By Yamei Han, Jiang Du, Jinhui Peng, Mengbi Fu, Libo Zhang, Zhengfu Zhang

"A continuously pilot synthesis by microwave-heating was used in preparing the cathode material LiNi113Co113Mn11302 for Li-ion battery, which used Ni1/3Co1/3Mn1/3(0H)2 and LizC03 as raw materials. Decomposition of the raw materials and synthesis of LixNi113Co113Mn11302 would be fmished in single roasting process. In addition, using microwave-heating would reduce the reacting time largely. Furthermore, the yield of LixNi1/3Co1/3Mn1/302 synthetized in single roasting process was 50 kg. Meanwhile, the effects of Li:(Ni+Co+Mn) molar radio (Li:(Ni+Co+Mn)=l.06, 1.075, 1.09, 1.15) was studied in this paper. XRD, SEM and EIS were used in characterizing the cathode material. The results showed that the best Li:(Ni+Co+Mn) molar radio was 1.075. It was found that the LiNi113Co113Mn11302 synthetized with Li:(Ni+Co+Mn)=l.075 had homogenous distribution of particles and ideal layered structure. The galvanostatic charge-discharge(O. l C, 2. 75-4.3V, vs. Lt /Li) tests showed that the initial discharge capacity of the LixNi113Co113Mn11302 was 159.5mAh·g-1, and the discharge capacity was 157.6mAh·g·1after10 cycles.IntroductionRecently, as the cobalt was expensive and the restriction of dynamic power, the commercial cathode Li2Co02 which was expensive, toxic, and high pollution had exposed its defects[1·2l. Since T.Ohzuku[3l first reported the layered LiNi113Co113Mn11302, this material had high reversible capacity and caused the attentions of researchers[4l. Its reversible capacity was l 60mAh/g and 200mAh/g in the voltage range of 2.75-4.3V[5-61. But for the present, preparing LiNiwCowMnw02 by traditional had lots of disadvantages, such as the long heating time, the high cost and the volatizing of lithium and so on[7-9l. According to these, traditional prepatation wasn't good for sustainable development and energy conservation."

Jan 1, 2013

By Satu Strömberg

Four different nickel concentrates were oxidized in a laboratory scale laminar flow furnace in simulated flash smelting conditions. The major nickel- and iron-bearing minerals in the con- centrates were pentlandite, violarite, gersdorffite, and pyrite and pyrrhotite, respectively. Thermal decomposition, ignition and oxidation behavior of nickel and iron sulfides were examined by using optical and scanning electron microscopy. General reactivity of the concentrates was monitored with sulfur removal which was most effective in violarite-based concentrate. Pentlandite-concentrates needed higher experimental temperatures for complete desulfurization and gersdorffite-based concentrate contained 5 - 10 % of the original sulfur even in the most oxidizing conditions studied (1 100°C, 50 vol-% 02). The reactivity of the iron minerals was found to depend on the other minerals present in the concentrate. In this paper, the observed re- action products and mineralogical changes are presented and preliminary conclusions of possible reaction mechanisms of nickel-bearing minerals are discussed.

Jan 1, 1997

By Wellington Pereira Inácio, Fernando Wypych, Sergio Neves Monteiro, Artur Camposo Pereira, Rafael Marangoni

"The efficiency by which an applied load is transmitted from the matrix to reinforcing fibers in a composite depends on the fiber/matrix adhesion strength. This is determined as the interfacial shear strength, IFSS, which may be measured by means of pullout tests that measure the force needed to pull a single fiber out of a block of material simulating the composite matrix. Different techniques are used to perform pullout tests. The objective of this work was to characterize the IFSS of sisal fibers embedded in epoxy matrix through the determination of the critical length pullout curves. As the main results, a relatively small critical length was found for the sisal fiber/epoxy pullout specimens, corresponding to a weaker IFSS. This was compared to other results applying different pullout techniques. Scanning electron microscopy observation identified the mechanism responsible for the weak sisal fiber adhesion to the epoxy matrix.IntroductionSynthetic fiber reinforced composites is today one of the most successful class of materials with increasing industrial applications from house appliances to large airplanes like the modem Airbus 380. However, environmental issues are revealing serious drawbacks related to the fabrication, use and post-use discard of these composites. For instance, the thermoset polymer composite reinforced with E-glass fiber, known as ""fiberglass"" has an energy-intensive fabrication associated with a surplus emission of C02, which is responsible for global warming [1]. Moreover, the glass fiber is considered toxic and also causes long term pollution after being discarded."

Jan 1, 2011

By Yoshio Waseda

A laser flash method has been applied to obtain the thermal diffusivity values of Zr55Al10Ni5Cu30 alloy in the liquid, glassy, crystallized and supercooled liquid states. The electrical resistivity of this particular alloy was measured in the glassy, and crystallized states by a direct current four probe technique. A specific heat of Zr55Al10Ni5Cu30 alloy was also determined by a differential scanning calorimeter in the glassy state. On the other hand, thermal diffusivity values for two alloys of Zr60Al15Ni25 and Zr65Al7.5Cu27.5 were measured in the crystallized and liquid states. The thermal diffusivity values of three Zr-based alloys in the liquid state are summarized in the linear equations with positive temperature dependency and it is noted that the lower the thermal diffusivity values of Zr-based alloys at liquidus temperature, the lower the critical cooling rate to obtain metallic glass phase becomes. The thermal diffusivity values of Zr-based alloys were compared with those of Pd-based alloy case. These results suggest that thermal diffusivity of alloy liquids might be an indicator of the glass-forming ability of Zr-based and Pd-based alloys.

Jan 1, 2006

By Larry M. Southwick

Considerable process and equipment development and analysis were conducted during design of Freeport Sulfur's laterite nickel facilities in the late 1950's. These covered ore concentration at Moa Bay, Cuba, and concentrate refining at Port Nickel, Louisiana. Both facilities utilized acid pressure leaching and product refining steps that were similar to those later used elsewhere in the laterite processing industry. Unfortunately, developments in Cuba removed the Moa Bay facilities from Freeport control. This deprived the project of a start-up that would have allowed thorough resolution of difficulties and a quicker attainment of production capacity. This meant lost opportunity to positively prove and complete the technology when optimum resources and staff were available. This paper reviews the original rationale of how design was developed via laboratory, bench scale and pilot studies by Freeport Sulfur. Some later operating problems will also be discussed. This case is unusual, but the lessons learned may be instructive in the application of difficult and complicated technologies, as well as the need to understand and retain access to the original development and design activities Keywords: Moa Bay, Freeport Sulfur, Port Nickel, acid pressure leaching, pilot plant, pachuca, Chemical Construction, pressure letdown, cobalt, titanium

Jan 1, 2004

By Jing Zhan, Chuanfu Zhang, Yonglin Yao

"The Ni/Co arbitrary ratios of fibrous precursor were investigated during coordinated coprecipitation by changing the precipitating medium. The results show that the original molar ratio ofNi2+ to Co2+ in reaction solution can be maintained in the coprecipitate at pH'.'05.0 and the coprecipitate is single phase solid solution using water and water-X precipitating medium. But the original Ni/Co ratios are no longer kept and composition of the coprecipitate is not uniform at pH>5.0 in water precipitation medium. In order to obtain the precursors with the required morphology and accuracy Ni/Co ratios, the optimum conditions of fibrous precursors were chosen as follows: ammonia used as complex agent and pH adjustor, water-X solvent as precipiting medium, oxalate as coprecipitated agent, 8.0-8.4 for pH value, 50-70°C of reaction temperature, 0.5-0.8 mol/L of initial nickel and cobalt salt concentrations and excesses of oxalic acid of 10% - 20%.IntroductionNi-Co alloy as an important transition metal alloy with high mechanical strength, good anti-deformation, corrosion resistance, thermal conductivity, thermal stability, electrical conductivity, electrical contact, and special magnetic properties indicates that it can be used as high-temperature catalyst, special magnetic material, high-temperature electrochemical devices, and so on [1-6]. An ideal composite powder should have an appropriate stoichiometric ratio, good uniformity of chemical composition, appropriate phase, low impurity content and small particle size [7]. Similarly, the composition of nickel-cobalt alloy powder has an important impact on its crystal structure, properties and applications. Guo[8] found that magnetisms of CoxNi1-x such as magnetic anisotropy, curie temperature, and the shifts of the spin steering are very sensitive to the composition of alloy powder."

Jan 1, 2013

By Torma A. E.

Biotechnological processes are considered to be cost effective especially for situations where the recovery of metals from 'Very large volumes containing trace metal concentrations (less than 10 ppm) is concerned. Microorganisms, alive or dead, or their products can be highly efficient and selective biosorbents for metal concentration. It is important that the metal bound to the biosorbent can be stripped by suitable agent(s) and regenerated for repeated use. The stripped solution should be concentrated enough to be introduced into the common metal recovery circuit. The industrial acceptance of biosorption processes is dictated by increased competitive advantage over other processes. This paper reviews the pertinent literature?, regroups the information, and points out future possibilities for the mineral and metal processing industries.

Jan 1, 1992

By Jan Vrestal, Josef Tomiska, Pavel Broz

"Thermodynamic investigations on fcc solid ternary Fe-Ni-Cr alloys have been performed by means of the computer-aided Knudsen cell mass spectrometry. Ternary T.AP.-series (Thermodynamically adapted power series) are used for the algebraic representation of the thermodynamic excess properties. At 1650 K the molar excess Gibbs energy GE is negative over the whole field of stable fcc phase. The molar heat of mixing HE is exothermic in the predominant part of the fcc phase field. Only between the section with a constant ratio of mole fraction Xcr/XNi = 0.64 and the fcc phase field boundary the HE values are slightly endothermic. The results of this work can be used successfully for phase diagram calculations.IntroductionThermodynamic investigations on multicomponent alloy systems such as the Fe-Ni-Cr ternary system including the three binary boundary systems are very time-wasting and usually beset with considerable experimental difficulties. Additionally, the required experimental equipment is very expansive and the obtained results are not always satistying. Therefore it is understandable that many phase diagram calculations are based only on few experimental values of the molar excess free Gibbs energy GE. Consequently, Kundrat and Elliott [1] as well as Hillert and Qiu [2] used in their reassessments of the phase diagram of the Fe-Ni-Cr system thermodynamic data mainly assumed and/or optimized by means of various reasoning.Lee [3] reported recently, a revision of the used thermodynamic description of the Fe-Ni liquid phase is necessary to obtain a better agreement with the experimental data on the bcc/liquid or fcc/liquid tie lines and liquidus temperatures in the Fe-rich region of the Fe-Ni-Cr ternary system than in the previous assessments. This is 'in full agreement with mass spectrometric investigations of Fe-Ni alloys in the liquid and in the fcc solid phase, published earlier [4,5]. Indeed, phase diagram calculations based upon the molar excess free Gibbs energies GE obtained in these studies yield liquidus and solidus lines in excellent agreement with experimental phase diagram data [5]. Nevertheless, these experimental data have not been considered later on any more, not even in the revision by Lee [3]."

Jan 1, 1996

By Augusto Viana Leandro Teixeira

Rare Earth Elements (REE) are fundamental for modern life products and green technologies. Supply constraints and the price peak of 2011 boosted intensive research for alternatives for processing and separation. Complex monazite- type, rare earth ores usually contain high acid consumption impurities, such as iron and aluminum, and radioactive thorium in their composition. These impurities are not removed by conventional concentration processes due to fine, micro-level association between the REE carrying minerals and the gangue minerals. This work presents a selective process route for REE extraction from iron-rich, monazite ores. The process involves sulfation by addition of concentrated sulfuric acid and pyrohydrolysis at temperatures of approximately 700–750 °C. Experimental results show REE extraction higher than 70% and low iron (below 5%) and thorium extraction (below 10%). A method based on thermogravimetric analyses was shown to be adequate to predict the behavior of a given ore sample in the sulfationselective pyrolysis-leaching process.

By Kimio Itagaki

The distribution ratios of Ag, Pb, As, Sb and Bi for the Cu2S-FeS or Ni3S2-FeS matte / FeOx SiO2, FeOx-SiO2-CaO or FeOx-CaO slag equilibration in a MgO crucible were determined experimentally at 1523~1573K under controlled partial pressures of S2 and O2 at given PSO2 of 10.1, 50.7 and 101.3 kPa (0.1, 0.5 and 1 atm) and be observed dependency of distribution ratio on the matte grade, SO2 pressure and slag basicity were analyzed on the basis of thermodynamics,

Jan 1, 2003

By Guanghui Li

Nickel pig iron (NPI), used as a substitute for electrolytic nickel, is able to reduce the production cost of stainless steel greatly. Aiming for preparing NPI from nickeliferous laterite ore, a pilot-plant scale test of coal-based rotary kiln direct reduction of laterite ore was performed and reported in this study. In this process, the ground laterite sample (18.85% TFe and 1.52% Ni) mixed with additives, pulverized coal and binder was briquetted into briquettes with the size of 40mm×40mm×31mm, laterite ore briquettes and reducing coal were charged into a rotary kiln with the diameter of 1.6 m and the length of 16 m, for a retention period of 6~7 hours, in which reduction section temperature was ranging from 950~1050 oC. The reduced briquettes were water quenched, ball mill ground and beneficated via low intensity magnetic separation. A magnetic concentrate, Ferronickel powder, with 86.9% TFe and 8.0% Ni was obtained, and the corresponding magnetic recovery of iron and nickel are 75% and 96.3%, respectively.

Jan 1, 2014

By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-Si02 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [m(Mgo)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, m(Fe)/m(SiO2) is 1.1-1.4 and the temperatures are within 1473?1773K, the slag viscosities increased with the increase of m(Mgo) and m(Fe)/m(sio,). When m(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When m(Mgo» 10%, the temperature should be kept above 1633K. When the content of MgO is higher, a lower viscosity slag ean be produced by decreasing the ratio of m(Fe)/m(sio,). The appropriate ratio of m(Fe)/m(sio,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Y. Pokhvisnev, S. Vandariev, A. Yatshenko-Juk, V. Valavin, V. Romenets

The technology of the liquid-phase reduction process known as Romelt was developed in the Moscow Institute of Steel and Alloys in 1979. The pilot plant was constructed at the Novolipetsky Steel Works (Russia) in 1984. Investigations into processing zinc-containing blast oxygen furnace dust and slag from the Lead and Zinc Works at the pilot Romelt plant proved the perspective of using this technology for processing zinc and lead-containing materials. In this article, the description of Romelt technology, basic technological information of trials at the Romelt plant using zinc-containing materials, compositions of charging materials, metal, slag, gas and dust are presented. The influence of flue gas composition on the composition of zinccontaining dust is shown.

Jan 1, 2000

By Dong Liang, Honggang Zhong, Zhenxing Yin, Qijie Zhai

"2507 super duplex stainless steel (SDSS) has been widely applied in a marine environment, attributing to its excellent pitting corrosion resistance and mechanical properties which are particularly determined by the nitrogen precipitation behaviors and volume fraction of ferrite. In this paper, various cooling rates were obtained by applying four different moulds with the common gating system. By which the influence of cooling rates on nitrogen precipitation behaviors and the ferrite fraction in cast 2507 SDSS was comparatively investigated. The results showed that nitrogen porosity could easily precipitate in cast 2507 SDSS under standard atmospheric pressure. The number of nitrogen holes increased with decreasing the cooling rates, and the holes mainly distributed in three zones, i.e. the interface between the horizontal and vertical columnar grains, top vertical columnar grains and the final solidification region. Additionally, higher ferrite fraction was obtained with lower cooling rates.IntroductionDuplex stainless steels (DSS) have a dual-phase microstructure consisting of ferrite (d) and aus-tenite (?). Due to the combined advantageous properties of d and ? phase, their application rapid-ly increased in industry [1, 2]. Super duplex Stainless Steel (SDSS) is the third generation of du-plex stainless steels, of which the alloy elements Cr, Ni and N content are higher than the stand-ard 2205 DSS. Because it has high contents of alloy elements, the SDSS has better mechanical properties, and its pitting resistance equivalent number (PREN) reached a point 43. Hence SDSS has been used in petroleum chemical industry, the marine equipment and harsh corrosion environments [3]. SDSS contains ferrite stabilizing elements, such as Cr, Mo and Si, and austenite stabilizing elements like Ni, Mn and N [4]. Many researchers have studied the effects of these elements on the stabilization of d and ? phase and the ratio of the two phases. High nitrogen con-tent is another prominent feature of SDSS. Nitrogen addition to SDSS is very effective for improving its mechanical properties [5] and corrosion resistance [6], such as pitting resistance in NOx environment. To increase the nitrogen content in steels, a lot of work had been done. N. Nakamura and S. Takaki [7] examined the behavior of nitrogen absorption in Fe-23Cr alloy powder by sintering in nitrogen gas atmosphere, they found nitrogen content easily up to 1.0 wt. %. Using devised NH3 gas injection system, W. Park et al. [8] successfully produced austenitic Fe–23.5Cr alloys containing over 3 wt. % of nitrogen. Further-more, W.P. Tong et al. [9] stated that nitrogen percent was extraordinary high (about 10 wt. %) in pure iron plate. However, the above methods are difficult to be applied to large-scale industrial production."

Jan 1, 2012

By Kimio Ilagaki

The distribution ratios of Ag, Pb, As, Sb and Bi for the Cu2S-FeS or Ni3S2-FeS matte I FeOx-SiOl, FeOx-Si02-CaO or FeOx-CaO slag equilibration in a MgO crucible were determined experimentally at 1523 ~1573K under controlled partial pressures of S2 and 02 at given PS02 of 10.1,50.7 and 101.3 kPa(O.I, 0.5 and I atm), and the observed dependency of distribution ratio on the matte grade, S02 pressure and slag basicity were analyzed on the basis of thermodynamics.

Jan 1, 2003

By John R. FitzPatrick

The separation and purification of uranium from either nitric acid or hydrochloric acid media tan be accomplished by using either solvent extraction or ion-exchange. Over the past two years at Los Alamos, emerging programs are focused on recapturing the expertise required to do limited, small-quantity processing of enriched uranium. During this period of time, we have been investigating ion-exchange as a method for extraction/purification of uranium from acidic media. In addition, waste stream polishing is associated with this effort in order to achieve more complete removal of the uranium prior to recycle of the acid. Extraction chromatography has been demonstrated&apos; to further polish the uranium from both nitric and hydrochloric acid media thus allowing for a more complete recovery of the actinide material and creation of less waste during the processing steps. We will discuss contact experiments for evaluation of eleven different resins for uranium removal from nitric acid, the evaluation (again by contact experiments) of uranium elution from the ion-exchange media by various chemicals, and small-scale experiments for the removal of 235U from nitric acid. Larger-scale (100-gram) flow experiments using depleted uranium, were done after the small-scale evaluation Of the selected resin. A discussion is also included concerning the shortcomings of the contact experiments and how the flow experiments were modified in order to overcome these problems. We will also discuss the application of ion-exchange for some specific process needs at Los Alamos Contact experiments were used to evaluate some commercially available solvent-impregnated resins in addition to evaluation of several resins of this type synthesized in our laboratory. These experiments&apos; involved both nitric and hydrochloric acid media. The data from these experiments will be used to determine the column size and&apos; amount of resin required to polish the waste stream produced by the ion-exchange process described above. Small-scale flow experiments will be described and data given on the mass balances achieved using this two step process. Future work for evaluation of new ion-exchange and solvent-impregnated resins as well as the search for new eluants will be discussed. Other future experiments for both processes, including large-scale experiments, will be discussed in detail.

Jan 1, 1996

By Evgueni Jak

Pyrometallurgy is an important sector of modern industrial society actively participating in solving current environmental, economic, materials scarcity and other challenges. Recent advances in analytical methods, experimental techniques, thermodynamic, phase equilibria and process modelling tools provide new opportunities to increase the productivity of pyrometallurgical reactors, the treatment of complex feeds and metal recoveries. Fundamental theoretical models can now be used to make a significant next step towards the development and implementation of computerised models describing real industrial processes—Virtual Reactors, and computer-aided smart-decision-making systems that may be called Pyro-GPS by analogy to GPS; these developments can facilitate knowledge-based improvement and optimisation strategies. The implementation of these improvements require ongoing collaboration between researchers, industry and government.

By Michael B. Mooiman, David J. Kinneberg, Philippe Cettou, Leo W. Simpson, Pierre Ramoni

"The demand for high purity precious metals began with certain industrial applications having uncompromising requirements for quality and performance. As industrial uses proliferated and as the jewelry industry became increasingly sophisticated, the demand for high purity gold has reached the point where 99.99% is now the standard in the marketplace. A similar evolution is expected for other precious metals.In this paper, we examine both the production and use of high purity precious metals, specifically gold, silver, platinum and palladium. After defining what is meant by ""high purity"", we discuss the various analytical techniques used for measuring impurity concentrations. Next, we review process strategies employed by extractive metallurgists to produce high purity precious metals. Lastly, we describe some of the principal applications for high purity materials including thick films, thin films, bonding wire, thermocouples and jewelry manufacture.Precious metals have unique physical properties that, despite their expense (and the ever-continuing search for more economical alternatives), make substitution difficult if not impossible. These physical properties are dramatically affected by small concentrations of certain impurities. As long as manufacturers continue to demand quality and performance, there will be a need for high purity precious metals.IntroductionIn the precious metals industry, the qualifier ""high purity"" describes any specification over and above commodity grade. High purity specifications delineate lower limits on overall metal purity or upper limits on individual impurities or both. Sometimes, if these special requirements become commonplace, either because of improved refining technology or because of market pressures, yesterday's ""high purity"" material becomes tomorrow's commodity. This transition is now occurring with gold bullion and probably will soon occur with platinum and palladium as industrial use of these materials grows."

Jan 1, 1998

By Patrik Fredriksson

Thermodynamic data concerning FeO-containing slags is of importance in ladle refining of steel. With a view to generate a set of reliable and self-consistent thermodynamic data for these slags, experimental determination of the activities of FeO in binary and ternary slags was carried out using the gas equilibration method involving CO-C02-Ar gas mixtures at steelmaking temperatures. The slag samples in Pt crucibles were quenched after the equilibration and subjected to chemical analysis. The thermodynamic activities of "FeO" in the slags were calculated from the experimental data. The results are incorporated into a thermodynamic description of silicate melts in the present laboratory. The model is based on a Temkin-Lumsden approach and is able to compute the thermodynamics of higher order systems from the lower order ones.

Jan 1, 2003

By Katja Reinharter

Arsenic can be found in different sulfidic copper concentrates and residues, which for several years have commonly been used in copper metallurgy, as the “arsenic-free” resources are getting rare. Due to the high toxicity the removal of arsenic in the copper smelting process is a very important topic. The typical chemical slag and sulfur attack on the refractory material is getting enhanced by the presence of arsenic. This work deals with post-mortem investigations of a magnesia-chromite brick and castable used in copper smelting furnaces showing an additional and increased chemical attack by arsenic. The knowledge on the wear behaviour is not only based on a detailed chemical and mineralogical characterization, but also on thermochemical FactSageTM calculations, which are carried out on provided post-mortem samples. Post-mortem investigations on used refractory materials represent an important prerequisite for the product development, as well as for special engineered lining concepts to support our customers.