By Yuanbo Zhang, Mingjun Rao, Weiguang Tian, Huimin Tang, Guanghui Li, Lei Ye, Guoshen Liang, Zhiwei Peng, Foquan Gu, Tao Jiang

The amount of slag produced from a typical ferronickel smelting pro- cess is 4 to 6 times that of the metal product, and handling this slag is a huge challenge to the ferronickel industry. The feasibility of a technological route for preparing refractory materials from a ferronickel slag was verified in this study. Based on the thermodynamics analysis, the effect of the sintering temperature on the properties of refractory material from the slag was studied in the presence of magnesia. The results of thermodynamics calculation showed that the reaction of MgO with SiO generated forsterite and enstatite, whereas the reaction between 2 MgO and Fe O /Al O produced corresponding magnesia spinels. The experi- 2 3 2 3 mental results showed that a refractory material with refractoriness of 1580 °C, bulk density of 2.88 g/cm3, compressive strength of 106.9 MPa, and apparent porosityof 5.8%was obtained under the conditions ofmagnesia addition of 15 wt %, sintering temperature of 1350 °C and sintering time of 3 h. With increasing sintering temperature, the bulk density and the compressive strength of refractory material increased but the apparent porosity decreased, mainly attributed to the formation of the liquid phase which promoted the densification of the refractory material. (cid:1) (cid:1) (cid:1)

Mar 1, 2018

By Mei Yang, Wei Gao, Jian Yang, Qingcai Liu, Wenchang Xi

"TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel technology. In APCVD method, TiC14 and O 2 were used as reaction precursor. TiC14 was gasified by using N2 as carrier gas which was controlled to 500sccm. Its reaction temperature and reaction time were limited to 773K and 30min respectively. The physical properties, SEM and SEM-EDX of the TiO2-cordierite carrier and the properties of SCR catalysts prepared by these carriers have been tested. The tests showed that TiO2 loaded by APCVD method were of graininess shape and even accumulation. The loading rate of TiO2 and the specific area of carrier sample were increased 114% and 21 % respectively comparing with sol-gel technology. In the result of sol-gel method, the maximal difference of Ti content was 66.92%, while the result of APCVD method was 18.89%. It demonstrated that TiO2 was uniformly attached with the cordierite ceramic by using APCVD method, which would ensure more active ingredients well loaded on the Ti02-cordierite carrier. This difference made the denitrification ratio of catalyst prepared by APCVD method was 8.1 % higher than that of catalyst prepared by sol-gel method.IntroductionIn recent years, the emission of NOx, which were caused by coal-fired power plants, has gotten more and more attention. SCR (selective catalytic reduction) is the most effective technology to DeNOx [ll. The core technology of it is the catalyst. The SCR catalyst usually uses Ti02 as the carrier, and V2O 5 as the active component [2, 3] . However, the thermal stability and mechanical properties of TiO2 carrier are unstable, which would influence the performances of the catalyst. The commercial catalyst generally uses WO3 or MoO3 to promote its heat stability at present [4-7] Besides, TiO2 is expensive. Compared with TiO2, the cordierite is of good thermal stability and lower price. So loading Ti02 on cordierite porous ceramic as carrier to produce SCR catalyst is of good prospects [S, 91 • Currently, TiO2 is usually loaded on cordierite by the sol-gel method. But some research has shown that the sol-gel method easily reduced the loading performances of TiO2, such as distribution, combination, etc. APCVD (atmospheric pressure chemical vapor deposition) has many advantages to preparing TiO2 films, such as high bonding strength, fast reaction rate and so on [l0-13l_ In this paper, TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel methods. The properties of the carriers prepared by the two processes have also been compared."

Jan 1, 2011

By John Duff Erickson

Computer use has become an integral part of mine planning at Kennecott Copper Corporation?s Utah Copper Division, Bingham Canyon mine. Engineers are using the computer for development drilling calculations, mineralization grade interpolations, ore value summaries, long-range mining plans and short- range mining plans. The versatility of the computer has made it possible to explore many mining plan variations and to develop plans covering varying time intervals and production rates. This paper will summarize computer use in long-range mine planning, tell how short-range mining plans are prepared by conventional methods and discuss the development and application of short-range mine planning by computer.

Jan 1, 1966

By Yuanyuan Wang, Hong Li, Xueting Liu, Hao Bai, Kang Zhou

"Phase change materials are widely used in efficient utilization of energy and new energy technology. Especially, more attention has been paid to composite phase material, which is applied on architectural energy-saving and efficient working fluid. In this paper, stearic acid-silicon dioxide composite material was prepared by sol-gel process from tetraethyl orthosilicate (TEOS) and stearic acid (SA). The material was investigated by Field emission scanning electron microscopy (FE-SEM), Fourier transform infrared spectroscopy (FT-IR) and Differential scanning calorimeter (DSC). The FE-SEM results show that 3D-grids of silicon dioxide were formed clearly and SA was encapsulated in the silicon dioxide shell. The FT-IR results show that there were no chemical reactions between silicon dioxide and SA, which is the chemical property of the composite material, is stable. The DSC results show that the composite phase change material has favorable heat capacity. This material is expected to be used to make a cooling working fluid.1. IntroductionEnergy thermal storage becomes increasingly prominent issue in recent years, because thermal storage has been used in many aspects, for example, it can be added into building materials to improve heat conditioning. Another potential application of thermal storage materials is that the intermittent waste heat can be collected and recycled effectively by using the thermal storage facility. Thus, energy thermal storage plays a significant role in conserving available energy and improving its utilization [1]. Energy thermal storage includes sensible heat storage and latent heat storage. The latent heat storage has great heat density with a constant temperature during the phase change process [2-5]. Large quantities of latent heat storage will be absorbed and released when phase change takes place. Based on the former researches, some phase change material (PCM), such as fatty acid and paraffin waxes, has been proved to have high latent heat storage capacity and appropriate thermal properties [5-6]. However, using the PCM in energy storage systems directly is restricted, e.g. some properties of organic PCM, like form-stability and thermal conductivity, are not good enough to use. Meanwhile, almost all the inorganic PCMs are corrosive and most materials may cause sub cooling and segregation [7-9].The other problem is that the leakage when the temperature reaches the phase change point. Therefore, encapsulated composite phase change material (CPCM) emerged in order to solve the problem of leaking out, minimize the sub cooling and prevent phase segregation. [10-13] However, the easy flammability of fatty acid also has hindered the development of PCM. Accordingly, it has been found out that silicon compounds are environmentally friendly promising substitutes for halogen-containing flame retardants. Especially, silsesquioxanes are excellent in the flame retardancy. So CPCM can be encapsulated with SiO2 acting supporting material."

Jan 1, 2014

By Xianjun Lyu, Junxiang Wang, Peng Wu, Minjie Lian

"In recent years, the efficient cementation of mine tailings is a new way to manage mine solid wastes. The traditional cement materials have a slow setting time, large dosage and poor cementation strength for fine aggregate such as mine tailings. Therefore, the preparation of new type cementitious materials for the cementation of fine tailings has great potential in the treatment of mine waste solids. The paper mainly focuses on exploring the critical factors affecting the cementing performance of granulated blast furnace slag and its performance in the cementation of fine aggregate. Results indicate that the fineness of slag has a significant effect on its cementitious activity and Portland cement clinker has a better stimulation effect on the cementitious properties of slag than lime. And, anhydrite has a better early stimulation effect on the cementitious properties of alkali-activated slag compared to semi-hydrated gypsum and dihydrate gypsum. According to a series of tests on the cementation of fine iron tailings, the optimal ratio of slag, Portland cement clinker and anhydrite is determined as 60:30:10. Compared with P.O 42.5 ordinary Portland cement, the new slag based cementitious material shows much better cementing performance on fine tailings sample. Under the dosage of 12%, the compressive strength of fine tailings mortar using slag-based cementitious material in 3 curing days is increased to 168% that of using P.O 42.5 ordinary Portland cement, while the compressive strength in 28 days curing period is increased to 194%."

Jan 1, 2018

Sm-Co alloy is a kind of magnetic material with high power and has been applied in modern industry widely. In this study, the wet chemical co-precipitation was developed for synthesis of the Sm-Co alloy oxide precursor. The thermodynamic analysis of the studied system was done to clarify the solution behavior theoretically based on the thermodynamic equilibrium and simultaneous equilibrium. Then, the experiments were done to address the various effects on the wet chemical process, including solution pH, reactant concentration, dispersant, reaction temperature and time, etc. It is found that by precise control of the process, the Sm-Co alloy oxide precursor was synthesized with fine crystallization and special size & size distribution.

Jan 1, 2005

In this study, the method of chemical co-precipitation?reduction?diffusion was developed for the preparation of magnetic SmCo5 alloy. In the chemical co-precipitation process, the effects of solution pH, the reactant concentration, the dispersant on the process were investigated. The optimum conditions of the process were determined, and the SmCo5 alloy oxide precursor particles with fine crystalline structure, narrow size distribution was obtained. Then, by reduction-diffusion treatment of the precursor particles, the SmCo5 alloy with high quality was produced. It is anticipated that the co-precipitation-reduction-diffusion is a novel method available for SmCo5 alloy production.

Jan 1, 2006

By Bingliang Gao, Junli Xu, Michal Korenko, Jinzhao Guan, Liangxing Li, Zhongning Shi, Zhaowen Wang, Aimin Liu

Al-Si alloy, a precursor of solar grade silicon, was prepared by direct electrolysis in cryolite molten salt at 950 oC using high purity silica as material, liquid aluminum as the cathode and high purity graphite as the anode. The electrochemical behavior of Si(IV) ion was investigated using cyclic voltammetry method. The electrolysis products were characterized by XRD, SEM/EDS and ICP. The results indicate that the reduction process of Si(IV) on tungsten electrode is a two-step process and there is about 0.6 V gap between the two steps. The contents of boron and phosphorus in the aluminum-silicon alloy are 3 ppmw and 8 ppmw, which will make the directional solidification purification effectively and reduce the cost of preparation solar grade silicon from metallurgical grade silicon.

Jan 1, 2015

By Sheng-hai Yang

The ultrafine, monodispersed, spherical cobalt powder has been fabricated by reducing cobalt hydroxide with glycol. It were investigated that the effect of NaOH concentration on the reaction rate and the effects of the concentration of cobalt hydroxide and surfactant on the morphology and particle size. The particles were characterized by the X-ray diffraction(XRD), scanning electron microscope(SEM), laser diffraction particle size analyzer and BET specific surface analyzer respectively. The XRD shows that the cobalt powders exist mostly in face centered cubic (fcc) structure, a little in simple hexagonal. The cobalt powders prepared at Co(OH)2150g/L, NaOH 40 g/L and surfactant 30g/L, its average particle size, specific surface area and cobalt content, were 0.88µm, 2.705m2/g. and more than 99.5% respectively.

Jan 1, 2006

By Wen L. Chen

The steam coal quality is less stringent than metallurgical coal quality. The steam coal is prepared either by cleaning full size range of raw coal or cleaning coarse coal only, leaving the fine coal raw. The latter scheme is more cost competitive. It is particularly applicable to U.S. eastern soft coal where low ash coal is concentrated in fine sizes. For raw coal size separation, a recently developed Rotating Probability Screen, developed by the British Coal Board, may be advantageously used for easy change of raw coal separating size and to avoid screen deck plugging when handling wet and clayey raw coals.

Jan 1, 1983

By B. S. Taylor, J. D. Fraser, W. L. Chen

Steam coal quality is less stringent than metallurgical coal quality. Steam coal is prepared either by cleaning a full-size range of raw coal or cleaning coarse coal only, leaving the fine coal raw. The latter scheme is more cost competitive. It is particularly applicable to US eastern soft coal where low ash coal is concentrated in fine sizes. For raw coal size separation the Rotating Probability Screen, developed by the British Coal Board, may be used for easy change of raw coal separating size, and to avoid screen deck plugging when handling wet and clayey raw coals.

Jan 1, 1985

By Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Liang Yin, Xiaohui Fan

Straw char exhibited considerably faster burning speed than coke breeze for its porosity, which significantly degraded sinter quality when it replacing coke breeze as sintering fuel. In this investigation, preforming technology has been employed to densify raw straw. The properties of straw char preformed show that its density was increased, and the structure was also densified, which made the difference of combustibility between the straw char and coke breeze smaller. The proper preforming temperature, residence time and pressure were 200℃, 1min and 120MPa respectively. Sinter pot trials show that the product carbonized from preformed straw made the proper replacement ratio to coke breeze increase from 20% to 40%, and the emission reduction of SOx, NOx in flue gas increase from 11.50%, 14.15% to 37.85%, 23.60% respectively, compared with non-preformed straw char.

Jan 1, 2015

By Paul A. Hodges

With plant start-up slated for early 1966, Palabora Mining Co. will take its place among the large copper mining properties of the World. Located near the town of Phalaborwa in the Lowveld area of Transvaal Province, approximately 250 air miles northeast of Johannesburg, Palabora is the result of a cooperative project between Rio Tinto-Zinc Corp. and Newmont Mining Co. Other large shareholders are American Metal Climax, Inc., Union Corp. Ltd., and Selection Trust Ltd. Earliest known mining activity in the area is thought to date back about 400 years, when the Bantu tribes were migrating southward from the great lakes of Central Africa. Old workings and hand tools have been found in numerous places on the flanks of Loolekop, the hill that contains the outcrop of the Palabora orebody. Nearby ruins of small furnaces give added evidence of the knowledge of copper smelting possessed by these natives.

Jan 3, 1966

By Toshiharu Hayashi

We prepared the water dispersed with Au particles ranging from 10 to 20 nm size by a novel wet chemical synthesis; generating seeds of Au cluster by adding a borane dimethylamine complex into chloroaureic acid (gold salt) solution, and then growing simultaneously with aminoalcohol included in the solution. As-prepared Au nano-particles with chemical surface modification were found to have some attractive performances, i.e., showing a high dispersiveness in an aqueous solution in a long time, sintering nano-particles at low temperature, and having low resistivity in the film prepared from nano-particles. In the case that smaller Au nano-particles were removed from as-prepared colloid, especially, Au thin film formed on the surface of Si plate showed the excellent value of 7.0x10-6ohm cm (reference peculiar resistance: 2.35x10-6 ohm cm).The sintering temperature was dependent on the elimination of 2-aminoethanol that modified on the surface of Au nano-particles.

Jan 1, 2006

By Huimin Lu, Zhijiang Gao

Reduction reaction can happen among Al, V2O5 and TiO2 powders. Al can deoxidize metal V and Ti from the metal oxides. The electric igniter can be used to trigger the reduction. The reaction between Al and V2O5 is very intense and release large amounts of heat, but the heat which is needed to initiate the reaction between Al and TiO2 is not enough. These two reactions have been initiated first and V-Al and Ti-Al alloys can be obtained with a higher metal recovery percent. Through adjusting the ratio of Al, V2O5 and TiO2 powders, the system which combines these two reactions can ensured enough heat to react. KClO3 is added to the system, as the ignition agent, in order to make the reaction much complete. Finally, Ti-Al-V alloys can be obtained and need remelt to adjust the constituents.

Jan 1, 2016

By Fangqing Yin, Qingyu Deng, Zhengfeng Qu, Mengjun Hu, Meilong Hu

Titanium bearing blast furnace slag, which contains 20%-30% TiO2, is a valuable secondary titanium resource. Based on the thermodynamics calculation effect of the temperature on the reduction of the slag in vacuum were studied at certain vacuum degrees. The results show that magnesium vapor and silicon monoxide vapor can be obtained at the condition of high temperature and low pressure. The purity of TiC increases with temperature increasing. When the temperature arrives at 1623K TiC can be obtained besides the reductant carbon. XRD result of the powder collected from the furnace cover show that magnesium and silicon in the titanium bearing BF slag leave the slag system during carbothermal reduction in vacuum. From the above it can be concluded that TiC can be obtained from the titanium bearing BF slag and silicon and titanium in the slag can be separated by carbothermal reduction in vacuum and acid leaching.

Jan 1, 2016

By Run Huang, Xuewei Lv, Songli Liu, Chenguang Bai

"Titanium alloy was prepared from titania-bearing blast furnace slag (Ti-BF slag) by aluminothermic process in an induction furnace. The effects of aluminum amount on the titanium silicon yield and titanium recovery ratio were studied. The phase transformation and chemical composition of the prepared alloy were investigated by X-ray diffractometry (XRD) and X-ray fluorescence (XRF) respectively. It was found that the mass fraction of silicon and aluminum increased with increasing the aluminum amount, however, the mass fraction of titanium increased first and then decreased with increasing the aluminum amount. Furthermore, both the titanium alloy yield and titanium recovery ratio increased with the increase of aluminum amount. The main phases of the alloy were TixSiy and AlTi3. The titanium alloy samples prepared in various conditions had a composition (wt.%): 38–50% Ti, 29-34% Si, 4-11 Al%, 1.6-2.2 Mn%.IntroductionPanzhihua and Xichang regions in the southwest of China are rich in vanadium-titanium magnetite containing iron, vanadium, titanium and gangue. According to the characteristics of the resource, iron and vanadium are successfully recovered with a blast furnace process and a converter process. However, most content of titanium are entered in the blast furnace slag with TiO2 22% -26% and metallic Fe 2%–6% called Ti-BF slag. Due to the dispersed distribution of Ti in various fine grained mineral phases with a complex combination between Ca, Al and Si, it is difficult to recover the Ti components[1]. This slag is generated at a current rate of 3.6 million tons per year, which adds to the existing 70 million tons of slag produced so far[2]. The slag has had to be piled as large as the mountains, which not only waste of resources but also cause a pollution of the environment. Therefore, the study of integrated utilizing Ti-BF slag has become very significant."

Jan 1, 2012

By Zhang Hanbo, Niu Liping, Zhang Zhiqi, He Jicheng, Dou Zhihe

"Rutile, ilmenite and Al-Ca complex reducer were used to prepare high titanium ferrous alloy by enhanced reduction-SHS method. The effects of the complex reducer compositions and slag types on the enhanced reduction-SHS process were investigated. The high titanium ferrous alloys were characterized by XRD and SEM. The results indicate that the high titanium ferrous alloys consist mainly of TiFe2, AlTi3 and Al2O3. The oxide inclusions exist resulting in directly the high oxygen content and micro-structural defects in the alloys. The titanium and oxygen contents decrease, but the aluminum content in the alloy increases while the mass ratio of calcium in the Al-Ca complex reducers increases. When the mass ratio of Al/Ca in the Al-Ca complex reducer is 6:1, titanium, oxygen and aluminum contents are 63.75%, 3.01% and 10.72% respectively. When the mass ratio of Al/Ca is 5:1 titanium content is 55.00% nearly and aluminum content is higher than 14.00%, but oxygen content is lower than 2.0%.1. IntroductionThe high titanium ferroalloys with 65%~75% titanium have the advantages of low melting point and high titanium content. They are widely used in special steel refining, while they are also a kind of very important quality orientation alloys in the rage of aviation and aerospace. At present, the methods of preparing high titanium ferroalloy include vacuum remelting and thermit reduction. The alloys prepared by the vacuum remelting method have good qualities and low oxygen content, so it is widely used in Russia, Western Europe and other developed countries. In China, there are abundant rutile resources, but waste titanium is lack, therefore, the preparation method is the thermit reduction. But there are many quality defects in the high ferrotitanium alloy, including high oxygen content, unstable quality and so on. In order to improve the qualities of the high titanium ferroalloy, especially to reduce oxygen content, the domestic and overseas have done a lot of further researches. For example, Sichuan E-mei ferroalloy plant and Beijing Nonferrous Metal Research Institute have prepared high titanium ferrous with 73.77% titanium with natural rutile, but the oxygen content is high. Through controlling the quality of raw material, they obtained the better qualities, but the oxygen content is still very high. South Africa Mintek company have prepared high titanium ferrous alloy with low nitrate by plasma heating under the isolation air conditions, but they couldn’t also remove effectively oxygen in the alloy. The oxygen exists in the form of Al2O3 and titanium protoxide. So it can be speculated that except TiO2 not being fully reduced, the no-sufficient alloy-slag separation is the direct reason resulting in high oxygen and poor microstructure. In view of present technical difficulties during preparing high titanium ferroalloy by thermit reduction, this paper proposed a new method of preparing high titanium ferrous with low oxygen by enhanced reduction-SHS with Al-Ca complex reducer. Ca in Al-Ca complex reducer has stronger reductive ability, it can effectively strengthen the reductive degree of TiO2. The slagging agent CaO CaF2 and MgO can effectively reduce the viscosity of Al2O3 slag to improve its liquidities to strengthen alloy-slag separation effects so that to remove inclusions and oxygen. In this paper, effects of slagging agent type on the reduction and the qualities of high-titanium ferroalloy were studied."

Jan 1, 2012

By Leizhang Gao, Zhengfeng Qu, Pingsheng Lai, Chenguang Bai, Meilong Hu

FFC process could be used to prepare titanium foams. The mixed oxides CaO-TiO2 with mole ratio 1:2 were sintered into CaTiO3-TiO2 mixture. CaTiO3-TiO2 was then used as cathode and electrolyzed in molten CaCl2 to prepare porous titanium. The porous titanium with the porosity of about 72.15% was first fabricated. The internal pores are in the presence of circular cavities and the pore size is in the range of 50–100 lm. Compared with the powder metallurgy technique using the space-holder this method promises to be lower cost and less processing. It is potential to fabricate titanium foams using FFC process.

Mar 1, 2018

By Y. F. Guo

Laboratory scale experiments were conducted to produce titanium-rich material from Panzhihua ilmenite. The results showed preoxidation with sodium salt additive especially for Na2B4O7 signif- icantly advance the reduction of iron in Panzhihua ilmenite. Acceleration mechanism of preoxidation with Na2B4O7 has been studied here. The maximum metallization of iron 92% can be obtained under conditions of preoxidation at 850? for 30 min and subsequent reduction at 1100? for 150 min. The rusting separation technique to reduced ilmenite has been further studied, obtaining titanium-rich product with TiO2 over 82% and the recovery of TiO2 above 97%.

Jan 1, 2014