By N. Tiner

In an article on magnesium and its alloys, Gann and Winston! stated that manganese has a limited solubility in the liquid state. W. Schmidt2 showed a diagram according to Joseph Ruhrmann indicating that the solubility of manganese in liquid magnesium falls from about 2.65 per cent at 790°C. to about 0.5 per cent at 675°C. The curve was extrapolated to show zero solubility at the melting point of pure magnesium (Fig. I). This work suggested that at the lowest manganese contents it was not possible to detect either a eutectic or the formation of a solid solution, so that manganese was stated to be present in the structure as large individual crystals. Two years after the presentation of, these results, Gann3 brought evidence to show that some manganese is capable of dissolving to form a solid solution, any excess of manganese present then assuming chiefly the form of small blue-gray particles scattered throughout the primary magnesium crystals, occasionally in clusters but seldom at the boundaries. He presented micrographs of cast alloys containing 0.1, 0.4 and 1.0 per cent manganese that show a small amount of coring around the individual particles due to solid solution, and indicate that the location of the manganese particles is closely associated with the original dendritic structure of the primary crystallization. He also pointed out that the amount of manganese that can be dissolved in magnesium depends on the amount of other alloying elements present, the effect of the second alloying element being to decrease the amount of manganese retained in the alloy. E. Schmid and G. Siebe14 have determined the solid solubility of manganese and its variation with temperature by means of precision X-ray diffraction measurements. They found that the solubility is 3.4 per cent at 645°C. and decreases to practically zero at 200°C. It is apparent that the X-ray diffraction measurements of Schmid and Siebel are not in agreement with the results of Ruhrmann as presented by Schmidt. This disagreement, and also the lack of data on magnesium-aluminum-manganese and magnesium-zinc-manganese systems, led the author to the present investigation, to determine accurately the liquid solubility of manganese and its variation with temperature. Experimental Method The experimental method for making solubility determinations consists of saturating the molten magnesium or the alloys with manganese at various temperatures and analyzing the dip samples taken from these melts. Melting is carried out in a cylindrical steel pot heated by an electric resistance furnace. The pot had a metallic outside coating to protect the steel against oxidation, and a graphite inside lining to prevent the contamination of the melt by prolonged contact with iron. The inside diameter of the pot was 4 in. and the depth 12 inches.

Jan 1, 1945

By A. G. Lyle, J. D. Runkle, G. A. Gillies

THE evaluation of data obtained by selective flotation from even a simple ore is a very difficult process, and when the ore tested is complex the process becomes extremely difficult and cumbersome. The authors, in the course of an investigation into the selective behavior of various flotation reagents on nonmetallic minerals§ were confronted with an aggravated form of this difficulty, owing to the large mass of data that had accumulated over a period of years. They finally devised a method whereby the results of the various flotation tests could be correlated and interpreted by means of graphs representing recoveries and rejections of the component minerals in the ore. This method of graphical analysis proved so useful in nonmetallic flotation that it was afterwards applied to sulphide flotation, where it yielded equally satisfactory results. Since this method of analysis leads to very definite conclusions as to the effect of changes in reagents and flotation procedure, it is felt that a wider application of the method might assist the industry by reducing the amount of test work required, and possibly increase the accuracy of the final analysis. GRAPHS In Fig. I, four curves are plotted on the same graph with cumulative percentages as ordinates and cumulative weights as abscissas. In this instance the four curves are named, respectively: the barite-recovery curve, the limestone-rejection curve, the silica-rejection curve, and the summation curve. In these tests barite was the mineral concentrated, therefore a barite concentrate was produced. Definitions Before explaining the curves in detail it might be advisable to define several new terms, such as "percentage rejection," "summation index," and "summation curve," as well as the word "test," which has been used in a special sense. A "test" will include all the operations performed upon a batch of ore from the time it is placed in the rod mill until the last product has been assayed. Thus a test may be a comparatively simple procedure producing only one concentrate and a tailing, or it may be a very complicated procedure producing five or more concentrates of a specific mineral as well as a tailing. The number of concentrates produced will depend entirely upon whether the collector was added to the pulp in the flotation cell in one lot or was added in five or more portions. Percentage Rejection.-The ability of a selective flotation collector to reject an undesired mineral is just as important as its ability to collect the desired mineral. The percentage rejection curves shown on the graphs give this factor due consideration and its value is calculated as follows: Suppose a concentrate contains 5 per cent of an undesired mineral. This indicates

Jan 1, 1942

By R. J. Sherman, M. R. Achter

IT has often been reported that coatings may strengthen single crystals and polycrystalline specimens of coarse grain size. This note reports the effect of a surface layer of fine grains on the creep-rupture properties of coarse grained nickel 99.8 pct pure. Sheet specimens were machined from cold-rolled material, finished by surface grinding and annealed at 1230°C in vacuum for 4 hr. Half of them were re-ground on faces and sides and annealed at 925"C for 1 1/4 hr. The double grind-anneal treatment produced a structure consisting of a surface layer of fine grains of 0.02 mm diam on a coarse-grained substrate of grains of 0.40 mm diam. Comparison with specimens which received only the single grind showed that the second grind-anneal did not alter the structure of the substrate. Several modifications were made in specimen design to eliminate erratic rupture behavior outside of the gage length. In the final design the gage section, oriented parallel to the rolling direction, was 1.00 in. long, 0.4 in. wide, and 0.0625 in. thick. End tabs were pinned in place. Although other configurations (welded end tabs, transverse orientation, and wider gage section) showed similar effects of a layer of fine grains, because of the erratic rupture behavior, only the data from the final design are reported here. Creep tests were performed at 650°C in air and in a vacuum of 10~5 mm Hg. Creep rates were measured from the movements of the lever arm. Since the broken sheet specimens could not be fitted together, elongations at fracture measured by means of gage marks, do not include the necked portions adjacent to the fracture. Results of the creep tests with and without the fine grained surface are given in Table I. An explanation for the lower strength in air than in vacuum has been proposed previously in terms of the reduction of crack propagation energy by gas adsorption.l In both environments the fine-grained layer produced a small decrease in minimum creep rate and, except for the shortest test in air, a substantial increase in rupture life. The elongation values at rupture, as they are measured here, do not demonstrate an appreciable effect of the grain structure but do show much smaller ductilities in air than in vacuum. Greater elongations maybe associated with the finegrained layer, however, especially in vacuum, in creep curves such as those in Fig. 1. Duplicate tests were not run to determine the re-producibility of the data. It is felt, however, that, in view of the consistent behavior, the prolongation of rupture life may be attributed to the effect of the fine-grained surface. In the data not reported be-

Jan 1, 1962

By Fred C. Bond

AN improved method of measuring the surface area of a comminution product down to any desired particle size has been developed. The method is largely graphical, and requires relatively little calculation. It can be used with materials containing large amounts of clay, or excess fines of any kind. The surface area S is expressed in terms of square meters per 100 c.c. of solids. This expression is based upon volume rather than weight, and is considered to be more suitable for crushing and grinding problems, where the machines ordinarily are operated under constant volume conditions. It has the advantage that surface areas of different materials can be compared directly, even though their specific gravities may be unknown. The "specific surface" of a material, or the number of square centimeters of surface area per gram, is equal to 100S divided by the specific gravity. Particle diameters are expressed in microns, K being the diameter of the largest particle present and L the grind limit, or lower size limit of the particles formed directly by grinding. The value of K does not always coincide exactly with the diameters of the largest particles retained on the coarsest testing sieve, since the largest particles formed in crushing and grinding are often slabby, or have other irregular shapes. L has been chosen as 0.700 microns, or number 27.5 in the size number series, for reasons to be explained later. S is the total surface area of all particles larger than L microns in diameter. When a homogeneous comminution product is separated into fractions whose diameters bear a constant geometrical relationship p to each other, and the log per cent weight retained upon each size and passing the next larger size is plotted against the log diameter, a straight line results, which is called the distribution line, and which has a slope in called the distribution modulus. The distribution line can be extended to any desired limiting size, and the total surface area of all particles larger than that size can be calculated. The equation of the distributi0n line is [w = Cx" [I]] where w is the per cent weight retained on each successive sieve; x is the particle diameter; and C is the per cent weight retained on an opening of unit diameter.2 Theoretically, the distribution line can be extended to include infinitely small particles. When it is so extended, and the assumption is made that no fine particles are present other than those accounted for by the equation; the log per cent cumulative weight passing any series of sizes, plotted against the log diameter passed, will result in a straight line lying parallel to and above the plotted distribution line.

Jan 1, 1941

By D. Kruse, M. Sanaei

"A three dimensional nonlinear finite element model was constructed to simulate and analyze the behavior of large diameter segmentally lined shafts when subjected to seismic waves. To reduce computation time, a less complex shell model was also constructed. Transient excitation was applied to the supported nodes of both models, at the base of the shaft, with a time-function representing the 1994 Northridge earthquake. The models are developed at the end of an original phased construction-stage analysis of the shaft. Displacements, forces and moments are monitored and compared during the analyses steps. During the initial 15 seconds of the earthquake, the top and bottom of the shaft show similar displacements. The maximum horizontal displacement within the shaft is approximately 3.5 inches in the solid model and the shell model results conform to this by a factor of 50%. Keywords: Segmentally Lined Shaft, Soil Structure Interaction, Seismic Analysis, Finite Element Modeling, Ground Modification INTRODUCTION TO SEGMENTALLY LINED SHAFTS Large diameter segmentally lined shafts (SLS) are underground systems, constructed sequentially using precast concrete segments to form a ring which provides both temporary earth support during excavation and permanent structural support. The segments are connected via alignment pins, bolts, packer material and other structural components that ensure the continuity of the SLS. In this analysis, the construction process uses a top-down sequence wherein each soil layer is excavated, damp-proofing is installed and concrete segments are assembled to form each ring. This process is repeated until design depths are achieved completing the shaft. It is known that cylindrical structures sustain lateral (earth) pressure mainly through the mechanism of hoop-stress. As Timoshenko’s ring theory goes, a cylinder shell structure is prone to buckling under external pressure [1]. In typical designs of small diameter shafts and tunnel linings with small diameter to wall thickness ratios, nonlinear buckling analysis (i.e., nonlinear geometric analysis) is not considered, since the buckling capacities for those structures are much higher than typical pressures encountered at their design depths. However, in shafts with large diameter to wall thickness ratios, buckling could become a critical issue. In any given mode, as buckling occurs in a ring, some sections of the structure move inward while alternating sections protrude. Although the presence of the surrounding soil could mitigate the buckling by resisting the movement (Soil structure interaction) seismic loads can cause ground movements and lateral pressures, exceeding the capacity of the structure. It is therefore essential to design the load bearing capacities of the shaft to minimize the possibility of any catastrophic failure due to earthquakes. This study explores the structural response of the SLS when subjected to seismic loads."

Jan 1, 2016

By George D. Roberts

INTRODUCTION CIVIL engineers are primarily interested in maximum core recovery. This is even more important in foundation work than in mining investigations where sludge samples are of some value. The soft materials, such as clay, gouge, or partially decomposed seams that are most readily ground up or washed away, are the materials that usually have the greatest influence on foundation and leakage conditions. Undisturbed samples of such materials should be obtained for detailed geological examination and laboratory tests. Therefore the attainable goal of sampling in connection with foundation investigations is the recovery of 99.9 pct of undisturbed core. FACTORS CAUSING CORE LOSSES The principal factors contributing to core losses are: (I) coring badly fractured or very soft material; (2) use of improperly designed coring equipment, including the use of bits of too small a diameter; (3) lack of the proper training and attitude on the part of the drillers and pertinent technical information on the part of the supervising personnel. Little can be done about the character of the material being cored but the other two factors contributing to unsatisfactory performance can be corrected. Although the title of this paper is the improvement and standardization of core barrels, it is believed that the drillers' shortcomings and the lack of pertinent technical literature are more detrimental to good core recovery than either of the other factors. USES FOR LARGE DIAMETER CORE BARRELS It is well known that the use of larger diameter bits and core barrels generally produce better cores, particularly when sampling soft or broken material. The use of larger and larger bit diameters and the insistence on better core recovery is well demonstrated by the change in practices of the various districts of the Corps of Engineers. Today NX core is the smallest diameter commonly permitted for investigational work and the more active districts are using coring bits up to 6 in. in diameter, as well as 36 and 40-in. calyx rigs. The latter size has proved to be just as economical because it provides more room for core removal and cleanup operations. The use of large diameter cores to replace the driving and jacking methods of obtaining soil samples is also increasing. The 5 7/8-in. Denison sampler, developed by H. L. Johnson to obtain samples from soft formations, is one example. The principal uses for bits larger than NX are: sampling soils and semi-consolidated rock; sampling decomposed rock or rock with soft seams; sampling concrete; obtaining samples for laboratory tests; drilling drainage holes, and other miscellaneous work. CORE DRILLING PRACTICES OF SEVERAL ENGINEER DISTRICTS Little Rock District The writer was employed in the Little Rock District from 1938 until 1942. Prior

Jan 1, 1947

By Alec M. Crowell, Thomas D. Bailey

Although natural gas was first discovered in Northwest Arkansas in 1887, . near Fort Smith, Sebastian County, the literature contains very little information on the region, which is separated distinctly from the oil area of Southern Arkansas. For that reason this brief and concise report is a summary of developments from discovery to the present time. Northwest Arkansas produced 5,736,-ooo,ooo cu. ft. of natural gas during 1942, the trend of production having been generally upward over the past five years, as is shown in Fig. I. Since 1904 a reserve of 237 billion cubic feet of natural gas has been discovered in Northwest Arkansas, of which approximately 162 billion cubic feet have been expended, leaving a reserve of approximately 75 billion cubic feet available as of Jan. 1, 1943. A prolific new field discovered in Pope County Oct. 23, 1942, will add to the reserve of the region materially. Per well reserves, over-all, are unusually high because of the practice of multiple completion. As yet no commercial deposits of oil have been discovered in Northwest Arkansas. but the gas deposits have proved of immense value industrially, principally in the processing of zinc ore mined in the local area as well as that imported from distant states. With the war, new interest in the exploitation of the metallic ores of the region lends new significance to the gas reserves tabulated herein. Geological Discussion The region covered in this report comprises the Arkansas Valley from Pope County weslward to the Arkansas-Oklahoma state line as shown in Fig. 2. This valley is a westward trending structural trough with sharp-topped ridges and mesa-like mountains rising above the valley's undulating surface. It is bounded on the north by the Ozark Highlands and on the south by the Ouachita Mountains. The sedimentary beds of the Arkansas Valley are composed mainly of noniossil-iferous shales and sandstones. The rocks contain a high content of carbonaceous material and many coal beds are found in the region. The Gxed carbon ratios (ratio of fixed carbon to volatile combustible matter of surface coals) are very high and average about 80 per cent over the region covered in this report. Little or no calcareous material is present. Rocks of the Arkansas Valley are sharply folded, and igneous intrusive rocks cut the sedimentary beds at a few places. The Arkansas Geological Survey' made a detailed reconnaissance survey of the Arkansas Valley province in 1927, the purpose being to delineate the major structural features (Fig. 3) and to point out the possibilities of discovering addi. tional gas deposits. More than fifty anticlines were mapped as a result of this survey. The information gained by this

Jan 1, 1943

By Thomas D. Bailey, Alec M. Crowell

Although natural gas was first discovered in Northwest Arkansas in 1887, . near Fort Smith, Sebastian County, the literature contains very little information on the region, which is separated distinctly from the oil area of Southern Arkansas. For that reason this brief and concise report is a summary of developments from discovery to the present time. Northwest Arkansas produced 5,736,-ooo,ooo cu. ft. of natural gas during 1942, the trend of production having been generally upward over the past five years, as is shown in Fig. I. Since 1904 a reserve of 237 billion cubic feet of natural gas has been discovered in Northwest Arkansas, of which approximately 162 billion cubic feet have been expended, leaving a reserve of approximately 75 billion cubic feet available as of Jan. 1, 1943. A prolific new field discovered in Pope County Oct. 23, 1942, will add to the reserve of the region materially. Per well reserves, over-all, are unusually high because of the practice of multiple completion. As yet no commercial deposits of oil have been discovered in Northwest Arkansas. but the gas deposits have proved of immense value industrially, principally in the processing of zinc ore mined in the local area as well as that imported from distant states. With the war, new interest in the exploitation of the metallic ores of the region lends new significance to the gas reserves tabulated herein. Geological Discussion The region covered in this report comprises the Arkansas Valley from Pope County weslward to the Arkansas-Oklahoma state line as shown in Fig. 2. This valley is a westward trending structural trough with sharp-topped ridges and mesa-like mountains rising above the valley's undulating surface. It is bounded on the north by the Ozark Highlands and on the south by the Ouachita Mountains. The sedimentary beds of the Arkansas Valley are composed mainly of noniossil-iferous shales and sandstones. The rocks contain a high content of carbonaceous material and many coal beds are found in the region. The Gxed carbon ratios (ratio of fixed carbon to volatile combustible matter of surface coals) are very high and average about 80 per cent over the region covered in this report. Little or no calcareous material is present. Rocks of the Arkansas Valley are sharply folded, and igneous intrusive rocks cut the sedimentary beds at a few places. The Arkansas Geological Survey' made a detailed reconnaissance survey of the Arkansas Valley province in 1927, the purpose being to delineate the major structural features (Fig. 3) and to point out the possibilities of discovering addi. tional gas deposits. More than fifty anticlines were mapped as a result of this survey. The information gained by this

Jan 1, 1943

By E. I. Larsen

Powder metallurgy has been described as being "as old as the pyramids and yet as new as the latest bomber." While this may be true literally, it has been only in the last Io or 1 5 years that widespread use has been made of this method of fabricating various articles One of the first items fabricated by powder metallurgical methods on a commercial scale was electrical contacts, which were fabricated from metal powders as early as 1920. The reason why these contacts have been made for so many years by powder metallurgy is because the compositions of most of these materials arc such that they could not be made by the conventional methods of melting, casting, rolling, drawing, etc. Classes of Contacts In general, electrical contacts fabricated from metal powders fall into two classes, both from the point of view of the method of fabrication and the components that make up the chemical composition. One class is composed of silver or copper and a refractory metal such as tungsten, molybdenum, or compounds thereof such as carbides. The second class contains a predominant amount of silver and a semi-refractory material such as cadmium oxide, nickel, cobalt, or graphite. Electrical contacts of the first class have been developed primarily as facing materials for heavy-duty circuit-interrupting devices. This class of material unites the high melting point, high boiling point, great resistance to electrical erosion, and the refractory characteristics of molybdenum, tungsten, or their carbides with the high thermal and electrical conductivities and low contact resistance properties of silver or copper. The second class of material is used for lighter duty or specialized applications such as heavy-duty, direct-current aircraft relays. Varieties Electrical contacts fabricated from metal powders are made in a wide variety of compositions, shapes, and sizes. In general, the sizes of electrical contacts fabricated from powders vary from contacts weighing approximately 0.001 oz. up to those weighing 3 to 4 Ib., the contacting face being as small as 0.001 sq. in. up to approximately 6 sq. in. in area. The shapes consist of: sound or rectangular buttons, some of which have radii or bevels on the contacting faces; rings, cups, rectangular bars, the contact face of which may have a radius across the width and/or at one end; and form-pressed pieces of a wide variety such as angles, both acute and obtuse, irregular shapes comprising a radius blended into a flat, which in turn may have steps. The size or shape of the contact is dictated principally by the mechanical design of the manufacturer, who in turn may have problems to be met such as: (I) size, weight, or space limitations; (2) electrical conditions such as blowout coils arc chutes, baffies, gas passages.

Jan 1, 1945

By Jehan Rondot

Les trois intrusions alcalines de Suzorite en haute Mauricie, bien que non datees, son! sans doute d ,attacher aU)( nombreuses autres intrusions alcalines dispersees sur les blocks Grenvillia et Laurentia et datees de I 050 Ma =t= 10%, done reliees d l'orogene grenvilien. L 'utilisations de la Suzorite est liee d sa forte proportion de phlogopite (>50%). Le rapport Mg/Fey varie de 3 d 7. Sa mineralogie et sa composition particulieres (forte proportion de Mg, Ket H20) en font son attrait.

Jan 1, 1984

By White L. R, Boger D. V

The paper describes the surface chemistry and particle physics that control the fundamental flow properties (Theology) of mineral particle slurries. We further address, through a series of case studies, the design data that emerges from experimental studies of the flow properties of complex, high volume fraction mineral slurries. The case studies are drawn from mineral oxide concentrate processes, tailings dewatering operations and from filter cake production and management. The paper emphasises the essential links between design of process slurry handling systems and the control of the flow of such slurries by control of the pulp chemistry.

Jan 1, 1992

By Frank Firmstone

In April, 1873, No. 2 furnace at the Glendon Iron Works being out of blast, it was decided to alter it from an open to a closed top. The three side flues, through which a part of the gas was formerly taken off, were 15 feet below the top, and as, for various reasons, it was not convenient to cut new flues through the brickwork at the top, as is commonly done with closed-top furnaces, a modification of Coingt's charger was employed. This apparatus, as figured by De Vathaire,* consists of a cup or hopper, like that used with the cup and cone, and a central pipe for taking off the gas, which descends some distance into the furnace, and has a projection around it forming a seat for a ring of a triangular cross-section, which closes the opening between the cup and the central gas-pipe. The charge is put into the cup, and by lowering the ring, is thrown into the furnace, a part going outside of the ring toward the walls, and a part through the inside toward the gas-pipe. In this form the apparatus was not applicable, for: 1st. With a gas-pipe three feet in diameter, in a top eight feet in diameter, the openings left by lowering the ring would not be large enough to let lump coal pass through. 2d. For the charger to shut tight, the ring must bear equally against the projection made for it on the gas-pipe, and against the edge of the cup. This would not be difficult to effect when the apparatus is first put up, but a comparatively small change in the relative position of the parts, such as is almost certain to occur from expansion, would cause the ring to touch the pipe or the cup, whichever happened to be the lower, first, and leave a leak between it (the ring) and the other. In the plan adopted (Figs. 5 and 6, Plate I), the central opening in the ring is closed by the bottom of the gas-pipe, whereby more room is left for the passage of the stock when the charger is open, than if the pipe descended into the furnace; and the pipe, instead of being rigidly supported, rests on the ring, when the charger is closed, and follows it for two or three inches as it opens, until stopped by the counter-balance lever C. When the ring is raised to close the furnace top, it comes in contact first with the bottom edge of the gas-pipe, then both are raised together, until stopped by the ring touching the edge of the cup. In this way a good joint is made at both places.

By Frank Firmstone

IN April, 1873, No. 2 furnace at the Glendon Iron Works being out of blast, it was decided to alter it from an open to a closed top. The three side flues, through which a part of the gas was formerly taken off, were 15 feet below the top, and as, for various reasons, it was not convenient to cut new flues through the brickwork at the top, as is commonly done with closed-top furnaces, a modification of Coingt's charger was employed. This apparatus, as figured by De Vathaire,* consists of a cup or hopper, like that used with the cup and cone, and a central pipe for taking off the gas, which descends some distance into the furnace, and has a projection around it forming a seat for a ring of a triangular cross-section, which closes the opening between the cup and the central gas-pipe. The charge is put into the cup, and by lowering the ring, is thrown into the furnace, a part going outside of the ring toward the walls, and a part through the inside toward the gas-pipe. In this form the apparatus was not applicable, for: 1st. With a gas-pipe three feet in diameter, in a top eight feet in diameter, the openings left by lowering the ring would not be large enough to let lump coal pass through. 2d. For the charger to shut tight, the ring must bear equally against the projection made for it on the gas-pipe, and against the edge of the cup. This would not be difficult to effect when the apparatus is first put up, but a comparatively small change in the relative position of the parts, such as is almost certain to occur from expansion, would cause the ring to touch the pipe or the cup, whichever happened to be the lower, first, and leave a leak between it (the ring) and the other. In the plan adopted (Fig's. 5 and 6, Plate I), the central opening in the ring is closed by the bottom of the gas-pipe, whereby more room is left for the passage of the stock when the charger is open, than if the pipe descended into the furnace; and the pipe, instead of being rigidly supported, rests on the ring, when the charger is closed, and follows it for two or three inches as it opens, until stopped by the counter-balance lever C. When the ring is raised to close the furnace top, it comes in contact first with the bottom edge of the gas-pipe, then both are raised to¬gether, until stopped by the ring touching the edge of the cup. In this way a good joint is made at both places. * Etudes our lea Haut Fourneaux, page 108.

Jan 1, 1874

By B. Wilshire, W. J. Evans

W. J. Evans and 8. Wilshire SEVERAL recent investigations1-6 have shown that the strain, c, during transient and steady-state creep is well-represented by the expression: € = e0 + et(l - e-mt) + Esl [l] where Eo is the instantaneous strain on loading, ET the total transient strain, C, the steady creep rate! and m a constant relating to the rate of exhaustion of transient creep. However, it has been noted6 that deviations from this equation occur over the first 10 to 15 pct of the transient stage, when the creep rate, (. decreases more rapidly than is predicted by this equation. This rapid decrease has been attributed to a large change in work-hardening coefficient. It 1s widely accepted that steady-state creep results from a balance between the rate of strain hardcning h and the rate of recovery r (=-s(st) as: dE/dt = Es = r/h [2] Comparison of values obtained for h at the end of the initial extension and during steady creep suggests that h increases several fold during the transient stage. which has the effect of reducing the creep rate proportionally.7 To examine the dependence, on r and h, of the deformation behavior during transient and steady-state creep. a series of constant-stress creep tests was carried out at 413°C at 6000 psi using 70-30 a brass. Prelinlinary investigation showed that. with this material. the transient stage constituted a significant portion of the total creep life (-0.4tf. where tf is the time to fracture). The alloy. obtained from Metals Research Limited. was made from high-purity copper, 99.999 pct. and zinc. 99.99 pct. Heat treatment at 675°C for 4 1/2 gave a uniform grain size of 5 mm-1. Details of specimen preparation and creep testing procedures have been given previously.6 Values of h (?s/?E) were determined by measuring the instantaneous strain. ?E. which occurred on increasing the stress during creep by a small amount. ?s. Similarly. v (= -?s/ ?t) was derived from the incubation period. At, after a small decrease in stress.' Several values of v and h were obtained throughout duplicate creep tests. using different stress increments in the range 300 to 800 psi. The accuracy with which Eq. [I] represents the present creep curves was established by determining the best value of the constants Es, Et, m , and 6, using a digital computer program based essentially on the graphical solution for this equation devised by Conway and Mullikan.9 About 40 strain/time readings were taken during transient and steady-state creep. Over most of the creep curve, the average difference between the measured reading and the calculated strain at the appropriate time was less than 0.0001. However.

Jan 1, 1969

By Clarence Zener, Howard Clarke, Cyril Stanley Smith

The importance of cold-working in the fabrication of metals is in marked contrast with our ignorance as to the nature of the accompanying internal changes. The failure of the usual methods of testing to provide a consistent picture of these internal changes has given the incentive for the present program of investigating the effect of cold-working upon the internal friction of metals measured at small strain amplitudes. It has previously been shown1,2,3, that the internal friction introduced by cold-work is removed by annealing at comparatively low temperatures. In the present paper the following additional factors are investigated: (I) frequency of measurement, (2) amount of cold-work, (3) temperature of measurement. Special care was taken to minimize the internal friction due to causes other than cold-work. The present paper is purely experimental, the authors believing that any conclusions drawn from this work as to the nature of the internal changes accompanying cold-work would be premature.'l PrEpaRations oF Specimens In this study of cold-work it was desirable to eliminate as far as possible all other sources of internal friction. One disturbing source is the lack of temperature equilibrium between adjacent crystallites of a vibrating specimen.4 Temperature equilibrium is aided by small grain size and by the use of low-frequency vibrations. Unless unduly long specimens are used, low frequencies can be obtained only in transverse vibrations. But in transverse vibrations a second source of internal friction is present, that arising from transverse thermal currents.5 The effect of these may be reduced by increasing the transverse dimensions. The grain size and transverse dimensions of the specimens were thus so chosen as to render the vibrations simultaneously nearly isothermal with respect to intercrystalline thermal currents, and nearly adiabatic with respect to transverse thermal currents. The material for this investigation was a 70-30 brass, part of the same lot of material that was used for some earlier studies on the effect of strain on proportional limit.10 It had the following composition: copper, 70.59 per cent; zinc, 29.39; lead, 0.01; iron, 0.01. This material was received from the brass mill in the form of 3/4-in. rod, cold-drawn to final size by a 65 per cent reduction of area from material that had been annealed to give a grain size of 0.060 mm, Rods of appropriate length were annealed for 2 hr. at 400°C. and cooled in air. The annealed rods (grain size, 0.012 mm.) were then stretched in a tension-testing machine, using special grips1' to ensure axial application of the load. The rate

Jan 1, 1942

By A. M. Gaudin

IT is only in recent years that substantial progress has been made in developing a physico-chemical picture of the solid state. The molecular concept, so useful in dealing with gases, was naturally carried over to the field of crystalline solids; it has resulted in the firm implanting of erroneous concepts that only now are being eradicated successfully. Two simply written and effective books on the subject are Crystal Chemistry by Stillwell1 and An Introduction to Crystal Chemistry by Evans.' A more complete treatment of the subject is available in a book by Wells.' The monograph by Hückel4 also touches on a subject most easily perceived by reference to the brief introduction by Bragg,5 that master of the field. These texts make it clear that while some solids are built of molecules, many are built of ions, others of atoms connected in the form of giant molecules, and still others of cations and electrons. The various lattices in which these entities are systematically arranged, the joint use of several of these entities, and the transitional character of some of the bonds make for the great variety of crystalline solids. The purpose of this paper is to point out a most important corollary of present views on the structure of solids. In this connection the classification of solids in Table I is helpful. Atomic crystals are those formed by the noble gases, e.g., helium and argon. They are soft, sublime at very low temperature, of very low specific gravities, and not encountered in ores. Molecular crystals are uncommon among inorganic materials, common among organic materials. Typical examples from both inorganic and organic fields are sulphur, iodine, naphthalene, benzene, and carbon tetrachloride. These crystals are soft and have low specific gravities; where the molecules are small, the sublimation temperature is low. Filament and sheet crystals are rare. They are typified by elemental selenium and elemental arsenic, respectively. Graphite and molybdenite come near being sheet crystals. These crystals are soft in some directions, tough in others, sublime at various temperatures. Diamantine crystals, typified by diamond, are very few in number, stable at high temperatures, and extremely hard. Ionic crystals are common. Most salts, acids, and alkalies belong in the two classes of ionic crystals; examples are rock salt, fluorite, calcite, and angle-site. The salts, acids, and alkalies that do not belong in these classes are more properly regarded as transitional between ionic crystals, framework crystals, and diamantine crystals, e.g., ice and quartz. Fiber crystals are relatively uncommon mineral-ogically speaking, but common in the fields of living processes. Examples are asbestos, silk, cellulose, and wool. Many fiber crystals are so little known even now that their crystallinity may be doubted. Layer crystals, among the more interesting and useful of solids, include a wide variety of substances

Jan 1, 1956

By Howard Clarke, Cyril Stanley Smith, Clarence Zener

The importance of cold-working in the fabrication of metals is in marked contrast with our ignorance as to the nature of the accompanying internal changes. The failure of the usual methods of testing to provide a consistent picture of these internal changes has given the incentive for the present program of investigating the effect of cold-working upon the internal friction of metals measured at small strain amplitudes. It has previously been shown1,2,3, that the internal friction introduced by cold-work is removed by annealing at comparatively low temperatures. In the present paper the following additional factors are investigated: (I) frequency of measurement, (2) amount of cold-work, (3) temperature of measurement. Special care was taken to minimize the internal friction due to causes other than cold-work. The present paper is purely experimental, the authors believing that any conclusions drawn from this work as to the nature of the internal changes accompanying cold-work would be premature.'l PrEpaRations oF Specimens In this study of cold-work it was desirable to eliminate as far as possible all other sources of internal friction. One disturbing source is the lack of temperature equilibrium between adjacent crystallites of a vibrating specimen.4 Temperature equilibrium is aided by small grain size and by the use of low-frequency vibrations. Unless unduly long specimens are used, low frequencies can be obtained only in transverse vibrations. But in transverse vibrations a second source of internal friction is present, that arising from transverse thermal currents.5 The effect of these may be reduced by increasing the transverse dimensions. The grain size and transverse dimensions of the specimens were thus so chosen as to render the vibrations simultaneously nearly isothermal with respect to intercrystalline thermal currents, and nearly adiabatic with respect to transverse thermal currents. The material for this investigation was a 70-30 brass, part of the same lot of material that was used for some earlier studies on the effect of strain on proportional limit.10 It had the following composition: copper, 70.59 per cent; zinc, 29.39; lead, 0.01; iron, 0.01. This material was received from the brass mill in the form of 3/4-in. rod, cold-drawn to final size by a 65 per cent reduction of area from material that had been annealed to give a grain size of 0.060 mm, Rods of appropriate length were annealed for 2 hr. at 400°C. and cooled in air. The annealed rods (grain size, 0.012 mm.) were then stretched in a tension-testing machine, using special grips1' to ensure axial application of the load. The rate

Jan 1, 1942

By E. F. Ketterer, D. B. Collyer, A. B. Wilder

AISI constructional alloy steels are a series of steels in which a numbering system signifies the chemical composition limits. SAE (Society of Automotive Engineers) and AISI (American Iron and Steel Institute) use basically the same numbering system. The steels contain, in part, alloy additions of chromium, molybdenum, nickel, and vanadium. They are used widely in the automotive industry but have not been adopted for high temperature service. The purpose of this investigation was to study changes in microstructure observed in typical AISI constructional alloy steels in the welded and un-welded conditions after exposure for 34,000 hr at 900" and 1050" and, in several instances, 1200°F. The tensile and creep rupture properties after exposure for 10,000 hr were also evaluated. The investigation is a continuation of the work previously discussed. Little was known concerning the existence of graphite in medium or low carbon steels before 1943. It is important to note that continued exposure at elevated temperature is required in order to develop graphite in steels. Interest in the presence of graphite in steel, and also in changes in the properties of steels after long service at elevated temperatures, developed after 1943 when a failure of a welded joint of high temperature piping was associated with the graphitization of a relatively low carbon content steel with 0.50 pct Mo,8,0 Numerous investigations have beeen made in recent years studying the relationship of this type of failure to changes in properties. Attempts have been made to evaluate the performance of a number of steels, particularly in the heat-affected zone of welds. It was the unfortunate failure of a weld-heated zone in high temperature piping in the steam-power industry which focused attention upon possible failures, and upon the need for improved steels for high temperature piping service. Investigation by the National Tube Div., U. S. Steel Corp., Lorain Works, has included a wide variety of steels in an attempt to learn the effects of numerous factors and elements upon the long time performance of steels, although many of the compositions studied will never be used at elevated temperatures.1,4-7 Included were the well established AISI steel series, which offered opportunity to test moderately high carbon content steels as well as observe the effect of nickel, chromium, molybdenum, etc., upon the properties of these well known steels. The properties of the AISI steels were also studied for comparison with the previously reported properties of the Cr-Mo steels, now used by the steam-power industry.5,7 Materials and Testing Procedure The AISI alloy steels in Table I were exposed for 10,000 and 34,000 hr at 900°, 1050°, and 1200°F.

Jan 1, 1958

By Gerald M. Ellis

Exploration for gold .deposits on Hispaniola has taken place sporadically over the years but has expanded in the past decade. There are veintype, disseminated, alluvial and elluvial deposits. Investigations were previously undertaken in Haiti by combined Haitian, Bureau of Mines, and UN geological teams at Grand Bois Limbe(Milot) and Cap Coq areas. Later studies were conducted at the Miches and Moncion districts. Gold occurrences were reported in quartz, silicic-barite veins and gossans. An important deposit ?at Pueblo Viejo is? a disseminated type where extraction is taking place in the oxidized zone. Exploration by Japanese and West German firms with local geologists are described in this paper together with Pueblo Viejo, Miches, Restauracion, Milot, and Meme ?areas where occurrences are known. Copper deposits with associated gold va1ues are also described. These include vein deposits in Central Cordillera and disseminated deposits at Terrier Rouge and Blondin.

Jan 1, 1989

By Blake M. Loring

RECENTLY the S-curves for 30 to 40 alloy steels have been published.1,2 These steels show individual characteristics, which make each additional S-curve of great interest. There are important differences in the mechanism of the transformation process, the type of transformation product, and the influence of alloying elements. Steels of the same general alloy composition may possess such variable characteristics with regard to the length of time of isothermal transformation that an S-curve for each heat of steel may be desirable. In the present work the isothermal transformation of a steel having the following composition and grain size was studied: 0.20 percent carbon; 0.21 manganese; 0.026 phosphorus; 0.017 sulphur; 0.056 silicon; 1.45 chromium; 3.25 nickel; austenite grain size, 7. The progress of the isothermal transformation was followed by several different methods, including hardness measurements, dilatometer observations, and examinations of the microstructure. It was not expected that these methods would be in precise agreement.3 Accordingly, the changes in microstructure and hardness were given additional weight in determining the initial stage of transformation and the dilatometer measurements were relied on in estimating the completion of the process. The beginning of transformation was indicated by I per cent of transformation products and the end of transformation by about 99 per cent. The reproducibility of the various methods in the ranges of highest sensitivity was checked by several observations at each time and temperature. The steel used in this investigation was annealed for 24 hr. at 925°C. Macroetching revealed no serious segregation. The specimens for the metallographic and hardness investigations were 1 1/4 by 1/2 by 1/8 in. Wires attached to the samples were used for handling, instead of tongs, to avoid chilling. The specimens were heated at 845°C. for 1/2 hr. and quenched into constant-temperature salt baths held at various temperatures from 205° to 650°C. The time required to transfer the specimens was found to be about x 1 1/2 sec., and nearly 5 sec. more was required for them to come to the temperature of the bath. After various lengths of time in the constant-temperature baths the specimens were quenched in water at 21°C. The specimens were cut in half for the metallographic examination, to provide a surface free from decarburization. To determine the beginning and end of the transformation the percentage of transformation determined metallographically and by hardness was plotted against time. A planimeter was used in the metallographic determination. The hardness and metallographic determinations made at room temperature were confirmed reasonably well by dilatometer measurements taken during the process of transformation at the various temperatures. Two dilatometers were used to

Jan 1, 1941