By Adrien Berton

FOR nearly a century, the Corocoro deposit has been renowned among geologists from the fact that it shares with the Lake Superior deposits of the United States the distinction of being the only important copper districts where native copper is worked commercially. The Corocoro district, named after the city of Corocoro, the capital of the Province of Pacajes (Department of La Paz, Bolivia) is situated towards the western edge of the Bolivian high plateau, at an altitude of a little over 13,000 ft. The most interesting part of the district is that immediately surrounding the city of Corocoro, at a distance, by railway, of 65 miles from La Paz and 210 miles to the Chilean port of Arica on the Pacific Coast. The climate of the region is that of the semi-desert, dry and relatively cold, with big differences of temperature between day and night. The rainy season begins in December and ends in March. The cupriferous lodes of Corocoro have not attracted as much interest as the silver mines of Potosi but they have been known for a long time. In the precolonial period the Indians were using the charquis, or natural native copper sheets, to make small brass objects, and the beautiful pale green brochantite of the outcrops as a source of green pigments. During the colonial period, the oxidized ores of the outcrops were worked for copper, which was used by the mint at Potosi for making currency. The native copper ores were neglected because the Spanish miners were at a loss how to concentrate and smelt them. About 1830, work by rudimentary processes, which were improved little by little, was begun on the native copper ores. The total production of native copper in the following hundred years amounted to 100,000 tons. This native copper, which was remarkably pure, was much appreciated on the European markets before the introduction of electrolytic copper. It was useful for making special ornamental brass or bronze and the granular concentrates of native copper, called barrilla, containing 80 to 85 per cent copper were suitable for making copper sulfate by direct oxidation and subsequent leaching with sulfuric acid.

Jan 1, 1936

By R. M. Larsen

The Rocky Mountain region is defined with some variations for different purposes or by different organizations. For oil and gas development, Wyoming, Montana, Colorado, northwestern New Mexico, and Utah are included in the order of their apparent importance. Portions of adjoining states, such as North and South Dakota, Nebraska, Arizona, Nevada, and Idaho, arc attributary to this region, but have little or no oil or gas production. Nebraska and New Mexico are considered separately (see pp. 412 and 415), and most of the discussion in this report will be confined to Colorado, Montana, and Wyoming. Utah has produced about 200,000 bbl. of oil from the San Juan and Virgin fields, which are isolated and shut in at present. The Clay Basin field in northeastern Utah produces natural gas and distillate, and the Farnham field in central Utah produces carbon dioxide gas. Other Utah areas of some interest are listed in Table I. The Cedar Creek (Baker-Glendive) field in southeastern Montana extends into North Dakota, but is listed under Montana. The other states are in the main wildcat areas, and exploration in 1944 was at a minimum. However, geological and geophysical parties are reviewing them for further testing. Oil production in Colorado, Montana and Wyoming was 459,000 bbl. more than in 1943. Increases of 713,000 bbl. in Colarado and 731,000 bbl. in Montana offset a loss of 985,000 bbl. in Wyoming. This was the first decline in Wyoming since 1938. Field production figures and state totals are given in Table I. Total drilling activities in these three states and Utah increased from 687 wells making 1,442,511 ft. of hole in 1943 to 916 wells making 2,245,803 it. in 1944. Wildcat drilling increased from 163 wells making 331,193 ft. of hole in 1943 to 171 wells making 389,144 it. in 1944. These figures include all drilling wells making footage, not starts or completions, and represent an all-time high in drilling. The year 1944 witnessed the greatest concentration of seismograph activity that the region has had. The Rocky Mountain Oil Scouts Association reported that in 1943, the previous peak year, 91 crew months of work were performed; in 1944, the time was 254 crew months. About 67 per cent of the work was in Wyoming, 18 per cent in Montana, and 12 per cent in Colorado. Twenty-three blocks totaling 400,000 acres were reported assembled in Colorado, and 161 blocks totaling 4,000,000 acres in Wyoming. Information about other states was not given. Fourteen unit agreements were approved by the Department of the Interior, as compared with 13 in 1943. The 1944 agreements were all in Wyoming. In five of the unit areas, oil or gas discoveries were made, four were dry, and five were drilling Or pending' Oil companies find it advantageous to unitize blocks containing any proportion of public domain. Units for

Jan 1, 1945

By D. B. Rushmore, K. A. Pauly

Of primary importance in mine-installations is the hoist, which has a very direct bearing on the successful operation of a mine. Conditions vary greatly with different mines, and especially in different localities. Such factors as depth, incline, the number of levels, permissible or desirable speeds, conditions of ore, etc., are always more or less special in each case. Veins of ore are never exactly duplicated, and the nature of the ground through which shafts are sunk may considerably modify permissible values. As mining-laws are made by the different States, they necessarily vary somewhat, and, even when not fully observed, they introduce factors which qualify the conditions of hoisting men and ore. The amount of timbering required is often of importance as relating to hoisting-conditions. Methods of loading ore affect the time required, as also does the question of the use of cars or skips. Safety-precautions must be very carefully considered, and the number of men in each mine, the number of compartments, and often the method of removing water from the mine, must have careful consideration. While a general discussion of the subject of hoisting is possible, most cases are entirely special, and can be considered only in connection with the peculiar conditions pertaining to that particular installation. The cost of installation of the hoisting-plant may be an appreciable amount, while the cost of raising the ore may be but a small part of the total operating-charge. In many cases, however, the output of the mine is limited by the capacity or the hoist, and the latter thus becomes of the first importance.

Jan 1, 1911

By D. S. G. Hanson

The Flin Flon Mine has been in production for over fifty years, and current mining is dependent on pillar and remnant recovery. One of the last major blocks of ore, and an important economic entity to the Mine, is the North Main Shaft Pillar. A rock mechanics program was initiated through under' ground instrumentation and other subsequent analyses, to establish the degree of instability as min¬ing progressed. Several studies have been and will be undertaken to evaluate the general stability, and possibly improve the chances of stability during pillar recovery. The North Main Shaft Pillar is immediately bounded by cemented cut and fill supporting rib stopes which inturn are bounded by slag and waste filled stopes. The min¬ing method involves a modified longhole open stoping and slag fil¬ling sequence for each mining block in a general mining upwards scheme.

Jan 1, 1983

By T. D. Lynch, N. B. Pilling

The development of a proper treatment for shells in conncction with war contracts has brought to our attention the fact that the temperature of the liquid bath in which steel is quenched has a decided influence on the speed of cooling in the case of some liquids and very little in the case of others. Widely different physical results have been obtained by the use of water spray, water immersion, and oil immersion and further experiment has shown that the quenching effect of water used as a spray or an immersion varies greatly with the temperature of the water. The present experiments were undertaken with the idea of obtaining information of a quantitative nature regarding the quenching properties of a number of liquids used commercially in hardening steel. The general features of such cooling media are common knowledge and in the literature may be found records of numerous attempts to evaluate the cooling power of a liquid when used as a quenching bath. Much, if not most, of the data given on this subject is in the form of a simple statement of the time required for a certain heated mass to cool between two arbitrary temperatures when immersed in the liquid, quite regardless of the path of the temperature change. Our own purpose has been somewhat different. We have attempted to isolate that property of these liquids having to do with their ability to absorb heat rapidly, as distinct from the behavior of a considerable mass when exposed to different thermal environments. More specifically, from the data obtained through autographically recorded cooling curves of a small standard mass quenched under various conditions, we have tried to analyze the mechanism of heat absorption by the several liquids, measure the changes in its rate as a function of the temperature of the surface of transference, and ascertain the influence of the temperature of the liquid itself upon both. Without attempting an exhaustive citation of the literature, mention may be made of some of the more important contributions, notably the pioneer work of Le Chatelier,' followed by the extensive investigations

Jan 1, 1920

H. H. Bleakney (Dept. of Mines and Technical Surveys, Ottawa, Canada)— The work of Dr. Machlin and his colleagues at Columbia University is so scholarly that one hesitates to take issue with them. Nevertheless the writer feels compelled to enter a demurrer to the mechanism of intercrystalline cracking proposed in this paper. The principal obstacle to its acceptance is found in its preoccupation with purely mechanical influences and its disregard for the chemical effect of impurities. The writer believes that the destruction of metallic cohesion by concentration of impurities at the grain boundaries is a necessary and sufficient condition for the development of intercrystalline cracking; and he believes that discussion of the numerous mechanical explanations proposed should wait until some valid objection to the chemical hypothesis has been advanced. It is nearly twenty years since Gillett" drew attention to the possibility that the chemical influence of precipitation might be the cause of intercrystalline cracking. As early as 1935, Greenwood'" remarked that grain-boundary precipitation of impurities in lead appeared to promote intercrystalline cracking. Again in 1939, Scott commented as follows on a paper by Thielemann and Parker:'" "There are at least two familiar phenomena that can influence grain-boundary cohesion: 1) intergranular oxidation; and 2) grain boundary precipitation. An important consideration in this work, therefore, is to determine which, if either, of these factors is responsible for the low values of cohesive strength observed." In 1952. the writer presented evidence," some original and some abstracted, which indicated that in copper, silver, aluminum, lead and iron, intergranular cohesion was a function of the purity of the metal. In 1954 Glen, discussing a paper by Ridley and Tapsell14 indicated his belief in a precipitation mechanism for the intercrystalline embrit-tlement of molybdenum steel and suggested that with an absolutely pure metal it would be almost impossible to obtain an intercrystalline crack. This suggestion has

Jan 1, 1959

By J. J. Becker

Changes in magnetic properties with particle size are used to study the precipitation process in a Cu-Co alloy. In particular, the effect of a field during aging in producing anisotropy is shown to occur entirely during the growth of the particles, after precipitation is complete. HEAT-treatment in a magnetic field is done commercially to improve the magnetic properties of a number of materials. These can be divided into solid-solution alloys and precipitation alloys. The Permalloys are representative of the first type, and magnetic annealing greatly increases their maximum permeability. On the other hand, in precipitation alloys such Alnico 5 the important result is an increase in maximum energy product. The effect of the field in all cases is to bring about an additional magnetic anisotropy, uniaxial in nature, which makes the hysteresis loop more upright when measured in the direction in which the field was applied. The structural origin of the anisotropy brought about by magnetic annealing is not well understood. In the solid solution alloys, one possible explanation is based on ordering.' Another possibility is the orientation of like-atom pairs.' The precipitation systems known to respond to magnetic heat treatment are Alnico 2, in which the effect was first discovered," Alnico 5, cobalt ferrite (oxide),' and Cu-Co alloys.3 n these materials, the field affects the precipitation process itself in some way. Although there has been much work on Alnico 5. its nature is still incompletely understood. According to Geisler,' the precipitation reaction is of the

Jan 1, 1959

By B. J. Nelson, F. N. Rhinos

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a' continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By F. N. Rhinos, B. J. Nelson

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a' continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By B. Russell, J. R. Tuffley

The stability regions of the normal sulfate and the various basic sulfates of lead in 02-SO2 and PhS-SO2 gas atmospheres were calculated from available thermodynamic data over the temperature range 600o to 1200oC. Roasting experiments were carried out on samples of synthetic lead sulfide at various temperatures and for various roasting times. Compounds in the oxidized surface layers were identified by X-my techniques. The order in which the various reactions occurred was determined by considering the experimental results in conjunction with the thermodynamic calculations. The results of these investigations were applied to the sintering of lead sulfide concentrates, and the extent to which each of the various reactions occurred in a sinter bed was determined. PRODUCTS which may be formed during the roasting of PbS are PbS04, PbSO4. PbO, PbSO4 . 2PbO, PbSO4 . 4PbO, PbO, and Pb.1, 2 The formation of some sulfates has been studied by a number of investigators3-' whose experiments have mostly been confined to the temperature range between 500" and 850°C. Culver, Gray, and spooner3 were able to isolate the reactions which formed PbSO4 and PbSO4. PbO by carefully controlling the compositions of the roasting gases. The kinetics of these reactions were studied within the temperature range 673" to 807°C. Gardner4 and Merrick5 also studied the kinetics of oxidation of PbS. Gardner disregarded the existence of basic sulfates and, as a result, misinterpreted some of his experimental data. Merrick recognized that most of the products of oxidation were mixtures of basic sulfates, but was unable to identify the individual components. Hoschek6 oxidized PbS in air at temperatures up to 800°C. The products were analyzed after roasting had proceeded for some minutes, but no attempt was made to follow the reactions in the initial stages. Consequently, no roasting mechanism was derived. He also showed that PbSO4 and PbSO4 - 4PbO decomposed slowly in air at temperatures in the region of 800°C. The stability regions of sulfates in the temperature range 500" to 850°C have been only partially determined, while practically no information is available for higher temperatures. In the lead sintering process, PbS concentrates are roasted at temperatures within the range 1000o to 1200°C. In order to investigate sulfate formation, it is necessary to determine the effects of temperature and gas composition upon the various oxidation reactions and upon the regions of stability of the various lead sulfates. Kellogg and Basu2 introduced an equilibrium diagram similar to those in Figs. 1 to 3 which provides a convenient medium for represent-

Jan 1, 1964

By William E. Ford, Edward Salisbury Dana

The Silicates are m part strictly anhydrous, in part hydrous, as the zeolites and the amorphous clays, etc. Furthermore, a large number of the silicates yield more or less water upon ignition, and in many cases it is known that they are, therefore, to be regarded as basic (or acid) silicates. The line, however, between the strictly anhydrous and hydrous silicates cannot be sharply drawn, since with many species which yield water upon ignition the part played by the elements forming the water is as yet uncertain. Furthermore, in the cases of several groups, the strict arrangement must be deviated from, since the relation of the species is best exhibited by introducing the related hydrous species immediately after the others. This chapter closes with a section including the Titanates, Silico-titanates, Titano-niobates, etc., which connect the Silicates with the Niobates and Tantalates. Some Titanates have already been included among the Oxides.

Jan 1, 1922

By J. L. Gregg

RECENTLY there has been considerable interest in the production and use of, extra hard alloys composed primarily of tungsten and carbon. Dr. Hoyt's recent paper1 gives a good description of these alloys and describes their performance when used as tools. There are a number of these alloys on the market sold under various trade names, and it is the purpose of this paper to describe the results of an investigation of the structure of five of these alloys by means of microscopic and X-ray methods. The samples studied were in the form of small tools or wire-drawing dies, which were either purchased or supplied as samples. They were in some cases not supplied by the original makers but were furnished by the agents in this country, and we wish to call attention to the fact that they may not be truly representative of the materials supplied under the various trade names. No performance data are given and no inference as to the inferiority of one alloy as against any other is made K Schröter2 recently described methods for polishing alloys of this type for microscopic examination and has presented photomicrographs of several alloys. However, he did not identify their constituents or describe methods for their identification.

Jan 1, 1929

Elected Died 1895 ABBOTT, AI ATTHUR 1908 1882 ABBOTT, ARTHUR V 1906 1905 ABE, MASAYOSHI 1909 1903 ADAMS, CHARLES C. 1905 1906 ADAMS, JOHN C. 1913 1905 ADAMS, WILLAMS 1909 1903 ADAMS, W. EDWARDS 1910 1884 ADDY, MATTHEW 1896 1906 AFFLECK, WILLIAM A. 1911 1889 AKERS, WILLIAMS A. 1906 1905 ALABASTER, RUPPERT C. 1911 1899 ALBERGER, LOUIS R. 1911 1894 ALLEN R B 1896 1905 ALLEN, R. SCOTT 1906 1886 ALLISON, ROBERT 1916 1874 AMIOT, H. 1892 1886 AMSLER, CARL 1894 1898 ANDRSON, JOHN W 1905 1895 ÅNGSTROM, CARL 1901 1887 ARCHBALD, JAMES 1910 1900 ARLETT, GEORGE H 1906 1895 ARMSTRONG, JOHN F 1898 1905 ARNOLDS, LEO F. 1917 1882 ARNOLDS, HUGO 1886 1875 ASHBURNER, CHARLES A 1889 1872 ASIIBURNER, WILLIAM 1887 1883 ATKINS, C M , JR 1885

Jan 1, 1923

By H. N. Eavenson

Prior to 1907 nearly all coke was made in beehive ovens, and most of the gas produced was made in the old-style gas retorts, and while there were a few coke plants in southern West Virginia, southwest Virginia and Kentucky operating on high-volatile coals the proportion of the total product made by them was small and usually was used locally. The greater part of the coke made, and the coal gas produced, came from the Pittsburgh seam of western Pennsylvania and northern West Virginia, which was then regarded as the standard coking and gas coal of the country, and the best coal available anywhere for these purposes. With the advent of the byproduct oven and the building of coke plants at the furnaces, the restriction of the use of one grade of coal for making coke was removed and the use of mixtures of low-volatile and high-volatile coals began. The change in the locations of the coke plants removed the necessity of using Connellsville coal and also made sources of gas available to the public utilities other than of their own manufacture. Most of the first oven plants were built at points distant from the Connellsville region and this afforded an opportunity for the use of coals from the southern Appalachian fields, which were then at approximately equal distances from the ovens. Since that time development has been made on a number of seams of coal of great purity in southern West Virginia, southwestern Virginia and eastern Kentucky, which have been largely used for gas, cokemaking and metallurgical purposes where low amounts of ash, sulfur and phosphorus are determining factors. These coals are much lower in the objectionable elements than most of the coal shipped from the Pittsburgh seam, or than any northern coal, and when blended with low-volntile cod produce coke in byproduct ovens that is not excelled for any purpose by any coal mined in this country, and is equaled very seldom. Coal from several of these scams is shipped in great quantities without beneficlation and is lower in ash and sulfur than any but the best washed product from the Pittsburgh seam in the north. The writer has made a study of these coals to ascertain their relative qualities and the areas and reserves of coal available in each of them. No attention has been paid to the coals of Alabama, which do not compete with any of these coals, and no coal of equivalent quality is found in

Jan 1, 1934

By J. Szekely, J. W. Evans

A formulation is given for radiant heat loss from the surface of molten steel held in a ladle and numerical solutions are presented for the resultant integrodif-ferential equations. The results are shown on plots of the net rate of heat loss against time, with the geometlry, emissivities, thermal properties of the walls, and Preheat as parameters. It was found that the rate of the vadiant heat loss from the exposed metal surface was comparable to the conductive losses from the Portion of the metal in direct contact with the walls. The radiant heat loss was markedly affected by the geometry and by the thermal properties of the walls the net radiant heat loss from the steel could be drastically reduced by providing a top cover and also by the provision of preheat. The results of this work are thought to be relevant to heat loss calculatious concerned with vacuum degassing and with operatzons in which molten metals are held in ladles. WhEN molten steel is held or transferred in ladles heat losses inevitably occur. The accurate assessment of these heat losses is of importance in process design considerations, as the temperature of the metal may have to meet rigid specifications in certain stages of the processing sequence. As shown in Fig. 1, the principal mechanisms responsible for heat loss are: i) Conduction into the walls and ii) Thermal radation from the top metal surface (possibly augmented by natural convection) The conductive heat loss may be readily calculated as much information is available in the literature on both the general theory1'' and on its particular applications to ladle heat loss calculations. Evaluation of the radiant component of the heat loss is less straight-forward. In two recent papers it has been shown that the presence of a slag layer 2 to 3 in. thick would prevent any significant heat loss for periods up to an hour,5'" however, should bare metal be exposed, constituting the radiant surface, substantial heat losses could occur. This latter case is of considerable practical interest in various degassing operations and in the vacuum processing of certain specialty steels, where the top surface of the metal is not covered by a protective slag layer. Under these conditions a substantial radiant flux is emitted by the top metal surface; part of this flux leaves the system, part of it falls in the ladle walls. The radiant flux incident on the ladle walls is in part absorbed and conducted away, and in part reflected and re radiated. The purpose of the paper is to present a general formulation of the problem, the resultant solution of which should enable computation of the net radiant heat loss from the metal surface. The principal variables, the effect of which will be investigated, include initial metal temperature, geometry, thermal and radiative properties of the wall, and various modes of preheat. FORMULATION Consider a cylindrical enclosure, shown in Fig. 2, with a diameter D, height H, and wall thickness W, the cover at the top of the cylinder having a wall thickness L. If the temperature of the base (representing the top surface of the metal) is kept constant, say, Tb, the problem is to calculate the net rate of heat loss from the base as a function of time, geometry, the initial temperature distribution, and the thermal properties of the system. As customary, the formulation will consist of the mathematical statement of the conservation of thermal energy within the system.

Jan 1, 1970

By E. S. Leaver

THE presence of soluble base metals in precious-metal ores usually precludes cyanidation as the best method of treatment. The laboratory experiments described in this paper show the possibility of cyanidation of gold-silver ores containing less than 0.5 per cent. of cyanide-soluble copper and the effect of zinc in the cyanide solution. PART 1.-COPPER IN CYANIDATION The proposed process of cyanidation of precious-metal ores containing copper is based on the regeneration of about 80 per cent. of the cyanide used in the dissolution of the copper. The method of regeneration involves a combination of the sulfide and the acid precipitation of the copper and silver. The resultant solution is made alkaline with lime, and the gold is precipitated with zinc dust.

Jan 1, 1929

THE decades immediately before and after the end of the nineteenth century (1890-1910) were a period of increased activity in mineral industry education. One reason for this, undoubtedly, was the rapid increase in mineral production in the decade 1880-1890; pig iron and copper production tripled; coal, lead, and zinc output more than doubled. Most of the other mineral substances followed the same general trend. Aluminum production began in 1886; petroleum output, which in 1888 was less than it was in 1882, almost doubled in the next three years. Gold alone showed no appreciable change until its discovery at Cripple Creek in 1891, followed by the Klondike in 1896, brought to boiling a public interest in minerals that had been simmering for some years previously. The first cyanide plant in the United States was erected at Bodie in 1892, and the first chlorination plant at Cripple Creek* the next year. Silver- lead smelting had already greatly developed, and the metallurgy of copper was almost transformed. The hearth area and smelting capacity of copper reverberatory furnaces more than quadrupled between 1878 and 1894; matte converters were first erected at Butte in 1884. Copper production of the United States in 1899 was 20 times that of 1872. While it was the increased technology used in mineral production that really made the field attractive for educated young men, undoubtedly they did not realize that, and were impressed mainly by the quantitative increase in output. Another factor was the increased general interest in engineering education; three times as many men took engineering degrees in the United States in 1890 as in 1880; 1892 showed almost a 56 per cent increase over 1890. Industry had come to recognize that technical training was worth while. The mineral industry lagged somewhat at first; the total number of mining degrees

Jan 1, 1941

By R. S. Dean

The commercial production of electrolytic manganese on a small scale commenced in 1939. The writer made a short report on the progress of production and utilization in Mining and Metallurgy for January 1941. Progress during the last two years, naturally, has been more rapid. In June 1940, Congressman (now Senator) Scrugham presented a proposal to Congress for an appropriation authorizing erection of a pilot plant for " the production of metallic manganese by electrolytic or other means." As a result of this, a pilot plant, having a capacity of a few hundred pounds per day was built at Boulder City, Nev. Subsequent appropriations permitted expansion of the plant to about a ton per day. Much has been learned in this plant about electrolytic manganese, and the product even in its small way has found war uses of considerable importance. Meanwhile, the Knoxville plant of the Electro Manganese Corporation, the sole commercial producer, was expanded to about 4 tons per day to supply needed material for the war program. Other proposals for commercial plants have not been favorably received by the War Production Board. The Bureau reported on one such proposal by the American Alloys and Chemical Corporation. Practice at BouldeR City The present practice, as carried out at Boulder City, which is being described in more detail in a current paper by the Bureau staff at Boulder City, starts with a manganese dioxide ore containing about 20 per cent manganese. Currently this ore comes from the Three Kids deposit near Las Vegas. The steps for the production of electrolytic manganese, in general, are as follows: 1. The manganese in the ore is reduced to MnO. 2. The MnO is dissolved from the ore in spent electrolyte, which contains about 38 to 47 grams per liter of free sulphuric acid, 135 grams per liter of ammonium sulphate, and 10 to 12 grams per liter of Mn as sulphate. In the leaching step the manganese is built back up to 32 to 36 grams per liter of Mn as sulphate; the pH is adjusted to neutral by means of gaseous ammonia and passed through thickeners. 3. The electrolyte is purified by adding H2S, which precipitates the heavy metals. After filtering, ferrous sulphate is added to the solution and oxidized with air and the solution is filtered and clarified on a precoat filter. 4. The purified catholyte is electrolyzed in a diaphragm cell using stainless-steel cathodes and lead-silver anodes. The current density is about 45 amp. per sq. ft. Current efficiencies of 60 to 65 per cent are regularly obtained.

Jan 1, 1944

By R. S. Dean

The commercial production of electrolytic manganese on a small scale commenced in 1939. The writer made a short report on the progress of production and utilization in Mining and Metallurgy for January 1941. Progress during the last two years, naturally, has been more rapid. In June 1940, Congressman (now Senator) Scrugham presented a proposal to Congress for an appropriation authorizing erection of a pilot plant for " the production of metallic manganese by electrolytic or other means." As a result of this, a pilot plant, having a capacity of a few hundred pounds per day was built at Boulder City, Nev. Subsequent appropriations permitted expansion of the plant to about a ton per day. Much has been learned in this plant about electrolytic manganese, and the product even in its small way has found war uses of considerable importance. Meanwhile, the Knoxville plant of the Electro Manganese Corporation, the sole commercial producer, was expanded to about 4 tons per day to supply needed material for the war program. Other proposals for commercial plants have not been favorably received by the War Production Board. The Bureau reported on one such proposal by the American Alloys and Chemical Corporation. Practice at BouldeR City The present practice, as carried out at Boulder City, which is being described in more detail in a current paper by the Bureau staff at Boulder City, starts with a manganese dioxide ore containing about 20 per cent manganese. Currently this ore comes from the Three Kids deposit near Las Vegas. The steps for the production of electrolytic manganese, in general, are as follows: 1. The manganese in the ore is reduced to MnO. 2. The MnO is dissolved from the ore in spent electrolyte, which contains about 38 to 47 grams per liter of free sulphuric acid, 135 grams per liter of ammonium sulphate, and 10 to 12 grams per liter of Mn as sulphate. In the leaching step the manganese is built back up to 32 to 36 grams per liter of Mn as sulphate; the pH is adjusted to neutral by means of gaseous ammonia and passed through thickeners. 3. The electrolyte is purified by adding H2S, which precipitates the heavy metals. After filtering, ferrous sulphate is added to the solution and oxidized with air and the solution is filtered and clarified on a precoat filter. 4. The purified catholyte is electrolyzed in a diaphragm cell using stainless-steel cathodes and lead-silver anodes. The current density is about 45 amp. per sq. ft. Current efficiencies of 60 to 65 per cent are regularly obtained.

Jan 1, 1944

By W. F. Campbell

One of the deepest coal operations today is the Springhill No. 2 mine of Cumberland Railway & Coal Co., subsidiary of Dominion Coal Co. Ltd. Mining is now conducted at a slope distance of 14,000 ft, with 4400 vertical ft of cover. The record of Springhill No. 2 can be said to contain the history of bumps in the Province of Nova Scotia. The Springhill coal field forms part of the Cumberland field of Carboniferous age. There are seven mineable fields in the area, numbered in the order they were discovered. Mining has been carried on in all but the No. 4 and 5 seams, but present operations are confined to the No. 2. Fig. 1 shows a vertical section through the seams. Opened in 1873, No. 2 mine was first worked from parallel slopes driven from the outcrop of No. 2 seam down to the 7700 level. As the mine went deeper, a two-place auxiliary slope was driven from the 6900 level to the present workings. A transfer level at the 7800 connects the main haulage with the auxiliary haulage slope. The No. 2 mine plan is shown in Figs. 2 and 3. The seam is bituminous, averaging 8.5 to 9 ft thick. There is a well defined parting 14 to 16 in. from the roof, and this roof coal is harder than the rest of the seam. Average pitch at the outcrop is 30°; at the 6500 level, 20°; at the 7900 level, 16°; and at the 13,800 level, 10°. Immediate roof and floor strata consist of beds of variable thicknesses of shales, grading to arenaceous shales to shaly sandstones to sandstones. A characteristic of the strata is the appearance and disappearance of sandstone bands, of considerable thickness, over distances of several hundred feet. MINE HISTORY Entrance to No. 2 mine is obtained by three parallel slopes, separated by 100-ft pillars except in the upper portion of the mine where the pillars are smaller. Main haulage levels were originally driven 600 ft apart for room and pillar extraction. A parallel drainage and intake airway was driven below each haulage level and a parallel return airway (counter level) above. Pillars 80 to 100 ft wide separated these two servicing entries from the center haulage level. Inclines up to 700 ft apart were driven off the levels up pitch to the upper levels, and at 40-ft centers level rooms 12 ft wide were driven off each side of the inclines, separated by crosscuts every 50 to 100 ft. The rooms were driven up to 350 ft or until they were holed into the room from the adjoining incline—a plan followed until the level reached its boundary. When the entire area between two levels had been divided into pillars, the pillars were extracted from the boundary back to the slope pillars. As depth of cover increased, mining conditions required larger pillars, and at the 3300 level, where NECESSARY PRECAUTIONS FOR MINING AT DEPTH In Room and Pillar Extraction: 1) Pillars must not be too small. 2) Pillar size must be uniform. 3) Extraction lines must be kept as straight and as uniform as possible. If they are irregular they should be brought back into line slowly. 4) Peninsulas of coal surrounded by gob must be avoided. 5) Pillars should not be disturbed after they have been formed. If it is necessary to increase the width of an opening, stripping or ribbing should be done gradually over a long distance. If increased width of openings is necessary at certain locations and can be anticipated, the openings should be widened during development. 6) Under no conditions should small pillars be left in the gob that would interfere with caving. In Long wall Operations: 1) Pillars formed during development for retreating longwalls should be uniform in size and shape. 2) Pillars should not be split after development, but if pillar splitting does become necessary it should not be carried out within the zone influenced by the working faces. 3) Width of levels should not be increased after the levels have been developed. If it does become necessary to widen a level it must be done gradually over a long distance by stripping or ribbing the coal ribs. 4) Extraction lines should remain uniform. If several walls are worked together—one behind the other—a uniform distance must be maintained between them and the wall faces must be kept as straight as possible. If the walls do get out of line, they must be brought back into line gradually to allow for a gradual change in the stress distribution over the area. 5) Stumps of coal, roof supports, etc. must not be allowed to remain in the gob to interfere with caving. 6) Midwalls should be built as rigidly as possible and properly maintained.

Jan 1, 1959