By H. M. Strong, R. A. Oriani

THE technological interest attaching to light, age-hardening alloys for structural uses has been pointed out to one of us.1 A potentially interesting alloy would be titanium-rich Ti-Mg alloy, provided that sufficient solid solubility exists. or could be induced at high pressure. and provided also that age hardening can be induced by proper temperature and/or pressure annealing. It was decided therefore to explore the feasibility of producing a Ti-Mg alloy in the high-pressure apparatus. Experimental. Three high-pressure runs have been carried out. In each case the geometry of the sample was that of a cylinder of titanium of commercial purity, into which a narrow hole had been drilled along the axis; this hole was filled with magnesium wire,

Jan 1, 1967

By Carl E. Williams

A computer program has been developed which will locate the economic limits of an open-pit mine and also designate which ore and waste blocks to remove per period (years or quarters) to maximize the discounted cash flow over the life of the mine. A set of operating constraints was carefully selected so that the following functions are controlled: (1) the removal of overburden by preproduction and production stripping exposes a fixed amount of ore; (2) a constant manpower and equipment usage is insured (except for trucks); (3) the tons of mill ore, concentrate, and stockpiled ore are regulated; (4) the number and extent of shovel moves are minimized; (5) the grindability of the rock is considered as well as the variable haulage cost caused by variable haulage distances and depths; and (6) the size of the shovel working area is regulated. As many as 50 alternate schedules can be produced per computer run. They are arranged in descending order starting with the best solution.

Jan 1, 1975

By N. G. W. Cook

At present, tunnels can be driven in rock by either of two essentially different techniques, in one of which rock-breaking is accomplished by drilling and blasting and in the other by mechanical loading. The methods based on these techniques are comparable in terms of the rates at which tunnels may be advanced, although they differ widely in their range of applicability to different types of rock and lengths of tunnel. The method based on drilling and blasting has reached a high degree of development. It is applicable to even the hardest rocks and rates of advance in excess of 50 ft per day (fpd) are attainable. The main disadvantages of this method are that it involves a sequence of operations punctuated by blasting and that it is relatively uncontrolled, resulting in overbreaking the tunnel profile and damage to the surrounding rock. However, its flexibility, mobility, and low capital cost constitute real advantages in many situations, such as those involving short lengths of tunnel or low rates of advance. Tunneling machines based on mechanical breaking of the rock are a more recent development. They offer a continuous and controlled means of tunneling capable of rates of advance in excess of 100 fpd under favorable conditions. However, these machines weigh many tens of tons and consume several hundred horsepower, so that they are costly and lack mobility. At present, their applicability is limited to long tunnels in relatively soft rock where the high rates of advance and tunnel quality can offset their onerous capital cost. Many situations exist in which the superior quality of a machined tunnel and freedom from blasting would be real advantages, but where the rock is either too hard for existing machines or the length of the tunnel does not justify their capital cost: What are the possibilities of developing cheaper, more flexible, and mobile tunneling machines? Most existing tunneling machines fragment all the rock at the tunnel face to facilitate its disposal. If a machine were used to cut only the profile of a tunnel as one of a sequence of operations, it would be required to break

Jan 1, 1970

Coal Division Industrial Minerals Division Minerals Beneficiation Division Mineral Economics Division Mineral Industry Education Division Mining, Geology and Geophysics Division MINING BRANCH AND DIVISIONS OFFICERS AND COMMITTEES Council Ralph E Kirk, '55, Chairman (Coal). C M Cooley, Secretary, M D Cooper, '56 (Coal), Harold Bannennan. '55 (Ind Min Div ). R C Stephenson, '56 (Ind Min Div ) , E P Pfleider, '55 (MGGD) . J D Forrester. '56 (MGGD) , Donald W Scott, '55 (MBD). S D Michaelson, '56 (MBD). J K Richardson (MED). J R Van Pelt, Jr (MIED) COAL DIVISION Established as a Division September 20, 1929 M D Cooper. Chairman H F Yancey, Chairman-elect David R Mitchell, Secretary-Treasurer Professor of Mining The Pennsylvania State University State College. Pennsylvania

Jan 1, 1954

By Paul R. La Pointe

GEOTECHNICAL OBJECTIVES OF UCG PROGRAM Underground coal gasification (UCG) is one of several in situ extraction technologies for utilizing deep, otherwise unmineable coal. This technology involves the injection of air or oxygen into the target coal seam, ignition of the coal and recovery of product gases. Geotechnical characteristics of the coal and enclosing rock strata strongly influence the success of this Process. The flame front follows the coal cleats (Hill, 1979), and cleating and bedding control the manner in which coal collapses into the cavity, thereby affecting recovery efficiency (Ramirez and others, 1982). Moreover, coal seams typically behave as fracture dominated aquifers in which cleat orientations govern subsequent contaminant dispersal. For these reasons, the Anaconda Minerals Co. undertook a detailed study of fracturing within the Wyodak-Anderson Coal in the eastern Powder River Basin (PRB) near its Rocky Hill UCG test site (Fig. 1). STRESS HISTORY AND FRACTURING IN THE POWDER RIVER BASIN Vertical jointing, or cleating, in coals may arise from shrinkage shortly after deposition under low confining pressures, or later in time, soon after burial but after the coalification process is well advanced (Ting, 1977). There is much evidence to support the formation of cleating after coalification (e.g. Hawkes and Mellor, 1970; McCulloch and others, 1974), which suggests that the stress state existing at that time strongly influences cleat formation. McCulloch and others (1974) argue that the typically better developed face cleat forms parallel to the plane containing [ol] and [o2]. Where the relation between cleats and stess has been studied (McCulloch and others, 1974; Stone and Snoeberger, 1977; Ward, 1977; Kulander and Dean, 1978), the highly systematic face cleat strongly parallels the [o1] direction. Stone and Snoeberger (1977) report face and butt cleat measurements of N70E and N29W for the Felix Coals 220 m stratigraphically above the Wyodak at the Hoe Creek UCG site (Fig. 1). Structural trends also indicate the past state of stress in the PRB. Glaze and Keller (1963) suggest that the NE-SW regional compression during the late Permian formed major N-S fold lines and basement magnetic anomalies. Mapel (1959) describes folds having N60W and N30W rends in the northern PRB, as well as a large normal fault trending northeast. Glass (1976) also describes normal faults trending northeast. Similarly, Olive (1957) mapped normal faults

Jan 1, 1984

By H. H. Uhlig

IN our study of the mechanism of and the prevention of corrosion in stainless steels, it was considered of fundamental importance to obtain knowledge of the surface structure of such alloys. If corrosion resistance is due to a self-healing oxide layer, which like a paint film protects the underlying metal, it would be obviously relevant were the effort made to make the film less permeable and more adherent; for example, the surface might be expected to respond to an anodizing process, which is found successful in increasing the film thickness and corrosion resistance of aluminum. However, if passivity and corrosion resistance of stainless steels are due to another cause, the attack of the problem would follow another path. One of the most effective techniques for studying passivity and corrosion tendency is the measurement of the electrochemical potential. Not only can one determine by potential measurements whether a metal is active or passive, but also one can determine the degree of passivity and rate of transformation of passivity with time. Chemical media that build up or destroy passivity when in contact with the steel can also be classified by potential measurements. Something can be learned, too, of the effect of alloy additions such as molybdenum to 18-8, known to decrease corrosion of the alloy in chloride solutions. A study of alloys in previous investigations has sometimes included data on the electrochemical potentials. Tammann and Sotter1 measured the electrochemical potentials of alloys of iron-molybdenum and iron-chromium and reported the critical concentration of molybdenum or chromium at which passivity initiates. Strauss2 made similar measure-ments for the iron-chromium system. The electrochemical potential' has also been used to indicate carbide precipitated 18-8. In 18-8, heat-treated to precipitate carbide, active metal exists at the region of the grain boundaries, contrasted with passive metal within the grains, the active metal accounting for a resultant active potential. Several

Jan 1, 1939

By W. E. D. Stokes

WHEN history is written, the year of the blitzkrieg will go down as giving aviation its greatest impetus. No perceptible drop in military business, even with cessation of hostilities abroad, seems likely. The combined air force of the U. S. Army and Navy on July 1 was approximately 5000 planes, as against 50,000 planes currently discussed as necessary. Observers at the fronts are giving designers and metallurgists back home some realistic ideas to shoot at. As conventional runways reveal the location of airports to enemy raiders, operating bases are now masked. Difficult, often muddy and rough landing strips, requiring strong landing gears and exacting take-off and maintenance characteristics, are the specifications of war. This is "old stuff" to numerous mining operators in mountainous jungle areas where gradients up to 8 per cent are in more or less common use in such mountain landing fields. Although airplane building is not readily adaptable to assembly-line methods, a trend towards mass productions is now in evidence. Incidentally, a U.S. Army "Curtiss P-40" requires about 10,000 man hours of work to complete and is tied together with 75,000 rivets. During the past year a number of aircraft factories adopted the "shot-

Jan 1, 1941

By F. W. Jessen, C. A. Johnson

The effect of treatment with ferrochrome lignosul-fonate on both sodium and calcium bentonites has been examined. In the early stages of treatment it appears that some base exchange of iron and chromium for sodium may occur with the sodium bentonite. Such exchange appears specific for exchange of sodium ions when the calcium ion concentration represents 40-5.5 per cent of the total exchangeable cations, and when additions of lignosulfonate are less than 1 lb per bbl. Adsorption appears entirely physical above 1 lb per bbl treatment level for all concentrations of calcium studied. Gel strength and plastic viscosity of both calcium and sodium bentonite systems were reduced with treatments of ferrochrome lignosulfonate up to 2 Ib per bbl, the greatest reduction occurring within a range of calcium concentration of 40-5.5 per cent of the total exchange capacity of the clay. INTRODUCTION The problem of control of viscosity and gel strength of drilling fluids by the action of thinners or dispersants has been studied by many investigators.1-7 In addition, much work has been done on formation of gel structure in clay suspensions. However, gel formation and structure still are incompletely understood, and the use of the various dispersing chemicals is based, to a large extent, on data almost entirely empirical in nature. In recent years the lignosulfonates have become increasingly important in the treatment and control of drilling fluids. More specifically, ferrochrome lignosulfonate has found rather wide acceptance, particularly in calcium systems.5-7 Lignosulfonates are refined lignin products made from spent sulfite liquor from which the fermentable sugars have been removed.15 The exact structure of lignin is not known; however, it is believed to be a phenolic propane type polymer which may exist as a branched chain or cross linked structure. The molecular weights of lignosulfonates probably range from 300 to 100,000 or more.15 A better understanding of the mechanism of adsorption of dispersants is essential before improvement and development of characteristics of drilling fluids and drilling fluid control is possible. This investigation was undertaken to determine the action of ferrochrome lignosulfonate on sodium and calcium montmOrillonite' LABORATORY INVESTIGATION A Stormer viscosimeter and Fann V-G meter were used to measure viscosity and gel strength. A Zeiss spectrophotometer was used for analysis of Fe and Cr and the flame attachment was employed in the analysis of Na, Ca and Mg. A General Electric X-ray diffraction unit utilizing Copper Ka radiation and a Ni-filter was utilized in the X-ray studies. PROCEDURE Two systems were studied. Predominately sodium clay, obtained from Wyoming, and a predominately calcium clay from Texas were used. These particular samples were chosen because of the extensive work of characterization completed by Mungan. Ionic base exchange capacity determined by flame photometry and total exchange capacity by the Kjehldahl method were obtained experimentally. A 7-per cent suspension of the sodium clay and a 20-per cent suspension of the calcium clay in distilled water were prepared by mixing with a high-speed mixer. The suspensions were allowed to stand for two weeks for complete hydration. Calcium chloride was added to portions of the sodium and calcium cla suspensions to obtain suspensions varying in Ca++ concentration as shown in Table I. A series of treatments was run with 500-ml portions of the original suspensions using a ferrochrome lignosulfonate. Treatment was carried out in the same way with each of the suspensions of varying Ca concentration. Viscosity and gel strength were measured and a filtrate obtained at each treatment level. Ten ml of filtrate were diluted to 50 ml, and aliquot portions of the 50 ml were taken for the Na, Ca, and Mg analysis by the flame photometer. The pH of these filtrates ranged from 7 to 7.3. Standard

By Robert E. Brand, Strathmore R. B. Cooke

For a study of the bonding that occurs in magnetite pellets during oxidation, cubes of magnetite, hematite, and quartz were prepared, each with one surface polished and nearly optically plane. These faces were fired together under pressure and at various temperatures to determine whether bonding would occur. Sections of surfaces that bonded were examined microscopically. An attempt was made to measure the strength effected by this treatment. EARLIER work1,2 has shown that the strength developed by fired magnetite pellets containing silica or silicates is due to three separate effects. Two of these are associated with the formation of slag in the interior of each pellet at temperatures above 1000°C, where the atmosphere is substantially though temporarily neutral. The third is independent of the silica content and is responsible for the development of a hard shell around the pellet during the initial stages of firing, a condition which permits the pellet to assume the increasing load of the overlying burden and prevents extrusion of the slagged and semi-liquid interior. Pellets made from hematite concentrates do not show these effects unless specific additives are incorporated, and it is these differences in behavior which in large part account for the difficulty in producing satisfactory pellets from such concentrates. Elsewhere it has been stated that "the most important factor responsible for the development of strength in fired magnetite pellets containing no additive is the oxidation of magnetite to hematite and the subsequent recrystallization and grain growth of this constituent."' The object of the investigation reported in the present paper was to study in detail the mechanism described above and to evaluate its contribution to the strength of the fired pellet compared with other possible mechanisms, excluding slag bonding. This was effected by placing together polished faces of two cubes prepared from specific minerals and then heating them under constant pressure at different temperatures both in air and in nitrogen. The materials used were magnetite, hematite, and quartz. The magnetite was coarsely crystalline material from western Montana, the hematite was Itabira ore from Brazil, and the quartz was of optical grade but of unknown origin. A high-grade Lebanon (Pennsylvania) magnetite concentrate was used to prepare briquets for the investigation of bonding strength. Analyses of the iron oxide materials are given in Table I. The specimens for furnace treatment were prepared with a carborundum cut-off wheel, which cut the minerals into cubes approximating % in. along each edge. Care was taken to make the sides as parallel as possible. The edges of the faces to be polished were beveled, and the cubes were mounted in brass rings with sealing wax, this being essential to prevent the specimens from rocking during polishing. To prevent excessive friction, the wax was recessed so that only the brass ring and the face of each specimen would be in contact with the polishing lap. Each specimen was then ground with No. 600 carborundum to produce a level surface before polishing. The Graton-Vanderwilt process was not used for polishing because of the long time required by this method, but several other methods were tried. Cloth laps using levigated alumina or chromium oxide did not produce the desired polish. Satisfactory results were obtained by means of a pitch lap: which was used for all the mineral cubes, with levigated alumina as the polishing medium. The lap was operated in a machine similar to those used in the preparation of single optical surfaces. It was run at low speeds and moderate pressures, and polishing was stopped occasionally to prevent overheating of the lap. A good polish with flat surfaces could be obtained in about 5 min. After polishing the sealing wax was removed either in hot water or in a solvent such as turpentine.

Jan 1, 1955

By Martin A. Moyers

THE nation's effort to win the war speedily is reflected in current trends in coal utilization, as in all other fields of our lives. In all industries, wherever coal is used for the production of heat and power the emphasis is on getting the most useful result with the least expenditure of matt.ria1. In addition to carrying its own share of the load, increased as it is by the demands of war industry, coal has had to fill in for the other fuels, mainly petroleum products, whose distribution from their more distant sources has been crippled by lack of shipping. Thus, the outstanding note in the utilization of coal this year is not the development of new methods of burning or handling coal but the extraordinary job that the industry has done in producing enough coal to serve all needs.

Jan 1, 1943

By Lewis T. Wright

(Pittsburg Meeting, March, 1910.) I HAVE long been aware that ferruginous copper furnace slags if fused in the electric arc will yield metallic iron containing copper, and in order to confirm this knowledge, and to obtain further information of the behavior of such slags in the high temperature and reducing conditions of the electric furnace, a number of samples of slag were fused in an experimental electric furnace. The results obtained, given in Table I., show that a very large amount of metallic iron was produced, and that this iron carried with it practically all the copper, gold, and silver, and more than 50 per cent. of the sulphur, of the original slag. The metallic buttons formed in the electric furnace were clean, hard, but not brittle.

Mar 1, 1910

By A. L. Lee, M. H. Gonzalez, R. F. Bukacek

Experimental viscosity data for methane are presented for temperatures from 100 to 340F and pressures from 200 to 8,000 psia. A summary is given of the available data for methane, and a comparison is presented for that data common to the experimental range reported in this paper. Correlation of the data is presented, and predicted values are given for temperatures up to 460F and pressures up to 10,000 psia. INTRODUCTION The increasing ranges of temperature and pressure at which fluids are produced, transferred and processed in the petroleum and chemical industries stress the need for accurate information on physical properties, both for engineering calculation and for improving the methods used to estimate physical properties. A survey of the literature reveals that disagreements between published data on the viscosity of methane are common and that most investigations have been conducted over restricted temperature and pressure ranges. This situation made it desirable to undertake an investigation with a scope common to most of the literature data available. APPARATUS AND MATERIALS The apparatus used in this investigation was the capillary tube viscometer'described by Dolan,10 with modifications introduced in the general design and operation of the instrument. It has an effective pressure range from 14.7 to 10,000 psia and a temperature range from room temperature to 400F. The design of the viscometer is based on the establishment of a manometric head between two vessels containing the test fluid and a volume of mercury. The reservoirs are connected by a capillary tube through which the test fluid flows and a tube through which mercury flows. A pressure gradient is established by elevating one of the vessels above the other, the resulting flow of mercury displacing the test fluid through the capillary. The schematic diagram of the system (Fig. 1) shows the arrangement of the equipment auxiliary to the viscometer. The density cells assembly (E, Fig. 1) was not used in this investigation since reliable data are available on methane. 23 The assembly consists of a bank of eight 316 stainless steel pycnometers. Experimental values of the density of a natural gas19 and i-butane14 samples have been obtained for pressures up to 8,000 psia and temperatures up to 340F. The methane used was obtained from the Southern California Gas Co. Mass spectrometric analysis showed a composition of 99.8 percent CH4, 0.1 percent C2H6 and 0.1 percent C3H8. EXPERIMENTAL VALUES AND ACCURACY OF DATA Determinations were carried out at several temperatures. With the temperature in the cabinet controlled at a given level, a series of runs were made at various pressures. To establish pressures lower than that obtained from the methane cylinder, it was necessary to vent the gas slowly to the atmosphere until the desired pressure was reached. The consistency of the test run time for a particular condition can be used as a criterion for the accuracy of the data. A further check is obtained by comparison of the viscosity values obtained using different driving heads. To establish the instrument's reproducibility, a large number of runs were made at three completely different conditions of temperature and pressure. Data obtained were analyzed statistically to determine the most reliable value for the variance of the experimental data. It was found that the variances of the data taken at different experimental conditions were not statistically equivalent, but they were small. The largest variance was found at 8,000 psia and 100F, where the standard deviation was 0.385 micropoise. Therefore, 99.9 percent of the data can be expected to fall within 1.15 micropoises of the population mean, except for the intervention of systematic errors in operation.

By H. H. Uhlig

In our study of the mechanism of and the prevention of corrosion in stainless steels, it was considered of fundamental importance to obtain knowledge of the surface structure of such alloys. If corrosion resistance is due to a self-healing oxide layer, which like a paint film protects the underlying metal, it would be obviously relevant were the effort made to make the film less permeable and more adherent; for example, the surface might be expected to respond to an anodizing process, which is found successful in increasing the film thickness and corrosion resistance of aluminum. However, if passivity and corrosion resistance of stainless steels are due to another cause, the attack of the problem would follow another path. One of the most effective techniques for studying passivity and corrosion tendency is the measurement of the electrochemical potential. Not only can one determine by potential measurements whether a metal is active or passive, but also one can determine the degree of passivity and rate of transformation of passivity with time. Chemical media that build up or destroy passivity when in contact with the steel can also be classified by potential measurements. Something can be learned, too, of the effect of alloy additions such as molybdenum to 18-8, known to decrease corrosion of the alloy in chloride solutions. A study of alloys in previous investigations has sometimes included data on the electrochemical potentials. Tammann and Sotterl measured the electrochenlical potentials of alloys of iron-molybdenum and iron-chromium and reperted the critical concentration of molybdenum or chromium at which passivity initiates. Strauss2 made similar measurements for the iron-chromium system. The electrochemical potential3 has also been used to indicate carbide precipitated 18-8. In 18-8, heat-treated to precipitate carbide, active metal exists at the region of the grain boundaries, contrasted with passive metal within the grains, the active metal accounting for a resultant active potential. Several

Jan 1, 1940

By H. H. Uhlig

In our study of the mechanism of and the prevention of corrosion in stainless steels, it was considered of fundamental importance to obtain knowledge of the surface structure of such alloys. If corrosion resistance is due to a self-healing oxide layer, which like a paint film protects the underlying metal, it would be obviously relevant were the effort made to make the film less permeable and more adherent; for example, the surface might be expected to respond to an anodizing process, which is found successful in increasing the film thickness and corrosion resistance of aluminum. However, if passivity and corrosion resistance of stainless steels are due to another cause, the attack of the problem would follow another path. One of the most effective techniques for studying passivity and corrosion tendency is the measurement of the electrochemical potential. Not only can one determine by potential measurements whether a metal is active or passive, but also one can determine the degree of passivity and rate of transformation of passivity with time. Chemical media that build up or destroy passivity when in contact with the steel can also be classified by potential measurements. Something can be learned, too, of the effect of alloy additions such as molybdenum to 18-8, known to decrease corrosion of the alloy in chloride solutions. A study of alloys in previous investigations has sometimes included data on the electrochemical potentials. Tammann and Sotterl measured the electrochenlical potentials of alloys of iron-molybdenum and iron-chromium and reperted the critical concentration of molybdenum or chromium at which passivity initiates. Strauss2 made similar measurements for the iron-chromium system. The electrochemical potential3 has also been used to indicate carbide precipitated 18-8. In 18-8, heat-treated to precipitate carbide, active metal exists at the region of the grain boundaries, contrasted with passive metal within the grains, the active metal accounting for a resultant active potential. Several

Jan 1, 1940

By Lewis T. Wright

It is commonly believed by metallurgists that in copper-smelting, the copper in the slags, which is irreducible by continued " settling," is retained in the form of " prills " of matte. I have frequently held well-settled slag in a molten condition for a long period without being able thereby to reduce the copper-content. The slag acted as though it contained a minimum of dissolved or combined copper that could not be settled out by gravity. I have used reagents, but without satisfying myself in what form this copper existed. The same slags, by fine grinding and elutriation, could not be separated into portions containing more or less copper than the average content. By treating copper-slags in an electric furnace a button of metallic iron and copper was produced, but the high temperature and the strong reducing-action of the furnace mere influences that suggest an explanation of a result not obtainable with ordinary smelting-temperatures. If all the copper in the slag were in the form of copper-matte, and not existing as a dissolved compound with some of the elements of the slag, then the other metals in the matte, such as gold and silver, should occur in the slag in the same ratio to the copper as to the copper in the accompanying matte. This reasoning led me to study the ratio of metals in the products of smelting, and, apart from the issues discussed in this paper, the research has proved both interesting and illuminative. On the assumption of a similar ratio of metals in matte and slag, if the percentage of copper in the slag accompanying a matte containing 50 oz. of silver and 1 oz. of gold per ton of copper was 0.3 per cent., or 96 oz. per toll of slag, there should be found 0.15 oz. of silver and 0.003 oz. of gold per ton of slag; but, in my experience, there is less silver and much

Jan 1, 1910

By J. V. Richards

(Canal Zone Meeting, November, 1910,) THE Altar district, State of Sonora, Mexico, is for the most part a desert with but little rain-fall and few running streams. On account of this scarcity of water it is necessary for the natives to " dry-wash" the placer-gravel, and the object of the present paper is to describe some of the more common Mexican dry-washing devices. My observations were confined to a property known as Las Palomas placers, 15 miles from the Gulf of California and about 150 miles south of the United States border; a brief description of which property may be of interest as illustrating what is, perhaps, a typical Sonora dry placer. It is said that as long as a century ago the Yaqui Indians discovered rich cement-gravel, known as argo masa, at Las Palomas, and that there has been a more or less steady production of gold from the property ever since. The argo masa is a fairly-coarse gravel, the pebbles being quite firmly held together with a lime cement. Gold is scattered through this cement in particles ranging from fine specks to pieces several grams in weight, and occasional large nuggets are encountered. The contents vary so widely that it is difficult to estimate the average value, but returns of from $10 to $50 per cubic yard are common, and it is doubtful if the Indians considered anything less than from $4 to $5 a yard as "pay dirt." This argo masa occurs in channels varying in thickness from a few inches to several feet, and in width up to 300 ft.. These channels are continuous and are probably ancient stream-beds. They are for the most part covered with an over-burden of a more recent gravel, varying from 30 to 50 ft. thick, and the fact that this over-burden contains values as high as $1.50 per cubic yard, and yet was not worked by the Indians, shows that their idea of what constituted pay-ground was high.

Apr 1, 1911

By E. A. Gulbransen, W. S. Wysong

The behavior of tungsten and its surface oxides in oxidizing and reducing atmospheres and in high vacua at elevated temperatures is a question of considerable technical importance. The use of tungsten as a a Or as an important component in alloys in high temperature Oxidizing atmospheres has been limited because of the unprotective nature of its oxide film and the volatility of its oxide. This paper will present results of a micro-balance study of the following problems: (1) the oxidation behavior in the ternperature range of 25 to 550°C (') the reduction with pure hydrogen Of thin Oxide films formed On tungsten, and (3) the volatility Of thin Oxide films On tungsten. Tungsten is an interesting metal to study for the following reasons: (1) although the Oxide to to ratio is greater than one, the oxide is not considered protective, ('1 the meta1 readily Oxidizes at temperatures from 30" to 55o°C (3) the oxides WO² and WO³ are reduced at temperatures as low as 500°C. by hydrogen, and (4) the Oxide WO3 is volatile at temperatures from 800 to 1100°C. Literature The oxidation of tungsten in its thin film range has not been studied critically. In the thick film range Dunn3 has made the only systematic study. He found the oxidation rate to obey the parabolic rate law in the temperature range of 700 to 900°c. The temperature variation of the oxidation rate constant was found to follow an exponential law of the Arrhenius type. An inflection was noticed in the temperature plot of the rate law constant at 850 to 900°C. This was attributed to a phase change in the oxides, Schei14 has studied the oxidation rate at 500 and 700°C over long periods of time and found a linear rate law. This result was interpreted as evidence for the presence of a nonprotective film. Pilling and Bed-worth's5 analyses of the oxide volume to metal volume ratio would indicate that a compact protective film should form. McAdam and Geil6 have studied the oxidation of tungsten in the thin film range using the interference color method. A parabolic rate law was found. Their curves showed that tungsten oxidizes faster than nickel but more slowly than iron. The lattice structures found in the oxidation of tungsten surfaces have been studied by Hickman and Gulbransen.? They have reported that WO3 is the stable oxide in contact with the metallic substrate up to approximately 600°C while wo³ forms first at 7oo°c. Hagg and Magneli8 have recently reported a study of the lattice structures . observed in the tungsten oxidcs using the X-ray diffraction method. In addition to an a-phase WO3 and a '-phase WO2, they reported the existence of two new phases. A 8' phase, homogeneous between

Jan 1, 1949

By E. C. Pechin

THE Lucy furnace, owned by Messrs. Carnegie, Kloman & Co., and located on the Alleghany River, on the outskirts of Pittsburgh, is a splendid modern furnace, 75 feet high, and 20 feet bosh. She had been working well on low grade ores of about 50 per cent., producing daily 68 to 75 tons. There was on stock 500 tons of Republic ore, one of the purest and best of the Lake Superior ores, averaging over 68 per cent. of iron, which had been procured for the purpose of making a trial for Bessemer iron. This was charged by itself, and Mr. Skelding, the founder, reports that he did not succeed in getting a single cast when it came down, before the furnace chilled from the hearth to the top of the boshes, some 25 feet. Every effort was made to save her, without avail, and the disagree-

Jan 1, 1874

By N. J. King, R. F. Hadley

Alluvial valley floors constitute a valuable land resource and are important to ranching operations in the semiarid western United States. This resource may be in jeopardy locally if the alluvial deposits are disturbed by surface mining of coal deposits. Erosion problems caused by poor land-use practices can cause trenching of the unconsolidated alluvium with a consequent lowering of the water table and depletion of soil moisture needed to support vegetation. Historical evidence of this sequence of events is abundant in the geologic literature and serves as the basis for assessing potential impacts of surface mining. The potential geomorphic impacts of surface mining on alluvial valley floors with regard to fluvial processes are. (1) disruption of the longitudinal profile followed by valley trenching and high sediment yields downstream, and (2) replacement of the excavated alluvium with unconsolidated material that does not have similar physical characteristics and may be susceptible to erosion. Mining may disrupt the existing hydrologic framework affecting stream flow, ground-water levels, and water quality of both surface and ground water. Although functional hydrologic and geomorphic processes are similar, each valley represents a complex environment that does not submit to broad generalizations.

Jan 1, 1981

By Edmund C. Pechin

The Lucy furnace, owned by Messrs. Carnegie, Kloman & Co., and located on the Alleghany River, on the outskirts of Pittsburgh, is a splendid modern furnace, 75 feet high, and 20 feet bosh. She had been working well on low grade ores of about 50 per cent., producing daily 68 to 75 tons. There was on stock 500 tons of Republic ore, one of the purest and best of the Lake Superior ores, averaging over 68 per cent. of iron, which had been procured for the purpose of making a trial for Bessemer iron. This was charged by itself, and Mr. Skelding, the founder, reports that he did not succeed in getting a single cast when it came down, before the furnace chilled from the hearth to the top of the boshes, some 25 feet. Every effort was made to save her, without avail, and the disagree-