coal. The heavy liquid used was a mixture of carbon tetrachloride and benzene which assured complete wetting of all of the particles. As usual in batch separations, adequate time was allowed for each separation so that even the near gravity particles had ample time to separate. The separations were made at increments of 0.01 sp gr from 1.25 to 1.28 and also at 1.32 and 1.59. Each specific-gravity increment was assayed for ash content. From these data it was concluded that 1.27 sp gr was best for the continuous separation of the coal. The products from the batch separation were composited into float 1.27 and sink 1.27 sp-gr fractions; these were assayed for ash, iron, and silicon. Table I shows the results of the batch separations. The composite float 1.27 fraction contained 66.04 pct of the total weight, and had an analysis of 0.79 pct ash, 0.073 pct iron, and 0.112 pct silicon, or 0.185 pct iron and silicon combined. These data are indicative of the results possible if a perfect separation is made at 1.27 sp gr under static conditions. Inasmuch as the method under investigation is a dynamic system these results could not be obtained. It remained to be determined, however, just how close to the theoretical results the actual continuous separation would be.

Jan 1, 1953

By Henry F. Hebley

In preparing this paper it has been the aim of the writer to keep the problems of both producers and consumers in mind. Until now, no attempt has been made to familiarize each group with the other's practice and limitations. This paper is an effort to acquaint the readers with some of the factors pertaining to the problem and cost of mining and preparing steam coal, and also to the economics of producing steam with such coal. In recent years all lines of endeavor have turned to intensive mechanization in order to lower the unit cost of production. The average fuel consumption in steam electric generating stations has dropped in 20 years from 4.0 lb. to 1.4 lb. per kilowatt-hour; while the modern power station can generate 1 kw-hr. on a fraction under 1 lb., or 13,000 B.t.u. coal. Also, the amount produced per man has in that same period risen from 3.8 to 8.2 tons, owing to the use of modernized equipment below ground for coal cutting, drilling, shooting, loading, hauling and hoisting. Unfortunately, the rapid speed of 5 tons per minute of operation at which the coal is loaded mechanically precludes any appreciable removal of impurities at the coal face, so that the raw coal is hoisted containing a markedly higher percentage of impurities than the hand-loaded coal, which was subjected to the scrutiny of the miner during loading. Also, during the past 20 years, certain seams of coal lying close to the surface have been made economically available by the improved design of electrically operated shovels and draglines for the removal of overburden running as high as 56 ft. This strip coal frequently contains so much ash in the raw state (Table 1) that it would have no sales value. Therefore, coal preparation must be adopted to beneficiate the raw product. Some seams in the United States have a decreasing ash content with decreasing size, owing, in all probability, to the fact that the coal is friable while the impurities are hard, causing a concentration of the low-ash material in the fine sizes. Illinois No. 6 coal being rather hard, naturally the reverse is true.

Jan 1, 1938

By Henry F. Hebley

In preparing this paper it has been the aim of the writer to keep the problems of both producers and consumers in mind. Until now, no attempt has been made to familiarize each group with the other's practice and limitations. This paper is an effort to acquaint the readers with some of the factors pertaining to the problem and cost of mining and preparing steam coal, and also to the economics of producing steam with such coal. In recent years all lines of endeavor have turned to intensive mechanization in order to lower the unit cost of production. The average fuel consumption in steam electric generating stations has dropped in 20 years from 4.0 lb. to 1.4 lb. per kilowatt-hour; while the modern power station can generate 1 kw-hr. on a fraction under 1 lb., or 13,000 B.t.u. coal. Also, the amount produced per man has in that same period risen from 3.8 to 8.2 tons, owing to the use of modernized equipment below ground for coal cutting, drilling, shooting, loading, hauling and hoisting. Unfortunately, the rapid speed of 5 tons per minute of operation at which the coal is loaded mechanically precludes any appreciable removal of impurities at the coal face, so that the raw coal is hoisted containing a markedly higher percentage of impurities than the hand-loaded coal, which was subjected to the scrutiny of the miner during loading. Also, during the past 20 years, certain seams of coal lying close to the surface have been made economically available by the improved design of electrically operated shovels and draglines for the removal of overburden running as high as 56 ft. This strip coal frequently contains so much ash in the raw state (Table 1) that it would have no sales value. Therefore, coal preparation must be adopted to beneficiate the raw product. Some seams in the United States have a decreasing ash content with decreasing size, owing, in all probability, to the fact that the coal is friable while the impurities are hard, causing a concentration of the low-ash material in the fine sizes. Illinois No. 6 coal being rather hard, naturally the reverse is true.

Jan 1, 1938

By J. C. Williams, M. J. Blackburn

Several of the decomposition processes that can occur in supersaturated phases in a Ti:11.6 wt pct Mo and a Ti:20 wt pct V alloy have been studied by transmission electron microscopy. The deformation induced "marternsitic phase" in the Ti:Mo alloy has been found to have a bcc or bct structure rather than the previously reported hexagonal structure. The morphology of&apos; the transformed region is a rather complex asserrlblage of twins, twinning occurring in one or more systems; this internal twinning has been found to occur on (112). The w phase is formed in both alloys on aging and is present in the Ti:Mo alloy after quenching. The structure of this phase has been confirmed as hexagonal in both systems, however, differences in morphology and stability are found between the two alloys. Thus in the Ti-Mo alloy the w phase has an ellipsoidal morphology with the major axis lying parallel to <111>ß or [0001]w while in the Ti-V alloy the phase forms as cubes, the cube faces lying parallel to {100}ß or {2021}w Some observations on the particle sizes, volume fraction, and composition of the w phase in the Ti-Mo alloy are listed. The mode of formation of The a phase from the (ß + w) structures is also different in the two alloys. In the Ti-Mo alloy the a phase is formed by either a cellular reaction or by the growth of isolated needles, whereas in the Ti-V alloy the a phase is nucleated at an w:ß interface and grow to consume the w phase. Some of the difjerences in behavior of the w phase are attributed to the mismatch between it and the solute enriched ß matrix in which it forms. MaNY transition elements tend to stabilize the bcc or ß-phase when added to titanium. In general two types of phase diagrams are produced, either a ß-stabilized (ß-isomorphous) system, e.g., Ti:Mo, -Ti:V, Ti:Nb, or a ß-eutectoid system, e.g., Ti:Cr, Ti:Fe, Ti:Mn. In previous papers&apos;-4 the phase transformations in the a-phase and (a + ß)-phase alloys have been described and this work has been extended to ß-stabilized systems. Specifically, transformations in the alloys Ti:20 wt pct V and Ti:11.6 wt pct Mo have been studied; in both of these alloys the ß phase is retained at room temperature when quenched from the ß-phase field. A number of phase transformations can occur in such metastable ß phases and the two alloys were chosen to include most of the transformations reported for ß-stabilized systems. We list these possible phase transformations below. Ti:11.6 Mo quenched from >780°C to retain the ß phase: a) The w phase can form on quenching.5 b) Martensite can be produced by subzero cooling or deformation. Two martensite habit planes have been reported in Ti:Mo alloys; (334)ß and (344)ß=6 c) On aging at temperatures <-550° C the w phase is formed before the a-phase.5,7 d) On aging at temperatures >550°C the a phase is formed.7 e) The martensite can be tempered. It has been reported that the a phase rather than the ß phase is precipitated during tempering.&apos; Ti:20V quenched from >660°C to retain the ß phase:9 a) At aging temperatures <260°C separation into two bcc phases occurs. b) The w-phase is produced prior to the a phase on aging at temperatures <-400°C. c) At temperatures 2400°C the a phase is formed directly. T-T-T diagrams describing the temperature and time regimes for the formation of these phases have been published7,9 for a Ti:12 pct Mo and a Ti:20 pct V alloy. We have attempted to investigate these transformations using transmission electron microscopy, however thin foils undergo a spontaneous transformation in all conditions except the equilibrium (a + ß) structure. This transformation has been reported previ0usly10,11 and we will comment on its morphology and nature in the various sections of experimental results. EXPERIMENTAL The compositions in wt pct of the two alloys investigated were: Ti:11.6 Mo, 0.100 02, 0.006 N2, 0.0015 H2 Ti:20V, 0.0574 O2, 0.0111 N2, 0.005 H2 These alloys were cold-rolled to 0.020 in. thick sheet. Specimens were heat treated in vacuum or in inert gas at temperatures >500°C and in a circulating air furnace at temperatures <500°C. Thin foils were prepared using standard techniques, described in detail previously." Dark field micrographs were obtained using high resolution technique. RESULTS Martensitic Transformation in Ti:11.6 pct Mo. Detailed study of the deformation induced martensite is not possible due to a spontaneous transformation which occurs near the edge of thin foils as shown in Fig. 1. Similar transformations have been observed in iron-" and copper-base13 alloys as well as other titanium alloys, but some observations specific to the Ti:1l.6 Mo alloy are listed below. a) The boundaries of these transformed regions are glissile and move under the influence of the electron beam during examination. b) Selected area diffraction indicates the transformed regions have the same structure as the matrix, being separated by tilt boundaries. The misori-

Jan 1, 1969

By H. Kenyon Burch

PaQe Introduction.............................................................. 708 Plant Sites................................................................ 709 Type of Construction...................................................... 710 Mine Plant............................................................... 710 Dual Arrangement.................................................... 711 Underground Haulage............................................. 711 Tipples........................................................... 712 Underground Pockets............................................. 712 Automatic Measuring and Loading Devices......................... 712 Shafts ............................................................. 716 Ore and Spillage Skips............................................ 716 Automatic Hoists................................................. 716 Man Elevator..................................................... 717 Crushing Plant....................................................... 718 Storage Bin........................................................... 720 Sampling Plant....................................................... 720 Motors and Other Equipment.......................................... 721 Compressor Equipment................................................ 721 Concentrator............................................................. 722 600-Ton Test Mill..................................................... 722 The 15,OO0-Ton Concentrator...................................... 726 Grinding Section.................................................. 726 Floor Arrangement........................................... 726 Marcy Ball Mills............................................. 729 Performance of Crushing Machines............................ 730 Flotation Section.................................................. 780 . Flow-Sheet with Callow Flotation Cells....................... 731 Flow-Sheet with the Inspiration Flotation hfachines............. 731 Flotation Air Supply.......................................... 733 Concentrates Filter Plant.......................................... 733 Drag Classifiers................................................... 733 Tailing Settling System........................................... 735 200-Ft. Dorr Thickener ...................................... 736 General Equipment and Supplies.......................................... 737 Water Supply......................................................... 737 Power Supply......................................................... 737 Transformer Stations.................................................. 738 Shops and Railroad Facilities.......................................... 739 Conclusion................................................................ 740

Jan 1, 1917