By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y' formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y' was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y'."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y' appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y' phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y' plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By P. E. Doherty, B. Chalmers

Subboundaries may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits do not form in the vicinity of high- or low-angle boundaries. They are attributed to the condensation of vacancies from a super saturation produced during coolirzg. Using the vacancy pit and Schulz X-ray techniques for observing low-angle boundaries, a study was made of the transition from the nearly perfect seed to the striated structuke characterist-ic of aluminum crystals grown from the melt. It was found that the individual striation boundaries develop by the coalescence of very small-angle boundaries, as well as by the addition of individual dislocations. Several mechanisms for the formation of striations are discussed. Evidence was found suggesting that a super-saturation of vacancies exists near a growing interface, and it is proposed that the resulting climb of existing dislocalions produces "half'-loops" at the interface, which combine to form the low-angle striation boundaries. LINEAGE, or "striation" boundaries, have been studied in detail by Teghtsoonian and Chalmers 1,2 in crystals of tin grown from the melt, and by Atwater and Chalmers3 in lead. They found that single crystals grown from the melt consist of regions which are separated by subboundaries that lie roughly parallel to the growth direction. A difference in orientation of 0.5 to 3 deg exists between the striated regions; the misorientation is such that the lattice of one region could be brought into coincidence with the lattice of its neighbor by a rotation about an axis approximately parallel to the direction of growth of the crystal. They observed an incubation distance for the formation of striations which increased with decreasing growth rate. They also found that in any crystal, the sum of all rotations of the lattice in one sense, in going from one striation to the next, is very nearly equal to the sum of all the rotations in the opposite sense. A striation boundary, which is a low-angle grain boundary, can be described as an array of dislocations. If it is assumed that suitable dislocations are introduced into the crystal during solidification, the formation of striation boundaries can be explained as a result of the migration of the disloca- tions into arrays. The formation of arrays is energetically favorable since the energy of an assembly of dislocations can be reduced by the interaction of the stress fields when a suitable array is formed. This investigation presents and interprets new information concerning the nature and origin of striation boundaries in aluminum. EXPERIMENTAL TECHNIQUE Single crystals of high-purity aluminum (Alcoa 99.992 pct) were prepared by horizontal growth from the melt.'' The specimens were subsequently electropolished in a solution of 5 parts methanol to 1 part perchloric acid kept between -10° and 0°C in a bath of dry ice and alcohol. The current density was approximately 6 amps per sq in. Doherty and Davis9 have shown that in aluminum sub-boundaries with misorientations of not less than several seconds of arc may be revealed by the vacancy pit technique. During cooling from elevated temperatures pits form on electropolished surfaces of aluminum crystals as a result of the condensation of vacancies.11 Pits do not form in the vicinity of small- or large-angle grain boundaries, presumably because such boundaries act as sinks for vacancies. Boundaries of misorientations down to 3 sec of arc are revealed as pit-free regions, see Fig. 1. The Schulz X-ray technique12 was used to determine the angular misorientations of subboundaries. In this method, white radiation from a micro-focus X-ray tube is used to produce an image of a fairly large area of a single crystal surface. Subboundaries cause splitting in the diffracted image, see Fig. 2. Misorientations down to about 15 sec of arc may be observed with this technique. OBSERVATIONS AND DISCUSSION Figure 1 shows a striated aluminum crystal grown at 10 cm per hr etched by the vacancy pit technique. An incubation distance of about 1 cm is observed before the initiation of striation boundaries. Fig. 2 is a Schulz X-ray photograph of a striated crystal similar to that shown in Fig. 1. A large area of the crystal was studied by means of a series of photographs. Fig. 2, which is a reflection from the (100) plane, included about the first 4 cm of crystal to freeze. There is an incubation distance of about 1 cm, and a distance of about 2 cm over which the angle of misorientation builds up to its final value of approximately one degree. Some twist component can be seen in Fig. 2 at the right side of the photograph. From Fig. 2 it can be seen that the sum of all rotations of the lattice in one

Jan 1, 1962

By J. H. Holden

Operations involving the processing of coal, oxygen, and steam into synthesis gas by means of two pressure-type gasifiers have demonstrated the effect of heat loss and operating variables on carbon gasified and oxygen and coal requirements. Carbon gasified is the fraction of carbon in the coal that is converted to gas. Oxygen and coal requirement is the quantity of each that is needed to produce a unit volume (M std. c.f.) of carbon monoxide and hydrogen. Operating pressure of the gasifiers ranged from 150 to 300 p.s.i.g. and coal was fed at 200 to 500 lb./hr./cu.ft. of reaction-zone space. Oxygen-to-coal ratios were 8.5 to 10.5 std. c.f./lb. Heat loss and residence time have opposite effects on carbon gasified; increasing the heat loss decreases the carbon gasified, but increasing the residence time (by raising the operating pressure or reducing the coal-feed rate) increases the carbon gasified. The effects of these two factors are difficult to separate because they usually change simultaneously. A comparison of the results obtained from the operation of two gasifiers with different levels of heat loss, however, permitted the effect of heat loss to be separated from that of pressure and coal-feed rate. When the results were deter- mined on the basis of constant heat loss, increase of the residence time increased the carbon gasified until the reaction virtually had come to completion. For example, at 150 p.s.i.g., decreasing the coal-feed ratio from 500 lb./hr./cu.ft. to 200 lb./hr./cu.ft. substantially increased the carbon gasified. At 300 p.s.i.g., however, changing the coal-feed rate had little effect on the carbon gasified because the reaction had almost reached completion and further increase in residence time resulted only in a negligible change.

Jan 1, 1962

By J. G. Haymes

This report by the Bureau of Mines is the first of two proposed papers on evaluation of spectrophotometric, spectrographic, polarographic, and other analytical methods for quantitatively determining impurities in high-purity tungsten. Some of the methods described are standard methods that have been successfully applied to determine low-level impurities, several are modifications of known methods, and some procedures are entirely original. The Bureau of Mines is actively engaged in tungsten research because tungsten has an extremely high melting point, in fact the highest of any known metal. The metallurgist must know the content of impurities in tungsten because of the marked effects even micro amounts of impurity elements have on its physical properties. The Bureau procured a number of analyzed samples of above-average purity from research laboratories of companies engaged in production and fabrication of tungsten. These samples were investigated by the analytical procedures of those companies for several metallic impurities. Subsequent analytical laboratory determination of impurities in these samples agreed with the analyses as reported. With this assurance that analytical methods were basically accurate for metallic impurities, procedures for the determination of several of these elements were modified to lower the limits of detection and increase the sensitivity of methods. Carbon and the gases hydrogen, nitrogen, and oxygen were determined by standard instrumental methods, modified to provide greater sensitivity for reliable determinations when content of these elements was low. After the reliability of the modified procedures was affirmed, they were used as a product evaluation guide in the development of a vapor-plating technique for the production of high-purity tungsten. The following list of elements can be determined by one or more of these methods: AI, B, Be, Ca, Co, Cr, Cu, Fe, Mg, Mn, Mo, Ni, Pb, S1, Sn, Ti, V, and Zn. In addition, a vacuum-fusion method for the determination of H, N, and 0, and a conductometric method for carbon are described. Lower limits of determination and detection for each element listed are given.

Jan 1, 1962

By H. Warlimont

In recent investigations of the microstructure and crystallographic features of martensite by electgon microscopy,', '9 thin films (about 50 to l000A in thickness) have been used as specimens. It was found by W. Pitschl ,2 that the lattice relationships between the supefiaturated fcc matrix and the martensite formed in thin films were different from those observed after transformation in bulk material. Corresponding differences are to be expected in nucleation and in reaction kinetics in the formation of martensite in thin films, but have not yet been reported. In the course of the preparation of thin films of iron-base alloys for investigation by electron microscopy it was observed that films of alloys, whose martensite formation temperature (Ms) was below room temperature, formed martensite during the electrochemical thinning process conducted at or above room temperature. The chemical compositions and approximate bulkM,-temperatures of the three materials on which this observation was made are listed in Table I. The alloys were vacuum-melted from high-purity metals. It can be seen that the effect occurred in alloys that contain only sub-stitutional components as well as in alloys that contain carbon as an interstitial solute. The appearance of martensite formed in this manner is illustrated in Fig. 1, which represents a polished film of alloy No. 1 at XI0 magnification. The martensite plates can be recognized by their surface relief effects. In addition, heavily strained (owrinkledo) austenite can be seen near the edges of the film where it is thinnest and transformation stresses or strains can be accommodated by plastic deformation most easily. The nonuniform distribution of transformed regions is probably due to the varying thickness of the film. These observations were common to all materials listed in Table I. Because effects of supercooling or straining can

Jan 1, 1962

By R. W. Stahl

An emergency is defined as an unforeseen combination of circumstances that calls for immediate action. When applied to a coal mine, an emergency may call for prompt removal of the men to the surface through travelways other than the haulageway or intake airways, which are generally contaminated with irrespirable air as a result of an explosion or fire. Therefore, maintenance of adequate and travelable escapeways from all working areas of a mine is vitally important insurance against disaster. Several mine disasters could have been avoided if well-defined escape routes had been provided and made known to all mine employees. Such occurrences, unnecessary as they generally are, unfairly indict the industry when only a small segment thereof is involved. As a result of a rather recent disaster, which might not have happened if good escape routes had been provided, the Bureau of Mines decided to delve into the escape procedure to determine (1) what is being done in the industry and (2) what might be done at reasonable cost.

Jan 1, 1962

By George C. Carter

It was just a little over three years ago that the "Go" button was pushed to start operations on the blending piles at Oro Grande. As is usual with any new installation, there were problems that had to be solved. This paper will concern itself with those problems directly related to quality control. To obtain a consistent outgoing quality level at the most economical level for a finished product requires two main points: 1. Measurement of variations in the process, 2. A method of making a predictable change to adjust for variations. The manufacture of cement requires a relatively high degree of accuracy if a consistent outgoing quality level is to be maintained. The blending piles were our solution to this problem.

Jan 1, 1962

By J. J. Gilman

Rates of prisnzatic plastic glide ( {1010}<2110>) in pure Cd crystals have been measured at temperatures from 158° to 276°C. The glide rate is proportional to the 2.75 power of the applied shear-stress. The activation energy is 29.2 kcal per mol. It is suggested that the rates of prismatic glide in Cd and Zn crystals are determined by the strengths of the atomic bonds across the prism planes. ALTHOUGH zinc and cadmium crystals both have hexagonal structures with nearly the same c/o ratios, their mechanical behaviors are quite different. Whereas zinc becomes quite brittle below room temperature, and cleaves readily on (0001) planes, cadmium is very ductile even at 4.2°K, and cannot be cleaved at any temperature. As part of a search for the explanation of this difference in behavior, a study has been made of prismatic glide in cadmium. It complements a previous study of the same phenomenon in zinc.1 The primary glide plane in cadmium is the basal (0001) plane, and the primary glide direction is the direction of atomic close-packing <2110>. However, if a tensile stress is applied parallel to the basal plane, then the shear stress on the basal plane equals zero so basal glide cannot occur. At low temperatures, deformation by twinning occurs; but at high temperatures, it has been found in this study that gliding on prismatic planes (1010) occurs in the close-packed direction. This is completely analogous with the case of zinc, except that lower temperatures are required. EXPERIMENTAL The experiments were done in nearly the same way as for zinc.&apos; Therefore, only the differences in the two sets of experiments will be described here; for other details the reader is referred to the previous paper. Crystals 6 by 6 mm sq were used that were grown from "Super Purity" 99.999 + pct Cd purchased from the New Jersey Zinc Co. The crystals were grown with their basal planes parallel to both the rod axis and one of the flat sides of the square cross section, A close-packed direction in the basal plane was oriented parallel to the rod axis. Gage sections were carefully machined into the crystals, and the surface damage caused by machining was removed with the same chemical polishing reagent as had been used for zinc. Thus, specimens of the same form and size as the previous zinc ones were produced. The crystals were heated to the test temperatures in a silicone oil bath (fused salts were tried first, but they reacted badly with the cadmium). An Instron tensile-testing machine was used for applying stresses to the crystals at various constant strain-rates. RESULTS The general behavior of cadmium crystals is much the same as for zinc. Only the constants that measure specific properties are different. Just as

Jan 1, 1962

By A. Lawley, H. W. Schadler

TWINNING has long been recognized as a possible mode of deformation in crystalline solids and has been studied in a wide variety of crystals.&apos; Recently, deformation markings which have the topographical characteristics of twins have been seen in tungsten" and the body-centered cubic alloys of tungsten and molybdenum with rhenium.3-7 These markings have been identified as twins because: 1) they are visible after polishing and etching;2,3 2) their formation is accompanied by an audible click and a drop in load;4 and 3) the habit plane is {112}, the plane which has been identified as the twinning plane for several body-centered cubic metals.&apos; However, there has been no published evidence for the specific determination of the twinning direction in rhenium alloys of tungsten and molybdenum, because usually the deformation twins were not broad enough to be detected with a conventional X-ray beam. Consequently, [111] is inferred as the twinning direction since the latter must lie in a plane of symmetry perpendicular to the twinning plane (112). As Sims and Jaffee3 and Lawley and Maddin4 have shown, the addition of rhenium to molybdenum and tungsten increases the ductility of the alloy over that of the pure metal, but twinning is much more profuse in these alloys than in the pure elements, particularly at Mo-35 pct Re*and W-30 pct Re. Since twinning is often associated with brittle fracture in iron8 and the silicon-irons,9 direct experimental proof that the deformation markings in tungsten and molybdenum alloys of rhenium are twins seemed to be needed. Using the Laue back-reflection technique, the deformation markings in a Mo-35 pct Re alloy are shown to be deformation twins. The twins have a (112) habit plane and the twinning direction is <111>. The Mo-35 pct Re specimen used was taken from a 0.060-in. zone-refined single crystal deformed 6 pct in tension at 78°K. The Laue back-reflection technique, with a film to specimen distance of 2 cm, and white radiation from a copper target were used.

Jan 1, 1962

By J. G. Croeni

The titanium-iridium alloy system was investigated to determine whether alloys of this system would merit further development as control-rod material for nuclear reactors. A study was made to determine the titanium-iridium phase diagram by using melting-point, thermal analyses, X-ray diffraction, dilatometric, electrical resistivity, and metallographic techniques. The titanium-iridium alloy system was investigated between 500° and 2,400° C. Results indicate the formation of two intermetallic compounds, Ti3Ir rind TiIr3, and one intermediate solid solution centered about the 50 atomic percent iridium composition. A eutectic reaction occurs at 1,475° C, and 19 atomic percent iridium. The Ti3Ir decomposes peritectically at 1,520° C. The intermediate solid solution exhibits a maxima of 2,140° C. at 50 atomic percent iridium. This phase is also believed to undergo an order-disorder transformation at 1,750° C. Another eutectic reaction takes place at 2,000" C. and 60 atomic percent iridium. The compound TiIr3 formed at 75 atomic percent iridium decomposes peritectically at 2,115° C. Further increases in iridium content result in the formation of an iridium-rich terminal solid solution. Information obtained below 900° C. in titanium-rich alloys indicates that iridium acts as a beta stabilizer in titanium, and the authors believe that a eutectoid decomposition of beta-titanium occurs near 500° C. and 10 atomic percent iridium.

Jan 1, 1962

By G. V. Sullivan

This report summarizes the results of a preliminary study concerning manganese extraction from low-grade dolomitic materials from the Philipsburg district in Montana by the Dean-Leute ammonium carbamate process. Studies were made to determine the relationship between the variables involved in treating these materials by a roast-leach process and the amount of manganese extracted. The variables studied were the roast temperature, the roast particle size, the molar ratio of NH3 to CO2 in the leach solution, the liquid-solid ratio in leaching, the leach time, and the size of the particles being leached. The roast-leach studies were statistically designed, and the experimental results were evaluated by an analysis of variance.

Jan 1, 1962

By Leonard Klein

Reduction of oxygen-containing copper has always heretofore been brought about with wood poles. This paper reveals the first successful, economical, and Practical substitute for poles: a gaseous reductant, of which the production and plant use are detailed herein. THE art of fire refining of copper, consisting of melting, oxidation, slag removal, and finally reduction with wood poles, has been practiced for many centuries. An authentic record, discussed in detail in De Re Metallica,* mentions that as early as 1200 A.D. workers in this field of metallurgy were already acquainted with and practiced the basic principles of copper purification. Undoubtedly, the art was well developed marly centuries before the first written records began to appear. Notwithstanding the many advantages gained by application of mechanical con. trivances and by the tremendous increase in size of operations over the centuries, the reduction phase of the process has persisted essentially the same to the present time except for a very recent breakthrough. Numerous articles have been published and many patents have been issued on the subject of substitutes for wood poling in the past half century. They have dealt with a variety of gaseous, solid, and liquid reducing agents. But to the knowledge of the writer, no procedure has ever been prosecuted to a complete success on a large operating plant scale with the single exception of gaseous reduction of oxygen-containing copper revealed in detail herein. A natural gas-air reformer with ample capacity for

Jan 1, 1962

By Hsun Hu

Direct observations were made on the recrystalli-zntion of a cold-rolled (110) [001] crystal of 3 pct Si-Fe by annealing thin sections of the specimen inside the electron microscope during examination. Subgrain formation, presumably by polygonization, occurs rapidly, followed by a slow increase in the subgrain size before recrystallization can be detected. No migration of the subgrain boundaries was observed, and the formation of recrystallization nuclei by coalescence of subgrains is suggested. Re-c~ystallization characteristics of various texture components were individually examined. AS reported in a previous paper: orientations of the various deformation texture components in a 70 pct cold-rolled (110) [0011 crystal of 3 pct Si-Fe were completely confirmed by transmission electron diffraction patterns taken at various areas of the specimen. These orientations can be summarized as follows: Over most areas of the deformed crystal (111) planes are parallel to the surface. These areas correspond to either $- the two main defor: mation textures, the (111) [112] or the (111) [112].2-5 Within a few areas, (100) planes parallel to the surface are frequently found. These areas represent the minor deformation texture component, the (100) [Oll] type, which is derived from rotated Neumann bands.2&apos;4&apos;5 Only in very rare instances are (110) planes found parallel to the surface. This orientation corresponds to the very weak texture component of the (110) [001] type. In a pole figure, this (110) [0011 orientation is located within the orientation spread between the two main (111) [1121 type textures. Usually the electron diffraction patterns taken at various areas of the specimen are very simple ones, i.e., for any one area the pattern consists only of sharply defined spots of a single orientation. In some areas, however, more or less continuous rings of weaker intensities are superimposed on a simple pattern, indicating the presence of a wide range of additional orientations. In order to understand in detail the recrystallization of this cold-worked crystal, the recrywtallization characteristics of each of the various deformation texture components must be examined. This can best be done by using a high-temperature stage and transmission electron microscopy techniques, whereby small areas corresponding to the various texture components can be selected individually for examination. The present paper presents results obtained by this method. MATERIAL AND METHOD Specimens were prepared from a previously studied1 single crystal of a commercial grade 3 pct Si-Fe alloy with an initial orientation (110) [00l], cold-rolled 70 pct from 0.014 in. to 0.004 in. in thickness. Thin foils were prepared by electrolytic polishing as described in the earlier paper.&apos; Specimens of this thin foil were then mounted in a high temperature stage similar to the one designed by Whelan.6 A direct current was used as the heating source. The temperature of the heating grid was calibrated by means of a Pt vs Pt-10 pct Rh thermocouple in a vacuum chamber (0.01 to 0.02µHg). Maximum variation within the temperature range of 250o to 000°C was about ± 25°C. After the desired areas were selected for examination, the specimen was heated to a low temperature for some time while the selected area was constantly watched. When no further change in structure and orientation could be observed, a higher temperature was applied. Photomicrographs and diffraction patterns were taken from time to time during examination, with the heater temporarily turned off* while the photographs were

Jan 1, 1962

By Larsen. Edward P.

The principle of "bed blending" in the agglomeration of materials is about 56 years old, but de- spite all education via technical papers, operating reports and results from functioning installations, the concepts of blending are still somewhat vague. Confusion exists between "mixing", "blending," and the basic role of each. The terms "blending" and mixing" are often used interchangeably, yet they describe two different processes. As properly understood and applied, a blend is a combination of different varieties of material which produces a desired quality, or the mingling of different elements to form a harmonious whole. In other words, blending is a process of combining granular materials by mechanical means, wherein the final product, or a portion thereof, must contain an exact proportional amount of every one of the several different materials which contributed to the mass and wherein all particles are so thoroughly intermingled with each other as to have lost their individual identities and become a part of the whole so that when a portion of the blend is taken at any time it will be substantially identical, chemically and physically, to any other portion taken throughout.

Jan 1, 1962

By John D. Bardill

Data from extensive tests was obtained on friction-head losses of various sand slurries, composed of materials of different specific gravities and under varying transport conditions, to provide useful information for designing hydraulic transport systems. The tests were run in a pilot plant through 2-, 3-, and 4-inch lines with slurries composed of relatively pure barite and limestone solids. Available grinding and classification equipment did not permit attaining a comparable size distribution in the two materials tested, thus preventing direct correlation of friction-head loss values to physical properties or mineral composition. A total of 495 measurements were made of limestone slurries in the 2-, 3-, and 4-inch pipe test sections at flow velocities from 6 to 14 feet per second and pulp densities from 40 to 70 percent solids. A total of 640 measurements of barite slurries were made in the 3-and 4-inch pipe test sections at flow velocities between 7 and 14 f.p.s. and pulp densities ranging from 40 to 80 percent solids.

Jan 1, 1962

By S. Y. Ogawa

The effects of sulfur (up to 0.1 pet) on the deformation and fracture characteristics of iron, in cast form, were studied at strain rates up to 100 pct pcr sec and at temperatures of 1600o to -3300 oF. The effects of oxygen and manganese additions on the behavior of Fe-S alloys were studied under comparable test conditions. Brittle fracture characteristics, evident at all strain rates, resulted from the presence of the liquid iron sulfide phase at grain boundaries. Ductility could be restored in three ways: solution of the sulfide in solid y iron at higher temperatures, spheroid-zzation of the liquid sulfide, and increase. in the melting point ot the sulfide. THE literature shows that most previous studies of deformation and fracture at hot working temperatures have been based on measurements of energy absorption, reduction of height in forging upset tests, torsion tests of bar or wire samples, and so forth,&apos; but that relatively few tension tests have been used at high temperatures and strain rates. The present work was initiated to study the ef- fects of temperature, strain rate, composition, and structure on the deformation and fracture characteristics of iron, utilizing cast specimens tested in tension. As in a previous study,&apos; strain rates up to 100 pct per sec were chosen for the temperature range 1600° to 2400° to provide data which might be useful in the interpretation of the deformation and fracture behavior of steels under hot working conditions. The previous work was with Fe-P solid solution al10ys;2 this work is concerned with Fe-S alloys, and with the effects of oxygen and manganese additions. MATERIALS AND PROCEDURE Cast tes! specimens were employed throughout, since most of the difficulty during hot working occurs in the initial breakdown of the ingot. Alloy Systems. Ten 25 lb. heats containing sulphur were prepared. Of these, three had manganese additions, and two had oxygen additions. The sulfur content varied from 0.023 to 0.10 pct. Manganese contents were intended to be ten to twenty times the sulfur content of the particular alloy. Oxygen, being more difficult to control in small melts, was varied by the amount of solid deoxidizer added, but poor control of the oxygen content was experienced in most instances. Table I shows the chemical analyses of the heats. Melting and Casting. Electrolytic-iron chips were melted by high frequency induction in a prefired, clay-graphite crucible lined with rammed magnesite.

Jan 1, 1962

Jan 1, 1962

By V. F. Swanson

As part of the Bureau of Mines titanium resources examination program, samples of altered rock (saprolite) and unaltered rock from the Roseland anorthosite near Roseland, Nelson County, Va., were tested for amenability to beneficiation by flotation. A flotation technique was developed to produce bulk concentrates of ilmenite, rutile, sphene, and leucoxene. It was necessary to first float apatite using oleic acid as the collector, in an alkaline pulp with dextrine as a titanium mineral depressant. The titanium minerals could then be floated from the apatite tailing, using fluosilicic acid to depress the remaining apatite, morin to depress ferromagnesian minerals (when present), and oleic acid as the collector. A bulk titanium mineral concentrate, analyzing 66.0 percent Ti02 and 0.08 percent P205, was obtained from a sample of the unaltered rock which contained 5.45 percent TiO2 and 2.81 percent P205. Overall recovery in the concentrate was 47.1 percent of the total TiO2 in the ore. About 55 to 65 percent of the saprolite sample was clay and was removed by attrition scrubbing and decantation. The apatite prefloat procedure was applied to the saprolite sands; subsequent titanium mine: 1 flotation recovered 72.2 percent of the Ti02 in a bulk concentrate containing 65.1 percent TiO2 and 0.20 percent P205.

Jan 1, 1962

By I. C. Edwards, D. C. Smith

THE milling plant of Bicroft Uranium Mines Limited at Ban-croft, Ontario, was one of the first in Canada to employ ion excl1ange for the selecti1•e recovery of uranium from acid leach liquors. The ion ex-change circuit started operating early in November, 1956, and by June 1 I959, had handled more than two million tons of pregnant solution containing I,830,000 pounds of U3Os. Each column had been saturated and eluted about 430 times. The ion exchange columns are the conventional fixed bed type. Uranium is eluted from the resin with a sodium chloride-sulphuric acid solution and is precipitated continuous-ly with magnesia. After filtering and drying, the precipitate, or "yellow cake," is packaged in drums for shipment to the refinery.

Jan 1, 1962

By S. A. Ronlov

The importance of recognizing vibration problems during the plant design stage is emphasized in this paper. Often an experienced designer can recommend what type of support to use and how to tune the structure. However, obtaining sufficient information is a serious problem dealing with vibration. Vibration is a well known phenomena which, simply and generally, can be defined as a periodic motion. It is experienced in nature as caused by eerth- quake, wind, or ocean waves, and must be dealt with in the design of structure or ships. It must be realized that wherever there are moving or rotating elements, it is possible that unbalanced forces may induce vibration in the elements themselves, in adjacent parts, or in the supporting structure. Under certain circumstances, vibration will destroy machines or structures quickly and totally. The most widely known case is the total collapse of the Tacoma bridge when subjected to a wind of only 42 mph. Failures due to vibration of machines and/or their supports may occur in industrial plants where heavy equipment employed in the process must be supported and several machines are combined in close proximity. In the Metallurgical and Chemical Div. of The

Jan 1, 1962