By Bernard G. Carbajal

The dielectric properties and thermal stability of glow-discharge polytnerized films of styrene, chloro-benzene, and other organics and photoresist filrns are presented. Variations in the glow-discharge polymerization procedure are related to thermal stability. Thermal treatwzents to improve the dielectric properties of both positive (A2 340) and negative (KMER) photoresists are given. THIS study of the dielectric properties of thin organic polymer films is part of a program to investigate the electronic applications of organic materials. Thin organic polymer films have been produced in an ac glow discharge,13 with a low-energy electron-beam process,4 and in an rf dicharge. A process has been developed during the course of this program for forming thin organic polymer films in a dc glow discharge. These glow-discharge polymerized (GDP) films exhibit some useful dielectric and insulative properties. Variations in the properties of the GDP films can be induced by changes in the source material (monomer) andor in the conditions of the glow discharge. Thin organic polymer films can also be produced from typical positive and negative photoresists. Some variations in the properties of the photoresist films can be induced by suitable post-application treatments such as thermal crosslinking. The properties of interest in this study are dielectric constant, dielectric strength, resistivity, and thermal stability. POLYMER FILM PREPARATION I) GDP Films. The GDP films were prepared in a dc glow discharge in an atmosphere of organic monomer vapor. The details of the glow-discharge procedure have been presented previously.6 Briefly, under the influence of a dc glow discharge organic vapors can be polymerized in the vapor phase and the resultant polymer (GDP film) deposits on and in the vicinity of the cathode. Substrates placed behind a screen cathode can be uniformly coated over all exposed areas. Pattern definition can be achieved using normal mask stencil techniques. Table I presents the pertinent parameters in the preparation of GDP styrene. Conditions of Forrrzation of GDP Styrene. The rate of deposition for GDP films was monitored using a current-time integrator. The thickness of the deposited film for a given set of experimental conditions was a function of the current-time integral. The fifth row in Table I is a compilation of the deposition rate of GDP styrene films. Other organic monomers behave in a similar fashion. With the exception of the highly halogenated saturated hydrocarbons, all organics subjected to the conditions of the glow discharge form GDP films. 11) Photoresist Films. Photoresists are normally recognized to exist in two forms, a low molecular weight, soluble polymer form (A) and a high molecular weight, crosslinked insoluble form (B). Typical negative photoresists are applied in the low molecular weight form A and converted to the high molecular weight form B by the action of light. (Positive photoresists are applied in form B and converted to form A by the action of light.) Eastman Kodak Metal Etch Resist (KMER) has been chosen as a typical negative photoresist. Polymer film samples were prepared in the same configuration used for GDP films. The KMER was applied in the usual fashion using a 120°C drying step (infrared-lamp heating) and a 180°C post-bake. Care must be taken to completely remove the solvent in the drying step and to properly develop and postbake to exposed photoresist. If the photoresist film is not properly dried and postbaked, severe blistering and peeling will occur during subsequent elevated-temperature exposure. Thickness can be controlled by varying the viscosity of the form A photoresist and the spin rate at application. AZ 340 was chosen as a typical positive photore-

Jan 1, 1967

By R. H. Maes, R. E. de Strycker, J. J. Jacobs

A simple method, based upow density measurements, has been perfected in order to determine the critical temperature of liquid miscibility gaps. Applied to the Pb-Cu system, it yielded a value of 980"C for the critical tempevature of the miscibility gap in this system. In the Pb-Cu-As system, the immiscibility between lead and coppev evolves towards a miscibility gap be-tween lead and copper arsenides; the liquation temperatures were determined joy different avsenic contents and values up to 1065°C were found. Combining these results with those given by the clzemical analysis of liquid samples taken at dqj.event temperatures, it has been possible to make a cowzplete determination of the liquid miscibility gap in this ternary system. In the Pb-Cu-Fe-As system, a ternary miscibility gap has been discovered; for some compositions, the molten and slowly cooled alloys separated into three layers: an Fe-As alloy, a Cu-As alloy, and a lead-rich layer. ThE Pb-Cu-Fe-As system is of interest for the study of the behavior of speiss or arsenical alloys in the lead blast furnace. The speisses produced in lead metallurgy generally have complex compositions, but they may be considered, in a simplified way, as a mixture of copper, iron, nickel, and cobalt arsenides; there is often an excess of metallic constituants, and lead is also present. Speisses liquate from lead at various temperatures according to their composition; according to industrial experience, iron speisses are already distinctly separated from lead bullion at temperatures of the order of 1100°C, whereas copper speisses only begin to liquate from lead at much lower temperatures, near their solidification points, which were never accurately determined until now. Besides these considerations of practical interest, the present study is of importance for the knowledge of liquid miscibility gaps. Particularly the data of the literature about critical temperatures of liquation are incomplete and present sometimes considerable disparities; a method has been perfected in the present work to determine these temperatures with accuracy. MISCIBILITY GAP OF THE LEAD-COPPER SYSTEM Review of Literature. The generally admitted outline of the Pb-Cu equilibrium diagram is shown by Fig. 1. This figure, with its numerical indications, is taken from the review of Hansen and ~nderko;' compositions are given in weight percent, as will be the case in the remainder of this paper. Between 36 and 87 pct Pb, Pb-Cu alloys separate into two layers, in the liquid state. The critical temperature of liquation has been much disputed in earlier studies, where values up to 1500°C were claimed; but a reliable study of ~ohnen,' based upon differential thermal analysis, gave a value of 990°C; this rather low value was verified by a recent study of Schiirmann and Kaune? based upon thermodynamical properties of the Pb-Cu alloys, which predicted a value of 1002°C. Liquid miscibility gaps were also studied by means of chemical analyses. Satisfactory results were generally obtained with the method consisting in taking samples of the two liquid layers in equilibrium and submitting them to chemical analysis; however, this method becomes delicate near the critical temperature. With this technique, Friedrich and waehlerts ob-

Jan 1, 1968

By W. B. Hickman, J. J. Pickell, B. F. Swanson

Many physical properties of the porous media-immiscible liquid system are dependent upon the distribution of fluids within the pores; this in turn, is primarily a function of pore structure, liquid-liquiri interfacial tcnsion and liquid-solid wetting conditions. The cnpillary pressure hysteresis process provides a means of investigating the influence of pore structure upon fluid distribution for consistent sur/acc conditions. Invcstigntiot2s indicate that residual non-wetting-phase saturations /ollozuir,g the imbibition process (i.e.,wetting phase displacing nor2-wctting phase) are dependent upon both pore structure and initial non-raetting phase saturation and suggest that residual fluid is distributed as Discontinuous ,globules, one to a few pore sizes in dimension, thrnugh the entire range 01 pore sizes originally occupied. It clppears that air-mercury capillary pressure dala adequntely rellect the distribution of fluiris in a water-oil system when strong wetting condition preliczil. An oil-air counter-current imbibition technique has also been found to provide a rapid rneans of obtaining residual-initial saturation data. In a majority of cnses, rcsidual saturations detf-rniinecl from the oil-air or air-mercury process reasonably approximate residual oil saturation following water drive of a strongly water-wet medium. INTRODUCTION A reliable estimate of recoverable reserves depends not only on the amount of original oil-in-place but also on pore geometry and distribution of fluids within the pores. A critical parameter determining the recovery from a reservoir under waterflood, for example, is the amount and distribution of residual oil within the various rock types present. The purpose of this paper is to investigate the mechanism of capillary trapping and assess its importance in laboratory measureqents of residual oil saturation. The degree of wettability of a reservoir rock is recognized as an important factor in waterflood or imbibition experiments. In this paper, however, only the water-wet case has been considered. Considerable experimental evidence1 suggests that for water-wet rocks, capillary forces predominate in tile distribution of fluids and that viscous forces in the range normallv of interest in the reservoir have a minimum influence on residual oil saturation. It follows that if the ultimate recovery is controlled by pore geometry, a unique residual non-wetting phase saturation should exist for a given set of initial conditions. Two laboratory procedures.found to be extremely useful in the study of pore structure and degree of fluid interconnection at various saturations are decribed. Although air-nercury capillary injection curves have been used2 previously to characterize the drainage case, the withdrawal or imbibition case can provide valuable supplementary data. The air-mercury process, however, has several disadvantages; it is difficult to run in a sufficiently accurate manner, mercury does not always act as a strongly non-wetting liquid and in the air-mercury process the sample is rendered unsuitable for future analyses. An alternative process is described in which air is the non-wetting phase and naptha, hentane, octane or toluene is the wetting phase. INTERFACIAL TENSION AND CAPILLARY PRESSURE Interfacial tension between immiscible fluids is due to the difference in attraction of like molecules as compared with their attraction to molecules of the neighbouring fluid. This net attraction results in a tension at the interface. To extend the interface; thus, interfacial tension s can also be thought of as free surface energy. Interfacial tension is normally expressed as dynes/cm, and interfacial energy is measured in ergs/cm2 hence, both have dimensions ml A 2 and are numerically equal.

Jan 1, 1967

By S. Usui, I. Iwasaki

The adsorption mechanism of dodecylammonium acetate (DAA) on mercury in potassium fluoride solutions at natural, near neutral pH was investigated. Difler-ential capacity combined with electrocapillary measurements on a dropping mercury electrode were found to provide a sensitive and reliable approach. A shift in the electro capillary maximum (or the point-of-zero-charge) towards positive polarization of the surface due to the adsorption of amine indicated a specific affinity of dodecylammonium ion for mercury surfaces. The amine was shown to adsorb competitively with potassium ion on mercury. Through correlation of the adsorption density of the amine, calculated from the thermodynamic analyses of the electrocapillary curves, and of the diflerential capacity curves, the adsorbed state and the orientation of the amine at the interface were considered. The similarities and the differences in the adsorption behavior of the amine on mercury and on such ionic solids as quartz, silver sulfide, and silver iodide were evaluated. With the promise of flotation providing a cheap and large-scale process for the upgrading of low-grade ores and magnetic concentrates, the iron ore industry has made a sustained search over the years for a flotation reagent of general applicability and high selectivity. Having shelves full of commercial reagents already on hand and anticipating more, both the users and the suppliers are in need of an experimental approach sensitive enough to differentiate the individual characteristics in each group of reagents. Therefore, the adsorption behavior of various flotation reagents on mineral surfaces from aqueous solutions has been a subject of much investigation. The current view of adsorption based on the electrical double-layer theory is formulated on the assumption that certain ions in solution act as potential-determining ions. Their concentrations fix the potential drop across the double layer and their adsorptions govern the surface charge.' Two methods used to study the adsorption

Jan 1, 1971

By Tuncel M. Yegulalp, Malcolm T. Wane

In general, many problems relating to the exploitation of mineral deposits are probabilistic in nature. This derives from the fact that the geologic universe is inherently random. Probability theory and statistics have been found useful for forecasting the behavior of natural events that occur in the geologic universe. The objective of this paper is to illustrate the application of the theory of extremes to this fore-casting problem. For example, it is customary for design purposes to determine the rupture strength of geologic materials. The theory of extremes is exceedingly useful in describing that portion of the frequency distribution of rupture strength which contains the least strengths. Parameters describing the distribution of the least strengths are more important to the designer of mining excavations than parameters describing the total distribution. The basic principles of the theory of extremes will be detailed and illustrated. Any person required to work in the laboratory of nature is aware that uncertainty is a salient feature of all mining enterprises. A mining engineer required to plan the most efficient, practicable, profitable, and safe mine finds himself face to face with numerous ill-understood and often unquantifiable states of nature. Basic information necessary for adequate planning is often lacking or derived from incomplete tests on samples or experience of doubtful validity. The planning procedure usually takes the form of determining a feasible layout with the intent of determining an optimal layout when and if the necessary details and information become available. The crux of the entire procedure is the choosing of numbers to put into the operational and structural models which encompass the plan. Many times these numbers must be assigned qualitatively from past experiences and are called the "most probable ones." At other times, load records, performance records and material tests provide a basis for extrapolation. In any event, the numbers are chosen from a distribution or set of all numbers. Since each number in the distribution represents a possible state, the choice of any particular value is based upon a decision rule. To illustrate, consider the design of an underground structure or the design of a rock slope. The initial step is the formulation of the various possible structural actions which result from the geometry of the layout. For a given structural model various intensities of behavior are possible depending upon the load, deformation, and material characteristic spec-trums, respectively. Of particular interest to mining people is the failure behavior or condition, i.e., when there is a complete collapse of structural resistance by either structural instability or fracture. A necessary feature of the analysis is the "rupture strength" of the material. Information on the rupture strength is derived from testing either in situ or in the laboratory and the usual outcome is a variation in the test results. The methodology used to overcome this variation is to construct a frequency distribution of rupture strengths, and then determine a measure of central tendency and variability. The main idea involved is that the central tendency number will be used in the failure calculations and the measure of dispersion will be used to estimate the probability of failure. In particular if the distribution of rupture strength is normal, the mean rupture strength is the central tendency number and the standard deviation of the rupture strength is the measure of variability. Suppose the mean value of rupture strength is 1000 psi and the standard deviation is 200 psi. Insertion of 1000 psi into the failure calculation produces results that are unsafe, hence a common decision rule is to reduce the mean value by a "factor of ignorance" so that the failure calculation will produce a "safe result." If two is chosen as a factor of ignorance, this means the value inserted in the calculation is 500 psi or 2.5 times the standard deviation. The next step is to determine the percentage chance that failure will occur from a design created on this basis. Tables on the normal distribution function show that this percentage chance is 0.621% or approximately 7 times out of 1000. In practice, however, the situation is more complicated than represented by the foregoing illustration. The laboratory or field testing program usually constitutes a pathetically small sample of the geologic universe of interest and not enough testing is carried out to determine the exact form of the distribution of the test results. The normal, Cauchy and Student's T distributions are strikingly similar, and it becomes a matter of mathematical convenience to assume the normal law for phenomena which follow other laws.

Jan 1, 1969

By A. H. Underwood, M. –Ls. Trépanier

INTRODUCTION The King and Beaver mines of Asbestos Corporation Limited (ACL) were joined in 1957 to form the King-Beaver mine. In 1964, ACL purchased the Johnson's Asbestos Company. The combined underground workings are a part of the King- Beaver mine. Asbestos ore is mined at the rate of 4080 metric tons per day (mtpd) to provide 15% of the company's daily requirement in the Thetford Mines area. Figure 1 shows the location of Thetford Mines. Two shafts service the underground. No. 3 shaft, 457 m deep, is used for personnel and material transportation, downcast ventilation, and ore hoisting. No. 4 shaft, 820 m to the south, is 389 m deep. It is used for material transportation and upcast ventilation. Figure 2 shows the relative locations of the shafts and the underground workings. The ore is mined by block caving. HISTORY The orebody outcropped at surface and was first mined as an open pit. Underground mining commenced when open pit mining became impractical. Shrinkage stoping, used initially, was unsatisfactory in the highly fractured ore. Sublevel stoping improved ore recovery and safety, but did not overcome the adverse effects of the un- stable rock. Observations of the rock failures indicated that block caving would be satisfactory. This was confirmed by careful investigation and testing. A method of block caving similar to that used at the Miami Copper Company was adopted. The first block commenced production in June 1933. BLOCK CAVING General A large block of ore is undercut above pre- pared drawpoints. The ore above the undercut caves by its own weight. Caving progresses up- ward as the caved ore is drawn. A large proportion of the rock breaks up in the caving action so that it will pass through the drawpoints. Oversize blocks are broken by drilling and blasting or mudcapping. Figure 3 shows the progressive stages of block caving. In the central part of the ore zone, the vertical dimension of a block is determined by the 132 metres between production levels. When isolated ore pockets are developed, the vertical dimensions of a block depend on the extension of the ore zone above the undercut. The minimum horizontal dimension of an under- cut determines the cavability of the overlying block. When necessary, caving is assisted by drilling long horizontal holes into the block above the undercut and blasting them. This procedure speeds up or restarts caving. It will not ensure complete caving of blocks having undercuts less than 30 m wide. Orebodies suitable for block caving are highly fractured and wide enough to cave freely without excessive dilution. Undercutting must

Jan 1, 1981

By Franklin J. Hill, Theodore D. Tiemann

Sized fractions of Wisconsin Gogebic taconite were reduced with hydrogen over the temperature range from 600° to 1000°C. In general, the degree and rate of reduction increase with temperature. Particle size has no observable effect except in the smaller fractions at 900°C and above, where reduction is impeded, possibly due to the siliceous nature of the ore. Gaseous diffusion appears to be significant as a rate controlling factor at certain stages. THE depletion of high grade iron ore reserves in the United States has established the need to utilize all available iron ore deposits, both in long range planning and from the viewpoint of national emergency. This has led to extensive research and development in this field. The beneficiation of Wisconsin Gogebic taconite ore has been previously studied by investigators at the University of Wiscconsin, 1 the United States Bureau of Mines,, Battelle Memorial Institute, 3 and others. Methods investigated have included concentration by flotation processes, magnetic and gravity separation, magnetic roasting and various combinations of them. The foregoing studies have been concerned with the production of an enriched ore suitable for blast furnace use. If the ore could first be reduced to metallic iron and then beneficiated, the product could be used directly in the open hearth or electric steel-making furnace. The by-passing of the blast furnace should enhance the economic feasibility of the beneficiating process. The work reported here,4 was undertaken to establish data on the hydrogen reduction of Wisconsin taconite that would eventually lead to the development of an economic direct reduction process for this and perhaps other low grade siliceous ores. The volume of work on direct reduction can be judged by the fact that 240 direct reduction processes were patented in the United States alone up to 1951, 5 and numerous additional processes have since been developed. Some of the factors contributing to direct reduction development are: 1) The increasing capital cost of the blast furnace and its accessory equipment. 2) The decreasing availability of high grade domestic ore. 3) The high cost of steel scrap for use in the open hearth and electric furnaces. In general, direct reduction processes can be divided into two types; those using a solid reductant (coal, peat, lignite) usually carried out in a kiln, and those using a gaseous reductant (H2, CO) in a shaft furnace or a fluidized bed retort. As there is no low cost coal readily available in northern Wisconsin but natural gas could be quite easily obtained, it is believed a gaseous reductant process would offer the greater feasibility for use on Wisconsin taconite. It is hoped that this preliminary work will beof interest to other investigators in this increasingly important field. TACONITE ORE The ore used in the investigation was obtained originally from the U. S. Bureau of Mines, and consisted of a representative composite made up from trench samples of the Norrie, Pabst, Plymouth, Pence, and Yale members of the Wisconsin Gogebic range iron formation. Chemically, the ore contains approximately 52 pct SiO, and 30 pct Fe. X-ray diffraction and other studies indicate the principal minerals to be quartz (SiO2), hematite (Fe2O3), and goethite (Fe2O3. H2O). Minor amounts of iron containing silicates, siderite (FecO3), and magnetite (FeO-Fe2O3) are present. The iron minerals and quartz are so finely disseminated that the ore requires grinding to less than 200 mesh (74 µ) for essential liberation.l,2 The iron content of each of the several size fractions studied is shown in Table I. EXPERIMENTAL METHOD The method used throughout the investigation was based on that developed by the U. S. Bureau of Mines in Minneaopolis6,7 in which the course of reduction is followed by the loss in weight of the ore sample. More specifically, a 100-g sample of the size frac-

Jan 1, 1962

By Albert Sir Kitson

THE manganese ore deposits of the Gold Coast, British West Africa, occur in very ancient rocks, of both sedimentary and metamorphic types. In. certain respects they strongly resemble those of India and Brazil, as contrasted with those of Tertiary age in Georgia. Viewed from the present condition of the maganiferous rocks, the oldest deposits are in the sediments. Later than these are the progressively metamorphosed representatives of these sediments; youngest are the products of decay and degradation with the concentration of manganese oxide of both areas. The oldest occurrences are in argillaceous and siliceous phyllites and slates, which show only a moderate amount of metamorphism. They belong to a series which also includes mudstones, sandstones, grits, conglomerates and subordinate limestones, with tuffs and lava-flows largely of basic types. To this series I have given the name Birrim. Its age is unknown, for no definite fossils have been discovered in it. As the characteristics of these non-fossiliferous strata at many places are the same as those of strata in many parts of the world that are suitable for the preservation of fossils and that contain them, it is assumed that the Gold Coast deposits are pre-Cambrian. These rocks of the Birrim series have normally a northeast-southwest strike and are folded, but not to any very great degree except in certain belts., From the Eastern Province of the Gold Coast they may be traversed across their strike for more than 600 miles to the extreme northwestern corner of the Northern Territories. Thence. they probably extend much further into French Territory.

Jan 5, 1927

By W. C. Snow

The plant of the Electrolytic Zinc Company of Australasia Limited, situated at Risdon on the estuary of the River Derwent, near Hobart, was designed and erected primarily to produce high-grade zinc from zinc concentrates produced by the mines of Broken Hill, N. S. W. Consequently the metallurgy of the process has been influenced in its development by the peculiar characteristics of the Broken Hill concentrate, which on treatment gives into solution relatively large amounts of cobalt, manganese and silica. The Risdon works (Fig. 1) produces high-grade electrolytic zinc, leaded electrolytic zinc, zinc dust, cadmium, sulphuric acid and superphosphate. This paper, however, is concerned only with the zinc plant and process. Roasting The roasting of raw concentrate is not a major feature of Risdon's process, and in this respect practice is unlike that of most zinc plants. The roasting is mostly done on the Australian mainland at centers where the sulphuric acid made from the roaster gases can be used for superphosphate manufacture. A small amount, approximately 40 tons per day, is roasted at Risdon, acid being manufactured from the gases. The amount that can be roasted there is limited by the acid requirements of the zinc plant and of the superphosphate plant. Roasting is not carried to completion at the mainland plants, and the product, known as preroast calcine, largely constitutes the raw material for the Risdon zinc plant. It contains about 6 per cent of sulphur as sulphide. Roasting is completed at Risdon for reasons that are set out later in this paper. The zinc plant proper is divided into four main divisions: (1) final roasting division, (2) leaching and purification division, (3) electrolytic division, (4) melting and casting division. There are two subsidiary divisions—the cadmium division and the preroast, acid and superphosphate division.

Jan 1, 1937

By J. H. Fletcher

AIR has been cooled, heated, washed; humidified and dehumidified for many purposes and in many industries. At a number of metal mines air is conditioned to reduce the high humidity and unbearable heat found in deep workings, and at some mines air is washed to allay siliceous dust. Steam is introduced into the intake air at many coal mines, particularly in winter, for the purpose of keeping loose coal dust so moistened that the hazard of an explosion is lessened. This paper will describe a further successful application of air conditioning in a coal mine, where, for over three years, all intake air has been cooled to a constant temperature for the sole purpose of preventing roof falls.

Jan 1, 1931

By L. M. Pidgeon, W. Curlock

FREE energies of formation of zinc sulfide and magnesium sulfide had previously been estimated to an accuracy of ± 5.0 kcal per g mol. In the present work, these values were determined experimentally. As the determinations of the free energies of formation of zinc sulfide and magnesium sulfide presented different problems, separate experimental procedures were employed for each. ZINC SULFIDE It is difficult to measure the free energy of formation of either zinc sulfide or magnesium sulfide by measuring their decomposition pressures directly, as they are very stable compounds. An attempt was made by Jellinek and zakowski3 to study the equilibrium. zns(s) + H2(g) = Zn(g) + H2S(g) [I] They passed hydrogen over zinc sulfide and analyzed the gases leaving the reaction zone for H2S. They were unable to determine the true partial pressures of the H2S by this method, as some of the H2S on being cooled from the reaction temperature, reacted with the zinc in the gas to produce ZnS. Consequently, they were unable to establish any true equilibrium data for reaction [I]. More recently,' the equilibria ZnS(sphaledte) + Fe (s) — FeS(s) + Zn(g) [2] and ZnS(sphalerite) + 2Cu(s) — Cu2S(S) + Zn (g) [3] were studied. As the standard free energy of formation of Cu2S is known to * 3.0 kcal, and of FeS to ± 1.0 kcal, it should be possible upon performing equilibrium studies on reactions [2] and [3] to deduce the standard free energy of formation of ZnS (sphalerite). However, as both of these equilibria involve 2 solid sulfides, and as it is possible for these sulfides to dissolve in one another, it is necessary first to ascertain the activities of the various sulfides in these solid phases.

Jan 1, 1959

By F. P. Nichols, F. A. Renninger

At one time, mineral aggregates were considered physically and chemically inert substances whose junction was that of an inex-pensive, easily obtainable source of bulk. This philosophy applied regardless of the use to which the aggregate was put. Research approaches dealing only with such gross physical properties as hardness, toughness, impact resistance, etc., dominated the early growth years of the industry and influenced specifications to a large extent. The accelerated pace of highway construction, which began toward the end of the depression years, focused attention on the need for extensive aggregate research. The realization in the early 1940's that aggregates interacted chemically as well as physically with their environment provided the stimulus necessary to translate the drab, systematic aggregate technology of the early 20th century into the changing, dynamic, challenging field it is today. Current research problems are discussed in detail. These efforts being pursued by contract research organizations, universities, governmental agencies, and industry transcend many fields. The mineral aggregate industry is the world's largest mining and processing endeavor, yet it is graced with little of the romance or public awareness that accompanies mention of gold, silver, iron, copper, uranium, or aluminum mining efforts. Much of this reaction is undoubtedly due to the fact that the uses to which crushed stone and sand and gravel are normally put are not fully recognized or appreciated by the general public. Almost 2 billion tons of mineral aggregates are quarried or mined, processed, and sold yearly in the United States alone.= The largest uses to which this vast tonnage is subjected are as ingredients of portland-cement concrete, bituminous concrete, and dense-graded aggregate-base course mixtures in the highway and building construction fields, two industries closely related to the expenditure of public funds. It is for these uses, partially in justification for the expenditures of vast sums of public funds, that mineral aggregate research truly finds its emphasis. The research efforts expended relative to the highway and building construction uses to which mineral aggregates are subjected are those of primary concern to the industry. These efforts, while of direct consequence to the industry due to the volume market represented, are of interest as well to public agencies, universities, and contract research firms. All actively conduct research, exchange information, and make contributions to the overall knowledge relative to aggregate usage and limitations. The research efforts of the mineral aggregate industry is the subject to be discussed throughout this paper. It covers all aspects of highway and building design, construction, and technology. The effects of research pertaining to quarrying and mining methods, blasting and processing techniques, storage and handling facilities, and equipment employment and development have left their mark on the crushed stone and sand and gravel industries. Such specialized efforts have resulted in dramatically increased production rates which in turn have served to keep costs, and hence prices, down. Despite the many inflationary pressures over the years, the cost of a ton of aggregate today is little more than it was 25 or 30 years ago. Mention is made of these efforts simply to emphasize the diversity of research in the mineral aggregate field. The remainder of this paper focuses on the complexity of what might be termed "product knowledge" research.

Jan 1, 1971

By J. A. Pusateri, M. A. Orehoski, N. R. Arant

Plant studies on commercial-size ingots and laboratory experiments with induction furnace heats have demonstrated that the major source of ingot cracks is associated with two conditions arising during top-pouring practice: 1—solidification during pouring, and 2—turbulence created by the impact of the stream. Methods of controlling the two factors were effective in eliminating or significantly reducing ingot cracks. BECAUSE the process of removing surface defects from hot-rolled product is so costly, the steel industry is striving constantly to develop methods of preventing, or at least decreasing, the occurrence of surface defects. Investigations have revealed steel-making and processing variables related to major surface defects, and controlling these variables has led to improvements in surface quality. However, the fundamental causes of major surface defects, such as ingot cracks, have not been determined; consequently such defects persist. At the Research and Development Laboratory of the United States Steel Corp. in Pittsburgh, a seam research program was initiated to determine the fundamental causes of certain major defects. As a part of the program, ingot cracks in killed, finegrained C1020 steel were selected for study. A cost survey indicated that, of the steels produced in sizable tonnages, carbon steels in the range of 0.18 to 0.23 pct C content require the most conditioning. Since this is particularly true of C1020, any im-provement of surface quality that might be effected from the study would be beneficial. Also, since the frequency of ingot cracks is exceedingly high for this grade, the steel would provide an excellent opportunity for a thorough study of the ingot-crack-ing problem. Why steels in this carbon range tend to exhibit more ingot cracks than do other steels was not considered in the investigation; the mechanism of ingot-crack formation was of paramount importance. Also, only the top-pouring practice was considered in the investigation, because this pouring procedure is used more extensively than others. In this study, ingot cracks are defined. as deep surface defects that sometimes are observed in an ingot prior to rolling but usually are observed during the initial stages of rolling on the primary mills. These defects may occur at any angle to the rolling direction but are most prominent in the transverse or nearly transverse direction. The appearance of ingot cracks on the rolled product varies with respect to their angle of formation and with the extent of rolling after their first occurrence. Ingot cracks are also termed "deep seams," "arrowheads," "irregular cracks," and "transverse cracks." Fig. 1 shows ingot cracks in a rolled bloom. This report summarizes: l—the exploratory investigation of commercial-size ingots; 2—the labor-atory investigations related to determining the source of ingot cracks and developing corrective methods; and 3—the plant evaluations of laboratory methods of decreasing ingot cracks. Exploration of lngot Cracks in Commercial Ingots Materials and Experimental Work: At the Du-quesne Works of the United States Steel Corp., five heats of killed, fine-grained C1020 steel were selected for the exploratory phase of the seam-research program. The heats were made by open-hearth practices that are considered most conducive to good surface quality. They were top-poured into 22x25 in. big-end-up hot-topped molds. One as-cast ingot and four other ingots rolled to the following cross-sectional sizes were set aside from each heat: 16x20 in.; 9 1/2x10 in.; 5x5 in.; and 2x2 in. The processing of the heats, from the time of charging in the open hearth furnaces to the end of the rolling operation on the primary mill, was observed carefully and recorded. The cast ingot and the four rolled ingots from each heat were examined for surface defects. The cast ingots were split longitudinally near the vertical center plane to expose the ingot structure beneath badly cracked regions. Also, a series of transverse sections was cut at about 1 in. intervals in a badly cracked area of one ingot. All sections were ground, polished, examined by sulphur printing and deep etching, and photographed. The rolled ingots

Jan 1, 1955

By Herbert Clark Hoover, Lou Henry Hoover

QUALITIES which the perfect miner should possess and the arguments which are urged for and against the arts of mining and metallurgy, as well as the people occupied in the industry, I have sufficiently discussed in the first Book. Now I have determined to give more ample information concerning the miners. In the first place, it is indispensable that they should worship God with reverence, and that they understand the matters of which I am going to speak, and that they take good care that each individual performs his duties efficiently and diligently. It is decreed by Divine Providence that those who know what they ought to do and then take care to do it properly, for the most part meet with good fortune in all they undertake; on the other hand, misfortune overtakes the indolent and those who are careless in their work. No person indeed can, without peat and sustained effort and labour, store in his mind the knowledge of every portion of the metallic arts which are involved in operating mines. If. a man has the means of paying the necessary expense, he hires as many men as he needs, and sends them to the various works. Thus formerly Sosias, the Thracian, sent into the silver mines a thousand slaves whom he had hired from the Athenian Nicias, the son of Niceratus1. But if a man cannot afford the expenditure he chooses of the various kinds of mining that work which he himself can most easily and efficiently do. Of these kinds, the two most important are the making prospect trenches and the washing of the sands of rivers, for out of these sands are often collected gold dust, or certain black stones from which tin is smelted, or even gems are sometimes found in them ; the trenching occasionally lays bare at the grass-roots veins which are found rich in metals. If therefore by skill or by luck, such sands or veins shall fall into his hands, he will be able to establish his fortune without expenditure, and from poverty rise to wealth. If on the contrary, his hopes are not realised, then he can desist from washing or digging. When anyone, in an endeavour to increase his fortune, meets the expenditure of a mine alone, it is of great importance that he should attend to his works and personally superintend everything that he has ordered to be done. For this reason, he should either have his dwelling at the mine,

Jan 1, 1950

By S. G. Cupschalk, J. J. Wert, R. A. Buchanan

The uniaxial deformation of thermally ordered and disordered polycrystalline Cu3Pt was studied by means of the X-ray line - broadening analysis according to Warren and Averbach and the extension of this analysis to ordered fcc materials by Mikkola and Cohen. Because of the heat treatment history, extinction had a pronounced effect on the X-ray spectra of ordered and disordered C%Pt at small plastic strains. After an appropriate correction for extinction, the long-range order in thermally ordered ChPt was found to decrease at a slow constant rate with plastic strain. Furthermore, the antiphase domain probability increased at a constant rate to 17.5 pct strain. The effective particle size behavior indicated that the stacking fault energy is lower in ordered than in disordered Cu3Pt. Analysis of the stress-strain curves shouled that ordered Cuzt has a slightly lower yield Point but a much higher work-hardening rate than disordered Cu3Pt. THE presence of long-range order in a solid-solution alloy has a marked effect on its mechanical properties. While this effect has been known qualitatively for many years, it was not until recently that detailed investigations have been performed to determine the exact role long-range order plays in this strengthening mechanism. The development of an advanced, quantitative. X-ray diffraction analysis by Warren and Averbachl and the extension of this analysis to the L1, type super lattice by Mikkola and cohen2 have greatly accelerated research in this field. The research reported in this paper consisted of two primary phases. The first phase was to determine the effect of long-range order on the tensile properties of polycrystalline Cu3Pt. This objective was accomplished by comparing the stress-strain behavior of thermally ordered CusPt to that of thermally disordered CusPt. The second phase of the research was to determine the difference between the atomic arrangements in thermally ordered and thermally disordered Cu3Pt as a function of uniaxial deformation and thereby gain a deeper insight into the mechanism by which long-range order affects the tensile properties. This second objective was accomplished by applying the Warren-Averbach method of peak profile analysis to the X-ray diffraction patterns obtained from ordered and disordered Cu3Pt after given amounts of uniaxial deformation. EXPERIMENTAL PROCEDURE The Cu3Pt was prepared by vacuum melting and casting. After a homogenization anneal, the ingot was cold-rolled to sheet form. Two tensile specimens with gage sections of 2.50 by 0.500 by 0.115 in. were carefully machined from the sheet. The specimens were polished with a final step of 600-grit paper to insure smooth diffracting surfaces. Finally, one specimen was heat-treated to yield an average grain diameter of 0.016 mm and an initial degree of long-range order, S, of 0.825. The other specimen was water-quenched from above the critical temperature, 645"C, to yield an average grain diameter of 0.017 mm and zero long-range order. The heat treatment history of each specimen is shown in Table I. The tensile tests were performed utilizing a Research Incorporated Model 900.95 Materials Testing System. This unit employs a closed-loop feedback system which maintains a constant strain rate through an extensometer clipped to the gage section of the tensile specimen. A strain rate of 1.32 i0.02 x 10"4 sec-' was employed in testing both specimens. In the X-ray diffraction analysis, a General Electric XRD-5 diffractometer equipped with a pulse-height analyzer set for 90 pct efficiency was employed. The goniometer speed selected was 0.2 deg, 20, per min. Filtered Cu radiation was used for all peaks and all peaks were chart-recorded. Because of nonuni-form grain size. it was necessary to spin the specimens during X-ray analysis in order to obtain reproducible integrated intensities. The spinning rate was 2000 i100 rpm. The application of the Warren-Averbach method of peak broadening analysis to a diffraction pattern is very time consuming if done manually. In this research, the calculations involved were performed with the aid of a computer program by wagner.3 As reported by Wagner, the program is written in Fortran TV computer language. It was modified to Fortran I1 so as to be handled by the IBM 7072 computer at Van-derbilt University. In the X-ray diffraction analysis of uniaxially deformed Cu3Pt, the 100, 200. 400. 111, and 222 reflections were recorded from the initially ordered sample after 'plastic strains of 3.0, 6.0, 9.0, 12.0,

Jan 1, 1970

By A. S. Yue

The interface morphology of the Mg-32 wt pct A1 eutectic has been studied in terms of the freezing rate, the temperature gradient, and the impurity content. For the impure eutectic it has been found that for a given temperature gradient a fast freezing rate favors the formation of a cellular intwface with sub-grain strucfure. This cellular interface can be changed to a planar interface of the same substructure either by decreasing the freezing rate or by increasing the temperature gradient. For the eutectic of highest purity, as purified by zme-refining, no cellular interface was found for any growth condition and only a planar interface with subgrain structure was observed. Furthermore, a layer of liquid adhering to the interface during de-cantation freezes with shapes and sizes of the phase particles different from those in the main eutectic solid. WHEN a molten metal or a binary eutectic liquid with zero freezing range is solidified unidirec-tionally, a cellular interface is usually formed-3 This interface is schematically represented by Fig. 1. The profile of the solid-liquid interface has a corrugated shape, as shown in Fig. l(a), while the decanted interface consists of cells, as shown in Fig. l(b). The cell boundary in a frozen eutectic is distinguishable from the cell interior by changes in particle shapes, as shown in Fig. 4. The formation of a cellular interface, according to Weart and ack,' is attributed to a layer of constitutionally supercooled" liquid generated at the advancing interface by the simultaneous rejection of an impurity by the two phases of the eutectic mixture, which then permits freezing over an appreciable temperature range. This concept has been further elaborated by Tiller, who predicts that even in the absence of an impurity the rejection of solute ahead of each lamella of the eutectic may promote the formation of a cellular interface. More recently, Chilton and Winegard, and

Jan 1, 1963

By S. W. Kennedy, M. Cohen, L. D. Calvert

A high-temperature X-ray diffraction method has been used to study the composition and the kinetics of formation of oxide scales at 800 °C on iron and pure iron-nickel alloys containing 25.6, 75, and 84 pct Ni. This technique has been combined with chemical analysis, and metallographic examination, and determination of weight-gain time curves. The 75 and 84 pct Ni alloys form a three-layer scale consisting of porous NiO next to the metal, a spinel layer, and a -Fe203 on the outside. The 25 pct Ni alloy produces a scale of spinel and Fe,O,, in which, however, traces of FeO and NiO are observed near to the metal. On all the nickel alloys the Fe20, is orieqted with the (107) plane parallel to the surfaces. The exposed surface of the Fe20, is in the form of needles whose axis is perpendicular to the specimen surface. Although the alloys show nonuniform oxidation rates as determined from weight-gain measurements, the X-ray data indicate that the total scale and individml scale layers grow uniformly and parabolically. Deep subscale formation is observed in the 25 pct Ni alloy only. This appeared to be associated with cracking of the scale and penetration of the oxygen along the grain boundaries. ALTHOUGH film formation has been investigated by high-temperature electron-diffraction techniques, for example by Gulbransenl and Hickman,' there have apparently been no investigations of scaling by methods permitting study of the scale during formation at the reaction temperature. Methods involving quenching of scales are based on the working assumption that no significant changes take place on cooling. In general, however, compounds may disproportionate, and the different thermal expansions of constituents may cause disruption of the scale on cooling. In particular, some scales cannot be quenched without spalling. These difficulties are avoided by X-ray diffraction examination at the temperature of formation. High-temperature diffraction procedures also provide a method of determining the kinetics of formation of each phase separately in a multicom-ponent scale. The scaling of binary iron-nickel alloys Containing up to 30 pct Ni at a temperature of 800°C has been studied by Benard and Moreau using cooled specimen~,~ whilst Foley, Druck, and Fryxel14 made an electron-diffraction study of cooled oxide films formed on an iron 42 pci Ni alloy. In the present work the scaling of three iron-nickel alloys containing 25.6, 75, and 84 pct by weight of nickel, at 800°C in oxygen at atmospheric pressure was investigated by X-ray diffraction techniques using a Norelco Geiger-counter diffrac-tometer. The oxidation of iron was investigated for comparison. In addition normal metallographic examinations and chemical and X-ray analyses were made, and weight-gain time curves obtained. EXPERIMENTAL Materials Used—The analyses of the alloys were as follows: Percent by Weight Nickel 25.6 pct 75.4 pct 83.2 pct Aluminum 0.004 None found 0.002 Cobalt — 0.05 0.05 Chromium — — — Silicon — 0.01 None found Carbon All less than 0.05 pct The chemical analysis of the iron was: Al— 0.002 i 0.001 pct, C—0.007 pct, Cr less than 0.001 pct, Cu—0.002 ± 0.001 pct, Mn—0.003 ± 0.001 pct, N—0.0002 pct, 0-0.013 pct, P—less than 0.0002 pct, Pb—not detected, S—0.0017 pct, Si—0.0095 pct, Sn—none detected. This iron was the same as that used to make the alloys and was obtained from the same source-Vacuum Metals Corp. One specimen of pure iron from The British Iron and Steel Research Association was used for preliminary investigation. Specimens were machined to shape from cast rod, polished (the final polish being with 600 Sic paper), degreased in trichlorethylene, washed, and etched. The etching and neutralizing procedure adopted by

Jan 1, 1960

By W. A. Krivsky, R. Schumann

Relaxation calculations were made to find the temperature distribution in the refractory wall surrounding a tuyere pipe. One set of boundary conditions approxiwated those of a standard copper converter while a second set represented a hypothetical,thermally insulated tuyere pipe. The pvonounced cooling effect of the tuyere is related to the problem of tuyere accretions and tuyere bunching. PARTICULARLY severe service conditions are encountered in the tuyere zone of a basic copper converter during the matte blow. High-temperature gradients result from the juxtaposition of the hot charge and the tuyere pipe carrying cold air. Refractory temperatures near the tuyere mouth vary rapidly with time when the blast is turned on or off. One of the most serious problems is the formation of magnetite accretions around the tuyere mouth, which occurs very rapidly under some operating conditions. As a result, continual punching of the tuyeres is necessary to maintain a satisfactory rate of converting. Thus, if some means could be devised for keeping the tuyere pipes fully open without necessity for punching, a considerable saving should result from reduction in labor cost, maintenance of full capacity operation, and reduction in refractory costs. Recent quantitative studies of the FeO-Fe,O,-SiO, system1 have shown that the solubility of magnetite in iron-silicate slags decreases rapidly with de- creasing temperature in the range of copper converting temperatures. Data taken from the previous work are shown in Fig. 1. Thus the formation of "horns" and accretions around the tuyere mouth can result simply from the freezing out of magnetite on the cooler areas of refractory immediately adjacent to the tuyere pipes. One might expect to find a correlation between the severity of magnetite formation and the area of refractory surface which is cooled below the freezing point of the slag (corresponding to magnetite precipitation). Magnetite itself has a very high melting point (1597°C) so that the accretions are for all practical purposes infusible. The accretions might be dissolved by increasing the silica content of the slag and at the same time raising the temperature, but this approach is not feasible because it results in rapid corrosion of the basic refractory lining of the converter as a whole. In order to understand better the problems involved in tuyere design and operation, it seems essential to have at least a semiquantitative idea of the thermal conditions in the tuyere zone. Accordingly, this paper presents results of thermal calculations for an idealized copper converter tuyere. These calculations follow the so-called relaxation

Jan 1, 1960

By H. J. Struth

A glance into the immediate future of the refining industry, and a retrospective view of 1929, cannot fail to emphasize the need for effective measures of control of refinery still runs. With oil producers alert to the need for control of the crude supply, it has become more than ever necessary for refiners to complete the movement toward stabilization by concerted determination to maintain still run schedules within the limitations prescribed by the demand for gasoline. The outlook for continued growth in the demand for gasoline appears to be well sustained by a preliminary survey of requirements for 1930. In fact, it is apparent that the industry will be assured of a market for gasoline that will aggregate in volume at least 472,000,000 bbl. this year. This indicates a gain in total demand over 1929 of about 9 per cent. or about 4.6 per cent, less than the gain recorded during 1929 over 1928, which amounted to 13.6 per cent. Despite the indicated increase in gasoline demand this year, it is apparent that little, if any, more crude will be required than last year. This is shown in Table 1, presenting estimates of gasoline demand and probable crude requirements for 1930. Table 1.—Preliminary Survey of 1930 Gasoline and Crude Run Requirements Millions of Barrels Doniestic gasoline demand................................... 397 Foreign gasoline demand..................................... 75 Total indicated demand...................................... 472 Natural gasoline content..................................... 53 Net gasoline from crude...................................... 419 Imported gasoline........................................... 13 Net gasoline required from refineries.......................... 406 Indicated excess stock Dec. 31, 1929........................... 10 Maximum protluction required................................ 396" At 40 per cent. gasolitlc recovery, this represents a maximum crude converson of 990,000,000 bbl., or a daily average for the ycar 2,712,000 barrels. Year after year, the refining branch of the petroleum industry has been found guilty of running crude to stills greatly in excess of normal requirements, causing frequent periods of market depression. A review

Jan 1, 1930

By T. N. Dixon, J. E. Briggs

A study was made of numerical techniques for solving the large sets of simultaneous equations that arise in the mathematical mode ling of oil reservoir behavior. It was found that noniterative techniques, such as the Alternating Direction Implicit (ADI) method, as well as some other finite difference approximations, produce oscillatory or unsmooth results for large time steps. Estimates of time step sizes sufficient to avoid such behavior are given. A comparison was made of the Point Successive Over-Relaxation (PSOR), Two-Line Cyclic Chebyshev Semi-Iterative SOR (2LCC), and iterative ADI methods, with respect to speed of solution of a test problem. It was found that, when applicable, iterative ADI is fastest for problems involving many points, while 2LCC is preferable for smaller problems. INTRODUCTION With the advent of high speed, large memory, digital computers, there has been an increasing emphasis on the development of improved methods for simulating and predicting reservoir performance. Two-dimensional, three-phase reservoir models with various combinations of PVT effects, as well as gravity and capillary forces, are common throughout the industry. Such models are also available through consulting firms, to anyone desiring to use them. Three-dimensional models will probably be practical in only a few years. We conducted a study of some of the numerical methods used for solving the large sets of simultaneous equations that arise in such models. A typical set of equations for a reservoir model is shown below:

Jan 1, 1969