Search Documents

By H. Biloni, H. R. Bertorello

GruZLESKI and winegard1 have recently reported on the origin and development of the cellular substructure in Sn-Cd eutectic unidirectionally grown with different amounts of constitutional supercooling (CS). This communication deals with the results obtained in a parallel study on the instability of a plane interface in Al-Cu eutectic unidirectionally grown. Similarities as well as differences with the results of these authors1 will be presented. A1-Cu eutectic alloy ingots of 99.999 pct purity were grown unidirectionally under different G/R ratios where G = thermal gradient in the liquid, R = solidification rate. The ingots were cut in slices perpendicular to the solidification axes and the substructure studied on parallel sections following the sense of growth. It was generally found that the last part of the ingot to solidify presented a well developed colony substructure as a result of impurity build up and constitutional supercooling. The results obtained were: 1) When the structure was observed with low niagnification (of the order of 150 to 300 times) the first instabilities were observed at the grain boundaries and node-like structures formed at the junctions of the growth-induced boundaries, as reported by Gruz-leski and Winegard.1 Inside the grains the first signs of instability appear later and correspond to the type shown in Fig. 1; this is a two dimensional cell substructure. ' 2) Figs. 2 and 3 correspond to the evolution from a two dimensional substructure to a cellular type. In the A1-Cu eutectic the boundaries of the two dimensional cell are always perpendicular to the laniellaes instead of parallel as in the Sn-Cd eutectic. 1

Jan 1, 1970

By P. O. Metz, E. L. Wiehe, J. S. Foster

BASED on their analyses of growth kinetics, ibbs' and Harris et al.' have recently proposed that the rate of subcritical graphitization of steel is controlled by the rate of diffusion of carbon in ferrite. illert has concluded that this is the rate controlling growth mechanism when the growing graphite particles are relatively large. Harris et al.' also propose that the matrix surrounding a growing graphite particle is plastically deformed to make room for the growing particle. If this plastic deformation does occur, then preferred recrystallization may be observed around the larger particles. If diffusion of carbon in ferrite is rate controlling, then a graphite particle growing in a matrix of, say, tempered martensite or pearlite, should be surrounded by a carbide depleted zone. Thus, the simple metallographic experiments reported here are sufficient to determine whether or not diffusion of carbon in ferrite is the dominant mechanism for the growth of graphite in steel. The present investigation considers graphitization in five alloys. The compositions are given in Table I. Graphitization was carried out at three temperatures: 900°K (627"C), 950°K (677"C), and 990°K ('717°C). Samples were reacted in both the martensitic and the pearlitic initial conditions. In the hypoeutectoid steels, Sets 7 and 8, .and in the hypereutectoid Fe-C binary, Set 6, graphitization was very limited after 1000 hr at temperature. In these samples graphite particles observed were less than 10 p in diam. In the hypereutectoid commercial steels, Sets 1 and 3, large graphite particles (100 p) did not appear until after 250 hr at temperature. The limited number of graphite particles observed and the range of sizes obtained prohibited measurement of growth rates in this investigation. However, in all samples showing graphitization, neithe a carbide depleted zone nor recrystallization was observed. illert's model predicts that diffusion of carbon in ferrite should become dominant for graphite particles larger than about 300 p in diam. The largest graphite particle observed in this investigation was approximately 450 p in diam. No evidence of carbide depletion was noted. Fig. 1 shows a typical graphite particle. This nodule is from an initially pearlitic sample from Set 3 after

Jan 1, 1970

By R. E. Miner, J. K. Jackson, T. L. Wilson

THE nature of the decomposition reactions producing hardening in aluminum-rich A1-Ag alloys is now fairly well understood. The silver is not uniformly dispersed even at temperatures above the solvus line: rather, it is clustered into zones and associated with dislocations.' During quenching, nearly all of the silver segregates into zones' and some is attracted to dislocations, producing stacking faults. Growth of these faults produces the semicoherent y precipitate.1 During aging, the larger zones and the y precipitates grow at the expense of the smaller zones. The large zones persist up to about 350°C; where they redissolve in favor of the y' and y precipitates.' The equilibrium hcp y precipitate occurs both by a cellular reaction at the grain boundaries1 and by growth of the Y' plates to a critical size where incoherency results. Damask and Nowick 4 observed an internal friction peak in an A1-6 at. pct Ag alloy at about 140°C (0.25 cps). The peak was found to exhibit a systematic instability. After aging at successively higher temperatures between 155' and 23Z°C, the peak first migrated to higher temperatures while increasing in height, then returned to lower temperatures and decreased in height. After aging at temperatures above about 200°C, the peak position remained constant while the height decreased very slowly. In quenched specimens, elastic after-effect measurements inhcated a rapid initial transient in peak position from low temperatures up to 155°C. The authors concluded that a stress induced growth and resolution of the clusters and the 7' was the most reasonable mechanism to account for the behavior. It would seem, however, very unlikely that both the clusters and the y' precipitate would provide damping contributions whose relaxation time and activation energies were identical, which is required for them to produce the same internal friction peak. The present investigation was motivated by this apparent anomaly and the development of a very low thermal inertia torsion pendulum5 capable of monitoring transient behavior. Low frequency internal friction measurements were made on four binary A1-Ag alloys nominally containing 5, 10: 15, and 20 at. pct Ag. The results of measurements made on a 10 at. pct Ag alloy in the quenched condition are shown in Fig. 1. There are two peaks apparent in the spectrum, one centered at about 160°C, the second at about 210°C. The two peak spectrum was observed in each alloy, but it was best resolved in the 10 pct Ag specimens. Because of the instability in the internal friction, 4 it seemed possible that the second peak was not a peak at all, but simply a manifestation of a single, sharply transient, peak. This effect has been observed in Au-Ni alloys.6 The existence of the higher tempera-

Jan 1, 1970

By Thomas C. Wilder

ALTHOUGH there is an abundance of thermodynamic information available in the literature today, no experimental data on the standard molar properties of formation of zinc oxide have ever been reported for the temperature range 419.5" to 908°C. This is the temperature range for which zinc metal is a liquid. so that the formation reaction is: Data have been reported for Reaction [I] where zinc is a solid or a gas. Maier. Parks, and nderson' measured the electromotive force of the cell: in order to obtain the free energy of the reaction: over a limited temperature range. With the known properties of H2O, those of ZnO were calculated. These workers found that t;j of ZnO is -75,930 ± 150 cal per gfw and Mtf is-83,000 300 cal per gfw at 25°C. akolkin made similar measurements to obtain ilF7 and AH; of -75,870 and -82,540 cal per dw respectively at the same temperature. Truesdale and arirlg and Kitchener and 1gnatowicz4 measured the equilibrium of the reactions: respectively, in order to determine Ff of ZnO from the known values of CO, CO2, and H/X The thermodynamic properties of ZnO, presumably taken from the above investigations, are tabulated by Kubaschewski and vans' and Wicks and Block" The latter reference also gives values for the range where zinc is a liquid. These numbers are probably acquired from the known extremities of the range plus Cp data of the components. In the present work the electromotive force of the cell: was measured in order to calculate the properties of ZnO from the well known values of NiO for the temperature range where zinc is a liquid. In Cell [B] the cathode reaction is: and at the anode: The overall reaction is: for which the free energy change is: where is the electromotive force in volts of cell [B] after correction for the Pt-Ta thermocouple. The standard molar free energy of formation of NiO is very well known as a function of temperature. Kiukkola and agner's data are used in most tabulations. The error is probably less than I00 cal per gfw, The latter authors were the first to use solid mixed oxide electrolytes in galvanic cells. Their work with NiO and other oxides was performed with cells similar to Cell [B] using a variety of reference electrodes of fixed oxygen potential. There may be a small composition range for which either NiO, ZnO or both exist. If nonstoichiometry does exist for these oxides, then the properties described herein are those for the metal saturated compositions. The simple cell design was the same as described elsewheres except that the molten metal electrode was about 125 g of pure zinc including a small (0.25 to 0.50 g) amount of ZnO. The mixture of pure nickel and NiO powders making up the reference electrode was contained in a tube of the ZrOl + CaO electrolyte which was immersed in the molten zinc. A platinum contact was made to the reference electrode; tantalum to the zinc. A refractory cement plug was necessary at the open end of the electrolyte tube in order to prevent zinc vapor from contaminating the reference electrode. Experimental details such as the vessel containing the cell, furnace, temperature control and measurement, and electromotive force determinations of the cell have all been outlined previously. The temperature was varied randomly in the range between the freezing and boiling points of zinc. After each temperature change, time was allowed for the drift at the new temperature to be less than +;"c whereupon a series of three cell readings was taken at least 10

Jan 1, 1970

By C. Laird, C. E. Feltner

IN previous workif2 we have shown that the steady state cyclic stress response of pure copper tested in the low cycle fatigue range was determined only by the plastic strain amplitude and the test temperature. hus, copper, at any given temperature, has a unique cyclic stress-strain curve independent of prior history. Cu-7.5 wt pct Al, however, showed a stress response for a given plastic strain amplitude and temperature which depended sensitively on prior history. From this work we predicted that all wavy slip mode materials, typified by copper, would have a unique cyclic stress-strain curve; whereas all planar slip mode materials, typified by Cu-7.5 pct Al, would not. This prediction has now been tested for a number of materials of widely varying crystal structure and slip character. Wavy slip mode materials studied include: Fe. Al, Cd, disordered FeCo-V, and Cu-3 pct Co (quenched and aged). Planar slip mode materials investigated include: Fe-3 pct Si, ordered FeCo-V, disordered Ni3Mn, ordered Ni3Mn, and Zn. The treatment and properties of these materials are listed in Table I. Cyclic stress-strain curves were determined by controlled plastic strain tests (see Ref. 1 for details) at room temperature for all materials in both the initially annealed and cold worked conditions. The results obtained for iron and Fe-3 pct Si are typical of wavy and planar slip mode materials, respectively. The cyclic stress-strain curves for these materials are shown in Fig. 1 and it can be seen that iron has a unique cyclic stress strain curve while Fe-3 pct Si does not. Aluminum, Cu-3 pct Co, and disordered FeCo-V showed a behavior like that for iron, while Ni3Mn in both the disordered and ordered condition behaved in the same manner as Fe-3 pct Si. These results therefore support the general conclusion drawn in Refs. 1 and 2 that. for wavy slip mode materials, a cyclic mechanical equation of slate it =t.(hcp, i. T) is approximated in which the satura-

Jan 1, 1970

By L. W. Sink, B. H. Kear, S. M. Copley, M. F. Hornbecker

IT is well known that under appropriate conditions of chill casting, many metals and alloys develop a columnar grain structure having a high degree of preferred orientation.' In cubic materials, this principle has been employed to produce shaped castings with a unidirectional cube oriented columnar grain structure as well as shaped single crystals with a cube axis parallel to the growth ais.' "he purpose of this note is to describe how this same principle can be enlployed to produce wires, rods, or more complex crystal Shapes with a variety of conlpositions in cube or random orientations by a single casting operation. The procedure for directional solidification of in Fig. 2. Examination under crossed polarizers indicated that the striations were a second phase (presumably the B19 phase) which frequently forms initially at primary grain boundaries and then grows toward the interior as thin ribbons. X-ray studies on filings of this alloy reannealed at 1300°C for 15 min indicated a strong pattern of the fcc phase together with a substantial pattern of the B19 phase. The un-annealed filings, however, showed only the pattern of a cold-worked, fcc structure. In these two-phase alloys it appears, therefore, that the B19 phase is transformed into a disordered fcc structure by cold-working. The mechanical properties of these alloys would be of some interest since a fcc structure might be expected to possess greater ductility than the or-thorhombic B19 structure from which it forms. The author wishes to thank Mr. Harvey Yakowitz and Mr. Richard Manuszewski for obtaining the photomicrograph in Fig. 2. This research was partially supported by Research Grant DE-02455 from the National Institute of Dental Research. columnar grained ingots involves pouring a melt into a preheated mold having a water-cooled copper chill at its base? and controlling the temperature gradient in the mold so as to maintain columnar grain growth from end to end of the ingot.4 This is illustrated schematically in Fig. l(a). It should be noted that the longitudinal temperature gradient promoting unidirectional columnar grain growth is maintained by heat loss primarily through the solidifying ingot to the chill, so that both the temperature gradient and the growth rate diminish with increasing distance from the chill. As the distance from the chill increases? the columnar structure coarsens, and the perfection in preferred orientation tends to increase progressively. Using this same procedure of gradient solidification, Fig. l(b) shows a simple scheme for producing a batch of crystals having the same cube orientation rather than an assemblage of columnar grains. Wires and rods are produced by cementing ceramic tubes to the wall of the mold. The steep temperature gradient produced in the central chamber is controlled by the mold heater to produce favorable conditions for crystal growth. Clearly the success of the operation lies in the selection of individual growing columnar grains by some kind of orifice at the base of each channel in the mold. Using simple constrictions, experience with nickel-base alloys has shown that 4 -in.-diam holes at a distance of -1 in. from the chill yield crystals within 7 deg of (100); closer control of orientation is possible by placing the crystal selector farther away from the chill.

Jan 1, 1970

By Michael A. Arkoosh, E. A. Peretti

ANALYTICAL results have previously been presented for the diffusion-controlled solution of a second phase in a finite medium for planar, cylindrical, and spherical geometries.' These results were obtained by numerical methods using digital computer techniques and are applicable not only to the stage of the problem where the unstable phase shrinks to zero size, but also the subsequent stage where the concentration gradients in the matrix phase become negligible (essentially complete homogenization). It is anticipated that the results of such an analysis may be of use to those workers who are interested in the processes

Jan 1, 1970

By B. C. Wonsiewicz, W. W. Wilkening

Following a procedure proposed by Wheeler and Ireland, Plane stress yield loci were constructed from Knoob hardness numbers. Basically, six differently oriented hardness measurements were made on three orthogml surfaces through pure poly crystalline magnesium sheet, a magnesium single crystal, and sheet of the magnesium alloys: Mg + 0.5 pct Th, Mg + 4 pct Li, AZ31B, and EKOO. Hardness loci were found to be in poor agreement at small strains (E < 0.05) with loci established by a more rigorous technique. At larger strains (E - 0.10) the agreement is fair, but at this stage in deformation the conventional locus has lost much of the asymmetry that characterizes these anisotropic materials. Two effects which will lead to distortions in the Khn locus are discussed with reference to the geometry of plastic flow during a hardness test. DETERMINING a material&apos;s resistance to multiaxial loading is of interest not only from a structural design viewpoint but also from that of deformation processing. Unfortunately, the determination of the yield locus, although simple in principle, involves tedious procedures if the results are to be at all rigorous.&apos; The idea, first proposed by Wheeler and 1reland2 of determining the yield locus by means of six Knoop hardness impressions along the principal directions in a material has obvious appeal. It is simple, quick, and should be applicable to very thin sheets. If such a technique could be demonstrated to produce consistently reliable results, it would be of interest to both researcher and designer. Lee, Jabara, and ackofen have compared the yield locus determined by Knoop hardness measurements (the Khn locus) to a locus determined by more rigorous techniques. They found good agreement for two titanium alloys at a plastic strain of about 1 pct. The purpose of this paper is to investigate if the Khn locus construction is a reasonable approximation to the locus of a highly anisotropic material. Examples of such materials are magnesium and magnesium alloys which have severely distorted yield loci which in turn reflect markedly dfferent yield strength in different directions.&apos; In pure magnesium, for example, the yield stress in tension along the transverse direction may be four times the yield stress in compression in the same direction and twice the tensile yield stress in the rolling direction. Predicting such large differences ought to serve as a severe test of the Khn locus construction. EXPERIMENTAL PROCEDURES Samples of rolled sheet, 0.250 in. (6.35 mm) thick, of pure magnesium and four magnesium alloys (Mg experimental materials. The pure magnesium together with the lithium and thorium alloys were those used in the study of Kelley and Hosford. The grain size was ASTM number 4 for the pure magnesium and number 6 for the alloys. HARDNESS TESTING The materials were sectioned along the rolling and transverse planes, mounted in a quick setting resin, and mechanically polished. Most of the hardness tests were performed on a surface prepared by electro-polishing (30 pct nitric acid in methanol at 0°C and 20 v) with the exception of the AZ31B and EK00 alloys which were made directly on a metallographically polished surface. However, subsequent hardness tests on the same sample after heavily electropolishing, revealed essentially the same hardness as before. At least twenty Knoop hardness impressions under a 100-g load were made in each of the six orientations shown in Fig. 1. The average hardness number and standard deviation were then calculated for each orientation. CONVENTIONAL LOCUS CONSTRUCTION Yield loci were constructed using a technique described in detail by Lee and ackofen,&apos; in which the flow stress (stress at a given plastic strain) fixes the coordinates of a point on the locus and measurements of the strain ratio serve to establish the slope of the locus at that point. The loading paths which correspond to uniaxial tension or compression tests establish the four intercepts of the locus with the coordinate axes plus one point on the balanced biaxial tension line Tensile testing was performed along the rolling and transverse (r, t) directions. Samples had a uniform rectangular gage length 1 by 4 by 4 in. (25.4 by 6.35 by 6.35 mm) and were deformed at a strain rate of 3.33 x 104 sec-&apos;. The tests were interrupted periodically to unload the sample and measure the plastic strains by means of X-Y post yield strain gages. Compression tests in the rolling, transverse, and through-thickness (r, f, z) directions were performed on 1/4 in. (6.35 mm) cubes at an initial strain rate of 8.33 x sec-&apos;. Lubrication was provided by 0.002 in. (51 pm) Teflon sheet which was renewed after unloading for micrometer measurements used to calculate the strains.

Jan 1, 1970

By R. J. Fruehan

The oxygen activity and concentration were measured in Fe-Cr-0 melts in equilibrium with an oxide phase at 1600°C (2912°F). The activity was determined by ,use of the following solid oxide -electrolyte galvanic cell CY-Cr8,(s) I ZrOz(CaO) I Fe-CY-G(saturated)(l) The oxygen concentration decreases with increasing Cr concentration to about 270 ppm 0 at about 7pct CY and then increases gradually. The activity coefficient of oxygen (fo) decreases with increasing Cr. In melts containing up to about 20 pct Cr, log f is approximately a linear function of wt pct Cr with a slope (e q 2) of —0.037. The activity of chromium was calculated and found to exhibit a small negative deviation from Raoult&apos;s law. From the activity and solubility data for low chromium melts, the free energy of formation of chromite, FeCr204, was found to be -79.8kcal per mole where pure liquid chromium and oxygen at I wt pct in Fe are the standard states. ThE effect of chromium on the chemical behavior of dissolved oxygen in liquid iron is of great importance in controlling the deoxidation of steels containing a significant amount of chromium. Chen and chipman&apos; equilibrated Fe-Cr melts in the presence and absence of slag with hydrogen-water vapor mixtures. They concluded that at 1595°C chromite was the oxide phase in equilibrium with Fe-Cr alloys containing less than 5.5 pct Cr while at higher chromium concentration Cr,O, was the stable phase. In the composition range 0 to 10 pct Cr they found that the interaction coefficient, was equal to -0.041. Turk-dogan,&apos; Schenck and Steinmetz,, and pargeter4 measured egr) in a similar manner and found the value to be -0.064,-0.04, and -0.052, respectively. McLean and Be11 evaluated egr) from their data on the equilibrium of Fe-Cr-Al-0 alloys with H2/H20 mixtures and found it to be -0.058. However, McLean and Bell&apos;s value should only be considered an estimate because the effect of aluminum on the activity coefficient of oxygen is about a hundred times greater than that of chromium. Consequently, an error in the value of egl) used, which at the present time is not well-known, or an error in aluminum analysis, which is present in very small quantities, will result in a significant error in egr). Fischer et a1.6 determined the interaction coefficient (eEr) in Fe-Cr-0 melts not in equilibrium with an oxide phase and containing less than 18 wt pct Cr at 1600°C electrochemically. They determined a value of -0.031 for egr). Hilty et aL7 measured the oxygen content of Fe-Cr melts in equilibrium with an oxide phase containing up to 50 pct Cr. They found that the solubility of oxygen decreased as the chromium content increased to about 6 pct Cr and then increased gradually. They concluded that the equilibrium oxide phase was chromite below 3 pct Cr, distorted spinel from 3 to 9 pct Cr, and Cr,04 above 9 pct Cr. Adachi and lwamotoa also investigated this system, but did not find Cr30,. They X-rayed the equilibrium oxide phases and did not find the presence of Cr,O,. They also X-rayed the oxide phase extracted from a 65 pct Cr melt which was heat treated and did not find metallic chromium as would be expected if Cr3O4 were the equilibrium oxide phase as indicated by the reaction : 3Cr3O4 — 4Cr2O:, + Cr [lj It was the purpose of the present investigation to determine the effect of chromium on the activity coefficient of oxygen in Fe-Cr melts by measuring the activity and solubility of oxygen equilibrated with an oxide phase in the composition range 0.18 to 50.5 wt pct Cr at 1600°C (2912°F). The activity of oxygen in the melts was determined by use of the following galvanic cell: The relationship between the partial pressure of oxygen in equilibrium with the melt and the reversible electromotive force of the cell (E) is where 11 = 4, F is the Faraday constant, pb, is the oxygen pressure in equilibrium with the meit and is the oxygen pressure in equilibrium with Cr203 as determined from the free energy data compiled by Elliott et al? The oxide phase in equilibrium with pure chromium was assumed to be Cr If Cr30, were the equilibrium phase the activities derived would be approximately the same, since the best estimated free energy of formation of Cr,O,, if it does exist, is approximately % the free energy of formation of The activity of chromium in Fe-Cr alloys at 1600° C was also determined from the measured electromotive force. The activity of chromium (aCr) is related to the electromotive force as follows: , The oxide phase in equilibrium with pure chromium and Fe-Cr melts from 10 to 52 pct is assumed to be Cr203 so that n equals three. If future work proves the existence of Crs04 in equilibrium with Fe-Cr melts and pure chromium, the experimental results can be reevaluated using a value of $ for n in Eq. 141. A value of ^ for n will make the activities about 10 pct higher. In order for Eqs. 131 and [4J to be valid the electrolyte, ZrOa(CaO), must exhibit predominantly ionic conduction at the temperature and oxygen partial pressure of its use. Previous work1&apos; has demonstrated that ZrOz(Ca0) is predonlinantly an ionic conductor

Jan 1, 1970

By Shiro Ban-ya, John F. Elliott, John Chipman

The activity of carbon in Fe-C austenite at 1150°C has been determined for concentrations up to about 2.1 pct C using the equilibrium: C + COz = 2CO; equations have been derived expessing the activity as a function of carbon content on the basis of twelve mathematical models. Several of these represent the data satisfactorily. ACCURATE information on the thermodynamic properties of austenite in the binary system Fe-C is needed as a basis for studies of transformation and precipitation in steels of all sorts, alloy as well as plain carbon. The many attempts to approach this problem through statistical thermodynamics require sound and dependable experimental data in order to evaluate the several models which have been suggested. In this paper we are concerned with the experimental determination of the activity-composition relation in austenite at the temperature of its widest range of stability, approximately the eutectic temperature (1153°C). Accurate investigation of the activity of carbon in austenite may be said to have begun with the work of Dunwald and wagner.&apos; A more detailed study was carried out by R. P. smith2 on the two equilibria: More recent work on these two equilibria has been reviewed by Chipman,3 who pointed out the experimental hazards associated with studies of Eq. [I]. Studies of this reaction involve rather small values of the ratio these are susceptible to errors due to traces of moisture in the apparatus according to the reaction: Ellis, Davidson, and Bodsworth4 evaluated K, for their experimental temperatures and used desiccants to control water vapor pressure. While they were able in this way to obtain consistent values for K1 it cannot be said that all of the uncertainties of the method have been overcome. Results by both methods reported by Schurmann, Schmidt, and wagener5 appear to be consistent except at very low carbon content. Reaction [2] was employed in the experimental work reported here. It is to be recognized, however, that it is not applicable to projected studies of certain alloy steel compositions involving stable oxide-formers.

Jan 1, 1970

By C. S. Samis, J. C. Mitchell

Sodion activity data have been obtained for the Na-A1 system for sodium concentrations in aluminum between NN, = 25 . 10-and 300 x 10&apos;. This concentration intert-a2 encompasses those sodium concentrations nor1)zally encountered in aluminum reduction cell operation. The sodium activity data were measured by a two-phase equilibration of sodium between a lead and an aluminam rich phase. The Na-Pb system was emplojed as a reference for the determination of the actiz7itj 0.f sodium. The activity of sodiin in aluminuwz exhibits large positi2.e deviations frorn ideality and a strong dependence, on concentration below NN, = 100 x 1K6. The inteated data indicate that the activity of aluminium is equal to its mole fraction over the range of miscibility of the Na-A1 sgstem. The data on the Na-A1 binary have been combined with experimental data on the cryolite-A1 system at 1025°C to obtain the activities of Na F and AlF, in liquid cryolite oz2er the cornposition 1-ange encountered in aluminum cell operation. The results are in agreement with activities calculated from the NaF-AlF, phase diagram. ALUMINUM is produced commercially by the electrolytic reduction of aluminum oxide dissolved in molten cryolite. There is considerable controversy over the actual mechanism of the discharge processes, but sodium potentials in the systems appear to play an important role in the reduction mechanism. The metal-salt reaction involving NaF and aluminum to produce A1F3 and sodium is responsible for the presence of sodium in the aluminum metal phase. Additional sodium may be produced from the simultaneous deposition of sodium and aluminum at the cathode as a result of a cathodic overvoltage. runert&apos; has suggested that sodium gas at atmospheric pressure would be the result of reaction between cryolite and aluminum at 1000°C. Subsequent investigations have shown that production of sodium at atmospheric pressure does not occur. These later investigations can be conveniently separated into two categories. The first involves sodium, aluminum, and cryolite, in which the sodium activity was measured. The second includes a lead phase for sodium activity measurement. Jander and errmann,&apos; studied the reaction: at 1090°C in alumina crucibles under an atmosphere of dry, oxygen-free nitrogen. The equilibrium constant for the reaction was expressed in terms of concentration. Their results in Fig. 1 show an increase in sodium content of the aluminum with increasing NaF/A1F3 weight ratio. Pearson and waddington3 performed similar experiments at 1000°C. Their results are included in Fig. 1. Dewing and ollinshead have measured the sodium content of aluminum as a function of the NF/AF, ratio at 1025"C, Fig. 1, and ewin&apos; measured the sodium content of the aluminum in a system involving the solid reactants NaF, cryolite, and liquid aluminum. This reaction is different from those discussed above. Two solid phases, NaF and Na3A1F6, and a liquid aluminum phase were present. The sodium concentration in the aluminum was determined by the temperature. Dewing&apos;s measurements covered the temperature range 679" to 896°C. Omo, Matsushima, and 1t02" investigated the equilibrium 6NaF ential thermal analysis. Stokes and Frank6 determined sodium activities by

Jan 1, 1970

By C. D. Williams, C. E. Ells

The susceptibility of quenched and aged Zr-2.5 wt pct Nb alloy to embritt2ement during irradiation has been examined for a number of solution temperatures and aging times. Material quenched from temperatures approximately 40°C below the transus has high tensile ductility, and this ductility is insensitive to aging at 500°C or to irradiation. If, however, the material is quenched from temperatures above the transus it becomes highly susceptible to loss of ductility either from aging at 500 or from irradiation. Inter granular failure is characteristic of the materials having low ductility. The distribution of the equilibrium phase is found to control the susceptibility to embrittlement by restricting 6 grain growth during heat treatment and thus influencing crack propagation. IN zirconium, as in titanium, -stabilizing alloy additions are used to obtain high strengths via quench and age heat treatments, and the Zr-2.5 pct Nb alloy has been developed1 because of its strength advantage over the Zircaloys. Early in the development of the Zr-2.5 pct Nb alloy the problem of 13 embrittlement was appreciated, and for this reason the solution temperature was chosen below the p transus.&apos; In the course of irradiation studies on quenched and aged Zr-2.5 wt pct Nb alloy it was found&apos; that irradiation introduced an important aspect of p embrittlement, riz., material quenched from the phase and aged 24 hr at 500°C was severely embrittled by moderate doses of neutron irradiation. This effect had not been studied in titanium alloys. In titanium the metallurgical features leading to 0 ernbrittlement were found to be structures with: a) coarse a platelets at the grain bondaries, b) finely dispersed a uniformly distributed throughout the (0) matrix,6 c) Widmanstatten a-13 with more than 50 pct P, d) the presence of some metastable p transformation products,3 and e) large prior -phase grain size.5 Alternatively, the presence of a uniform distribution of coarse a was conducive to high ductility and a structure largely of equiaxed a was very dctile. The detailed mechanisms of the embrittlement have not been worked out for all of these conditions, although weakness at either a-matrix boundaries or prior p grain boundaries have been prominent in the eculation. It was proposed that acicular a might act as a mild notch, and low ductility has been associated with easy fracture along its boundary.&apos; There have been two opposing suggestions for the source of the high ductility associated with equiaxed a phase. JaffeeB proposed that this a would accept a large por- tion of the oxygen, thus increasing the ductility of the matrix, whereas after study of a Zr-Nb-Cu alloy Weinstein and oltz proposed that the a phase, softer than the martensitic matrix, acted to blunt cracks formed in the matrix. In the present work we have studied the effect of neutron irradiation on the ductility, particularly the P embrittlement, of the Zr-2.5 wt pct Nb alloy. By a variation of solution temperature and aging time a variety of metallurgical conditions have been examined, and a range of resultant ductilities obtained. The ductility has been related to the material microstructure and mode of fracture. EXPERIMENTAL The alloy used in the present work came from two separate ingots fabricated into rod of 3/8 or i in. diam, Table I. For both batches the P transus temperature was approximately 890° C. Most of the heat treatments were done directly on lengths of the j} in. diam rod, after which the tensile test specimens were machined. Quenching was achieved by dropping rods from a dynamic vacuum into water, the cooling rate estimated to be 2 100°C per sec. For aging the rods were encapsulated in evacuated silica tubes. Round tensile test specimens, with gage diam and length 0.160 and 1.0 in., respectively, were used throughout and pulled at room temperature or 300°C on Instron tensile machines, at a crosshead speed of 0.05 ipm. Specimens were irradiated in the NRX and NRU reactors, in facilities described in previous publications.&apos;0 The metallurgical conditions examined have been: All tensile test specimens were machined with axes in the axial direction of the swaged rod. Although the specimen had a degree of preferred crystallo-graphic orientation with basal plane normals both parallel with and perpendicular to the tensile axis, the material was comparatively isotropic." The techniques of thin foil examination in the electron micro-

Jan 1, 1970

By Mark J. Klein

The creep of 043 was studied over the temperature range 1650" to 3200°F and over the stress range 3000 to 44,000 psi. The steady-state creep rate over this range of stress and temperature can be expressed by the equation where A is a constant, is the stress, and is -0.8 x 103 psi-&apos;. Over a narrow range of stress variations c0 a and for this proportionality n varies from 3 to 30 in accordance with the relation n = aB. Above about 2400° F, H, the apparent activation energy for creep, is 110,000 cal per mole, a value about equal to that estimated for self-diffusion in this alloy. Below 2400°F, H increases with decreasing temperature reaching a value of -125,000 cal per mole at 1700° F. In this temperature region, H appears to be a function of the interstitial concentration of the alloy. MOST of the detailed creep studies of dispersion strengthened metals have been concerned with metals having fcc structures. However, there are a number of important refractory alloys with bcc structures that derive part of their high temperature strength from an interstitial phase and whose creep behavior has not been well defined. This paper describes the creep behavior of the bcc alloy, D43, over the temperature range 1650" to 3200°F (0.4 to 0.7 Thm) and over the stress range 3000 to 44,000 psi. In addition to colum-bium, this alloy contains 10 pct W. 1 pct Zr, and sufficient carbon (-0.1 pct) to form a carbide dispersion throughout the matrix of the alloy. The effects of variations in temperature and stress on the steady-state creep rate of this alloy are presented in this paper. EXPERIMENTAL PROCEDURES Creep tests were made in a vacuum of 106 torr under constant tensile stress conditions using a Full-man-type lever arm.&apos; Creep specimens were machined from 0.020-in. D43 sheet (grain size -5 x l0-4 in.) processed in a duplex condition (solution annealed -2900°F, 40 pct reduction in area, aged 2600°F). The specimens were tested in this condition without further heat treatment. Specimen extensions over 1-in. gage lengths were continuously recorded using a high temperature strain gage extensometer. Differential temperature and stress measurements were used to determine temperature and stress dependencies of the creep rate. Activation energies were calculated from the changes in strain rate induced by abrupt shifts in the temperature during constant stress creep tests. The 100°F temperature shifts used in most of the activation energy determinations required 15 to 90 sec depending upon the temperature at which the shift was made. The dependence of strain rate on stress was determined by measuring the change in strain rate for incremental stress reductions during constant temperature tests. It has been shown that columbium-base alloys such as D43 are susceptible to contamination by gaseous interstitial elements during vacuum heat treatments.&apos; In this regard, it is unlikely that these alloys can be heat treated without some loss or gain of interstitial elements despite the precautions taken to control the heat treating environment. However, several factors suggest that changes in interstitial concentrations of the specimens during testing did not affect the results presented in this paper. First, the dependence of the creep rate on the stress or temperature determined during the course of a single creep test showed no variations with the duration of the test. A variation would be expected if a loss or gain in interstitial concentration during the course of the test affected results. In addition, precautions taken during this investigation to minimize interstitial contamination by wrapping the gage lengths of the specimens with various foils2 (Mo, Ta, W) did not produce a detectable change in the stress and temperature dependencies relative to the unwrapped specimens. The averages of duplicate analyses for carbon and oxygen in several specimens determined before and after creep testing are listed in Table I. The combined nitrogen and hydrogen concentrations which were ordinarily less than 50 ppm did not change in a detectable way with creep testing. The analyses show that only minor changes in carbon concentration occurred during creep testing except for specimen 4. This specimen which was tested at 3100°F lost a significant amount of its carbon concentration to the vacuum environment. Specimen 1 gained 100 ppm of O, while specimens 2, 3, and 4, which were tested at progressively higher temperatures, lost increasing portions of their initial oxygen concentrations during testing. RESULTS AND DISCUSSION The Temperature Dependence of the Creep Rate. The apparent activation energy for creep, H, was de-rived from creep curves similar to that shown in Fig. 1. Steady-state creep was rapidly attained at the beginning of the test and with each change in temperature. This behavior suggests that the alloy rapidly attains a stable structure with each shift in temperature or that the structure is constant throughout the test. Since the dispersion will tend to stabilize the structure, the latter is probably the case. The activation energy was found to be independent of the direction of the temperature shift and the magnitude of the shift (50" or 100°F). Although H was approximately independent of the strain, there was a tendency for it

Jan 1, 1970

By Hsun Hu, B. B. Ruth

The rates of migration of high-angle boundaries in zone-refined aluminum crystals rolled 20 to 70 pct in the (110)[i12/ orientation were studied. Following a recovery anneal at an appropriate temperature to stabilize the polygonized structure, boundary migration rates of artificially nucleated grains were measwed isothermally at several temperatures. Results indicate that the rate of boundary migration depends strongly on the amount of deformation and on the cell size of the polygonized matrix, and is related to the driving free energy by a power function. The degree of anisotropy in growth 0.f the re crystallized grains nn&apos;th preferred mientation is independent of deformation; the migration rates of the fast-moving and the slow-moping boundary segments of a gowing grain differ by as much as one order of magnitude. The actir\ation energy fm a grain boundary migration, although nearly the same for both the fast-moving and the slow-moving boundaries for a given deformalion, decreases from 45 to 30 kcal per mole with an increase in deformation from 20 to 70 pct reduction. Re crstallization by the growth of the artificially nucleated grains results in preferred orientation. The Percentuge of&apos; grains favorably oriented for growth increases with increasing deformation. None of these grains corresponds to the ideal Kronberg-Wilson orientation relationship. The observed growth aniso-tropy is discussed in terms of boundary structure. The boundary velocity as a function of the cell inter -facial area, or the driving free energy, is discussed in the light of current theories of boundary migration. It is well established that recrystallization with re-orientation occurs by the migration of high-angle boundaries of strain-free grains. The driving force for this process is provided by the free energy stored in the metal during deformation. A quantitative study of the effect of varying driving force on grain boundary migration in deformed metals has not been possible heretofore, primarily because of: 1) concurrent recovery steadily decreasing the available driving free energy for boundary migration, &apos;-3 and 2) in-homogeneity of strain in the deformed metal.4 Aust and Rutter3 studied grain boundary migration in striated single crystals of zone-refined lead. Although the driving free energy in such crystals remains unaltered during annealing, this method does not provide a range of driving free energies over which measurements of grain boundary migration can be made. In the present investigation, the rates of migration of high-angle boundaries in deformed aluminum zone- refined single crystals were studied at various temperatures, after deformation ranging from 20 to 70 pct reduction by rolling at -78°C in the (ll0)[i12] orientation. The boundary migration rates along different crystallographic directions were determined under steady-state conditions, i.e., in the absence of competing recovery processes or impingement of recrystallized grains growing into the deformed single crystal matrix. Simultaneous recovery was eliminated by suitable anneals prior to the boundary migration measurements. The recrystallized grains, which grew a ni so tropically into the homogeneously polygonized matrix, developed flat boundary segments during early stages of growth. These boundary segments subsequently migrated along a direction approximately normal to the boundary plane into the matrix rystal. Increasing deformation over the range employed was estimated to increase the driving free energy for boundary migration by about five times. The kinetics of the boundary migration process, examined under these conditions, indicate that the boundary velocity is greatly affected by a small change of the driving free energy in the matrix crystals. These results were examined in the light of the current theories of grain boundary migration. EXPERIMENTAL PROCEDURES Single crystal strips (9 by 1 by 0.125 in.) of zone-refined aluminum, were seed-grown by the Bridgman method in a high-purity graphite mold (<lo ppm ash) at 1 in. per hr. Precautions were taken to minimize contamination of the metal during crystal preparation and subsequent handling. Spectrographic analysis of the metallic impurities in the grown crystals is Qven in Table I. The crystals were rolled in the (110)[112] orientation at -78°C to various reductions in thickness, ranging from 20 to 70 pct, in 10 pct increments. The desired reduction was achieved by many rolling passes, each being no more than 0.002 in. To minimize surface friction, the crystal was rolled between two thin layers of teflon. For those crystals rolled more than 40 pct, it was necessary to remove the disturbed surface layers by electropolishing at -5" to -10°C at an intermediate stage of rolling. The edges of deformed crystals were removed by a jeweler&apos;s saw while submerged in alcohol at -78° C to obtain samples of about ? by i in. The distorted metal at the cut edges and the surface layers were then removed by electropolishing, with removal of a minimum of 0.004 in. from each surface. The thickness of the crystals prior to rolling was chosen so that the final thickness was 0.025 in. for all samples. These deformed single crystals were each prean-nealed for 1 hr at an appropriate temperature in the range of 130" to 280°C, depending upon the amount of deformation. The purpose of this preannealing was to

Jan 1, 1970

By Neils Hansen

The microstructure of dispersion-strengthened aluminum aluminum-oxide products containing from 0.2 to 4.7 wt pct of aluminum oxide has been examined by optical and transmission electron microscopy, and the flow stress has been determined at room temperature and at 400C by tensile testing. Products were examined as recrystallized and as high-temperature extruded, and the microstructures consisted of a fine dispersion of oxide particles in a matrix divided by respectively recrystallized grain boundaries and subgrain boundaries. The flow stress (0.2 pct offset) at room temperature of recrystallized dispersion strengthened aluminum aluminum-oxide products is the superposition of dispersion strengthening and grain boundary strengthening. This superposition has been found to be linear. The flow stress (a) can be related to the grain size (t) by the Petch equation: ing content of oxide and k is a constant independent of the oxide content. For extruded products a similar relation has been found by replacing the grain size by the subgrain size. The k-value is of the same order for the two types of structure, which shows that the subgrain boundaries are as effective slip barriers as grain boundaries. Tensile testing at 400C of re-crystallized and extruded products shows that oxide dispersion strengthening is very effective, whereas the strengthening effect of grain boundaries and subgrain boundaries is small. THE microstructure of dispersion-strengthened products consists of hard particles finely distributed in a metal matrix. The strengthening effect of the dispersed phase has been fairly well established,1 and it has been found that the size and volume fractions of the dispersed particles are important structural parameters. However, in many dispersion-strengthened products which have been worked and heat-treated during manufacture the matrix is divided into well-defined grains or sub-grains, which may also have a strengthening effect. A model of the matrix strengthening in dispersed products worked during manufacture has been proposed,2 introducing the energy of the structure as a strengthening factor, especially at low temperatures. A difficulty in this model is, however, to relate this (stored) energy to the structural parameters directly observable as for instance grain size. The strengthening effect of the matrix grain size after recrystallization has been in- vestigated for nickel-thoria (TD-Nickel) products3 and for copper aluminum-oxide products. Conclusive results were, however, not obtained as the grain size of TD-nickel was constant. 5 to II , after recrystallization at temperatures from 700 to 1200°C and as the copper products containing 5 to 1 wt pct of aluminum oxide could not be recrystallized even after severe cold reduction and heat treatment at 1050C. For aluminum aluminum-oxide products containing from 1 to 5 wt pct of aluminum oxide it has been shown that the tensile strength at room temperature decreases when an extruded product is cold-worked and recrystallized. The matrix in the extruded products is divided into well-defined subgrains of micron size, and as the grain size of the recrystallized products is about two orders of magnitude higher, it is obvious that grain boundary strengthening occurs. Preliminary results8 have indicated that the flow stress containing no grain boundaries, A is a constant and t is the subgrain size. At elevated temperatures the effect of boundaries is more complex; it has been shown11 that recrystallized products having an oxide content of about 3 wt pct are more creep resistant than extruded material in the temperature range 400° to 600°C, whereas on application of a higher strain rate the tensile flow stress (0.2 pct offset) is higher in extruded than in recrystallized aluminum—5 wt pct aluminum oxide products at temperatures from room temperature to 427°C (800), Finally it has been shown12 that the Brinell hardness at 350°C of extruded products having about the same content of aluminum oxide increases with decreasing grain size, determined by X-ray line-width measurements. The present study was undertaken to obtain a quantitative relationship between the tensile strength and the grain size of aluminum aluminum-oxide products in the recrystallized as well as in the extruded state. The tensile testing was performed at room temperature and at 400uC. The grain size of the recrystallized products was varied by changing the degree of cold-work preceding the recrystallization heat treatment. In extruded products grain (or subgrain) size variations were obtained by high-temperature heat treatment after extrusion. EXPERIMENTAL a) Materials. Aluminum aluminum-oxide products have been manufactured by consolidation of aluminum powder covered with a layer of aluminum oxide formed during powder manufacturing. The products examined were manufactured from atomized powder containing

Jan 1, 1970

By Thomas C. Wilder, Walter E. Galin

Measurements of the electromotive force of the cell at 995°C have shown that the cell may be used to detennine the zinc content of molten Cu-Zn alloys to the nearest 0.05 wt pct. The cell is used for brass melts to which no ZnO is added intentionally, because essentially all oxygen in the Cu-Zn-O system is present in the form of ZnO. The cell is also used to detev,nine the thernodynamic activity of zinc for Cu-Zn al1oys of the brass composition range, from which the equilibrium partial pressure of zinc for such alloy may also be calculated. The electrochemical measurement of the concentration of the most active metal in other engneering- alloy systems by a similar technique is also considered. IN recent years there have been many studies concerning the direct electrochemical measurement of oxygen content in molten engineering metals.&apos; These investigations employ galvanic cells in which the electrolytes are various solid mixed-oxides which conduct current by movement of oxide ion vacancies under the influence of an oxygen potential gradient. Similar cells have also been used to measure the thermodynamic properties of mixing of solid alloys,&apos; one component of which has a much greater affinity for oxygen than the other component(s). One alloy system of obvious engineering importance comprised of two metals of greatly differing affinity for oxygen is copper-zinc. At the casting temperature of molten brasses, the zinc concentration is very difficult to control not only because its vapor pressure is very high, but also because of its high affinity for oxygen to form ZnO. Inasmuch as brass castings may be required to have a zinc concentration within very narrow limits, it would be advantageous for the brass industry to have a means for quickly measuring the zinc content in the molten alloy just prior to pouring. A calculation based on earlier thermodynamic studies of oxygen and zinc in dilute solution in binary Cu-O and CU-Z&apos; alloys indicates that the oxygen concentration of molten 70 wt pct Cu-30 wt pct Zn brass must be much less than 1 ppm for the separate phase ZnO not to exist in the ternary Cu-Zn-O system. Thus it can be assumed that all molten brasses, both in the laboratory and in the foundry, are sufficiently saturated with oxygen for the separate phase ZnO to be present. In view of the foregoing reasons, the cell investigated at 995°C for the purpose of measuring the zinc concentration in molten copper-zinc alloys, particularly those of brass compositions. In this cell the left hand electrode is a reference electrode comprised of a mixture of the pure powders of nickel and nickel oxide, to which a platinum contact is made. The electrode of interest is a molten Cu-Zn alloy of unknown zinc concentration with a tantalum wire contact. The electrolyte is the commercially available (Zircoa) calcia stabilized zirconia. The ZnO in the Cu-Zn electrode compartment is not intentionally added, but is naturally present as a result of the infinitesimal amount of oxygen required for its formation in this alloy system. In cell [A] nickel oxide is reduced at the cathode where O= represents the electrolyte. At the anode dissolved zinc of the Cu-Zn alloy is oxidized to form ZnO(s) in its standard state Thus the overall reaction is for which the molar free energy change is where 5 is the Faraday equivalent (23,063 cal per v equivalent), is the electromotive force of the cell in volts after correction for the Pt-Ta thermocouple, FOf (ZO) and AFF (NO) are the standard molar free energies of formation of the respective oxides, and a2n is the thermodynamic activity of zinc in the molten Cu-Zn alloy. The reference state of zinc in this case is taken to be the pure liquid. At constant temperature all the terms of Eq. [I] are constant except and azn Thus since all other participants in the electrochemical reaction are in their standard states, the change in the electromotive force of Cell [A] is represented only by a change of the thermodynamic activity of zinc at constant temperature. The zinc concentration is related to the activity by sampling the alloy for chemical analysis after cell measurements are taken. EXPERIMENTAL A typical cell construction is shown in Fig. 1. This and other experimental details were similar to that described earlier with the exception of some minor modifications which are detailed below.

Jan 1, 1970

By G. Sandoz, D. A. Meyn

The fracture surfaces of specimens of titanium a1loys which exhibited susceptibility to subcritical crack growth in a wide variety of environments, including aqueous solutions, alcohols, hydrocarbon gases, carbm tetrachloride, and dry air, were examined. The dominant and characteristic fracture mode was cleavage. which became mixed with an increasing porportion of ductile fracture modes (dimples. and so forth) as the applied KI was increased. The cleavage plane in all the alloys was oriented at 15 deg from (0001) of the a phase. No indices could be assigned to the 15 deg cleavage Plane because of uncertainty as to which zone it belonged to. SLOW crack growth and delayed fracture take place in certain titanium alloys at stress intensity (KI) lower than the critical values for complete fracture (KIc) found in short-time tests for plane strain fracture toughness.&apos; Such crack growth may take place in very dry air on sustained loading if the alloy contains a sufficient amount of hydrogen and if the stress intensity factor is higher than a threshold value designated KIH.2 Similarly, a number of environments such as water, alcohols, and hydrocarbons may cause slow crack growth provided the stress intensity factor exceeds the threshold value KISCC. In this paper it is intended to examine some fracto-graphic and crystallographic details of this subcritical crack propagation process as related to alloy composition, environment, and stress intensity. It has been previously reported that subcritical crack growth takes place in titanium alloys in aqueous environments by cleavage.2"6 The observations to be described here indicate that in the alloys investigated the mode of subcritical crack propagation is more dependent on the stress intensity during cracking than on the environment. The fracture mode is illustrated with photographs of the fracture surfaces at a wide range of magnifications. The crystallographic character of the cleavage mode is also presented and the results discussed. EXPERIMENTAL APPROACH The studies were made on four titanium alloys— Ti-8A1-1Mo-lV, Ti-5A1-2.5Sn, Ti-7Al-1Mo-lV, and Ti-0.350. Of these four alloys the first two were mill annealed and fine grained. The latter two were noncommercial and coarse grained, having been prepared for other experimental purposes. The crystallographic studies required a large-grain size. Consequently the fine-grained alloys were an- nealed in a vacuum at 1950°F and furnace cooled to produce samples for these studies. This treatment did not alter the microstructure significantly except for grain size. All the aluminum-containing alloys showed primary a with a network of ß-phase particles within the a grains; Figs. 1 and 2 show this microstructure for the specific case of fine-grained Ti-8A1-1Mo-1V. The cracks in the figures will be discussed later. Fractographic studies were made on all the alloys, but the electron fractographs displayed herein are from the Ti-8A1-1Mo-1V alloy in the fine-grained condition. Emphasis was placed on this commercial alloy because considerable information was available on the stress-corrosion cracking characteristics in a variety of environments. Sufficient supplementary studies of the alloy after the anneal to produce large grains were conducted to establish that the stress-corrosion cracking susceptibility and fractographic characteristics were not changed significantly. Thus it could be inferred that the crystallographic data obtained exclusively on large-grained specimens would apply also to fine-grained specimens. Fracture surfaces for study were obtained using precracked cantilever beam specimens loaded as described by Brown. The precracked section of a specimen was immersed in the environment of interest. Values of initial stress intensity factor Kli were chosen slightly higher than KISCC in order to obtain a fairly extensive region of slow crack growth. Fracture surfaces representative of a variety of stress intensity levels could then be examined because in the cantilever beam test KI increases as the crack propagates.

Jan 1, 1970

By W. L. Mamme, G. Y. Chin

The problem of selection of the active slip systems for a crystal undergoing an arbitrary strain was analyzed by Taylor and by Bishop and Hill in terms of a minimum (internal) and a maximum (external) work criterion, respectively. These two criteria have now been generalized to include crystallographic slip on several sets of slip systems, twinning mixed with slip, and slip by (noncrystallographic) pencil glide. The generalized treatment also takes into account the possibility of a Bauschinger effect and of unequal hardening among the shear systems, which were considered in the Bishop and Hill work. Optimization techniques of linear and nonlinear programming are shown to be applicable for the numerical calculation of the minimum or maximum work. In the case of crystallographic shear, the constraint functions are linear and hence the optimal work is obtained as the saddle value of the lagrangian function Wi(y) e minimum and W,(u) + (a) for the maximum, where Wi is the (internal) work, We is the (external) work, Y is the crystallographic shear strain, u is the applied stress, and and are constraints. It is shown that the Lagrangians are functionally the same and the saddle value of one problem is identical to the saddle value of the other, proving that the two analyses are completely equivalent. In the case of pencil glide, although the constraint functions are nonlinear and neither convex nor concave, the equivalence of the optimal values to the saddle value of the Lagrangian (which is again identical for both problems) is still valid. WHEN a crystal deforms plastically by crystallographic shear, five independent shears are generally required to accommodate five independent strain components specifying the deformation. Assuming slip as the only shear mechanism, Taylor1 in 1938 analyzed the deformation in terms of a minimum work criterion. He hypothesized that of all combinations of five slip systems which are capable of accommodating the deformation, the active combination is that one for which the internal work C is a minimum, where 1 TI is the critical resolved shear stress for slip on the 1-th slip system and is the corresponding simple shear. By further assuming equal 72 for all equivalent slip systems and no Bauschinger effect, Taylor re- duced the minimum work problem to one of minimum and applied the analysis to the case of axisym- Metric flow by {111}(110) slip in fcc crystals. However, he did not consider the question of whether the resolved shear stress has in fact attained the critical value for slip on the newly found active systems without exceeding it on the inactive systems. In 1951 Bishop and ill&apos; put forth the maximum work analysis in which slip is again assumed as the only deformation mechanism. In this analysis, the work o1 done in a given strain ij by a stress ujj not violating the yield condition is maximized. In addition, the analysis takes into account the possibility that the critical resolved shear stress for slip may not be equal among the slip systems and that the slip behavior may exhibit the Bauschinger effect. As with Taylor, a single set of slip systems—{111)(110) — was analyzed numerically. It thus appears that the Bishop and Hill treatment is on a more sound physical basis than the Taylor treatment. However, Bishop and Hill showed that where there is equal hardening among all slip systems and when there is no Bauschinger effect, Eq. [11 ] of Ref. 2, as assumed by Taylor, the results of their maximum work analysis are the same as those of Taylor&apos;s minimum work analysis. Hence at least under those conditions there is an implication that the Taylor analysis does lead to a critical resolved shear stress for slip on the predicted active systems without violating the yield condition on the inactive systems. Recently, the Taylor analysis was applied for numerical solutions of the axisymmetric flow problem, for slip on {110}(111), {112}(111). {123)(111) systems as well as a mixture of all three sets of svstems."1 Computational techniques based on the optimization theories of linear and nonlinear programming4 were employed in these solutions. The same techniques were employed in the solutions of an axisymmetric flow problem of deformation by slip on (111) (110) systems and twinning on (111)(112) systems5 which had been considered theoretically from a modified Taylor approach. The utilization of these techniques has led to the realization that the solutions of Taylor&apos;s minimum work problem imply the solutions of Bishop and Hill&apos;s maximum work problem. The two problems turn out to be dual problems in the well known sense of mathematical programming. It is thus the purpose of this paper to first generalize the minimum and maximum work analyses to include crystallographic slip on several sets of slip systems, twinning mixed with slip, and slip by (non-crystallographic) pencil glide, as well as the possibility of a Bauschinger effect and of unequal hardening

Jan 1, 1970

By J. Szekely, V. Stanek

Heat and gas flow interactions in nonisothermal packed beds were examined in the paper. A study was made of the response of the system to a step or pulse change in the inlet gas temperature, with a fixed value of the overall pressure drop across the bed. Under these conditions the heat flow and fluid flow transients are coupled because the convective heat transfer rate is alfected by the mass flow rate of the gas which, in turn, for a fixed pressure drop will depend on the temperature profile in the system. The Problem was stated in terms of differential equations, which were integrated numerically. The parameters used in the computation were so chosen to reflect the operation of the stack region of blast furnaces and sinterbeds. The computed results showed that the pressure drop-flou1 relationships and the rate of progress of the temperature fronts (waves) were strongly interrelated and were also markedly affected by variations in particle size and in void fraction. MANY metallurgical processes involve the contact of solid particles with a gas stream in a packed bed arrangement under nonisothermal conditions. Examples are shaft furnaces, regenerators, pebble heaters, and the sinter process. Although the heat and mass transfer aspects of packed bed processing have been extensively studied, the associated flow phenomena and in particular the effects of nonisothermality on the flow, have received little attention to date. :In fact, most of the previous workers considered the flow rate of the carrier gas time invariant and independent of the heat or mass transfer processSzekely and carr2 have shown that the pressure drop-flow relationships in nonisothermal packed beds may be strongly affected by the temperature profile within the system. These authors have devised a method for relating the pressure drop to flow for a given temperature profile. thus providing an extension of the Ergun equation to steady nonisothermal systems. Finally, in a recent paper willmot3 examined the response of regenerators to externally imposed changes in the gas flow rate. Both these investigations were somewhat specialized since, in general, neither the temperature distribution nor the gas flow rate may be regarded as truly independent variables, thus the heat transfer and the fluid flow problems have to be solved simultaneously. The work reported here is divided into two parts: in Part 1 the general formulation is given and a detailed discussion is presented of fixed bed systems. Part is devoted to systems in which a gas and particulate solids are contacted in a counter flow arrangement. FORMULATION Consider a nonisothermal fixed packed bed, extending from through which a gas is flowing. The problem is to develop a relationship between pressure drop and gas flow (with the gas flow being the dependent variable) and to evaluate the rate at which a change in the gas temperature, imposed at the inlet, travels through the system. Let us consider an infinitesimal section of the bed and establish differential heat, mass, and mechanical energy balances over this region. In addition, relationships are needed describing the temperature dependence of gas density (equation of state) and the temperature dependence of viscosity. These may be written as: where c, and are constants. It is noted that in this formulation we neglected any temperature gradients within the solid particles, thus assuming these to be either sufficiently small or of sufficiently high thermal conductivity to meet this condition. The justification and consequences of this assumption will be mentioned in the discussion.

Jan 1, 1970

By J. Szekely, V. Stanek

Steady state heat transfer and fluid flow rates are predicted for the counter-current contacting of gas and solid streams. For a .fixed pressure drop across the bed the convective heat transfer rate is affected by the gas flow rate, which in turn is affected by the temperature distribution in the system. Variations in bed voidage and in particle size were found to change the predicted temperature profiles quite markedly, in particular when the thermal capacities of the gas and solid streams were equal. IN Part I we examined the effect of step and pulse changes in the inlet gas temperature on transients in the flow of gases through fixed packed beds. Here we shall discuss heat flow and fluid flow interactions in the counter-current heat exchange between packed solids and a gas stream. Counter-current heat exchange in packed beds has been extensively studied. In his now classical paper, Furnas&apos; assumed constant property values and developed a simple analytical. expression for the temperature profiles in the gas and in the solid stream. A highly sophisticated analysis of counterflow systems, allowing for transients and interparticle conduction was developed by Amundsen. In preparing a very readable review of this topic Elliott&apos; also presented a number of elegant solutions, including the case involving heat generation. A great deal of work has been done on the application of these concepts to the modelling of the blast furnace. However, in all this previous work the mass flow of the gas was regarded as a quantity independent of the gas-solid heat exchange process. In the following we shall consider counter-current heat exchange between a gas stream and a packed bed of solids, under conditions where the pressure drop across the bed is specified, rather than the mass flow of the gas. FORMULATION Consider a packed bed, extending from y&apos; = 0 to y&apos; = L, in which moving solids and a moving gas are contacted in a counterflow arrangement. Let cold solids, with an initial temperature Tsi and mass flow GA, enter at y&apos; = L, and hot gas with an initial temperature of Tgi and mass flow Gg enter at y&apos; = 0. In contrast to the problems considered in Part I this system has a nontrivial steady state and we shall restrict our attention to the study of the pressure drop flow relationships and the resultant temperature distributions for steady state conditions. Under these conditions the formulation of the problem requires the statement of the following: 1) heat balance on the gas 2) heat balance on the solids 3) the mechanical energy balance equation and in addition the knowledge of the equation of state, and a functional relationship between viscosity and temperature and an expression for the heat transfer coefficient in terms of the other parameters. On neglecting temperature gradients within the solids and for a constant mass flow of the gas, the solution to this problem is well known.&apos;" The expressions for the temperature profiles of the gas and solid streams may be put in the following form: where Tg and T, denote the dimensionless gas and solid temperatures respectively, y is a dimensionless distance, and R is the ratio of the thermal masses. These quantities are defined as follows: For the particular case of equal thermal mass capacities by the gas and the solid, that is R = 1, the Eqs. [1]and[2] simplify to Eqs. (71 and[8], respectively: i.e., the resultant profiles are linear. As for most practical cases , solutions given by Eqs. [7] and [8] will contain only the inlet temperatures as parameters. For a fixed, predetermined value of C;b the above

Jan 1, 1970