Search Documents

By J. F. Smith, J. R. Ogren, N. J. Magnani

The uapor pressrcres of magnesium over binary alloys of magnesium with twelve of the yare-earth eletnetzts have been measured by the Knudsen effuion method in the temperature range 675° to 910°K. These vapor-pressure measurments were combined with data concerning the tevtrlitzul magnesium solubility and the vapor pressure of pure magnesinm to evaluale the standuvd free energies of pluase jormation. These free-etzergy values indicate that the CsCl structures of the heacy rave earths tend to be somewhat less stable than those of the light rare earths. This dif-]eying- behaviov covrelates with differences which have been obsevz~ed in other alloy systetns wherein a phuse appeurs, disappeavs, or changes crystal stvucture as the atomic number of the rare-earth com-ponent is changed. This behauior also appears to correlate with the struclurul rariations within the rare-earth elements themselves, and it is speculated that cariations in the spatial extent of the 4f orbitals are responsihle. STUDIES of the phase relationships and crystal structures in the binary systems between rare-earth metals (lanthanons) and magnesium are extensive but far from complete. However, the currently available information1-10 does produce a rather interesting pattern. This is illustrated in Table I. If one excludes europium and ytterbium from consideration because of their generally atypical behavior, it can be seen from the table that the phase relationships in the magnesium-rich regions show a distinctly different pattern for the lighter lanthanons as compared to the heavier lanthanons. For the lighter lanthanons, LnMg2 phases occur from lanthanum to gadolinium with the cubic MgCu2 structure, LnMg3 phases occur from lanthanum to terbium with the BiLi3 structure, and magnesium-rich phases occur from lanthanum to gadolinium with stoi-chiometries between Ln5Mg42 and LnMg12. In contrast, for the heavier lanthanons, those LnMg2 structures which have been examined have the hexagonal MgZn2 structure, LnMg3 phases have not been observed beyond terbium, and the magnesium-rich phases occur with the a manganese structure near a stoichiometry of Ln5MgZ4. The heavy lanthanon-magnesium systems thus appear to be analogous to the Y-Mg system""2 wherein YMg has the CsCl structure, YMg2 has the MgZn2 structure, and the region Y4Mgz5-Y5Mg24 has the a manganese structure, and no other intermediate phases are observed. Similarity in alloying behavior between yttrium and the heavy lanthanons occurs commonly, and on this basis it seems likely that LnMg2 phases will be found with the MgZn2 structure in the binary systems of dysprosium, thulium, and lutetium with magnesium when the appropriate investigations are made. In the case of the magnesium-rich phases of the lighter lanthanons, only the Ce-Mg phase relationships have been investigated thoroughly and in detail, and until similar investigations are made for the other systems there will remain questions as to which magnesium-rich stoichiometries represent equilibrium phases and what systematic variations occur in the sequence from lanthanum to gadolinium. Thus the data in Table I show that only the LnMg phases occur with the same crystallographic structure throughout the sequence from lanthanum to lutetium. It was speculated that the relative stability of these LnMg phases might vary from one lanthanon to the next in such a way as to presage the differences which occur among the more magnesium-rich lanthanon-magnesium phases. On this basis the present investigation of the thermodynamics of phase formation was Gndertaken for the LnMg phases. PROCEDURE AND RESULTS A generalized phase diagram for the lanthanon-rich portion of a lanthanon-magnesium alloy system is shown in Fig. 1 where ß represents a high-temperature bcc

Jan 1, 1968

By R. Kossowsky

Structural changes in Be-Cu, Be-Ni. Be - Ag, and Be-Fc alloys pressurized in a solid medium were invesligated by resistivity measurements , X-ray diffrac lion in situ and metallogvaphic examination. Some limited tests in liquid medium were also conducted. Good correlation was oblained between diauges of slope of relative resistance us pressure and changes in diffraction pattern. Metallographic examination rez:ealed that the copper, silver, and nickel alloys lwiu heauily due to the applicalion of pressure at room temperature. Using polarized light technique {1012}, {1011}, and possible {1010} twinning planes were identified. At eleuated temperature twinning was moslly confined to the {1012} planes. Although twin-ning could be promoted by application of hydroslutic pvessure (liquid medium), it was strongly enhanced by the pvesence of a nonhydvostatic shear component due to pressurizalion in a solid medium. It was further obserced that a decrease in grain size inlnibiled twinnitzg activily. A great deal of effort has been expended in recent years to render beryllium useful for structural applications. Efforts were concentrated towards a possible phase change and to promoting other than basal deformation modes. Quenching experiments to obtain the high-temperature bcc phase have failed,' nor were alloying additions successful in improving ductility of the brittle hcp phase.2 Herman et a1.3 have reported a new {1011} twinning mode in a Be-4.4 wt pct Cu alloy oriented for a C axis compression sustaining loads to 440,000 psi. A new approach using high-pressure techniques was undertaken at Curtiss-Wright, Wright Aeronautical Division Laboratories. Marder4 reported a 25 pct decrease in relative resistance of commercially pure beryllium at 92 kbar. He proposed that this discontinuity corresponded to the bcc phase found at high temperature; however, X-ray diffraction in silu did not confirm a phase transition.5 contre6 has recently shown that the bcc transition in pure beryllium is lowered to 800°C at 80 kbar accompanied by a 50 pct increase in relative resistance. The purpose of this paper is to report on one phase of an investigation of the effects of high pressures and temperatures in beryllium alloys, namely, twinning behavior in Be-Ni, Be-Cu, Be-Fe, and Be-Ag alloys pressurized to nearly 100 kbar and temperatures up to 200°C. EXPERIMENTAL METHODS Material was obtained from Nuclear Metals, Inc., in the form of a 1.5-mm-diam wire extruded in stainless-steel cladding at 1600° F. Nominal composition of the alloys is listed in Table I, and the major impurities are are given in Table 11. Pressures to 100 kbar* were ob- tained using a National Bureau of Standards type 100/400 ton tetrahedral unit supplied by Barogenics, Inc. This type of apparatus contains a retaining sleeve with a conically tapered internal surface and four pressure-intensifying anvil assemblies with tungsten carbide tips. The 10-mm-long specimen fits into a pyro-

Jan 1, 1968

By K. A. Gschneidner, O. D. McMasters

DgIel-ential thermal, nretallographic, and X-ray paramzetric methods were used to establish the Yb-Pb phase dingram. The terminal solid solubilities in the system are less than 0.2 at. pct. Lead additions lower the 792°C transformation tewzperature of pure ytterbiun~ at 787°C by means of an inverted peritectic veaction. Ytterbium additions raise the 327oC melting point of lead to 329°C by means of a perilectic reaction. Three intermetallic compounds Yb2Pb, YbPb, and YbPb, melt congruerttly at 1246", 1116o, and 740°C. respectively. YbsPb3 forms by a peritectic reacliorz at 1250°C. YbzPb crystallizes in the PbCh (C23) type structure and the orthorhombic latliceo constants are a, = 7.478. bo = 5.225, aud C0 = 9.549A. YbsPbs crystallizes in the hfnsSi3 (D8a) type structure. The hexa~nal lattice constants for this phase are a, = 9.325 and co = 6.92d. YbPbl crystallizes in the cubic AuCU3 (Ll2) type structure with a: = 4.8628 + 0.0008A. YbPb is diwrorphic with the structure change occurring al 507°C upon healing. The crystal structures of the two forttzs were not determined. Eulectic reactions occur at 5.1 at. pct Pb and 769oC, 41.5 at. pct Pb and 1086oC, and G8.0 at. pct Ph and 717°C: RELIABLE information concerning the alloying behavior of most of the rare-earth metals is scarce. A systematic study of the rare earth-lead alloy systems now in progress is an effort to supply such information. Determination of the phase diagram of the Yb-Pb alloys is the first step of this study. Variations in the valence of normally divalent ytterbium may be studied by comparing the characteristics of the Yb-Pb alloys to those of the trivalent rare earth-lead and of the divalent alkaline-earth-lead systems. Of particular interest are the melting temperatures of the intermetal-lic compounds since these are known to be high relative to the melting points of the constituent metals. Crys-tallographic and magnetic susceptibility data for the rare earth-lead alloys are to be included in the comparative study. Results from this and subsequent investigations should provide a better understanding of alloy formation. EXPERIMENTAL PROCEDURE Materials. The major impurities in the ytterbium and lead used in this investigation are listed in Table I. The lead was obtained from Cominco Products, Inc., and was specified to be 99.99 pct pure. The ytterbium was prepared in this laboratory by the lanthanum reduction of the oxide followed by a distillation of the ytterbium. Alloy Preparation. The alloys were prepared by

Jan 1, 1968

By O. Hoover, M. Herman, V. V. Damiano

The Jetter and borie' teclznique of determining textures using a spherical specimen has been applied to tlze study of compression-rolled beryllium sheet. Snzall spheres the order of 1 mm in diam cut from the beryllium sheet were autotnatically rotated about tz41o axes using the G.E. single-crystal goniometer. Quantitative pole figures were obtained without tke need to apply absorption corrections. Compression-rolled beryllium exhibited peak intensities ,for (0002) planes of positions tilted 10 deg to the rolling plane and a near random distribution of (1010) planes about the nornal to the rolling plane. TECHNIQUES for determining textures of rolled sheet material are amply described in the literature. The techniques are found to be variations of two basic methods. One due to Decker, Asp, and arker, referred to as the transmission method, utilizes a thin-sheet specimen in which the X-ray beam enters the specimen from one side and the intensity of the beam which emerges from the opposite side is measured. The second method due to chulz,3 referred to as the reflection method, utilizes a thick specimen and the intensity of the beam emerging from the same side is measured. The two rotations of the specimen in the beam are designated a and 8. In order to completely determine the texture of sheet material, it is generally necessary to use a combination of the two methods. The calculations involved in correcting the raw X-ray data for absorption effects and the combining of the data obtained by the two methods are very laborious and time consuming. To avoid the intensity corrections which arise as a result of the changing diffraction volume and path length within the sample other methods have been proposed. The Norton method utilizes a cylindrically shaped specimen cut from the sheet material. Since the rods have rotational symmetry, the absorption correction is constant for rotations about the sheet texture. Jetter and Borie' employed a spherical specimen to analyze the fiber texture of extruded aluminum rods. The spheres were rotated rapidly about the fiber axis to include a large number of grains in the X-ray beam and changes in intensity with respect to tilts of the fiber axis were measured. The absorption correction was constant for all angles and was neglected. The Jetter and Borie' technique finds excellent ap- plication to very fine-grained low-absorbing metals in which the entire sphere volume can contribute to the diffraction volume. In the case of low-absorbing metals, however, serious limitations on specimen thickness occur as demonstrated by Braggs due to de-focussing effects. Peak shifts may occur which negate the assumption that integrated intensities are proportional to peak intensities. These limitations in sphere size to the order of 0.5 to 1 mm for beryllium require that the grain size be sufficiently small to include a large enough statistical sample. The present paper describes the application of spherical specimens less than 1 mm in diam to the quantitative determination of pole figures for compression-rolled beryllium sheet having a grain size the order of 10 p. EXPERIMENTAL 1) Specimen Preparation. Two techniques for spark-machining beryllium spheres were tried. One involved the use of a hollow cylinder as a cutting tool. The tool was fed into the rotating cylindrical specimen as shown in Fig. l(a). The hollow cylinder was carefully aligned such that the axis of the cylinder and the axis of the specimen lay in the same plane and were 90 deg to each other. As the hollow cylinder was fed into the rotating cylindrical specimen, a spherical shape was formed as shown in Fig. 1. Alignment was very critical. Slight misalignment resulted in the formation of a barrel-shaped specimen instead of a sphere. A second technique involved the use of a cutting wheel shaped as shown in Fig. 2 with a groove of the desired radius. A section of the sheet specimen was first turned into a cylinder on the left part of the cutting wheel. It was then shifted to the right and a spherical specimen was turned as shown in Fig. 2. The axis of the cylinder lay in the plane of the sheet. Flats corresponding to the rolling plane of the sheet were used to grip the specimen during the machining operation and these served to identify the rolling plane of the sphere. 2) Rotation of Spec=. The spherical specimen is shown mounted on the G.E. single-crystal goniometer in Fig. 3. The knob A of the goniometer shown in Fig. 3 rotates the specimen about the pedestal axis. These angles have been designated as @ angles. The knob B rotates the specimen about an axis perpendicular to the pedestal axis. These angles have been designated as p angles. A device was made to automatically drive the single-crystal goniometer by means of two flexible shafts connected to the A and B knobs as shown in Fig. 3. The motor system was designed to rotate the knob A, thus rotating the specimen through angles of $I while the B knob remained stationary. After one complete

Jan 1, 1967

By E. H. Rennhack

When cast hypoeutectic Zn-Ti alloys are rolled, the TiZn15 compound particles arising from eutectic decomposition form a network of fibers promoting improved creep resistance.' The effect is magnified with increasing titanium content and extends to hy-pereutectic concentrations. Strip produced from the latter-type alloys, however, also contains large, primary crystals of the compound that tend to initiate cracking during subsequent fabrication operations. In a study of the influence of various casting modifications on the size and distribution of these crystals, the phase relationships existing between the eutectic and the TiZnIs intermetallic compound in the Zn-Ti system were of major interest. Although several in- vestigators1 4 have explored the equilibria within this compositional range, their results show considerable lack of agreement. Consequently, with the exception of the solvus boundary, the constitution of this system containing up to approximately 1.0 wt pct Ti was . The findings are reported in the present note.

Jan 1, 1967

By E. Miller, K. L. Komarek

Equatiorzs have been derived which related maximum solid solubilities in semicondcting compounds having retvograde solidus curves with 1iqllidus data. Liquidus curves in Lke Pb-Te, Pb-Se, ard PB-S systetris have been defermined by thertrzal aralyses. Fvotrz expevimental maximum solibilities ia CdTe, PbTe, uxd PbS vetvograde tetrperatures hale beep1 calculated. TIze resllts support the concept that under certaiz conditiots pronounced itjlections in the liquidis curves arc indzcatiz:e of retropade solidus curves and that the tenlperatltre of the lmaximum solid solubility will be close to the temperature of the point of inflection in the liquidus curve. The maximum solid solihility within a gvoup of homologous cottrpoods SeetlLs to increase with increasing flatness ol the liquidus curvres. The phenomenon of retrograde solubility in metals, i.e., maximum solubility in a solid terminal phase in equilibrium with a liquid phase, has been theoretically predicted by Van aar' in his calculations of hypothetical binary phase diagrams. It was not until 1926, however, that retrograde solubility was experimentally verified in the Zn-Cd system.' Since then many sys- tems with retrograde solubility have been found, so that at present approximately fifty binary diagrams with a retrograde solidus curve are known.3 Meijering4 has critically appraised the accumulated data and has presented calculations which alloy predictions as to whether or not a solidus line will be retrograde. Interest in retrograde solubility increased when it was found that the solidus curves of germanium and silicon alloyed with a great many doping elements are retrrade. The problem was treated thermody-namically by odkinson,% d all available data on solid solutions in germanium and silicon were summarized by Trumbore.7 Although it is to be expected that intermetallic compounds will also exhibit retrograde solubility, experimental evidence is much more limited. Until now retrograde solidus curves have been reported for the compounds de,' be, Ps:" ne," SnSe," and SnS.13 All these compounds are semiconductors, and the solidus curves were usually obtained by determining the carrier concentration at room temperature of samples equilibrated at elevated temperatures and then quenched. It has been hown,'' however, that it is not always possible to quench in the equilibrium compositions from above a certain temperature. Theoretical discussions have either explicitly excluded intermetallic compounds4 or not treated them with respect to retrograde slubilit.j In the following a thermodynamic treatment of retrograde solu-

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By G. L. Fisher, R. Maddin

The rate of self-diffusion in silver single crystals during torsional strain was measured over a wide range of tenperatures and strain rates. The torsional strain was applied in a cyclic manner by reversing the divection of twist aftev a certain fraction of the total strain was reached. Surface roughening was substantially reduced in cyclically strained specimens compared with those strained entirely in one direction. Diffusion coefficients were determined using a special sectioning technique whereby slices could be removed parallel to the surface of a strained torsion specimen. The accuracy of the technique was first determined using roughened specinzens statically diffused to various penetration depths. Simultaneous strain-diffusion experiments were then performed over the temperature range 550' to 800 using strain rates of lo-' to 2.2 x 10' sec-'. The increase in silver self-diffusivity during torsional plastic strain was small. In only one case was the enhancement greater than twice the static value of the diffusion coefficzent. The enhancements increased slightly with decreasing tenzperature and increased with increasing strain rate. A dislocation pipe mechanism of enhancement was found to explain the present results satisfactorily. The magnitude of the enhancements and the tenzperatures at which they were observed suggests that a steady-state dislocation density of 10' to 109 dislocations cm-2 existed during the high-tempevature deformation. The diffusion coefficient in an fcc metal can be increased by 1) an excess concentration of point defects and 2) the rapid movement of diffusing atoms along grain boundaries and dislocations. Plastic deformation may be responsible for enhancements by both of these mechanisms. The results of simultaneous strain-diffusion experiments have caused a controversy over the magnitude of the effect of strain upon diffusion. Experiments reporting large enhancements have been criticized for the manner in which the diffusion coefficient was measured. Several of these experiments have been contradicted by other results obtained in a similar manner. No enhancement was reported by two investigators''' who performed their experiments at high temperatures where strain is expected to have little effect upon diffusion. A recent theoretical analysis3 indicates that strain enhancement by a vacancy mechanism will be small and exist only at low temperatures and rapid strain rates. It is doubtful whether any experiment has yet proven that strain enhancements can occur by an excess vacancy mechanism. In the present research, experiments were performed at extremes of temperature and strain rate in an attempt to measure enhancement of diffusion by strain. Self-diffusion of silver during torsional deformation was chosen since two separate investigations4j5 indicate that at least a small enhancement exists under these conditions. An accurate method of determining the diffusion coefficient, mechanical sectioning, was employed after a technique was devised to apply it to the roughened surface of a strained torsion specimen. First, the accuracy of the technique was determined for different penetrations (2fi). Then diffusion experiments were performed at temperatures between 550" and 800°C at strain rates of 10"" to 10"" per sec. I) EXPERIMENTAL PROCEDURE Preparation of Specimens. The experimental procedure detailing the growth of crystals, their treatment, and the annealing techniques during straining are contained in earlier publications.496 The dimensions and orientations of the torsion specimens are shown in Figs. 1 and 2. licatiin of Torsional Strain. The torsion procedure was changed from that used previously. The specimens were strained in cycles to reduce the gross distortion and surface roughening inherent in twisting to high strains in one direction. For all strains above 0.30, the total surface strain was obtained as follows: the specimen was twisted to 0.10 strain in a clockwise direction; the direction was reversed; the backlash in the torsion apparatus was taken up; and the specimen was twisted in a counterclockwise direction through the initial starting point to 0.20 surface shear strain in the opposite direction. The strain reversal took no more than 1 min to accomplish. The total accumulated surface shear strain was arbitrarily taken as the sum of the 0.10 strain in the clockwise direction plus 0.20 in the counterclockwise direction. Although cyclic torsional strain was beneficial, surface roughening and specimen distortion were not entirely eliminated. The variation in the diameter at various points on the specimen was often much greater than the depth of the diffusion zone. Since serious errors might result if specimens were sectioned in the usual manner, a technique of lathe sectioning was devised to allow sections to be taken parallel to planes of equal concentration.

Jan 1, 1967

By C. G. Dunn

This note describes a method for revealing micro-structures in tantalum through an {hkl} effect which was found during a study involving amorphous and crystalline tantalum oxides. Three steps are involved. First, an amorphous film of Ta2O5 is formed anodically1 on the surfaces of the tantalum. The amount needed depents on the thickness of the substrate tantalum; 1600Å of oxide, however, is generally satisfactory in the 1/2 -mil (12 µ) to 3-mil thickness range. The film at this point is uniform in color. Second, the anodized specimen is heated to 800°C in. vacuo during a period of a few minutes and held at temperature for 5 min. During such a treatment some oxygen leaves the oxide through dissolution into the substrate tantalum (e.g., at 10-8 Torr oxide films thinner than about 800 completely disappear on 5-mil strip). Considerable crystallization of the amorphous oxide also occurs adjacent to the metal/oxide interface but not throughout the oxide thickness. The thickness of oxide needed as a residue is not too critical; values between 500 and 1000Å (optical estimate') may be most useful. (The presence of a residual oxide layer after the heat treatment usually is not apparent; in fact, in most instances the surfaces have a metallic appearance. This can be the case also for thicker residual films needed in the detection of a crystalline oxide phase by surface X-ray diffraction—e.g., if the initial oxide film is 3000Å thick, enough crystalline oxide is formed for X-ray detection.) The third step eliminates the metallic appearance at the surface and reveals (or produces) a varied colored film of tantalum oxide. Two methods can be used and both will be illustrated. If the specimen is dipped in 48 pct HF for a few seconds, the tantalum is found to be covered with a multicolored oxide. Moreover the colors correlate with the grain structure of the substrate tantalum through an orientation dependence of the type illustrated in Fig. 1, where results of an orientation analysis by the Laue X-ray method have been plotted. Other film conditions would have provided a different set of colors for the same orientations. Any such correlation, however, provides a basis for a qualitative assessment of the distribution of orientations in a large sample. The cold-rolled structure of tantalum foil produced by a recrystallization anneal and a cold-rolling reduction of 95 pct is not easily obtained by usual metal-lographic methods.' The structure, however, is easily revealed by the present technique, Fig. 2. The alternative third step is to reanodize the specimen. The optical nature of the final anodic film depends on the presence of the crystalline oxide phase; color variations indicate optical thickness variations in the film. As the reanodization voltage is increased from zero, straw and light brown colors appear (as usual), followed now by variations in color from grain to grain depending on {hkl} orientation. Suitable end points, which are determined by voltage and time, are easily established. Fig. 3, for example, shows the grain structure developed in 5-mil tantalum strip during a 30-min re-crystallization and grap-growth anneal at 1800°C. An anodic film of 1600Å thickness was added prior to the special 800°C anneal. Reanodization was done at constant current density (near 0.2 ma per sq cm) in an aqueous solution of H3PO4 (0.01 pct) and was terminated after the initial brown colors were replaced by a deep blue at approximately 30 v. Although good grain contrast can be obtained with bright field illumination, even greater contrast for black and white micrographs may be obtained with polarized light, as in Fig. 3.

Jan 1, 1967

By S. J. Rothman, J. J. Hines, D. Rokop, R. Bastar

Self-diffusion has been measured along each principal axis of mosaic-structured and relatively perfect a uvaniuln single crystals. The anisotropy reported before,' D[loo] = D[001] » D[010 , has been confirmed. and is shown to represent volume diffusion. Diffusion along the dislocations in the imperfect crystals increases the measured value of D significantly without changingr either the shapes of the penetvation plots or the anisotropy. SINCE a uranium is orthorhombic, the diffusion coefficients along the principal crystallographic axes need not be equal. A previous measurement of self-diffusion in three mosaic-structured a uranium single crystals1 showed that Dil00| =D[001 >>D[010 This result was deduced from penetration plots similar to those in Fig. 1. That is, the plots for diffusion along [loo] and [001] were the straight lines expected from the solution of the diffusion equation for the boundary and initial conditions of the experiment, while the plot for diffusion along [010] was curved so that the part near X = 0 had a much steeper slope than the straight lines did. The observed anisotropy could have been due either to volume diffusion or to diffusion along the very large number of dislocations in such crystals, according to the model proposed by aart.' The authors of Ref. 1 argued that the latter possibility was unlikely, but did not exclude it. To settle the question, a simultaneous measurement of self-diffusion in mosaic-structured and mosaic-free crystals was carried out. This paper reports the results, as well as a measurement of the temperature dependence of self-diffusion in a uranium. EXPERIMENTAL The single crystals of a uranium used in this experiment are listed in Table I, together with other experimental details. '(Mosaic structured" here means crystals grown by solid-state phase change.3 The Laue spots from such crystals spread over about 6 deg of arc, which indicates that the density of dislocations is very large. "Perfect" crystals are ones grown by Fisher's grain-coarsening tehnique; the Laue spots from these are quite sharp,4 which shows that the dislocation density in these crystals is much lower. All of the crystals were made from high-purity uranium; a typical analysis is given in Ref. 1. The actual diffusion directions were within a few degrees of the nominal. The thin layer-sectioning method was used. The experimental techniques were similar to those described in Ref. 1, except the sectioning. Crystals Za, 2b, 2c, 4a, 4b, and 4c were sectioned on a lathe. Crystals 3a, 3b, and 3c were sectioned by grinding on glass plates, with 1 p diamond powder in butyl alcohol as the abrasive. The use of glass plates eliminated the crowning noted in Ref. 1, and the use of butyl alcohol as a lubricant simplified the chemical processing of the sections. Material from the sides of these three crystals was removed by spark machining before sectioning. The sectioning of crystals 4a and 4c was botched. A small cylinder of metal was extruded from the center of crystal 4a while turning off material from the side of the sample. Crystal 4c was misaligned by 2.1 x 10"3 cm because the dial gage jammed during the alignment. Notwithstanding these errors, useful data were still obtained from these crystals. The points

Jan 1, 1967

By O. J. Kensok

THE literature contains three previous studies of the chemical activities of Cd-Mg alloys: Trumbore, Wallace, and craigl obtained chemical activities of magnesium at 543" by performing electromotive-force measurements; Borg and irchenall calculated activities at 590°K based on vapor-pressure measurements of cadmium over Mg-Cd alloys by the Knud-sen effusion method; and Terpilouski and arcka measured the chemical activities of magnesium in the liquid state by means of electromotive-force measurements. In this study the vapor pressure of cadmium was determined over nine solid Cd-Mg alloys in the temperature range 571" to 697°K by the Knudsen effusion method. This study was prompted by the lack of precision in the data reported by Borg and Birchenall. Knudsen cells used during this study were fabricated from 0.020-in.-thick tantalum tubing. The tops and bottoms of the cells were cut from 0.010-in.-thick tantalum sheet, press-fitted, and welded in place. The orifice was drilled in the cell top and subsequently reamed to a knife-edge thickness. The diameter of the orifice was measured with a traveling microscope capable of reading 0.0001 cm. The sample was heated by means of a resistance

Jan 1, 1967

By Charles E. Lundin, Albert S. Yamamoto

The phase eqrtilibria of the binavy system, Nb-Al, weye established by metallographic, X-ray diffraction, hardness, and thermal-analysis techniques. Three intermediate phases were identijied, Nb3.41, Nb2Al, and NbAl,. The N6,Al and NbAl phases have extensiue ranges of solubility. The maximum solubility of aluminum in niobiuitz is 23.0 i0.5 at. pct (8.0 wt pct) A1 clt 1960" i 10°C. The maximumt solinbility oj niobiunz in alunzinutz is less than 0.3 i0.1 at. pct (1.0 tut pct) fib. The A'h,Al and Nbgl interinediate phases forr peritectically at 1960° 1UcC and 1870" i 1U9C, respectively, zuhereas the NbAl, phase fornts congvuently fio11t the melt at 1605" 10°C. A eutectic reaction oc- The intent of an over-all research program was to develop niobium-aluminide-base coatings for refractory metals since these coatings exhibit useful high- curs at 57.8 i 0.5 at. pct (28.5 wt pet) A1 and 1500" 10°C between NbAl and NbAl3. The aluminum-rich region of the system has a peritectic reaction where liquid reacts with NbAL, to form aluminum solid solution. Structural and lattice -pavarneter data /or the intermediate phases were determined by X-ray diffraction analyses. An unusual transfov?nation having charactevistics of nucleation-growth and martensitic nleclanisils occurs on cooling the niobium solid solution in the region from 18 at. pct (6 wt pct) Al to 23 at. pct (8 wt pct) Al. The transfornzed product on rapid quenchirzg is an acicular NhAl. temperature resistance to oxidation. As a prerequisite, the phase equilibria of the system, Nb-A1, were necessary. A literature survey revealed that the phase-equilibria data reported by various investigators were rather incomplete and conflicting. Therefore a complete determination of the system was undertaken by the authors from 0 to 100 pct of solute addition.' In 1959 Savitskiyz presented a tentative diagram which

Jan 1, 1967

By J. E. Pavlick, W. W. Mullins, H. W. Paxton

The growth of nitrogen-austenite during nitriding of large-gvained ferrite between 650" and 800°C has been studied as a functimz oJ time and nitrogen potential of the atmosphere for a variety of alloying elements dissolved in the ferrite. Whereas no preferential grain boundary penetration by aistenite takes place in zone-refined iron, the addition of aboit I zot pct oj' V, Ti, Cr. Si, or A1 produces significant protrusion of austenite down former 0-0 boundaries. This group of elernents also produces ragged y-0 interfaces in the a grains which advance more slozuly than those in zone-refined iron. 1 zut pct of Ni, Co, Mn, or Mo dissolved in ferrite leads to essentially smooth 7-a interfaces, which advance at rates very sinzilar to those in zone-refined iron. The reasons for this effect are not clear. Two possible limiting hypotheses, not necessarily exclusive, are discussed. One involves p.referentia1 grain bozindary diffusion of nitrogen. the other the production of a zone of ferrite, stpersatcirated with respect to nitrogen, from which austenite precipitates helerogeneozisly on the a-a gyain boundaries. In many phase transformations which occur by nu-cleation and diffusion-controlled growth, information on the parameters which control the rates of nuclea-tion and of growth is frequently not quantititative. The present work describes a continuation of efforts to obtain quantitative data on growth rates in systems where thermodynamic and kinetic factors are known independently, and thus where comparison with models of the growth process is possible. The work has been conducted on iron-base systems for two reasons. Firstly, there are several interesting transformations in this system, many of which are of practical importance. Secondly, the information on phase diagrams, activities, and diffusion coefficients is more complete in this system than in any other. These data are still inadequate to check all the effects of alloying elements, but at worst it is possible to make estimates and thus examine order-of-magni-tude agreement with proposed models. It will be necessary to do this in the present work. The problem studied was the growth of nitrogen-austenite in from the surface of large-grained columnar crystals of alloyed ferrite exposed to an NHs/Hz atmosphere. Earlier work by Grozier et al.' had suggested that growth of austenite may occur preferentially along grain boundaries of alloyed ferrite, whereas zone-refined (ZR) iron shows no such effect, Fig. 1. Growth of nitrogen-austenite into single crystals of zone-refined ferrite is planar provided sufficient nu-cleation sites for austenite are present, and is controlled by volume diffusion of nitrogen through the

Jan 1, 1967

By P. M. Robinson, J. S. LI. Leach

The heats of solution oj' indiurrr, tin, lend, nrzd tellurium have been calculated from the measured heat effects when mechanical mixtres of indium and telLuium tin and tellurium, and lead and tellurium were added to liquid bismuth. The results are in good agreement xith publislzed values.s for the separate sollction of each eleltzent in bismuth. The heats oj solution of cadmium and tellurium calculated from the rneasuved heat effects on adding trechanical mixtures of these elements do not ugree zc,itl the published values jbv the separate solution of each element. It is shown that at 623°K Ile interaction between cadmium and tellurium dissolved in liquid bismuth is strong enough to led lo preciPitation of solid CdTc. The heats oj- jor-mation of CdTe at 273" nd 623°K (1)-c crilculated fi-or the measured heat ejlfecls. The calcnlaled az'erage deviation from the Kopp-l\'ez?,zunrz rule fov solid CdTe is less than 0.06 cat per g-atom- C over this lertzperalure range. Tlze importance 0.f these oDserl.ations to the determination of heals of formation hy metal solution calorimetry is considered. LIQUID metal solution calorimetry is a convenient method for determining the heats of formation of solid compounds. In this technique the heat of formation is the difference between the measured heat effects on dissolution of the compounds and of mechanical mixtures of the components in the liquid metal.' The heat of solution of the mechanical mixture may be calculated from the measured heat effect. At infinite dilution of the solutes, this heat of solution is equal to the sum of the heats of solution of the separate components. If the heat of solution of one of the components is known, the value for the other can be derived; if both are known, they may be used to check the accuracy of the calorimetric technique. The heats of formation of the tellurides of cadmium, indium, tin, and lead have recently been measured by metal solution alorimetr. The heats of solution of indium, tin, lead, and tellurium at infinite dilution in liquid bismuth at 623"K, calculated from the measured heat effects on solution of the mechanical mixtures, are in good agreement with the published values. The heats of solution of cadmium and of tellurium calculated from the measured heat effect on solution in bismuth at 623'K of mechanical mixtures of cadmium and tellurium, however, do not agree with values estimated from the literature. 1) EXPERIMENTAL PROCEDURE AND RESULTS The Heats of Solution of Indium, Tin, Lead, and Tellurium in Bismuth. The heat effects were measured when mechanical mixtures corresponding to the compounds In,Te, InTe, In2Te3, In2Te5, SnTe, and PbTe were dissolved in bismuth. The calorimetric procedure and the method of calculation have been described elsewhere.' The heats of solution of the mechanical mixtures were obtained by subtracting the change in heat content per gram-atom of the sample between the addition temperature (273°K) and the bath temperature (623"K), (H623°K - H273°K)S, from the measured heat effects. The calorimeter was calibrated with pure bismuth. The reported values of the measured heat effects are based on (HGoK - ^273oK)Bi = 4.96 kcal per g-atom.3 The measured heat effects are found to be linear functions of the solute concentrations of the bath in the dilute solution range. The values, extrapolated to infinite dilution, are listed in Table I, together with the heats of solution of the mechanical mixtures calculated using the published values of (H 623°K - H273°k)s for indium, tin, lead,3 and tellrium. All the error limits quoted in this work represent the spread of values obtained. The heats of solution in liquid bismuth at 623°K of mechanical mixtures of indium and tellurium in four different proportions were determined. Values of the heats of solution of the two components were then calculated from the resulting four simultaneous equations: The heats of solution at infinite dilution of tin and lead in liquid bismuth at 623°K were calculated from the heats of solution of the mechanical mixtures of tin and tellurium and of lead and tellurium using the heat of solution of tellurium calculated above. These values of the heats of solution are listed in Table I1 together with some published values for comparison.

Jan 1, 1967

By J. W. Spretnak, V. Kandarpa, G. W. Powell, R. A. Erickson

Neutron-diffraction pattens were obtained at room temperature from two austenitic manganese steels, oxc wth n carbon content of 1.23 zct PC/ and the olher 0.63 wt pct. Analysis of the data showed that the curOan atols (ions) occupy tile octaheadral site. any of the cavbon is in the tetahedral site, tile concentration is too strzall lo be detecled by tzeulr-on d$facton. AS part of a long-range investigation of eutectoid decomposition, a study of the structure of austenite has been undertaken in order to characterize as best as possible the parent phase in the Fe-C system. Austenite is a solid solution of carbon atoms in fcc iron, the carbon atoms being located in interstitial positions. Of the two kinds of interstitial sites, octahedral (0, +, +) and tetrahedral (4, a, $), in this lattice, the larger octahedral sites are usually considered as the probable position of carbon. The strain energy involved in pytting a neutral carbon atom (covalent di; ameter 1.54)' into a tetrahedral site (diameter 0.56A) is considerably greater than that associated with p2tting carbon into the octahedral site (diameter 1.08A). Dayal and arkeen' observed the migration of carbon in iron under the influence of an electric field indicating tha tye carbon is ionized. pe ionic radius of C'4 is 0.15A and that of C" is 0.29. Consequently, it is conceivable that carbon ions could occupy the tetrahedral sites if one considers only the strain energy. Size considerations alone do not provide a complete explanation for the formation of the interstitial solid solutions, however. because metals such as copper, zinc, and cadmium do not appear to form interstitial solid solutions in spite of their large interstitial sites. Evidence which suggests partial ioni-zation of the carbon in austenite has also been obtained by Speiser, Spretnak, and alor who derived formu- lae relating the observed change in lattice parameter to the effective diameter of the solute atom. Assuming the carbon occupies the octahedral site. they computed the effective diameter of carbon to be 1.33A whereas the covalent diameter is 1.54A. petch5 concluded from powder X-ray diffraction experiments that carbon atoms occupy the octahedral sites. His conclusion was based on the general trend observed in the intensity of the diffraction lines as the carbon content of the austenite was increased. However, the major difficulty associated with application of X-ray diffraction to this particular problem is the relatively poor scattering power of carbon. Williamson and smallman' utilized X-ray diffraction to study the line broadening caused by the strain field about carbon atoms inferrite: these investigators concluded that at least 85 pct of the carbon in ferrite occupies the octahedral (0: 3, B) site rather than the larger

Jan 1, 1967

By Donald B. Hunter

The Ti-Be system up lo 10 wt pct Be with cortlmercialll' pure titanium has been determined using metal-lographic techniques. Beryllium forms the p eutec-toid type of dinqarz with titanium; the eutectoid occurs at 0.5 xt pct Be azd 1500 F, while an eutectic is foritled at 1887°F containing between 5 and 7.5 rt pct Be. The solubility of beryllium in a titanium does not exceed 0.05 zvt pct and the maximum solubility of Beryllim in 0 titanium is 1 wt pet. PREVIOUS work on the Ti-Be phase diagram indicated that additions of beryllium to titanium resulted in a marked lowering of the melting point,''' and it was also observed that the solubility of beryllium in both a and p titanium was retricted.- With the limited data available, McQuillan and McQuillan constructed a partial hypothetical diagram of the Ti-Be system,= assuming that beryllium formed the 0 eutectoid type of system with titanium. Subsequently Bedford published a tentative diagram of the entire Ti-Be system: although he did not investigate alloys containing less than 10 wt pct Be. This diagram included several compounds described by other authorities.'-l3 The following account describes work directed toward determining the form of the titanium-rich portion of the phase diagram up to 10 wt pct Be. MATERIALS AND METHODS Titanium sponge and a master alloy containing 25 wt pct Be were used in the formulation of the alloys; the chemistry of these materials is detailed in Table I. The alloys were prepared as 250-g compacts which were melted into buttons by arc melting under purified argon on a water-cooled copper hearth. Results of analyses for beryllium are shown in Table I but no determination of other elements was made at this stage. The alloys were hot-rolled at 1650°F to produce 0.1-in.-thick sheet. Alloys containing up to 1.5 pct Be were fabricated without trouble; samples containing 2 pct cracked initially upon hot rolling, but thereafter rolled satisfactorily to sheet. The 5, 7.5, and 10 pct were hot short and could not be rolled. Surface contamination was removed from samples by sandblasting and pickling in a 5 pct HF-35 pct HNOs solution. For metal log raphic examination, heat-treated specimens were mounted transverse to the rolling direction, ground on silicon carbide papers of increasing fineness to 600 grit, and electropolished at 20 v using a solution containing 600 ml of methanol, 60 ml of perchloric acid, 360 ml of butyl cellosolve, and 2 ml of Solvent "X". Difficulty was experienced in obtaining good electropolished surfaces with samples containing more than 1 pct Be, the degree of difficulty in-

Jan 1, 1967

By J. D. Wood, J. T. Smith

ALLOYS with a dispersed second phase in a metallic matrix are generally much stronger than the matrix itself. Plastic deformation in dispersion-strengthened alloys is usually confined to the matrix phase when recovery processes are active, while in the absence of recovery both phases may yield.' The alloy system studied in the present research was WC-12 wt pct Co and consisted of noncoherent WC particles dispersed in the cobalt matrix. Some particle-to-particle contact existed but not enough to produce a continuous WC skeleton. The microstruc-ture of the WC particles was characterized by very straight edges, forming a trapezoidal shape in any plane of polish. Previous investigations with WC-Co alloys at room temperature have shown that fracture of the WC particles occurs in transverse rupture testing.' Room-temperature slip was reported for WC particles after indentation for hardness measurements.3 Elevated-temperature deformation of WC particles in a WC-12 pct Co alloy was suggested by recent electron microscope studies of specimens deformed at 900' to 1000°C.4 In highly deformed alloys, the WC edges were serrated in contrast to the usual straight or smooth appearance. WC-12 pct Co and WC-15 pct Co alloys have been previously studied under elevated-temperature com-pressive-creep conditions by the present authors. Electron microscope studies of two-stage replicas from deformed specimens showed no evidence of slip or fracture of the WC particles. These specimens were brought to temperature and allowed to equilibrate prior to the application of the creep load. It was believed that the load-application rate, a crosshead speed of 0.005 in. per min on an Instron universal testing machine, was sufficiently low that recovery within the cobalt matrix was sufficient to limit the deformation to this matrix. A series of experiments was performed to evaluate the influence of loading rate on the deformation of WC-Co alloys. A WC-12 pct Co alloy was selected for these determinations. The average WC particle size was 4.45 p with an average linear separation between particles of 0.59 p. The selected temperature was 800°C and was monitored with a Chromel-Alumel thermocouple attached to the specimen. Testing was conducted in an argon-atmosphere chamber to prevent oxidation of the WC-Co specimens. This chamber was mounted on an Instron universal testing machine equipped to apply the load at a fixed rate. Each specimen was loaded to 110,000 psi compression stress at 0.05 and 0.5 in. per min. The loading rate was monitored prior to insertion of the test chamber and was found to be almost precisely the nominal rate selected. The specimens were raised to temperature and held to equilibrate with the surroundings, and then the load was applied and held for 4 hr to duplicate the exposure time utilized for the creep specimens. The time to reach full load at a crosshead speed of 0.005 in. per min was some 500 sec and was reduced to 50 and 5 sec as the loading rate was increased to 0.05 and 0.5 in, per min, respectively. The model developed by Ansell,' when recovery processes do not occur, considers that fracture or deformation of the dispersed particles is necessary to relieve back stresses on dislocation sources and allow dislocations piled up against particles to sweep out in the matrix to cause plastic deformation; he further states that, even at elevated temperatures, the dispersed-particle deformation is necessary for yielding in the absence of recovery. For the case of straight dislocation segments piled up against a straight barrier, such as the straight-sided WC particles, the shear stress, 7 exerted on a particle is: where h is the spacing between particles (0.59 p), a is the applied stress (110,000 psi), p, is the shear modulus of the matrix (6.7 X lo6 psi at 80O°C), and b is the Burgers vector of the matrix dislocation. From Eq. [I], the shear stress, 7, exerted on the WC particles when no recovery occurs is of the order of 6 X lo6 psi at 800°C. The limiting stress, F, that will

Jan 1, 1969

By O. R. Morris, G. L. Hawkes

A galvanic cell, using as electrolyte a fused salt solution of calcium carbide and as electrodes carbon and a Fe-C alloy of known composition, has been set up to study the thermodynamics of Fe-C alloys in the temperature rmzge 800" to 1000°C. Time independence and reproducibility of the cell electromotive force were taken as evidence of the reversible behavior of the cell. Carbon was believed to be present in the electrolyte as the so-called acetylide ion, C;-. The plots of the cell electromotive force us temperature for a specific alloy composition were straight lines within the limits of experimental error. The average Partial molar enthalpy of carbon in iron relative to pure carbon was found to be +10,610 i 93 cal per g-atom C. Thermodynamic analysis of the data has led to the following equation for the carbon activity, ac, based upon pure carbon as the standard state: In ac = In Zc + 10,560/RT + (10.02 + 77O/T)ZC - 2.350 where ZC is the lattice ratio [nC/(nF, - nc )] and T is the absolute temperature. This equalion gives carbon activity values generally slightly lower than those from gas equilibration studies reported in the literature. METAL LOGRAPHIC examination of a polished cross section of the steel anode used in the electrolysis studies of fused salt solutions of calcium carbide by Morris and Harry revealed extensive carburization of the steel by the electrodeposited carbon. This carburization was reflected in the variability, with time, of the applied potential to the electrolysis cell, necessary to maintain a constant current density at the electrodes. This observation suggested the setting up of a galvanic cell of the "alloy concentration" type to study the thermodynamics of some metal-carbon alloys. Cells of this general type have been widely used for the study of alloy systems.2 In view of the availability of published data in respect of the austenite phase of the Fe-C system, it was decided to carry out measurements upon these alloys before proceeding to studies of less well documented systems. The galvanic cell may be written: where [C] is carbon dissolved in iron. The electrolyte was a fused salt solution of calcium carbide, containing some 5 to 10 mol pct of carbide. The cell reaction is believed to be: C(s)-[CI [I1 Carbon forms an interstitial solid solution in iron, with the atoms located in the octahedral interstices. In the fcc crystal structure of austenite there is one octahedral interstice per iron atom. Thus, the lattice ratio, ZC, shown by Gurney3 to be the fundamental concentration parameter in the context of interstitial solutions, is given by: where nc and nFe are the number of carbon and iron atoms, respectively. chipman4 has recently shown empirically the advantages of using this concentration parameter instead of the more usual atom ratio or atom fraction. The cell electromotive force, E, assuming reversible behavior, is related to the carbon potential or the partial molar free energy of carbon in the solid solution relative to pure carbon at the same temperature and pressure, GP at the composition ZC, by the equation: where z is the carbide ion valency and F is the Faraday constant. An activity of carbon, ac, in the solution relative to the value of unity assigned to pure carbon, and an activity coefficient, qC , are defined such that: where R is the gas constant and T the absolute temperature. GF is further related to the relative partial molar enthalpy Hm, and the temperature coefficient of the cell electromotive force, (aE/aT)Zc, by the equations: Measurement of the cell electromotive force thus enables calculation of the relative partial molar thermodynamic properties of carbon in iron, if z is known. At E = 0, the solid solution is in equilibrium with pure carbon. More convenient for many purposes is the standard state based upon the infinitely dilute solution, Henry's law. The relationship between the activity coefficient of carbon based upon this standard state, and that based upon the pure carbon standard state, qC , may be obtained by considering the free energy of transfer of carbon from the latter standard state to the former. The relationship is: where +:H is the activity coefficient of carbon in the hypothetical standard state based on a reference of

Jan 1, 1969

By Lucien F. Trueb

The microstructure of explosion-bonded pairs of similar and dissimilar metals has been investigated by electron microscopy. A review of the specific problems encountered and the methods used for obtaining surface replicas and thin-film transmission specimens of the bond interface is given. The bond area is mainly characterized by continuous and practically diffusionless metallurgical bonding. The very large shear stresses induced along the collision front of the plates being joined causes extreme grain elongation and a symmetrical pattern of subgrains in the bonding direction. The bond zone is also characterized by a very high density of dislocations and pressure-induced twins. Localized heating occurring during the cladding process can result in partial re-crystallization or the formation of thin layers of molten material. The force of precisely controlled explosions causing a high-velocity impact between metal plates has been used for several years to achieve metallurgical bonding between an extremely wide variety of metals. This method essentially consists of accelerating a plate to high velocity toward a stationary plate by a detonating explosive. Since the restrictions to bonding are not those encountered with conventional nethods, it becomes possible to bond pairs of metals having widely different mechanical properties that are immiscible or form brittle intermetallic compounds. Many applications of such composite metals are found in the field of corrosion protection as well as numerous other fields; for example, explosion bonding is being applied for fabricating the materials used by the United States Mint in the new sandwich-type coins. The primary condition for establishing a metallurgical bond is that absolutely clean metal surfaces be brought together. Any metal exposed to the atmosphere is covered with oxides, adsorbed gases, and other contaminants; even a very forceful impact of two such surfaces is not sufficient for bonding. Cowan and Holtz-man,"' who reviewed the dynamics of colliding plates in detail, showed that in order to achieve a good bond the explosion conditions must be chosen in such a way that the plate collision velocity is less than the sonic velocity, in which case no oblique shock waves are attached to the collision front. A pressure wave is then generated ahead of the collision line, and the material forming the colliding surface of each of the plates flows forward and is ejected in the form of a spray, the so-called jet. The dynamic elastic limit of the metals must be exceeded so that there is sufficient plastic deformation. At the point where the jet formed by the junction of the inner surface layers of both plates separates from the combined plates, the material experi- ences a very high shearing strain and the pressure can reach several hundred kilobars. This process strongly influences the microstructure of the bond zone as will be seen later. Behind the collision front, uncontami-nated layers of internal material are brought together under high pressure and are thus metallurgically bonded. I) STRUCTURE OF EXPLOSION BONDS The different types of explosion bonds that can be obtained depend on the explosion conditions, and have been investigated by Cowan and Holtzman,1'2 Holtzman,3 Klein; Bahrani and crossland,' and Buck and Horn-bogen. The preferred kind for practical applications is the so-called wavy bond, typical examples of which are given in Fig. 1 showing light micrographs of various metal-to-metal interfaces. In forming this type-- of bond the collision energy is mainly expended in jetting, the formation of waves, and localized melting. Beyond the crest of the waves, eddy-shaped areas are observed in which the two metals are mixed in a complex pattern of streaks. Cowan and Holtzmanl first proposed that this wavy pattern is analogous to periodic eddy shedding in the flow of a viscous fluid around an obstacle (Von Karman's eddy street). The mass of metal ahead of the stagnation point, which is associated with the jet and has forward momentum, plays the role of an obstacle and the eddies created in the flow of solid metal around the stagnation point are preserved in the final clad specimen. This idea has been reviewed more recently by Klein4 and the variables involved in the wave formation have been discussed in some detail by Bahrani and crosslands and Buck and Hornbogen.6 Several studies of the structure of explosion bonds by light metallography have already been published.1-6 Aside from the waviness and the eddies which were mentioned above, the most striking characteristic of the area in the vicinity of the bond interface is a very considerable longitudinal grain deformation which appears to be strongest at the metal-to-metal boundary and dies out as one moves away from it. Large twins are often observed within the deformed grains, and molten areas are found in the center of the eddy-shaped structures situated beyond the crest of the waves. The large hydrostatic pressures and shear stresses occurring at the interface modify the mechanical and chemical properties of the bond zone. Increases in hardness in this area have been reported by various authors.396 The defects along the interface can also cause a local increase of the chemical reactivity and thus might be expected to boost the etching rate. However, the effects of this preferential etching cannot be observed by light microscopy due to its inherently limited resolution power. The same limitation precludes the observation of morphological features directly along the bond interface as well as the interface itself. Furthermore, no information can be gained by light-

Jan 1, 1969