Search Documents

By Per Anders Eidem, Merete Tangstad, Jens Davidsen

"During excavations of submerged arc furnaces producing silicomanganese, silicon carbide (SiC) has been found. Contributing to the size of the inactive area of the furnace, the active area of the furnace where reactions occur will decrease, thus reducing the potential for pre-reduction in the furnace.This work studied the formation of SiC from the liquid-solid reaction between slag, metal, and metallurgical coke. Slags and metals with different levels of silica (S1O2) and silicon (Si) have been studied. The slag and metal has been heated together with coke, and the samples investigated by microprobe. The results show that SiC was formed on the coke particle through reactions with both slag and metal. For the metal, the carbon most likely diffused through the SiC to react with Si in the alloy. SiC formation with slag is likely to go through the reduction of Si02 to Si.IntroductionToday, Silicomanganese (SiMn) is produced in submerged arc furnaces (SAF) by reduction of S1O2 and manganese oxides, mainly with metallurgical cokes. Typically, the tapped metal has a silicon content of 17 - 20 wt.%. To achieve higher levels of Si, the metal can be refined by adding off-grade silicon metal, yielding low carbon SiMn. [1]. What is believed to be SiC that has been found during dig-outs of SiMn furnaces producing high silicon alloy. It is possible that excess amounts of SiC in the furnace cause operational problems, since SiC will occupy furnace volume. As SiC accumulates, the active volume of the furnace will decrease, increasing the flow of material and gas in the active areas of the furnace. Formation of SiC is inevitable, so it is desired to keep the formation as low as possible. To be able to control the formation of SiC, one has to understand the basic mechanisms."

Jan 1, 2012

By John Snowberger III, J. Brent Hiskey

The electrochemical dissolution of super alloys containing different amounts of rhenium was investigated. The initial part of the investigation focused on the anodic dissolution of rhenium from second-generation (3% Re) and third-generation (6% Re) nickel based alloys. Exploratory electrochemical tests were conducted to evaluate solution chemistries and to establish fundamental dissolution behavior of the alloys. These included rotating disc electrode (RDE) cyclic voltammetry, linear sweep voltammetry, and chronoamperometry tests. Electrolytes comprising sulfuric acid, hydrochloric acid, and ammonium sulfate were examined. Of these, a 0.1 M HCl solution proved to be extremely effective for electrochemical dissolution of samples of CMSX-4, CMSX-10, and SC-180 alloys. This paper discusses in detail the electrochemical behavior of these alloys.

Jan 1, 2014

By J. Smuts

The mixed-valence iron silicate ISCORITE (Fe7Si010) was identified recently in a number of ironmakingmater1als, some of which were first produced more than a century ago. Although the existence of iscorite was not reported before 1967 and published phase diagrams do not make provision for it, the morphology of the phase in all the materials that were examined suggests that it is stable under a variety of conditions. It is shown that is-corite can accommodate various foreign cations in its lattice where they can replace Fe and/or Si. The morphology of is-corite in a number of materials of different origin is shown in relation to iron oxides and silicates in optical and SEM/BSE images.

Jan 1, 1991

By Bingyi Bai, Wangjun Peng, Yanling Guo, Jieyu Zhang, Guoding Gao

The phase transformation of bayan obo ore with high concentration of iron and calcium was reduced at temperatures no more than 1000℃ were investigated in this study. The samples with insufficient carbon were treated at the temperature using a vertical furnace with a thermogravimetry (TG). The mineral phases and content were examined using Xray diffraction (XRD) and X-ray fluorescence spectroscopy (XRF) respectively. The complex phases of bayan obo ore transformed to some simple phases after treated with different content of carbon at the same temperature for 10 hours. The result of XRD、 XRF and TG showed that the reduction degree of Fe3O4 phase formation varied with the temperature and the carbon content of bayan obo ore.

Jan 1, 2015

By Lifeng Zhang, Zineb Benouahmane, Yaqiong Li

Experimental oxidation tests at high temperature (1000-1200 °C) on SiC samples have been respectively performed under wet and dry air atmosphere for different holding times. The thickness of thermally grown oxide was experimentally measured by DEKTAK Stylus Profilometry. The results showed that the oxidation rate was increased with temperature and holding time, corresponding to a passive oxidation regime which led to the formation of SiO2 layer. The sessile drop method was employed in order to measure the contact angles between Si and SiC at high temperature. Contact angle can be varied from 39.6° to 75.6° by controlling the atmosphere. The deoxidation of the oxide layer and infiltration of liquid silicon caused a decrease in the contact angle.

Jan 1, 2016

By James A. Sommers

Hydrolysis of NbC15 is used to recover oxide values for ceramic and metals production. Reaction of NbC15 with water is rapid, exothermic and vigorous, yielding a gelatinous slurry. In contrast, dissolution of NbC15 in 12 N HCl is endothermic, resulting in a clear yellow solution. Such solutions can be de-hydrochlorinated by controlled contact with air, to precipitate a tantalum¬rich solids, depleting the liquid of its tantalum content. In this way, cheap, useful Nb-Ta partial separation is achieved. The separation is based upon differential oxide-chloride stability. Nb2O5 with <200 ppm Ta/Nb has obtained from starting levels of 2000 ppm. Observations are made on the different types of hydrolysis.

Jan 1, 1992

By Tarasankar DebRoy

Professor Robertson’s recognized research on metallurgical thermodynamics and kinetics for over 40 years facilitated the emergence of rigorous quantitative understanding of many complex metallurgical processes. The author had the opportunity to work with Professor Robertson on liquid metals in the 1970s. This paper is intended to review the advances in the quantitative understanding of welding processes and weld metal attributes in recent decades. Over this period, phenomenological models have been developed to better understand and control various welding processes and the structure and properties of welded materials. Numerical models and animations of melting, solidification and the evolution of micro and macro-structural features will be presented to critically examine their impact on the practice of welding and the underlying science.

Jan 1, 2014

By J. W. Perez

In the treatment of process effluents containing metal ions, it is sometimes desired to remove all of the heave metal ions while at other time it is, desired to remove one heavy metal ion from another, selectively. Ion and precipitate flotation processes were evaluated to perform these functions using the copper-iron aqueous system as a model. Because preliminary foam fractionation experiments proved to be relatively inefficient, most of this work has focused on precipitate flotation using both hydroxide and sulfide precipitation. Test results indicate that by proper control of reagents and operating conditions, it is possible to substantially reduce the froth volume over that achieved with foam fractionation and to separate copper from iron selectively. Mechanisms for collector attachment to precipitates were studied.

Jan 1, 1992

By W. Petruk

The silver-rich cobalt-nickel arsenides ores of the Cobalt area in Ontario, Canada were mined for silver from about 1904 to 1985. The ores contained about 8 oz to 100 oz Aglt and about 1 wt% Ni and 2 wt% Co. They were processed by gravitational techniques, screening and flotation to produce separate silver and Fe-Co-Ni arsenide concentrates. The silver concentrate was smelted, and in some cases the arsenide concentrate was sold to custom smelters which recovered silver and other metals. The ores display a wide variety of textures and contain many minor and trace elements. This paper presents an evaluation of mineral characteristics that have a bearing on extractive metallurgy and smelting of this type of ore.

Jan 1, 1993

By V. V. Kutumbarao, M. T. Nimje, G. Balasubramanian

Wastes from the aluminium industry such as red mud from the alumina refinery, fly ash from the captive power plant and spent pot lining from the smelter, have been successfully converted into glass-ceramic products. The process involves addition of a small quantity of glass former along with traces of nucleating agents to aid crystallization, to a specific mixture ofred mud, fly ash and spent pot lining, followed by melting at around 1300°C and vitrification by cooling. The resultant glass is then converted into a glass- ceramic by a suitable heat treatment at around 700 - 750°C. The glass-ceramic products show excellent wear resistance, besides possessing an aesthetic appearance. The major application foreseen for such products is as decorative tiles in the building industry.

Jan 1, 2000

By Xu Zhong

The theoretical limit to smelting rate and possibly the size of a smelter is dependent on the rate of heat transfer, and the chemical kinetics of both sulfur removal and minor element volatilization. The fundamental kinetics of volatilization of minor elements such as As, Sb, Bi, and Pb from matte and white metal is being investigated. It has been shown that the molecular form of trace elements in matte depends on the chemical potential of sulfur and the propensity for the minor element to form a sulfide. The impact of the variable molecular form of the minor elements on the volatilization kinetics is unknown and is under investigation in this study. The experimental technique is reviewed and preliminary results are reported in this manuscript.

Jan 1, 1995

By Kazuya Koyama

The leaching of copper from a printed circuit board (PCB) and the electrodeposition of copper from a cuprous solution in ammoniacal alkaline solutions were examined in order to develop an energy-saving hydrometallurgical process for copper recovery from electronic scrap. In the leaching experiments, copper in the PCB was oxidized by Cu(II), and Cu(I)-ammine complex ions were formed. The copper(I)-ammine complex slightly depressed the leaching rate, while Cu(II)?ammine markedly enhanced it. During the electrodeposition experiments, the current efficiency of copper deposition was approximately 100% in the current density range of 200 to 1000 Am-2. The electrodeposition of copper from the Cu(I)-ammine complex solution favored the production of plates rather than powders.

Jan 1, 2003

By M. F. Chambers

Neodymium metal was electrowon from a molten-chloride electrolyte at 650° C using a molten-metal cathode. A 50 mol pct NdC13-50 mol pct KC1 mixture served as the electrolyte. Binary metal alloys of &apos;Mg with Zn and Mg with Cd were used as molten cathodes. Under the best conditions, current efficiencies were 90 pct with a Mg-Zn cathode and 80 pct with a Mg-Cd cathode. Vacuum distillation was performed at 1,100° C for 30 min under a vacuum of 10-3 to separate the cathode metals from the neodymium. Neodymium metal of 99.9+ pct purity was recovered from the Mg-Cd alloy cathode. Almost 2 pct zinc remained in the neodymium recovered from the Mg-Zn alloy.

Jan 1, 1989

By J. Murphy

The economics of microbial coal desulfurization are affected significantly by the proper selection of the plant site and by maintenance of variables at suitable levels. High sulfur coal particles below 200 mesh show sulfate production rates triple those with 150 mesh coal but grinding costs are greater. Slurry solids density increases from 5% to 20% reduced the rate constant by a factor of 10. Coal added to a batch reactor in the stationary phase resulted in a sudden second exponential sulfate production phase indicating feasibility of lower cost continuous operation. Successful operation in the absence of beef broth, yeast or added nutrients at non-sterile conditions enhanced projected economics. Finally, the need for adequate agitation and aeration was well established.

Jan 1, 1985

By M. A. Llavona

The study of the formation and components of copper patina and its conservation has assumed great importance. The changing environment has accelerated the processes of patinas degradation; thus, the exhaustive study of factors capable of affecting the patina formation, growth and durability has assumed great importance for the industrial activity of copper. The main components of the patina, oxides, chlorides, nitrates and sulfates, have been determined; the effect of physical, chemical and microbiological factors on patina formation, particularly the influence of acid rain, natural organic matter, particles and microorganisms have been defined. The effect of different electrolytic solutions that accelerate the formation of copper patinas has been determined, and a review of the state of knowledge of the formation and evolution of metal patinas has been made.

Jan 1, 1999

By K. S. Jeong

Since the start-up of the Onsan Smelter in 1979, LS-Nikko Copper has grown into a competitive smelter through continuous development. Several environmental improvements have been carried out, in particular, intensive investments in reducing SOx emissions, such as de-sulfurization plants, fugitive gas capturing and TMS(Tele Metering System). In addition, in recent years LS-Nikko Copper has spent more than 10 million USD every year to improve environmental conditions. In order to be a global leading smelter in every aspect especially environmentally, LS-Nikko Copper plans to inspire environment-friendly minds, co-operate with shareholders, and participate in global conventions. This paper describes the environment improvements carried out at Onsan and briefly introduces a sustainable vision for a green smelter.

Jan 1, 2006

By Morimasa Ichida

One of the key factors of stabilized blast furnace operation under the conditions of high productivity and high pulverized coal rate is to enlarge the raceway to reduce the dead man area. With a reduced dead man area, the descent area is enlarged and the central gas flow is maintained at the same time. In this study, raceway furnace experiments were conducted with tuyere velocity and coke strength changed both in hot and cold conditions to measure the coke degradation rate. Using the coke degradation rate measurements, we examined the equivalent relation between the coke strength and tuyere velocity for coke degradation in the raceway. In addition, in this paper, we discuss the increase in tuyere velocity in relation to an increase in coke strength.

Jan 1, 2006

By Kazuya Kitatani, Gen Sasaki, Naoto Ohta, Hideharu Fukunaga, Makoto Yoshida, Jin Pan, Kenya Nagahisa, Toshihiro Ishikawa

"A sintered SiC (Tyranno-SA) fiber-reinforced MAS glass matrix composite was fabricated by using a slurry infiltration method and hot-pressing. The microstructure and mechanical properties were investigated: To prepare the preform, the MAS glass slurry including a dispersing agent was infiltrated into a bundle of the fibers. The preform was then hot-pressed under the conditions of 1473 K, 30 MPa, 3.6 ksec. A unidirectionally-reinforced oxide matrix composite with 50% Vf. of the fiber and a density of 2.84 g/cm3 was obtained. As the mechanical properties at room temperature, the three-point flexural strength- and quasi-static adsorbed energy were 500 MPa arid 6,000 J/m2, respectively. Without graphite or an h-BN pre-coating on the surface of the fiber, pull-out and bridging of the fibers from the matrix was found, and this leads to a high value of the adsorbed energy. By TEM observation, nano-scale crystalline products were found between the fibers and the glass matrix. The push-out test reveals that this layer causes the appropriate debonding of the interface during the fracture process of the composite.Introduction It is known that the CFCCs (continuous-fiber-reinforced ceramic matrix composites) are characterized by their non-linear fracture behavior, which is' hardly found in monolithic ceramic materials. It is inevitable for the CFCCs to exhibit a large fracture toughness so 'that debonding of the fiber/matrix interface; pull-out and bridging of the fibers then' occurs during the fracture process. This series of fracture behavior is known as the so-called ""the mechanism of toughening of the CFCCs"". Thus, different from the MMCs in which strong interfacial bonding is necessary, the interfacial strength of the CFCCs has to be controlled. As techniques for controlling the interfacial strength, it is also known that both a CVD-graphite coating and an h-BN coating are effective to induce the mechanism of toughening[1,2]. In the case, of the Si-C-O or Si-Ti-C-O fibers/glass or crystalline oxide matrix composites, it is reported that the formation of the in-situ graphite layer, which is also effective to increase the fracture toughness of the CFCCs, is often found during the fabrication process such as hot-pressing. The lower the crystallinity of the Si-C-O fibers, the higher is the tendency to form the in-situ graphite layer as found by the chemical reaction between the fibers and the glass matrices[3-12]. On the-other hand crystallized stoichiometric 'SiC fibers are attractive for high temperature service because of the higher phase stability compared to the Si¬C-O or Si-Ti-C-O fibers. However, in the previous, studies, the mechanical properties and the interfacial chemical reaction of the crystallized SiC fibers / glass matrix Composites have still been unknown. In this study, a polycrystalline 'sintered SiC fiber-reinforced MAS glass composite was fabricated. The mechanical properties and microstructure were then investigated. The slurry infiltration technique followed by hot-pressing was used to prepare the composites. The formation of the in-situ graphite layer and the relationship between microstructure and mechanical properties at room temperature were examined by the TEM observation of the fiber/matrix interface."

Jan 1, 2000

By Daniel C. McLean

Extraction data for Cu, Zn and Fe were obtained from 4.5" and 10" columns using massive sulfide ore and natural acid mine water. The purpose was to determine if recycling of solution through the column would produce leach liquors of 4 g/l Cu and Zn at extraction rates of 1 g/l per pass at typical flow rates of 0.002 to 0.006 gpm/sq.ft. Test results exceeded expectations. Cu and Zn concentrations of 4 g/l were obtrained within 4 to 6 cycles. Concentrations greater than 6 g/l Cu and 8 g/l Zn were reached within 10 cycles. Concentrations of greater than 40 g/l of Fe and free sulfuric acid were obtained with no decrease in biological activity being observed. No reagents were used.

Jan 1, 1995

By G. Archer

ASARCO, a large and diverse producer of nonferrous metals, is involved primarily in the smelting and refining of lead and copper. Lead-antimony alloys, antimony trioxide, bismuth, cadmium oxide, selenium, tellurium, silver and gold are among products which result from processing by-products of smelting and refining. The complex mixture of concentrates at some smelters and the high impurity loads at some refineries result in various drosses, sludges, dusts and slags. In this paper, the complex interplant and intraplant transfer of by-products is addressed. These by-products result in an exchange of metals between the lead circuit and the copper circuit. Examples of the transfer of by-products and the prospects for the recycle of valuable products from wastes generated by customers and unrelated processors are also discussed.

Jan 1, 1992