By J. H. Clemes

The process of leaching silver ores with sodium hyposulphite is comparatively new, and published accounts of the details and losses of the process are as yet very few. The following account of a careful series of experiments to determine the actual loss in this process may therefore be acceptable to members of the Institute. The ore treated was highly calcareous, and the principal sulphide present was iron pyrites. Following is an analysis by Professor Price, of San Francisco, of the ore treated : Per cent. Silica,..........15.13 Sulphur,.........13.31 Arsenic,.......... 9.82 Iron............ 17.33 Alumina,..........1.35 Zinc,...........4.92 Lead,..........1.78 Carbonate of lime,..33.78 Magnesia,.......... 2.58 100.00 Ten tons were crushed dry with a 30 X 30 screen = 900 holes per square inch. In order to feel our way with this ore, two experimental or "pilot" charges were roasted. Pilot Charge No. 1. Treated 1000 pounds in a four-hearth reverberatory. 8.30 p.m.—Entered fourth hearth, remaining there one and onehalf hours; sulphur began to burn. 10 p.m.—Changed to third hearth; ore became red-hot half an hour after entering; the fireplace was kept almost destitute of fuel. 2.30 A.M.—Changed to second hearth. Charge continued, giving off a large quantity of sulphurous fume; the fireplace was kept dark.

Jan 1, 1884

By V. Annamalai, J. B. Hiskey, L. E. Murr

The kinetics of copper cementation on rotating disks of body and tear-top beverage can aluminum alloys were studied as a function of temperature and copper ion concentration. Both alloys followed the two-step kinetic regions, an initially slow rate followed by an enhanced rate. Experimental activation energy determinations (9.04 to 19.62 kJ/mol) indicated that ionic diffusion controlled the reaction mechanism between 20° and 60°C. At low temperatures (< 20°C), the system appeared to be controlled by the presence of an aluminum oxide surface film. The results of this study showed that cementation kinetics for the beverage can aluminum alloys are similar to those for pure aluminum. It was also found that the chemical removal of the oxide layer is less important for the alloys than /or the pure aluminum system. The characteristics of the resultant copper deposits were studied under a scanning electron microscope, and the reaction kinetics seemed to depend strongly on the nature and morphology of the deposits. In addition, maximum rates occurred when the deposit structures were fine feathery dendrites.

Jan 1, 1980

Discussion Of the paper Of GEORGE K. BURGESS, J. J. CROWE, H. S. RAWDON, and R. G. WALTENBERG, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin NO. 93, September, 1914, pp. 2433 to 2437. ALBERT SAUVEUR, Cambridge, Mass.-The Bureau of Standards has once more rendered a public service. Manufacturers and consumers of steel rails alike should welcome the important results now laid before them by Dr. Burgess and his co-workers. Personally I welcome these results all the more that in the past, as some of the members may remember, I have never failed, when occasion arose, to call the attention of rail manufacturers to the importance of controlling the finishing temperature of their rails. The pioneer metallographic work conducted at the South Works of the Illinois Steel Co. in the early &apos;90s clearly brought out the close relations existing between the manufacture, properties, and finishing temperature of steel rails and I think I may say without fear of being contradicted that the results of this early investigation had considerable influence in drawing the attention of manufacturers to the importance of finishing temperature and of heat treatment in general. The results now before us should be, it seems to me, of great value to rail manufacturers in their efforts to produce a better and, above all, a safer rail. It seems to be demonstrated in this paper that there is no difficulty in installing in rail mills pyrometric outfits, making it possible to record, without interfering in the mill operations, the temperature of the rails as they leave the finishing rolls, or of the ingots as they are withdrawn from the soaking pits, or at any intermediate point in the process of manufacture. The inference necessarily follows that manufacturers should see to it that such pyrometric installations are made, in order that they may actually know, instead of guessing at, the temperature of their rails;, and, for obvious reasons, rail consumers should insist upon such installations. In the rolling of heavy sections especially should care be taken to lower their finishing temperature, seeing that the present tendency is to finish them at higher temperature, whereas, owing to the slower cooling of their central portions, which makes for coarseness of grain, they should, if anything, be finished at a lower temperature than lighter rails.

Jan 4, 1915

By E. DeGolyer

I. INTRODUCTION VOLCANIC origin. was among the first of the theories advanced to account for the occurrence of the salt domes of the Gulf coastal plain, northern Louisiana., and eastern Texas, and it is still being re-stated in various forms by the most recent contributors to our knowledge of the geology of such deposits. Argument has been largely by analogy and attention has repeatedly been called to the Mexican oil fields, particularly those of the Tampico-Tuxpam region, because of the occurrence of oil in close proximity to volcanic plugs in those fields, an occurrence supposed to have some resemblance to the common occurrence of oil in the salt domes of the United States. The author, having spent several months of the past year in a general study of salt domes and in a detailed study of certain domes in the United States, and having been acquainted for some time with the exploration of similar domes in the Isthmus of Tehuantepec region, Mexico, and with the general geology of the Tampico-Tuxpam region, Mexico, has reviewed the various theories of volcanic origin for salt domes which have been advanced to the present time. The purpose of this paper is to present such review and to discuss the supposed Mexican analogy.

Jan 5, 1918

By AIME AIME

FOR the mineral industry, as for many others, the year 1944 brought to fruition the seeds planted in previous war years. Accomplishment in attaining ends in the production of minerals has given more time for the consideration of postwar problems, such as plans for resuming production for civilian uses and measures to prevent possible mass unemployment. The hectic atmosphere in production circles lessened during the latter half of 1943, conditions becoming static during 1944 as peak production rates were reached. Withdrawal of deferment of young men from the mining districts by Selective Service connotes that man power at the battlefronts became more important than the persistence of pressure for metal production. This is in contrast to the return of soldiers in 1943 to augment the labor ranks in the mining districts. The year ended in the midst of changing needs. Over-all metal production in the United States in 1944 will record a lessening, compared with the previous year owing to labor shortages which affected both development work and ore output.

Jan 1, 1945

By Frank Firmstone, Kenneth Robertson

Peculiar crusts having appeared on certain irons made at Glendon and Pequest, which, in our experience, were entirely new, some analyses of them were made; and these analyses, together with an account of the manner of appearance of the crusts, are herewith submitted to the Institute. At Pequest the ores mere: & Peters, from Ringwood, N. J.; + roasted sulphurous ore, from Charlotteburgh, N. J.; and + red ore (decomposed magnetite), from Chester, N. J. The fuel was 7/8 Lehigh anthracite and + Connellsville coke, and the limestone a dolomite from Andover, N. J. The resulting iron varied in silicon from 0 84 per cent. in No. 1 foundry to 0.51 per cent. in gray forge; in phosphorus, from 0.81 per cent. to 0.55 per cent.; sulphur, 0.035 per cent.; manganese, 0.375 per cent. It was highly "chilling" in its properties, and very strong. In running, it invariably appeared to be of a lower grade than it really was; the higher grades scintillating as much as hard iron usually does. After getting into the moulds, and beginning to cool, a black crust began to show itself, seeming to exude from the pigs, till finally, when the iron was cold enough to break, it completely covered the face of the pigs. At this time it was dense black, but after some exposure to the air it ac .

Jan 1, 1884

By C. H. Mathewson

BERYLLIUM, magnesium, zinc and cadmium, together with mercury, constitute a coherent sub-group of the periodic system and these metals, excepting mercury; have been studied in sufficient detail by the new X-ray diffraction methods to prove their common adherence to the hexagonal close-packed type of crystal structure with a progressive increase in axial ratio as we pass through the group from beryllium to cadmium. The first four columns of Table 1 summarize the data on crystal structure of these metals reported in the International Critical Tables.1 The last two columns are based on results obtained in the present investigation. TABLE 1.-Lattice Constants and Twinning Law of the Be-Cd Group of Hexagonal Metals Dimensions of Unit Axial Cell, A Ratio Description of Twinning Element a° c° (c°/a°) Composition Axis Plane Beryllium 2.28(3) 3.60(7) 1.58 {1012} Probably 1 {1012} Magnesium 3.22 5.23 1.621 ,1 {1012} Zinc 2.65(7) 4.94(8 1.86(2) 11012 } 1 {1012) Cadmium 2.98 5.63 1.88(5) {1012} Probably 1 {1012} Twinning has often been observed in zinc and cadmium. The general aspects of this twinning are abundantly illustrated by photomicrographs, diagrams, etc., in the papers by Romig, and Mathewson and Phillips reported to this Institute in 1927.2. A determination of the composition

Jan 1, 1928

By H. H. Stout

THE high copper price during the war stimulated the capacity to produce far beyond a possible normal consumption. The curves in Fig. 1 show this. The line YZ indicates, what the world production and consumption of primary copper nor-mally would have been, had not the 3 war upset the rhythm of industry. Granting that the maximum world production of 3,150,000,000 lb. in 1917 was obtained by crowding both the equipment and the grade of ore mined, yet in many instances addi-tional capital was invested, upon which the producer will be driven to earn at least a reasonable interest. During the period of deflation, or C liquidation, which we have entered, the consumption of copper will nat-urally be below the normal. Fig. 1 shows the actual consumption ex-pressed-in per cent. of normal : 1919, 96 per cent.; 1920, 94 per cent.; 1921, 70 per cent. The copper industry, consequently, faces: (1) Potential over-production capacity; I (2) Diminished consumption. To deny the existence of these factors would be illogical. To minimize the menace of this potential producing capacity might lead to regret. All past attempts at artificial control have not proved very successful. Obviously the remedy is to increase, if possible, the consumption of copper to a point where these factors cease to be dangerous. In ultimate analysis, this means: Produce an article so cheap and so good that no one can afford to use substitutes. The problem can be solved by: (1) Re-ducing price; (2) Improving product offered.

Jan 11, 1922

By Clarence Wright

THE average lead and zinc content of the ores mined and milled in the Joplin district is low as compared with that of other lead and zinc deposits throughout the United States. Because of this fact and of the high grade of the concentrates, the ratio of concentration is unusually high. Most of the operating companies have aimed to produce as high a grade of concentrate as possible in order to obtain the highest price for their product. They have done this at the sacrifice of the percentage of zinc recovered. The average percentage of zinc recovery is from 60 to 70 per cent. For percentage of recoveries from actual mill tests, see tables. The concentration is commonly effected by crushing the ore to h-in. (12.7 mm.) size and subjecting it to a roughing and cleaning over two or more large Cooley jigs, of the Harz type, the finer sands being treated on the usual types of sand and slime tables. The treatment of slimes by flotation is being tested at several of the larger mills. COARSE CONCENTRATION When the ore. has been hoisted from the mine it is dumped onto a chute leading to a grizzly made of iron bars, usually heavy rails, spaced 4 to -5 in. (101 to 127 mm.) apart. The oversize is caught on the grizzly, the mineralized pieces are broken with sledge hammers so as to pass through, and the boulders that are practically barren are sorted out by hand and trammed to the waste-rock pile. The proportion of waste rock thus sorted out varies from a fraction of 1 per cent to 15 per cent., depending on the nature of the rock.

Jan 10, 1917

By H. C. Miller

THE gas-lift method of flowing oil from wells is the outstanding feature of petroleum technology today. Its forerunner, the air lift, was used successfully first, in the Baku fields of Russia, in 1899, and later in the Gulf Coast fields of Texas and Louisiana and the Kern River field of California. It is still used to a limited extent in certain oil fields. The use of compressed natural gas for lifting oil from wells has supplanted the air-lift method in a measure in those fields where a sufficient quantity of gas accompanies the oil to make the gas lift possible, or where natural gas is plentiful and inexpensive. We find therefore in California, that, natural gas is used at practically every well where a gaseous medium is employed to flow the oil. The use of natural gas has many advantages over that of air. It is possible to recover and save the gasoline from the gas that accompanied the oil to the surface. This gasoline would be wasted if air were used as the lifting medium. Also, certain proportions of air and gas form an explosive mixture that cannot be handled safely by compressors. Another advantage that gas has over air is that gas under pressure is more soluble in oil. Gas in solution in oil reduces the viscosity of the oil that is being produced and causes it to flow more readily through the. tubing and flow lines. The gas lift has made it possible to recover many thousands of barrels of oil from deep wells in California that could not have been produced otherwise. It would not have been economical, had it been mechanically possible to produce such wells as the world&apos;s deepest producing oil well (Miley Athen&apos;s No. 6, Rosecranz field, California) by any other method of pumping known today. At this well, production is obtained from between 7305 and 7591 ft. and 11 months after completion of the well, production was being maintained on the gas lift it approximately 2000 bbl. a month. The crookedness of the hole, or its diameter and depth will not prevent the successful application of gas-lift pumping when other conditions are favorable.

Jan 1, 1927

By G. Sachs, E. J. Ripling, S. I. Liu, J. J. Lynch

INTRODUCTION IT is a generally recognized fact that by repeated straining the fracture stress of any metal is reduced to a fraction of its value for static loading. The value of this fatigue strength depends upon numerous factors, such as the states of strain and stress, the limits of straining, and the number of repeated loadings or cycles.1.2,3 The large volume of previous investigations on fatigue is concerned entirely with large numbers of cycles, say exceeding 10,000 and up to 500,000,000. However, the changes in fracture stress and fracture strain occurring after a small number of repeated loadings have attracted little attention. Apparently the only investigations of this type are those byLudwik4,5 who subjected steel, copper, and aluminum wire to repeated torsion. In each test the torque was varied between identical values in the two directions of twisting. Depending upon the magnitude of the moment, fracturing occurred after a number of cycles, up to 10,000. The results of Ludwik&apos;s tests will be discussed later. Such torsion does not readily yield actual stress and strain values. Therefore a preliminary study was made of the effects of repeated direct stresses, i.e., tension and compression stresses. Because such tests are considerably more tedious than torsion tests, only high stresses were used in the preliminary work, yielding definite changes in metal properties after a few cycles. It was found in these tests that strains could be controlled more readily than stresses in the investigated range of high stresses. This paper, consequently, deals with the effects of strains of equal magnitude but different signs. The metal was first prestrained in static tension by a certain amount then subjected to compression to yield the same amount of strain after unloading. This loading cycle was repeated up to a maximum of seven times. After various cycles, the stress-strain curves in tension were determined, up to fracturing. As material for these tests, the aluminum alloy 24ST was selected because it exhibits a comparatively small amount of necking in the tension test. This alloy permitted, therefore, rather accurate control at the high strains necessary to produce fatigue failures at less than seven cycles. The results of this investigation appear sufficiently interesting to extend the method of attack in various directions. It is intended to study (I) the effects of cycles up to a few thousands and (2) the effects of strains of different magnitude in tension and compression, respectively. The latter variable also includes as a special case the effects of compressive strains.

Jan 1, 1948

By S. H. Gelles

Samples of poly crystalline zinc of 99.999+ pct purity were observed metallographically after having been exposed to hydrostatic pressures of up to 27 kbars. The deforrnation produced by this treatment was analyzed using X-ray and metallogaphic techniques. Basal-plane slip occurred universally in all grains exumined at the lowest pressure used (8 kbars). At pressures of >23 kbars, {1012} twin nucleation and growth were noted as well as slip. Formation of bend planes, complex kink bands, and recrystallization at the gain boundaries were also observed in this pressure range. These observations are discussed in reference to the expected deformation behavior of zinc under high hydrostatic pressure. It has been shown over the past few years1&apos;3 that anisotropic, poly crystalline metals can be made to deform plastically by the application of a hydrostatic pressure. The effect is greater 1) the larger the anisotropy of linear compressibility and 2) the smaller the stress level needed to produce plastic deformation. Zinc having both very anisotropic linear compressibilities and a very low critical resolved shear stress (CRSS) for basal-plane slip has been shown to exhibit large amounts of plastic deformation when subjected to a hydrostatic pressure.2,3 At pressures up to 15 kbars, grain boundary migration and slip on one set of glide planes have been reported.&apos; After exposing samples to 20 kbars pressure, grain boundary migration, single slip, multiple slip, and twinning have been noted.&apos; The identification of the deformation modes operative under these conditions has not been reported. It was the purpose of this research to identify the deformation modes induced in poly crystal line zinc by the action of a hydrostatic stress and to study the strain accommodation at grain boundaries. Hydrostatic pressure could affect the operational modes of deformation by altering the Peierls-Nabarro stress. This may be roughly approximated by the relationship4

Jan 1, 1967

By P. H. Brace

THE study of the relations between gases and metals is one of perennial interest to all who are connected with the production of high-grade metallurgical products. The data reported here are the outcome of work of which the object is to determine the effects of dissolved gases upon the properties of metals and to gain a more detailed knowledge of the reactions between gases and molten metals, particularly iron, under definitely controlled conditions. We have attempted to reduce our margin of error by dealing with relatively large quantities of metal, from 4 to 13 lb. (2 to 6 kg.), and keeping the ratio of refractories to metal as small as practicable. The ingots produced are large enough to provide adequate material for making determinations of magnetic and other physical properties. In choosing the bell-jar type of furnace we were influenced by the results of considerable experimentation along the same general line which indicated that, for the scale or which we were to work, it was important to have the furnace structure independent of the vacuum enclosure. The use of a bell-jar surrounding the entire furnace accomplishes this and also gives great freedom of observation during operation and ready accessibility for the replacements which are necessary after each run. Our choice of analytical method was made in the light of the results secured by H. M. Ryder, who used a method similar in principle for the analysis of very small quantities of gas extracted from strips of metal heated electrically in high vacuum. We have presented some selected preliminary experimental data as being illustrative of the quantity and nature of the gases which occur in iron of different origins, but do not urge any hypothesis at this time.

Jan 1, 1928

By Walter Renton Ingalls

In addition to the localities in which tin-ores have been found in Mexico, mentioned in my paper on the a Tin-Deposits of Durango," presented to the Institute in March, 1895,* the following should be recorded. I am indebted to Captain Henry Freeman, of Durango, for the notes as to these occurrences. In the Sierra de la Candela, west of the Sierra de Sail Frailcisco and El Promontorio (the Llano de Guatimape intervening between the two ranges), cassiterite is found in veins and stream-beds. The veins are narrow, and the ores have the same characteristics as those of Potrillos. They were exploited by miners from Coneto in 1882-86, the more extensive work having been done on the northern side of the mountains. In the Sierra de las Palomas, on the western edge of the Otinapa, ranch, about 25 miles W.N.W. from the Diablo mine in the Cacaria district, there are several small veins, of which the ore, gangue and country-rock are similar to those of the Cerro de los Remedios, near the city of Durango. The latter are essentially the same as the Potrillos veins. In the Cerritos del Olote, in the Murphy grant, about 50 miles W.S.W. from Durango, there are old mines, now partially filled. The veins are narrow and poor; the ore is highly ferruginous; the country-rock is rhyolite, with some granite; immense quantities of chalcedonic rubbish are strewn along the course of the veins. In the Cerro Blanco, overlooking the pueblo of Mezquital, 48 miles south of Durango, tin-ore is mined by the natives.

Jan 1, 1898

By G. Austin Schroter

ALTHOUGH there is now an extensive literature on the bleaching clays, not a great deal of material is to be found concerning the geological fea-tures of these deposits and their bearing on problems of exploration and development. At the same time, chemical and crystallographic research on the clay minerals during the past few years has laid a suitable founda-tion upon which to base conclusions of economic value drawn from field observations. All of the criteria and deductions herein presented are based upon extensive field work by the senior author, both in the United States and Canada, and when subjected to the ultimate tests of development and exploitation they have held up remarkably well, despite the fact that many of these conclusions apparently have not been reviewed in the litera-ture heretofore. The nomenclature of the bleaching clays is rather confusing in the light of present-day commercial standards and has even led to litigation." The old term "fuller&apos;s earth" is largely based upon trade usage and the definition of the term therefore is dependent upon the changing standards of commerce. For statistical purposes the Bureau of Mines81 classes as "fuller&apos;s earth" all natural bleaching or filtering claylike materials that possess high adsorptive capacity without previous chemical treat-ment or activation. Conversely, the so-called activated or acid activated clays are now generally recognized as any clay mineral or mixture of the clay minerals whose adsorptive capacity has been developed to commercial standards by chemical or physical treatment. Therefore, without attempting to propose any additions to the nomen-clature of bleaching clays, this paper will refer to naturally adsorptive clays and activable clays, respectively, for the two types indicated.

Jan 1, 1940

By G. Austin Schroter

ALTHOUGH there is now an extensive literature on the bleaching clays, not a great deal of material is to be found concerning the geological fea-tures of these deposits and their bearing on problems of exploration and development. At the same time, chemical and crystallographic research on the clay minerals during the past few years has laid a suitable founda-tion upon which to base conclusions of economic value drawn from field observations. All of the criteria and deductions herein presented are based upon extensive field work by the senior author, both in the United States and Canada, and when subjected to the ultimate tests of development and exploitation they have held up remarkably well, despite the fact that many of these conclusions apparently have not been reviewed in the litera-ture heretofore. The nomenclature of the bleaching clays is rather confusing in the light of present-day commercial standards and has even led to litigation.76 The old term "fuller&apos;s earth" is largely based upon trade usage and the definition of the term therefore is dependent upon the changing standards of commerce. For statistical purposes the Bureau of Mines81 classes as "fuller&apos;s earth" all natural bleaching or filtering claylike materials that possess high adsorptive capacity without previous chemical treat-ment or activation. Conversely, the so-called activated or acid activated clays are now generally recognized as any clay mineral or mixture of the clay minerals whose adsorptive capacity has been developed to commercial standards by chemical or physical treatment. Therefore, without attempting to propose any additions to the nomen-clature of bleaching clays, this paper will refer to naturally adsorptive clays and activable clays, respectively, for the two types indicated.

Jan 1, 1940

By John Patek

KNOWLEDGE of the relative floatability of silicate minerals is increas-ing in importance as flotation is being applied to the concentration of nonsulfides. Many silicates are in themselves commercial products amenable to concentration by flotation. Moreover, the selective flota-tion of other nonsulfide minerals, such as cassiterite, depends largely upon the floatability of associated. gangue silicates. Differences in floatability existing between the various silicates have not been suffi-ciently appreciated; for example, the feldspars that differ greatly in floatability have generally been merely treated as "feldspar." It was the purpose of the work described in this paper to determine by experi-ment the differences in floatability between silicates; to investigate the causes for such differences, and to discover a means of predetermining approximate floatability without the necessity of experimentation.

Jan 1, 1934

By John K. Berry

The handling and disposal of mine water is a much larger problem than is apparent at first glance. Many more tons of water are removed from underground coal mines in the United States each year than tons of coal. In the old anthracite region of Pennsylvania the average was around 36 tons of water for each ton of coal produced, while bituminous mines average about 5 or 6 tons. Water encountered in the mines may come from several different sources. In mines with light cover and without a firm solid roof, rain may seep directly into the workings. This is also true of deeper mines where pillar falls have broken the roof to the surface. The top under creek beds is generally faulty and broken and water comes through the roof at this point. Deeper mines are frequently overlain by water-bearing strata and pillar breaks and faulty top can admit water, while places running to the dip often accumulate water which comes up through the bottom. In all cases, except where passing under a year-round stream, the amount of water made is usually pretty closely connected with the weather-more water during the rainy season, less in the dry, although the deeper a mine is, the longer it is before changes in rainfall are felt. Another source of water, not connected with seasonal changes, is old water, accumulated over a period of time in abandoned workings of the mine, or from flooded adjacent mines. Here the water filters through the coal, the parting, or comes up through cracks in the bottom. Similarly, core holes, drilled to prospect the property, can be a source of unexpected water and modern safety requirements for dust-allaying water at the working faces can turn a pleasant working area into a soggy mess over the weekend if the system is not properly maintained and operated. Why water must be disposed is obvious. If allowed to accumulate, sooner or later the mine will fill up, or at least it will become "roofed" in low places, blocking ventilation and traffic. But it must also be controlled long before it reaches this stage. Water standing in the working faces is unpleasant for the men who have to work there and also cuts down on the amount of work they can do, as they must watch where they step all the time. It is especially unpleasant in low coal.

Jan 1, 1973

By A. I. Blank, S. E. Maddigan

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,&apos; the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White&apos;s range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940

By S. E. Maddigan, A. I. Blank

Many experimental and theoretical investigations have been made on the processes involved in annealing and recrystallization of metals. Most of these, however, have treated the time element as constant and heat-treatments used have been for relatively short times. Aside from the early work by Carpenter and Elam,&apos; the few that have investigated the effect of time on the processes have usually done so for fairly short time periods. During recent years the growing interest in long-time creep properties of metals and alloys under stress has made increasingly important a better knowledge of the recrystallization during prolonged heating. The recrystallization temperature of 70-30 brass given by Clark and White" in 1932 was somewhat above 400°F. (204°C.) but under 500" (260°C.), whereas in our laboratory recrystallization has been observed in creep specimens at 204°C., the lowest temperature of Clark and White&apos;s range. Since the creep properties are quite different above and below the recrystallization temperature, erroneous conclusions can readily be drawn by the application of short-time recrystallization data to creep problems. It was thus considered of both practical and theoretical value to make long-time annealing studies near the minimum recrystallization temperature. In this way useful additions could be made to data on recrystallization temperatures and, since the reactions in this range are relatively slow, additional insight could be obtained into the factors involved in annealing. Several comprehensive reviews of recrystallization processes have been written,3-6 therefore only a brief review of the generally accepted facts will be given here. Though the effects of heat-treatment usually are expressed as related to observations with varying temperatures, it is logical to assume that the same order of occurrence will exist with time as a variable. Thus, we may postulate that with increasing time we mill observe the following

Jan 1, 1940