By Bradley Stoughton

As a part of the systematic study of the alloys of iron under the auspices of the Engineering Foundation, and preliminary to the commencement of comprehensive work on this larger subject, the authors have undertaken an investigation of the available literature dealing: with the alloys of iron and silicon. The purpose is to collect all the data in English and foreign languages and present them in two mono-graphs, one of a more scientific and the second of a more industrially useful nature. Of course, a great deal of information upon the constitution of the iron-silicon alloys was found specificially upon the changes of phase in the equilibrium diagram and the different phases present, such as solid solution, chemical compounds (iron silicides), etc. While no extended research was contemplated in the particular study undertaken, nevertheless the data collected proved to be so contradictory in many respects that a simple study of some of the outstanding problems involved in the constitution and equilibrium diagram was undertaken Because research was not a primary object of the work, and also because of the extreme industrial importance of the silicon alloys between 0.80 and 14 per cent. silicon, and finally because of the unsatisfactory state of knowledge existing as to these alloys, the experimental investigation was limited entirely to alloys with less than 10 per cent. silicon.

Jan 1, 1930

By Walter J. Johnson

The coals in northern Wyoming and Montana are free-burning and non-caking and range from lignite to bituminous C in rank. Strip and underground mining are employed to supply railroad, utility, industrial, and domestic fuel. The market area includes Iowa, Nebraska, Minnesota, North and South Dakotas, Wyoming, Montana, the Pacific Northwest, and western Canada. THE larger producing coal mines in northern Wyoming are located in the Powder River Basin lying between the Black Hills region of South Dakota, eastern Wyoming, and the Big Horn Mountains in north central Wyoming, see Fig. 1. The mines are located particularly in the area along the route of the Chicago, Burlington & Quincy Railroad from Gillette, Wyo., to a point approximately 15 miles northeast of Sheridan, Wyo. Fig. 2 is a graph of coal production in the state of Wyoming from 1918 to 1951. Across the Big Horn Mountains lies the Big Horn Basin, situated between the Big Horn Mountains and the Rocky Mountains proper. Mining in the Big Horn Basin is almost entirely confined to a small area known as the Gebo Field, near the town of Kirby, which is located on the Chicago, Burlington & Quincy Railroad. This paper will describe present operating areas, making only brief reference to the history of mining and marketing primarily because of the large area to be discussed. The coal beds presently mined in the Powder River Basin are all of Tertiary age and are of Fort Union and Wasatch formations of Paleocene and Eocene ages, see Fig. 3. The Fort Union formation, consisting of 2000 to 3200 ft of alternate sandstone, shale, and coal, is divided from oldest to youngest into the Tullock, Lebo Shale, and Tongue River members. Most of the mineable coal is in the Tongue River member, which is 500 to 800 ft thick. The Carney coal bed, varying from 7 to 20 ft in thickness, is considered the base of the Tongue River member. About 85 ft above the Carney is the Monarch bed, ranging from 18 to 42 ft in thickness. At approximately 210 ft above the Monarch is what is locally known in the Sheridan district as Dietz No. 3 bed, which varies from 12 to 30 ft in thickness. One hundred feet above the Dietz No. 3 is Dietz No. 2 bed, which is 7 to 12 ft thick. At about 100 ft above the Dietz No. 2 is Dietz No. 1 bed, 7 to 15 feet in thickness. Two hundred and fifteen feet above Dietz No. 1 is the Smith bed, approximately 5 ft thick. One hundred twenty-five feet above the Smith is the Roland bed, which is estimated to be approximately 13 ft thick. The Roland bed is considered the base of the Wasatch formation, which in the Powder River Basin is 1000 to 3500 ft thick and is composed largely of shale, sandstone, and coal. The foregoing measures are the only ones above the Tongue River member that have been mined in the Sheridan field. To the east of the Sheridan field, particularly in the area of Gillette, the Roland bed is considerably thicker and is considered the thickest and most extensive coal bed in Wyoming, reaching a maximum thickness of 106 ft. From 125 to 225 ft above the Roland lies the Arvada bed, average thickness 9 ft. Three hundred seventy-five to four hundred feet above the Arvada is the Felix bed, which reaches its maximum thickness of 30 ft near Echeta on the Chicago, Burlington & Quincy Railroad. East of the Powder River the bed averages more than 10 ft in thickness, but it thins in a northwesterly direction. The highest mineable coal in the Powder River field is the Healy bed, about 400 ft above the Felix bed and exposed only in the highest parts of the area where much of it has been burned along the outcrop. Where it has not been burned, the thickness at most of the outcrops is 10 to 15 ft.

Jan 1, 1954

By Arthur C. Forsyth, R. L. Dowdell

A search through the available literature shows that the cobalt-nickel-silicon system has not been systematically studied. This seems rather odd because all three elements are fairly abundant and have better than average corrosion resistance; however, they have high melting points, which makes experimental work difficult. Cobalt and nickel form a continuous series of solid solutions and each metal dissolves about 7.5 per cent silicon. Many ternary alloys have been studied and the results have been published in a great many different ways, but to present such data in a short but clear and understandable manner is still a problem. The following pages describe the results of the study of 76 alloys from which the partial ternary diagram (Fig. 1) of the cobalt-nickel-silicon system has been drawn. The alloys were chosen according to the plan in Fig. la by taking definite ratios of cobalt and nickel, such as 70 Ni, 30 Co or 40 Ni, 60 Co, and adding silicon in various percentages. Each section was studied in detail by means of thermal analysis and microscopic examination, but only two of these detailed sections were thought necessary in the point perspective drawing to give a comprehensive picture of the liquidus, solidus and solid transformations that take place over the temperature ranges studied. Complete thermal analyses and microscopic data are given in Table 1. Experimental Procedure The alloys were prepared from metals of commercial purity, as follows: electrolytic nickel 99.60 + 0.35 Co; chemically purified silicon 99.79 per cent plus impurities of Fe 0.027, A1 0.008, Ca 0.014, C 0.004, N² 0.10; and cobalt 98.82 per cent plus impurities of Ni 0.42, Fe 0.12, CaO 0.27, S 0.012, Mn 0.10 and SiO² 0.15. It should be noted that the largest impurity in cobalt is nickel, one of the alloying elements. The alloys were melted in a small Ajax induction furnace, the nickel and cobalt being melted first because of their better ferromagnetic

Jan 1, 1940

By Arthur C. Forsyth, R. L. Dowdell

A search through the available literature shows that the cobalt-nickel-silicon system has not been systematically studied. This seems rather odd because all three elements are fairly abundant and have better than average corrosion resistance; however, they have high melting points, which makes experimental work difficult. Cobalt and nickel form a continuous series of solid solutions and each metal dissolves about 7.5 per cent silicon. Many ternary alloys have been studied and the results have been published in a great many different ways, but to present such data in a short but clear and understandable manner is still a problem. The following pages describe the results of the study of 76 alloys from which the partial ternary diagram (Fig. 1) of the cobalt-nickel-silicon system has been drawn. The alloys were chosen according to the plan in Fig. la by taking definite ratios of cobalt and nickel, such as 70 Ni, 30 Co or 40 Ni, 60 Co, and adding silicon in various percentages. Each section was studied in detail by means of thermal analysis and microscopic examination, but only two of these detailed sections were thought necessary in the point perspective drawing to give a comprehensive picture of the liquidus, solidus and solid transformations that take place over the temperature ranges studied. Complete thermal analyses and microscopic data are given in Table 1. Experimental Procedure The alloys were prepared from metals of commercial purity, as follows: electrolytic nickel 99.60 + 0.35 Co; chemically purified silicon 99.79 per cent plus impurities of Fe 0.027, A1 0.008, Ca 0.014, C 0.004, N² 0.10; and cobalt 98.82 per cent plus impurities of Ni 0.42, Fe 0.12, CaO 0.27, S 0.012, Mn 0.10 and SiO² 0.15. It should be noted that the largest impurity in cobalt is nickel, one of the alloying elements. The alloys were melted in a small Ajax induction furnace, the nickel and cobalt being melted first because of their better ferromagnetic

Jan 1, 1940

By G. Ansel, J. O. Betteron

THE PURPOSE OF THIS PAPER is to give a brief picture of present day magnesium rolling practice, to elaborate on laboratory and development rolling experiments; and finally, to discuss the possible Future rolling of magnesium. The present production practice is so varied between various mills that it can only he concluded that no single producer is now using a process that is outstandingly superior to others. In view of this, only the general features of present day production practice have been presented and attention is focussed on the results of laboratory find development rolling of magnesium-base alloys as indications of the Future trend of magnesium rolling. MAGNESIUM ROLLING LITERATURE The literature relating to magnesium rolling is divided into three groups: the deformation mechanisms of the hexagonal magnesium crystals, the metallurgical aspects and laboratory type experiments in rolling, and finally, the articles on production rolling methods. This literature was reviewed and is summarized below. In the first group of references, the existence of basal slip in magnesium single crystals was shown by Schiebold and Siebel1 and of {102} twinning by Mathewson and Phillips2, Schmid3 predicted and partially established {101} slip at hot working temperatures. Bakarian and Mathewson4 confirmed the above and eliminated {101} twinning as a probable deformation mechan-

Jan 1, 1948

By J. O. Nelson, C. J. Altstetter

Single crystals of hcp cobalt, 3 mm in diameter and up to 35 cm long, were grown using an electron-beam, zone-melting technique. The martensitic-phase transformation was studied in single-crystalline and polycrystalline specimens by making length-change measurements as a function of temperature under various elastic compressive stresses. Upon thermal cycling, single-crystalline or polycrystalline specimens repeatedly transformed almost entirely on the same variant of close-packed plane provided the maximum temperature did not exceed 600°C. Cycling to 1000°C resulted in transformation on more than one {111} variant. This behavior is termed multivariance. The multivariant transformation occurred very rapidly at an M, temperature 2° to 6°C lower than the M, of a transformation which would result in a single-crystal product. Elastic compressive stresses (up to 253 g per sq mm) tended to lower the A, and raise the M, temperatures, decreasing the width of the temperature vs dilatation hysteresis loop. The transformation habit plane and transformation shear direction of an as-grown single crystal were not grossly affected by elastic compressi?ie stress. This was evidenced by similar dilatations on the temperature us dilatation loops joy specimens with and without compressive stress. A dislocation mechanism is proposed to explain the observed results. IT has been shown that, on heating, cobalt transforms martensitically from the hcp to the fcc phase.' The transformation habit plane is (0001)hcp || (lll)fcc and the transformation shear direction is (1010)hcp || (112)fcc. The transformation involves a shear of 1g°28', which may be achieved by a shearing of a/6(112) of every two planes with respect to the plane beneath, thus changing the ABABAB stacking of hcp to the ABCABC stacking of fcc. Associated with the phase change is a 0.3 x 10"3 contraction in the habit plane and a 4.2 X 10"3 expansion perpendicular to the habit plane resulting in a 3.6 x X volume increase on heating.' On cooling, an identical volume decrease takes place. The temperature at which the fcc phase begins to form on heating (A,) is reported as 430°C, and the temperature at which the hcp phase begins to form on cooling from an elevated temperature (A&) is reported as 390oC1,3 Consequently, temperature vs dilatation plots have the form of a hysteresis loop. If heating or cooling is reversed during a transformation, a smaller hysteresis loop results. Upon heating, the transformation is always complete; whereas, fcc is often retained at room temperature as a metastable phase entrapped in the polycrystal-line hexagonal matrix.1,4,5 Two obstacles in the theory of the allotropic-phase transformation of cobalt have been: 1) a detailed knowledge of the product nucleus, and 2) a plausible method of propagation of the transformation. Bilby,8 christian, 7 and seeger 8,9 have suggested a "pole mechanism" as a means of propagation of partiai dislocations from plane to plane. A pole dislocation and a Shockley partial come together at a node. The a/6(112) Shockley partial rotates about the pole dislocation effecting the transformation shear. The pole dislocation must have a 2a/3(111) screw component which causes extension of the transformed region by two atomic planes with each full rotation of the Shockley partial. Bollmannl0 suggested, on the other hand, that transformation propagation occurs due to the stress fields of intersecting (111)-type stacking faults. As faults intersect, a stress distribution is set up about their intersection which is in turn reduced by the emergence of another fault on the second nearest plane. This process continues with the final result of a complete phase transformation. In view of the similarities between deformation and transformation in cobalt, the effect of stress on the transformation would, hopefully, yield valuable information concerning nucleation and propagation. In the present work single-crystalline and polycrystalline specimen length changes were measured as a function of temperature at various compressive loads. PROCEDURE Several orientations of single crystals of hcp cobalt in lengths up to 25 cm were grown by electron-beam floating zone melting from 99.95 and 99.999 pct, 3-mm-diam cobalt rod as supplied by Johnson

Jan 1, 1964

By Chandler Morse

RENEWABLE VS. NONRENEWABLE NATURAL RESOURCES Nonrenewable resources, such as minerals, are the inevitable center of attention in discussions of depletion and exhaustion. Nevertheless, it may well be proper to regard some nonrenewable resources as not subject to exhaustion, and renewable resources may sometimes be treated as if they were finite stocks. Thus, the availability of nonrenewable resources is not and probably never will be known completely Chap. 2.5A, and therefore is not subject to firm predictions concerning exhaustibility. Moreover, because exploration and discovery are more or less continuous processes it is often appropriate to regard mineral supplies as flows, and to treat the estimated reserves as working capital, an inventory, continually depleted by use and augmented by discoveries.23 The aggregate economically exploitable stocks of a given mineral are seldom estimated (or estimatable) with precision, as Chap. 2.5A shows, and even when they are, forecasts concerning years of remaining life can be and often are falsified by changes in one or more of the multidimensional conditions of supply and demand; or the productive services formerly derived from an exhausted stock may continue to provided without material impairment by one or more substitutes b Conversely, the renewable resources are all subject to depletion when the rate of use exceeds the natural or induced rate of replenishment, and cases of exhaustion or near exhaustion, as through soil erosion, overcuttmg of forest lands, and overfishing, are rather common c Where exhaustion is a clear possibility the resource may either be exploited on a consciously adopted "sustainable yield" basis or be treated as an exhausting asset." In some cases, conscious treatment

Jan 1, 1976

Jan 1, 1951

By R. M. Brick

THE etched microstructures of cold-worked alpha brasses, after reduc-tions in excess of about 20 per cent, exhibit dark lines or markings, which have been termed "deformation bands," "etch bands," and "strain markings." The terms will be used synonomously in this report. The markings are similar in their general appearance to etch figures found in cold-worked iron, aluminum and other cubic metals but in certain respects may differ noticeably. At reductions of from about 20 to 50 per cent in brass, they appear as straight dark lines of irregular spacing and at random directions in different grains, but apparently intimately associated with definite crystallographic planes, usually {111}, in each crystal. At higher reductions, the markings on the rolling plane tend to appear in a direction transverse to the rolling direction in all crystals but may bend away at considerable angles, particularly near grain boundaries. Samans,1 on the basis of X-ray and micrographic studies of two single crystals of brass, rolled to a 50 per cent reduction, showed that the lines of deformation were the edges of thin mechanical twins parallel to octahedral planes. Barrett and Levenson2-4 have made comprehensive studies of the deformation of iron and of aluminum. They show that in these two metals the deformation markings originate by division of the original homogeneous crystal into banded areas differing in orientation by an amount that increases with the degree of deformation. The markings thus cannot be twin bands, and Barrett, in a review of this subject,2 attributed Samans' results on brass to an accidental choice of deformation that left the bands in approximately a twinned relationship. On the other hand, Mathewson5 has suggested that in some cases mechanical twinning offers a better rationalization of the coverage of some (111) pole figures of worked brass than the assumption of band rotation into sym-metry positions. Considering next a deformed and annealed alpha brass, the most striking aspect of its microstructure is the multiplicity of twin bands.

Jan 1, 1940

By P. M. Robinson, M. B. Bever

The heats oj formation at 273°K of the compounds CdTe, I)z2Te, InTe, In2Te3. In2Te5, SrzTe, and PbTe have been rleasrred in a liquid metal solutiotz caloritrete? 1.t1itlz bismuth as solvent. The?, are iterpretecl in yelation to tlze stability and bonding of the cott/pozltzds. Tile heats of fusion atzd the melting- points of tlze cotlzpounds InTe and Itzz,Te3 1lcti.e been measured in a cotrslant-temperature gradient calorimeter. The entropies of fusion are disc,ztssecl in YIIIS 01. the degree of order in the solid at the melting point. THE heats of formation of the tellurides of cadmium, indium, tin, and lead have been measured as a continuation of research on the thermodynamic properties of compounds of tellurim.' The tellurides of these metals were selected with a view to examining the relation between the heat of formation and the position of the metal in the periodic system. The elements cadmium, indium, and tin are in the same period and tin and lead are in the same group of the periodic system. The tellurides of indium are of special interest because four compounds, In2Te, InTe, In2Te3, and InzTe5, occur in this system. The available information on the heats of formation of the compounds investigated consists of values for CdTe, SnTe, and PbTe derived from electromotive-force measurements,J a value for CdTe obtained by tin solution alorimetr, and values for InTe and In2Te3 determined by combustion calorimetry.5 These values, however, refer to various temperatures ranging from 273' to 673°K and some of the reported error limits are large. Liquid metal solution calorime-try may be expected to yield more accurate values for the heats of formation than electromotive-force measurements or combustion calorimetry. The heats of fusion and the melting points of the compounds InTe and In,Te3 were determined in a constant-temperature gradient calorimeter. No published information appears to be available on the heat of fusion of these compounds. The results reported here give an indication of the degree of order in the solid compounds at the melting point. 1) MATERIALS AND EXPERIMENTAL PROCEDURE Materials. Samples of the compounds SnTe and PbTe were obtained from the Westinghouse Research Laboratories and samples of the compound InTe from Lincoln Laboratory, Massachusetts Institute of Tech- nology. Additional samples of the compounds InTe, SnTe, and PbTe and samples of CdTe, In2Te, In2Te3, and In,Tes were prepared from 99.995 pct Cd (Baker Chemical CO.), 99.999+ pct In (American Smelting and Refining Co.), 99.99 pct Sn (Baker Chemical Co.), 99.999+ pct Pb (Fisher Scientific Co.), and 99.999+ pct Te (American Smelting and Refining Co.). Stoichiometric amounts of the component elements were melted in sealed, evacuated Vycor tubes. The melts were held at approximately 100°C above the liquidus for about 16 hr and shaken repeatedly. The melts of the compounds In2Te and InzTe5, which form by peritectic reactions, were quenched into iced water. The melts of the other compounds, which have congruent melting points, were slowly cooled to room temperature. The samples were then annealed for 5 days at approximately 50°C below their respective solidus temperatures. Metallographic examination did not reveal any evidence of second phases or segregation. At least two batches of each compound were prepared. Samples from each batch were used in determining the heats of formation and, in the cases of InTe and In,Te3, the heats of fusion. The Heats of Formation. The heats of formation at 273°K of the compounds were measured by metal solution calorimetry with liquid bismuth at 623" as solvent. In this technique, the heat of formation is determined from the measured heat effects on dissolution of the compound and of a mechanical mixture of the component elements. The difference between these heat effects adjusted for changes in the composition of the bath gives the heat of formation at the temperature from which the samples are added to the bath (273°K). The experimental technique and method of calculation have been described in detail elsewhere.= It should be emphasized that the reported heats of formation depend on the thermodynamic data used in calculating the heat effects for the calibration additions. In the present investigation, the calorimeter was calibrated by adding pure bismuth at 273°K to the bismuth bath at 623°K. The reported heats of formation are based on a value of 4.96 kcal per g-atom for the difference in the heat contents of bismuth at 623" and 273". If a new value for this quantity becomes available, the reported results may be adjusted in direct proportion. The concentration of solute in the bath at the end of a calorimetric run did not exceed 1.7 at. pct and was usually less. In this range, the heat effect on dissolution of the solute was a linear function of the concentration of solute. In determining the heats of formation of the compounds in the system In-Te, a few runs were carried out in which two neighboring compounds such as InTe and In,Te3 and the corresponding mechanical mixtures of the components were added to the calorimeter. The

Jan 1, 1967

By Yingchang Tsenshan Wang

UUIN L&SS 1» Paqb I. Introduction........................................................658 1. Subject and Scope...............................................658 2. Acknowledgments...............................................659 3. Review of Previous Work........................................659 Field Data...................................................659 Experiment.a1 Data............................................662 4. Plan of Present Investigation.....................................662 Method of General Procedure...................................663 I1. Experimental Work..................................................663 A. The Solution of Sphalerite..............................:........663 1. The Solvent Effect of Iron Sulphates upon Sphalerite...........663 2. The Solubility of Sphalerite in Salt Solutions of Silver, Copper and Lead...............................................668 B. Formation of Zinc Carbonates....................................674 3. The Reactions of Carbonates and Bicarbonates With Solutions of Zinc Salts............................................674 4. The Reaction of Zinc.Sulphate Solution With Limestones.......684 C. Peculiar Conditions Affectitig the Formation of Zinc Silicate (calamine) and Zinc Carbonate (smithsonite)..........................686 5a. The Effect of Carbon Dioxide Upon the Basic Silicate and the Carbonates of Zinc in Water, and Its Bearing Upon the Conditions of Theii Precipitation..............................686 5b. The Reactions of Solutions of Soluble Silicate With calamine and Smithsonite in Solution in Presence of Carbon Dioxide..689 6. The Reactions of a Mixture of Hydroxide and Silicate of Sodium with a Dilute Solution of Zinc Sulphate...................691 D. High-Temperature Methods.....................................692 7a. The Influence of Temperature on the Formation of Calamine..692 7b. Possible Effect of Heat on Calamine and Srnithsonite.........697 E. Summary of the Experimental Work..............................698 III. Petrographic Work....................................................700 1. The Occurrence of Sphalerite in Limestones or in Cherts............701 Summary of the Blende in Limestones and in Cherts.............7432 2. The Partially Altered Sphalerite and the Oxidation Products........702 a. Smithsonite with Blende....................................702 b. Calamine with Blende......................................703 c. Smithsonite and Calamine..................................703 d. Summary on the Partially Altered Sphalerite and Its Oxidation Products..............................................704 IV. Concl~~siom ........................................................-705 V. Microphotographs and Photographs with Their Explanations.............705

Jan 1, 1916

"Salt Lake City was founded July 24, 1847, by Mormons under the leadership of Brigham Young. It had a population of 118,110, according to the United States census of 1920, and of 151,968, according to a civic survey, January 1, 1925. The Salt Lake metropolitan district is estimated to have 180,079 inhabitants.The city's area is 51.8 square miles. Its altitude is 4,354 feet. It has 514 miles of streets, of which 91 miles are paved. The streets in the main portion of the city are 132 feet wide and the blocks are 660 feet long. It has 144 miles of street railway and 2,200 electric street lights. It has fifteen parks and playgrounds, forty public schools and six private schools. It has eighty-nine church edifices, of which forty-nine are devoted to denominations other than the Mormon Church.It is the capital of the state, the headquarters of the Mormon Church and the headquarters of most of the mining companies and many other business institutions of the state and adjacent territory.The State University, the State School of Mines and the Inter-Mountain Experiment Station of the U. S. Bureau of Mines are in the eastern part of the city. Fort Douglas is east of the University the country clubs are in the southeastern portion of the city. The State Fair Grounds are in the northwestern portion.The city is the center of a trade area about 700 miles in diameter and is in almost the exact center of a circle that embraces the principal western mining areas. It is the home of several widely-known mining supply companies and all the other leading concerns in that line are represented by agency or branch house."

Jan 1, 1925

By H. N. Thomson

GENERAL. THE Tooele plant of the International Smelting & Refining Co. is situated at the mouth of Pine canyon, Tooele county, Utah. It is connected with the main line of the San Pedro, Los Angeles & Salt Lake railroad by the Tooele Valley railway, and is about 7 miles from Tooele Junction. Fig. 1 is a general view of the plant. FIG. 1.-TOOELE PLANT OF THE INTERNATIONAL SMELTING & REFINING Co. The copper plant has been in operation since July, 1910, and the first blast furnace at the lead plant was blown in on Feb. 29, 1912. The location of the plant was selected on sloping ground with the idea of using gravity to the fullest extent and thus keeping labor at a minimum. Practically the entire plant is constructed of steel, reinforced concrete, and brick. Bingham ores, both lead and copper, are received over the Utah Consolidated Aerial Tramway. The tram buckets, each containing

Jan 7, 1913

By C. E. Shoenfelt

Jan 1, 1942

By C. E. Shoenfelt

Jan 1, 1942

By Guillermo Zuloaga

THE iron deposits of the Imataca Range of Venezuela, which occur along the Orinoco River, in the northern border of the Guayana High-lands, have lately attracted attention on account of their economic possibilities. Many deposits occur in this area; some of slight economic importance and others that may rank with the largest masses of high-grade iron ore of the world. The geology and the character of the ores seem to be remarkably similar to those of the large iron deposits of Brazil. In the investigation of the Venezuelan deposits a definite relationship has been found between the mineralization of the large orebodies and igneous intrusions, especially norites and granites. The following paper is the result of a field and laboratory investigation of the ore deposits. The field work was done during the months of February and March of the year 1929, partly in the company of Prof. W. H. Newhouse. The laboratory studies have been made in the Massachusetts Institute of Technology, under the supervision of Profes-sor Lindgren and Professor Newhouse.

Jan 1, 1933

F. G. SMITH, Waterbury, Conn.-I would like to ask whether small amounts of iron give the maximum resistance at a low temperature, and if the large amounts of iron raise the temperature at which the maximum resistance occurs? That is, with a small amount of iron, will a maximum be at, say, 10°? F. E. BASH.-With the small amount of iron, the maximum is at a lower temperature, and with the increase of iron, the maximum increases; it seems to come to a maximum and then decrease; that is, increasing the iron up to a certain value increases the temperature at which there is a maximum of resistance, and any increase of iron beyond that value will start decreasing this temperature. With 2 per cent. of iron, the maximum is lower than for 1.5 per cent. which was the value that we found to be satisfactory. F. L. DRIVER,* Jr., Harrison, N. J.-I would like to ask what chance there is of the instrument companies getting together and deciding on standards for both manganin and constantan? We make both of these alloys in this country and we find that each one of the instrument com-panies who buy these materials require different standards of specific electrical resistance and thermal e.m.f. For instance, some of our cus-tomers require an electrical resistance in manganin or therlo of 240 ohms per circular mil foot and others require it with a specific electrical resist-ance of 270 ohms per circular mil foot. They buy these alloys in relatively small quantities so that it means much extra melting and supervision when making up small quantities for each consumer. If something could be. clone to eliminate this, it would be a benefit to the instrument com-panies, who could secure their material more cheaply, and to the manu-facturers, who would not have to spend so much time and effort in special manufacturing.

Jan 12, 1919

By C. C. Furnas

IT is well known that particles of different sizes are not distributed evenly throughout the average charge in an iron blast furnace. Just how great the disparity in particle size in different parts of a single plane in a furnace may be is indicated by the results of some recent investigations1 conducted by the Bureau of Mines on a furnace operating on Lake ores. The wide variations found in gas velocity, gas composition, and temperature from the periphery to the center of the upper charge column were caused by the great variation in particle size of the raw materials used and were also greatly influenced by the methods of charging. This paper summarizes the results of an investigation of the influence of different methods of charging and of the treatment of raw materials upon the size distribution of the solid particles in the blast furnace. A more complete report will appear later as a Bureau of Mines technical paper.

Jan 1, 1929

Jan 1, 1951

By Henry Mulryan

THE largest and purest known deposit of diatomite is being actively mined and processed 3 ½ miles south of Lompoc, Santa Barbara County, Calif., by the Johns-Manville Products Corporation. The workings FIG. 1-LOCATION OF DIATOMITE DEPOSIT AT LOMPOC. cover 4000 acres, the depth of economically recoverable diatomite being 1000 ft. (Fig. 1). Lompoc, a community of 2500 population, is situated in the Santa Ynez River Valley 10 miles inland from the Pacific Ocean. It is 44 miles

Jan 1, 1936