By Homer F. Staley, C. P. Karr

The casting alloy 88 copper, 10 tin, 2 zinc, commonly known in England as Admiralty metal and in this country as Government bronze, gun metal, or Naval Department composition G, has, at its best, many valuable properties. However, its physical properties are known to vary widely with slight changes in method of manufacture of the castings, such as slight variations in composition, variation in pouring temperature, kind of mold used, method of pouring and gating of molds, size and shape of castings, amount and kind of heat treatment, and so forth.' The microstructure of castings made from this alloy is influenced by slight variations of composition, rate of cooling, and kind and length of heat treatment. This is best understood by reference to the equilibrium diagram. The part of the diagram in which we are interested and the effect of the thermal equilibrium relations on the physical properties of the alloy 88 copper, 10 tin, 2 zinc, have been discussed by Hoyt, Campbell, Primrose, and Rawdon.2 In Fig. 1 is given the equilibrium diagram of the copper-tin alloys. Briefly stated, the relations of composition and temperature changes are as follows. Compositions between A and a consist of but one constit ent—the a bronze, which is a solid solution of copper and tin, rich in copper. On cooling from the molten state these compositions gradually crystallize, at temperatures above 790°, into a mass of interwoven treelike crystals or dendrites. The cores of the dendrites are rich in copper and the percentage of tin gradually increases as the surfaces are approached. AS cooling progresses, after a11 the metal has crystallized, no further changes occur in the crystals other than diffusion within the crystals, which tends to erase the dendritic pattern and to render the structure more homogeneous. * Metallurgical Ceramist, U. S. Bureau of Standards, Associate Physicist, U. 8. Bureau of Standards. A. D. Flinn: Iron. Age (1915) 96, 1292-3. C. P. Karr: U. S. Bureau of Standards Tech. Paper 59, Pt. 1. S. L. Hoyt: Enging. (1913) 96, 667-7, 704-5. William Campbell: Trans. Am. Inst. Met. (1912) 6, 158-172. H. S. Primrose: Metal Ind. (1916) 14, 202-4. H. S. Rawdon: U. S. Bureau of Standards Tech. Paper 59, Pt. 11.

Jan 1, 1921

By Marcus A. Grossmann

The Institute has established this lectureship to honor the memory of a great American metallurgist, one whose fame has continued long after his passing. As one scientist recently stated it, "All metallurgical texts gradually become outdated and outmoded, except those of the great Henry Marion Howe." It seems fitting, then, that, once every year, we shouId review, in his honor, some aspects of the science in which he was such a distinguished leader, and also discuss any new data that may help to clarify our concepts. It is my privilege, for which indeed I express the deepest appreciation to this Institute, to offer for consideration a few thoughts on the toughness and fracture of hardened steels. Before proceeding to the data, I wish to express my great indebtedness to many associates whose stimulating discussions, generous contributions of data and cooperation in experiments are gratefully acknowledged. (But I wish to absolve them of any blame that may arise from the way in which their discussions and data have been used!) First, Dr. Edgar C. Bain, Vice President, Carnegie-Illinois Steel Corporation, whose amiable but merciless criticisms and always constructive and thoughtful suggestions help unfailingly to guard against pitfalls. Then to associates at Gary Steel Works, especially Mr. H. B. Wishart, Mr. W. K. Smith and Mr. V. Elliott, for great assistance in securing data. Also to Col. C. H. Greenall, Director of Laboratories, Frankford Arsenal, and his metallurgical staff, including Messrs. J. K. Desmond, H. Markus, D. F. Armiento, H. Rosenthal and Henry George, for numerous data and illustrations. Further to Dr. J. R. Low and Dr. M. Asimow, for helpful discussions of effects of states of stress during deformation and rupture, to Mr. J. M. Hodge for discussions and data, to the staff of the U. S. Steel Corporation Research Laboratory for advice and data, and to the Metallurgical Staff at Duquesne Steel Works. The individual acknowledgments will also be found under illustrations. Acknowledgment is also due to Mr. S. C. Snyder for incredibly meticulous scrutiny of manuscript. To all of these, grateful thanks. Introduction The discussion to be offered here will deal with quench-hardened steels only, and may perhaps be considered under three headings: 1. It was found that, when ferrite was precipitated in the (prior austenite) grain boundaries of hardened steel, the notch-bar toughness was much less than in pieces fully hardened. The fracture took place in the ferrite, and the loss in toughness is attributed to the lower cohesive (cleavage) strength of the ferrite, as cornpared with martensite. 2. When notch-bar impact test pieces of quenched and tempered steels were examined as to their mode of fracture, it

Jan 1, 1947

By Marcus A. Grossmann

The Institute has established this lectureship to honor the memory of a great American metallurgist, one whose fame has continued long after his passing. As one scientist recently stated it, "All metallurgical texts gradually become outdated and outmoded, except those of the great Henry Marion Howe." It seems fitting, then, that, once every year, we shouId review, in his honor, some aspects of the science in which he was such a distinguished leader, and also discuss any new data that may help to clarify our concepts. It is my privilege, for which indeed I express the deepest appreciation to this Institute, to offer for consideration a few thoughts on the toughness and fracture of hardened steels. Before proceeding to the data, I wish to express my great indebtedness to many associates whose stimulating discussions, generous contributions of data and cooperation in experiments are gratefully acknowledged. (But I wish to absolve them of any blame that may arise from the way in which their discussions and data have been used!) First, Dr. Edgar C. Bain, Vice President, Carnegie-Illinois Steel Corporation, whose amiable but merciless criticisms and always constructive and thoughtful suggestions help unfailingly to guard against pitfalls. Then to associates at Gary Steel Works, especially Mr. H. B. Wishart, Mr. W. K. Smith and Mr. V. Elliott, for great assistance in securing data. Also to Col. C. H. Greenall, Director of Laboratories, Frankford Arsenal, and his metallurgical staff, including Messrs. J. K. Desmond, H. Markus, D. F. Armiento, H. Rosenthal and Henry George, for numerous data and illustrations. Further to Dr. J. R. Low and Dr. M. Asimow, for helpful discussions of effects of states of stress during deformation and rupture, to Mr. J. M. Hodge for discussions and data, to the staff of the U. S. Steel Corporation Research Laboratory for advice and data, and to the Metallurgical Staff at Duquesne Steel Works. The individual acknowledgments will also be found under illustrations. Acknowledgment is also due to Mr. S. C. Snyder for incredibly meticulous scrutiny of manuscript. To all of these, grateful thanks. Introduction The discussion to be offered here will deal with quench-hardened steels only, and may perhaps be considered under three headings: 1. It was found that, when ferrite was precipitated in the (prior austenite) grain boundaries of hardened steel, the notch-bar toughness was much less than in pieces fully hardened. The fracture took place in the ferrite, and the loss in toughness is attributed to the lower cohesive (cleavage) strength of the ferrite, as cornpared with martensite. 2. When notch-bar impact test pieces of quenched and tempered steels were examined as to their mode of fracture, it

Jan 1, 1947

By B. E. Grant

THE major metal mine operations of the United States Smelting Refining and Mining Company in Utah are in the Bingham area. The Company also owns and operates metal mines in the Ophir district, twelve miles south of Bingham, and in the Tintic district, 28 miles south of Ophir. Operations of the Company in the Park City area have been idle since early in World War II. These mining camps, lying at moderate elevations, serviced by railroads, hard-surfaced highways, in close proximity to mills, smelters, cities and towns, fertile valleys, winter and summer vacation areas, and airports are probably as favorably situated as any mining camps in the world. The Bingham district, known principally for its copper production from

Jan 1, 1948

By N. A. Gjostein

The real and apparent dependence of the surface self-diffusion coefficient, Ds, of gold on crystallo-graphic orientation has been investigated by isolated scratch smoothing and grain boundary grooving experiments. No systematic variation of Ds with orientation was found along the [100] zone. In view of the experimental scatter in these results, however, only aniso-tropy ratios, p, greater than -1.3 would be detectable. Anomalously low values of Ds were found on the [0ll] and [110] zones when the diffusion direction lies along (the scratch or grain boundary groove is perpendicular to) these zones. By comparing these results with a previous y plot study of gold, it is hypothesized that this is not an intrinsic diffusivity effect, but rather it results from a decreased driving force for mass transfer at orientations where the y-plot curvature is negative and appreciable in magnitude relative to y. The characteristics of this type of anisotropy do not appear sEVERAL investigations1-7 have dealt with the anisotropy of the surface self-diffusion coefficient, Ds, of metals as measured by the decay of single or multiple to be in agreement with the hypothesis of fast diffusion along ledges in the surface structure. In certain cases the Fourier method of determining Ds, described in Paper I of this series9 was compared with the second moment analysis in order to determine whether or not the method of analysis affects the anisotropy ratio. While the type of analysis does influence the magnitude of the anisotropy ratio, this effect is not associated with the shape of the profile, but rather is connected with the iterative volume diffusion correction used in conjunction with the second moment analysis. It is further demonstrated that the volume diffusion correction can be too large by either method when the y-plot curvature effect is large. Certain orientations exhibit an unusual temperature dependence of Ds ; this is discussed in terms of the y-plot curvature effect and/or the influence of impurities on Ds . scratches in the surface. Depending on the system investigated, both large1"3'6'7 and small4'5 anisotropies in Ds have been found. Although adsorbed impurities undoubtedly play an important role in determining the magnitude of the anisotropy,8 there are other factors that can give rise to an apparent anisotropy in Ds, thus obscuring the true nature of an intrinsic anisotropy in

Jan 1, 1968

By C. C. Hatch, C. R. Larsen, A. L. Mular

INTRODUCTION As part of a general project to simulate a concentrator, the Brenda Mines Limited secondary crushing plant, located near Peachland, B. C., was sampled during the summer/winter of 1975 and during the summer of 1978 to develop a digital crushing plant simulator specific to the Brenda operation. The purpose of this simulator was to study the influence of manipulable process variables on important responses, to permit study of alternative circuit configurations if desired and to perform off-line optimization. This chapter describes the methodology employed to develop the simulator (1,2) along with typical applications thereof. SECONDARY CRUSHING PLANT FLOWSHEET Figure 1 is a schematic diagram of the Brenda Mines Ltd. secondary crushing plant circuit. The 41,000 tonne coarse ore stockpile(a) is -17.8 cm oversize (3B belt) from two 2.4 m x 6.1 m double deck vibrating screens (not shown). The screens are fed by 2 conveyor belts operated in series with two 198 cm apron feeders that handle discharge from a 152 cm x 226 cm primary gyratory crusher(520 KW). The primary crusher (not shown) treats up to 2725 tonne/hr of run of mine ore. Minus 1.9 cm undersize from the primary screens (#19 belt), referred to as the primary fines, joins secondary screen undersize (#18 belt) for conveyance to fine ore bins (not shown). Feed from the coarse ore stockpile is transferred by means of vibrating feeders and two 120 cm conveyors (#6 and #7) to transfer belts #8 and #9 (Figure 1). The belts feed two secondary 2.1 m standard heavy duty cone crushers (bl and b2). Each crusher is equipped with a modified coarse mantle liner and a standard coarse bowl liner. Mantle throw is 9.2 cm; nominal close side set is 3.2 cm. Crusher .countershafts (443 rpm) are driven by single 260 KW synchronous motors (710 rpm). Discharge from the secondary cone crushers joins discharge from four 2.1 m tertiary heavy duty shorthead cone crushers (fl, f2, f3 and f4). With the exception of the cavity (modified medium mantle liner and standard coarse bowl liner; close side set is nominal .84 cm) and motor (224 KW), these machines are similar to the secondary crushers. The combined discharge is transferred from a 183 cm conveyor to #14 belt which empties into a 1452 tonne secondary screen surge bin (c). Vibrating feeders beneath the bins feed five 2.4 m x 6.1 m double deck vibrating screens (dl, d2, d3, d4 and d5) sloped at 200 from the horizontal. The upper decks are punched plates with 2.7 cm x 7.6 cm slots. Lower decks are woven wire (1.27 cm diameter) sections with

Jan 1, 1982

By J. Hoover Mackin

The iron ore bodies of the Iron Springs district are replacement deposits of magnetite and hematite in Jurassic limestone around the borders of three intrusions of quartz-monzonite porphyry. Production in the period 1923-1965 was about 72,000,000 tons, nearly all of which was direct-shipping ore from open pits. The intrusions are laccolithic in form; all three were emplaced at the same stratigraphic horizon, which had been a zone of decollement gliding during the Laramide orogeny. The intrusions and associated volcanic rocks are post-orogenic. There was no change in the thickness of the limestone during the metallization. Comparison of the composition of the limestone and stratigraphically equivalent replacement ore indicates that, with every million tons of iron, there were additions of 40,000 tons of silicon, 20,000 tons of magnesium, and 10,000 tons of aluminum. The ore-forming fluid was derived from the exposed porphyry. The iron was first incorporated in hydroxyl-bearing mafics, which crystallized in depth and were carried upward in the magma that formed the hypabyssal intrusions. The mafic phenocrysts decayed deuterically in the new environment, releasing iron into the interstitial fluid of a consolidating crystal mush in the interior of the intrusions. Primary tension joints, which opened in areas of late intrusive distention, served as roots through which the ore-forming fluid was drawn from the crystal mush.

Jan 1, 1968

By G. M. Crosby

Seven mines with important production records in the Coeur d'Alene lie adjacent to the Gem stocks —the Frisco (Gem), Hercules, Interstate, Rex (Sixteen to One), Success (Granite), Sunset, and Tamarack. Old records are incomplete, but available data given in Table I show these mines have produced 10.550,721 tons of ore containing more than 50 million oz of silver, more than 1.5 billion lb of lead, and about 1 billion lb of zinc (approximately 1.25 million tons of lead and zinc combined). Average ore grade is 4.8 oz of silver per ton, 7.2 pct Pb, and 4.6 pct Zn. This impressive production represents about 12 pct of the District's yield. At present metal prices, with modern beneficiation, the gross value would be more than $400 million. THE GEM STOCKS The Gem stocks, considered to be outliers of the Idaho batholith of Late Cretaceous age, are located in the northern half of the Mullan quadrangle, and extend from the town of Gem, Idaho, along a strike of N30°E for a distance of approximately five miles. They occur as two major masses of monzonitic rocks commonly referred to as the North stock, which covers an area of 1.1 sq miles, and the South stock, which covers 2.6 sq miles. The areal pattern is roughly club-shaped, the North stock representing the handle and the South stock the head of the club. Two and a half miles west and five miles northeast are two groups of smaller stocks, isolated from the main masses but of the same general rock type. This discussion is limited for the most part to the North and South stocks. At the north end, where the intrusion is about 3200 ft wide, the walls are about parallel and dip very steeply west. At the south end, where the mass is about 7000 ft wide at surface, the walls dip away from each other at moderately steep angles. An aeromagnetic survey' detects and outlines with surprising accuracy the two main stocks. as illustrated on the magnetic contour map (Fig. 2). Of particular interest is the location and shape of the magnetic anomaly representing the South stock. The anomaly is centered over the south end of the outcrop, and a westerly extension joins it with a smaller anomaly over the Dago Peak stocks. The latter anomaly, likewise, is located over the south end of the isolated stocks. This pattern suggests the intrusion has greater extent at depth to the south and west. Though correlation between the Dago Peak stocks and the larger masses is suggested, the controversial aspects of the Dobson Pass fault, which separates the two areas, casts doubt on a correlation. Topographically the monzonite stocks are ignored by the drainage pattern indicating these rocks, and the invaded rocks of the Lower Belt Series react similarly to erosion. The drainage patterns of Nine Mile and Canyon creeks cut indiscriminately across the monzonite-Belt contact, resulting in both valleys and ridges in the southern end of the intrusion. Nine Mile Creek traverses diagonally the entire five-mile length of the stocks. The monzonite rocks of the intrusion are referred to locally as granite, but granite is rare and the rocks comprise a wide variety of types. Their characteristics, described in detail by F. L. Ransome and F. C. Calkins,' are summarized by P. J. Shenon.' The principal rock type is coarse-grained, light gray, porphoritic monzonite containing black crystals of hornblende. Pyroxene, epidote, and titanite

Jan 1, 1960

By A. Vignes, J. P. Sabatier

A study of ternary diffusion at 1315°C in the Fe-Co-Ni system covering the entire ternary phase diagram has been carried out. Experimental values of the four interdiffusion coefficients DFeNico,DFeCoCo, DFeCoNi were computed at 33 points of the ternary diagram. The limiting values of these coefficients on the three sides of the ternary diizgram have also been determined. This set of data is presented as a contour map on the ternary isotherm for each of the four coefficients. Assuming that the Fe-Co-Ni system can be considered as ideal, the phenomenological coefficients Lk ij (with k = Fe) have been computed and the Onsager reciprocal relutions verified. It is shown that, in the Fe-Co-Ni system, the diffusion process can also be described by only two interdiffusion coefficients DFeFe and DCoNiFe, the second cross diffusion coefficient DCoFeNi being equal to zero and the second direct difusion coefficient being given by The values of the cross interdiffusion coefficients and of the Onsager coefficients are explained in terms of atomic mobilities of the three components with the help of a kinetic calculation due to Lane and Kirkaldy.8 It is shown that all the results are explained if the tracer difusion coefficients of the three components are such that DFe > DNi ~ DCo in complete agreement with experimental data on the three binary systems. DIFFUSION in a ternary alloy system is basically and significantly different from diffusion in binary alloys. In binary diffusion, there is just one independent composition variable and only one coefficient Dij is needed to describe the interdiffusion process. In ternary diffusion, we must allow for cross interaction between two independent species, and four interdiffusion coefficients are necessary to describe the transport process. Kirkaldy et al.1,2 have determined interdiffusion coefficients in the systems, Cu-Mn-A1 and Zn-Cu-Al. Guy and Leroy4 have reported intrinsic diffusion coefficients for the r phase at 1300°C of Co-Ni-Cr alloys as a function of composition using the analysis of Philibert and Guy.3 Interdiffusion coefficients were measured at three different compositions at 850°C in the single phase copper-rich corner of the Cu-Zn-Mn system by Dayananda and race.5 Zie-bold and Ogilvie6 have determined interdiffusion coefficients in the single-phase field of the Cu-Ag-Au system at 725°C. Preliminary results on diffusion at 1136°C in the system Fe-Co-Ni have been reported.7 In this study, data are reported on a more complete determination of interdiffusion coefficients in the Fe-Co-Ni system in the entire ternary at 1315°C. There is complete solid solubility with the fcc structures at 1315ºC, and this system can be considered as nearly ideal. This approximation allows the computation of the Onsager phenomenological coefficients. These values can then be used to test a kinetic calculation of the Onsager L coefficients in ternary substitutional solid solutions due to Lane and Kirkaldy.8

Jan 1, 1970

By AIME AIME

DOUBT in anyone's mind that this is the age of metals, industrially speaking, could easily have been dispelled by attending the National Metal Congress in Chicago, Sept. 22 to 26. Iron, copper and aluminum; zinc, lead and nickel, often alloyed with each other or with some of a dozen minor metals, make the materials without which the modern world could not run. Science, pure and applied, is doing marvels in finding new mixtures, new alloys to meet new needs; in developing new means of rolling, fabricating, casting and welding metals cheaply-and effectively. These and related matters were the subject of 100 papers presented at 33 seperate sessions of the organizations that participated in the congress.

Jan 1, 1930

By Thomas V. Falkie

Mining and exploration, in the year 1971, can be characterized as a year of politics and the beginning of an era of legislation. Certainly the activities of our state and federal lawmakers and international politicians over-shadowed technical developments, which are outlined in the following pages. The nationalization of the Chilean copper industry was the most far-reaching event of the year. Not only will it have an effect on international metal trade, but the nationalization will also affect the major mining companies in such a way as to cause strategic, managerial and technical adjustments in metal mining and exploration efforts in other parts of the world.

Jan 2, 1972

GENTLEMEN : Herewith are submitted reports for the calendar year 1933 of your Treasurer and the Chairmen of the following standing committees: Finance, Admissions, Membership, Papers and Publications, Library, and MINING AND METALLURGY. TO these reports you are referred for additional details of the year's activity. Finances.-Income for 1933 from all sources totaled $121,690 com- pared with $138,331 in 1932. Incidentally, this exceeded the income as estimated in the budget by $7,190; the largest item being a "surplus" of $3,316 over the budget expectancy as to member dues. As compared with 1932 the most important items of shrinkage in income were $9,000 from dues and initiation fees; $5,500 from the magazine, MINING AND METALLURGY; and $2,500 from sales of publications other than the magazine.

Jan 1, 1934

By Frederick G. Coqueron, Joseph E. Pogue

FOR a number of years, the Department of Petroleum Economics of The Chase National Bank has been conducting a study of the capital employed in the petroleum industry. The technique followed is that of combining and summarizing the available financial and operating data for a group of thirty representative oil companies, doing about two thirds of the domestic business of the entire industry. This paper presents the results of the findings for the year 1943, and supplements the survey, "Sources, Disposition, and Characteristics of the Capital Employed by Thirty Oil Companies During the Nine-Year Period, 1934-1942," presented before the Petroleum Division of the American Institute of Mining and Metallurgical Engineers on Feb. 24, 1944, and also published as a pamphlet by The Chase National Bank.

Jan 1, 1944

By J. E. Harris

By elimination of other possible nucleation processes, it has been demonstrated, for commercially pure magnesium and a Mg-Al alloy, that at stresses less than that necessary for triple-point cracking creep cavities are most probably nucleated heterogeneously at second-phase particles. Evidence for the existence of such particles is presented and the role of grain boundary sliding in the nucleation process is examined quantitatively. DURING creep deformation of polycrystalline magnesium and its dilute alloys in the temperature range 0.45 to 0.7 Tm (Tm = absolute melting temperature) cavities form mainly along grain boundaries oriented normal to the stress axis and failure eventually occurs by their growth and impingement.' The possibility of low-ductility creep failure of magnesium-alloy reactor cans during service has prompted a number of studies of cavity formation in these materials.2-5 In this paper divergent theories of cavity nucleation6-10 are examined critically and conclusions drawn regarding the most probable mechanism of formation of cavities in magnesium. The paper is divided into two parts. The first section consists of the review and quantitative assessment of the possible role of grain boundary sliding in the nucleation process. In the second part an experimental program is described where an electron-microscope technique has been used to determine if second-phase particles exist in as-received commercially pure magnesium and in a magnesium alloy 1) THEORETICAL REVIEW Possible nucleation sites for creep cavities are: a) high-angle grain boundary triple points,11-14 b) subboundary/grain boundary intersections,15-18 c) ledges in the grain boundary, 19-25 d) second-phase particles. 9,26-30 Each of these possibilities is now considered with special reference to deformation of magnesium. 1.1) Triple-Point Cracking. The stroh31 condition to nucleate fracture is: " > vr [1] where ss = applied shear stress, ? = surface energy, C = shear modulus, L = length of sliding interface. This relationship is independent of the nature of the interface and it is possible to calculate the stress concentration at the end of a sliding high-angle grain boundary and thus deduce, approximately,* the minimum applied stress necessary to nucleate triple-point cracking. Such theoretical predictions for Nimonic alloys have been made by McLean13 and found to agree quite closely with the minimum stress determined by experiment. Stresses capable of nucleating triple-point cracking should also be sufficient to nucleate fracture at a grain boundary due to intragranular slip, for the lengths of sliding interface in the two cases are approximately equal. Thus the minimum stress for triple-point cracking should represent a demarcation between failure due to general "cracking" and that due to cavitation. Hauser, Landon, and Dorn32 have demonstrated that for polycrystalline magnesium in the temperature range 78° to 298°K the fracture stress is inversely proportional to the square root of the mean grain diameter. As pointed out by stroh31 this result indicates that Eq. [I] describes the fracture characteristics of magnesium at low temperatures. Heal3 has reported that for rapid deformation (112 pct hr-1) of polycrystalline magnesium the transition from cracking to cavitation occurs in the temperature range 175" to 275°C. He also presented the fracture-stress values for the same material tested under similar conditions. From Eq. [I] taking G = 1.3 x 10" dynes , ? = 600 ergs . cm-2,33 and L = 0.017 cm, a Stroh-McLean13,31 tensile stress of -266 kg. cm-2 is calculated, corresponding to a transition temperature of -190°C; this is in

Jan 1, 1965

By E. E. Donath

Application of the coal hydrogenation process for the production of chemicals is described. It has been estimated that a plant to produce 31,090 bbl per day of chemicals and fuels would cost $326,- 000,000. These products would consist of 6.1 pct by weight tar acids, 50.8 pct aroma tics, 16.4 pct LPG, and 26.7 pct gasoline. THE coal hydrogenation process is well known as a means for the production of liquid fuels from coal. In this paper the possibilities of the coal hydrogenation process as a source of chemical raw materials will be discussed. The recovery of chemicals from coal hydrogenation products necessitates some modifications and additions to the equipment used for the production of fuels. The conversion of coal into liquid fuels such as gasoline requires two steps: liquid phase and vapor phase hydrogenation. Intermediate oils obtained in the liquid phase contain oxygen and nitrogen compounds, especially aromatic compounds, since the coal itself is composed mainly of cyclic compounds. These oils are the raw material for the separation of high molecular weight aro-matics and of tar acids and tar bases. The relative amounts of heavy and middle oil—boiling above and below, e.g., 325°C—can be influenced by temperature, residence time, and catalyst of the liquid phase hydrogenation. In the vapor phase hydrogenation a solid bed catalyst is used to convert the intermediate oil from the liquid phase operation into hydrocarbons of the gasoline boiling range. Essentially pure hydrocarbons with a low content of sulphur, oxygen, nitrogen, and olefines are obtained. Depending mainly on the catalyst, the high ring compound content of the liquid phase oil can be preserved and gasoline rich in aromatics obtained. However, with other catalysts, these ring compounds can be split into gasoline with a high content of isoparaffins.' Again, depending on the operating conditions, products of varying boiling range can be obtained. Selection of catalyst and operating conditions therefore makes possible the production of different grades of motor fuel and also variations in the relative amounts of benzene, toluene, and xylene when aromatic hydrocarbons are produced. The schematic flowsheet, Fig. 1, shows the main steps of the coal hydrogenation process, and the product streams used for the recovery of chemicals are indicated. In the liquid phase hydrogenation stage, coal is made into a paste with recycle heavy oil. The coal paste is mixed with hydrogen and preheated at a pressure of 300 to 700 atm in heat exchangers and preheaters. The coal paste and hydrogen enter high pressure converters where the liquefaction of coal, conversion of the high boiling liquid materials initially obtained, into intermediate oils is performed at a temperature around 470°C. The reaction products enter the hot catchpot in which lower boiling oil vapors are separated from the residue containing unreacted coal, ash, and heavy oil. This residue, usually called H.O.L.D. (heavy oil let down), is processed to separate solid and liquid material. By thermal treatment of the residue, e.g., a coking process, distillate oil is obtained, which can be recycled as part of the pasting oil. This stream is rich in polynuclear aromatics and can be, and has been, used for the recovery of such material. The oil vapors and hydrogen from the hot catchpot are cooled in heat exchangers and a cooler, and the condensed oil is separated from the recycle hy-

Jan 1, 1953

By E. E. Donath

Application of the coal hydrogenation process for the production of chemicals is described. It has been estimated that a plant to produce 31,090 bbl per day of chemicals and fuels would cost $326,- 000,000. These products would consist of 6.1 pct by weight tar acids, 50.8 pct aroma tics, 16.4 pct LPG, and 26.7 pct gasoline. THE coal hydrogenation process is well known as a means for the production of liquid fuels from coal. In this paper the possibilities of the coal hydrogenation process as a source of chemical raw materials will be discussed. The recovery of chemicals from coal hydrogenation products necessitates some modifications and additions to the equipment used for the production of fuels. The conversion of coal into liquid fuels such as gasoline requires two steps: liquid phase and vapor phase hydrogenation. Intermediate oils obtained in the liquid phase contain oxygen and nitrogen compounds, especially aromatic compounds, since the coal itself is composed mainly of cyclic compounds. These oils are the raw material for the separation of high molecular weight aro-matics and of tar acids and tar bases. The relative amounts of heavy and middle oil—boiling above and below, e.g., 325°C—can be influenced by temperature, residence time, and catalyst of the liquid phase hydrogenation. In the vapor phase hydrogenation a solid bed catalyst is used to convert the intermediate oil from the liquid phase operation into hydrocarbons of the gasoline boiling range. Essentially pure hydrocarbons with a low content of sulphur, oxygen, nitrogen, and olefines are obtained. Depending mainly on the catalyst, the high ring compound content of the liquid phase oil can be preserved and gasoline rich in aromatics obtained. However, with other catalysts, these ring compounds can be split into gasoline with a high content of isoparaffins.' Again, depending on the operating conditions, products of varying boiling range can be obtained. Selection of catalyst and operating conditions therefore makes possible the production of different grades of motor fuel and also variations in the relative amounts of benzene, toluene, and xylene when aromatic hydrocarbons are produced. The schematic flowsheet, Fig. 1, shows the main steps of the coal hydrogenation process, and the product streams used for the recovery of chemicals are indicated. In the liquid phase hydrogenation stage, coal is made into a paste with recycle heavy oil. The coal paste is mixed with hydrogen and preheated at a pressure of 300 to 700 atm in heat exchangers and preheaters. The coal paste and hydrogen enter high pressure converters where the liquefaction of coal, conversion of the high boiling liquid materials initially obtained, into intermediate oils is performed at a temperature around 470°C. The reaction products enter the hot catchpot in which lower boiling oil vapors are separated from the residue containing unreacted coal, ash, and heavy oil. This residue, usually called H.O.L.D. (heavy oil let down), is processed to separate solid and liquid material. By thermal treatment of the residue, e.g., a coking process, distillate oil is obtained, which can be recycled as part of the pasting oil. This stream is rich in polynuclear aromatics and can be, and has been, used for the recovery of such material. The oil vapors and hydrogen from the hot catchpot are cooled in heat exchangers and a cooler, and the condensed oil is separated from the recycle hy-

Jan 1, 1953

By R. W. Kewish

The preparation of massive uranium metal containing very low concentrations of a number of light elements by bomb reduction of UF4, with calcium is described. Details of procedures are given for preparing high-purity ingredients for the bomb reduction. The as-reduced uranium metal contained, on the average, less than the following amounts of light element impurities, in ppm: Li, 0.1; Be, 0.1; B, 0.1; C, 25; 0, 70; Na, 1; Mg, 3; Al, 2; and Si, 7. Other impurities for which the metal was examined averaged, in ppm: Ca, < 10; V, < 10; Cr, 2; Mn, 6; Fe, 50; Co, < 5; Ni, 8; and Cu, 1. THE preparation of very high-purity uranium metal in massive form for research purposes is of great importance. Recently the kilogram-scale preparation of uranium metal containing less than 70 ppm of detected impurities was accomplished by Blumen-thal and coworkers by vacuum remelting of high-purity crystals of uranium obtained by fused salt electrolysis.1"3 Albert and coworkers4 have reported successful experiments in lowering the concentrations of certain impurity elements in uranium, notably iron, to a few ppm by the zone-melting method. The present paper describes the preparation of high-purity massive uranium metal by the bomb reduction of UF4, with calcium. Early in 1951 a program was undertaken at the Los Alamos Scientific Laboratory to prepare uranium metal of very high purity with respect to a number of the light elements. The methods considered for this purpose were 1) bomb reduction of a uranium halide with calcium, 2) electrolysis of fused salts, and 3) hot wire decomposition of UI4, The first of these processes had been used extensively at Los Alamos since 1943 (and still is used) for the production of uranium metal.5 In considering the three processes it was evident that either of the last two would require an extensive development program with no certainty of success. On the other hand, a study of available data showed that uranium metal of very high purity with respect to some light elements had occasionally been made in routine processing by the first method. It was therefore decided that an intensive study of the bomb-reduction process would be made to see if it could be improved to yield uranium metal with very low concentrations of light elements. DEVELOPMENT OF PROCEDURES The bomb-reduction process used at Los Alamos consists of reducing UF4 with calcium, using iodine as a booster. The reaction is carried out in a magnesium-oxide crucible enclosed in a steel bomb. Argon is used in the bomb to avoid objectionable side reactions which would occur in the presence of air. All ingredients for this bomb-reduction process were examined as possible sources of light elements. It was known that high-purity UF4 was required. The calcium used in the reductions was a source of carbon and magnesium. The magnesium-oxide crucibles were sources of boron, silicon, and magnesium. The iodine did not appear to be a source of any impurities. Pure UF4- The UF4 for bomb reduction is prepared from U3O3 , by successive reduction to UO2, with hydrogen and hydrofluorination of the UO2, with anhydrous HF. Since it was known that no impurities were normally introduced during the gas-solid reactions, effort was directed toward the preparation of high-purity U3O3. Of the many possible procedures for the purification of uranium solutions the following were investigated: 1) Precipitation of uranium peroxide. (Two procedures were tried. The first consisted of simultaneously adding hydrogen-peroxide and ammonium-hydroxide solutions to a uranyl-nitrate solution, containing citric and malonic acids, at such relative rates that precipitation was carried out at a constant pH of 1.5 The second consisted of simultaneously adding uranyl-nitrate, ammonium-hydroxide, and hydrogen-peroxide solutions to an aqueous solution

Jan 1, 1960

By Henry M. Howe

PART I. § 1. Introduction. After giving certain definitions, this paper gives the reasons which led to Roozeboom&apos;s form of the diagram of the freezing-point curves and general equilibrium of the iron-carbon compounds, steel and cast-iron ; and then those which led to replacing it with the present or double diagram, in which graphite is at all temperatures held to be the more stable and cementite the less stable (metastable) form of carbon. Next in § 10 the evidence supporting this greater stability of graphite is examined, then in § 17 that which seems to oppose it, and in § 22 a summary of the evidence is presented. The second part of the paper considers the topography of the graphite-iron diagram, rejecting summarily the solubility-lines based on the data of Charpy and Grenet and of Mannes-mann, on the ground that the data even on their face do not really point toward these lines, and that they are wholly incompetent to determine any solubility-lines whatsoever, because they report together with the dissolved carbon also an indeterminate quantity of cement-carbon, and because even such carbon as is actually dissolved, only in part represents the solubility of graphite, and in another and indeterminate part represents the solubility of cementite, or at least of carbon in presence of cementite as distinguished from graphite. It might be thought that graphite is but slightly soluble in iron, because of the absence of any suggestions of eutectoid graphite, corresponding to the eutectoid cementite of pearlite in very many cases in which the cast-iron seems to consist of ferrite and massive graphite only, and because of the micrographs of Goerens and Gutowsky. In these the primary austenite of cast-iron quenched but little below the eutectic freezing-

Jan 7, 1908

By Michael Tenenbaum

The importance of semikilled steel as a high tonnage grade has long been recognized. The increasing severity of the applications for which semikilled steel is used makes it desirable to obtain further information regarding the features of open hearth practice and ingot structure that can affect steel performance in subsequent rolling and fabricating operations. Accordingly, an investigation is being carried out studying the structure of various types of semikilled steel ingots. This paper reviews some of the observations made and information gathered in this investigation. By definition, semikilled steel may be considered to include all nonrimming steels in which the natural shrinkage occurring during ingot solidification is offset to an appreciable degree by gas formation. Accordingly, this type of steel includes the entire range intermediate between rimmed and fully killed steel. The resultant ingot structures range from those of steels that have been capped to suppress a weak rimming action to those steels that have been killed in the furnace or ladle to the extent that no mold deoxidizer is required. A survey reported to the 1946 -AIME Open Hearth Conference&apos; reviewed the practices being used at 28 major plants for the deoxidation of semikilled steel. It was found that most plants divide the deoxidizing additions between the ladle and the mold—many of the plants adding only minor amounts of deoxidizer to the bath or none at all. Silicon, aluminum and titanium were the only elements used for ladle and mold deoxidation. Mold deoxidizers were added as capping additions or as uniformly fed additions. Several practices were reported in which the steel was deoxidized in the ladle to the extent that little or no mold deoxidation was needed. No reference was made to grades capped by using special mold designs or special closures over the top of molds. .Accordingly, specific examples of this type of practice will not be considered in this paper. It appeared from this survey of deoxidation practice that semikilled steel can be divided into three types, namely, capped semikilled, in which aluminum is added near the end of pour or after shut-off, intermediate semikilled steels, in which aluminum is fed uniformly throughout the pour, and semikilled steels requiring no mold deoxidation. In an attempt to cover the ingot structures obtained by the range of practices reported in the preceding survey, three series of experimental heats were made using increasing amounts of aluminum, silicon and titanium for ladle deoxidizers. The ladle deoxidizers were added as stick aluminum, 50 pct ferrosilicon and 20 pct ferrotitanium (4 pct carbon), respectively. Two methods of studying ingot structures were used. Ingots were removed from production, burned longitudinally and machined to allow observation of the central pipe and coarse blowholes. During the machining operation much of the finely porous subsurface structure was obliterated. Accordingly, observations were also made

Jan 1, 1949

By Michael Tenenbaum

The importance of semikilled steel as a high tonnage grade has long been recognized. The increasing severity of the applications for which semikilled steel is used makes it desirable to obtain further information regarding the features of open hearth practice and ingot structure that can affect steel performance in subsequent rolling and fabricating operations. Accordingly, an investigation is being carried out studying the structure of various types of semikilled steel ingots. This paper reviews some of the observations made and information gathered in this investigation. By definition, semikilled steel may be considered to include all nonrimming steels in which the natural shrinkage occurring during ingot solidification is offset to an appreciable degree by gas formation. Accordingly, this type of steel includes the entire range intermediate between rimmed and fully killed steel. The resultant ingot structures range from those of steels that have been capped to suppress a weak rimming action to those steels that have been killed in the furnace or ladle to the extent that no mold deoxidizer is required. A survey reported to the 1946 -AIME Open Hearth Conference&apos; reviewed the practices being used at 28 major plants for the deoxidation of semikilled steel. It was found that most plants divide the deoxidizing additions between the ladle and the mold—many of the plants adding only minor amounts of deoxidizer to the bath or none at all. Silicon, aluminum and titanium were the only elements used for ladle and mold deoxidation. Mold deoxidizers were added as capping additions or as uniformly fed additions. Several practices were reported in which the steel was deoxidized in the ladle to the extent that little or no mold deoxidation was needed. No reference was made to grades capped by using special mold designs or special closures over the top of molds. .Accordingly, specific examples of this type of practice will not be considered in this paper. It appeared from this survey of deoxidation practice that semikilled steel can be divided into three types, namely, capped semikilled, in which aluminum is added near the end of pour or after shut-off, intermediate semikilled steels, in which aluminum is fed uniformly throughout the pour, and semikilled steels requiring no mold deoxidation. In an attempt to cover the ingot structures obtained by the range of practices reported in the preceding survey, three series of experimental heats were made using increasing amounts of aluminum, silicon and titanium for ladle deoxidizers. The ladle deoxidizers were added as stick aluminum, 50 pct ferrosilicon and 20 pct ferrotitanium (4 pct carbon), respectively. Two methods of studying ingot structures were used. Ingots were removed from production, burned longitudinally and machined to allow observation of the central pipe and coarse blowholes. During the machining operation much of the finely porous subsurface structure was obliterated. Accordingly, observations were also made

Jan 1, 1949