This report describes aperiments by the Bureau of Mines and reviews theoretical aspects of the use of organophosphate solvent extraction for recovering beryllium from sulfate leach liquors. The leach liquors were prepared by sulfuric acid leaching of lime-sintered low-tenor beryl flotation concentrates. The experimental work on sulfate leach liquors showed that the acidic esters of organophosphates extracted beryllium slowly but in preference to aluminum. Three common alkylphosphoric acids, di- (2-ethylhexyl) (EHPA), heptadecyl (HDPA), and dodecyl (DDPA), in order of decrmsing selectivity, yielded a partial separation of beryllium from aluminum.

Jan 1, 1962

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962

By C. J. Bechtoldt, H. C. Vacher

Quenched alloys, prepared by powder metallurgical techniques, were examined by microscopic and X-ray diffraction methods. The compositions and heat treatments were chosen so that the chromium and nickel solvuses could be determined and a range of composition and temperature, in which a eutectoid had been reported, could be explored in small intervals. The results showed no evidence of eutectoid reactions having taken place. ALLOYS containing iron, chromium, molybdenum, and nickel are extensively used in high-temperature applications. In order to provide basic information on the solid-state reactions that occur in such alloys, the National Bureau of Standards is engaged in an extensive study of the equilibrium phases in the binary, ternary, and quaternary systems involving these four metals. Attention was directed to the chromium-nickel system because a review of the literature showed conflicting data. A recent compendium1 of the constitution of binary alloys gives two diagrams for the chromium-nickel system, one a simple eutectic and the second a diagram showing a eutectoid and a eutectic. The eutectoid was the result of an allotropic transformation in a high-temperature solid-solution form of a chromium-rich phase called 0. The approximate temperature and composition of the eutectoid was 1200°C and 30 at. pct Ni. In the preliminary study, at the Bureau, no transformation was indicated in the chromium-rich phase of ternary and quaternary alloys in which chromium and nickel were major components. Similar results have been reported from time to time in the literature,2-8 In consequence of this situation, a systematic study was made of the constitution of heat-treated chromium-nickel alloys using metallographic and X-ray diffraction methods. The compositions of the alloys were selected so as to determine the boundaries of the chromium-rich and the nickel-rich phases and to explore in small intervals the ranges in composition and temperature in which the eutectoid had been reported. The results of this study are reported and discussed in the present paper. EXPERIMENTAL PROCEDURES Materials, Alloys, and Heat Treatments—The alloys were prepared by a powder metallurgy technique similar to that used in earlier work.9 Analyses of the materials used are given in Table I. Powders were mixed using a vibrator in 30-g batches of predetermined composition; 2-g pellets were made from the mixture by compacting at room temperature in a 1/2-in. diam mold under 60,000 lb per sq in. pressure. The pellets were sintered in dry hydrogen for 10 days at 1300°C. At the end of the sintering treatment the specimens were quenched in water, which caused a pale green film to form on the chromium-rich alloys and thin black scale to form on the nickel-rich alloys. The pellets after sintering were approximately 1/2 in. diam by 3/32 in. thick. The purification train9 was modified by inserting a tube of titanium turnings, heated at 700°C to increase the efficiency of the removal of oxgen and nitrogen. It was found in the earlier work that the sintering treatment lowered the carbon, oxygen, and nitrogen contents of chromium-rich alloys to 0.01, 0.01, and 0.004 wt pct, respectively, and that there was a loss of chromium. In order to ascertain the extent of this loss, the chromium contents of certain alloys were determined chemically. They included those alloys used to determine the parameter-composition curves and those of critical composition, used to determine the chromium-solvus microscopically; these analyses were made on samples after the final heat treatments. The mixed powder values for the chromium content of those alloys that were not analyzed were adjusted to conform to a smooth curve based on the chemically analyzed values for

Jan 1, 1962

By Shiou-Chuan Sun

This paper is to be presented at the Annual Meeting of the American Institute of Mining, Metallurgical and Petroleum Engineers, New York, New York, February 18-22, 1962. Permission is hereby given to publish with appropriate acknowledgments, excerpts or summaries not to exceed one-fourth of the entire text of the paper. Permission to print in more extended form subsequent to publication by the Institute must be obtained from the Secretary of the Institute. If and when this paper is published by the Institute, it may embody certain changes made by agreement between the Technical Publications Committee and the author, so that the form in which it appears here is not necessarily that in which it may be published later.

Jan 1, 1962

By M. J. Ginsberg, N. A. Gokcen

THE preliminary study of electrochemical desul-furization performed by Ohtani and Gokcen1 left a number of points concerning the process to be investigated. Two of these were i) the determination of the effect of greater current and voltage on the desulfurizing Flower of acid slags (% CaO/% SiO2- 1) and ii) the possibility of the loss of silica in slag by the reactions 2C (in metal) + SiO2 (slag) = Si (in metal) + 2CO(g) and C + SiO2 (in slag) = SiO(g) + cO(g) proceeding to a point at which the composition of the slag was sufficiently altered toward the basic side so a1.s to noticeably affect the rate of de-sulfurization. The apparatus and the procedure used in the present investigation were the same as those used by Ohtani and Gokcen, except the control circuit was connected to 120 v dc instead of 24 v dc and thereby allowed greater freedom in choosing the values of both current and voltage. The graphite crucible containing the melt and serving as the cathode was 3-in. high, and was of 1 1/2-in. ID with a graphite bar of 3/8-in. diam and 8-in. length threaded into the bottom for electrical connection. This was placed into a magnesja outer crucible with a hole in the bottom and alumina insulation was packed between the two crucibles. A charge consisting of 180 g of

Jan 1, 1962

By J. R. Ross

A reconnaissance for sources of scandium and a metallurgical investigation of recovery methods for byproduct scandium from uranium mill solutions were conducted by the Bureau of Mines. The work on scandium was undertaken to obtain information on domestic resources and to explore and develop recovery procedures in consonance with the Bureau&apos;s long-range program for conservation and wise utilization of mineral resources. The element scandium is widely distributed in the earth&apos;s crust in trace amounts, but it seldom occurs as an important constituent in any mineral. An exception is thortveitite, (Sc,Y)2 Si207) a rare mineral that contains various amounts of scandium and yttrium and may contain up to 42 percent scandium oxide (SC203). Knowledge of the chemistry of scandium has expanded rapidly in recent years (1, 4, 9)4 but only fragmentary information is available about the metal because it is still largely a laboratory curiosity without established uses (2, 3). A recent study shows some of the physical proper-ties of the metal are (1) density of 3.05 grams per cubic centimeter) (2) melting point of 1,540° C, (3) hexagonal close-packed structure) (4) hardness of about 50 Brinell (500-kilogram load), and (5) an alloy behavior similar to yttrium and rare-earth metals (2). The price of $2,850 a pound for scandium oxide of 99.9 percent purity and $2,700 a pound for oxide of 99 percent purity reflects the scarcity and complex chemistry of the element.

Jan 1, 1962

By M. A. Klugman

[This paper represents a portion of a lager study, concerning dispersion patterns of major, minor and trace elements in wall-rock about ore-bodies in part of the Colorado Mineral Belt. This phase of the work pertains to the Mg/Ca ratio variations in wall-rock adjacent to ore-bodies in two mines of the Alma-Horseshoe Mining District of Central Colorado. The mining district is located 80 miles southwest of Denver (Figure 1) on the east flank of the Mosquito Range. The area is typified by rugged relief with altitudes from 10,500 to 14,000 feet.]

Jan 1, 1962

By H. P. Stüwe

HE recent papers of Aust and Rutter112 have again brought to mind the importance of certain "special" orientation relationships between the lattices of two fcc crystals on the mobility of the grain boundary separating them. No theoretical treatment of this problem has been offered till now. The only principle published so far that has given an indication why certain orientation relationships should be "special" is the counting of "coincidence sites" according to the suggestions by Kronberg and Wilson.3 The "coincidence plots" published by these authors show, for instance, that two fcc lattices rotated by 38 deg around a common (111)-axis have 1/7 of their lattice sites in common. Such an orientation relationship is also characteristic for high boundary mobility. The accuracy of the orientation relationship needed for high mobility is not too rigid. Deviations up to 10 deg from the ideal orientation seem to be tolerable as can be gathered from the experimental data.&apos;j4 The auestion arises, then. how the density of coincidence sites will be affected by a deviatioi from mathematical accuracy. This can be checked by a simple model. Two sieves are prepared, the arrangement of the holes corresponding to lattice sites on a (111)-plane in a fcc crystal. They are placed upon each other, Fig. 1. One is kept fixed, the other is rotated around an axis pushed through one hole in common to both. The light falling through holes of both sieves is then a measure for the density of coincidence sites. If the diameter of the holes is very small, light intensity is contributed only by holes the centers of which coincide "exactly." If the diameter of the holes is rather large, some intensity will be contributed by

Jan 1, 1962

By Harry A. Schrecengost

The Bureau of Mines has found considerable lack of uniformity in style and content of record books used for reporting the results of examinations made by coal-mine officials. These books range from elaborate forms designed for specific examining and operating procedures at certain large mines to simple composition books, tablets, and pocket-style notebooks at other mines. Examination of thousands of these record books discloses that the reports of many examinations are so brief and so poorly worded that they cannot be understood readily. The contents, in some instances, appear to be deliberately ambiguous. The value of keeping accurate accounts of safety inspections in coal mines is often underestimated. Well-kept records reflect managerial attitude and indicate well-governed operations as well as training of official personnel to conform to considered policy and regulations and if necessary, may serve as documentary evidence to protect the mine officials and the operators.

Jan 1, 1962

By Michael Hoch, Walter C. Wyder

The isothermul section of the Nb-Ti-Zr-O system at 1500°C was investigated using X-ray dzffraction and metallographic techniques. UP to 66.7 at. pct 0, the system contains nine four-phase regions. Tsopleths at 10, 20, 30, 40, 50, and 55 at. pct 0 weye constructed. The purpose of this investigation was to determine the general shape of the quaternary equilibrium phase diagram of niobium, titanium, zirconium, and oxygen at 1500°C. The system was truncated at 66.7 at. pct. O., PREVIOUS INVESTIGATIONS The Ti-Zr-O system was investigated in this laboratory.&apos; The binary systems of interest have been compiled and discussed by anssen2 and Levin, McMurdie, and Ha11. Elliott4 has determined the Nb-O system by metallographic and X-ray diffraction techniques. He shows the existence of three oxides, namely NbO, NbO2, and Nb2O5. At 1500°C the solubility of oxygen in niobium is about 4 at. pct. No solid solubility region is shown for either NbO or NbO2. EQUIPMENT The same equipment as that for the study of the Ti-Zr-O system was used. The X-ray diffraction patterns were analyzed with the help of the ASTM card set5 and NBS circulars.6 MATERIALS The niobium powder (99 pct pure), the titanium powder (99.6 pct pure), the niobium pentoxide, and the zirconium dioxide used in this study were purchased from the Fairmount Chemical Co., Newark, N.J. The zirconium powder (99.4 pct pure) was obtained from the Charles Hardy Co., Inc., N.Y. Reagent-grade titanium dioxide was purchased from the Matheson Co., Inc., Norwood, Ohio. The oxides were dried in air at 700°C for 24 hr before use. Though the materials used were not "hyper-pure," the impurities present do not affect the results (lattice parameters, phase boundaries), within the experimental accuracy. PROCEDURE Samples of the desired compositions were made up, in mole pct, from the materials listed above. In some cases the intermediate binary compounds, such as NbO and TiZrO4 were prepared beforehand and used in the preparation of the samples. This technique enabled equilibrium to be reached from two sides. The components of each sample were mechanically mixed in a mortar and pestle and pressed into 3/16-in. diam pellets. The pressures used in compacting were of the order of 50 to 100 x 103 psi. Sintering was accomplished by heating the samples in a tungsten crucible (3/4-in. high, %-in. diam, 1/8-in. wall, lid with XB-in. hole). The pellets were separated from each other and from the crucible by means of small spiral coils of tungsten wire placed between the stacked pellets and on the bottom of the crucible. The sintering time was from 4 to 12 hr at 1500°C under a vacuum of 6 x 101-5 to 1 x 10-6 mm of Hg. All samples were reground after the first or second heating repressed, and reheated. In most cases: equilibrium was obtained after the first heating, as the X-ray diffraction pictures after each heating remained unchanged. Quenching of the samples from 1500°C was at first only possible by allowing the crucible and its contents to lose heat by radiation. The temperature dropped from 1500° to 900°c in approximately 1 1/2 min, which was considered adequate when compared to the times used by other investigators to reach equilibrium in the temperature range of 1000°c and lower. Later, a new technique for faster quenching of the samples was cleveloped. This technique involved the removal of the samples from the crucible, whereupon they were quenched by coming in contact with the water-cooled copper base of the furnace. This manipulation was performed without breaking the vacuum. The sample pellets were placed on a tungsten wire rack inside the crucible. The wire rack passed through the hole in the crucible lid, where it was connected to a small nonmagnetic chain. The chain was fed to the side of the furnace by means of a brass rack which fitted between the body and lid of the furnace. Suspended at the end of the chain, near the furnace wall, were three magnetic washers. With the use of a strong

Jan 1, 1962

By V. E. Edlund

Pyrometallurgical studies by the Bureau of Mines demonstrated the feasibllity of sintering and smelting a low-grade flotation concentrate made by pilot-plant processing 10-percent manganese ore from the Maggie Canyon deposit, Mohave County, Ariz. Under optimum conditions 85 percent of the manganese in a flotation concentrate that assayed 36 percent manganese was recovered as standard ferromanganese. A blend of this flotation concentrate with high-grade dithionate pilot plant precipitate was similarly processed with a recovery of 90 percent of the manganese. Thorough mixing and pelletizing of the charge before treatment on the sinter hearth was necessary to produce a well agglomerated product by single pass sintering. Although satisfactory sinter was produced from a variety of material combinations, best results were obtained on a charge that contained 80 percent flotation concentrate and 20 percent return sinter fines. This combination was mixed with 6 percent coke, based on weight of concentrate; and 12 percent moisture. Sintering such a charge yielded a well agglomerated product containing over 80 percent coarse material, The results of standard crushing tests showed that the product was physically comparable to iron ore sinters and manganese nodules.

Jan 1, 1962

By C. M. Marquardt

The materials handling systems in the large concentrating plants have required the employment of a considerable number of workmen, many of whom had very little to do except to act as watchmen to avoid bad spills at belt junctions and to operate tripper cars, shuttle belts, etc. Much time also was spent in watching bins to make sure they were properly filled. Approximately four and one-half years ago the author, Yin coopera¬tion with the engineering and supervisory personnel of The Anaconda Company at Anaconda, Montana, began to give this problem serious consideration. Prior to this the author had developed, at the request of The Anaconda Company, a transistorized resistance-sensitive probe relay system for detecting the level of ore in bins. With this system cables or chains were suspended from insulators above the bins and were of suitable length to determine the elevation of the ore in the bins.

Jan 1, 1962

By Robert W. Burns

Gentlemen, my subject today is glass reinforced plastics. By definition, this encompasses a wide variety of materials: at least a half dozen basic varieties of polyester, epoxy, and phenolic; virtually infinite compounding variations within the basic groups: literally limitless variations in the amount and the nature of the glass reinforcing. Complicating all of this is the fact that different modes of application of the same material fall appreciably alter&apos; the product&apos;s general strength and suitability. These many, many differing materials are what we conveniently call "glass reinforced plastics" or, more simply, fiberglass". This common name is actually a large part of the problem when dealing with fiberglass materials. Far too often a specification is written calling for simply "fiberglass reinforced polyester&apos;, based on successful prior use of a polyester laminate. Such a specification is very nearly worthless since such tremendous variation is possible under it. Success of a laminate furnished under such a specification is entirely dependent on good fortune

Jan 1, 1962

By J. E. Hilliard, J. W. Cahn

calculation has been made of the standard deviations to be expected in the measurement of volume fractions by areal analysis, lineal analysis and four point-counting Procedures. The effect of experimetztal errors is not included. Our conclusion is that a point count using a two-dimensional grid will be the most efficient method of volume fraction analvsis providing the grid spacing IS coarse enough. The predicted standard deviation for such an analysis is shown to he in good agreement with that determined experimentally. A metallurgist wishing to estimate a structural property by means of quantitative metallography is often faced with a choice between several different procedures. In such a case, he will naturally wish to know: a) Which procedure is the most efficient in the sense of requiring the least effort for a given precision? b) For a given procedure, what are the conditions for maximum efficiency? c) Under these conditions, how many measurements are required to attain a given precision? It is our aim in this paper to provide at least partial answers to these queries as they relate to the estimation of volume fractions from measurements on a random two-dimensional section of an opaque specimen. The commonly used techniques1,2 for volume-fraction analyses are based on one or more of the following principles: i) For an areal or Delesse3 analysis: That the areal fraction of a three-dimensional feature intercepted by a random plane provides an unbiased estimate of the volume fraction of that feature. ii) For a lineal or Rosiwal4 analysis: That the fractional intercept on a line passing at random through a two-or three-dimensional feature provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. iii) For a point-count analysis: That the fractional number of randomly or regularly dispersed points falling within the boundaries of a two-dimensional feature on a plane, or within the boundaries of a three-dimensional feature in a volume, provides an unbiased estimate of, respectively, the areal or volume fraction of that feature. The absence of bias referred to in these principles does not, of course, imply that the results of an analysis will be free of error, but only that the expected result is equal to the true one. Application of the foregoing principles provide the following six possible experimental procedures: a) An Areal Analysis—This involves the measurement with a planimeter (or other means) of the area of a constitutent intercepted by the plane of polish b) A Two-Dimensional Random Point Count—Apos-sible experimental procedure for this analysis is to superimpose a sheet of transparent graph paper on a micrograph, and then use a table of random numbers to select coordinates for the points. c) A Two-Dimensiotuzl Systematic Point Count-Similar to b) except that the points are distributed in a prescribed manner, usually at the corners of a lattice superimposed on a micrograph or the screen of a projection microscope. d)A Lineal Analysis—A measurement of the fractional line length intercepted. It is usually performed by traversing the specimen under the cross hairs of a microscope and recording the distance travelled in each constituent. e) 4 One-Dimensional Random-Point Count— This could be performed by traversing the specimen with stops at random intervals to identify the constituent then present under the cross hairs. f) A One-Dimensionul Systematic Point Count— Similar to e) except that the traverse is stopped at prescribed (usually equal) intervals. It will be noted that the point-counting procedures b) and c) can be regarded as methods of estimating the areal fraction. Similarly, e) and f) are indirect methods of making a lineal analysis. All of the six procedures described above involve at least one stage of sampling. Thus, quite apart from any experimental errors, there will always be a statistical uncertainty associated with the final results. It is with the calculation of this uncertainty that we will be concerned. To avoid unnecessary repetition, the statistical relationships that will be used in the calculations are collected together in the appendix. For a fuller discussion reference should be made to one of the many textbooks5,6 on statistics. For symbols relating to the specimen structure we will follow as far as possible the terminology used by Smith and Guttman.7

Jan 1, 1962

By William Rachunis

This publication describes the construction of 43.64 miles of underground tunnel to be used as an aqueduct, known as the West Delaware aqueduct. In the past, the accident history of tunnel operations has not been favorable, the "rule of thumb" being a death for each mile of progress, according to the meager accident statistics available for the tunnel-driving industry. The accident experience at this project and the use of modern equipment established safety and progress records that were accepted by tunnel people as a record at the time. The city of New York comprises 5 boroughs, with a total population of approximately 8 million people, and uses about 1,210 million gallons of water each day. The water supply for the city is the responsibility of the New York City Board of Water Supply. This organization has constructed an extensive aqueduct system, the Delaware aqueduct, to convey water to the city from the distant mountain and river sources in the Catskill Mountains in the Southern Tier areas of New York State (figs. 1 and 2).

Jan 1, 1962

By C. Feng, P. Levesque

HE addition of rhenium to molybdenum is known to produce alloys with good workability.&apos; Lawley and Maddin found that the critical stress for twinning in this system was lowered by the addition of 35 pct Re, which suggests that twinning may re- place the usual slip operation as the major element of deformation. The twinning elements in bcc Mo-Re alloys have been reported as the (112) planes and the <111> directions.3 This note represents the continuation of this investigation, in which the authors found that the occurrence of twinning promotes the formation of a bcc tetragonal phase, previously identified as u by Greenfield and Beck.4 Specimens of Mo-35 pct Re alloy, prepared as described previusly, were solution annealed at 2400o, cooled to room temperature, and plastically deformed by compression to induce twinning. After subsequent aging for 8 hr at 1300°C, traces of a were observed along the grain boundaries and at the interfaces between the twins and the matrix, Fig. 1. With increased aging time the cr phase grew into larger clusters and finally occupied the entire twinned area, Fig. 2. Experiments also indicated that if twinning did not precede aging, there was no visible evidence of a in the microstructure.

Jan 1, 1962

By R. J. Grace

Primarily, this report presents the results of direct efficiency tests which were conducted on the 200-hp Coal-Pak, hot water generator, No. 3 unit, at the Otterbein College heating plant in Westerville, Ohio. Also included is a comparison of fuel consumption of the old plant with that of the new plant, a comparison of efficiencies obtained by the indirect method on a 300-hp Coal-Pak, and the cost of gas vs coal to show the savings effected by the latter. Tests were conducted with ten different bituminous coals selected by Mr. S. A. Frye, business manager at Otterbein College. The coals, of ten different suppliers, from four different states and eight different seams, represented competitive products economically available to the heating plant. The tests were conducted by the usual plant personnel which consisted of the plant superintendent and two assistants. No outside supervision of any kind was given during the tests. The tests were made from Dec. 13, 1960, through Mar. 4, 1961. During this period, 300.03 tons of coal were burned in the No. 3 unit. This tonnage represented 25.5 pct of the total coal requirements for the 1960-61 season. Operation during the period was typical for the comfort heat load which the plant supplies. Of the 78.12 operating days, the boiler was on bank or holdfire 14.31 days, or 18.32 pct of the time. The length of individual bank periods varied from 2 hr to three days. Run periods varied from about 2 hr to 7.26 days. DESCRIPTION OF PLANT AND HEATING EQUIPMENT The new Otterbein College heating plant, completed in the summer of 1957, is located in a 50x50 ft boiler room on the lower level of a combination maintenance building and heating plant. The building is situated away from the main college complex on a hillside, which allows for on-grade delivery of coal to the three bunkers. The bunkers are located directly above and connected with the individual stoker hoppers. Fig. 1 shows an in-plant view of the Coal-Pak installations. The No. 3, hot water, unit is at the extreme right. The heating plant consists of three 200-hp Coal-Paks. Unit No. 1 is operated at 4 psi and carries the steam heating load of 14,000 sq ft EDR (steam) installed in two buildings. Provision has been made to convert these buildings to hot water heating at some future date. Since the unit under maximum load conditions operates only at about 50 pct steaming capacity, a heat exchanger was installed to convert steam to hot water. Thus, during light loads in mild weather the unit can be employed more efficiently to supply both steam and hot water and eliminate the need for operating either of the two hot water units. Units No. 2 and No. 3 serve a hot water heating circuit for a large group of 21 buildings of the College. These boilers deliver hot water at temperatures up to 200°F to the various buildings through distribution lines in tunnels. The present calculated maximum heat loss for the College is 15.195 million Btu per hr. The Coal-Paks have individual design capacities of 6.700 million Btu per hr. Table I lists the design date for the Coal-Paks. The No. 3 unit was chosen as the test unit, primarily because of its bunker location at the far end of the delivery ramp. Because of this location any excess coal above bunker capacity could be conveniently stored and isolated from the adjoining bunkers. Each bunker has a capacity of 30 to 35 tons of coal. The No. 2 and No. 3 hot water generators are equipped with automatic controls which maintain the

Jan 1, 1962

By H. L. Noblitt, Pauline Moyd, Louis Moyd

The deposit, which forms a ridge -adjacent to the York river, in Mont-eagle township, is held by Monteagle Minerals Limited, of Toronto. The ore is in a Precambrian gneiss which is composed of nepheline, scapolite, andesine and microcline feldspars, muscovite and biotite micas, and -corundum. The major orebody is tabular and is exposed for 1,200 feet along the crest of the ridge. It aver-ages about 90 feet in thickness, dips at about 70°, and was intersected by drilling at a vertical depth of 600 feet. The deposit was prospected for corundum in the early 1900's. Recent exploration was undertaken to deter-mine its potential as a source of high-alumina ceramic material, with by-product corundum and white mica. The program included prospecting, mapping, trenching, diamond drilling, bulk sampling, beneficiation research, a large-scale beneficiation test, product evaluation, market investigations, and plant design. Reserves, to a depth of about 300 feet, are estimated at about 3 million tons.

Jan 1, 1962

By Kevin Malone

Chrysotile asbestos occurs in many counties in California, and a small production had been reported at times, but development of deposits had been disappointing. A reconnaissance survey by the Bureau of Mines indicated that several deposits in the serpentine belt in Shasta, Trinity, and Siskiyou Counties might contain enough asbestos of filler grade to supply the growing demand on the west coast. Accordingly from 1956 to 1958 parts of the Mount Eddy and Shasta View deposits were investigated by trenching and diamond drilling to determine their potential. The work comprised construction of roads, bulldozer trenching, excavation of areas for diamond drilling, sampling, and upping. The trenches were excavated to expose the surface extent of some of the asbestos-bearing areas, To determine the downward continuation of asbestos-bearing sections and to secure samples for test purposes, six diamond drill holes, totaling 1,738 linear feet, were drilled in two selected areas. The trenching and core-drilling indicated that the asbestos-bearing material occurs as ribs and lenses of varying thicknesses in a broad belt of serpentine, about 600 feet wide and several miles long,

Jan 1, 1962

By D. E. Swets, R. C. Frank

It is well known that hydrogen is introduced into iron or steel as a result of many chemical processes (acid pickling, electrolytic cleaning, plating, etc.). One of the reactions that has been of recent interest1 is the reaction between an iron surface and water vapor. It was shown a few years ago2-4 that hydrogen can be introduced into steel at an accelerated rate during abrasion as a result of this reaction. Grun-berg and Scott have also observed that water in mineral oil lubricants increases pitting failure in ball bearings5 and they have suggested that hydrogen from the water is the primary cause of this effect.&apos; In this laboratory, the question was raised as to whether or not hydrogen is also introduced into the metal surface of a bearing as a result of the decomposition of the hydrocarbon lubricant itself, and an experiment was performed to try to find a satisfactory answer. All steel parts contain some residual hydrogen. Therefore, it appeared that the best way to carry out this experiment without the need for highly accurate quantitative analyses was to use deuterium as a tracer. The natural abundance of deuterium in H2 is only 0.015 pct. The tracer was obtained in the form of deuteroparaffin (CD,(CDJ, CD,) and 0.25 g were dissolved in 20 cc of mineral oil to form the lubricant to be used in the tests. The bearings used were New Departure Type QOLOO ball bearings with a ball diam of 0.187 in. Prior to adding the mineral oil-deuteroparaffin lubricant, the bearings were cleaned in warm trichloroethylene to remove the packing grease. After packing with the new deuterated lubricant, the bearings were operated in a bearing fatigue test machine under a radial load of 190 lb and a thrust load of 190 lb at a speed of 3800 rpm. The expected life under these conditions is about 500 hr. Two tests were made; one for a period of 27 hr and the other for a period of 102 hr. The bearings achieved a temperature of 120o F during the tests. When the tests were stopped the balls were mechanically removed from the bearings and were immediately placed in liquid nitrogen to reduce degassing until the analysis for deuterium could be made. Before analyzing, the balls were warmed to room temperature and scrubbed with several degreasing agents to remove all traces of the deuteroparaffin mixture. This cleaning procedure was shown to be satisfactory by running a control test in which one ball bearing was subjected to all parts of the test except running in the fatigue machine. The hydrogen and deuterium were removed from the balls using a hot extraction apparatus attached to a mass spectrometer. Four balls from each bearing were analyzed. Each one was analyzed separately by removing it from a cold storage volume of the hot extraction apparatus and transferring it to the oven tube with a magnet. As the gases were evolved they were analyzed with the mass spectrometer. Since the hydrogen and deuterium pass through steel in the atomic form and since there are many more hydrogen atoms than deuterium atoms in the sample, the probability of forming an HD molecule is greater than forming a D2 molecule. For this reason the evolution of HD and H was followed as each ball was placed in the oven. The results showed that as each ball from the test bearing was dropped into the oven, the mass spectrometer recording of the HD evolution increased by about ten divisions. When balls from the control test bearing were dropped into the oven, the increase was about one division or less. The hydrocarbon background in the mass spectrometer was also monitored to see if hydrocarbons or deuterocarbons were given off when the balls were dropped into the oven, but no change in the hydrocarbon peaks was observed. Since the balls contained a fair amount of residual hydrogen, isotope ratio measurements were made on the gas obtained from each ball. The D/H value found for those balls which had been operated in the fatigue testing machine was consistently about 0.3

Jan 1, 1962