By M. J. Collins

Pressure leaching of zinc sulphide concentrates has been practiced commercially for nearly two decades. The process, which includes direct leaching of concentrate with spent electrolyte in an autoclave, has been commercialized at four separate locations to date. In pilot studies carried out in the Dynatec lab in Fort Saskatchewan, dozens of additional zinc concentrates have been shown to be amenable to pressure leaching. This paper highlights recent improvements in zinc pressure leaching that have been identified through process development studies, and how the experience gained in these studies has been utilized in the development of a new copper pressure leach process.

Jan 1, 2000

By Norihiko Fukatsu

In order to use effectively the previously reported new sensing system for hydrogen and oxygen potentials in molten copper, the criteria of the potentials for getting sound castings have been determined in the laboratory experiment. The copper melt equilibrated with a given hydrogen and an oxygen potential was rapidly quenched in the crucible. The relations between the holding potentials and the gas porosity in the solidified sample were investigated by measuring the density of the sample and microscopic observations. It was found that the defects of the gas porosity became the maximum at the potentials where the dissolved amount of hydrogen and oxygen was in the mole ratio 2: I. The samples having the density more than 99% of the theoretical value were obtained in the higher oxygen and lower hydrogen potential region or in the lower oxygen and higher hydrogen potential region. The criteria thus determined were examined by comparing with the measured potentials in the practical easting machine. In tough-pitch copper casting, the problem due to gas porosity was found to be serious when the hydrogen potential increased. In the oxygen-free copper casting, the evolution of hydrogen was found not avoided. The gas porosity in the casting, however, was found eliminated when the oxygen potential was kept at a low value.

Jan 1, 2003

By Federica Paglietti

In this work is presented SEX (Structural & Elemental X-Ray Instrument), the first spectrometer completely portable which make non-destructive X-ray fluorescence and diffraction analysis, in contemporary and in real time. This instrument has been realized using miniaturized detectors, the same model installed on the mission Pathfinder NASA, and X-ray microtubes. SEX allows the chemical and mineplogical characterization of all kind of solid materials and allows to make chemical stratigraphy and liquids analysis.

Jan 1, 1998

By Norihiko Fukatsu

In order to use effectively the previously reported new sensing system for hydrogen and oxygen potentials in molten copper, the criteria of the potentials for getting sound castings have been determined in the laboratory experiment. The copper melt equilibrated with a given hydrogen and an oxygen potential was rapidly quenched in the crucible. The relations between the holding potentials and the gas porosity in the solidified sample were investigated by measuring the density of the sample and microscopic observations. It was found that the defects of the gas porosity became the maximum at the potentials where the dissolved amount of hydrogen and oxygen was in the mole ratio 2:1. The samples having the density more than 99% of the theoretieal value were obtained in the higher oxygen and lower hydrogen potential region or in the lower oxygen and higher hydrogen potential region. The criteria thus determined were examined by comparing with the measured potentials in the practical casting machine. In tough-pitch copper casting, the problem due to gas porosity was found to be serious when the hydrogen potential increased. In the. oxygen-free copper casting, the evolution of hydrogen was found not avoided. The gas porosity in the casting, however, was found eliminated when the oxygen potential was kept at a low value.

Jan 1, 2003

By P. Louis

Although cobalt is known and used for its hardness and wear resistance, ductile cobalt can be obtained by electrolysis in chloride solutions, under the following conditions : pH : 1.5 - 2, Co++ : 30 - 60 g/l, current density : 100 - 500 A/m2, temperature 40 - 70°C. No explanation was found for the ductility of the deposit under these conditions. Indeed the ductile P (FCC) cobalt and the hydrogen contents in the cobalt deposits are nearly the same as those obtained in a sulfate media, which gives brittle depo¬sits under equivalent electrolysis conditions. Malleable cobalt sheets can be easily obtained under the proposed conditions which could lead to new applications for cobalt.

Jan 1, 1988

By Li. Jiarong, Zuojian Liang, Qingyan Xu, Baicheng Liu, Shizhong Liu, Hailong Yuan

Single crystal solidification of turbine blades is a key technology for the production of reliable and high efficiency gas turbines. The solidification process of single crystal investment castings causes a number of problems that have to be solved such as the increase of casting defects and complexity of production process. Computer modeling and simulation is helpful to predict the defects and improve the process design. In the paper, a mathematical model for three dimensional simulation of solidification and single crystal growth of investment castings was developed based on CA, mechanism of crystal growth and basic transfer equations such as heat, mass transfer equations. Many factors including constitutional undercooling, curvature undercooling and anisotropy, which had vital influences on microstructure evolution, were considered in the model. Temperature, crystal growth interface and structure defects of investment castings of single crystal superalloy were investigated at withdrawal rates of 4.5mm/min and 7mm/min. Simulated results showed that microstructure evolution and structure defects were predicted reasonably and calculated results were coincident with experimental ones. The study indicated that three dimensional solidification simulation technique is a powerful tool for understanding the fundamental of solidification and the formation of structure defects in single crystal investment castings and finally for optimizing process design.

Jan 1, 2004

By H. Hirayama, T. Okura, O. Kato

"Saganoseki Smelter & Refinery, one of the largest copper smelters in the world, has the annual capacity of 300,000 metric tons in copper content with two flash furnaces, six Pierce-Smith type converters, two anode furnaces, four acid plants, three tank houses and perfect pollution control system.Coping with the many severe conditions surrounding the copper industry in the last decade, Saganoseki Smelter has kept performing the stable operation, while enhancing the smelting capacity and developing new technologies such as the hydrometallurgical treating of converter dust recovered at electric precipitators. Especially in the operation of flash furnaces, which are of Nippon Mining's conversion type using hot air in a temperature of l,000ºC some technological improvements and complete operation control factors have approved the concentrate feed rate to reach to 2,200 tons a day for a flash furnace.Reported in this paper are the production control design for copper smelting process, and the operation control scheme of the flash furnace following the brief review of the characteristic of Saganoseki Smelter's process and some improvements. Copper Smelting ProcessDescriptions of major unit operations and general specifications of the copper smelting facilities are summarized in Table 1, and the present flowsheet of the copper smelting is described in Figure 1 (1,2).Outputs and raw materials treated in the last five years are shown in Table 2, in which concentrate includes powder copper scrap which amounts to 3 to 4% of concentrate.A full operation was performed for a period of one month, for both one flash furnace operation and for two flash furnace operation. With one furnace operation, 19,200 tons of copper were produced. With the two furnace operation, 84,000 tons of concentrates were charged and 33,500 tons of anode (net 28,600 tons of copper) were produced.The actual production level, however, has been kept at 80 to 90% of the full capacity because of low copper price, tight market of copper concentrate or fall of net demand in Japan."

Jan 1, 1989

By B. C. Blakey

The economic feasibility of the sulphuric acid pressure leaching route for the extraction of nickel and cobalt values from limonitic ores is highly dependent upon the behavior of aqueous aluminium. This is primarily due to its precipitation as hydronium alunite ((H30)A13(S04)2(OH)6), which is one of the major scale-forming compounds found in autoclaves used for pressure leaching. As a result of renewed interest in the pressure leaching process, an investigation of the aqueous-solid eqilibria in the aluminium-sulphate-water system under acidic (< pH l), high temperature (230 to 270°C) conditions has been conducted. Pure hydronium alunite was synthesized in an autoclave by leaching boehmite (A100H) at elevated temperatures in sulphuric acid solutions initially 0.25 to 0.75 m H2S04 in concentration. Spontaneous, in situ precipitation of hydronium alunite followed. A high temperature solution speciation model was used for the analysis of the resulting solubility data in order to calculate equilibrium constants for the precipitation reaction.

Jan 1, 1994

By K. Dzieciol

The paper presents a study about three image correlation methods ?common cross-correlation, mutual information and phase-correlation ? applied to characterize microstructures reconstructed with X-ray tomography. It is shown that phase correlation is not only the fastest, but also the most sensitive method for detection of similar microstructure features, cavities in the present case. A new image correlation indicator is proposed, which takes into account both the phase shift and the amplitude of similar features in compared images. Some preprocessing aspects related to the tomographic reconstruction and filtering out of characteristic noise are also discussed.

Jan 1, 2009

By Harry Littleton, Jr. Scarber, Wanliang Sun

"The Lost Foam Casting (LFC) process is relatively immature when compared to other casting processes. To make the process more robust, computer modeling is needed to reduce lead times and casting defects. In this study, metal filling of lost foam aluminum castings was visualized using state-of-art real time X-Ray technology. Metal filling of the lost foam casting was simulated using a commercial software package. The result of the computer simulation was compared with the results of the real time X-Ray visualization. Some of the computer simulation results agreed with the real time X-Ray visualization, but some did not. Based on other studies using real time X-Ray technology, new input variables, such as foam density variations, were developed for the computer modeling. With the new variables, modeling of the lost foam casting process becomes more realistic. IntroductionMold filling of the Lost Foam Casting (LFC) process is an important step toward making a quality part. In the LFC process, molten metal is poured against a refractory coated foam pattern surrounded by dry sand. At the pouring temperature of aluminum, the foam pattern is decomposed into 30% (wt) gaseous and 70% (wt) liquid foam pyrolysis products. Existence of the gaseous foam decomposition products significantly increases the back pressure on the metal stream compared with the conventional open cavity sand mold. Entrapment of the liquid pyrolysis products during the metal filling generates many casting defects, such as internal pores, fold and blisters. Existence of these casting defects sometimes seriously degrades the quality of the components manufactured by the LFC process. Understanding and controlling the metal filling of the LFC process will certainly make this process more robust."

Jan 1, 2004

By Michael E. Stout

The recovery of the constituent components of spent lead acid batteries was pioneered in the early 1970&apos;s by M.A. Industries, Inc. MA&apos;s main reason for research and development in this area was to recover the polypropylene casings for use as feed stock in their injection molding plants. At that time spent and reject casings were either disposed of or being fed with the lead &apos;bearing materials into the ,smelting process. M.A. has since developed, built and operated plant for the conversion of scrap casing into reusable copolymer resins. The system is composed, of washing, .sizing, extrusion and pelletizing the polymer into a form which is ready to be injection molded into new products.

Jan 1, 1995

By D. J. Wang

Based on the thermodynamic arid kinectic aspects, the vaccum distillation processes for the separation and recovery of metals from wastes are analyzed. As to the separation criteria, The separation coefficient and equilibrium composition relation between vapor phase and liquid phase are the bases of recovery of metals by vacuum distillation, The vaporization rates and condensation mechanisms are also discussed. Some experimental results which deal with metals-containing wastes are described and the performances of a new kind of horizontal vacuum furnace are introduced, which demonstrate that , vacuum distillation may be a prospective technique for circulation and regeneration of some non-ferrous metals from industrial wastes.

Jan 1, 1996

By Qiang Yu

This paper reports on a research project supported by NSF, which aims at developing a multi-scale methodology for systematic microstructure prediction in thermo-mechanical processing of metals. This methodology is based on combining mesoscopic microstructure models with macroscopic process formulations and involves the following three main steps: (I) based on the given global processing conditions, the gross deformation patternof the entire workpiece is modeled using a continuum-based algorithm, (2) the resulting parameters are then extracted from the continuum-based simulation, post-processed and passed on to the mesoscopic numerical module, and (3) the microstructural changes are finally modeled at the mesoscopic scale. This approach is expected to overcome the disadvantages of current microstructure prediction practice employing empirical relationships between microstructural features and processing parameters. Keywords: Thermo-mechanical processing, Microstructure, Grain growth; Recrystallization; Mesoscopic models; Finite Element Method

Jan 1, 2003

By Gabriel Riveros, Ariel Balocchi, Andrzej Warczok, Daniel Smith

Blister copper from converting of copper matte is processed by fire refining prior to electrorefining. The fire refining consists of two steps: copper oxidation with impurities slagging and copper reduction. The classical batch process is carried out in vascular or reverberatory furnaces called anode furnaces. A new process for continuous copper fire refining has been proposed. The copper flows through two reactors in cascade, where is oxidized and reduced. The flow of a liquid copper through a ceramic packed bed increases the surface area and the rate of oxidation as well as the rate of reduction in the packed bed of charcoal. Mathematical modelling allowed for the design of a laboratory scale demonstration installation and industrial-pilot installation in Hernan Videla Lira Smelter (Paipote). The results have demonstrated the process feasibility and flexibility in operation.

Jan 1, 2009

By Klaus Bauckhage

Phase-Doppler-anemometry (PDA)-measurements have to be taken from representative measuring positions from inside the spray cone, helping - with the support of simulated data of improved process models - to describe the multiphase flow situations within the spray cone - and accordingly to that - the heat transfer conditions for the rapid cooling and (partly) solidifying melt droplets before their impact onto the substratddeposit. Simulations and PDA-measurements thus give the base to confirm the hypothesis of the existence of a semisolid mixed-layer and it&apos;s influence on the resulting material structure during compaction. The dispersed particles in the spray cone exhibit a cooling and solidification process within a split of a second, which leads - as far as the particles solidify - to a dendritic structure with very short dendritic arm spacings. This causes within the particles extremely short distances for the following equalizing diffision processes taking place on a high temperature level (between liquidus and solidus) in the semisolid mixed-layer of the deposit and explaining the short residence times within this zone of only seconds up to a few minutes. This and the fact that the globular structure of the mushy zone (in the semisolid mixed-layer) leads to an unidirectional crystallization process over very short distances also explains the chemical and morphological ,homogeneity of the sprayed material. The dynamics of these process steps, the very special buffer function of the mixing layer during parameter variations as well as the controlled cooling process of the preform in order to avoid hot cracks influence the quality of the material. Due to the necessity of measuring and controlling the particle bound mass-, momentum- and enthalpy- fluxes to the deposit the PDA-technique has been adapted and modified in order to receive in-line and (in the future) also on-line data from the dynamics of the multiphase flow conditions within the spray chamber.

Jan 1, 1999

By Keuncheol Choi, Yonghack Lee

"The new lead smelter based on the QSL technology was started operation from May 1992 at Onsan Refinery of Korea Zinc Co., Ltd. The smelter is designed to treat not only various types of lead concentrate but also secondary materials coming from the zinc plant without special pretreatment.Shortly after the start-up of the operation, it has demonstrated that the smelter have a capability to treat wide range of raw materials. Continuous modifications and improvements of the plant are still under way to increase the feed rate and also the ratio of secondary materials to the feed.In this paper, the operating experience and results of QSL smelter, especially the injection of gases and coal to the melt, will be presented with major operation parameters and data.INTRODUCTIONThe QSL lead smelter based on new injection technology was commissioned at the Korea Zinc's Onsan plant from May of 1992. After starting the operation, the QSL lead smelter faced various kinds of mechanical and metallurgical troubles. However, these were gradually worked out by the continuous improvements and efforts.At present, the QSL lead smelter is operated stably at the total feed rate of 57 tonnes per hour with an increased amount of secondary materials."

Jan 1, 1996

By C. Frias, M. Garcia, G. Diaz

Advances in hydrometallurgy promoted by Tecnicas Reunidas are providing increasingly simple and clean means for controlling the entire lead recycling chain. Used in parallel with pyrometallurgy, these processes allow furnace temperatures to be reduced and fumes and atmospheric pollution to be minimised. Furnace slags are digested, and residues (mainly gypsum) are non-toxic and convertible into marketable products. In addition, the global economy of the process is substantially improved by reducing the operating cost, increasing the lead recovery above 99% and obtaining a 99.99% pure lead product. These new PLACID and PLINT processes may provide the cleanest and healthiest practicable means for recycling lead from batteries.

Jan 1, 2000

By E. Gutierrez-Miravete

A computational method for the simulation of mold filling processes is described. The method is based on the representation of the flowing or deforming medium as a collection of mutually interacting parcels of material. Instantaneous positions of individual material parcels are calculated by numerical integration of the dynamic equations, subject to appropriate initial and boundary conditions. So far, the method has been used to produce qualitative simulations of some flowing and deforming systems encountered in mold filling technology, and our findings are summarized herein. In all cases, individual material particle motions can be followed in detail, allowing critical examination of potentially problematic mold design features.

Jan 1, 1992

By Norbert L. Piret

From the copper smelter operation a various outputs are to exert negative impacts on the environment. Particularly, emissions like SO2 and dusts, solid wastes like contaminated gypsum and arsenic sludge, effluents and heated cooling water are generated. Most countries have sitipulated an environmental legislation to provide the framework for an efficient environmental management. As part of the planning activities for x major greenfield copper smelter, the Following elaborations are required and were drawn up. -The Environmental Impact Assessment which is the first step of environmental management and mandatory for every new project. - The Environmental Monitoring Plan, which describes the monitoring procedures for the main impacts identified and assessed. -The Environmental Management Plan, which deals with the minimization of environmental impacts, and the methods of its implementation.

Jan 1, 1996

By Joel Anderson

Allvac 718Plus is a newly developed superalloy with a good potential for use in fabricated aircraft engine structures when service temperatures exceed 650°C; the limit for standard alloy 718. Fabrication involves welding, where cracking usually is a prohibitive factor. Comparison of the solidification cracking behavior between these two alloys was made by Transvarestraint testing. It was shown that the total amount of cracking was significantly lower for 718Plus alloy, which was associated with a lower amount of ?/Laves or ?/NbC eutectic-type constituents. This in turn is believed to be due to the lower iron content of the Allvac 718Plus material. The analysis of alloying element segregation both within primary dendrite and interdendritic constituents clearly indicates that the segregation of Nb is the controlling factor in determining the final solidification microstructure in these alloys. The Nb concentrations of these constituents are significantly higher compared to the bulk alloy concentration. This was confirmed by the SEM-EDS analysis and calculations assessed with JMatPro, the latter also indicated that alloy 718 is more prone to form Laves and NbC eutectic-type constituents compared to Allvac 718Plus material.

Jan 1, 2008