Search Documents

By Eleanor Haslem, Carl A. Zapffe

THE present investigation has three principal purposes: I. To develop a method for measuring hydrogen embrittlement that avoids certain errors complicating previously used methods. 2. To explore in a preliminary way some of the fundamental factors controlling embrittlement. 3. To apply the measurements specifically to stainless grades of steel, whose sensitivity or insensitivity to hydrogen embrittlement has never been clearly defined. SELECTING A TEST METHOD Hydrogen embrittlement is a condition of low ductility resulting from excessive absorption of hydrogen by the steel at some period in its history, and may be revealed by almost any test involving cold deformation. Tensile tests, impact tests, and bend tests are commonly used for detecting hydrogen embrittlement; although numerous other tests, such as cold-upsetting or extrusion, could be used. The simplicity of using a wire specimen for cathodic and acid pickling tests, and the especial adaptability of the bend test to wire specimens, led to selection of the bend test for the present research. Bend tests usually have been of three general types: (I) fatigue, (2) reversed bend, and (3) single bend. The first two types, though widely used, are inaccurate because their measurements are counteracted by an aging effect; and the third type has not been developed to its fullest utility. The effect of cold-working in removing hydrogen is well known. During a bend test hydrogen can be observed escaping from the convex side simply by coating the specimen with oil; and any technique employing flexing or reverse bending may therefore have its measurements masked because the mechanical action reduces the embrittlement during the test. This factor is so important that even elastic flexing of a hydrogen-charged wire specimen should be avoided before testing if accurate measurements are desired. DEVELOPING A MACHINE FOR MEASURING HYDROGEN EMBRITTLEMENT As for the single-bend test, its theory is good, and recovery caused by mechanical work is kept to a minimum. With a given degree of hydrogen embrittlement, a specimen will break at a given angle if the bending is applied unidirectionally and uniformly. The radius of the bend must be kept constant; and the rate of bending should be a constant, slow enough to allow reading of the breaking angle, and yet rapid enough to prevent significant recovery from the escape of hydrogen during bending. A simple apparatus (Fig. I) was constructed using a type H Foxboro drive unit A, which is a synchronous motor with a gear-reduction ratio of 600 to I. A cord, fixed at one end to a wooden pulley B on the drive shaft of the motor, follows the pe-

Jan 1, 1946

By C. R. Sundeen, C. W. Nicolson, J. D. McAuliffe, C. A. Campbell, P. D. Pearson

SHAFT SINKING SYMPOSIUM is a weighty term that could mean any number of things. However, in, this case it has been possible to utilize the transcription of the Annual Meeting Session of the same title and present it in much the same manner as the experts on the panel presented it to their audience Wednesday afternoon, February 18, 1953, at the Los Angeles Statler Hotel.

Jan 8, 1953

By Ernest Kirkendall

THE amount of research done in the last few years on the subject of diffusion in solid metals is significant of the importance of this problem. To review the literature dealing with diffusion is unnecessary here. Desch1 in 1912 reviewed the work that had been done on diffusion in solids and gave a bibliography of the literature published before that time. Mehl's paper in 1936 2 is an excellent review of diffusion in metals and contains a large bibliography. Of importance also for its review and bibliography is an article by A. I. Krynitsky.3 While considerable material has appeared in the literature on diffusion in brass, the amount of information is not great compared to that pertain-ing to some of the other alloys. Most of the information published is of a qualitative nature; that which is quantitative varies considerably. Thus the quantitative determination of the rates of diffusion of copper and zinc in alpha brass by a new method appeared worth while. In the present investigation the rate of diffusion of zinc in approxi-mately the same composition alpha brass has been determined at three temperatures.

Jan 1, 1938

By Thomas P. Oxford, Leslie G. Bromwell

The waste clay slurry produced during beneficiation of Florida phosphate ore presents a major environmental problem. The large volume of waste requires impoundment in above-ground disposal areas surrounded by earthen dams. As the result of a comprehensive research effort, three approaches to improving clay dewatering involving admixing of sand tailings have been developed. These provide satisfactory performance and appear to be compatible with the technological and economic constraints of the industry. Means of determining waste clay characteristics and analyzing mining waste disposal situations by computer simulation have been devised in support of the planning and field testing effort. Detailed examples demonstrating the applicability of the computer programs are presented.

Jan 1, 1980

By F. L. Ransome

THAT geology and mining should stand in close and mutually helpful relationship was recognized in the United States at an early period, but it is not possible to set a precise date at which the study of ore deposits became a thoroughly reputable and important branch of geological science. As early as 1850, appeared the first ,part of Foster and Whitney's report1 on the Lake Superior region, devoted mainly to the copper-bearing areas, followed, in the succeeding year, by the second part,2 on the iron lands. This appears to have been the first comprehensive report on what might, at that time at least, be called "western" ore deposits to be prepared and published under the auspices of the Federal government. An outgrowth from this work was Whitney's Metallic Wealth of the United States,3 which appeared in 1854. It was the earliest general work on the ore deposits of the country, and remained a standard reference book for marly forty years. From 1853 on, various parties were sent out by the War Department to explore routes for proposed railways and wagon roads from the Mississippi Valley to the Pacific Coast. Geologists were attached to most of these parties, but their work was mainly of broad reconnaissance character, little attention being paid to ore deposits. Although the

Jan 1, 1933

By E. Buehler

THE floating zone refining technique'-4 has provided a new experimental approach to the purification of many reactive materials especially those with high melting points. The method avoids the use of a crucible and at the same time it provides a favorable environment at the freezing interface for the growth of single crystals. The physical properties of refractory metals such as molybdenum and tungsten have long been of interest from a fundamental point of view and because of their widespread use in vacuum electronics. Single crystals are often desirable for study. Prior to the introduction of zone melting, single crystals of these metals were usually grown in the solid state at temperatures slightly below the melting point by strain annealing3 or by the application of a moving temperature gradient. Such techniques were mostly successful on wires, ribbons, or rods having small cross-sectional areas. Recently, larger samples of tungsten, molydbenum, tantalum, columbium, and rhenium were melted by a floating zone process which employed electron bombardment heating.10 Single crystals were obtained in many instances

Jan 1, 1959

By Carolyn Barnes

The Offshore Technology Conference, the world's largest technical conference and exhibition on the development of offshore resources and protection of the ocean environment, is sponsored annually in Houston, Texas, by 12 international engineering and scientific societies. This year's OTC, the seventh, will be held May 5-8 at the Astrodomain, and will be the largest in its history. The technical program for the first meeting in 1969 consisted of 100 papers, an exhibit display of 380 booths, and an attendance of 4300. This year. 280 technical papers are to be presented, and more than 2800 exhibit booths, representing some 1200 companies and nine countries, will be on display for an anticipated audience of 40,000.

Jan 4, 1975

By L. K. Eigenbrod, F. Notaro

Enactment of Public Law 91-173 (Federal Coal Mine Health and Safety Act of 1969) has placed new responsibilities on the mining industry. The new law, aimed at eventually solving the problem of pneumoconiosis, sets new respirable dust standards at 2 mg per cu m. Techniques employed to date have been shown to lack total effectiveness in meeting the prescribed standards. Since it is possible that even the new standards will eventually have to be lowered to effectively attack the medical problem, the need for new and more reliable methods of assuring clean respirable air will intensity. This paper presents, in a preliminary manner, both the present technical capability and growth potential of cryogenic technology for supplying miners with clean breathing air. Work with two sizes of prototype supplied-air (cryogenic-liquid) respiratiors in Union Carbide's Fawn Coal mine, will be described. Other potentially fabricable systems will be discussed and a preliminary assessment made of the potential cost of introducing cryogenic air breathing systems in coal mine service.

Jan 1, 1972

By John T. Norton, V.G. Mooradian

The diffusion of metal atoms into the crystal lattice of another metal and the assumption of regular positions to form a homogeneous alloy are some of the most fundamental phenomena of structural metallurgy. The mechanism of this process has been the subject of a great deal of study from many viewpoints, but the picture is still far from complete. It is generally believed that if one metal is to diffuse into another, the first must have some solubility in the second1. This means that the solvent must be able to accommodate the stranger atoms, either on points of its own lattice or in the interstices between, without losing its own crystal-lographic identity. It is also a general observation that cold-working is a distinct aid in the diffusion process, causing it to take place with greater rapidity at the same temperature or with the same speed at a lower temperature. There is considerable doubt, however, as to the real significance of the deformation in its effect on the diffusion mechanism. Several factors associated with the cold-working may be responsible for the increased diffusion rate. The plastic deformation causes a distortion of the solvent lattice, which may be an aid in the assimulation of atoms of another kind. There are many references2 in the literature that suggest that some distortion or "loosening" of the lattice is necessary for atomic migration and that diffusion cannot take place in the undis-torted lattice. On the other hand, it may be that the cold-working causes an increase in surface of contact between the two metals through fragmentation or provides a more intimate contact that is necessary for diffusion. If it is true that lattice distortion is an important factor in diffusion, it seems as if there should be some particular relation between

Jan 1, 1935

By V. G. Mooradian, John T. Norton

The diffusion of metal atoms into the crystal lattice of another metal and the assumption of regular positions to form a homogeneous alloy are some of the most fundamental phenomena of structural metallurgy. The mechanism of this process has been the subject of a great deal of study from many viewpoints, but the picture is still far from complete. It is generally believed that if one metal is to diffuse into another, the first must have some solubility in the second1. This means that the solvent must be able to accommodate the stranger atoms, either on points of its own lattice or in the interstices between, without losing its own crystal-lographic identity. It is also a general observation that cold-working is a distinct aid in the diffusion process, causing it to take place with greater rapidity at the same temperature or with the same speed at a lower temperature. There is considerable doubt, however, as to the real significance of the deformation in its effect on the diffusion mechanism. Several factors associated with the cold-working may be responsible for the increased diffusion rate. The plastic deformation causes a distortion of the solvent lattice, which may be an aid in the assimulation of atoms of another kind. There are many references2 in the literature that suggest that some distortion or "loosening" of the lattice is necessary for atomic migration and that diffusion cannot take place in the undis-torted lattice. On the other hand, it may be that the cold-working causes an increase in surface of contact between the two metals through fragmentation or provides a more intimate contact that is necessary for diffusion. If it is true that lattice distortion is an important factor in diffusion, it seems as if there should be some particular relation between

Jan 1, 1935

By Nelson Severinghaus

THE Rock Chapel plant of Consolidated Quarries Corporation (Fig, 1) is three miles northeast of Lithonia, DeKalb County, Georgia, It was opened about eight years ago for crushed stone aggregate. This paper reviews a number of experiments that have been tried in drilling and blasting, and gives the practice in use today. It also presents several theories on the action of explosives in this type of blasting. FIG, 1.-PLANT OF CONSOLIDATED QUARRIES CORPORATION, WITH QUARRY AT UPPER LEFT. The rock worked is a bare dome of granite gneiss about 3000 ft. in diameter, rising 150 ft. above the surrounding ground (Fig. 2). It is uniform in composition and quality, without seams, and extends down-ward to unknown depth below the quarry floor. A water well drilled 600 ft. remained in the same rock. The principal difficulty encountered in blasting is an easy split, which tends to break down the rock in large blocks.

Jan 1, 1938

By J. B. Ackerman, J. D. Miller

Alunite [KA13(S04)2(OH)6] is a promising non-bauxitic aluminum resource, the domestic reserves of which are estimated to be 800 x 106 tons at 35 percent alunite. The major gangue mineral associated with alunite is quartz. The thermochemical process that has been developed for treatment of this ore does not provide for the initial removal of gangue prior to processing. In this regard, it may be desirable to concentrate the ore to gain significant technical and economic advantages. Experimental results indicate the effectiveness of an oleic acid flotation technique and exemplify the problems encountered in fine particles processing. These results show that the quality of separation studied as a function of temperature, collector addition, and depressant addition is dependent on the degree of liberation achieved during size reduction. At coarse grinds the quality of separation was limited by the presence of locked particles while for finer grinds where more extensive liberation is achieved, better separations were obtained. The degree of liberation for each size interval was determined by an SEM/energy dispersive x-ray technique and found to be independent of the extent of size reduction, suggesting that liberation occurs by indiscriminate fracture and not by detachment. Up to 89 percent liberation was realized for a minus 400 mesh grind. Under these circumstances, the quality of separation appears not only to be limited by the remaining locked particles, but, also, by contamination of the alunite concentrate with fine quartz gangue (< 2µm). The best separation for the minus 400 mesh grind was a rougher recovery of 88 percent with a grade of 65% alunite at 50°C.

Jan 1, 1980

By Gregoire Gutzeit

THE development reported in this paper was begun by the author a number of years ago, while he was a lecturer on complex chemistry and metallurgy at the University of Geneva, Switzerland, and in charge of that institution&apos;s research laboratory. Completion of the development and reduction to practice did not occur until last year at the Westport mill, laboratories and testing plant of the Dorr Company, where this method is now in general use for identifying and localizing the mineral constituents of both metallic and nonmetallic ores. It has proved to be a practical tool of the metallurgical staff at the Westport mill, devising unusual milling flowsheets for complex and refractory ore bodies. In a number of instances the findings have been successfully used as fundamental factors in the design and specification of complete metallurgical plants. Seven examples of the use of this method in solving practical milling problems are included in this paper. GENERAL OUTLINE The microscopic study of an ore, at first only of scientific interest, has proved extremely useful both in practical geology and in ore dressing. The binocular magnifying lenses for rough observation of the products of an ore-dressing plant have been in use for a long time; but only within the last few years has a systematic microscopical examination of ore samples become a normal tool of any research laboratory dealing with ore-dressing problems. Such an investigation avoids considerable loss of time as well as empirical trials and useless experimentation. It will generally indicate the correct grinding and often will suggest the proper method of treatment. The petrographic determination of transparent minerals in thin sections, or even in grains, has been perfected, and very accurate methods have been devised to meet any requirement, such as Feodorof&apos;s rotating stage on the petrographic microscope. Almost all transparent minerals can be positively identified by their optical properties; i.e., isotropism, anisotropism, color, pleochroism, refractory index, cleavage, crystal form, birefringence, and others. The identification of opaque minerals is a much more difficult problem and can be done only by using polished specimens. Unfortunately, most of the valuable metallic ores, and even some of the nonmetallic ones, are not transparent; therefore it has been necessary to develop a special technique for the determination of these minerals. Some optical properties-for instance, isotropism, anisotropism, color, cleavage, reflecting power-are often adequate in roughly classifying the mineral. Only "reflecting power" is a measurable value, provided special photometric equipment (ocular photometer or Orcel&apos;s photoelectric cell) is available. The other optical properties mentioned are more or less relative,

Jan 1, 1942

By C. S. Matthews, H. C. Lefkovits

Drilling progress is often delayed by sticking of the drill string. The development of preventive and remedial methods has been hampered by incomplete understanding of the sticking mechanism. A recent lahorntory investigation hns indicated that one type of sticking may be attributed to the difference in pressure between the borehole and formation. This paper shows, by means of soil mechanics, that the primary cause for differential pressure sticking is cessation of pipe movement, whereas diflerential pressre and stanrtding time determine the severity of the sticking. The analysis stresses the importance of using low-weight muds with low solids content and low water loss to alleviate diflerential pressure sticking and describes why packed hole drilling, long strings of drill collars, and a large deviation from the vertical are conducive to sticking. Finally, preventrve and remedial methods ore evaluated, and a theory is presented on the release of stuck pipe by spotting oil. INTRODUCTION Since drilling with long strings of oversize drill collars has become standard practice in many areas, the incidence and severity of the stuck pipe problem has increased. It has been noticed that in the majority of these cases the sticking could not possibly be attributed to key seating or caving of shales. It appeared that, due to the differential pressure between the mud column and the formation fluid, the collars were pressed into the wall and so became "wall stuck". Points to note about differential pressure sticking are: (1) sticking is restricted to the drill collars, (2) the collars become stuck opposite a permeable formation, (3) the sticking occurs after an interruption of pipe movement, (4) circulation, if interrupted, can be restarted after the sticking is noticed, and (5) no large amounts of cuttings are circulated out after restarting circulation. Helmick and Longleyl investigated pipe sticking by differential pressure in the laboratory and found an empirical relationship between the differential pressure, the sticking time and the required pull-out force. In this paper an explanation of the mechanism is given based on Terzaghi&apos;s theory of clay consolidation. A qualitative description is given in the following paragraphs while the derivation of fonnulas is given in Appendices. This paper is a first attempt to explain pressure differential sticking and many points will require additional theoretical and practical investigation before the problem can be fully understood. PRESSURE DIFFERENTIAL STICKING AS A CONSOLIDATION PROBLEM In any borehole, where the mud pressure is higher than that exerted by the formation fluids, a mud cake is formed opposite the permeable sections of the hole and a continuous flow of filtrate takes place from the mud, through the cake and into the formation. This radial flow pattern requires a certain distribution of the hydraulic and the effective (grain-to-grain) stresses inside the mud cake. Any quantitative or qualitative change in the external pressure conditions will produce a change in the flow pattern and, consequently, also in the internal stress distribution inside the cake. In view of the low permeability and the high compressibility of a clay mud cake, the adjustment of the internal stress distribution is slow and is accompanied by a change in volume. Time dependent stresses are thus created which gradually diminish as the new state of equilibrium between internal and external pressures is approached. Some 30 years ago, Terzaghi developed his "Theory of Consolidation" to account for the time-dependent stresses and settling of clay formations under the influence of external loads. He derived a differential equation by which the time-dependent hydraulic stress and the consolidation can be computed for any point inside the layer during the consolidation process. His theory is based on the assumption that the change in stress is solely due to a change in water content and it may only be applied to one-dimensional consolidation phenomena. Other investiga-tors5,10 have expanded his theory to include processes of more than one dimension. The difference between the external pressures on the mud cake before and after sticking is a qualitative one (isolation of part of the cake by the static contact with the drill collars after pipe movement has been stopped)&apos;, and the time-dependent stresses thus created may be investigated by means of Terzaghi&apos;s theory. By this analysis the changes in the nature of the contact surface between the drill collars and the mud cake during the sticking can be explained; and the friction force between the two may be computed as a function of the sticking time, the borehole dimensions and the mud cake characteristics.

By Homer Staley

THE casting alloy 88 copper, 10 tin, 2 zinc, commonly known in England as Admiralty metal and in this country as Government bronze, gun metal, or Naval Department composition G, has, at its best, many valuable properties. However, its physical properties are known to vary widely with slight changes in method of manufacture of the castings, such as slight variations in composition, variation in pouring temperature, kind of mold used, method of pouring and gating of molds, size and shape of castings, amount and kind of heat treatment., and so forth.1 The microstructure of castings made from this alloy is influenced by slight variations of composition, rate of cooling, and kind and length of heat treatment. This is best understood by reference to the equilibrium diagram. The part of the diagram in which we are interested and the effect of the thermal equilibrium relations on the physical properties of the alloy 88 copper, 10 tin, 2 zinc, have been discussed by Hoyt, Camp-bell, Primrose, and Rawdon.2 In Fig. 1 is given the equilibrium diagram of the copper-tin alloys. Briefly stated, the relations of composition and temperature changes are as follows. Compositions between A and a consist of but one constituent-the a bronze, which is a, solid solution of copper and tin, rich in copper. On cooling from the molten state these compositions gradually crystallize, at temperatures above 790°, into a mass of interwoven tree-like crystals or dendrites. The cores of the dendrites are rich in copper and the percentage of tin gradually increases as the surfaces are approached. As cooling progresses, after all the metal has crystallized, no further changes occur, in the crystals other than diffusion within the crys-

Jan 9, 1919

By Norman Pilling

The deleterious effect on the mechanical properties of copper, resulting from heating in contact with reducing gases, is well known, but the mechanism of the action does not appear to have been definitely established. The purpose of the present investigation was not to determine the exact variations in physical quality of commercial copper, with its various impurities, as dependent upon the composition of the gas, temperature of exposure, etc., but rather to study the nature of the action and the conditions under which it occurs. The physical result of the so-called "gassing." of copper has been generally described as the development of "brittleness." There appears to be a striking decrease in tensile strength, associated with a considerable loss of ductility, and a small copper strip or wire affected in this way can he snapped in two when bent. Larger articles may have an outer layer alone affected, which can be detached from the core by hammering or bending. Perhaps the earliest reference to this subject is that of Heyn1 in 1900, and among the later observers may be mentioned Archbutt,2 Bengough and Hill,3 Johnson,4 Mathewson and Thalheimer,5 and Ruder .6 Bengough and Hill, while working with arsenical copper, were the first to suggest the possibility of the formation of gases within the copper itself, while Ruder endeavored to explain the action by the reduction of the

Jan 10, 1918

By S. F. Shaw

THE Sierra Mojada mining district is situated in western Coahuila, about 8 km. east of the Chihuahua state line, and about one-half way from the northern to the southern extremity of the state. It is at the terminus of the Mexican Northern R. R., 125 km. northeast of Escalón, Chihuahua; also about 240 km. due west of Monclova, Coahuila. The altitude is approximately 1500 m. above sea level. The Sierra Mojada valley is about 10 km. long, from east to west, with a width of 1 to 2 km. It is approached from the east through the Puerto del Oro, where the Mexican Northern R. R. enters the valley; the slope from west to east is gentle. The Sierra Mojada, of which about. 300 m. is an almost vertical wall, bounds the valley on the south side; on the north side, the slope to the crest of Sierra Planchada is more gradual, rising only 200 or 300 m. above the valley. Water is relatively scarce in the district, and there are no running streams. The rainy season, usually beginning at the middle of June, lasts through July, and occasionally into August or September. In some years the rains fail entirely. The slope of the ground is such that nearly all the water immediately runs off. The arroyos along &apos;the flanks of the mountains are not very deep, but in heavy rains, sometimes approaching cloudbursts, a tremendous volume of water rushes down them, carrying large boulders. A certain amount of seepage collects in the agglomerate, lying below the conglomerate, and is retained in the local fractures. Some shallow wells have been sunk in this agglomerate, and one well over 150 m. deep was sunk on, the Volcan ranch, supplying about 76 1. (20 gal.) per min. A considerable supply of water is collected in large earth reservoirs in and below the town of Esmeralda. In ordinary years this supply will last until January or February, after which the Volcan well has to be depended on until the next rainy season.

Jan 8, 1922

By Noel Stearn

OF THE many instruments devised for the measurement of magnetic anomalies, the ordinary dip needle, by virtue of its superior simplicity of construction, facility of manipulation, and definiteness of interpretation, seems to merit serious attention as the instrument most readily applicable to the detection of magnetic anomalies of the higher order of magnitude. , In spite of the fact that it has been used for many years for the discovery of iron ore in Europe and in the Lake Superior region of America, its capabilities as a geological instrument have not yet been thoroughly plumbed. The Wisconsin Geological Survey, under Dr. W. 0. Hotchkiss, E. F. Bean, and H. R. Aldrich, has been most thorough in developing the technique of the instrument, and the results it has obtained have aroused a general interest in a more widespread use of geomagnetics as an exploration method and the dip needle as a geological instrument. The simplicity of the instrument is an especial advantage, as it can be used by anyone, regardless of his technical training; but to insure useful results not only is a knowledge of the background of geomagnetics necessary but also an understanding of the principles of the instrument itself.

Jan 1, 1928

By C. Schlumberger

IN the course of the past few years the authors and their associates have had different opportunities to study the electrical phenomena which accompany the oxidation of pipe lines. The causes of such phenomena are very similar to those which have been described under the name "spontaneous polarization" with reference to metallic orebodies,1 and can be investigated in the same manner. These investigations, however, until recently were of a scientific and theoretical character, and had not found any important practical application. During the year 1931, however, the authors treated several industrial corrosion problems for public utility companies. These problems usually had to be studied in towns or in densely populated areas, where it was well-nigh impossible, or very expensive, to dig pits and trenches in order to make electrical measurements on the pipe itself. The authors were thus led to evolve a method and apparatus permitting the study, from the surface, of the direction of the currents flowing from pipe lines. The purpose of the present paper is to discuss the results obtained in the course of these investigations. However, in consideration of the importance and interest of the work carried out by other scientists along the same lines, a separate chapter will be devoted to a summary of the results achieved up to the present time in the study of pipe line corrosion.

Jan 1, 1932

OPEN-HEARTH refractories are not merely an accessory to the furnace. They are the furnace, to all intents and purposes. The steel work of the main structure is merely an open frame which helps to support the refractories ; and the regenerators, a necessary part of the furnace system, consist almost entirely of refractories. Not only do refractories constitute the essential part of the furnace, but they also carry the liquid steel all the way to the point where it begins to solidify. On leaving the furnace the liquid passes through a refractory runner into a refractory-lined ladle, then through a refractory nozzle closed by a refractory stopper on the end of a rod protected by refractory sleeve bricks. The liquid is sometimes sent through an additional refractory- lined tundish, a supplementary ladle, or a refractory runner for bottom pouring, until it finally enters the iron mold in which it solidifies. Even in the mold, refractory materials are sometimes used to provide a nonconducting "hot top." This series, from runner and ladle to hot top, inclusive, is often referred to collectively as the "pouring-pit refractories." REFRACTORY RAW MATERIALS The raw materials available are best classified into basic and acid types. The principal basic raw materials are magnesite, dolomite, and chrome ore. The principal acid materials are silica in various natural forms, and fireclay. Magnesite. Austria was the principal source of magnesite (MgCO3) until recent years, when the Province of Quebec, in Canada, and the states of Nevada and Washington became important sources for the American steel industry. More recently these natural sources have been supplemented by the so-called "sea-water magnesite"-which is the name somewhat incorrectly given to magnesium hydroxide obtained as one of the products

Jan 1, 1964