By R. G. Reddy

The oxidation kinetics of A13Ti intermetallics have been studied at the temperature range of 850°C to 100O0C in pure dry oxygen. The oxygen diffusion rates were investigated using TGA method. Parabolic rate constants were calculated. The oxidation scales were analyzed using SEM, EDS and X-ray diffraction. A continuous A120, scales with a little TiO2(rutile) were formed on the intermetallic surface. The A13Ti intermetallic exhibited excellent oxidation resistance among the Ti-Al base intermetallics.

Jan 1, 1997

By C. F. Ferron

A process has been developed to treat the copper gold ores from the Guelb Moghrein mine in Mauritania. The process consists of pressure leaching the sulphide concentrate, neutralising with the oxide ore, recovery of copper by SX/EW and of gold by cyanidation of the autoclave residue. This paper focuses on the pressure leaching step, and presents data from bench and pilot plant test programs. In particular, attention is drawn to the effects of temperature, grind size, neutralisation, retention time and solution recycle on the kinetics of copper dissolution from various flotation concentrates. Likely leach mechanisms are briefly discussed.

Jan 1, 2000

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

A novel ironmaking process is under development at the University of Utah aimed at producing iron directly from iron oxide concentrate in a flash reactor. This process will reduce hazardous emissions and save energy. The kinetics of magnetite reduction with hydrogen was previously investigated in our laboratory in the temperature range 1150 to 1400 oC at large temperature increments (~100 oC increments). Due to the significant melting that occurs above 1350 oC, the reduction kinetics was measured and analyzed in two distinct temperature ranges of 1150 to 1350 oC and 1350 to 1600 oC (~50 oC increments). Experiments were performed using magnetite concentrate particles of different sizes under various hydrogen partial pressures and residence times. Reduction degrees of more than 90 % were achieved in a few seconds at temperatures as low as 1250 ºC. Different rate expressions were needed to obtain reliable agreement with experimental data.

Jan 1, 2016

By Veneta Groudeva

A pyritic ore containing zinc, lead and copper as? the relevant primary sulfide minerals, .as well as gold and silver finely disseminated in the sulfide matrix, was? leached in percolation columns. Each column contained 30 kg of ore crushed to minus 10 mm. Firstly, zinc and copper were efficiently leached by means of chemolithothrophic bacteria? in acidic sulfate bearing medium. Zinc was leached more rapidly than copper but the final extractions of these metals were similar (about 75% in 300 days). A part of the galena was oxidized to the. insoluble lead sulfate during the leaching. The pyr:ite was, however, relatively slightly attacked. The ore was then leached by means of FeC11 - HCl solutions both in the presence and in the absence of bacteria to solubilize the lead. The chemolithotrophic bacteria grew in media containing both chloride and sulfat~ ions and maintained a high ferric to ferrous ion ratio in the percoiating solutions. The chemical leaching was, however, more efficient since ft was possible to carry it out at higher chloride ion concentrations. About 10% of the lead was leached in this way in 90 days. Finally, the ore was leached by thiourea in the presence of a gold-oxidant (oxone) to extract the gold and silver. Over 60% of the gold and over 55% of the silver were extracted from the ore in 150 days, while. the extractions of these precious metals from an untreated ore sample were lower than 25%.

Jan 1, 1991

By K. Fagerlund

In this work, the rate of dissolution, melting behaviour and phase separation of silica flux with molten slag and matte were investigated. Mutual dissolution between high-grade matte and silica was chemically determined. Silica dissolution rates ,in various iron silicate slags was determined using the rotating rod method. The reaction and separation phenomena of slightly oxidised chalcopyrite samples and cuprous sulphide-magnetite mixtures with silica sand were examined all about 1350°C. The samples were water quenched, and polished specimens were studied and analysed using a light optical microscope ,and a scanning electron microscope with energy dispersive spectrometer. The silica dissolution rate in slag was found to increase with decreasing silica content and increasing ferric iron content. The reaction rate of silica sand' with matte was found to increase with increasing oxidation degree and magnetite content of matte:

Jan 1, 1998

Roasting treatments were investigated to remove arsenic from a nickel concentrate. The main arsenic minerals and their proportions in the concentrate were niccolite (NiAs)-50%, gersdorffite (NiAsS)-40% and arsenopyrite (FeAsS)-10%. Thermal analysis showed that gersdorffite and niccolite began decomposing when heated above 640 and 830°C respectively. The maximum roasting temperature was limited by agglomeration of the concentrate above 900°C. A small vibrated bed reactor was used to investigate the effects of temperature and gas flowrate, the latter to sweep away evolved arsenic. At 900°C, 24% of the original arsenic remained in the concentrate. SEM examination of the calcine showed that the residual arsenic was associated with the calcium in the gangue minerals. Additions of sulphur (either as elemental sulphur or from pyrite) facilitated the decomposition of the arsenic-containing minerals, decreased reaction with calcium in the gangue and produced calcine containing 4-6% of the original arsenic. Treatment with chlorine during roasting was effective in reducing the arsenic content to similar levels. Generation of chlorine in the bed by sulphation of CaC12 also produced encouraging results. Arsenic, Nickel Concentrate, Roasting, Chlorine, Sulphur, Gersdorffite, Niccolite

Jan 1, 2005

By S. S. Babu, T. Hong, T. DebRoy, S. A. David

"Oxide inclusions form in welds because of deoxidation reactions in the weld pool. These inclusions control the weld microstructure development. Thermodynamic and kinetic calculation of oxidation reaction can describe inclusion characteristics such as number density, size, and composition. Experimental work has shown that fluid-flow velocity gradients in the weld pool can accelerate inclusion growth by collision and coalescence. Moreover, fluid flow in welds can transport inclusions to different temperature regions that may lead to repeated dissolution and growth of inclusions. These phenomena are being studied with the help of computational coupled heat transfer, fluid-flow, thermodynamic, and kinetic models. The results show that the inclusion formation in steel welds can be described as a function of the welding processes, process parameters, and steel composition.IntroductionThe relationship between inclusions and formation of a high-toughness phase, namely acicular ferrite in low-alloy steel welds, is well known (1-4). Past research has focused on maximizing acicular ferrite amount in welds by controlling welding processes, process variables, and welding consumable parameters. Research has shown that there is a complex interaction between inclusion characteristics, prior austenite grain size, and weld metal hardenability. In a low-alloy steel weld, the small addition of titanium lead to a change in the inclusion composition and resulted in a transition in the microstructure from bainitic to acicular ferrite [see Fig. I]. This in turn lead to the best combination of strength and toughness. This paper describes the inclusion formation in low-alloy steel welds."

Jan 1, 1999

By Bing Song, Fei Xi, Xuewei Lv, Kai Zhang

The electric arc furnace process is a common method to produce high TiO2 slag from ilmenite. The pre-reduction process was proposed in recent years in order to reduce electricity consumption. In order to enhance the pre-reduction degree, high energy ball milling was proposed to improve the specific surface area of the ilmenite prior to reduction. In this study, the carbothermic reduction behavior of milled ilmenite concentrate was investigated. It was found that the ball milling method can result in a higher reduction rate and improved metallization of iron. The metallization of iron increased with increasing the time of ball milling. The metallization of iron with milling reached 89.49% when the time of ball milling was 70 min., while the FeO content decreased with 70 min. of milling from 11.84% to 4.76%.

Jan 1, 2014

By Jianxun Song, Hongmin Zhu, Qiuyu Wang, Jungang Hou, Shuqiang Jiao, Xiaobo Zhu

This work presents the results of a study on the Ti3+/Ti2+ couple redox potentials vs. Cl–/Cl2 at the temperature range (673 to 1073 K) in fused LiCl-KCl eutectic by direct potentiometric method. Initial concentrations of TiClx in solvents did not exceed 5.0 mol%. Basic thermodynamic properties of the reactions TiCl2+1/2Cl2(g)=TiCl3 were calculated using the temperature dependencies of apparent standard potentials of the couples E* Ti3+ /Ti2+.

Jan 1, 2014

By W. B. Carter, A. T. Hunt, G. W. Book

"Combustion Chemical Vapor Deposition (CCVDSM ), an open air, flame assisted CVD process, is under development. The CCVD process produces non-line-of-sight, epitaxial deposition. Materials deposited include YBa2Cu3Ox' Y2BaCuOx, BaTiO3, Y2FesOI2, ZrO2, yttria stabilized ZrO2 (YSZ), partially (yttria) stabilized ZrO2 (PSZ), and amorphous silica. Two modifications of the CCVD process are being studied. Liquid fuel CCVD deposition, involves the combustion of an organic solvent that contains dissolved reagents carrying the desired coating cations. Gaseous fuel CCVD deposition uses a flammable gas as fuel. A non-flammable solution containing dissolved reagents is either aspirated into the flame or mixed with the fuel gas as an aerosol prior to its combustion. Substrates to be coated are held near the flames' ends.IntroductionThin films and coatings can be deposited using a wide variety of techniques including chemical vapor deposition (CVD). CVD is ""a materials synthesis process whereby constituents of the vapor phase react chemically near or on a substrate surface to form a solid product.""lIn conventional CVD processing, gases carrying coating constituents flow into a reaction vessel where deposition occurs onto a heated substrate. The deposition process is often conducted at reduced pressure. Both cold and hot wall reaction chambers are used. Heat can be provided by a resistance furnace, rf induction, or high-intensity radiation lamps. Plasma, microwave, photo, laser, RF, and electron-enhanced CVD processes have been developed. The necessity of using a reaction vessel limits the substrate size and affects coating economics. Although most CVD depositions are performed as batch processes, continuous deposition can be accomplished with the use of appropriate hardware.The chemical vapor deposition of thin, dense oxide films has been accomplished in the open atmosphere with a flame assisted process. The process is called combustion chemical vapor deposition (CCVDSM).2 Two modifications of the CCVD process have been developed. The liquid fuel CCVD process involves the combustion of an organic solvent in which reagents (containing the coating cations) are dissolved. The gaseous fuel CCVD process uses a flammable gas as fuel. In this modification, a non-flammable solution containing dissolved reagents is either aspirated into the flame or mixed with the fuel gas as an aerosol of small droplets prior to its combustion. Substrates to be coated are held near the flames' ends."

Jan 1, 1994

By Mei Song, Qingyu Deng, Xuewei Lv, Lu Liu, Chenguang Bai, Meilong Hu

"The carbochlorination of several silica materials was carried out in the temperature range from 900 °C to 1200 °C. In this study, silica oxides and gaseous chlorine with carbon as reductant were used. The optimal carbon silica mole ratio in different temperature was calculated by Factsage software and the results showed that the optimal values are 1.2, 1.4, 1.6, 1.8 at 900 °C, 1000 °C, 1100 °C, 1200 °C, respectively. According to the experiments, the chlorination ratios of several silica materials were increased with temperature increasing. In the same temperature, the chlorination ratio of diatomite is the maximum and the chlorination ratio reaches 79%% when C/SiO2 reaches 3 at 1100 °C.1, IntroductionPolycrystalline silicon is the main material to manufacture the silicon polished section, solar battery[1] and high purity silicon wafers[2], also which is the most basic function material of semi-conductor industry, electronic information industry and solar photovoltaic battery industry[3]. The conventional manufacturing process of polycrystalline silicon would be divided into three parts: the improved Siemens method, which was introduced and became the main process to produce the polysilicon products in China. Silane method and fluidized bed method. Silicon tetrachloride and chlorosilans have been employed as by-products in several fields like electronic, telecounications and metallurgy[4-6]• At present, the main applications of silicon tetrachloride include production of trichlorosilane by catalytic hydrogenation, synthesis of fumed silica and ethyl orthosilicate, production of optical fiber grade silicon tetrachloride.The conventional routes for the silicon tetrachloride production have been reported, including the direct chlorination and the chlorination process of ferrosilicon, abandon catalyst and silica[7]."

Jan 1, 2013

By C. A. Summers

The U.S. Bureau of Mines applied process mineralogy to investigate a lead and zinc deposit located near Story Creek, Colville Mining District, Alaska. Mineralization is hosted by the Kayak Shale in veins, veinlets, and breccia. Sphalerite and galena, with supergene anglesite, occur in symmetrical quartz veins and between breccia clasts. The study sample analyzed 2.11 percent Pb, 5.37 percent Zn, 0.014 percent Cu, and 1.2 oz/ton Ag. Analyses of crushed products showed that 33 percent of the sample weight, and more than 50 percent of the Pb and 65 percent of the Zn, are in the minus 850 um fraction. Liberated grains of sphalerite and galena were found in crushed products finer than 300 um. Beneficiation tests indicate the material is amenable to processing by traditional gravity and flotation techniques.

Jan 1, 1991

By M. Z. Mubarok

Effect of single addition of a lignin-based biopolymer additive, DP 2782, at various dosages as well as in combination with thiourea on cathode polarization during copper deposition was investigated by performing potentiodynamic and galvanostatic measurements using a potentiostat. The result of electrochemical measurements was compared with the behaviour of cathode deposition with glue and thiourea additives. Surface micro-appearance of the copper deposit after 1 h galvanostatic scan under current density of 330 A/m2 and various additive type and dosage was evaluated by scanning electron microscopy (SEM) examination. It was found that the addition of 2.5 mg/l biopolymer gave sufficiently polarizing effect of copper deposition. SEM examination of the cathode surface after galvanostatic scan revealed that the combination of the biopolymer with thiourea (2.5 and 3.5 mg/l) resulted in a compact deposit which is comparable with that resulted from the test with glue and thiourea.

By Dorothée Proffit

Characterization of solids containing cyanides is carried out according to recommendations and standard guidelines. Most of these procedures are based on the analysis of leachates collected either on site or after leaching in the laboratory of samples. Unfortunately, these sole results are often insufficient to identify the source of the pollution. To provide 'a more complete characterization of polluted solids, optical and electron microscopy, XRD, Mossbauer spectroscopy, and transmission infrared spectroscopy were combined to analyze leachates and raw or ground samples. This combination of techniques allows the determination of the kind of cyanoferrate complexes are present in the solid state, different from insoluble Prussian Blue, since they do not have the same extraction' behavior. The use of all these techniques to characterize solid samples combined ,to the usual analysis of solutions gives a better understanding of ' the cyanide behavior.

Jan 1, 1998

By Jinrong Zhang

Fresh cyanide solution was treated by near UV light with the assistance of photocatalysts. Cyanide was oxidized mainly to cyanate. Photochemical behavior of the anatase and rutile forms of TiO2 was compared. It is found that anatase has a much higher activity than that of rutile. Bubbling of oxygen in the reactor showed no appreciable increase in cyanide oxidation, implying that the reaction is surface controlling. A very interesting finding in this study is that a natural mineral, ilmenite, can replace chemical titanium dioxide as the photocatalyst. Ilmenite without any treatment did not catalyze the oxidation of cyanide. But, after being roasted at high temperature with oxygen, the oxidation was enhanced dramatically. The mechanisms of photooxidation of cyanide and the roasting of ilmenite are proposed.

Jan 1, 1991

By D. M. Hausen

A refractory siliceous low-grade silver ore (265 g/t Ag) from a prospect in Sonora, Mexico was investigated mineralogically and metallurgically to evaluate extraction of the silver by conventional methods. Approximately half of the silver was recoverable, occurring as coarsely crystalline acanthite (70-300 Am) that was liberated in material crushed to minus 10 mesh. The remaining silver is refractory and occurs mostly as finely locked (-2 to 0.2 Am) acanthite in cherty quartz, and as minor amounts of finely disseminated stylotypite or freibergite in fluorite. The mineralogic data have thus served to explain the 50-60% recovery of silver by flotation and cyanidation.

Jan 1, 1991

By Uday B. Pal

In the electrochemical vapor deposition (EVD) process, gaseous cation precursors are passed over one side of a porous substrate, and oxygen is passed on the other side of the substrate. The gases diffuse and react within the porous substrate, and the pores get filled with the desired solid oxide. Subsequent solid state electrochemical transport through the solid oxide in the pores continues the reaction, and the film grows over the porous substrate. The EVD process has been used to deposit lanthanum chromite interconnection films and yttria stabilized zirconia electrolyte films over porous air electrodes. The EVD growth of these solid oxide films is found to be parabolic in nature, which indicates that the solid state transport (diffusion) of ions through the film controls the growth. This solid state transport can be analyzed using Wagner's treatment of the electrochemical transport. Conductivity measurements and the information on the defect structure of the oxide can be combined with the EVD growth rate measurements to calculate the solid state transport properties (transport numbers and partial conductivities) of the rate-controlling minority species in the oxide. Using this approach, the EVD growth of other electronic, mixed conducting and ionic solid oxide films can also be analyzed.

Jan 1, 1992

By Hiroshi Maeta, Takao Kino, Hirota Osono, Kikuo Matsusaka, Azusa Shida

"Prior to refine an ultra-high purity material, it is necessary to estimate the surface cleanness of a base material. In this report, the cleaning method of a surface for refining of an ultra-high purity aluminum has been studied. Aluminum sample of 99.999% purity was p9lished mechanically and electrically and washed with various solvents. Surface composition and a depth profile near the surface were examined. Based on the experimental results, surface structure of an ultra-high purity aluminum was discussed.IntroductionRecently, studies on high purity metals have become of interest, and we have reported .various properties of an ultra- high purity aluminum1- 2)In order to purify a metal, it is necessary to clean a work area and to make vacuous as possible. So, we are studying the purification of aluminum by an ultra-high vacuum refining system and a zone refining system set up in a clean room with cleanliness class of 1000.Now, in order to avoid a mixing of impurities into the refining metal, a surface cleanness of a base metal is very important factor. The purity of the base aluminum used our work is 99.999%, but the surface state of the base aluminum is not clear. Aims in this work .are to investigate the surface state and to obtain the cleaning method of the base aluminum.Experimental procedureSamples used in this work were 99.9% (3N), 99.99%(4N) and 99.999% (SN) aluminum produced industrially and 99.9999% (6N) aluminum purified by us."

Jan 1, 2000

By S. S. B Wang

Zirconia-based ceramic materials have potential applications in high temperature furnace insulation, hot extrusion and casting dies, pressure nozzles, cutting tools, engine parts and electronic materials. High purity and superfine powders of zirconium oxide (baddelyte) were synthesized from a solution containing zirconium oxychloride and urea under hydrothermal conditions. crystallization of the metastable tetragonal zirconia using magnesium oxide or yttrium oxide as stabilizing agents was successfully achieved. The mechanism of hydrothermal reaction to produce these powders are discussed.

Jan 1, 1989

By Mikiya Tanaka

Keywords: Solvent extraction, nickel, electroless plating, accelerating effect With the increasing importance of electroless nickel plating technology in many fields such as the electronic and automobile industries, the treatment of spent baths is becoming a serious problem. Although the spent baths are currently treated by a conventional precipitation method, a method with no sludge generation is desired. Previously, we proposed the solvent extraction recovery of nickel from the spent baths by means of solvent extraction using LIX84I as the extractant. However, a problem of this method was that the extraction and stripping of nickel were not fast enough to achieve high efficiencies when the continuous extractor was used. We have overcome this difficulty by finding that the addition of an acidic organophosphorous reagent in small amount into the organic phase markedly promotes the extraction and stripping rates of the nickel. Shaking-out tests using a separatory funnel at 240 spm revealed that the time to reach the equilibria is more than 60 min with only 20 vol% LIX84I, but is reduced to 10 min and 2.5 min by adding 2 vol% DP8R, respectively, during the extraction and the stripping with sulfuric acid.

Jan 1, 2004