By J. T. Ryan

POISONOUS, irritating, or explosive gases are found in almost every industry, and manufacturers of gas masks are called upon to provide gas mask protection for a great variety of conditions, such as operators in horseradish factories, fumigators of homes and ocean liners, and men engaged in the manufacture of tetra-ethyl-lead, the new motor fuel. The modern type of gas mask and respirator, to provide protection against all such industrial gases, is an outgrowth of the gas mask developed during the World War to protect the soldiers against the poisonous war gases. So far, it has been possible to develop ample mask protection from all known noxious gases and fumes present in atmospheres encountered in mines, metallurgical works, and chemical and other industries, so long as there is sufficient oxygen present to support the flame of an oil lamp. The most important development of the gas mask was in providing protection against carbon monoxide- which is the noxious gas that mining men are most concerned with and, in fact, is the noxious gas that man is most frequently exposed to. This paper will be con- fined largely to the discussion of masks for underground use in metal mines. Gases that contaminate the normal air in mines can be divided into two classes: those that are given off normally by the workings, and those that are produced in mine operation.

Jan 1, 1926

By H. W. Schadler

The superplastic behavior of low carbon and manganese bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests are reported which indicate that high strain rate sensitivity (>0.5) and adequate elongations are achievable in ultrafine-grained steels 1 to 2 p, but at strain rates which are not commercially attractive. It has been demonstrated that the fine grain size is retained after long times and high strains if the temperature is kept within the range of the two-phase (a + ?) field. INTEREST in superplasticity has been stimulated by the desire to: 1) understand the origin of, and mechanisms responsible for, the large uniform elongations observed, and 2) exploit this property for commercial advantage in metal forming operations. Although the Zn-22 wt pct Al alloy presently being studied as a model material1-5 may find application in sheet forming and extrusion, the potential of super-plasticity should best be realized in large tonnage materials, such as steel and aluminum alloys. The degree of superplasticity in low-carbon and manganese-bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests on ultrafine grain size material are reported. Avery and Backofen6 and Hart7 have shown that geometrically stable flow leading to extensive uniform elongation in the tension test is associated with high values of the strain rate sensitivity, m, defined: Lozinsky had reported that titanium and zirconium experience permanent deformation if subjected to a constant load and cyclic heating through the temperature range of the phase transformation. Although strain rate sensitivities in excess of about 0.2 had not been reported previously for steel, permanent deformation had been observed11-13 in a wide variety of steels subjected to a constant load and cyclic heating through the temperature range of the a-? phase transformation. Thus by analogy, steel could be expected to exhibit high strain rate sensitivity but only in the a + ? condition. High strain rate sensitivity has been observed at 650°C (a + Fe3C), but not reported as such, by Bailey, Dickenson, and pearson14 in 1931 at a strain rate of about 10-9 per min. It then remained to determine whether high tensile elongations would be observed in a rate-controlled test at constant temperature and at what strain rate strain rate sensitivity values greater than 0.5 would be observed. Since previous experience8 had indicated the importance of fine grain size to realizing high m at reasonable strain rates, it was first necessary to produce an ultrafine grain size and then keep the grains from growing during the test. The results of this investigation show that fine grain size can be readily produced16 and maintained by restricting the temperature of testing to below the ? transus. Further, superplasticity (high m and large uniform elongation) is observed. However, the strain rate range is only marginally useful for commercial forming operations with the finest grain size produced. MATERIAL The material investigated initially was a 1.9 wt pct Mn, 0.42 wt pct C, hot-rolled bar previously used by Low and Turka1015 and available in the laboratory. The 0.500-in. round was cold-rolled to a 0.090-in. flat, annealed for 4 hr at 850°C in argon, air-cooled, and cold-finished to 0.050 in. Subsequently, four additional steels of the compositions given in Table I were investigated to explore the effects of manganese, carbon, and test temperature on the observed stress-strain rate behavior. These steels were melted under argon, cast to 0.75 by 2 by 5 in. slabs, hot-rolled at 850°C, surface-finished to 0.13 in., and cold-finished to 0.050 in. Sheet tensile specimens 0.200 in. x thickness with 1- or 2-in. gage length were cut parallel to the rolling direction. Table I also includes the nominal transformation temperatures for the AISI 1340 and the four experimental steels. EXPERIMENTAL PROCEDURE Production of Fine Grain Size. Ultrafine grain size (1 to 5 p) was considered essential for this studv. Grange16 has described two techniques for producing

Jan 1, 1969

By Oscar H. Hershey

COMPLAINT has been made that in the literature of economic geology the work of the "company or practical" mining geologists does not get enough attention. I propose to attempt to overcome this com¬plaint in reference to one important lead-mining district, that of the Coeur d'Alene in northern Idaho. Furthermore, I will assume that the reader is not so much interested in the geology of the district as in the methods of application used and incidents that have arisen in the work. All the important discoveries of ore in the Coeur d'Alene were made without benefit of geology. Certainly I would not claim the reputed discoverer of the Bunker Hill mine as a fellow geologist. It appears also that the mines were operated quite successfully for many years without geological specialists, though doubtless certain properties were visited at long intervals by such men as Waldemar Lindgren. It was known that the ores occur in quartzite, graywackes and slates as stated by J. R. Finlay in 1903. (TRANS., VOL. 33.) He described the ore as occurring in typical fissure veins that occupy fault-planes of indeterminate displacement. The Bunker Hill lode was based on a definite fissure with the mineralization all on the hanging-wall side, extending as far as 300 ft. from the fissure.

Jan 1, 1933

By T. MacDONALD

ATHOUGH flotation has been a commercial process for over twenty years, the last two years have witnessed a sudden and phenomenal increase in our knowledge of how to separate minerals heretofore not considered amenable to flotation at all. As remarked by Professor Locke in the January issue. "Either commercial or laboratory flotation is reported on zircon, ilmenite, carnotite, kyanite, scheelite, chromite, fluorite, feldspar, cassiterite, wolframite, barite, and clay. Attractive patents on soap flotation are U. S. Nos. 2,000,656 and 2,040.187. A survey by Ralston in the February E. & M. J. adds many other minerals to this impressive list. The simple but pregnant fact is that any mineral can be coated, directly or indirectly, with a water-repellent coating, and since this is true, it follows that any mineral can be floated. Fundamentally, this is no new discovery, where, for instance, is the mineral that cannot he washed from a pair of dirty hands by means of soap and water, given the absence of refractory greases or oils which would have no proper place in flotation ?

Jan 1, 1937

By J. E. Harris

The metallic elements, beryllium, calcium, cerium, lithium, manganese, titanium, vanadium and zirconium are used in metallurgical practice in relatively small percentages for the purpose of improving the physical properties of various alloys. No important uses for any of these elements have thus far been developed either in the pure form or in alloys of which they constitute the major constituent.

Jan 1, 1935

By E. T. Turkdogan, L. E. Leake

A number of measurements have been made on the vapor pressure of pure iron at 1600°C. Experiments were carried out by the transportation method in which a sample of iron is exposed in a furnace to a stream of pure argon, metered at a predetermined flow rate for a specified period of time. The vapor pressure was obtained from the weight loss of the sample. A detailed diagram of the apparatus used for the experiments is given in Fig. 1. It consisted of a horizontal molybdenum-wire-wound furnace fitted with a recrystallized alumina tube 1 1/8 in. internal diam. The boats, 1 by 3/16 by 1/8 in., were fired in argon at 1600°C to constant weight before use. After this treatment, subsequent heating of the boats to 1600°C gave little or no further change in weight, e.g. ±0.05 mg in 24 hr. The furnace and reaction tube were separately fed with argon from two independent flowmeters. These were connected to a common supply source via an argon purification furnace containing metallic titanium sponge at 700°C, and an anhydrone drying-tower. A rotary displacement-type meter was included in the gas train to provide a direct means of measuring the total volume of gas passed through the reaction tube. The material used was vacuum melted high-purity iron in the form of wire 2mm in diam. The following impurities were present in the iron: 0.008 pct C, 0.002 pct Si, 0.005 pct Mn, 0.008 pct S, 0.001 pct P, 0.01 pct Ni, 0.001 pct Cr, 0.006 pct Cu, and 0.001 pct Al. Samples consisting of three small pieces of this wire were laid end to end in a recrystallized alumina-combustion boat, and were separated by small fragments of alumina. The wire samples were then melted in argon to form spherical beads 2 to 3 mm in diam. After weighing, the boat with its contents was placed on the boat carrier and introduced into the cool end of the reaction tube. The entire furnace system was then flushed with argon for 30 min. At the end of this period, the flow of argon to both furnace and reaction tubes was adjusted to the desired level; then the boat was slid rapidly into the hot-zone of the reaction tube. After a known volume of gas had passed through the reaction tube, the boat was withdrawn quickly to the cool end of the furnace. When quite cool, the boat was removed from the fur-mace and placed in a desiccator for subsequent re-weighing. The semi-micro balance used in these experiments had a sensitivity of 0.005 mg. The above procedure was repeated at several flow rates within the range of 25 to 300 ml per min. The flow of argon in the annular space between the two tubes was at a rate of 300 ml per min in all experiments. During all the experiments the furnace temperature was maintained at 1600° ± 5°C by means of a temperature controller. The temperature of the reaction zone was measured with a Tinsley high precision disappearing filament pyrometer which was initially calibrated against a Pt-13 pct Rh/Pt thermocouple; the errors due to temperature measurements were within * 5°C. RESULTS Assuming that the iron vapor is in the monatomic state, the vapor pressure can be calculated from the weight loss of the sample and the volume of the carrier gas. The results obtained are plotted in Fig. 2 against the rate of flow of argon through the chamber containing liquid iron beads. At low flow rates, the thermal diffusion of iron gives an apparent high vapor pressure, but at high gas flow rates, the carrier gas is not saturated with the vapor, and therefore, low vapor-pressure values are obtained. This is now a well-known phenomenon. There is a distinct inflexion of the curve at about 120 to 160 ml per min rate of argon flow and the vapor pressure of iron within this

Jan 1, 1961

By Arnulf Muan, W. C. Hahn

Activities of "FeO" in "FeO"-MgO solid solutions have been determined in the temperature interval 1100" to 1300"C by equilibrating oxide samples with pure metallic iron in atmospheres of known oxygen partial pressures. The end members "FeO" and MgO form a complete solid solution series. The system shoztls a considerable positive deviation from Raoult's law. A large amount of data has been accumulated during the past 50 years on stability relations existing among various crystalline and liquid phases in oxide systems of importance in metallurgical processes. By comparison, very little is known about the thermodynamic properties within the various homogeneous phases present in the systems, particularly the crystalline phases. The present paper deals with determination of activities as a function of composition in solid solutions of wüstite ("FeO") and periclase (MgO). Such solid solutions ("Magnesiowustites") have simple sodium chloride structure and are known to be continuous between the end members at elevated temperatures (> 1000°C) and strongly reducing conditions such as prevail in contact with metallic iron. Wiistite has a defect structure in which the ratio of oxygen to iron varies and never has as low a value as 1:1 corresponding to the simplified formula FeO. Within the range of stability of this phase, the composition changes between a maximum oxygen content of approximately 25.6 wt pct (corresponding to the formula FeO.83O) and a minimum oxygen content of approximately 23.2 wt pct (corresponding to the formula Fe0-96O). The activity data to be reported in the present paper are based on using as standard state the wüstite which is in equilibrium with metallic iron at a particular temperature, i.e., "FeO" of minimum oxygen content at each temperature. For sake of simplicity, the formula FeO will be used to represent the wustite phase in the remainder of this paper. Consider the reaction 2 FeO solid solution = 2 Femeta1 + Ozgas in which FeO dissolved in another oxide dissociates to metal and gas. The activity of FeO in the solid solution, relative to "pure FeO" in equilibrium with metallic iron as a standard state, is then expressed as Here Po, and po2 * are the partial pressures of oxygen of the gas phase in equilibrium with metallic iron and the oxide solid solution or "pure FeO", respectively. The equation holds only if the metal phase is essentially pure Fe. The oxide combinations used in the present investigation fulfill this requirement. Magnesia is so much more stable than FeO that for all practical purposes aFe = 1 in the metal phase present in all mixtures used in this investigation. I. EXPERIMENTAL METHOD 1. General Procedure. The experimental method used was analogous to that developed by Foster and Welch1 and used recently by Hahn and Muan.2 It consisted of four steps: a) Determination of the equilibrium between FeO and Fe. b) Determination of d-spacing change with composition in oxide solid solutions (FeO-WO). c) Equilibration of various members of the solid solution series with a metal phase and a gas phase of known oxygen partial pressure. d) Determination of compositions of solid solutions resulting from step (c) by means of data obtained in step (b). 2. Starting Materials. General Aniline and Film Corp. carbonyl iron powder, type HP, was used as the source of metallic iron. A representative analysis was as follows: Fe, 99.6 pct; C, 0.01 to 0.04 pct; 0, 0.1 to 0.3 pct; N, 0.00 to 0.05 pct. Other elements were present as traces only. Wiistite was prepared from "Baker Analyzed" Reagent grade Fe2O3 of reported analysis as follows: Assay (Fe2O3), 98.8 pct; insoluble in HC1, 0.02 pct; not precipitated by NH,OH, 0.02 pct; Zn, 0.003 pct. Production of wüstite was achieved by a two-step

Jan 1, 1962

By AIME AIME

THE 1941 fall meeting of the Iron and Steel and the Institute- of Metal, Division held at the Ritz-Carlton Hotel, Philadelphia, during the first three days (Oct. 20-22) of the National Metal Congress was well attended as usual, and the seven technical sessions and the joint round table on order-disorder transformations were this year of considerably more than routine interest. Despite unseasonably warm weather, a scarcity of hotels (there were rumors, apparently well-founded, that , some of the metal man attending the Congress had to stay in tourist camp), and a multiplicity of technical and other ions of the co-operating societies that gave the Congress this year the general air of a three-ring circus the A.I.M.E. sessions attracted audiences that ragged from seventy or eighty up to 350

Jan 1, 1941

By James T. Kemp

AN historical society of particular interest to mining engineers all over the world was born in Cornwall in 1935. A hundred-year-old winding engine then finished its long labors at the Levant mine on the cliffs near Lands End, England. The engine was to be dismantled and scrapped. A few men living near-by, appreciating that this event was one of the final acts in closing a long century of extraordinary mining and engineering evolution. armed a committee to prevent the destruction of the old mine hoist and succeeded in purchasing the engine. They restored the engine house and in time arranged with the Manor of Trewellard, owners of the land, for a 99-year ground lease on a peppercorn rental.

Jan 1, 1947

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

The effects of increasing hydrogen content, introducing a notch, and changing the strain rate on properties of titanium and one of its alloys were investigated over a range of testing temperatures from —196° to 200°C. Both high purity and commercial purity A-55 titanium were used as representative a materials, while a commercial Ti-8 pct Mn alloy was used for an a-P alloy. It was found possible to analyze the data, using the ductile-to-brittle transition temperature concept. Increasing hydrogen, the presence of a notch, and increasing the testing speed raised the transition temperature for the a materials. The presence of hydrogen and notches raised the transition temperature of the a-B alloy also. However, increasing the testing speed generally decreased the transition temperature of the a-p alloy. IN previous papers, the authors have shown that hydrogen is most detrimental to the notch-bend impact toughness of a-titanium' and to the tensile ductility of a-B titanium alloys.' These general effects have been confirmed by Kessler and co-workers," and by Kotfila and Erbin." Kessler showed that the slower strain rate in notch-rupture tests was a more sensitive measure of hydrogen embrittle-ment of a-B alloys than the tensile test. In the present paper the authors cover, with tensile and notch-bend tests, the effect of testing speed, notches, and testing temperature on hydrogen em-brittlement. High purity and commercial purity titanium, examples of u materials, and a commercial a-,f3 Ti-8 pct Mn alloy were investigated. The purpose of the investigation was to correlate the factors producing embrittlement. Materials The high purity titanium for this investigation was obtained by arc-melting crystal bar from Foote Mineral Co. into 1 Ib ingots. As-cast hardnesses for these ingots ranged from 60 to 90 Brinell. The arc-melted ingots were forged to % in. diam rods at 1470°F. These rods were swaged to & in. diam at room temperature prior to machining of the specimens for hydrogenation and testing. The commercial A-55 titanium and the Ti-8 pct Mn alloy were obtained from Rem-Cru Titanium Inc., as % in. diam rod. The A-55 titanium was hot swaged to 1/4 in. diam at 1300°F prior to machining of the specimens for hydrogenation and testing. The a-p C-11OM alloy was hydrogenated prior to hot swaging to 1/4 in. roc1 at 1300°F. Hydrogenation prior to fabrication permitted testing of the a-P alloy in the equilibrated and stabilized condition. The equilibration and stabilization treatment used was an air anneal for 1 hr at 1300°F, followed by furnace cooling to 1100°F and then air cooling. Hydrogenation was done in a Sieverts apparatus described previously.' The hydrogenation treatment consisted of heating for 1/4 to 1/2 hr at 820 °C in purified hydrogen, slow cooling to 680"C, holding 1 hr for homogenization, and rapid cooling to room temperature. Intended hydrogen levels for the a-tita-nium materials were 0.05, 0.5, 1.0, 1.5, and 2.0 atomic pct—about 15 to 430 ppm. For the Ti-8 pct Mn alloy, the intended hydrogen levels were 0.05, 0.5, 1.0, 2.5, and 5.0 atomic pct—about 15 to 1100 ppm. The material for the 0.5 atomic pct level of hydrogen was vacuum annealed prior to hydrogenation to increase the accuracy of the addition. Vacuum annealing to remove hydrogen consisted of heating for 6 hr at 820°C, and resulted in a hydrogen content of about 10 to 15 ppm. When hydrogen contents were above 0.5 atomic pct—100 ppm—the hydrogen was added without prior vacuum annealing.

Jan 1, 1957

By E. C. W. Perryman

IN spite of the large amount of work which has been carried out on the recrystallization of aluminum and its alloys, there has been no complete investigation of the recrystallization characteristics of A1-Mg alloys. The most complete investigation is that reported by Bungardt and Osswald' who, working with commercial-purity materials, found that the temperature both of beginning and of complete recrystallization increased with magnesium content up to about 2 pct Mg, then decreased with a further increase in magnesium up to 5.0 pct, and thereafter increased again. Michaud and Segolz working with 99.93 pct A1 also found the temperature of beginning of recrystallization to decrease as the magnesium content increased from 2.13 pct to about 4.5 pct. Chossat3 using aluminum of 99.99 pct purity found that 0.12 pct Mg had no effect but that 0.4 pct Mg increased the recrystallization temperature by about 30°C. That no effect was found for 0.12 pct Mg does not agree with the later results reported by Demer and Beck4 who found that 0.025 pct Mg in 99.99 pct A1 increased the time for complete recrystallization and furthermore increased the activation energy for the recrystallization process. Kratz" using 99.997 pct A1 found that 0.5 pct Mg increased both the temperature of beginning and of complete recrystallization by 100°C. Chadwick and Hooper" working with commercial-purity material found that 1 pct Mg increased the temperature of complete recrystallization by about 40 °C for cold reductions in the range 17 to 72 pct. With smaller amounts of cold work produced by stretching (10 pct strain), they found no significant effect of magnesium. The latter result agrees with that obtained by Williams and Eborall' who found no effect of 2 pct Mg on the recrystallization temperature of commercial-purity aluminum strained 10 pct or less by stretching. Experimental Procedure Material Used: The chemical analyses of the materials used throughout this investigation are given in Table I. Fabrication: The alloys were cast in iron molds which had been washed thoroughly with alumina. After scalping, the ingots were annealed for 16 hr at 450°C, pressed, annealed at 450°C for 16 hr and hot rolled to 0.25 in. After hot rolling, the slabs were alternately annealed and cold rolled to 0.036 in. Cold-rolling reductions between intermediate anneals were kept at about 30 pct and a high intermediate annealing temperature of 450°C was used so as to obtain, as nearly as possible, similar starting grain sizes for the different materials. All intermediate anneals were done in a salt bath and were followed by cold-water quenching so as to retain all the magnesium in solid solution. The final cold reductions investigated were 20, 30, 40, 50, 60, and 80 pct. The initial grain sizes, that is, the grain size before the final cold reduction, were all very similar. Annealing Procedure: Specimens, 1 in. sq, were cut from the 0.036 in. sheet and annealed in a salt bath, the temperature of which was controlled to k2"C. Separate specimens were annealed for different times at 350°, 375", 400°, and in one or two cases at 415°C and after annealing were quenched in cold water. The time taken for a specimen to reach temperature was approximately 5 sec. Metal-lographic examination after annealing showed that no precipitation of Mg+413 occurred during cooling. Procedures Used for Determining Recrystallization Characteristics: All specimens were electrolyti-cally polished and etched by the method described previously1° and polishing was continued until about 0.002 in. had been removed from each side of the specimen. Using this technique, the smallest recrys-tallized grain which could be observed with cer-

Jan 1, 1956

By D. W. Levinson, L. F. Mondolfo, N. A. Gjostein

MANY investigations are reported in the literature on the age hardening of Al-Mg-Zn alloys but most of them are concerned mainly with mechanical property changes. The present investigation was started to determine the structural changes in an AlMgZn alloy. The alloy composition was chosen in the existing phase diagram" so as to lie on the quasi-binary section Al-(AlZn)Mg Actually, it was found that the diagram as published was inexact at the lower temperatures and that the phase in equilibrium with aluminum at the lower temperatures is not the ternary compound. Technique The alloy used for the investigation was prepared from high purity materials and the resulting composition as determined by chemical and spectro-graphic analysis was: Zn, 6.17 pct; Mg, 2.13 pct; CU, 0.03 pct; Si, 0.009 pct; Fe, 0.005 pct; and the remainder, aluminum. An ingot -in. thick was cast, homogenized, hot and cold-rolled to strip 0.064-in. thick for dilato-metric and powder work, and to foil 0.005-in. thick for single crystal work. Solution treatment temperature for all specimens was 475°±5°C for periods of at least 1 hr, either in air furnaces or lead baths. Aging was done in oil or Pb-Bi baths controlled to within ±3°C. The aging was investigated at the following temperatures: room (30°), 130°, ZOO0, 260°, and 300°C. For the dilatometric study, the length changes were measured continuously, at temperature, using strips of alloy 10 in. long, shaped as channels to eliminate undesirable deflection due to bending. To compensate for thermal expansion and contraction due to the variations in the temperature of the aging baths, the dilatometers were built of the same alloy as the one being tested, with the same shape and size, but with material fully annealed. Gages on which 0.0005 in. could be read and 0.0001 in. estimated were used to measure the dilation. Length changes were also measured at room temperature. Strips approximately 10 in. long were solution-treated, quenched, and measured in a supermicrome-ter in which 0.0001 in. could be read and 0.00001 in. estimated. The specimens were immediately aged for a given time, remeasured, and then the cycle was repeated, including the solution treatment. The error of measurement with this technique was somewhat larger, but the results confirmed those obtained by continuous measurements. The sheet used for the dilatometric work was checked to determine grain orientation. Both X-rays and etching methods revealed a rather coarse grain size but only a negligible amount of preferred orientation. Thus, volume changes calculated from length changes are not invalidated by preferential orientation effects. Pieces of the sheet used for the dilatometric work were also used for the metal -lographic work. Filings for the powder X-ray study were produced from a homogenized piece of sheet. These filings were magnetically purged of iron, screened to 200 mesh, sealed in a Pyrex tube containing an argon atmosphere, and solution-treated. When quenching, the glass tube was broken, so that the powder dropped directly into cold water. After drying with alcohol, the powder was sealed into capillary tubes containing an argon atmosphere and then aged for the required times. In spite of all these precautions the three strongest lines of a( Al2o) appeared in all patterns, and were used as internal standards. By the use of these standards, accurate corrections for film shrinkage were obtained. For the back reflection patterns, annealed nickel powder was mixed with the specimen to act as internal standard. A preliminary investigation was made in small (57.3 mm diam) powder cameras. From these patterns the changes which took place in the solid-

Jan 1, 1957

By W. L. Phillips

Single crystals of aluminum, brass, and copper oriented for (100) and (110) slip were extended at 25°, 400°, and 600°C in simple shear. Aluminum specimens oriented for nonoctahedral slip began to shear at a higher critical resolved shear stress than specimens oriented for octahedral slip. Parabolic stress-strain curves were obtained from zero strain. The initial rate of parabolic hardening was lower for specimens sheared on the (100) plane in a close-packed direction <110>, than for specimens sheared in a nonclose-packed direction <100>. metallographic evidence, however, showed that all slip traces could be explained in terms of (111) <100> slip. All attempts to cause nonoctahedral slip in copper and 70-30 a-brass single crystals were unsuccessful. Instead of shearing, the crystals bent, allowing {111} type planes to come into action. NONOCTAHEDRAL slip in aluminum has been reported under three different conditions: first, as the main mode of slip in tension experiments at elevated temperatures;&apos;-&apos; second, as the main mode of slip in direct shear experiments at room temperat~re; and third, as a minor mode of deformation, i.e., as cross-slip, in tension, shear, and bicrystal experiments at room and elevated temperatures."-l2 However, as far as the author knows, nonoctahedral slip has not been reported in either copper or 70-30 a-brass. The present study was undertaken to determine whether nonoctahedral slip could be obtained in aluminum, brass, or copper at room or elevated temperatures when the shear stress was approximately constant over the cross-section, a maximum at the center, or a maximum at the surface. EXPERIMENTAL PROCEDURE A detailed description of the crystal preparation and shearing apparatus has been given previo~sly. Cylindrical crystals 1/2 in. in diam and 8 in. long were grown from the melt in a temperature-gradient furnace. The aluminum contained 0.001 pct Zn, 0.001 pct S, and 0.001 pct Fe; the 70-30 brass contained 0.015 pct Pb, 0.001 pct Fe, 0.01 pct Ni, 0.02 pct Sn, and 0.005 pct Se; the copper was certified OFHC of 99.98 pct purity. All samples were electropolished prior to testing. The shear apparatus was a modified Bausch type. The strain sensitivity was 4 x lob4 Load was applied by clamping the rods attached to the shear plates in an Instron tensile machine. The rate of loading was 0.02 in. per min. In all cases a 1/8-in. gage length was used. For the tests performed at 400° and 600°C the shear plates, collars, and rods were made of stainless steel. These elevated-temperature tests were performed in an argon atmosphere. A) Aluminum at Room Temperature. Values of a and ß for the various slip planes and slip directions investigated are shown in Table I where a is the complement of the angle between the specimen axis and the slip direction, and ß is the angle between the specimen axis and the normal to the shear plane. The shear stress is a function of a (assuming ß - 0);10 when a is less than 27 deg, the shear stress on the slip plane for which the specimen is oriented has a maximum at the center of the crystal; at a = 27 deg the shear stress is constant across the slip plane; for a greater than 27 deg the shear stress is a minimum at the center. Fig. 1 shows the stress-strain curves for specimens cut from crystals 1, 2, and 5, which were sheared on the (010) plane in the [loll direction at room temperature. These three crystals have shear-stress distributions corresponding to the three dif-

Jan 1, 1962

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By R. H. Coats

MINING occupies a position of less importance than manufacturing or agriculture in Canada, but its relative contribution has increased greatly during the post- war period. Mineral production was only 5.14 per cent of the net value I of production of all kinds of commodities in 1919, but by 1936 the pro- portion had risen steadily to 12.76 per cent. Mining felt the depression, hut unlike agriculture, which is still &apos; sorely stricken, it has passed from early convalescence to complete recovery. For each of the last two years new high records were established for the industry as a whole and for the quantity of most metals produced. Mining has had a notable effect on - the growth of the power industry in Canada. Water power has been developed in the same or adjacent areas wherever mining camps have been 1 established, with few exceptions. Consumption of electrical energy by the mining industry gained 72 per cent within a decade, rising from 1604 million kw.-hr. in 1926 to 2754 in 1935. In. 1935 alone the mining industry purchased electric power

Jan 1, 1937

By W. O. Crosby

INTRODUCTION. THE crystalline belt of the Atlantic Seaboard, south of New York, attains its maximum breadth of 220 miles on the northern border of North Carolina; and in this State it is most widely characterized by the occurrence of gold in workable deposits. Half a dozen auriferous belts have been recognized by Nitze and Hanna.1 These are, in the main, coincident in position and trend with the NE.-SW. zones of metamorphic slates and schists, which, more than any other feature, give character to the geological map of North Carolina. The central gold-belts, accompanying the main zone of slates and associated igneous rocks, are much the more important and persistent, and may be regarded as continuous northward across Virginia and southward into South Carolina. Tile eastern belt, on the other band, is the shortest and, economically, one of the least important. Its extreme length does not exceed 25 miles, the narrow band of slaty rocks to which it belongs passing, both NE. and SW., beneath the coastal-plain formations. But, although limited in area and production, this belt is, perhaps, comparable with the central belts or any part of the sea-board crystallines in the variety of conditions under which the gold occurs. It lies chiefly in the NE. part of Franklin county and the NW. part of Nash county, on the watershed of Fishing creek and other tributaries of Tar river. The elevation is between 400 and 500 ft. ; and the Tertiary peneplain has here an exceptionally perfect development, the reliefs separating the slightly incised stream-courses consisting of broad, flat-topped peneplain remnants, bounded by gentle lateral slopes.

Mar 1, 1908

By T. E. Scott, R. P. Zerwekh

The charactevistics of the deformatiotz of fcc thorium were examined between 78 and 473 K. Activation energy, actiuation volume, and the temperature dependence of the flow stress were determined and conlpared uith several theories for the rate-controlling mechnnistn of the tempemture-dependent component of the flou~ stress. It was established that the Cottrell-Stokes law does not hold, even approximately, for thorium. Through consideration of the above factors and other parameters, it was concluded that the vandom solute barrier theory proposed by Friedel demonstrates the best agreement with experimental observations of the deformation of thorium below ambient temperature. THORIUM, the first metal in the actinide series of rare-earth elements, is interesting and important from two points of view. In the more practical vein, it is a potential reactor fuel. As such, it is important to know its properties. Of specific interest here are the mechanical properties of thorium. Second, no detailed information concerning the deformation characteristics of the actinide elements has been gathered to date. In view of the interesting physical and chemical properties of these metals, their mechanical behavior might reveal characteristics which could improve our understanding of the mechanisms controlling deformation of the more common metals. For example, it has been shown1 that thorium exhibits a yield point which is greatly enhanced by interstitial solute elements such as carbon. This is not a normal occurrence in fcc metals. The goal of this investigation, therefore, was to characterize the deformation of polycrystalline thorium. MATERIAL AND PROCEDURES Thorium, made by the magnesium intermediate alloy process described by Peterson et al.,2 was rolled and swaged to 0.065-in.-diam wire. The metal analysis is given in Table I. After preparation, the oxygen and nitrogen contents had risen to 308 and 60 ppm, respectively. The 0.065-in.-diam wires were cut into 2-in. lengths and annealed in a vacuum of lo-&apos; Torr at 750°C for 1 hr, producing a grain size of 2735 grains per sq mm. The ends of the 2-in. sections were masked off so that a 1-in. gage length could be electropolished. Specimens were polished at 35 v in a solution of 6 pct perchloric acid in methanol which was maintained at 0°C . The gage diameters after polishing were about 0.0625 in. The tests were run on a screw-driven tensile machine at a constant crosshead speed corresponding to a strain rate of 0.005 min-&apos;. The strain rate was changed rapidly after each 0.01-in. extension between 0.005 min-&apos; and one of three higher strain rates which were selected in order to achieve strain-rate ratios of 5, 10, and 20. Tests were run at several temperatures from 78" to 473°K; most were tested at 423", 300°, 215", and 78°K. EXPERIMENTAL RESULTS Flow Stress vs Strain and Temperature. Typical true stress-true strain curves for thorium are shown in Fig. 1 for several temperatures over the range 473" to 78°K. The curves for 78", 215", 300") and 423°K were obtained from strain-rate change tests using the lower (0.005 min-&apos;) or base strain-rate values of stress. Additional tests, using the same base strain rate at different strain-rate ratios, gave curves which virtually superposed on those shown, indicating that strain-rate changes did not materially influence the work-hardening characteristics at the base strain rate. The curves for 273") 373") and 473°K were standard tensile tests at 0.005 min-&apos;. The behavior of the flow stress with temperature is

Jan 1, 1968

By William J. Robinson

What is the cumulative rate of recovery of copper from a sulfide leach dump? The technical answers to this frequently asked question may vary from "I don&apos;t know" to "quite good" from people of the same company. Management also poses this question because it plays a vital role in planning future production. The answer is difficult because of the many variables between different operations such as physical construction of the dump, topography of the original site, characteristics of dump material, mineralization, and water application. Each of these factors and others have a bearing on the rate of recovery. Anaconda&apos;s method of water distribution at Butte is unique in that each dump is drilled to allow physical injection of water into the dump. The injection holes are drilled vertically on 25-ft centers from the surface of the dump [(Figs. 1 and 2)]. Normally, the holes are drilled 40 ft deep and cased with 4-in. PVC perforated pipe. The pipe is perforated at 1-ft intervals with four 1 -in.-diam holes at 90° spacing on the pipe circumference. Formerly, shallow holes (20-40 ft) were alternated with deep holes (80-180 ft) in an effort to cover the entire dump and hasten oxidation. The shallow hole depth varied according to the compaction thickness. The deep hole depth varied according to the height of the dump and the original ground profile. It is preferable to have the deep holes end 20-30 ft above the original ground level. This generally allows penetration of the coarse material at the bottom of the dump. Deep holes had to be discontinued in order to cover more

Jan 1, 1974

By John W. Weeton, Max Quatinetz, Robert J. Schafer

Nickel powders of 1-, 0.4-, and 0.2- average particle size were combined with 0.05- p MgO powder. Oxide was added in quantities of 4, 12, and 20 vol pct. The mixtures were vacuum hot pressed and extruded at 2100°F. In spite of a general tendency to growth of oxide particles during processing, dispersions of fineness comparable to those of Sintered Aluminum Powder, SAP, were achieved. A small amount of oxide considerably improved 1800°F stress-rupture strength, but further oxide addition resulted in a decrease of strength. RECENTLY there has been much speculation concerning the requisites for strong and stable dispersion-strengthened alloys. The nature of the dispersed phase, the stability of the alloys, and variables influencing the mechanical properties of alloys have been given consideration. Such topics have been reviewed by Bunshah and Goetzel. Of the many parameters related to the mechanical properties of dispersion alloys, mean free path between dispersed particles (a measure of the fineness of the dispersion), particle size, and vol pct of the dispersed phase have been shown to be very important. Generally, strength increases with decreasing mean free path, and there is an optimum vol pct of dispersed phase. Just how fine a dispersion ought to be is somewhat open to debate, but Irmann, Lenel, Backensto, and Rose, Gregory and Grant,4 and others have shown in the original SAP-type alloys, aluminum plus aluminum oxide alloys, that better strength is generally obtained with finer dispersions and the best strengths were obtained when the mean free path was less than . Further, Cremens, and rant&apos; showed that in nickel plus aluminum oxide alloys, stress-rupture strength at 1500°F was definitely increasing with decreasing mean free path. In their investigation, however, the finest dispersions that were produced were about 2.0 mean free path. To determine the potential of the nickel plus oxide type of product, it would be neces- sary to obtain dispersions analogous to those of SAP alloys; namely, ones where the mean free path between oxides is less than . Unfortunately, however, it is very difficult to produce extremely fine dispersions of oxides in metals other than those which naturally form refractory oxide skins. There are several approaches to this problem including such procedures as mechanical mixing, internal oxidation, reduction of mixed oxides, and metal deposition from solution. Work at the Lewis Research Center has shown that metal powders 0.1p or finer could be produced by ball milling, when selected grinding aids were utilized.&apos; Because these unusually fine powders were available, it was an initial objective of this study to determine if by mixing of these fine Ni powders with various amounts of MgO (0.05) a fine dispersion of MgO in Ni comparable to those in Al-Al203 might be achieved. A second objective was then to attempt to relate the parameters of structure to 1800°F stress-rupture strength of the alloys. Nickel powders of 1-, 0.4-, and 0.2-p average particle size were combined with 0.05- average particle size MgO powder. This oxide was added in quantities of 4, 12, and 20 vol pct. The mixtures were hot pressed and extruded at 2100°F.

Jan 1, 1962

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO&apos;AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor&apos; and Kay and alor&apos; determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.&apos; , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969