Search Documents

By M. C. Udy, P. C. Rosenthal

The use of minute boron additions to steel has been given considerable attention in recent years. Comparisons made between boron-free and boron-containing heats of otherwise identical analysis have indicated, beyond a doubt, the potent effect of boron for increasing hardenability. The actual hardenability increase has been expressed as a multiplying factor, or in terms of the percentage of other alloying elements boron might replace. The present study presents the results of a systematic survey of the use of boron as an addition to two types of alloyed steels and as a replacement for various percentages of molybdenum in these steels. Both cast and wrought steels of the two basic compositions were prepared. Molybdenum, because of its scarcity at the time the investigation was started, was selected as the element to be replaced by boron. Attention was also given to the effects of boron on other properties of the steels, particularly their notched-bar toughness, to investigate other advantages or limitations of this element as an alloy addition. Experimental Work Steels Investigated The two basic compositions used in this survey of boron as a replacement for molybdenum are given in Table I. The cast steels were higher than the wrought steels in silicon content to improve the casting quality. Table i.—Nominal Composition of the Two Base Alloy Steels composition. Per Cent. steel Mn Si Ni Cr Xi-Cr-Mo Wrought 0.28-0.70-0.15-o.45—o.45-0.32 0.90 0.25 0.55 0.55 Cast 0.28-0.70-0.35-0.45-o.45- 0.32 0.90 0.45 0.55 0.55 hln-&lo Wrought 0.28-I .go-o.0.15-0.32 1.70 0.15 Cast o. 28- I.40- 0.35- 0.31 1.70 0.45 a Sulphur was 0.040 per cent maximum and phosphorus 0.030 per cent maximum. Each of these base steels, both cast and wrought, was made with molybdenum contents of o, 0.10, 0.20, 0.30, or 0.40 per cent, the total comprising 20 steels. In addition, each of these 20 compositions was prepared with boron additions in amounts of o.oo15, 0.003, and 0.006 per cent as ferroboron; and in amounts of 0.002 and 0.005 per cent as two commercial intensifier alloys, designated alloys A and B. The boron-treated steels totaled 100, and the entire series 120. Test Procedure Each steel was melted as an individual heat in a 50-lb., magnesia-lined induction furnace. Ingot iron scrap or mixtures of ingot iron and steel. scrap were used for melting stock. Deoxidation was carried out in the furnace with 0.10 per cent aluminum. The aluminum addition was

Jan 1, 1948

By M. C. Udy, P. C. Rosenthal

The use of minute boron additions to steel has been given considerable attention in recent years. Comparisons made between boron-free and boron-containing heats of otherwise identical analysis have indicated, beyond a doubt, the potent effect of boron for increasing hardenability. The actual hardenability increase has been expressed as a multiplying factor, or in terms of the percentage of other alloying elements boron might replace. The present study presents the results of a systematic survey of the use of boron as an addition to two types of alloyed steels and as a replacement for various percentages of molybdenum in these steels. Both cast and wrought steels of the two basic compositions were prepared. Molybdenum, because of its scarcity at the time the investigation was started, was selected as the element to be replaced by boron. Attention was also given to the effects of boron on other properties of the steels, particularly their notched-bar toughness, to investigate other advantages or limitations of this element as an alloy addition. Experimental Work Steels Investigated The two basic compositions used in this survey of boron as a replacement for molybdenum are given in Table I. The cast steels were higher than the wrought steels in silicon content to improve the casting quality. Table i.—Nominal Composition of the Two Base Alloy Steels composition. Per Cent. steel Mn Si Ni Cr Xi-Cr-Mo Wrought 0.28-0.70-0.15-o.45—o.45-0.32 0.90 0.25 0.55 0.55 Cast 0.28-0.70-0.35-0.45-o.45- 0.32 0.90 0.45 0.55 0.55 hln-&lo Wrought 0.28-I .go-o.0.15-0.32 1.70 0.15 Cast o. 28- I.40- 0.35- 0.31 1.70 0.45 a Sulphur was 0.040 per cent maximum and phosphorus 0.030 per cent maximum. Each of these base steels, both cast and wrought, was made with molybdenum contents of o, 0.10, 0.20, 0.30, or 0.40 per cent, the total comprising 20 steels. In addition, each of these 20 compositions was prepared with boron additions in amounts of o.oo15, 0.003, and 0.006 per cent as ferroboron; and in amounts of 0.002 and 0.005 per cent as two commercial intensifier alloys, designated alloys A and B. The boron-treated steels totaled 100, and the entire series 120. Test Procedure Each steel was melted as an individual heat in a 50-lb., magnesia-lined induction furnace. Ingot iron scrap or mixtures of ingot iron and steel. scrap were used for melting stock. Deoxidation was carried out in the furnace with 0.10 per cent aluminum. The aluminum addition was

Jan 1, 1948

By W. Ivanick, Frank W. Glaser

ORDERING reactions of Fe-Si compositions in the a region have been mentioned in a number of review articles.7-8 However, little is known in regard to the critical temperature, T at which this transformation takes place. Greiner and Stoughton,' in a study of the constitution of iron-rich Fe-Si alloys below 800°C, placed the onset of order at a composition of about 4 to 5 wt pct (7.5 to 9.5 atomic pct) Si. They observed that at this composition the ductility and strength begin to decrease sharply and brittleness develops. During X-ray studies they observed only the appearance of superlattice lines for compositions containing 12.5 atomic pct Si. More recent X-ray diffraction studies- etected the appearance of superstructure lines (corresponding to the calculated positions of [Ill] and [ZOO] reflections) for alloys containing 9.5 atomic pct. This fact confirms Greiner and Stoughton's original hypothesis in regard to the onset of order at compositions containing about 7.5 to 9.5 atomic pct Si. The physical properties.of Fe-Si alloys containing more than 10 atomic pct Si have been studied only to a limited extent. Their extreme brittleness and difficulties of sample preparation render them of little industrial use in comparison with alloys in the 0 to 10 atomic pct Si range. The properties of Fe-Si alloys reported to date are mostly properties measured at room temperature on ordered compositions It appears that because of experimental difficulties fully disordered alloys could not be produced in the critical composition ranges and their properties could therefore not be reported. In Figs. la, lb, and lc, a summary of physical properties of Fe-Si alloys, measured during recent investigations of the influence of silicon additions to iron, is presented. No mention of determination of the critical temperature, T for disorder could be found in the literature. The following is an account of work done in an attempt to: 1) produce the disordered state of various Fe-Si alloys and establish the critical temperature, T for disordering, and 2) compare the electrical and thermal conductivity characteristics of the ordered and disordered phases as functions of composition. Materials, Preparation of Test Samples, and Testing Methods Fe-Si alloys with high silicon contents (about 10 atomic pct) are usually prepared using powder metallurgy techniques. This method insures accurate compositions and high purity through the use of protective atmospheres during solid state diffusion alloying of the mixed powders."" Iron and silicon powders were mixed in the desired proportions, cold or hot pressed, and then homogenized at 1150°C for periods ranging from 6 to 12 hr under a protective getter and in a hydrogen atmosphere. Fully homogenized samples were quenched in water from various and successively higher temperatures to establish the critical temperature for disorder. Temperatures were determined using Pt—Pt-Rh thermocouples in contact with the test samples. Test bars were approximately 0.6x1.25x7.5 cm. Electrical measurements were made at room temperature by determining the potential drop over a 1.5 cm span for a current of 10 amp. Densities of the samples were determined by immersion. High temperature electrical resistivities were measured using previously described techniques.'" Specific heat conductivity up to 200°C was measured by heating one end of the test bar and water-cooling the other; heat conductivity was then obtained by subtracting the rate at which heat entered the water from the

Jan 1, 1957

By V. Svalbonas

Presently the U.S. mining industry is very conscious of costs. It is timely, therefore, to review the dominant specifications used in the industry for procuring large size-reduction equipment. These are compared with other specifications and procurement methods, such as ASME and DOD, using the criteria of resulting costs, safety/ quality, and fitness-for-service.

Jan 1, 1987

By S. S. Huyett

The opportunity to cooperate with the Mining Department of the Pennsylvania State University in their Student-Trainee Program is accepted by The New Jersey Zinc Company who believes that the participation in this type of a program will lead to a larger supply of high calibre engineers in mining. Trainees compete with other employees to earn the cost of their education while gaining practical experience in the mining industry. The practical experience is arranged to complement the technical education through a variety of work assignments. Job opportunities for the trainee are related to the work requirements of the Company and to the performance of the trainee. Management must consider and deal with a good many problems uncommon with regular, full 'time employees. For a number of reasons this program is recommended to other companies as a means to encourage outstanding young men who are interested in a career in the mineral industry to obtain a professiona1 education.

Jan 1, 1963

By Basil B. Zavoico

During 1938 the Russian oil industry, while able to increase its production 4.69 per cent above the preceding year, was not successful in correcting some of its basic difficulties, and the industry's position as it entered 1939 was unsatisfactory. The internal political difficulties of 1937 and 1938 took a toll in the oil industry as they did elsewhere in the U. S. S. R., further complicating the solution of the problems facing it, most important of which still remain: lack of experienced and responsible leadership, able to make quick decisions; undisciplined and migratory labor; and insufficient and often unsatisfactory quality of the various equipment needed by the industry and its ineffective distribution. Recent developments in the U. S. S. R. suggest that during 1939 the management will be granted more latitude and hence somewhat better results may be anticipated from the executive branch, provided, however, the "purges" do not recur. The labor should be better disciplined and should not shift as easily, owing to the introduction, at the close of 1938, of individual labor passports to all workers in the country, the principal purpose of which is to correct those two deficiencies. It is not anticipated, however, that the service of supply will show any appreciable improvement in 1939, partly because of inherent difficulties and partly because the manufacturers of heavy machinery are working primarily and necessarily for munitions. Production Production of crude oil during 1938 is estimated at 224,714,000 bbl., as compared with 212,742,000 bbl. in 1937, an increase of 4.69 per cent but 12.76 per cent below the planned output. While there were no major readjustments in the source of supply of crude oil, both the older districts, Baku and Grozny, were barely able to maintain their 1937 levels of production, the increased output being supplied primarily by the fields of Maikop and Ural Permian Basin districts. While exploration work was outstandingly successful in 1937, in 1938 no discoveries of any

Jan 1, 1939

By Basil B. Zavoico

During 1938 the Russian oil industry, while able to increase its production 4.69 per cent above the preceding year, was not successful in correcting some of its basic difficulties, and the industry's position as it entered 1939 was unsatisfactory. The internal political difficulties of 1937 and 1938 took a toll in the oil industry as they did elsewhere in the U. S. S. R., further complicating the solution of the problems facing it, most important of which still remain: lack of experienced and responsible leadership, able to make quick decisions; undisciplined and migratory labor; and insufficient and often unsatisfactory quality of the various equipment needed by the industry and its ineffective distribution. Recent developments in the U. S. S. R. suggest that during 1939 the management will be granted more latitude and hence somewhat better results may be anticipated from the executive branch, provided, however, the "purges" do not recur. The labor should be better disciplined and should not shift as easily, owing to the introduction, at the close of 1938, of individual labor passports to all workers in the country, the principal purpose of which is to correct those two deficiencies. It is not anticipated, however, that the service of supply will show any appreciable improvement in 1939, partly because of inherent difficulties and partly because the manufacturers of heavy machinery are working primarily and necessarily for munitions. Production Production of crude oil during 1938 is estimated at 224,714,000 bbl., as compared with 212,742,000 bbl. in 1937, an increase of 4.69 per cent but 12.76 per cent below the planned output. While there were no major readjustments in the source of supply of crude oil, both the older districts, Baku and Grozny, were barely able to maintain their 1937 levels of production, the increased output being supplied primarily by the fields of Maikop and Ural Permian Basin districts. While exploration work was outstandingly successful in 1937, in 1938 no discoveries of any

Jan 1, 1939

The Porgera gold deposit in the Papua New Guinea highlands contains about 387 tonnes of gold. The results of its exploration show the benefits of persistence and commitment to this difficult deposit. The mineralization consists of a complex intermix of auriferous and argentiferous sulphides, gold tellurides and free gold as disseminations, veins, stockworks and breccia matrix. Its deposition was structurally contolled within a system of mafic diorite intrusions and adjacent sediments. Two styles of alteration accompany the mineralization. Gold grades vary erratically throughout the deposit. Over a period of 22 years nine phases of exploration have been undertaken by six companies or consortia of companies. Surface rock chip sampling, geological mapping followed by scout and systematic grid diamond drilling have been the most successful exploration tools. Exhaustive metallurgical process investigations and economic evaluations of mining options have been invaluable in guiding the exploration towards defining the ore body. Impetus was given to the project during times of flagging enthusiasm by several important discoveries and a breakthrough in the metallurgical processing approach. The discovery of high grade ore deep in Zone VII in 1984 turned this marginal deposit into a potentially very large gold mine.

Jan 1, 1987

By Arthur G. Strassburger

INTRODUCTION High in the Sierra Nevada Mountains of California, some 50 airline miles (80 km) northeast of Fresno, and near the John Muir Wilderness and Kings Canyon National Park, a large underground hydroelectric project is under construction. Pacific Gas & Electric (PG&E) Company's 1,125 MW Helms Pumped Storage Project exhibits a number of impressive statistics, unusual features, and other characteristics of interest to the tunneling or power plant designer and construction contractor. The most significant underground facilities include almost 20,000 ft (6,096 m) of 27-ft (8.2 m) diam concrete-lined pressure tunnel; 3,700 ft (1,128 m) of access tunnel; 1,600 ft (488 m) of steel-lined high-pressure conduit, 2 major underground chambers more than 1,000 ft (305 m) below ground; 3 deep vertical shafts, and one steep inclined shaft. Maximum static pressures within the conduits range from 200 ft (61 m) to 1,744 ft (532 m), with hydraulic transients that increase pressure to 2,500 ft (762 m). The purpose of these underground works is to provide 475,000 hp (354,350 KW) of water power to each of the 3 reversible pump-turbines, each connected to a 375 MW generator motor. The units, rated at 1,744 ft (532 m) maximum static head, are among the world's front-runners, considering the size-head combination. The Helms Project develops the existing power drop between two of PG&E's reservoirs, Courtright Lake and Lake Wishon. These reservoirs are retained by two concrete-faced rockfill dams completed in 1958, each storing approximately 125,000 acre ft (154 x 106 m3) of water. Although the project is intended to operate on a typical

Jan 1, 1981

By I. Cadoff, J. P. Nielsen

The Ti-C phase diagram exhibits a peritectic point at 1750°C and 0.8 pct C, and a peritectoid point at 920°C and 0.48 pct C. The maximum solubility of carbon in a titanium is 0.48 pct. The 6 region containing the Tic compound (20 pct C) extends to 11 pct C at the peritectic temperature. THE interest in the Ti-C alloy system stems from the fact that carbon occurs as an impurity in titanium alloys when graphite electrodes or graphite crucibles are used in their melting. Since titanium-base alloys are still in the development stage, some virtue may be found in carbon addition to titanium. The Tic compound is currently emerging as an important powder metallurgy base constituent similar to the WC compound. Ehrlich' identified the phases and structures present in the Ti-C system. The peritectoid region of the phase diagram was investigated by Jaffee et al." A preliminary diagram based on theoretical considerations was proposed at the outset of this research." The Tic compound has been investigated extensively and has been reported on in a large number of papers. Experimental Procedure Arc-melted alloys of 24 compositions in the range 0 to 20 wt pct C were investigated using metallography, X-ray diffraction, and, for the liquidus and solidus regions, incipient and complete melting. All alloys were prepared from iodide titanium (New Jersey Zinc Co., 99.95 pct Ti minimum) and spectroscopic grade carbon (National Carbon Co.). To prevent carbon spattering during arc melting the carbon was encapsulated in titanium. For alloys containing less than 1 pct C the powder was inserted into a capsule formed by drilling a hole in the as-received rod. For higher compositions, capsules were formed from titanium sheet. Arc Melting: The charges were melted in the copper-hearth cold electrode furnace shown in Fig. 1. This furnace is similar in principle to the all-metal unit adapted for titanium melting at Battelle Memorial Institute.' The transparent pyrex walls giving unlimited visibility during operation and the multiple-

Jan 1, 1954

By O. George Specht, Carl A. Zapffe

IN recent print, some remarkably contradictory statements have appeared regarding the importance to be attached to sponge iron,1-6 a metallurgical commodity whose history goes back at least to the time of Diodorus Siculus in the fourth century B.C. This disagreement, however, expresses the lack of a satisfactory method for producing sponge iron rather than defection in the commodity. The blast furnace is admitted to have certain inherent disadvantages, such as a general unsuitability for magnetite and the heating and blowing of vast quantities of undesirable nitrogen, so that a workable sponge-iron process remains attractive. In this respect, low-temperature gaseous reduction shows especial promise; but confusion persists regarding the factors involved. The present paper, therefore, has three principal divisions: (I) an exhaustive examination of all previous work on low-temperature gaseous reduction, (2) experimentation on the reduction of a magnetite with hydrogen, and (3) development of certain thermodynamic relationships in reduction, with a summarized depiction of the factors in the general process. PREVIOUS INVESTIGATIONS Gaseous media used in the reduction processes under discussion can be classified in three types: (I) H2, (2) CO, and (3) other gases. In the second, the CO is often admixed with H2. The third principally comprises hydrogeniferous gases, such as natural gas and producer gas, and in addition includes chlorine. Because hydrogen therefore features in all three, a study of hydrogen reduction based on investigations using pure hydrogen alone may be incomplete. The present paper reviews the three groups of investigations in the listed order, paying particular attention to hydrogen reduction. For the benefit of future workers, an exhaustive bibliography has been prepared and similarly classified. GROUP I: REDUCTION WITH HYDROGEN Equilibria Although the present problem is specifically one of kinetics, a first consideration is the equilibrium of the system, since the reactions to be studied comprise that equilibrium, and their direction and end points are defined by it. The historic development of these researches is interesting and informative.

Jan 1, 1946

By Henry M. Howe

The striking features of American Bessemer practice aré its large output and its low initial silicon and initial temperature. These are interdependent. Large outputs implies short blows and short intervals between blows. Short blows imply low silicon and fast blowing. Low silicon implies short intervals and fast blowing. Our blows are short because we have little silicon to remove, and because we remove it fast by supplying blast rapidly. We get enough heat even with little silicon, because our blows and the intervals between them are so short that relatively little heat escapes from our vessels. Were we to lengthen our intervals, or to blow more slowly, we would have to meet the increased loss of heat from our vessels, either by using more silicon, or by melting hotter, i.e., by burning more coke, in the blast-furnace or in the cupola. Finally, our short intervals imply powerful machinery, efficient organization, and extreme specialization and subdivision of labor, which can be profitable only when the output is large. Let, us now take these points up in more detail, first glancing at some examples of our large outputs, given in Table I., and of the composition of our iron. Output.—On presenting such results to some foreign metallurgists, I have been told, " Oh yes, we quite understand that. You really turn out no more steel than we do. As a matter of personal pride, your manager gets up a tremendous spurt for a day, or even a week, crowds on men wastefully, rushes through great quantities of metal, and then for months afterwards has to recuperate. The machinery has been strained ; the owner's money has been wasted ; the men have been prostrated—all to gratify the manager's vanity. Your average output is no larger than ours." Personal pride has, doubtless, played its part; without it we would still be savages, or apes, or mollusks, if you prefer. These baser motives are the mudsills of progress, the soiled roots of that growth of which civilization is the flower. Great outputs were made

Jan 1, 1891

By Jay R. Burns

TWO magnesium sand-casting alloys are commonly favored in the United States. These are referred to as H and C alloys (Dow Chemical Co.) or 4Mz65 and AM260 alloys (American Magnesium Corporation). Both are of an aluminum-zinc-manganese type. H alloy contains 6 per cent aluminum and 3 per cent zinc and is characterized by relatively good toughness. C alloy contains 9 per cent aluminum and 2 per cent zinc and is employed where high yield strength and pressure tightness are required. Examination of magnesium castings poured in Europe and England,'J however, demonstrates that H and C alloys are replaced by .%8 and AZ~I, respectively. That is, A8 reprcsents a magnesiurn alloy having superior toughness while A291 is suitable for high yield strength and pressure-tight applications. The basic difference between the .Ameri-can and European alloys is that the foreign alloys employ a somewhat higher aluminum content and less zinc than is found in H and C alloys. The mechanical properties of the alloys, when divided into high and low-aluminum groups, are quite similar, as determined from separately cast foundry-control type test bars ,In this paper the decrease of mechanical properties caused by any given amount of microporosity is measured for H, C, A8, and AZ~I alloys. The relative susceptibility of each of the four alloys to microporosity is also determined. Typical mechanical properties and nominal chemical analyses are reported in Table I. The apparent similarities between the two alloys in each group have led to considerable discussion as to the relative merits of each of the compositions.2 Popular points for comparison between the alloys have been the relative susceptibility of each of the four alloys to microporosity6 and the effect of this microporosity on their mechanical properties. It is primarily intended, in this paper, to show the

Jan 1, 1946

By Jay R. Burns

TWO magnesium sand-casting alloys are commonly favored in the United States. These are referred to as H and C alloys (Dow Chemical Co.) or 4Mz65 and AM260 alloys (American Magnesium Corporation). Both are of an aluminum-zinc-manganese type. H alloy contains 6 per cent aluminum and 3 per cent zinc and is characterized by relatively good toughness. C alloy contains 9 per cent aluminum and 2 per cent zinc and is employed where high yield strength and pressure tightness are required. Examination of magnesium castings poured in Europe and England,'J however, demonstrates that H and C alloys are replaced by .%8 and AZ~I, respectively. That is, A8 reprcsents a magnesiurn alloy having superior toughness while A291 is suitable for high yield strength and pressure-tight applications. The basic difference between the .Ameri-can and European alloys is that the foreign alloys employ a somewhat higher aluminum content and less zinc than is found in H and C alloys. The mechanical properties of the alloys, when divided into high and low-aluminum groups, are quite similar, as determined from separately cast foundry-control type test bars ,In this paper the decrease of mechanical properties caused by any given amount of microporosity is measured for H, C, A8, and AZ~I alloys. The relative susceptibility of each of the four alloys to microporosity is also determined. Typical mechanical properties and nominal chemical analyses are reported in Table I. The apparent similarities between the two alloys in each group have led to considerable discussion as to the relative merits of each of the compositions.2 Popular points for comparison between the alloys have been the relative susceptibility of each of the four alloys to microporosity6 and the effect of this microporosity on their mechanical properties. It is primarily intended, in this paper, to show the

Jan 1, 1946

By D. Loy LeRoy

As we are all aware, the impacts of the 1977 Surface Mining Act and the implementing OSM Regulations require application of new, as well as existing, equipment and technologies. Our firm recently completed (June, 1979) a study for the Department of Energy titled "Analysis of the Impact of Public Law 95-87 on Mining Performance." The objective of the study was to analyze the impact of the Act and its regulations on mining performance in order to provide recommendations to alleviate the impacts identified, including identification of research needs. This paper presents some of the highlights of that report: projected cost increases; additional equipment needed for compliance; review of methods currently practiced or those which can be modified; and will focus particulary on equipment and technology applications.

Jan 1, 1980

By C Simpson, J M. F Clout, G Plummer

Detrital iron deposits (‘DID’) in the Hamersley Province of Western Australia have been successfully mined and processed as small quantities of saleable standalone or blended lump and fine ore products over many decades. Despite their past, present, and potential future exploitation, they have received far less geological attention than the economically more significant higher grade bedded iron deposits (BID) or channel iron deposits (CID). DID are composed of Pliocene to Quaternary unconsolidated colluvial/alluvial hematite gravels with minor sand, silt, and ferruginous clay, as well as minor iron rich hematite clast conglomerates. DID mineralisation at Solomon has been subdivided into six distinct stratigraphic units, DID-5 (lowermost) to DID-0 (uppermost) based on differences in clast and matrix textures and mineralogy, degree of consolidation/lithification, particle size distribution and replacement textures. The most significant accumulations of DID-1 to DID-5 are in tributary valleys that have been cut through the Joffre Member of the Brockman Iron Formation on either side of the main Kings-Queens valley which contains the CID. DID-5 and DID-4 are ferruginous conglomerate, referred to as canga, with four subtypes recognised. DID-4 is composed of BID hematite clasts cemented by hematite or goethite. DID-5 is characterised by partial to complete replacement of BID hematite clasts and matrix by the yellow ochreous and brown to black vitreous forms of goethite. DID-3 to DID-0 are unconsolidated hematite detritals composed of largely (>80 weight per cent) fine to coarse gravel, minor sand and little silt or clay. The gravel clasts are largely composed of hematite and hydrohematite that replace BID, micro-nanoplaty hematite-martite-ochreous goethite (m-nplH-M-oG) BID, reworked canga, hematite pisoids, siliceous hematite BID (micro-nanoplaty hematite-martite-quartz, m-nplH-M-quartz), chert (~10–20 per cent) and minor (<5 per cent) Banded Iron Formation (BIF). Hematite abundance decreases from DID-3 to DID-0 whilst siliceous hematite BID is highest in abundance in DID-0 and lowest in DID-3. A key finding of the study is that >90 per cent of mineralised detrital clasts are derived from hypogene altered BID micro-nanoplaty hematite-martite with subsequent later supergene ochreous goethite mineralisation hosted by the Joffre Member. The DID genesis model entails interpreted Palaeoproterozoic siliceous hematite hypogene microplaty BID mineralisation of the Joffre Member undergoing Cenozoic supergene leaching of quartz and replacement by ochreous goethite to form low phosphorous BID micro-nanoplaty hematite-martite-ochreous goethite clasts. BID martitenanoplaty hematite-martite-ochreous goethite clasts and detritus eroded from hill slopes were deposited in the valleys as an initial single DID-5-DID-4 unit over a weathered pre-CID basal conglomerate. DID-5 and DID-4 underwent goethite cementation of the matrix followed by replacement by hydrohematite, hematite, and maghemite. DID-3 formed during subsequent periods of erosion of largely DID-4 hematite clasts and pisoids. Groundwater flow-through hematite canga resulted in partial to complete hydration replacement of DID-4 hematite clasts and matrix by ochreous and vitreous goethite to form DID-5. Deposition of DID-2 to DID-0 was via reworking and deposition of DID-5 to DID-4 canga and DID-3 as clasts and pisoids/ooids, as well as siliceous hematite and BIF sourced from the Joffre Member in the hill slopes.

Nov 8, 2021

By A. Wallace Mitchell

Barite deposits in Nevada occur as bedded and vein-types along a north-northeastern -trending zone which parallels the Antler orogenic belt The bedded deposits of Nevada are the most significant economically. They are presently supplying eighty-five percent of the domestic barite production which is used primarily as a weighting agent in the petroleum drilling industry. The ore bodies are controlled both structurally and stratigraphically, occurring along regional and local structural breaks in siliceous eugeosynclinal rocks of mid-Paleozoic age. Evidence for origin of the barite includes sedimentary and hydrothermal features indicating that localization probably took place along fractures in the seafloor.

Jan 1, 1980

By George F. Comstock

It has been reported recently1 that the hardenability and toughness of forging steels may be improved appreciably by the use of complex deoxidizers containing titanium, aluminum, and vanadium. In the light of these results, an investigation of similar deoxidizers containing various hardening and grain-refining elements was proposed. These deoxidizers included three manganese-silicon-aluminum-titanium al- loys with and without boron and calcium, three titanium-aluminum ferroalloys with vanadium, molybdenum and zirconium, respectively, an aluminum-zirconium ferroalloy, and plain ferroboron. Their approximate compositions are given in Table I, and the results obtained so far in the investigation of their effects on steel are presented in the later parts of this paper. Method of Using Deoxidizers The deoxidizers listed in Table I were used in three series of 0.40 per cent carbon steels, which were melted in a small basic-lined induction furnace and cast in the form of I7-lb. ingots about 2.75 in. square. The basic charge for each heat was 10 lb. Armco iron and 6 lb. of clean low-carbon sheet-steel scrap. When melted, this charge was deoxidized with 15 grams of ferrosilicon, then about 500 grams of pig iron was added to give the desired carbon content. After the pig iron was dissolved, nickel shot and high-carbon ferrochromium were added if required, and additions of 80 per cent high-carbon ferromanganese and 50 per cent ferrosilicon were made to provide the proper amounts of those elements. Aluminum was added to every heat 2 min. after the silicon, for grain-size control and preliminary deoxidation. One minute later the special deoxidizer was added to the clean bare surface of the molten steel, and 2 min. afterward the steel was poured into the ingot mold, using a hot-top and pipe-preventing compound after pouring to decrease the depth of the shrinkage cavity. The special deoxidizers were used mostly in the form of about ½ to¾-in. lumps,

Jan 1, 1942

By George F. Comstock

It has been reported recently1 that the hardenability and toughness of forging steels may be improved appreciably by the use of complex deoxidizers containing titanium, aluminum, and vanadium. In the light of these results, an investigation of similar deoxidizers containing various hardening and grain-refining elements was proposed. These deoxidizers included three manganese-silicon-aluminum-titanium al- loys with and without boron and calcium, three titanium-aluminum ferroalloys with vanadium, molybdenum and zirconium, respectively, an aluminum-zirconium ferroalloy, and plain ferroboron. Their approximate compositions are given in Table I, and the results obtained so far in the investigation of their effects on steel are presented in the later parts of this paper. Method of Using Deoxidizers The deoxidizers listed in Table I were used in three series of 0.40 per cent carbon steels, which were melted in a small basic-lined induction furnace and cast in the form of I7-lb. ingots about 2.75 in. square. The basic charge for each heat was 10 lb. Armco iron and 6 lb. of clean low-carbon sheet-steel scrap. When melted, this charge was deoxidized with 15 grams of ferrosilicon, then about 500 grams of pig iron was added to give the desired carbon content. After the pig iron was dissolved, nickel shot and high-carbon ferrochromium were added if required, and additions of 80 per cent high-carbon ferromanganese and 50 per cent ferrosilicon were made to provide the proper amounts of those elements. Aluminum was added to every heat 2 min. after the silicon, for grain-size control and preliminary deoxidation. One minute later the special deoxidizer was added to the clean bare surface of the molten steel, and 2 min. afterward the steel was poured into the ingot mold, using a hot-top and pipe-preventing compound after pouring to decrease the depth of the shrinkage cavity. The special deoxidizers were used mostly in the form of about ½ to¾-in. lumps,

Jan 1, 1942

By J. G. Peacey, G. Csicsovszki

The target of this study was to clarify the role of lead on the dissolution of gold in the (NH4)2S2O3-Cu leaching system via chronopotentiometry, linear sweep voltammetry and chronoamperometry. It was found that the dissolution of gold was significantly increased with lead concentration up to 10 mg/1 Pb in the system of 0.1 M (NH4)2S2O3 and 50 mg/1 Cu. \/oltammograms suggested that the anodic dissolution of gold was virtually independent of lead concentration in the range of 1-10 mg/1 in 0.1 M (NH4)2S2O3 solution while in solutions containing copper as well, addition of lead increased the anodic dissolution of gold.

Jan 1, 2011