By Reino Kurppa

The Pyhäsalmi mine of the Outokumpu Co. is located in central Finland (Fig. 1). The deposit was discovered in the autumn of 1958. Construction of the mine was started a year later, and production began on Mar. 1, 1962 (Fig. 2). At present, 750,000 metric tons (mt) of ore and a nearly equal amount of country rock are mined annually. Slightly over one-half million tons of various concentrates are produced per year, of which 85% is pyrite concentrate, 10% zinc concentrate, and 5% copper concentrate. The pyrite concentrate is treated in the company's pyrite smelter,1 yielding elementary sulfur, sulfur dioxide, and iron-oxide cinders, as well as electric power. Thus all the sulfides, totaling 75% of the ore, are of economic value. This is a fact which had a bearing on the development of the stoping method. GEOLOGY The ore is of breccia type containing fragments of country rock of varying sizes. It is coarse-grained pyrite ore containing sphalerite and chalcopyrite as a matrix between the pyrite grains. Only small amounts of pyrrhotite have been observed in certain marginal parts of the orebody. The ore averages 0.85% Cu, 3.0% Zn, 38% S, and 33% Fe. The orebody extends from the surface down to at least 500 m, which is the lowest level from which present information has been obtained. Horizontally, the orebody is 650 m long. It is 75 m wide at its central part, narrowing towards the ends (Fig. 3). At a depth of 115 m, the orebody suddenly narrows down to a thickness of 25 to 30 m. In the northern part of the orebody, the dip is 50° to 70°, but elsewhere it is almost vertical (Fig. 3).

Jan 1, 1969

By G. R. Wilms

A study has been made of the structural changes in polycrystalline high purity aluminum during the tertiary stage of creep under conditions of constant tensile load. It appears that there is no basic modification in the particular mechanism of deformation that characterized the preceding secondary stage of creep, but that the changes in crystalline structure produced during the tertiary stage are only a consequence and not a cause of the accelerated strain. Intercrystalline fissures were observed on entry into the tertiary stage, and these might supplement the accelerated rate of strain owing to local stress concentrations. There is evidence that the formation of these fissures may be associated with the presence of surface imperfections, and it is suggested that a more generalized treatment of the results may explain certain creep characteristics of commercial alloys. IN previous work'-4 a study was made of the changes produced when specimens of annealed aluminum were deformed at various temperatures and rates of strain, especially under conditions leading to creep under constant tensile load. It was shown that, as the temperature was increased or as the rate of strain was decreased, elements of the substructure produced within the grains became coarser, and with the strain rate constant at a given temperature, their size tended to an equilibrium value. The preliminary process of the breaking down of the grains into a substructure was identified with primary creep.' The subsequent equilibrium, condition was associated with secondary creep. The question then arose whether the tertiary stage corresponded to any further significant change in the substructure. The question is also of interest in view of the opinion, expressed for instance by Andrade,5 that the tertiary stage is merely an accelerated rate of strain due to the reduced area of section of a specimen under continuous tensile load, and the other opinion, as suggested by the observation by Sully, Cale, and Willoughby6 of a tertiary stage in com-pressive loading, that this third stage is a real effect in its own right. The object of this paper is to record some observations on the tertiary stage of high purity aluminum. Experimental Procedure The material was aluminum of 99.98 pct purity as previously used. The specimens had a rectangular section of l/8 x l/2 in., and extensions were measured over a 1 in. gage length. After machining to shape, the specimens were annealed to give a standard grain size of 0.2 mm and then electropolished. The general procedure involved metallographic and X-ray diffraction examination at progressive stages of elongation (marked by arrows on the curves shown in Figs. 1 and 2), the specimen being extended to fracture under constant load at a given temperature. The X-ray tests were made by the back-reflection method from a stationary specimen, using CoK radiation. The longer edge of the micrographs in the paper corresponds to the direction of applied stress. Results The previous work showed that, in the secondary stage of creep in aluminum, three basic types of structure could be developed according to the temperature and rate of strain. These were: 1—slip, which predominated at the lower temperatures and higher rates of strain and produced the finest and least perfect substructure; 2—cell structure, which superseded slip as the temperature was raised and the rate of strain decreased and which was characterized by a coarser and more perfect structure and an absence of slip lines; and 3—a stage termed "boundary microflow," which predominated at still higher temperatures and lower rates of strain when the cell size had increased and become comparable

Jan 1, 1955

By R. U. Jackson

Belt conveying is a method of transportation that requires proper servicing and maintenance if completely economical results are to be obtained from the system. With a trucking system, it is common practice to deliver the trucks to a servicing station each day or at the end of each shift. With railroad transportation there is a similar procedure. Sufficient credit is seldom given to this periodic inspection and maintenance procedure, yet it is the key to the successful operation of trucking and rail haulage systems. How about the belt conveyor transportation system? Here is a system that requires no operator for each individual unit. It requires only a main switch and an adequate sequence interlocking system, and the system is so simple to operate that maintenance is considered as only a casual requirement-nothing is done about it until after trouble has developed.

Jan 1, 1956

By Robert W. Thomas

LEACHING of mined-out areas at the Arizona property of the Ray Mines Division, Kennecott Copper Corp., was started on Jan. 20, 1.937, and by July 1, 1938, 10,000,000 lb. of copper had been produced by this method. Leaching operations at present are confined to the western portion of the ore body and over an area of approximately ten acres. The ore in this area was extremely high in pyrite and the copper content, which averaged slightly in excess of 1 per cent, was the result of incomplete secondary enrichment by solutions which apparently worked laterally from the main ore body. Above the ore was an unaltered zone of primary or protore averaging 125 ft. in thickness and containing approximately 0.6 per cent copper. Above this was the capping or leached zone averaging 50 ft. thick.

Jan 1, 1938

By H. N. Lawrie

Introduction. THIS study was undertaken on account of the lack of definite knowledge concerning the influence of bismuth on wire-bar copper, and the small elimination of bismuth from copper-matte during the smelting-operations. The early workers who studied the influence of bismuth on copper confined their investigations to malleability and ductility-two physical properties which are related to the others so intimately that their determination is of primary importance. Karsten ' and Levol,2 using bending- and mealleability-tests, seem to have been the first to take up the subject, and while their results are incomplete, they agree in the main with the later work of Hampe.3 The bending-tests used by the first investigators consisted in bending the specimen until it failed. The malleabilitytests were made by beating the material to a knife-edge with a hammer. Hampe not only determined the percentage of bismuth which would cause red-shortness and cold-shortness of the alloy, together with other influences of bismuth on the malleability and ductility of copper, but also took up the influence of the bismuth protoxide, BiO, on copper, and of bismuth sesquioxide, Bi2O3, on the copper protoxide, CuO. Hampe's conclusions of the influences of these two latter compounds of bismuth on copper are as follows "If the protoxide of bismuth be alloyed with metallic copper, it is not changed to metallic bismuth, but remains mechanically distributed throughout the copper.

Sep 1, 1909

NEW MEMBERS The following list comprises the names of those persons who became members during the period Apr. 10 to May 10, 1914: Members ADAMS, HENRY H., JR., Merchant, Henry H. Adams & Co., and Colonial Iron Co., 149 Broadway, New York, N.Y. ADAMS, LELAND D., Mine Mgr., Supt., East Canada Smelting Co.,Weedon, Quebec, Canada. AGUILERA, EUGENIO, Chief Engr. Mining & Foresting Dept. of Santiago, Santiago de Cuba, Cuba. ALFORD, NEWELL GILDER; Min. Engr., Asst. Chief Engr., St. Bernard Mining Co,. Earlington, KY.

Jan 6, 1914

By C. A. Heiland

FOR the past three years, the senior writer has carried out, with inter-ruptions, a series of investigations into the characteristics of prospecting seismographs of a wide variety of construction. Early in 1932, a com-plete equipment was developed for both refraction and reflection observa-tions; its first function being, however, the application in reflection shooting. The performance of the equipment proved to be highly satis-factory in a series of field tests' which were carried out by the junior writer, whose services were loaned to the Colorado School of Mines by courtesy of the Plains Exploration Co. in Denver. The various problems that were encountered in the construction of the equipment, in its application in the field, and in the interpretation of the results, are fully treated in Publication 47 of the Department of Geophysics of the Colorado School of Mines. Its first part deals with the various problems encountered in the design of the instruments, and presents a discussion of such topics as the free and forced oscillations of damped and undamped mechanical seismographs, the action of oscil-lographic recording instruments and amplifiers, the characteristics of electromagnetic seismographs, and the requirements of damping, natural frequencies and static magnification for the pickups, amplifiers and oscillographs used in refraction and reflection seismographs. Further-more, a detailed discussion of the various methods of static and dynamic tests of seismic receivers, and a description of the reflection equipment developed at the School of Mines is presented. Unfortunately, a delay has occurred in the publication of the first part of this investigation concerning the instrument problems. There-fore, the second part, dealing with the field problems, is herewith pre-sented first.

Jan 1, 1933

By Charles Behre

THIS paper deals with recent geologic studies in the slate belt of Northampton, Lehigh and Berks counties, Pennsylvania. The work was conducted under the auspices of the Pennsylvania Topographic and Geologic Survey. Three years have now been spent in detailed consideration of the economic geology of this region. In the field, particular attention was paid to the bearing of geology on quarry development and property valuation and the object of this paper is to summarize the results from that viewpoint. Excellent studies of a somewhat similar nature have already been carried out by Bowles,1 but with the emphasis upon the details of quarrying and fabricating methods, rather than upon the geologic relations. THE NORTHAMPTON-LEHIGH-BERKS DISTRICT Location The region here discussed lies in east-central Pennsylvania and extends southwestward from Delaware River, on the New Jersey line, to the Schuylkill in north-central Berks County. It is an elongated belt occupying the northern sections of the three counties mentioned and lying along the southern edge of Blue Mountain. Its length is about 50 miles and its average width five or six, though in places it attains a maximum of 10 miles.

Jan 1, 1928

US 4,183,794 - Electrowinning zinc from a zinc sulfate solution produced by leaching zinc ore with sulfuric acid. The leach liquor is subjected to electrolysis in a first cell having an insoluble anode to deposit primary zinc on the common electrode. The coated electrode is transferred to a second cell having an alkaline electrolyte, and electrolysis is effected in the second cell to transfer zinc from the common electrode to the second cell cathode in a spongelike form which is readily stripped. R.H.C.L. Ross. Jan 15, 1980. 10 pp. (204-119). Filed: 12-22-77 (863,190). Same: Canadian 1,051,820, dated Apr. 3, 1979.

Jan 1, 1982

By Alan J. Strauss

The Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. This paper reviews the properties of the pseudobinary solid solutions formed by these compounds, including the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and energy band structure. Particular emphasis is placed on the Pbl-xSnxTe and Pb1-xSn,Se alloys with rocksalt structure, because of current interest in these malerials for generating and detecting infrared ,radiation. ThE Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. Some of the physical and electronic properties of these compounds, including their melting points1-8 and energy gaps,4'9-12 are listed in Table I. Four compounds (SnTe, PbS, PbSe, and PbTe) have the cubic rocksalt (Bl) structure. At room temperature GeTe has a rhombohedra1 structure closely related to the B1 structure, into which it is transformed at about 400°C. Four compounds (GeS, GeSe, SnS, and SnSe) have the orthorhombic B29 structure. In samples which have not been intentionally doped with impurities, the electrical conductivity is due primarily to electrons or holes produced by the ionization of donor or acceptor lattice defects associated with deviations from stoichiometry. Undoped samples of PbS, PbSe, and PbTe may be either n type or p type, depending on whether they contain excess lead or an excess of the Group VI element, respectively, but only p-type samples of the other compounds have been reported. This paper will review the properties of the pseudo-binary solid solutions formed by the nine 1:l compounds. The topics to be considered include the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and band structure. Particular emphasis will be placed on the Pb]-xSnxTe and Pbl-xSnxSe alloys with B1 structure, which are promising materials for generating and detecting infrared radiation in the 8 to 14 µm atmospheric window and beyond. MUTUAL SOLID SOLUBILITY The extent of mutual solid solubility in the pseudo-binary systems has been investigated for fourteen of the eighteen ternary systems (in which the two terminal compounds have a common element) and for nine of the eighteen quaternary systems. In most cases, X-ray diffraction measurements made at room temperature were used to determine the structure and lattice parameter(s) of the phase(s) present in samples of various compositions prepared by freezing from the melt. In many investigations, including the extensive studies of Krebs and co-workers,13'14 the samples were annealed at elevated temperatures before X-ray measurements were made. In some cases, metallographic examination and thermal analysis have also been employed. The results for the ternary and quaternary systems are summarized in Tables II and III, respectively. (The original references should be consulted for the annealing temperatures.) The solubility of one compound in the other is at least 5 mol pct in all cases, and is often much larger. Complete solid solubility has been observed in all systems so far investigated in which the terminal compounds have the same structure, although in the PbS-PbTe system complete solubility is limited to elevated temperatures. Thus complete solid solubility occurs in five systems where both compounds have the B1 structure (SnTe-PbTe, PbS-PbSe, PbS-PbTe at temperatures above 805°C, PbSe-PbTe, and SnTe-PbSe) and in three where both compounds have the B29 structure (GeS-SnS. GeSe-~n~e-, and SnS-SnSe), as well as in two involving GeTe and a compound with B1 structure (GeTe-SnTe and GeTe-PbTe). On the basis of thermal analysis data, complete solid solubility at sufficiently high temperatures has also been reported for the GeSe-GeTe2 and SnS- pbS22 systems. This seems unlikely, however,

Jan 1, 1969

By William L. Fink and

Although age-hardening in an aluminum-base alloy containing magnesium was observed by Alfred Wilml as early as 1911, it was not until 1919 that a theory of the mechanism of age-hardening was proposed. Merica, Waltenberg and Scott12 studying the age-hardening characteristics of Duralumin at the National Bureau of Standards, came to the conclusion that age-hardening of this alloy is caused by the precipitation of CuAl2, which is less soluble at the aging temperature than at the solution heat-treating temperature. It was postulated that the initially precipitated particles were of fine colloidal dimensions but that they gradually grew in size. Maximum hardness was assumed to be attained when the particles reached a critical size. This theory was at first received skeptically, since it was a widely accepted view at that time that the solid solution state should represent the hardest state of an alloy. Shortly thereafter, Jeffries and Archer proposed their well-known slip interference theory.'13 They suggested that age-hardening was accomplished by the precipitated particles acting as keys interfering with slip along crystallographic glide planes. They showed that this mechanical theory led direct,ly to the assumption that maximum hardening would be produced by particles of a critical size, which they suggested would have a diameter approximately 10 times that of the aluminum atom. This contribution amplified and explained so rationally the age-hardening theory of Merica, Waltenberg and Scott that wide acceptance resulted. Objections to Simple Precipitation Theory From time to time certain experimental facts have been cited against the simple precipitation theory. The first of these was the discovery by Fraenkel4 that, although the electrical resistivity of Duralumin decreased during aging at higher temperatures (from 100' to 250' C.), it increased during aging at ordinary temperatures. This was not in accordance

Jan 1, 1940

By William L. Fink and

Although age-hardening in an aluminum-base alloy containing magnesium was observed by Alfred Wilml as early as 1911, it was not until 1919 that a theory of the mechanism of age-hardening was proposed. Merica, Waltenberg and Scott12 studying the age-hardening characteristics of Duralumin at the National Bureau of Standards, came to the conclusion that age-hardening of this alloy is caused by the precipitation of CuAl2, which is less soluble at the aging temperature than at the solution heat-treating temperature. It was postulated that the initially precipitated particles were of fine colloidal dimensions but that they gradually grew in size. Maximum hardness was assumed to be attained when the particles reached a critical size. This theory was at first received skeptically, since it was a widely accepted view at that time that the solid solution state should represent the hardest state of an alloy. Shortly thereafter, Jeffries and Archer proposed their well-known slip interference theory.'13 They suggested that age-hardening was accomplished by the precipitated particles acting as keys interfering with slip along crystallographic glide planes. They showed that this mechanical theory led direct,ly to the assumption that maximum hardening would be produced by particles of a critical size, which they suggested would have a diameter approximately 10 times that of the aluminum atom. This contribution amplified and explained so rationally the age-hardening theory of Merica, Waltenberg and Scott that wide acceptance resulted. Objections to Simple Precipitation Theory From time to time certain experimental facts have been cited against the simple precipitation theory. The first of these was the discovery by Fraenkel4 that, although the electrical resistivity of Duralumin decreased during aging at higher temperatures (from 100' to 250' C.), it increased during aging at ordinary temperatures. This was not in accordance

Jan 1, 1940

By D. B Kibler

The Florida hard-rock field extends from Suwanee and Columbia Counties in northwest Florida to south of Croom, Florida, in Hernando County. This area is approximately 100 miles long and varies from 2 to 30 miles in width. Florida hard-rock phosphate was discovered at Hale Springs, about one mile northwest of the town of Dunnellon, Marion County, in the year 1888, by Alber-tus Voight, who lived within a few hundred yards of the spring. Soon after this discovery there was a great influx of land speculators and wildcat operators into the vicinity of Dunnellon. A few years later phosphate was found in Alachua, Levy, Citrus and Hernando Counties, and a great number of small crude plants were built from Newberry, Alachua County, all the way to Croom, Hernando County. Phosphate was found in many places as "outcrops." Looking for outcrops was the first method used by the early prospectors in searching for deposits. Several years passed before any systematic method of prospecting was used. Early Mining The early method of mining hard-rock phosphate was with picks and shovels, wheelbarrows, mules and wagons. The pick-and-shovel method was used altogether until about 1900, when some of the larger operators began to use railroad-type steam shovels of from ½ to I-yd. capacity Picks and shovels, with negro labor loading the phosphate ore (called "matrix") into wooden side-dump skip-cars, was continued until about 1907. From the discovery of hard-rock phosphate until approximately 1905, overburden was removed with mules and scrapers. At some places, the overburden was loaded into side-dump skip-cars by negro laborers and the cars were then pulled up an incline with a steam hoisting engine. The maximum depth of overburden that could be economically removed by hand labor, mules and scrapers was approximately 15 feet. About 1905 one of the companies erected a producer-gas power- I house near Dunnellon and generated its own electricity and about the same time the larger companies began using hydraulic methods for the removal of overburden. From the year 1888 through the year 1939 approximately 75 companies were operating at one time or another in the hard-rock territory, on approximately 500 locations. The hard-rock deposits are more irregular and have higher mining costs than the pebble-rock deposits, therefore 1 they have not been competitive in the domestic market, but because of the higher grade of the hard rock it is in demand for I the export trade. Discovery of phosphate outside of the United States has made it increasingly difficult in recent years for the hard-rock companies to survive, so today i only three companies are operating. These

Jan 1, 1942

By D. B. Kibler

The Florida hard-rock field extends from Suwanee and Columbia Counties in northwest Florida to south of Croom, Florida, in Hernando County. This area is approximately 100 miles long and varies from 2 to 30 miles in width. Florida hard-rock phosphate was discovered at Hale Springs, about one mile northwest of the town of Dunnellon, Marion County, in the year 1888, by Alber-tus Voight, who lived within a few hundred yards of the spring. Soon after this discovery there was a great influx of land speculators and wildcat operators into the vicinity of Dunnellon. A few years later phosphate was found in Alachua, Levy, Citrus and Hernando Counties, and a great number of small crude plants were built from Newberry, Alachua County, all the way to Croom, Hernando County. Phosphate was found in many places as "outcrops." Looking for outcrops was the first method used by the early prospectors in searching for deposits. Several years passed before any systematic method of prospecting was used. Early Mining The early method of mining hard-rock phosphate was with picks and shovels, wheelbarrows, mules and wagons. The pick-and-shovel method was used altogether until about 1900, when some of the larger operators began to use railroad-type steam shovels of from ½ to I-yd. capacity Picks and shovels, with negro labor loading the phosphate ore (called "matrix") into wooden side-dump skip-cars, was continued until about 1907. From the discovery of hard-rock phosphate until approximately 1905, overburden was removed with mules and scrapers. At some places, the overburden was loaded into side-dump skip-cars by negro laborers and the cars were then pulled up an incline with a steam hoisting engine. The maximum depth of overburden that could be economically removed by hand labor, mules and scrapers was approximately 15 feet. About 1905 one of the companies erected a producer-gas power- I house near Dunnellon and generated its own electricity and about the same time the larger companies began using hydraulic methods for the removal of overburden. From the year 1888 through the year 1939 approximately 75 companies were operating at one time or another in the hard-rock territory, on approximately 500 locations. The hard-rock deposits are more irregular and have higher mining costs than the pebble-rock deposits, therefore 1 they have not been competitive in the domestic market, but because of the higher grade of the hard rock it is in demand for I the export trade. Discovery of phosphate outside of the United States has made it increasingly difficult in recent years for the hard-rock companies to survive, so today i only three companies are operating. These

Jan 1, 1942

By C. G. Dunn

With respect to theories of recrystalliza-tion in metals plastically deformed. it has been said that the present status of this subject is far from satisfactory.1 It may also be said that before any mechanism of recrystallization for metals and alloys can be set forth in a satisfactory manner, there must be made available considerable data on orientation changes that occur during the deformation and recrystallization processes. Although extensive data have been published on recrystallization in single crystals and in poly-crystalline specimens, more results of a type that can be classified according to simple orientation changes would be desirable in this complex field. It might even be said that before classifications are made according to types of orientation changes, it may be possible to classify a considerable amount of data into certain kinds of orientation states if groups of common or nearly common orientation occur. Methods for computing the probability of occurrence for various types of groups have been published2 and it has been pointed out in particular that it should be possible to analyze orientation data for high-order twin relationships between old and new grains even when agreement is not at all exact. In this connection, work on recrystallization in silicon ferrite reported in a paper concerned with complex groups of annealing twins3 indicated that some data were consistent with primary nucleation OCcurring according to a second-order or a third-order twin transformation. However, further work in this latter direction was definitely needed. It is, therefore, the purpose of the present paper to report data and analyses for primary nucleation in silicon ferrite following small deformations that have been carried Out at the Pittsfield Works' Laboratory of the General Electric Co. Analyses have been made with the aid of standard groups of twins that are reported elsewhere.4 PReparation oF Specimens and Experimental Procedure The material used in the present investigation was taken from the same heat of steel as that .used in a prior report.3 The finished strip in both cases was made by the Allegheny-Ludlum Steel Corporation according to methods that produce a high degree of preferred crystal orientation. Samples with large grains had the following composition: 3.45 per cent Si, 0.003 C, 0.008 P, 0.020 S, 0,075 Mn, 0.03I A1 and 0.072 Cu. Thickness of specimens was 0.012 inches. Plastic deformation was produced by cold-rolling the samples on a mill with 8-in. diameter rolls, the plane of the sample in each case coinciding with an XY plane (the plane of projection for the stereo-graphic plots) and the elongation occurring in the X direction. In general, elongations were held to about 3 or 4 per cent.

Jan 1, 1945

By N. A. Zeigler

GRaphitization phenomena occurring in solid cast iron have principally been studied from the angle of the reactions taking place during annealing of white castings in the manufacturing of malleable iron. The selected bibliography at the end of this paper presents the high spots of the published information in this field. Graph-itization of gray iron upon reheating has received much less attention, primarily because only on rare occasions is this material subjected to any kind of industrial heat-treating. Moreovcr, articles made from gray iron are seldom used commercially at temperatures when any graphitization can take place. When used in such conditions, it is assumed that the articles can be replaced at frequent intervals, which can be afforded because of the low cost of gray iron. However, there is at least one commercial process in which articles made from gray iron, during their manufacturing processing, are subjectcd to rather high temperatures; that is, manufacturing of cast-iron enamelware, which is glazed at about 1600° to 1700°F. (870' to 930°C.) From practical experience, it has been found that one of the convenient and economical compositions of gray iron suitable for enameling is, in round figures, as follows: Si, 2.50 per cent; Mn, 0.35; S, 0.07; P, 0.80; T.C., 3.35; C.C., 0.70. Since this iron usually is cast into thin-walled sections, the percentage of com- bined carbon in it is relatively high. Upon heating in the enameling furnaces, this combined carbon graphitizes, which causes permanent dimensional changes of the articles. Obviously, from practical considerations, it is desirable to maintain these dimensional changes as constant as possible. In the course of experimentation with this iron, two series of experimental heats were prepared in which the manganese to sulphur ratio of the standard cupola metal was offset by ladle additions of: (I) progressively larger amounts of sulphur, and (2) progressively larger amounts of manganese. Each one of these ladle charges was cast into experimental plates 8 by 4 in. and about 5/16 in. thick. All told, 13 ladle charges were thus treated. All of them are listed in Table I, together with their chemical analyses. It may be noted that the manganese to sulphur ratio in these samples ranges between 1.2 and 30.2. Every one of these compositions was subjected to thermal allalysis, using an automatic, self-recording differential dila-tometer. The specimens used in this instrument are 50 mm. long and 4 mm. in diameter. During the dilatometer cycle they are kept under a vacuum of about 3 microns. Each one of them was subjected to a thermal cycle by heating it to I830°F. (1000°C.) in 3 hr. and cooling to room temperaturc in 5 hr. Figs. I, 2 and 3 present three automatically recorded dilatometer curves for irons: Serial No. I (normal composition), Serial No. 6 (high sulphur), and Serial No. 13 (high manganese). All three of these figures are

Jan 1, 1945

By E. A. G. Colls

IN all branches of the chemical industry, corrosion plays a very costly part unless it is suitably com-batted, and as a result it is probably correct that chemical and design engineers are more corrosion conscious in the field of chemical industry than in others. Most metals occur in nature in combination with other elements. The refined or reduced state to which man converts them for his use, by removing the combining elements, leaves them in an unstable condition. Therefore in most of the media to which the metals are exposed they are constantly combining with the constituents of their environment, or in other words they are continually being corroded. Similarly, nonmetallic materials are corroded by undergoing chemical change. The rate at which corrosion takes place varies widely from metal to metal and medium to medium. In practically all cases the corrosion of metals in solutions (electrolytes) is electrolytic in nature and the rate of corrosion is dependent on many factors such as temperature, pressure, internal stresses, galvanic action, metal-ion concentration, and so on. In the chemical industry substances must be handled which are particularly corrosive to materials of construction. At the chemical plants of The Consolidated Mining and Smelting Co. of Canada, Ltd. (otherwise known as Cominco), situated at Trail, B. C., Canada, the following are some of the materials that have to be handled: Gases. Sulphur dioxide, sulphur trioxide, carbon dioxide, carbon monoxide, oxygen, hydrogen fluoride, ammonia, hydrogen sulphide, and oxides of nitrogen. Liquids. Solutions of ammonium sulphate, ammonium sulphite, ammonium nitrate, caustic soda and potash, sulphuric acid, nitric acid, hydrofluo-silicic acid, hydrofluoric acid, phosphoric acid, aqua ammonia, and formic acid. Solids. Gypsum (containing phosphoric acid), ammonium sulphate, ammonium nitrate, phosphate rock, caustic soda, potash, and phosphate fertilizers.

Jan 1, 1951

By E. A. G. Colls

IN all branches of the chemical industry, corrosion plays a very costly part unless it is suitably com-batted, and as a result it is probably correct that chemical and design engineers are more corrosion conscious in the field of chemical industry than in others. Most metals occur in nature in combination with other elements. The refined or reduced state to which man converts them for his use, by removing the combining elements, leaves them in an unstable condition. Therefore in most of the media to which the metals are exposed they are constantly combining with the constituents of their environment, or in other words they are continually being corroded. Similarly, nonmetallic materials are corroded by undergoing chemical change. The rate at which corrosion takes place varies widely from metal to metal and medium to medium. In practically all cases the corrosion of metals in solutions (electrolytes) is electrolytic in nature and the rate of corrosion is dependent on many factors such as temperature, pressure, internal stresses, galvanic action, metal-ion concentration, and so on. In the chemical industry substances must be handled which are particularly corrosive to materials of construction. At the chemical plants of The Consolidated Mining and Smelting Co. of Canada, Ltd. (otherwise known as Cominco), situated at Trail, B. C., Canada, the following are some of the materials that have to be handled: Gases. Sulphur dioxide, sulphur trioxide, carbon dioxide, carbon monoxide, oxygen, hydrogen fluoride, ammonia, hydrogen sulphide, and oxides of nitrogen. Liquids. Solutions of ammonium sulphate, ammonium sulphite, ammonium nitrate, caustic soda and potash, sulphuric acid, nitric acid, hydrofluo-silicic acid, hydrofluoric acid, phosphoric acid, aqua ammonia, and formic acid. Solids. Gypsum (containing phosphoric acid), ammonium sulphate, ammonium nitrate, phosphate rock, caustic soda, potash, and phosphate fertilizers.

Jan 1, 1951

By F. W. Bloecher

D ETERMINATION of the surface area of finely divided minerals is of interest to mineral engineers engaged in flotation, comminution, and dewatering studies. In the industrial minerals field, many materials are classified as to fineness according to their specific surface (surface area per unit weight). A method of surface area determination has been tested and used in the Richards Mineral Engineering Laboratories at M.I.T. It involves low temperature krypton adsorption measurements using the technique described by Beebe.1

Jan 3, 1951

By Rollin E. Hook, Attwell M. Adair

The yield and fracture behavior of recrystallized chromiztm have been studied in order to gain an understanding of the recrystallization embrittlement-rheotropic recovery phenomenon. The duc tile-brittle tensile transition temperature of recrystallized chromium was found to vary from 225 ° to -80°C as the ratio of specimen diameter/mean planar grain size decreased. The applicability of this observation to other bcc metals is briefly discussed. Brittle fracture in recrystallized chromium was found to be initiated predominately from intercrystalline rupture nuclei. Single crystals exhibit a high degree of ductility at 23 "C. The experimental data indicate that grain boundaries play a significant part in the yield and fracture behavim. Pres training significantly reduces the transition temperature, and high temperature aging does not result in re-embrittle-ment until complete recovery or re crystallization occurs. SEVERAL theories have been used to explain the recrystallization embrittlement-rheotropic recovery phenomenon in chromium. Wain, Henderson, and ohnstone' propose a Cottrell dislocation locking mechanism due to nitrogen, and Weaver and Gross and weaver 3 propose a strain-induced precipitation mechanism involving a chromium nitride precipitate. The researches of many investigators seem to leave little doubt that brittleness in chromium is promoted by interstitial impurities. Smith and seybolt4 have shown that the ductile-brittle transition temperature is lowered as the interstitial content is reduced. weaver3 provides evidence for a 150°C reduction in the tensile transition temperature as the nitrogen content is reduced from 20 to 5 ppm. Maykuth and affee' have suggested that the amount and orientation of grain boundary impurities may be responsible for the brittle nature of recrystallized chromium. This suggestion was based on their findings that wrought iodide chromium possessing a fiberous grain structure is ductile in tension at room temperature while a recrystallized grain structure is completely brittle. Previous investigations have not studied this phenomenon sufficiently to determine its cause. Perhaps this has been largely due to previous experimental findings that brittle fracture observed in chromium has been almost entirely transgranular.' In addition McNeil and imb,' who investigated coarse-grained as-cast chromium, describe the point of initiation of fracture as cleavage, close to the (100) plane, near or at grain bound-daries, or at included particles or voids. However, Hook, Adair, and ipsitt found that fracture in coarse-grained recrystallized chromium is initiated by intergranular rupture and then propagates nearly entirely by cleavage. This result, together with their finding that room temperature ductility in bending is observed for single crystals and coarse-grained polycrystalline specimens for which the number of grains through the specimen diameter is small, suggests that grain boundaries may play an important role in the brittle behavior of chromium. The recrystallization embrittlement problem can be resolved into two questions. These are, whether the controlling mechanism is predominately one of crack initiation or crack propagation, and whether brittle fracture is initiated predominately by slip or twin induced intergranular rupture or by cleavage. The following research was designed to study the role of grain boundaries on the brittle fracture of chromium in an effort to resolve these questions. EXPERIMENTAL PROCEDURES, RESULTS, AND DISCUSSION General Procedure. All tensile specimens (except 0.04 in. diam wires) were prepared from 1/4 in. diam swaged rod fabricated from one ingot. Details of fabrication are given elewhere. The results of impurity analysis for the swaged rod and for the

Jan 1, 1963