Search Documents

By A. C. Fraker, H. H. Stadelmaier

In the systems Mo-Fe-C, Mo-Co-C, and Mo-Ni-C the phase boumdaries of the cubic Ij carbides were determined at 1000°C and the variation of the lattice parameter with composition was measured. In the system Mo-Fe-C a single ternary carbide, Mo3Fe3C, was observed. In Mo-Co-C and Mo-Ni-C two new n phases of the type M12C were found: Mo6C06C and Mo6Ni6C. At 1000°C they coexist with the M6C phases MO3-4,CO3-2C and Mo3-4Ni3-2C, respectively. Mo3C03C and Mo4C02C are not separate phases but parts of a single M6C phase region, and the same is true of Mo3Ni3C and Mo4Ni2C. THE n carbide structure type has been known since it was determined by westgren' in 1933, yet reliable information on phase compositions of this type is ap-parently scarce. The following selection of suggested formulas illustrates the extent of the confusion con-cerning compositions: W2-3Fe4-3C,1W6Fe6C,2 W2_4Fe4-2C,3 (W,Fe)6C,4 Tj.-W4Co2C and nz-W6Co6C,5 n1-W3Co3C and n2-w4Co2C,5 W3C03C and w6Co3C2,7 MO3Fe3C,8n2-M04Fe2C,9 (MO,Fe)6C,4 MO3CO3C,8 n2-MO4CO2C.9 Many of these compositions obviously overlap, some disagree in carbon content. The use of the designations 77, and n2 is not consistent. There is uncertainty whether two carbides M6C coexist or whether there is only one M6C with a wide range of substitution of one metal for the other. The existence of M12C seems questionable altogether if one ignores the results of a neutron diffraction study of W6Fe6C supporting that particular metal to carbon ratio.'' More reliable information is available for the iso-typic oxides studied by Nevitt,11 Nevitt, Downey, and orris," and Meussner and carpenter.l3 That n car-bides and oxides are structurally identical, particularly with respect to the location of the metalloid atom, has been demonstrated clearly by Stadelmaier and Meussner14 and also by Parthe, Jeitschko, and sadagopan.15 Therefore the present paper, which attempts to establish the phase boundaries of n defini-tively for three carbon systems, has implications for the whole family of filled Ti2Ni types. EXPERIMENTAL PROCEDURE The samples were prepared in two stages. Pellets weighing 3 g were compacted from powders of the elements and presintered in a closed tube of fused silica that had been evacuated to lO-4 mm Hg. This was fol- lowed by arc melting the sintered samples under argon. Remelting the button once was sufficient to produce homogeneous specimens. The metal powders had the following minimum purities in wt pct: molybdenum 99.5, iron 99.0, cobalt 99.7, nickel 99.9, graphite 99.94. Carbon determinations by the gas volumetric method were obtained from thirty-one of the one hundred samples in the annealed condition. They were limited to compositions that were critical to placing a boundary line in the isothermal sections. The carbon losses were comparatively low and averaged less than 1.5 at. pct. For annealing, the samples were sealed in tubes of fused silica evacuated to 10-4 mm Hg. The annealing schedule was 20 hr at 1250°C followed by 150 hr at 1000" ±10°C. For the water quench the silica glass tubes were broken mechanically to speed the quench. The specimens were examined in the as-cast and annealed condition by standard metallographic techniques. Some of the as-cast and all annealed samples were studied by X-ray diffraction using a 114.6-mm powder camera with filtered Co radiation. The lattice parameters of the n phases were determined by graphic extrapolation to 8 = 90 deg on a plot against sin2 8. It is estimated that the maximum error in the lattice parameters is ±0.002A.. The phase fields were determined by the disappearing phase method, relying on X-rays for phase identification and on microscopy to detect small amounts of a phase. RESULTS Pertinent information on the binary side diagrams has been summarized by Hansen and Anderko16 and Elliott17 and will not be discussed further. Photomicrographs documenting the equilibria at 1000°C have been selected to avoid redundancy due to the similarity of the three systems. Thus there will be only one picture showing an equilibrium with Mo2C, and so forth. Molybdenum-Iron-Carbon. An isothermal section of most of the Mo-Fe-C system at 1000°C is shown in Fig. 1. No attempt has been made to distinguish between a and y iron or to determine their phase boundaries. A conspicuous absence is the phase Fe2 1Mo2C6 with the Cr23C6 structure, supporting the suggestion by Krainer4 that it decomposes by annealing at high temperatures. The only ternary phase is found in a narrow range around Mo3Fe3C (MO43Fe43C14). A microstructure with a two-phase mixture of Mo + n is seen in Fig. 2. The variation of the lattice parameter of n with the estimated composition is shown in in Table IA. The phase diagram does not agree with the results of Kuo9 who reported n2-Mo4Fe2C. Our lattice parameter Varies from 11.095A at the iron-rich end to 11.140Å at the molybdenum-richoend of the phase field whereas Kuo9reported 11.26Å for Mo4Fe2C. We are in agreement with the older work

Jan 1, 1970

CONTENTS [The Nature of Strain Markings in Alpha Brass (paper by J. E. BURKE and C. S. BARRETT, Met. Tech. Feb. 1948. TP 2327). ......................... 2 X Ray Studies of Twinning and Untwinning in Magnesium Alloys (paper by J. B. HESS and R. L. DIETRICH, Met. Tech. Feb. 1948. TP 2328) ................ 11 ]

Jan 1, 1948

By C. R. Wohrman

A melt of pure electrolytic iron with about 0.4 per cent. sulfur and 7 per cent. manganese was prepared in connection with a study of inclusions in iron. The alloy darkened rapidly when etched with a 10 per cent, alcoholic solution of nitric acid, and microscopic examination revealed the presence of a semimartensitic, semi-Widmanstättian structure (Figs. 1 and 2) closely resembling the structures found by Benedicks in his artificially prepared "meteoric iron."' The structures found by Benedicks were readily explained by the presence in his alloy of the two well-known iron-nickel solid solutions, taenite and kamacite, and of their eutectoid (?) aggregate, plessite. By analogy, one would infer the existence of similar phases in the iron-manganese alloy just described, such an inference being strengthened by the similarity displayed in many ways by nickel and manganese in their effects on iron. Iron-manganese Alloys are Regarded as Homogeneous Heterogeneity of iron-manganese alloys has not been recognized heretofore, judging from the data of standard metallographic books and those of original papers. In fact, iron and manganese are quite generally regarded as completely miscible in the solid state. Dr. Rosenhain,2 for example, writes: Alloys of group (a), of which those of gold-silver, iron-manganese, and copper-nickel are examples, when allowed to crystallize sufficiently slowly to attain their condition of final equilibrium, present a microstructure exactly similar to that of a pure metal—the homogeneous character of the molten solution is in that case so completely maintained that the microscope cannot detect the presence of any second constituent. Guillet and Portevin3 refer to the iron-manganese system as an example of the "case of metals completely miscible in the solid state."

Apr. 9, AIME, Chicago Section, Chicago Bar Assn., 29 S. La Salle St., Chicago. Apr. 11-12, Geological Society of America, Cordilleran Section, annual meeting, University of Arizona, Tucson. Apr. 15, AIME, Morenci Subsection, Longfellow Inn, Morenci, Ariz. Apr. 15-17, AIME, South West district meeting, Jefferson Hotel, St. Louis, Mo. Apr. 17, AIME, Utah Section, New House Hotel; Salt Lake City. Apr. 21-22, American Zinc Institute, annual meeting, Hotel Statler, St. Louis. , Apr. 21-23, Chemical, Metallurgical, and Mining Society, and Diamond Drilling Research Laboratory, symposium on diamond drilling, Johannesburg, South Africa. Apr. 22, Assn. of Consulting Chemists & Chemical Engineers, Inc., general symposium, Hotel Belmont Plaza, New York. Apr. 25-26, AIME, New England Regional Conference, Kenmore Hotel, Boston. Apr. 26-May 11, Liege International Fair, Liege, Belgium. May 4-8, Electrochemical Society, Inc., Spring meeting, Benjamin Franklin Hotel, Philadelphia.

Jan 1, 1952

By S. T. Wlodek

The scale md subscale reaction products were identified and their rates of formation were studied in air over the range 1600" to 2000°F (871 " to 1149°C) for periods of up to 400 hr and for hoth the solution-annealed and aged conditions. The effect of prior sltrface preparation on suhscale oxidation was also studied The general oxidation behavior of both Ni-Cr-Mo-Al-Ti type alloys was similar. A surface film of a, Al2O3, forms immediately on exposure Subsequent oxidation continued at a linear rate (QL = 55 * 5 kcal per mole) as colonies of Cr2O3 nucleated at the A12O3/gas interface Further oxidation proceeded at a paraholic rate zvhiclz could he fitted to two successive rate constants. During paraholic oxidation, and depending on temperature, the scale consisted of Cr2O3, NiCr2O4 , and TiO2 with traces of NiO. In the case of Rene 41, the activation energy of both paraholic processes was 66 * 3 kcal per mole suggesting that diffusion of cations tlzrozrgh Cr2O3 was the rate -determining process. An unusual decrease in the oxidation of Udimet 700 at 1900°F where a spinel of Ni(A1,Crh0, zuas the predominant reaction product prevented the accurate assignment of activation energies for this composition. In both alloys internal oxidation of Al2O3 commenced shortly after parabolic scaling was observed. Prolonged exposure prod7tced intemal oxidation of TiN, and in Udimet 700 a complex Mo-Ni nitride was also found. At 1900oF, the subscale reactions in Udimet 700 undergo an inversion which parallels the decrease in surface oxidation; internal oxidation ceases hut is replaced by the formation of "spherodized" 3.' colonies. Surface-preparation techniqtles which introduce appreciable working, such as coarse surface grinding or grit blasting. increase the amount of alloy depletion and internal oxidation in Reni 41. The reverse is true of Udimet 700 for which electropolished or mechanically polished specimens show much more subscale oxidation than strongly worked stirfaces. The strongest commercial nickel-base alloys presently available are generic to the Ni-Cr-Mo-A1-Ti base which exploits the precipitation of Ni3(A1,Ti) as the main strengthening mechanism, while relying on solid-solution strengthening by molybdenum and chromium reinforced by the pre- cipitation of carbides to attain maximum properties. This study characterizes the oxidation behavior of Rene 41, the strongest alloy of the Ni-Cr-A1-Ti type commercially available in sheet form, and Udimet 700, whose higher aluminum and titanium content allows it to exhibit one of the more attractive combinations of high-temperature properties available in a wrought product. The scaling processes of complex, type nickel-base alloys have received relatively little attention. Malamand and vidal as well as Poulignier et al.2'3 have determined the composition gradients across the metal/oxide interface produced by high-temperature oxidation and considered the effect of surface perature, Limited weight-gain data has also been published by Fere 5 for alloys of this type and Radavich6 has identified the reaction products on Udimet 500 and Inco 702 after oxidation at 1832°F. Reference can, of course, be made to the excellent reviews of Kubaschewski and Hopkins7 or Ignatov and Shamgunova8 for a summary of the data available on the oxidation of binary and ternary alloy systems which are related to the more complex alloys considered here. EXPERIMENTAL The analyses of the different commercial heats studied are given in Table I. Using the experimental procedures previously established,9 continuous weight-gain data were obtained on both heats of Rene 41 sheet (A and B) and 150-mil-thick slices of cast Udimet 700. Subscale oxidation reactions were followed by static exposure of cylindrical specimens obtained from swaged Rene 41 (Heat C) and Udimet 700 (Heats E and F). In brief, continuous weight-gain tests were performed on specimens with a surface area of 10 to 12 sq cm. These were abraded through 600 grit Sic paper, electropolished to 2p rms in an electrolyte of 10 pct H2So4 in ethanol, and lightly etched in 10 pct HCl in ethanol before final washing and rinsing in ethanol. All continuous weight-gain data were obtained in dried (-70°F dew point) flowing (1 liter per min) air to an accuracy of +0.1 mg. Subscale oxidation processes were followed by the metallographic examination of 0.5-in-diam by 1.0-in.-long specimens. After an initial center-less grinding, various additional surface treatments were employed to determine the effect of surface preparation on subscale oxidation processes. Before exposure in zirconia crucibles, all samples were lightly etched in 10 pct HCl-ethanol, washed in ethanol, and dried. The depth of internal oxidation was measured to ±0.00025 in. on unetched specimens mounted so as to provide a taper mag-

Jan 1, 1964

By George Krauss, Seth R. Thomas

One complete cycle, allstenite to martensite to aus-tenite, of Martensitic transformation was induced in a commercial 18 Cr-8 Ni stainless steel. Transmission electron microscopy showed that the reverse transfarmation, martensite to austenite, perpetuated the dense defect substructure of the martensite produced by the direct transformation, austenite to 'martensite, and reproduced the retained austenite matrix orientation. A general precipitation of lathlike M,,C, particles was noted to be present in, and is suggested as cause for, regions of martensite that Izad formed after a complete cycle of transformation. The habit plane of the precipitate particles was found to be within 5 a plane previously established as the habit of nitride precipitates of similar morphology in bcc iron. The direct transformation of austenite (y) to martensite (a) in metastable 300 series stainless steels has received considerable attention in the past,'-8 and the martensite product given special emphasis in recent years,9"*u but little information has been published about the reverse martensitic transformation during which bcc a martensite is converted to fcc y austenite."-" The reversal mechanism and the resulting crystallographic relationship between parent and product austenite are of fundamental concern. The reversal product, fully austenitic, and hereafter referred to as reversed austenite, exhibits a defect structure far different from its virgin counterpart. Some studies have been reported in which the structure of reversed austenite in iron nickel alloys is compared to annealed austenite with respect to austenite strengtheningM and Stabilization.' The martensite in these Fe-Ni alloys, however, shows a basic difference from that produced in stainless steels. Structurally, the Fe-Ni martensite is profusely twinned," while the (low-carbon) Fe-Cr-Ni martensite contains a high density of tangled dislocations and is apparently twin-free.I0 reediis" has recently shown in an Fe-16 Cr-12 Ni stainless alloy that this typical martensitic defect structure and the reverse transformation directly influence the structure of the reversal product. He found that much of the reversed austenite had returned to the orientation of the virgin austenite and that fine twins were formed in the austenite after the reverse transformation. This investigation was undertaken in order to describe as completely as possible the structural changes produced by a cycle of transformation in a typical 18-8 stainless steel. EXPERIMENTAL PROCEDURE The 301 stainless steel under investigation (17.44 Cr, 7.75 Ni, 0.80 Mn, 0.60 Si, 0.40 Mo, 0.40 Cu, 0.08 C, 0.03 N, bal Fe)was received as 0.060-in.-thick

Jan 1, 1968

McCulloch, Leon.-Experiments with Sherardizing. Discussed by Fred. L. Wolf, Willis M. Peirce, Jesse L. Jones, O. W. Storey, David R. Kellogg, William H. Finkeldey, L. H. Marshall 2 Bassett, W. H. and Davis, C. H.-Spectrum Analysis in an Industrial Laboratory. Discussed by C. S. Brainin, C. H. Davis, W. H. Bassett, George K. Burgess, George K. Elliott, Leonard Waldo, Keivin Burns 8 Roast, Harold J. and Pascoe, Charles F.-Arsenical Bearing Metals. Discussed by Jesse L. Jones, William A. Cowan,. William K. Frank, William M. Corse, Harold J. Roast 10 Bain, Edgar C.-Crystal Structure of Solid Solutions. Discussed by Ancel St. John, Edgar C. Bain, Paul D. Merica 14 Peirce, Willis M.-Studies on the Constitution of Binary Zinc-base Alloys. Discussed by George K. Burgess, Willis M. Peirce, D. H. Ingall, J. L. Haughton, K. E. Bingham 16 Webster, William R.-Application in Rolling of Effects of Carbon, Phosphorus and Manganese on Mechanical Properties of Steel. Discussed by George B. Waterhouse, J. O. Liebig, Ralph H. Sweetser, H. T. Morris, F. D. Carney, W. P. Barba, John H. Nelson, George K. Burgess 19 Barba, W. P. and Howe, Henry M.-Acid Open-hearth Process for Manufacture of Gun Steels and Fine Steels. Discussed by W. J. Priestley, Haakon Styri, C. T. Patterson, Harry Brearley, W. P. Barba, George F. Comstock, Alexander L. Feild 24 Kellogg, David R.-Electrolytic Deposition of Iron for Building up Worn or Undersized Parts. Discussed by Jesse L. Jones, William Blum, C. R. Hayward, George K. Burgess, C. P. Perin, David R. Kellogg 33 McQuaid, H. W. and Elm, E. W.-Effect of Quality of Steel on Case-carburizing Results. Discussed by H. J. French and L. Jordan, W. J. Priestley, M. H. Schmid, A. E. White, H. J. Stagg and S. C. Spalding, Henry S. Rawdon, J. S. Vanick 35 Phillips, Arthur and Davenport, E. S.-Malleableizing of White Cast Iron. Discussed by Samuel Epstein, H. A. Schwartz, A. E. White, R. S. Archer.... 58 Priestley, William J.-Effect of Sulfur and Oxides in Ordnance Steel. Discussed by Harry T. Morris, William J. Priestley, C. P. Perin, James H. Gray, W. P. Barba, Haakon Styri, Frank D. Carney, W. L. Harbrecht, George F. Comstock, E. J. Janitzky 67

Jan 5, 1922

By J. Gordon Parr, D. H. Polonis

The formation and subsequent decomposition of metastable phases in Ti-Ni alloys containing up to 11 pet (atomic) Ni have been studied. The decomposition of a completely retained ß phase and of a completely transformed 8 phase in a 6 pet alloy has been followed by X-ray diffraction and metallographic methods and by hardness determinations made during the process. The possible mechanisms of the reactions are discussed. PREVIOUS investigations of the Ti-Ni system have usually been limited to phase diagram studies; but little attention has been given to metastable phases and tempering processes. These are important, however, since equilibrium conditions are rarely achieved—nor, perhaps, are they desired—in practice. Up to the present time the available transformation data for titanium alloys appear to be restricted to isothermal transformation curves for selected binary and ternary systems. No quantitative studies have been made of the mechanism by which equilibrium is approached. Several independent investigations have been carried out to determine the Ti-Ni phase diagram. Early work by Wallbaum' and later by Long et al.' produced tentative phase diagrams which were not representative of true binary conditions, since the alloys were contaminated with oxygen and nitrogen. The most recent diagram (Fig. 1) is due to Margolin et al.," and a slight modification of the a + ß/ß boundary (shown dotted) has been proposed by McQuillan.' The structure of the phase Ti,Ni was shown by Duwez and Taylor" to be face-centered-cubic, with 96 atoms per structure cell. The formation of a martensitic ß phase (close-packed-hexagonal) in Ti-Ni alloys has generally been observed when specimens of low nickel content are rapidly cooled from the 0 (body-centered-cubic) range. Margolin et al. reported an increasing tendency for P to be retained in lump specimens as the nickel content increases. McQuillan' has studied the effect on the microstructure of delay time in quenching, and has reported the formation of pro- eutectoid a precipitate in a quenched hypoeutectoid alloy. In a previous study of Ti-Fe alloys," experiments were made on powder specimens produced by filing alloy ingots. Techniques were devised for the preparation and heat treatment of alloys, and X-ray diffraction methods were used both for structure determinations and phase ratio estimations. A similar approach has been made in this study of Ti-Ni alloys. Experimental Methods Ten alloys ranging from 0.25 pet to 18 pet Ni* * All compositions are in atomic percentages unless otherwise stated. were prepared from iodide titanium bar stock (hardness Rf 72) and Johnson-Matthey spectrographic standard nickel by levitation melting.' As a check

Jan 1, 1957

By Paul F. Kerr

The uranium-producing areas near Marysvale, Utah provide an unusual group of veins and replacement deposits associated with a Pliocene-Oligocene intrusive and extrusive igneous complex. Aside from several scattered occurrences in older volcanics, uranium-bearing veins occur in intrusive quartz monzonite or granite and in nearby rhyolite. The veins in general trend within a few degrees of N55-65°E, are more or less vertical, and are found along the western margins of a quartz monzonite intrusive. The replacement deposits are found in rhyolite intrusives and also in the lower portions of rhyolite flows close to places where veins forming solutions rising through quartz monzonite came into contact with the rhyolite. At least 14 veins have been mined since uranium mining operations began at Marysvale some 16 years ago, while ore has been extracted through about 10 miles of underground workings. The active mmmg area is approximately 3000 feet long and in the central portion 1500 feet wide. Ores have been found over a vertical spread of almost 2000 feet, between the highest occurrence on Jungfrau Hill ( ca. 7200 feet) and the deepest discovery of ore in a drill hole near the Prospector Mine (ca. 5200 feet). Under existing mining and marketing conditions, mining along the veins in the main area appears to have reached an economic limit at about 500-600 feet below the surface. However, orebodies in the rhyolite and in the upper portions of veins close to the rhyolite are subject to active mining. Isotopic dates indicate that the uraninitebearing veins and replacements are late Miocene or Pliocene (ca. 10-13 m.y.), the rhyolite is Miocene (avg. 17.5 m.y.), and the quartz monzonite and granite intrusives are late Oligocene (23.6 to 26.0 m.y.). The older Bullion Canyon Volcanic Series which encircles the area is Oligocene (28 to 31.1 m.y.). Two generations of alteration occur: ( 1) Earlier alunitic veins and replacement bodies are found in the Bullion Canyon Volcanic Series, none of which have produced uranium; (2) Later argillic alteration associated with the introduction of uranium is found along veins, replacing glassy rhyolite dikes and replacing phases of the rhyolite.

Jan 1, 1968

By Walter Loel

THE application of aerial photographs to all phases of geologic mapping is set forth, indicating the advantages to be gained in different types of country and under varying climatic conditions. Methods of field and office procedure are given from a geological point of view, as well as suggestions regarding the best methods of aerial mapping for different uses and under varying field conditions, including the study of submarine geology. Aerial photographs with accompanying geologic maps are shown to illustrate the appearance from the air of different geologic features under varying climatic and topographic conditions.

Jan 1, 1938

Division of Geology, State of Tennessee, 401 Seventh Ave, North, Nashville, Tenn. Walter F. Pond, State Geologist A selected list of Bulletins available: Bulletin 1(B), Bibliography of Tennessee geology (1911); 2(A) Outline introduction to mineral resources (1910), 2(D) Marbles (1911); 2(G) Zinc deposits (1910), 16, Red iron ores of east Tennessee (1913), 22, Geology and natural resources of Rutherford County (1920), 24(A) Geology and oil possibilities of parts of Overton, Clay, Pickett and Fentress counties (1920); 24(B) Oil and gas resources of northeastern Sumner County (1920), 26, Mineral resources of Waynesboro Quadrangle (1921); 28, Marble deposits of East Tennessee (1923), 29, Magnetic iron ores of east Tennessee (1923), 31, Zinc deposits of east Tennessee (1923), 33, Tennessee coal fields, 37, Geology and mineral resources of Hardin County, 38, Stratigraphy of the Central Basin (in press), 39, Brown iron ores of the Eastern Highland Rim (in press) From 1911 to 1919, inclusive, volumes were issued annually on The Resources of Tennessee Only a few of the separate papers contained in those volumes are now available Vol. 2 (1911): No 1, Explosions of coal dust in mines, and other papers, No. 4, Lignite and lignitic clays in west Tennessee, and other papers; 5, The growth of knowledge of Tennessee geol¬ogy; 9, The valley and mountain iron ores of east Tennessee, 10, The iron industry of Lawrence and Wayne counties, and other papers; 11, Barite deposits in the Sweetwater district, and other papers, 12, The iron ore deposits in the Tuckalioe district, and another paper Various oil maps (15 to 40 cents each) and traverse maps of counties (25 cents and 31 each) can be had, as well as pertinent U. S topographic maps.

Jan 1, 1933

[†AARONSON, ALFRED E., Vice-Pres., Mid-Co. Petroleum Co., Mid-Co. Bldg., Tulsa Okla. '18 ABADIE, EMILE R., Min. Engr Box 927, Porterville, Cal. '76 ¦ABADILLA, QUIRICO A. Student, Colorado School Of Mines, Golden, Colo. '20 ABBOTT, CLARENCE E., Gen'l Supt. Iron Mines Div., Tenn. Coal, Iron & R. I. Co., 1405 Minnesota Ave., Bessemer, Ala. '04] [ ]

Jan 1, 1925

By W. S. Holt, E. T. Tkac, R. A. Grange

QUANTITATIVE knowledge of the time element involved in austenite transformation in a particular steel provides a sound basis for understanding and planning heat-treatment. Such knowledge is conveniently obtained by measurement of austenite transformation as it occurs at each of a series of temperature levels. The results of these measurements usually are summarized in the form of the now familiar isothermal transformation diagram (I-T diagram, TTT diagram, or S-curve). Although a considerable number of such diagrams already have appeared in the literature, there remain many compositions of commercial importance for which no I-T diagram is available. The diagram for many such steels may be predicted from published data with sufficient accuracy for most practical purposes, but for others no satisfactory prediction can be made because the effect on austenite transformation of one or more of the important alloying elements present is not well enough known. Such a steel is Nitralloy, Type 135-Modified, which, containing about 1.25 per cent aluminum, differs from any whose I-T diagram has been published. This paper presents results of a study of the isothermal transformation behavior of a sample from a commercial heat of this aluminum-chromium-molybdenum steel, together with pertinent supplementary data including the equilibrium transformation temperatures (Ae3 and Ae1), the temperature range of martensite formation, and the end-quench hardenability. These data are directly applicable to the heat-treatment of this type of steel and are of interest in revealing some of the fundamental effects of aluminum as an alloying element in steel. MATERIAL All specimens were prepared from a 13-in. diam bar forged from a 5 by 5-in. billet from a commercial heat made in an electric arc furnace. The composition of the bar was; C, 0.41 per cent: Mn, 0.57: P, 0.016: S, 0.005: Si, 0.24: Ni, 0.17: Cr, i.57: MO, 0.36: Al, 1.26. The forged bar was normalized from 1750°F (955°C) and then tempered for one hour at 1200°F (650°C), this tempering treatment having been given to facilitate the machining of specimens. EQUILIBRIUM TRANSFORMATION TEMPERATURES In hypoeutectoid steel the minimum temperature at which austenite is completely stable, Ae3, and the maximum temperature at which austenite is completely unstable, Ae1, are of great significance in heat-treatment. Since these temperatures are dependent upon com-

Jan 1, 1946

By AIME AIME

MANY interesting papers, opportunity of seeing o1d friends, and an exposition showing all that is latest in equipment, all were factors in bringing a large crowd to Detroit during "Metal Week," October 2-6. The Institute's Iron and Steel and Institute of Metals Divisions held technical sessions at the Statler Hotel on October 4 and 5, and that hotel was also headquarters for the American Society for Steel Treating and the American Society of Mechanical Engineers, both of which also had technical sessions. The American Welding Society and the Wire Association met at the Book-Cadillac Hotel, and the exposition was staged at Convention Hall, out Woodward Avenue. All in all it was a big week for men interested in metal working. One of them stated to your reporter on the train en route to Detroit that this was the one convention that he never missed, and doubtless others felt the same way about it.

Jan 1, 1933

By P. Greenfield, P. A. Beck

RECENT work by J. Darby, Jr. in this laboratory has shown that the reported vanadium-rich limit of the s phase in the Co-V system at 1200°C is in error. The appearance of a second phase in s actually is restricted to alloys containing over 68 atomic pct V. The error in the original value is due apparently to a reaction that takes place along the numerous cracks in the s specimens between the alloy and the impurities present in the He + 8 pct H atmosphere in the annealing furnace. Such a reaction and the consequent appearance of a second phase can be suppressed if the alloys are sealed under vacuum in Vycor tubing. The new value of 68 atomic pct V for the vana-dium-rich limit of the s phase in the Co-V system effects slightly the s compositions calculated from average values of N, and N,. for various s phases. The standard deviation between experimental mean compositions and those calculated from the assumption that s is characterized by a constant number of 3d + 4s electrons per atom (N,), is slightly reduced from 9.1 to 8.8 pct. The maximum divergence for the V-Mn s phase is reduced from 15.5 to 14 atomic pct. The standard deviation calculated from constant electron vacancy numbers given by N.. = 4.66 (Mo + Cr + V) + 3.2 (Mn) + 2.2(Fe) + 1.71(Co) + 1.6(Ni) is now greatly reduced, as the maximum divergence for this correlation previously occurred in the V-Co system. This maximum divergence is reduced from 7.6 to 2.3 pct, and the standard deviation for all s- phases is reduced from 4.1 to only 2.9 pct. The correlation for electron vacancy numbers given by N. 5.66 (V when with Ni or Co) + 4.88 (V when with Mn or Fe) + 4.66 (Cr + Mn) + 3.3 (Mn) + 2.66 (Fe) + 1.71 (Co) + 0.61 (Ni) is made slightly worse, and the standard deviation increases from 2.8 to 3.9 pct. These changes, however, do not affect the conclusions of the paper.' The deviation between calculated and experimental s compositions is much less for either one of the electron vacancy correlations than for the correlation with the number of 3d + 4s electrons.

Jan 1, 1955

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS ?ARE ASSOCIATES. THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. *AARONS, J. BOYD, Vivian Gold Mining Co., Ltd., Harris, West. Australia. '05 *ABADIE, EMILE R., Cons. and Min. Engr., 214 Union Savings Bank Bldg., Oakland, Cal. '76 ?ABBÉ, MAX F., Prest., Abbé Engineering Co, 220 Broadway, New York, N.Y. '07 *ABBOTT, CHARLES W., Min. Engr. Pioche, Nev. ?08 *ABBOTT, JAMES W., Min. Engr: Ploche, Lincoln Co., Nev. '94

Jan 1, 1917

By Edgar Bain

SUMMARY THE results of an enquiry into the structural nature of some 70 iron alloys containing both nickel and chromium over a considerable range of concentration 'are briefly described in this paper. This study is a part of a comprehensive program of investigation into alloys involving chromium in progress at the Union Carbide and Carbon Research Laboratories. All the compositions studied contained carbon in amount comparable to commercial alloys.

Jan 3, 1927

By Charles Will Wright

THOSE that attended the seventeenth International Geological Congress held in Russia last summer had an excellent opportunity to gather data and to form impressions on the progress made in the industrialization of the country, particularly with regard to the mineral industries. Several trips to places of interest were arranged, supplementary to the technical sessions held in Moscow, the one to the Ural region being that which I selected as being most likely to be of interest. The accomplishments of the last decade in opening up new mines and building new metallurgical plants in the Soviet Union have been outstanding. This could only be accomplished by a central government ready to employ the best technical talent, which was

Jan 1, 1937

By R. V. Taborelli, P. B. Bucky

This investigation was carried on by means of models and the application of the principles of similitude to determine the effects of props, props and cribs and sand filling in longwall mining. The geologic structure and rate of face retreat were kept constant and the only change introduced was in the method of support. It is not felt necessary to repeat a description of apparatus, or to explain the fact that a scalar model made in all parts of the same material as the prototype will behave similarly to the prototype when rotated at speeds such that the centrifugal force is as many times the gravitational force as the prototype dimension is a similar linear model dimension. The reader is referred to earlier papers1,2 for further information regarding these statements. All models were made of sandstone and were as in Fig. 6. They are composed of a 3/16-in. ore body bed A, overlain by a 3/16-in. bed B, a ?-in. bed C and two ?-in. beds D and E. The model was rotated at + 2350 r.p.m. equivalent to a model ratio of 1268. It was worked back ¼ in. at a time before being replaced in the centrifuge and again rotated. Table 1 gives model and prototype dimensions occurring in this discussion, the prototype dimensions being 1268 times the model dimensions. Figs. 1, 2, 3 and 4 were taken while the model was rotating at 2350 r.p.m. One was taken for each face retreat of 26.4 ft., but for obvious reasons all are not presented. Fig. 1 (A-E) shows the behavior of this type of structure with face retreats of 26.4 ft. and no artificial support. Fig. 2(A-E) shows the behavior of this type of structure where breaker and face props were used. The props were exceptionally strong, being of steel ? in. square in cross section, and capped with 1/16 in. ± of soft wood and paper, to allow for roof deflection. The face props were

Jan 1, 1940

By P. B. Bucky, R. V. Taborelli

This investigation was carried on by means of models and the application of the principles of similitude to determine the effects of props, props and cribs and sand filling in longwall mining. The geologic structure and rate of face retreat were kept constant and the only change introduced was in the method of support. It is not felt necessary to repeat a description of apparatus, or to explain the fact that a scalar model made in all parts of the same material as the prototype will behave similarly to the prototype when rotated at speeds such that the centrifugal force is as many times the gravitational force as the prototype dimension is a similar linear model dimension. The reader is referred to earlier papers1,2 for further information regarding these statements. All models were made of sandstone and were as in Fig. 6. They are composed of a 3/16-in. ore body bed A, overlain by a 3/16-in. bed B, a ?-in. bed C and two ?-in. beds D and E. The model was rotated at + 2350 r.p.m. equivalent to a model ratio of 1268. It was worked back ¼ in. at a time before being replaced in the centrifuge and again rotated. Table 1 gives model and prototype dimensions occurring in this discussion, the prototype dimensions being 1268 times the model dimensions. Figs. 1, 2, 3 and 4 were taken while the model was rotating at 2350 r.p.m. One was taken for each face retreat of 26.4 ft., but for obvious reasons all are not presented. Fig. 1 (A-E) shows the behavior of this type of structure with face retreats of 26.4 ft. and no artificial support. Fig. 2(A-E) shows the behavior of this type of structure where breaker and face props were used. The props were exceptionally strong, being of steel ? in. square in cross section, and capped with 1/16 in. ± of soft wood and paper, to allow for roof deflection. The face props were

Jan 1, 1940