Search Documents

By Sherwin F. Kelly

THE principal interest in the meeting sings arranged by the Geophysical Committee this year centered around the many papers dealing with the practical applications of geophysical methods to solving geological problems in many other parts of the world. The program Wednesday morning dealt with work in South Africa, Poland, and South America. Rudolph Krahmann's first paper gave a perspective of the geophysical investigations upon mineral deposits in South Africa. A striking point in his story was the tremendous increase in magnetic work during the last two or three years. This is largely accounted for by the intensive exploration for the extension of the Witwatersrand gold mining area. The author mentioned many surveys in which other methods were used for the search for ores of copper, lead, and zinc, and in the study of water-bearing and oil-bearing structures.

Jan 1, 1935

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Charles Will Wright

ALTHOUGH the United States has long led all other countries in both the production and consumption of mineral products, the trend seems definitely toward an increasing dependence upon foreign sources of supply. This is not to take the position that we are either a have or a have-not nation. For years we shall continue to secure a large proportion of our needed minerals: from our own mines, but we must face the fact that this century has seen "a more thorough and intense development of the mineral resources of the United States and a greater depletion of its irreplaceable mineral reserves than has occurred in most other countries. An audit of our mineral production given in the attached charts discloses the extent of our deficiencies. Because of these facts, low-cost foreign sources offer a promising field for the investment of a portion of our mining capital and an opportunity to obtain for the United States a greater supply of strategic metals and minerals. How. ever, to reach this end, the industrialist investing in the foreign field must have the full co-operation and strong backing of the Federal Government and the involved Federal agencies.

Jan 1, 1947

By AIME AIME

BY COMBINING the sessions on reduction and refining of copper, lead and zinc it was possible to devote an entire day to nonferrous metallurgy. Four interesting papers were presented at the morning session and four more in the afternoon. In the discussion of papers on copper, F. R. Pyne acted as chairman, with H. M. Shepard as vice-chairman, whereas for those on lead and zinc, F. F. Colcord acted as chairman, with C. R. Hayward as vice-chairman. The paper by P. D. I. Honeyman on the smelting of raw concentrates in the reverberatory furnace was presented by Mr. Pyne and discussed by Messrs. Mazany and Hayward. The interesting paper by E. S. Bardwell, com- paring the use of various fuels in copper-refining furnaces at Great Fails, Mont., was presented by Mr. Shepard and discussed by Messrs. Boggs, Gronningsater and Hayward. That by R. G. Knickerhocker, describing the stationary basic copper converter at Messina, Transvaal, was presented by Mr. Pyne, together with a written discussion by c. R. Kuzell, of the United Verde Copper co. It was an interesting illustration of how well-known processes may sometimes be modified to fit into unusual conditions.

Jan 1, 1932

By C. M. Smith

PILOTED by Cadwallader, Evans, Jr., as chairman, the Coal Division got under way Monday morning for the first of three consecutive sessions. N. F. Patton started the ball rolling with a paper on the economics of anthracite distribution, which was ably discussed by H. J. Rose, W. S. Blauvelt, and others. Mr. Patton pointed out many incongruities in freight rates, dealers' margins, and other factors which are disturbing the distribution of anthracite, one result being that trucks are hauling at least six million tons of anthracite annually, half of which is stolen. In the discussion of the papers the desirability of greater uniformity in the production and shipment of coal from month to month was urged; with larger summer price concessions as a means toward this end. "Performance Expectancy of Domestic Underfeed Stokers for Anthracite," by Allen J. Johnson, brought this important platter down to date by showing the range in capacities and efficiencies to be expected from well-made stokers, and by detailing other of their operating characteristics. One of his most interesting points is that the efficiency of domestic stokers is practically equal to that of handfiring for good installations and operations of both

Jan 1, 1935

By R. Buehl

ALTHOUGH the main features of the transformations occurring in 18-8 have been published already,1-4 certain conclusions merit questioning and discussion. The questions may be summarized as follows: PERCENT REDUCTION BY COLD ROLLING FIG. 1.-VARIATION OF FERRITIC INDUCTION AND PERCENTAGE OF FERRITE WITH COLD REDUCTION. Composition of Alloy: C, 0.08; Mn, 0.40; Si, 0.24; P, 0.014; Cr, 18.13; Ni, 8.94. 1. If ferrite is formed by cold-working austenite, what happens to the carbon with which the ferrite and austenite are both pre-sumably supersaturated? 2. What is the nature of the alpha-ferrite formed at grain boundaries by chromium-carbide precipitation at these boundaries?

Jan 1, 1939

By F. L. Bosqui

NO metallurgical process developed in the last half century has been more widely advertised to both technologists and lay- men, or has done more to promote efficiency and economy in the extraction of the valuable portions of ores than has the flotation process. Practically everybody has heard of this strange procedure whereby the heavy portions of an ore are made to float while the light parts sink. Some- times it is called froth flotation, the mineral-bearing froth being from the first a distinguishing characteristic. Many times it is called oil flotation, because a thin film of oil was commonly applied to the particles to be floated to make them adhere to the bubbles that rise through the pulp to form the surface froth. Oil, though commonly used, is not, however, necessary for this purpose, which is one of the facts that has been learned as the process has been developed.

Jan 1, 1940

By John Treweek

FOR many years the Homestake Mining Co. has devoted serious attention to the elimination of accidents, and ground is steadily being gained in this direction. In accident prevention work it is line-plunging with perfect teamwork and not the spectacular forward pass that brings progress toward the goal. In both surface plants and under- ground workings we regard "good housekeeping" as a first requisite for safety as well as efficiency. Under this term are included all types of safety guards and protective devices as well as cleanliness and orderliness it working places. Perhaps the most important factor in safety work is to arouse and maintain employee interest. The general morale and contentment of employees is of particular importance.

Jan 1, 1938

By R. D. Russell, R. M. Farquhar

ISOTOPIC tracers have become an important aid in following the progress of chemical processes in the laboratory. It has recently been found possible to utilize a system of naturally existing isotopic tracers to obtain information about the geo- logical history of lead ores. Common lead, such as is found in lead deposits, is a mixture of four stable isotopes having atomic weights 204, 206, 207, and 208. Of these, the last three are identical with the lead isotopes produced as stable end products of the radioactive decays of uranium and thorium: the first, lead-204, is not known to be produced on the surface of the earth by any process. Since uranium and thorium occur in the surface regions of the earth in amounts comparable with lead, and since the half-lives of uranium and thorium isotopes are of the same order as the age of the earth, they produce the radiogenic lead isotopes in amounts com- parable to the amount of nonradiogenic lead present. Every significant exposure of a sample of lead to uranium and thorium will therefore lead to the permanent alteration of the lead isotope ratios in that sample.

Jan 5, 1957

By Northcutt Ely, Charles F. Wheatley

This chapter deals with the systems of laws by which governments regulate the exploration for and production of the minerals within their jurisdictions. It is a summary, restricted by necessary space limitations, of material assembled by the author for a forthcoming publication of the United States Bureau of Mines, "Summary of Mining and Petroleum Laws of the World." (Information Circular, 1959.) The present study is organized in three parts, dealing with (1) the historical background of these legal systems, (2) laws of the United States, and (3) laws of other countries of the world. The reader's attention is invited to the acknowledgments at the end of the chapter, which inadequately express the appreciation due those who have assisted in the collection of this material. Part I. Historical Development of Major Western Systems of Land Tenancy with Respect to the Ownership and Control of Minerals The use of metals in primitive societies was largely confined to the manufacture of weapons for self-preservation. The ruler's control over copper, then brass, then iron, was essential to maintenance of his own ascendancy at home and his group's position against neighbors who had access to similar metals. Ancient societies were thus characterized by the ruling group's ownership of minerals and metals. The Egyptian civilization, which emerged in the fourth millenium B.C. upon the agricultural subjugation of the lower valley of the Nile, was responsible for extensive development of the upper valley as a source of mineral wealth. The production of gold during the height of that civilization has been estimated at $30,000,000 per year, thus equaling the early placers of California and Australia. The mines of Egypt were the property of the Pharaohs and were controlled at their direction. Greek mining developed a different scheme of land tenancy which more closely resembled modem concepts. Development of mineral resources was

Jan 1, 1959

By B. W. Frazier

At a recent meeting of the North of England Institute of Min ing and Mechanical Engineers, during a discussion upon the com pression of air, attention was called to an apparent anomaly in the phenomena attending the compression. At a subsequent meeting this apparent anomaly was explained by Prof. Herschel, and all the facts observed shown to be strictly in accordance with the laws of thermodynamics. Upon reading the report of the discussion in the published transactions of the society, it occurred to me that an attempt to determine mathematically the amounts of energy (whether in the form of heat or of work) expended and absorbed in compressing air, and causing it to perform work by expansion, might prove of use to some who have not access to any treatise upon the application of the laws of thermodynamics to the compression of air, and who have not the time or the inclination to make such application for themselves. The apparent anomaly noticed was this: If air be compressed, and at the same time, by the sufficient application of a cooling medium, kept at a constant temperature, the indicator diagrams in the

By Stewart, J. B.

THE property at which this work was done consists of a large deposit of potash salts occurring in massive beds of rock salt, overlain by 600 ft. of salt-impregnated shales and marls. It is in the Province of Cataluiia, Spain, about 45 miles from the railway station of Mauresa and about a mile south of Suria. In addition to sinking the shaft, the program of construction work laid out by the European owners (not Spaniards) included a single-track narrow-gage railroad from Mauresa to the mine; one large office building and several large shop buildings, all of brick and concrete with steel truss roofs; two extensive benches for the future recovery plant; and a large village of stone dwellings for employees. The pay-roll showed approximately 1200 to 1500 men employed. After two years' operation, ending early in the autumn of 1920, the shaft had been sunk 325 ft. and still had an equal distance to go to reach the potash; all tunnels for the railroad were done and the road-bed $0 per cent completed; only a little more than the foundations were completed for all the large buildings, and the excavations of the benches were about 75 per cent done-while only a fair start had been made upon the employees' village. This was the state of affairs when the European owners decided to offer this property under a one-year option to an American syndicate, providing that they agreed to carry on the entire building program and to sink the shaft as fast as was consistent with the quality of work which they demanded, for they wished the shaft to endure at least 200 years.

Jan 1, 1926

By R. K. McGeary, B. Lustman

Orientation relationships and rates of annealing of 97 pct cold rolled zirconium have been studied by X-ray techniques, metallography, and by hardness measurements. The process of annealing occurring by the formation of domains, and their subsequent growth without recrystallization, is demonstrated. NUMEROUS investigators1-' have revealed sub-grain formation after annealing cold worked metal single crystals and have generally described the results in terms of a dislocation mechanism of polygonization.5,6 in heavily cold rolled polycrystal-line aluminum the first stages of heating cause an apparently spontaneous subdivision of regions of the deformed matrix into a great number of slightly disoriented domains followed or accompanied by rapid growth of certain domains to form a recrystallization texture.7,8 In the present investigation the isothermal rate of annealing of cold worked polycrystalline zirconium has been studied by X-ray techniques, metallography, and by hardness measurement. It will be shown that, rather than by the usual nucleation and growth mechanism,"12 the process of annealing can best be explained by the formation of domains early in the annealing treatment and the subsequent growth of these domains without recrystallization. Experimental Procedure All the experimental work was performed on an arc-melted ingot of high purity zirconium crystal bar made by Westinghouse in a production scale deBoer unit. The weight percentage of impurities in the zirconium were as follows: C, 0.04; Fe, 0.05; Hf, 0.014; W, 0.01; Ti, Ni, and Al, 0.003; Si and N, 0.002; Cr and Cu, 0.001. Metallographically the zirconium showed only a single phase. The 4 in. diarn ingot was forged at 760°C to a 1 1/2x3 in. plate and was then rolled at 760°C to 0.150 in. thickness and annealed at this temperature for 20 min to produce an equiaxed grain structure of about 0.1 mm average grain diameter. The hot rolled plate was roller-leveled, surface ground to 0.135 in., cold rolled 83 pct reduction in thickness on a two-high mill, and then to a total reduction of 97 pct on a Sendzimir mill. The 0.004 in. strip material so produced received no subsequent mechanical treatment. Specimens % in. square were sheared from the rolled strip and isothermally annealed at 104 mm Hg in an all glass vacuum system equipped with a Vycor furnace tube. The temperature data presented are the average temperatures during the runs and did not vary more than about k3"C. X-ray Diffraction Methods: When zirconium is drastically cold rolled, a high degree of preferred orientation results in which prism poles, {1010}, are perpendicular to the rolling direction. After fully annealing this material an entirely new texture develops which corresponds to a 20" or 40" rotation of the deformation texture about hexagonal axes of

Jan 1, 1954

By Y. C. Liu, G. A. Alers

The anisotropy of Young's modules has been measured in a series of Cu-Zn alloys containing from 1 to 28 wt pct Zn and cold-rolled to 97.5 pct reduction in thickness. These modulus data show a transition in texture as a function of zinc content. In alloys containing 3 pct Zn or less, the texture is essentially that of copper. A transition is clearly seen to develop in 5 and 8 pct Zn alloys, and to have been completed in a 12 pct Zn alloy. Increasing the proportion of zinc to 28 pct does not produce any further changes in texture. The ease and clarity with which this texture transition can be seen in the modulus data is in great contrast with the inccertainty in the visual detertiination of the range of texture transition from a series of pole figures. It is also shown that the rolling texture of the high zinc content alloys cannot be a one-COIIIponenl texture, characterized by the (110)(112) ideal orientations, as usually assumed. A second, quite important component must also be present. Furthermore, the present data are inconsistent with matrix orientations on which the "oriented growth" hypothesis of the Formation of recrystallization textures is based. THE rolling textures of binary fcc alloy systems have generally been considered to lie between two terminal textures. One of these terminal textures is the copper type and the other is the 70:30 brass type. Alloys of intermediate solute content exhibit a texture which is said to be a transition between the two terminal textures. On the basis of efforts to correlate rolling and recrystallization textures, two concepts have been advanced in the literature on the nature of these transition textures. One school1 suggests that the addition of alloying elements, e.g., zinc, causes a gradual rotation about one of the (111) poles from the (358)( 523) ideal orientation of the copper-type rolling texture to the terminal {1 10)( 112) ideal orientation used to describe the rolling texture of 70:30 brass. This concept is depicted in Fig. 1 with the angle of rotation corresponding approximately to the zinc content and is designated here as the "rotational concept", since the ideal orientation of the transition textures varies continuously with alloy content. The other concept,' the "mixture concept", suggests that the copper-type rolling texture is a two-component texture. {358) (523) and {110)(112). The addition of alloying elements affects only quantitatively the relative amounts of these two components—a decrease in the amount of material in the {385}(523) orientation and an increase of that in the {110)(112) orientation with increasing solute content. An experimental distinction between these two concepts is essential to a better understanding of both the mechanism of formation of rolling textures and the subsequent formation of recrystailization textures in fcc metals. Because of the lack of resolution inherent in pole figures, it has not been possible to differentiate between the two concepts on the basis of this data. Both concepts, in fact, make use of the same set of pole figures but interpret them in a manner acco-rding to the view held.'" Experimental results obtained from inverse pole figures or selected-area electron diffraction3j4 simply -yield more refined pole figures but do not eliminate the ambiguity of interpretation. Quantitative measurement of an entirely different, orientation-dependent property must thus be considered

Jan 1, 1967

By Gordon H. Geiger, J. Bruce Wagner

Electrical conductavity and therrnoelectvic nzeasuretnents on synthetic hematite slabs with 0.01 to 0.90 at. pet Ti and with 0.30 at. pet Ca were made. Additions of titanium and of calcium both increased the electronic conductivity with titanium yielding greater n-type behavior and calciurn p-type behavior. Reduction studies of hematite to magnetite in CO-CO2 atmospheres between 600° and 900°C initially exhibited linear kinetics. These linear rates were increased by additions of titanium and decreased by calcium. IN recent years many studies have been reported in the literature on the kinetics of the reduction of hematite and magnetite to iron. In addition, Hansen and Josephl and Schenck and Schultz2 have reported studies on the reduction of hematite to magnetite, the first step in total reduction to iron. In order to evaluate the results of the studies of over-all reduction in terms of the actual mechanism of the reaction and to define further the important factors in the rate- controlling mechanism of the magnetic roasting reaction, the following experiments were undertaken. Specimens of undoped hematite and hematite containing titanium or calcium in solution as doping agents were reduced to magnetite in CO-CO2 mixtures. In addition, electrical-conductivity measurements were correlated with the reduction kinetics using concepts of defect solid-state chemistry. EXPERIMENTAL Fisher certified Fe2O3 powder was used to make specimens for both the electrical and kinetic studies (see Table I for analysis). Doping with titanium and calcium was accomplished by adding TiO2 and CaO powders to the Fe2O3 powder. The powders were mixed in a Waring blender for minimum times of 1/2 hr. Satisfactory blending was achieved based on comparison of analyses of individual specimens af- ter reduction. The specimens were formed in a steel die using opposed punches with a rectangular opening 10.0 by 40.0 mm. The Fe2O3-TiO, platelets were pressed cold at 16,000 psi. They were sintered for approximately 16 hr at 1075°C in air, in accordance with information in the literature3, 4 on the time and temperature needed to obtain solution of the titanium in the hematite. The Fe2O3-CaO mixtures were first cold-pressed at 20,000 psi and sintered for 3 hr at 1225°C to insure solution of CaO. This material was then ground to -325 mesh in a 6-in. ball mill and the resulting powder was used to make platelets in the same manner as above. The sintered platelets were usually between 1/16 and 1/8 in. thick. They were ground on a carborundum wheel and polished on 2/0 paper. Typical dimensions of the kinetic-study specimens were 1.6 by 0.8 by 0.05 cm, and a typical weight was 0.3 g. Conductivity and thermoelectric specimens were approximately the same size, but were subjected to further sintering in order to ensure maximum densification. Finally, all specimens were measured to the nearest 0.0005 in. and weighed on a Mettler H-15 balance to the nearest 0.0001 g and the density calculated. The average density of the specimens used for the reduction studies was 4.87 g per cc, or 7.1 pet total porosity. The standard deviation ranged from 0.14 to 0.063 g per cc within a composition group. In the present study, the apparent surface area as measured with a micrometer was taken as the true surface area. The chemical analyses for calcium and for titanium within a group showed maximum variations of 50.04 pet from the average values used in Figs. 9 and 11. In order to suspend the specimen from the balance for the kinetic studies, a hole, 0.03 in. in

Jan 1, 1965

By C. W. Kovach, A. Moskowitz

Studies were undertaken to investigate the effects of manganese content on the machinability and other Properties of a free machining martensitic stainless steel (AISI Type 416). Machinability was found to be significantly improved in steels of high manganese content, and a direct relationship was obtained between machinability and steel Mn:S ratio. As the manganese content of the steel increases, the sulfide Phase present changes from CrS to (FeMn)Cr2S4 to (MnFeCr)S, and finally to MnS. The average sulfide inclusion hardness decreases through the same range of increasing manganese content. The mechanism for machinability improvement is discussed in terms of a soft ductile sulfide affecting deformation in the secondary shear zone. Type 416 containing relatively high manganese for improved machinability shows good general properties. The effects of increasing manganese content on mechanical properties, cold formability, and corrosion resistance are described. THE addition of sulfur is commonly used to improve the machinability of stainless steels. However, little attention has been paid in the past to the composition and characteristics of the sulfur-containing phase or phases present in these resulfurized steels. Recent information on the properties of sulfide phases, and their role in metal cutting, suggests that variations in these phases could have critical effects on machin-ability, as well as important effects on formability and other properties such as corrosion resistance. Manganese, chromium, and iron are strong sulfide forming elements present in stainless steels! of these, manganese has the greatest sulfide forming tendency and iron the least.1"1 The manganese content of resul-furized 13 pct Cr steels, often about 0.5 pct, can be insufficient or only barely sufficient to combine with the sulfur that is present; thus, the precise level of manganese can strongly influence the nature of the sulfide phase. Sulfide phases which may be present in stainless steels have been reported to include CrS, a spinel-type sulfide, chromium-rich manganese sul-fide, and manganese Sulfide.5,6 Detailed phase relationships for the Fel3Cr-Mn-S system have been reported by the present investigators,7 and a portion of this work will be referred to subsequently in this paper. Recent work by Kiessling6 and Chao et a1.8 has shown that sulfide phases can display wide variations in hardness, and may undergo considerable plastic deformation under isostatic loading.9-12 Early theories of metal cutting attributed the influence of sulfur to a lubricating effect. It is now apparent that the influence of the nonmetallic inclusions and their properties on crack initiation, deformation in the shear zones, and boundary films must also be considered in relation to the machining process. This paper presents the results of studies conducted to relate machinability to the various sulfide phases which occur in stainless steels. This work has led to the development of alloys with improved machinability, and has generated information on the effects of inclusions on metal cutting processes. Effects of sulfide inclusions and steel composition on other important metallurgical properties are also discussed. MATERIALS For drill machinability and inclusion studies, 10 lb laboratory heats were melted in an air induction furnace. These heats were made with sulfur contents be tween 0.10 and 0.50 pct and manganese contents be tween 0.05 and 3.0 pct. Residual elements were added to the heats in amounts typical for commercial steels. The typical compositional range covered by the heats is shown below: C Mn P S Si Ni Cr Mo Cu N 0.10 0.05 0.007 (M0 0.40 0.40 13.0 0.20 0.10 0.03 3.0 0750 The laboratory ingots were forged in the temperature range of 1800" to 2100°F to 3/4-in. sq bars, and all bars tempered to a hardness aim of 200 Bhn prior to testing. Because of differences in composition and tempering response, the tempered bars showed some variation in hardness (175 to 275 Bhn) as well as variations in delta ferrite content (0 to 50 pct). Composition, hardness, and delta ferrite content were considered in the analysis of the machinability data. Additional tests involving tool-life evaluation and determination of other properties were conducted on materials from commercially melted and processed 15-ton electric furnace heats. TESTS AND PROCEDURES Machinability of the laboratory heats was evaluated in a drill test. In this test, 1/4-in. diam holes, 0.4 in. deep, were drilled alternately in a test bar and in a standard bar for a total of four holes in each. This sequence was repeated three times using a freshly sharpened drill each time. The average time required to drill a hole in the test bar was compared to that for the standard bar. A drill machinability rating was assigned to the test bar relative to a rating of 100

Jan 1, 1970

By I. E. Campbell, R. I. Jaffe

Oxygen, nitrogen, and hydrogen are known to be absorbed by titanium at elevated temperatures. Ehrlichl reports that about 30 at. pct oxygen can be dissolved in solid solution by alpha-titanium. Nitrogen also has a solid solubility in alpha-titanium, but there is no information as to its extent. The solid solubility of hydrogen in titanium also is high. Kirshfeld and Sieverts2 report 50 at. pct soluble, while Hägg3 reports about 33 at. pct hydrogen to be soluble in alpha-titanium. General statements are made in the literature that oxygen, nitrogen, and hydrogen embrittle titanium, but no quantitative measurements have been made of the effect of these gases on the mechanical properties of the metal. One reason for this is the lack of a source of titanium pure enough to be considered a suitable starting material. Iodide-refined titanium, made by thermal decomposition of titanium iodide vapor on an incandescent wire,4 contains small amounts of carbon, silicon, iron, and aluminum, but is very low in oxygen, nitrogen, and hydrogen content, and, therefore, was used in this work. A further reason for the lack of quantitative information on the effect of these gases, particularly oxygen, is the difficulty of carrying out accurate analytical determinations at the low concentrations of interest in this work. For this reason, the oxygen, nitrogen, and hydrogen were added in measured amounts as gases, and diffused into the titanium, to avoid the necessity of chemical analysis. The purpose of the work reported here was to isolate and measure the effects of oxygen, nitrogen, and hydrogen on titanium of the highest purity available at the time. The concentrations studied were 0.25, 0.5, and 1 at. pct in each case. Experimental Work One-half of a 24-in. hairpin of iodide-refined titanium was available for this work. The rod was approximately 0.25-in. in diam and had a 0.003-in.tung sten core. From chemical and spectro-graphic analyses, the purity of the sample was estimated to be between 99.80 and 99.95 wt pct. The chief impurities (aside from the tungsten core) were iron (0.04 pct), silicon (0.01-0.1 pct), aluminum (0.05 pct), carbon (0.03 pct). The tungsten core constituted 0.05 pct by weight of the sample. Although some alloying undoubtedly took place between the tungsten and the titanium during the deposition reaction, the core remained substantially intact in the deposited metal. The initial average hardness of the titanium as deposited was 105 Vickers (10-kg load). The maximum hardness was 116 Vickers and the minimum 91 Vickers. The metal was somewhat harder than that currently being obtained by the iodide process, that is, 75-90 Vickers. The rod was cold swaged to ¼-in. diam and then cold rolled in diamond shaped rolls to about 0.080-in. square, using reductions of 15 pct in area per pass. The 0.080-in.-square wire was cut into 6-in. lengths for the preparation of the alloys by the gaseous absorption and diffusion method. ADDITION OF OXYGEN, NITROGEN, AND HYDROGEN TO TITANIUM A modified Sieverts' absorption apparatus, shown in Fig 1, was used in

Jan 1, 1950

By THOMAS G. FEAR

THE COAL DIVISION started its share of the annual meeting Monday morning with a study of coal classi fication. A. C. Fieldner was in the chair. The report of the tellers of the ballot for division chairman, stating that Thomas G. Fear had been elected to that office, was read by M. D. Cooper. Mr. Fear acknowledged the honor in a few words. In reviewing the history of the Coal Classification Committee the chairman pointed out that this was its third symposium, the last previous one having been held at the 1930 Annual Meeting. Throughout its work the com¬mittee has had the active cooperation of the Canadian workers who are interested in the subject which should result in a uniform scheme of classification in Canada and the United States. F. E. Lathe, of the National Research Council, Ottawa, abstracted the first two papers of the session entitled "Determination of the Alkali-Soluble Ulmins in Coal," by Edgar Stansfield and K. C. Gilbart, and "Moisture Determination for Coal Classification," by the same authors. The third paper "Condition of Water in Coals of Various Ranks"' was presented by its author, A. W. Gauger. Written discussions of these papers were presented by H. C. Porter and Gilbert H. Cady. In the oral discussion which followed, W. T. Thom, Jr., brought out the advisability of considering age as a factor in classification. Mr. Fieldner favored retaining bed moisture as a partial classification basis, stating that a review of many coal analyses revealed a remarkable consistency in this item in samples from a given mine particularly where the moisture content was not high. Mr. Porter pointed out that the structure and porosity of coal often have much to do with its moisture content and that these vary in different parts of a seam, particularly in anthracite. Mr. Gauger expressed doubt as to whether the Stansfield method gives the true moisture content of coal, which is needed for classification purposes.

Jan 1, 1932

By W. L. Doyle

SLAG weights were taken on a series of twenty-eight 6-ton bottom-pour heats. These weights varied from 573 to 1050 lb. Of these, four were chosen for study of the effect of cleaned and uncleaned foundry scrap on the variations of slag weights. Data regarding the make-up and results of the heats are given in Table I. For heat No. 3 the actual slag weight was checked, using the Mn-MnO calculation method-weight 1050 lb. [5,600 X 0.0055 = 30.80 heads and gates 6,000 X 0.004 = 27.00 plate scrap 800 X 0.0083 = 6.64 pig iron 450 X 0.0034 = 1.53 iron ore]

Jan 1, 1947