By H. Y. Sohn

The ignition and combustion of chalcopyrite particles under suspension-smelting conditions, in which the particle-particle interaction is neglected, has been analyzed by considering the intrinsic kinetics of oxidation and heat and mass transfer between the particle and its surroundings. Reasonable agreement has been obtained between the calculated results and experimental results from a laminar-flow furnace reported in the literature. This computation- al procedure has further been applied to flash-smelting conditions. Under suspension-smelting conditions (Sh = Nu = 2), chalcopyrite particles ignite at around 960 K. The effects of various parameters, such as oxygen concentration, particle size, and gas temperature, have also been evaluated. Comparison between calculated results in this work and experimental observations indicates that SO is the important gaseous product that forms at the surface of the particle.

Jan 1, 1993

By Yanhui Liu, Xuewei Lv, Pingsheng Lai, Chenguang Bai

The purpose of this paper is to study the effect of slag basicity on the Si content in stainless steel master alloys prepared by smelting reduction of Fe-Ni-Cr sinters. Theoretical analysis focusing on the gas, slag and alloy phases of the smelting reduction process at 1600°C was carried out by thermodynamic calculation software----FactSage, showing that the increase of CaO within the slag can result in the decrease of Si within the master alloy. Experiments were also carried out in vacuum melting furnace at 1600°C , and chemical analysis method was used to detect Si content in the alloys. When the MgO content is 9.00%, the experimental results were consistent with the calculated values. However, when the MgO content rises up to 14%, the content of Si in the alloy reaches the maximum when SiO2 equals to 22.81%.

Jan 1, 2016

By Harrison Cooper, Stephen Pack

"Data from samples taken during rotary air blast and reverse circulation drilling are crucial to properly assessing economics of mineral deposits in the case of exploratory work, and are equally critical in accurately delineating ore and waste in execution of mine operation plans. Past studies of sampling procedures, comparing results of conventional splitting to more precise extraction of representative samples, illustrate the significant degree of error frequently encountered. Economic impact of error in mine blast hole sampling work can be shown to result in theoretical losses valued at millions of dollars annually in operating large scale mining projects. Results of past drill sampling studies are reviewed.Drill sampling technique can be improved by collecting coarse and fine particles together and extracting samples for assay from the complete flow of rock and dust simultaneously. This can be accomplished with a collection unit attached to the drill stem through which all except a small proportion of extreme fines are retained. The bulk mass can be static sampled as flow takes place through the collector when size reduction is not required. Alternately, collected mass with fines and coarse intermingled can be processed for increased accuracy through size reduction to obtain proportional samples."

Jan 1, 1999

By N. Menad

Thermal treatments of five different types of non-ferrous metallurgical wastes, under controlled atmosphere, were carried out at temperatures lower than 800 °C. The aim of these treatments was to reduce the toxic elements content and to increase that of valuable metals in the residue. <Best results were obtained by their treatments in air or hydrogen or successively both of them. Simple treatments using air or hydrogen of three samples allowed the elimination of more than? 95 % of their toxic elements and&apos; almost doubled their valuable metals&apos; concentration. For the rest two samples, combined treatment was necessary for their efficient decontamination and the concentration of valuable metals, in the treatments residue, to a reasonable value. Most of the solids issued from these treatments can be recycled in .the current non-ferrous metallurgical processes.

Jan 1, 1995

By Shengli Tao, Hongxu Li, Hao Bai, Yu Chen, Daqiang Cang

"China is the world's largest steel producer, in order to give environment load comprehensive analysis of steel and iron industry in china using LCA method, the life cycle inventory was compiled and assessment model based on Gabi software was also established. Environmental impact of two different routes ofBF-BOF and the EAF were analyzed respectively and intercompared. The results show that the modem EAF route is superior to the traditional BFBOF route on almost all the environmental impact indexes, which including acidification potential, eutrification potential, global warming potential, ozone depletion potential, etc. In the whole life cycle ofBF-BOF route in China, the transporting process ranks the biggest contribution part to the overall global warming potential, which can be explained by the fossil fuel burning of transporting vehicles during the long distance from Australia to China as the iron ore used are mainly imported from Australia. Apart from transporting process, Coking, blast furnace and iron mining processes could induce great environmental problems, while for the EAF route, the electricity consumption is considerable, which causing large amount ofC02 emission indirectly. Based on the analysis, several further countermeasures were proposed. Key words: Iron and steel industry, LCA, Gabi software, C02 emissionIntroductionCrude steel of china which reached 101.24 million tons in 1999 ranked the first column in the world since1999, So far has been to keep the world's largest steel output. At the year of2009, China crude steel output of 568 million tons, accounting for 46.6% of the global crude steel production, more than the total sum of crude steel production produced by 20 countries ranked behind. In 2011, China's crude steel production which is expected to be or close to 700 million tons, an increase of 12% than last year, will account for half of the global steel production.The steel industry, however, is intensive resources industry with huge consumptions of energy and water together with mineral resources. Energy consumption of the iron and steel industry has been about 10% of the total energy consumption since 1980. Coal dominants, power next and other energies share least in the energy consumption structure, for example coal accounts for 72.19%, power 23.52% and other total sums less than 5% in the steel energy consumption at year of 2002[2,3]. The consumption of coal discharges much emission of CO2, yet emissions of C02 in China steel industry, secondary only to the power and cement industry, ranked the third, and the coal dominant energy structure and its process have a close relationship. The aim of this research is to target steel production of typical blast furnace-converter (BFBOF) and electric furnace, using GABI software to evaluate and analyze resources and environment influence of LCA, directing at the existing problems in the development of China steel as well as finding the possible way to improve ability of reducing pollution and energy consumption in order to realize the sustainable development of the steel industry [ 4-7]."

Jan 1, 2012

By Jay S. Gunasekera

Metal parts are traditionally processed by either filly-liquid (e.g., casting) or filly-solid (e.g., forging) state. Semi-solid metal forming incorporates elements of both casting and forging. In 1991, Gunasekera(5) developed a model illustrating the influence of flow stress by the liquid fraction. The result fits Kiuchi&apos;s (1979)(7) experimental data quite well. This model assumed the liquid part is surrounded by solid as small pockets inside the material, which is opposite to the real practical situation. Since the melting usually first happens at the grain boundary, it is better to treat the semi-solid material as small metal crystal surrounded by liquid.

Jan 1, 1997

By Jianguo Yin, Wenqiang Yang, Xiaoli Yuan, Juan An, Wentang Xia

Low grade iron ore with phosphorus (LGIOWP), a raw and wasted industrial solid material was used as an adsorbent to remove Pb(II) from wastewater. The effects of initial pH value, adsorptive time, initial Pb(II) concentration, adsorptive temperature and LGIOWP dosage on the Pb(II) removal efficiency were studied. The results show that the Pb(II) removal efficiencies exceed 99.4% and Pb(II) concentrations are less than 0.30 mg/L under the conditions of pH value 7.0, adsorptive temperature 50 oC, adsorptive time 30 min, initial Pb(II) concentration 100 mg/L, particle size <0.25 mm, adsorbent dosage 5 g/L and stirring speed 260 r/min. After Pb(II) removal reaction, the Pb(II) concentrations of wastewater completely accord with the requirement of national discharge standards of pollutants from lead and zinc industries (GB 25466-2010) (TPb= 0.5 mg/L) in China. Therefore, it can be concluded that LGIOWP is a new low-cost adsorbent which is suitable for the adsorption of Pb(II) from wastewater.

Jan 1, 2015

By Katsutoshi Inoue

Pectic acid gel crosslinked with epichlorohydrin was found to have very high selectivity to lead(II) and iron(III) ions over zinc(II) ion compared with commercial weakly cation exchange resins containing the same carboxylic functional groups, suitable for removing small amount of impurity metal ions from waste zinc plating solutions. In order to lower the cost, new adsorption gel was prepared from orange juice residue containing pectic acid by crosslinking with epichlorohydrin, which was also found to be suitable for removing these impurities. Further, very cheap adsorption gels was prepared not only from orange but also from apple juice residues by a simple method through just saponificating pectin substances contained in these residues into pectic acid by calcium hydroxide followed by water washing and drying. These adsorption gels exhibited excellent adsorption behaviors for removing the impurity metal ions away from zinc.

Jan 1, 2003

By D. E. Woolley

The rate of reduction of iron oxide from calcia-silica-alumina slag by carbon in liquid iron has been measured over the temperature range 1400-1600°C by monitoring the rate of carbon monoxide (CO) evolution. Slags containing ferric iron have been used in order to study the reduction of both ferric and ferrous cations. Results show that ferric iron is reduced before ferrous iron, so that the ferrous iron concentration increases initially. It is also shown that the rate constant, k, decreases at low reaction rates, or, equivalently, at low concentrations. The authors conclude that the reaction occurs in two periods. During the first period, ferric iron is reduced to ferrous iron. During the second period, ferrous iron is reduced to metallic iron, and the rate-limiting step during the second period is the mass transfer of ferrous cations in the slag phase to the slag-metal interface.

Jan 1, 1998

By Mike Trovant, Stavros A. Argyropoulos

"A fixed grid numerical model for phase change problems is proposed. The model solves for heat transfer and fluid flow, via the coupled solution of the energy, continuity and momentum equations. In addition, the numerical scheme accounts for temperature varying thermophysical properties and determines the shrinkage profile resulting from phase and density change. Simulations are run to determine the effect of varying model parameters and wall cooling rates on the location and shape of the shrinkage void formation in cylindrical casts. Results are shown for both aluminum and magnesium.IntroductionThe mathematical modeling of phase change processes (be they solidification or melting problems) entails solving for many interrelated phenomena. A comprehensive numerical simulation of the casting of a metal, for example, would have to account for: (a) heat transfer in both the solid and liquid portions of the metal and in the mold, (b) the release of latent heat during phase change, (c) fluid flow behavior in the liquid portion of the metal, (d) temperature induced shrinkage caused by liquid contraction and solidification contraction, and (e) the development of thermal stresses with accompanying shrinkage in the solid portion of the cast and mold. A schematic of the relationships that exist between the coupled equations which govern solidification is shown in Figure 1."

Jan 1, 1994

By I. Gaballah

About forty percent of the SOx emissions are generated during the processing of metal sulfides of Cu, Pb, Zn, Ni, etc. Although new technologies for metal sulfide&apos;s smelting allow the production of H2S04 with a reasonable cost and decrease the emissions of sulfur oxides, the generated quantity of SOx is considered as a serious threat to environment. This paper suggests alternatives for low temperature processing of complex sulfide ores or concentrates &apos;CSO or CSC&apos; under neutral, reducing and chlorinating atmospheres or their combination. At T > 400 "C, The neutral and reducing treatments allow the decomposition of pyrite and the partial recovery of sulfur as So and H2S. At 300 "C, the chlorinating treatment of CSC is fast, exothermic and allows the separation of FeC13 from the valuable elements&apos; chlorides. It also generates SyCIx that can be either reduced by H2 or hydrolyzed in presence of sodium sulfide. The recovery rate of elemental sulfur with respect to the sulfur input exceeds 90 %.

Jan 1, 1999

By S. K. Wu, Ray Y. Lin, Sunil Annaji

Infrared joining of TiAI using aluminum foils as the filler material was investigated at temperatures between 1050 °C and 1350 °C in a flowing argon environment for times varying between 15 and 60 seconds. Using aluminum foils, the attempt was to form the Al3Ti phase in the joint as a result of reaction between Al and TiAI at temperatures above the melting point of Al. It has been found based on X-ray diffraction and TEM analysis that, Al3Ti, indeed is the product of infrared joining of TiAI using Al as the joining alloy. Al3 Ti was detected even in the joint processed at 1050 °C for only 15 seconds. Since the aluminum foil used in this study contains 27 at% Si, the t 2 phase in the Ti-Al-Si ternary system is believed to have also formed at the joint/base TiAI interface. Cross sectional studies on the joined specimens have shown different degrees of reaction depending on the temperature and time of joining. Micro hardness evaluations across the joint show that the hardness near the center of the joint is typically smaller than that near the joint edge next to the base material. However, as the joining temperature and time increase, the increment of the hardness at the center of the joint is faster than that around the periphery of the joint.

Jan 1, 1996

By I. Gaballah

High and low grade concentrates of tantalum and niobium oxides were obtained by leaching a medium grade tin slag. Chlorination and carbochlorinalion of these concentrates were studied between 200 and 1000 "C. Chlorination or carbochlorination of the low grade concentrate led, at 1000 OC, to the extraction of about 95 % of the tantalum and niobium oxides. However, the tantalum and niobium chlorinated compounds were contaminated by iron and manganese chlorides. Complete extraction of the niobium and tantalum pentoxide was achieved during the carbochlorination of the high grade concentrate at 300 and 500 "C, respectively. While chlorination of this concentrate at 1000 "C, allowed to the volatilization of about 60 and 80 % of Ta205 and Nb205. In both cases, condensates were composed of almost pure tantalum and niobium chlorinated compounds. The results demonstrate the advantages of the lixivialion based on the "pseudo- structure" of the raw tin slag to obtain the high grade concentrate. The conclusions of this work suggest that the carbochlorination of the high grade concentrate is an efficient process for the extraction of refractory elements from tin slag.

Jan 1, 1993

By Seksak Asavavisithchai, Natthida Jareankieathbovorn, Areeya Srichaiyaperk

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."

Jan 1, 2012

By Katia Vutova, Vania Vassileva

Investigations and results on the refining of tungsten scrap applying electron beam melting (EBM) in vacuum are presented and discussed. In this work EB melting experiments were performed in single or double-melt operations with different power inputs and refining times for tungsten purification and recovery of multiple metals (including refractory and other metals such as Mo, Nb, Cu, Zn, etc.), which are alloyed elements or impurities with high concentrations in the initial materials. Evaluations for extraction of some valuable metals, generated in the condensate at their removal from the liquid metal during the refining process are provided. Efficient technological regimes for e-beam melting and refining that enable the simultaneous production of pure metal ingots and condensates that can be used directly or can be used for subsequent extraction of expensive and valuable metals are presented.

Jan 1, 2016

By C. Lupi

"The energy consumption of copper production by electrowinning, generally represents more than 1/4 of the total energy requirement in hydrometallurgical traditional process (roasting, leaching, purification and electrowinning). The considerable saving can be achieved just in this step that requires about 2.2 kWhlkg of the produced copper. To save energy the cell voltage, or more appropriately its anodic component, can be reduced: that is because the anodic voltage represents the main component of cell voltage and so it is largely responsible for the excessive energy consumption in copper sulphate electrowinning.In this work some ways are studied to lower the anodic voltage. First the cobalt ions were added to the sulphate solution in order to study the catalytic effect on oxygen discharge. Then lead alloys anodes (Pb-Ag, Pb-Sb-Ag and Pb-Ca) were used to promote a better oxygen evolution as a result of a different anodic surface. Their behaviour was compared with the PbSb traditional ones. Finally, as already pointed out by several authors for zinc electrowinning, ethylene glycol was employed as anodic depolariser in order to verify its effectiveness in the case of copper electrowinning. By combining all the above-mentioned ways, energy saving ranging from 20% to 27% is achieved.All the tests were carried out on a laboratory pilot-plant for long time to simulate the industrial conditions. The obtained copper deposits were observed by SEM to highlight their morphology."

Jan 1, 1997

By Naixiang Feng, Shaohu Tao, Zhihui Wang, Yuezhong Di

"A novel vacuum aluminothermic reduction lithium process was developed in present work which used lithium carbonate, alumina and calcium oxide as raw material. The process mainly contained three steps. The first step is that LiA102 clinker is prepared in ambient environment, then metal lithium is vacuum extracted from LiAl02 clinker with aluminum power as reducing agent, and the last step is that alumina is leached from the reduction residue with a mixture of sodium hydroxide and sodium carbonate. The results show that the lithium reduction ratio can be over 95% under the conditions of reduction temperature 1423K, reduction time 3h, and aluminum excess 20%. The main components of reduction residue are CaO· Al203 and 12Ca0·7Alz03. The alumina leaching rate of calcium aluminate in residue is over 80%. High-whiteness aluminum hydroxide can be obtained by carbonation precipitation of the reduction slag leaching solution.IntroductionWith a density about half of water, lithium is with the lowest density of all solids, mere 0.5 g/cm3 at 20 °C [l]. Lithium is widely used in aerospace, aviation, nuclear-generated power and electric battery industry. Nowadays, over 90 % of the world's primary lithium is produced by molten salt electrolysis [2-4]. But the development of molten salt electrolysis will be effected by some factors: cost, environment, and so on. Vacuum thermal reduction may be used extensively in future because of its low-energy consumption, high-purity and short-cycle."

Jan 1, 2013

By Lin Li, Xiang Li, Yifang Zheng, Jilai Xue, Jun Zhu

"Al drops and gas bubbles in the anode-cathode space of aluminum electrolysis cell are of great importance for cell operation improvement in metal loss, current efficiency and energy consumption. A direct observation on the Al drop, gas bubble and ultrasound was carried out through a see-through cell. The Al drop immersed into the cryolitic melt was found moving up and down irregularly in the anode-cathode space without electrolysis, which was then completely dissolved into the melt. During electrolysis, the Al drop came to the anode area and reacted with the gas bubbles generated on the anode. Under ultrasound, the gas bubbles were removed from the anode surface while the Al drop was kept on the side of anode. The observed phenomena were useful for technology improvement in reducing the anode-cathode distance or lowering the energy consumption in aluminum electrolysis.IntroductionDuring aluminum electrolysis, aluminum metal drop and anodic gas bubble are in close contact each other within the anode-cathode space, and the interaction between them can produce significant impact on metal loss, current efficiency and energy consumption. The motions of the Al drop and the gas bubble are also related to the dissolution of aluminum metal into cryolitic melt and the cell voltage drop due to the bubble layer covering the anode surface.A number of studies have been carried out using different types of see-through cells, where the dissolving process of metal Al into cryolitic melts (metal fog) in the anode-cathode space was directly observed and photographed [1, 2]. With the similar method, some direct observations on the anodic bubble behaviors with and without ultrasound were performed during aluminum electrolysis [3-6]. However, to our best knowledge, there is no published work on direct observation on the behavior of Al drops and anodic gas bubbles staying together within the same anode-cathode space, as well as the motion and interaction of them in cryolite-alumina melts."

Jan 1, 2011

By Richard J. Abitz

Thennodynamic geochemical models have been applied to assess the relative effectiveness of a variety of reagents added to aqueous waste streams for the removal of radioactive elements. Two aqueous waste streams were examined: effluent derived from the processing of uranium ore and irradiated uranium fuel rods. Simulations of the treatment train were performed to estimate the mass of reagents needed per kilogram of solution, identify pH regions corresponding to solubility minimums, and predict the identity and quantity of precipitated solids. Results generated by the simulations include figures that chart the chemical evolution of the waste stream as reagents are added and summary tables that list mass balances for all reagents and radioactive elements of concern. Model results were used to set initial reagent levels for the treatment trains, minimizing the number of bench-scale tests required to bring the treatment train up to full-scale operation. Additionally, presentation of modeling results at public meetings helps to establish good faith between the federal government, industry, concerned citizens, and media groups.

Jan 1, 1996

By N. S. Raghavendran

Based on the weld pool length and width calculations due to an empirical model (1) for submerged arc weld metal, an elegant quantitative definition of tandem submerged arc welding is established. On the basis of this theoretical consideration optimum welding parameters for joining 25 mm thick low carbon steel plate in two passes by tandem wire submerged arc welding have been experimentally found out. An assessment of the metallurgical quality of weld metal and the dependence of mechanical propenies on pool overlap has been made. Also the solution of Rosenthal (2) etc. for a moving point source of welding, which was used as a guide line in formulating the empirical model for the calculations of weld pool dimensions, is compared with the solution of empirical model for submerged arc weld pool dimensions.

Jan 1, 1990