By Leo P. Tarasov

Magnetic torque studies of ferromagnetic single crystals have been carried out in a number of laboratories during the last decade&apos;s2 and some work has been reported on polycrystalline material showing preferred orientation. Goss3 used the method extensively in developing electrical sheet with desirable magnetic properties, but he used it as a control rather than as a means of studying the texture. Bozorth4 made a quantitative correlation of a torque curve he obtained from some cold-rolled iron with the texture as determined from X-rays, but did not extend his studies beyond the one specimen. Other studies, which have been reported from time to time2,5 have also been incomplete in the sense that no effort was made to study a whole series of samples, differing only in degree of cold reduction or in the annealing temperature, in order to ascertain the effect of such treatments on the texture as revealed by torque measurements. It is the purpose of this investigation to make such a study, mainly in order to see how useful the method can be made when used under favorable circumstances and to find what kind of a correlation can be expected between magnetic and X-ray studies of texture. Before proceeding further, it is desirable to say a little about single crystals, so as to make clear the concepts involved in magnetic torque measurements. Magnetic Torque Method It is fairly well known nowadays that single crystals of ferromagnetic substances have directions of easy magnetization and of hard magnetization. In Fig. 1 are reproduced typical magnetization curves for a single crystal of iron, which show that in a < 100 > direction saturation occurs at low fields compared to those required to saturate the same crystal in a <110> or a <111> direction. (The magnetization intensity I is defined by the equation B = H + 4pI.) At fields high enough to

Jan 1, 1939

By Charles White Merrill, James W. Pennington

No metallurgical process developed in the 20th century compares with froth flotation in its effect on the mineral industry. Processes like gravity - concentration, amalgamation, and pyrometallurgical reduction are of ancient origin; others like cyanidation and electrolytic reduction were well established by 1900. Such metallurgical processes as heavy-media separation, ion-exchange, and solvent extraction belong to this century, but their influence is small compared with froth flotation. Data collected by the U. S. Bureau of Mines* in a canvass of 202 froth flotation plants reveal that, in 1960, 198- million tons of material was treated to recover 20-million tons of concentrates which contained approximately $1 billion in recoverable products. SIGNIFICANCE OF FLOTATION Froth flotation as described in this chapter refers to a wet process for separating properly ground mineral particles into two or more products. It involves the separation of mineral particles from each other in a liquid pulp by means of air bubbles. Finely crushed ore is agitated in water with the addition of air or other gases. Various chemicals and oils are added to cause the selected mineral particles to attach themselves to the air or gas bubbles. These bubbles, carrying the mineral particles, rise to the surface where they are removed in a froth, while the other particles remain suspended in the pulp. The earliest flotation divided the raw material into two products: a bulk concentrate that was removed as a froth and a tailing that remained in the flotation machine. The froth usually contained the valuable constituents. The successful application of such a process depended on the recovery of a single concentrate from which one or more valuable constituents could be recovered by a chemical or smelting process. With the advance of the art, however, the principle of selective flotation, by which two or more relatively pure products could be recovered from complex raw materials, was evolved. Other chapters in this volume describe the developments during the last 50

Jan 1, 1962

By J. F. Lewis

Much has been written on this great engineering work, principally from the civil engineer&apos;s stand-point. In presenting the subject to the Institute, it seems necessary to include something of geology as well as engineering. In this case, it is particularly the glacial and post-glacial periods with which we are concerned; for it has been clearly proved that the canal recently excavated has not for the first time opened the Des Plaines valley for drainage away from Lake Michigan, and that this valley, as well as the site of this city, is very closely connected with the processes and effects of the ice period. We have simply renewed a channel and a drainage direction which formerly existed. As the days of deep water-ways for commercial purposes are fast approaching, engineers may find the consideration of ancient topography and geologic changes highly useful. For what I may say on this subject I am greatly indebted to Mr. Ossian Guthrie, who has made an earnest study of glacial geology and labored especially to decipher the records of its history in this region. * Chicago is situated in the track of one of four great glacial ice-streams that swept down from the North: one moving due South from Marquette and entering the Illinois valley at Ottawa; one through the Lake Michigan valley, entering the Illinois valley near Lemont; one from Saginaw Bay diagonally across the States of Michigan and Iadiana, entering through

Jan 1, 1898

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By N. S. Stoloff, M. Gensamer

The effects of temperature, grain size, and magnesium content on the strength and ductility of cadmium were studied in the range -269° to 23 °C. A sharp drop in ductility between -140° and -190°C marked a transition in fracture mode from ductile shear to inter gvanular fracture. The addition of up to 15.35 wt pct Mg in solid solution raised the transition temperature, and for two compositions produced basal cleavages. The relatively high ductility of unalloyed cadmium at cryogenic temperatures is attributed to temperature independence of the yield stress and the absence of dislocation locking. ALTHOUGH numerous studies have been made of the mechanical properties of cadmium single crystals,1-5 no comprehensive investigation of deformation and fracture in polycrystalline cadmium has been carried out. This investigation was initiated to determine the mechanisms of deformation and fracture in polycrystalline cadmium, and to attempt to correlate these mechanisms with the behavior of other metals of hexagonal close-packed structure. A second objective of this work was to determine whether the slip systems and mode of fracture of polycrystalline cadmium could be altered by reduction of the axial ratio, which is 1.886, through alloying. Dorn and co-workers&apos; have been able to induce prismatic slip in magnesium through alloying to reduce the axial ratio. Single crystals of cadmium are so highly ductile that glide strains of 400 pct are observed at room temperature, and 80 pct at -269°c.l Failure in every reported case is by necking down and shearing off of the crystal. Cleavage in cadmium single crystals has never been observed. Magnusson and aldwin reported a ductile to brittle transition for polycrystalline cadmium at about —160 C for specimens tested at a strain rate of 0.05 in. per in. per min in tension. However, even at -196° substantial ductility was retained. The transition temperature was strain rate dependent, impact loading at 19,000 in. per in. per min raising the transition temperature to about -85°C while leaving the low temperature ductility unchanged. No information was given on microstructures or fracture mode, nor were stress-strain characteristics reported. In the present investigation, tensile tests were carried out on polycrystalline cadmium and solid solution Cd-Mg alloys to determine flow stresses, work-hardening behavior, fracture strength, and fracture ductility. Variables employed included temperature, alloy content (and c/a ratio), and grain size.Some compression data also have been obtained for comparison purposes. I) EXPERIMENTAL PROCEDURES A) Polycrystalline Cadmium. Two purities of cadmium were employed in this investigation. Cadmium of 99.95 pct purity was supplied by Belmont Smelting and Refining Co. Cadmium of 99.99+ pct purity was supplied by American Smelting and Refining Co. Threaded cylindrical tensile specimens were machined to give approximately a 1/2 in. long straight gage section with a reduced diameter of about 0.110 in. Specimens were heat treated in evacuated pyrex capsules in the range 140" to 290°C to produce desired grain sizes. All specimens were polished in a solution containing 320 g Cr03 and 20 g NaS04 in 1000 cc of H20. Occasionally this solution caused staining of the specimen, in which case a further polish with a solution of one part HN03 and two parts H202 in two parts ethyl alcohol was employed.&apos; Tensile testing was carried out on a screw-driven Instron machine, at a constant rate of crosshead movement, which for most tests was 0.01 in. per in. per min. Load vs time, and therefore load vs total strain, were recorded. Temperatures from -196" to -40°C were obtained by passing nitrogen gas through a copper coil immersed in liquid nitrogen, and then feeding the gas into a jacket around the specimen. Tests at -269°C were carried out in a helium cryostat, at a crosshead rate of 0.1 in. per in. per min, with specimens of 1 in. gage length. Compression specimens were tested in a jig similar to one designed by ilman. The jig was mounted on the under side of the Instron crosshead. Load was transmitted by means of a rod connected to a movable part of the jig at one end, and the load cell at the other end. A downward movement of the crosshead applied a compressive load to the specimen.

Jan 1, 1963

By C. R. Ramachandra, C. C. Patel

Flotation of chalcopyrite from a low grade ore was studied by using different xanthates and dixanthogens as collectors and by conditioning the flotation pulp with oxidizing gaseous systems. The improvement in the recovery of chalcopyrite with the oxidizing systems was mainly due to the auto-activation of chalcopyrite, leading to the enhanced adsorption of xanthates and dixanthogens even when the latter were formed by oxidation of the xanthates. With air or oxygen as oxidizing system, the amount of ethyl xanthate required at pH 8.5 was much less than normally employed in the industry, the recovery being 97-99% of chalcopyrite with a concentrate of 24% copper. With isopropyl and isoamyl xanthates, the recovery was improved but the grade was lowered. By conditioning the pulp with air-CO2 or oxygen-CO2 mixture, the recovery was lowered with ethyl xanthate only, mainly due to the depressant action of bicarbonate formed. Flotation with dixanthogens gave cleaner concentrates of chalcopyrite. because iron pyrite did not float with these collectors. Of the dixanthogens tried, diisopropyl dixanthogen gave the highest recovery, 99% chalcopyrite with a concentrate containing 28.5 to 30% copper, when the pulp at pH 8.5 was condi-tioned with air. Isopropyl dixanthogen was found to be the best collector of all the xanthates and dixanthogens studied. It was found that the adsorbed ethyl, isopropyl and isoamyl xanthates at chalcopyrite surface, activated by cupric sulfate, and at iron pyrite surface were oxidized to the corresponding dixanthogens to different degrees in presence of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture.&apos; The dixanthogen formed at chalcopyrite surface was, however, firmly adsorbed while that at iron pyrite surface was easily desorbed. Since dixanthogens formed have greater hydrophobicity than the corresponding xanthates, as revealed by contact angles,1,2 the former were expected to improve the flotation results. It was, therefore, thought desirable to find out the effect of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture on the selective flotation of chalcopyrite when individual xanthates were used as collectors. The effect of direct use of dixanthogens as collectors on the selective flotation of chalcopyrite was also investigated. For these studies, low grade chalcopyrite ore, received from the Indian Copper Corp., Ltd. (I.C.C.), Ghatsila, Bihar, was employed. At the milling plant of the I.C.C., chalcopyrite is floated at a pH of 8.5, employing ethyl xanthate as collector. EXPERIMENTAL Materials Employed: XANTHATES - Ethyl, isopropyl and isoamyl xanthates of potassium were prepared in a pure state by the methods described earlier.4 A 0.03% aqueous solution of a xanthate was freshly prepared in air-free distilled water for flotation studies. DIXANTHOGENS - Diethyl, diisopropyl and diisoamyl dixanthogens were prepared by the oxidation of xanthates by iodine and purified by extraction with petroleum ether. A 0.03% alcoholic solution of dixanthogen was used as a collector. FROTHER - A 0.2% solution of pine oil in ethyl alcohol was employed. SODIUM CARBONATE - A 0.4 N solution was used. ORE - The composition of the -100 +200-mesh size (Tyler standard) powdered ore, as determined by standard methods of analysis, was: copper 1.57%, iron 10.29%, sulfur 3.15% and acid insolubles 66.10%. Iron present as chalcopyrite (CuFeS2) was 1.38%, while that present as iron pyrite (FeS,) was 1.37%. Both chalcopyrite and iron pyrite were found to be liberated from the gangue minerals and from each other, as observed under a microscope. Flotation of Chalcopyrite with Xanthates in Presence of Different Gaseous Systems: Fifteen grams of -100 + 200-mesh size ore were shaken well with 100 ml of distilled water. The pH of the pulp was adjusted to 8.5 by the addition of sodium carbonate solution. Then 0.1 ml of xanthate solution (0.005 lb xanthate per ton of the ore) was mixed with the pulp, and the latter together with washings transferred to a

Jan 1, 1963

By H. I. Aaronson, C. Laird

The kinetics of thickening and of lengthening of ?&apos; plates in an Al-3.93 pct Cu alloy in the temperature range 203" to 300" C were determined by means of transmission electron microscopy. The rate of thickening was found to be less than that allowed by volume diffusion control at all temperatures, by amounts which increased with decreasing temperature, in agreement with the predictions of a general theory of precipitate morphology.1 Thickening was treated on the basis of the ledge mechanism. Ledges were deduced to spread across the broad faces of ?&apos; plates at volume dzjrfusion-controlled rates, as anticipated from the disordered structure of their edges. Lengthening of 8&apos; plates, on the other hand, took Place more rapidly than allowed by volume dzjrfusion. This occurred despite clear morPhological evidence of a bmrier to growth at the edges of these plates. It was concluded that the misfit dislocation structure comprising the barrier requires that lengthening take place by a jog mechanism. The tnisfit dislocations, however, also serve as diffusion short circuits, and allow high overall lengthening rates to be achieved. In Part I&apos; it was shown that, within the range of aging temperatures and times studied, the broad faces of 8&apos; plates formed in Al-4 pct Cu are fully coherent with the a, matrix. Virtually .all of the dislocations present in these faces were found to have developed as a result of plastic deformation in the a phase. Such dislocations are thus "intruders", rather than the more usual misfit-compensating variety. The edges of 8&apos; plates were confirmed, by extension of the earlier studies of Mat-suura and Koda,3 to be made up of edge-type misfit dislocations, in sessile orientation with respect to lengthening of the plates. These interfacial structures should cause 8&apos; plates to thicken and to lengthen at rates less than those allowed under the condition of volume diffusion control, such as would be expected if the interphase boundaries had disordered structures.&apos; The narrow width of 8&apos; plates, the reproducible crystallography of their broad faces, and the appearance of these plates in cross section as octagons rather than as circular discs2 provide qualitative support for these deductions. The present study of the rate of thickening and the rate of lengthening of 8&apos; plates was undertaken in order to examine them on a quantitative basis. I) THICKENING KINETICS OF THE BROAD FACES OF?&apos; PLATES A) Literature Review. The measurements now available on the thickening kinetics of single-phase precipitate plates consist of one plot of the thickening of a proeutectoid ferrite plate in an Fe-C alloy,&apos; showing (as predicted) thickening rates less than those allowed by volume diffusion control. B) Experimental Procedure. Details of the preparation of the 4-3.93 pct Cu alloy used in this study have been previously reported.4 As in Part 1,&apos; transmission electron microscopy was the observational tool employed. A general description of the apparatus and procedures of the electron microscopy studies is given in Section I of Part I. In thin foils, 0&apos; plates tend to form at and parallel to the foil surface.&apos; A direct investigation of the thickening process by means of hot-stage transmission electron microscopy was therefore not feasible. It was thus necessary to use the conventional method of aging individual bulk specimens for a wide range of different times at the various temperatures studied. In each specimen, the thicknesses of a number of plates were measured. Since thin foils prepared from "bulk-aged" material contain a large proportion of grains with orientations near (001) , it was relatively easy to find, near the edges of the foils, the characteristic multifold patterns of intersecting extinction contours which indicate regions where the foil is exactly at an (001) orientation. The thicknesses of large numbers of plates were measured along the (200) branches of the "stars" so that the 8&apos; plates were precisely parallel to the optical axis of the microscope. Wherever possible, intersecting extinction contours were adjusted with the parameter s > 0 to improve the visibility of the plates in bright-field illumination. These precautions, in combination with taking the measurements at the thinnest parts of the foils, minimized the errors in the measurement of the thickness of the plates resulting from inexact parallelism to the electron beam. Since the plates were very thin, it was not easy to measure their thickness on the photographs. The techniques of enlargement and of microdensitometry were employed to minimize errors from this part of the measurement. A further source of possible error, that the plates can appear thicker because of contrast associated with mismatch normal to the plane of the plate, was also considered. The images of the plates were usually thinner than those of dislocations, however, and no anomalous changes in apparent plate thickness were observed when regions of foil containing plates were tilted through various diffracting conditions. Any error from this cause must therefore be small. Other sources contributing errors were: a) the microdensitometer traces per se and the subjective estimates of their peak limits, and b) slight fluctuations in magnification associated with small changes in the current of the objective lens of the electron microscope. The overall error probably amounted to no more than 5 to 10 pct. In order to obtain readily interpretable data on thickening kinetics, it is essential that the diffusion fields of adjacent ?&apos; plates not be allowed to overlap. Calculations&apos;-&apos; showed that this condition is definitely not ful-

Jan 1, 1969

By H. Conrad, E. Stofel

The fracture behavior of 60-deg-oriented sapphire crystals was investigated for both tension and compression. Plastic flow on the basal plane was found to be a factor in reducing the tensile stress required to produce fracture in the temperature RECENT experiments1-&apos; have shown that single crystals of a alumina (sapphire) can deform plastically, particularly at temperatures greater than 1000°C. The effect of this plastic flow on the fracture behavior of sapphire was not established, but range 1100º to 1500ºC. Mechanical twins, both (0001) and (0111) types, were produced by compression in the temperature range 1100" to 1300°C. Cracks propagated more readily along the twin boundaries than in the nontwinned crystal. experiments with other ceramic crystals4&apos;5 have shown that plastic flow can initiate cracks that lead to catastrophic failure. This suggests by analogy that plastic flow might also be an important factor in the fracture of sapphire crystals. A recent experimental investigationS undertaken to determine the mechanism of plastic flow in sapphire provided an opportunity to study the type of fracture produced after various amounts of plastic shear strain. The results of this study of fracture are reported in the present paper. During the course of

Jan 1, 1963

By A. H. Grobe, F. N. Rhines

AT elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible&apos; and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver Norbury2 and Leroux and Raub3 have reported internal oxidation (subscale formation) in alloys of silver with 2, 7 5, and 30 per cent of copper The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver&apos; Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detail 5,6 The present research confirms this anticipation The oxidation of a series of 20 dilute alloys of silver has been studied metallographically, some types of subscale not encountered among the copper alloys have been found Instances of internal oxidation in alloys of most of the metals of the I-b and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation, i e , they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them In a study of 4o alloys of these white metals only a few cases of internal oxidation have been found The probable reasons for this difference in behavior will be discussed presently EXPERIMENTAL PROCEDURE Silver -The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99 993 per cent Ag)* and the purest avail-

Jan 1, 1942

By G. Willard Quick, John R. Freeman

Jan 1, 1930

By C. O. Brawner

FACTORS THAT INFLUENCE STABILITY AND STABILIZATION METHOD The most effective stabilization method and design can only be developed if the cause(s) and mechanics of the slide are known. Therefore, it is important that the stability be evaluated by an engineer who has had extensive rock stability experience. The most important factors that influence stability are structural geology, ground water, blasting and the mining method or methods. Structural Geology - The majority of failures in rock slopes occur along discontinuities in the rock (joints, bedding planes, shear or fault zones, etc.). Therefore, on all surface mining projects, the development and maintenance of a comprehensive structural geologic mapping program should be a first priority program that is considered a part of the operations function. This program should include mapping all major features - faults, shear zones and through going joints. All structural features which could influence stability should be mapped and presented in a structural domain format for the entire mine (Canmet, 1977). Where planes, wedges or blocks will be undercut by the mining excavation, shear strength and strain to failure tests should be performed on the joints, fault gouge and gouge-rock contact surfaces. These tests must be performed on the samples in the direction of potential slide movement and must determine the range of peak and residual shear strength values. A preliminary assessment of friction angle can be obtained from measurements of failed surfaces in the field (Figure 1) or from core sliding tests (Barton, 1981). An assessment must be made of the past geologic history of

Jan 1, 1983

By Clarence Seyler

THE technical difficulties of cutting thin sections of coal for examination by transmitted light have hitherto restricted the investigation of the important subject of the microstructure of coal to the few possessed of the requisite skill and time. Apart from this, the method fails with anthracites and other coals rich in carbon, owing to the opacity of the material. Occasional use of the method of polishing a surface, with or without etching, has been made, but it was not until Winter1 published an account of his results that attention was seriously directed to the method. In May, 1923, a specimen of dull anthracite came into my hands; I tried Winter&apos;s method on it and the presence of megaspores and other vegetable structures became clearly visible. A preliminary notice was published by me;2 but I soon abandoned the use of Schulze&apos;s solution having found that a mixture of chromic and sulfuric acids gave far better results. In the meantime Turner and Randall, in America, had independently developed the method of flame etching, as applied to anthracite, with great success. I have spent a year studying the method of chromic etching, which gives excellent results with bituminous coals and cannels, as well as with anthracite. For anthracites, I have used the chromic method and Turner&apos;s method of flame etching, whichever was the more convenient or as a check one on the other. The polishing is done, according to metallurgical practice, by the use of a polishing machine and successively finer emery paper, followed by polishing on cloth moistened with a suspension of levigated green oxide of chromium, and a final rubbing on "selvyt" (a cotton velvet polishing cloth) moistened&apos; with alcohol. The polished sample is examined by reflected light with a 2/3 and 1/6 in. objective. Bituminous coals usually show considerable structure, and even anthracites show it faintly in places. The sample is then etched by immersion in a boiling solution made by adding 10 c.c. of concentrated sulfuric acid to 30 c.c of a saturated solution of chromic acid; enough water is then added to dissolve

Jan 3, 1925

By E. S. Bumps, W. F. Craig, M. Baeyertz

Metallurgists have looked at fractures macroscopically for many years and have evolved a vocabulary in which such words as "cleavage," "brittle," "shear," "ductile," "granular," "fibrous," and "silky" are used to describe the appearance of the fractured surface; but the meaning of these words in terms of metal structure is not well established. Observations of the structural meaning of "brittle" and "ductile" fractures in plate steels have been made, notably, by Kramer and coworkers1 and by Tipper.2 Grossman3 has studied the fracture of tempered martensite and combinations of ferrite and martensite. Notwithstanding these and other less concerted attacks on the problem, present understanding of fracture rests more on assumptions and logic than on experiment. It is the purpose of this paper to add a little to the growing fund of experimental observations of the nature of fractures in steel. The particular fractures to be described were obtained in conventional impact testing of an ordinary structural steel shape. In impact tests of the Charpy type, the specimens fail in a characteristic manner that depends on the steel and the temperature of testing. With ordinary structural and many other steel products, an appropriate range of testing temperature will cause a considerable change in the energy absorbed before fracture. This change is known as the energy transition and is accompanied, more or less closely, by alteration in the appearance of the fracture. At testing temperatures below the transition, the terms "brittle," "cleavage," or "granular" are used to describe the fracture; above it, "ductile" or "shear" are often used. Within the transition, the fracture changes from "brittle" to "ductile" by a progression in appearance, wherein the "brittle" portion of the fracture becomes restricted to a smaller and smaller central area of the fracture, as the testing temperature is raised and the "ductile" type of fracture is approached. All this is well known to metallurgists. The specimens under consideration are of the conventional V-notch Charpy type. They were taken from a structural steel shape of the following analysis: C Mn P S Si 0.17 0.46 0.009 0.029 0.03 Both longitudinal and transverse specimens were tested and examined. Fig 1 shows the energy values plotted against testing temperatures in the usual way. The curves for both longitudinal and transverse specimens show an energy transition, although the maximum energy absorbed at testing temperatures above the transition is greater in the case of the longitudinal specimens. Fig 2 illustrates the changes in the macroscopic appearance of the fractures that are associated with the energy transitions shown in Fig 1. Macrographs of the fractured surfaces of the specimens have been identified with the fracture ratings at intervals on each fracture curve. The numerical fracture rating on the ordinate of Fig 2 indicates the percentage of the area of each fracture that was considered to be "brittle" on macroscopic observation. Such rating of the fracture type in impact tests is now customary in many laboratories. Hereafter the specimens will be identified by reference to Fig 2 as 90 pct "brittle," 80 pct "brittle," and so on, in accordance with this macroscopic evaluation of the appearance of the fractured surface. The discussion of the fractures is divided into three parts. The first two are concerned with the mode of fracture and its relation to general structural features. As the same metal-lographic features occur in both longi-

Jan 1, 1950

By A. F. Giamei, E. J. Freise

A discussion of the various factors affecting the accuracy of volume fraction determination by the direct comparison X-ray diffraction method is presented. To minimize errors introduced by nonrandomization effects such as preferred orientation and large grain size, as well as errors introduced by statistical effects, an iterative mathematical analysis is introduced. This analysis is applied to all observable diffractio~ spectra from a given specimen by means of computer techniques and is statistically superior to the standard direct comparison technique which utilizes only one or tm sets of intensity spectra. The computer program also presents a graphical interpretation of- the results which enables the investigator to visualize and readily assess the scatter in volume fraction estimates caused by deviations from randomness. Finally, the iterative analysis is applied to experimental data collected from a series of plain carbon steels in both the as-received and spheroidized conditions to determine the volume fraction of cemen-tite present in each case. The results show markedly good agreement with chemical analyses for all spheroidized specimens. In theory, quantitative X-ray diffraction is a power-ful analytical technique for precise determination of the volume fractions of various phases present in a multiphase poly crystalline aggregate. There are two generally used methods; both utilize the fact that the intensity of a diffraction line of a particular phase is a function of volume fraction of that phase present in the aggregate. The more common method is the so-called internal standard technique where a known amount of standard substance is mixed with the aggregate containing the unknown. The resulting ratio of the intensity of a particular diffraction line of the unknown to the intensity of a diffraction line from the standard is used to find the weight fraction of unknown material by reference to the intensity data obtained from a previously prepared set of standards containing the same amount of standard material. The details of this technique are outlined in standard works on X-ray diffraction.&apos; The disadvantages of the technique are that it requires the use of powder specimens and that the powder mixture must be homogeneous near the surface to the maximum effective beam depth. The alternative technique is the direct comparison method in which the ratio of the intensity of a diffraction line of a phase in the aggregate to the intensity of a second-phase diffraction line yields the ratio of the volume fractions of each phase present. This method has been applied most extensively to the determination of the percentage of retained austenite in martensitic steels and to determining the amounts of hcp and fcc allotropic modifications in pure cobalt5 and the amounts of hexagonal and rhombohedra1 modifications in graphite.8 This method is applicable to bulk as well as powder aggregates and is the technique which will be considered in the following text. It is the purpose of the present communication to show that by combining the results of X-ray diffrac-tometry with the use of high-speed digital computers the results of the direct comparison quantitative X-ray analysis technique can be optimized by using all of the data available on a diffraction pattern. THEORETICAL DISCUSSION In optimizing any quantitative X-ray diffraction experiment, the problem of accuracy vs time to collect and analyze the experimental data arises. For any method to be practical, it is required that both experimental and analytical procedures are reasonably short. In most of the previous work performed by the direct comparison method, intensity data from only one or two sets of peaks were used to calculate the volume fraction of phases present in the aggregate. Consequently, rather long-time experimental measurements are required to assure that the intensity data are sufficiently accurate to justify the use of one or two sets of data. By using computer techniques to analyze the experimental data it becomes feasible to use all of the available data on a diffraction pattern. By so doing, the time spent in measuring any one diffraction maxima can be appreciably reduced. Although this results in poor counting statistics for any one maxima, the number of data points available for analysis is greatly increased. Based on the above discussion, it will be assumed that a continuous scanning counter-diffractometer technique will be used to collect intensity data from a two-phase mixture. The integrated intensity of the ith diffraction line from the a phase in the aggregate is given by:&apos;" where is the volume fraction of the a phase, The various quantities in Eq. [la] are angular independent while those in [lb] depend on the hkl spectrum of a particular phase. The meaning of the individual quantities in Eqs. [la] and [lb] are given in Appendix 1. It is convenient at this point to outline briefly the factors which will affect the measured intensity of any one hkl spectrum. a) Extinction effects arise from two independent experimental conditions. Primary extinction arises from a high degree of crystal perfection and results in spectra having lower intensity than predicted by Eq. [I]. Any treatment, such as powdering, which reduces

Jan 1, 1968

By P. E. Baker

An experimental study of heat flow in steam flooding was carried out with steam displacing water in a plane-radial fluid-flow model. Temperature distributions in the model reservoir, overburden, and substratum were measured at frequent intervals during flooding by means of a fixed array of thermocouples. Heat losses to overburden and substratum and the division of heat between the steam and hot-water zones in the reservoir were calculated from the temperature data by performing numerical integrations over the appropriate volumes. Temperature profiles and heat distribution results are presented. Some results were (1) the fraction of injected heat that is lost to overburden and substratum, when expressed as a function of time, did not depend on injection rate; (2) a significant portion of the injected heat was contained in the hot-water zone ahead of and underlying the steam front in the reservoir. The division of heat between the steam and hot-water zones did depend on injection rate; and (3) considerable gravity override was observed. The experimental results are compared with those of several published theoretical studies of heat transfer in hot-fluid injection; approximate agreement on heat losses is found with some of the most idealized theories. A valid comparison cannot be made in regard to steam us hot-water zone; basic interpretation of the hot-water zone, in terms of a vertical steam front, is clouded by gravity override in the experiments. INTRODUCTION The experimental study reported here primarily concerns two problems of heat transfer in steam flooding that have economic and engineering importance. These are (1) the fraction of injected heat lost to the overburden and substratum, and (2) the division of the remaining heat between a zone containing steam and a zone of hot water at lower-than-boiling temperature. The volume of the steamed region, which has a direct effect on oil recovery, can be calculated readily from these results. Several valuable theoretical studies have been published on this problem, but no experimental tests of the theories have previously appeared. Tests were needed because the effects of the necessary simplifications in the theories could not be determined otherwise. The basic, untested theoretical problem is the effect of "decoupling" heat and mass transfer, and the resulting inability to include the effects of heat transfer and condensation on fluid flow. The theoretical problem solved so far has been a heat transfer problem in which fluid is present as a heat carrier and flows in a stipulated manner, either linear or plane-radial. The simplifications that have sometimes been made in regard to thermal conductivity by, for example, Marx and Langenheim,l Lauwerier2 and Thomas3 apparently do not have an important effect on heat loss calculations, although the results of the different methods disagree to a certain extent, as shown by Spillette4 and by Ramey.5 A recent paper by the author6 compared the results of experiments in hot-water flooding with several theoretical results and showed a rather poor agreement. It will be seen that the experimental heat loss results for steam flooding, however, show acceptable agreement. These comparisons are discussed in a later section. EXPERIMENTAL APPARATUS AND PROCEDURE The system studied was one in which a sand pack, initially water saturated and at a uniform temperature, was flooded with steam at a constant rate and temperature. The temperature distribution in the "reservoir" and adjacent "strata" was measured with an array of thermocouples, and heat losses were determined from these measurements. The sand pack contained no oil because the only concern of the experiments was heat flow, and it was important to have the flow pattern as simple

Jan 1, 1970

By William N. Poundstone

What attracts young engineering graduates into the coal industry? What do these young men expect of a career in coal mining? These questions are often asked and debated by mining men throughout the country. In order to present a comprehensive answer to them, an opinion survey was conducted at West Virginia University&apos;s School of Mines among the junior and senior classes and part of the sophomore class. The tabulation of the answers showed that the present-day mining engineering student is an older, more mature individual as compared with former years and as compared with other present-day college students. The average age of the country&apos;s record-breaking 150,000 college graduates is 24 years. Among this year&apos;s mining graduates at West Virginia University, 78% are of this age or older. Over half (54%) of those polled in the survey are married. This is com- pared to 30% as a national figure. Of those married, 38% have one child and over 6% have two children. The entire senior group covered by this survey has averaged almost three years in the armed forces. An article entitled "The Class of &apos;49" in the June issue of Fortune magazine states that this year&apos;s class is the oldest, most mature class in history. Our survey indicates that the mining engineering students at West Virginia University are well above the average in this respect.

Jan 1, 1949

By Charles Eichrodt

THE ore that is being treated by the present plant lies between the leached zone, or capping, and the mixed sulfide and oxide zone. The principal copper minerals are chalcanthite (CuSO4.5H20), brochantite (CuS04 3Cu (OH)2) and atacarnite, (CuC12.3Cu (OH)2). There are, in addition, some other minerals such as cuprite and kröhnkite (CuSO4. Na2SO4.2H20). These minerals, with many others, occur in a greatly crushed granodiorite rock. Most of the copper-bearing minerals occur in the cracks and veinlets, but there are disseminated values and it is probably the relative proportion of these that accounts for some otherwise unexplainable variations in extraction. The entire mineralization of the ore is complex and varies with depth. This variation, the problems presented thereby, and the effect of various constituents of the ore will be taken up in detail. An analysis of an unweighted composite of the ore treated during 1927 follows:

Jan 1, 1930

By Galen G. Waddell

Several years of rock-burst research conducted by the U.S. Bureau of Mines in cooperation with the mining companies of the Coeur d&apos;Alene mining district, Idaho, in addition to progress made by others throughout the world, have led to a good understanding of the rock-burst problem. This paper describes conditions which have caused specific bursts, present capabilities of detecting stress buildup and bursts, control methods, and a suggested approach to analyzing any individual mine-burst problem. A rock burst is the sudden, violent release of stored strain energy in rock by some mechanism of rock failure, generally accompanied by expulsion of rock with consequent damage to the mine. A burst may be audible for only a few hundred feet, or on the surface it may sound like a sonic boom miles away. A Dictionary of Mining, Mineral, and Related Terms, U.S. Bureau of Mines (USBM)* 1968yand defines a burst as Bureau "That phenomenon which occurs when a volume of rock is strained beyond the elastic limit and the accompanying failure is of such a nature that accumulated energy

Jan 1, 1971

By R. Ebeling, M. F. Ashby

The paper is in two parts. The first develops the formulae and method needed to calculate the size, nu)nber, spacing, and volume fraction of hard or inert particles in the interior of a specimen from measurernents made on an extraction replica; throughout, the spread of- particle sizes in a single specimen is taken into account, and the extraction efficiency of the replica is considered. A method for testing whether the particles are randotnly distributed in space is described, and the spacing of randomly distributed particles is discussed. The second Part describes the application of the method to copper containing spherical particles of silica; the description includes an estimate of the errors involved, and a comparison of this with alternative methods. All parameters except uolume fraction can be determined satisfactorily, and the method offers advantages over other electron-,rzicroscopic techniques when dealing with hard particles in a softer matrix, or inert particles in a chem-ically less inert matrix. 1 HE experimental measurement of sizes and numbers of discrete particles of a second phase embedded in a matrix material from opaque, plane sections has been considered by many authors, notably by Fullman.&apos; It is assumed that, when the specimen is sectioned, the particles are also sectioned, so that the diameters of the circles of intersection of particles with the plane of the cross section ("surface diameters") are measured. It is difficult to derive the distribution of true particle diameters ("volume diameters") from measurements of the distribution of "surface diameters" on a plane section. The measurement of size and numbers of small second-phase particles by transmission electron microscopy through thin foils of matrix containing the particles has been described by Cahn and ~uttin~&apos; and by ~illiard.~ Because of overlap and the fact that particles which intersect the foil surface may be sectioned whereas those in the bulk of the foil are not, it is again difficult to measure the true distribution of particle sizes. The use of replicas for this sort of measurement has not been analyzed in detail. A replica made from an opaque cross section, thus replicating the circles of intersection of particles with the plane of section, is analyzed by Fullman&apos;s method and suffers from the same difficulties. Under certain circumstances, however, extraction replicas can be used, and offer a special advantage in that they make the determination of the true distribution of particle diameters particularly simple. It is the purpose of this paper to describe this extraction replica method. Consider the example of an alloy consisting of SiOz particles, whose mean diameter is about 1000A, dispersed in a copper matrix. When the alloy is sectioned and mechanically polished, the particles are not sectioned, because they are much harder than the matrix, and so will be either left in the surface or pulled out whole, and because the particle size is smaller than the abrasive size of even the finest abrasive. The particles are chemically inert in solutions which chemically etch or electropolish the matrix, so that chemical treatments do not section the particles either. (Experimental measurements of particle shape in this alloy confirm this—truncated particles are never seen.) Small, hard or inert, particles are therefore not sectioned when the specimen is sectioned and polished. An extraction replica taken from this polished surface shows the true "volume" diameter of each extracted particle; the distribution of diameters seen on the replica is the surface distribution of true "volume" diameters, and the volume distribution of true "volume" diameters is easily derived from it. The extraction replica method is not subject to the difficulties associated with sectioning of particles, and avoids the problem of overlap from which the transmission method suffers. The method is well-suited for studying hard particles in a soft matrix. Examples are provided by internally oxidized alloys, oxide-dispersion strengthened metals like T.D. Nickel, and carbides, nitrides, and strong intermetallic compounds in metals. It should be possible to adapt polishing techniques in alloys containing softer but inert particles to avoid sectioning the particles (say by electropolishing or etching). The method is tested and illustrated in Sections 8 and 9 by applying it to a dispersion of spherical SiO2 particles in a copper matrix. I) SYMBOLS Symbols are defined where they first appear in the text. Volume fractions of particles are denoted by the symbol f, particle diameters by x, center-to-center particle spacings by D, and numbers of particles by N. Mean particle diameters and standard deviations about these means are denoted by x and a. Both arithmetic (subscript A) and geometric (subscript G) means are employed. In this paper we measure the distribution of true diameters of particles which touch or pass through a random-plane section of the specimen. We may want to know the distribution of particle diameters in the

Jan 1, 1967

By H. I. Aaronson, H. A. Domian, G. M. Pound

The thernodyna,nics of I the Proeutectoid ferrite re-action ha1.e been investigated on the bases of three diifevent descviptions of the statistical thernzodynamics of interstitzal solid solutions. Especially at low ternperatures, substantial dijeretzces are found in the valltes of the extrapolated y/y + a and cr/a + y equilibriurn curls, and in the To- co7nposilion metastable eqliilibriunz curl-es thus co,npited. Although neither actiztity nor phase-diagram date are able to distingrish udeqiutely among the various descviptions, the statustics of Lacher, Fouller, and Guggenheinz provide the ?nost conplete epresentation az3ailable of the single carbon-ctrbon interaction energy (w) nzodel of an intevstitiril solid solution, and the relationships deduced frojrl then2 are accordingly pre.ferred. The findings tlzut w in austenite &apos;aries significu?ztly uith tenpevntrue and that phase-diagawr data arc not accurately con?palible usith eqcrctions deduced on the basis of actility infoation indicate, hou&apos;e13er, that a wzore cornplex nlodel of the uustenite , und pvobably of the .feyrite, solirl solutions will have to forn the basis of f4tuve statistical t1.eat1nents. Some suggestions for such a ruodel arc advanced. Althoug11 w represents a vepltlsio energy in austozite, it was found to corvcsporzd in ferrite to a binding energy, in qualitatit.e accord zc,itlz the internal-friclion results of Keefer and wert. ThE transformation of austenite to proeutectoid fer-rite is becoming recognized as an exceptionally useful vehicle for quantitative studies of the kinetics of phase transformations.&apos;" Reasons for this popularity include well-characterized microstructures which develop on a convenient scale with acceptable kinetics within a considerable temperature-composition region, the absence of great sensitivity to common impurities, and, especially. the availability of a unique wealth of the ancillary information indispensable for the quantitative interpretation of kinetic measurements, including phase diagram,3 crystallographies diffusivity,5 inter-facial energy,=17 elastiit," specific vlume, &apos;&apos;&apos; and ativity&apos;-&apos; data. Development of considerable amounts of additional thermodynamic information from activity data is of particular importance with respect to kinetic studies, since much of this information is needed in temperature-composition regions not directly accessible to presently available techniques for the measurement of equilibrium properties. A generally useful approach to the thermodynamics of solid solutions, which is of especial value in this situation, is based upon the formulation of the free energy of such solutions as a function of temperature and composition. The free energy of solid solutions has been resolved into many components. Particularly in the case of interstitial solutions, with which we shall be concerned in the present study, however, only the positional entropy component has been intensively studied. The other components are conventionally taken into account by fitting equations for the activity of the interstitial species or the temperature-composition path of phase boundaries, derived principally from positional entropy considerations, to experimental information on these quantities through adjustment of one or more constants in the equations. A number of studies of the thermodynamics of interstitial solid solutions have been made primarily on this basis,&apos;"25 but only Kaufman, Radcliffe, and cohenZ2 (hereafter KRC) and ener&apos;&apos;% ave applied the results of such studies to develop relationships for the thermodynamic quantities of interest in the austenite —- proeutectoid ferrite transformation. KRC made use of a model developed by cheil&apos;&apos; (on the basis of a previous study by ohansson&apos;), and subsequently rede-rived correctly by Speiser and retnak,&apos; in which a carbon atom is considered to inhibit occupancy of a certain number of its nearest-neighboring interstitial sites. schei120 determined the number of sites in austenite thus excluded by matching calculated and experimentally measured curves for the variation of carbon activity with the mole fraction of carbon. zener17 used a different approach. He assumed that the positional entropy of carbon is ideal both in austenite and in ferrite (i.e., no excluded interstitial sites), and included all other contributions of carbon in a temperature-independent "free-energy change" accompanying the transfer of 1 mole of carbon between the two phases. This quantity was determined by "pinning" an equation derived for the boundaries of the a + y region to experimental data on the compositions of these boundaries at a single temperature. In the present investigation, three different approaches to the thermodynamics of the proeutectoid ferrite reaction are examined comparatively: I) the method of Zener; 2) the model employed by KRC and predecessors; and 3) the more detailed statistical thermodynamic treatment of the same model developed by acher and Fowler and uenheim, &apos; in which the problem of overlapping regions of influence of individual interstitial atoms is resolved. In order to make these comparisons, it is necessary to undertake an extension of one aspect of Zener&apos;s method; since the Lacher- Fowler -Guggenheim (LFG) treatment has not been previously used in the present context, the necessary thermodynamic "superstructure" for this treatment will be developed in parallel

Jan 1, 1967