Search Documents

By A. E. Jenkins, L. A. Baker, N. A. Warner

Rates oj decarburization of levilated Fe-C droplets conlaining 5.5 to 0 pct C have been measured at 1660°C. Gas mixtures of 1, 10, and 100 pct 0, with helium diluenl were used at velocities of 12.5 and 62.5 cm per sec. Rates were independent of carbon concentration in the mell and in good agreement with the calculated rule of oxygen diffusion through the gas boundary layer. The effects of flow rale and total pressure are as predicled and the rates are approxitnalely 2.5 times those with CO2 as oxidant. The mass-transfer correlation used incorporaled the efject of natural convection as well as forced conrection. Graphile spheres are shown to oxidize at the same rate as Fe-C droplets under the same experimental codlions. It is concluded that, for high carbon concentrations in the melt, the rate of- decarburizalion is controlled wholly by the rate of gaseous diffusion. Rate measurements with pure CO, are reported for low carbon concentrations where CO bubbles nucleate within the droplet. Under these circumstances the decarburi-zation decreased with carbon concentration and it is proposed that carbon diffusion is significant in conlrolling the decnvburization rate. In an earlier paper1 decarburization rate measurements were reported for levitated Fe-C alloys at 1660°C but with CO2 as the oxidant. The decarburization rate was found to be independent of carbon concentration in the melt but slightly affected by total pressure. The authors were unable to explain the slight pressure effect but in all other respects the results were consistent with control by diffusion in the gas boundary layer. Subsequent work has been directed at finding the reason for the slight pressure effect and whether the kinetics with oxygen as oxidant parallel those with CO2. Recently Ito and Sano2 have shown that with water vapor-argon atmospheres the decarburization rate is gaseous diffusion controlled until an oxide film appears on the surface. In this work the melts were contained in crucibles. MASS TRANSFER IN THE GAS PHASE In the earlier analysis1 only forced-convection mass transfer was considered. Subsequent recognition of the existence of some free-convection mass transfer explained the observed small effect of total pressure on the decarburization rate. Steinberger and Treybal3 and Kinard, Manning, and Manning4 have developed correlations involving the linear addition of the contribution of radial diffusion, free and forced convection. Steinberger and Treybal&apos;s correlation was chosen as the most applicable to the present work since it correlated most of the data available in the literature and handled the low Reynolds number region exceptionally well. The correlation for (Gr&apos;Sc) < 108 is where Nu&apos; is the Nusselt number for mass transfer based upon the total surface of a sphere in an infinite medium, G&apos; is the mean Grashof number for mass transfer defined by Eq. [2], Sc is the Schmidt number (µ/pDAB)f, Re is the sphere Reynolds number (dpu,pf/µf), p is the viscosity of the gas (poise), p is the density of the gas (g cm-3), Dab is the binary diffusivity for the system A-B (sq cm sec-&apos;), dp is the sphere diameter (cm), u is the approach velocity of the gas (cm sec-I), and subscript f denotes the property value is computed at the film temperature Tf defined by Tf = +1/2(To + Tr) where To is the specimen temperature and T, is the approach gas temperature (oK). Natural convection occurs when inhomogeneities exist in gas density. These may be caused by concentration gradients, temperature gradients, or both. In the present work the temperature gradient between the sphere and the bulk gas was very large and in some cases, for example the runs with pure oxygen, the concentration gradient was also appreciable. The Grashof number defined by Mathers, Madden, and piret5 was used since it took account of both temperature and concentration gradients: where Gr&apos; is the Grashof number for mass transfer (p2fgd3|-yA-yA|/µ2f), Gr is the Grashof number for heat transfer (p2f gd3p|To - T,]/µ2fTf), Pr is the Prandtl number (cpµ/k)f, g is the acceleration due to gravity (cm sec-&apos;f, a is the concentration densification coefficient (1/p)(ap/ayA)T, yA is the mole fraction of component A at the gas-metal interface, yA is the mole fraction of component A in the bulk gas stream, cp is the heat capacity of the gas per unit mass at constant pressure (cal g-I OK-&apos;), and k is the thermal conductivity of the gas (cal cm-&apos; sec-1 OK-1). Mathers et al. tested this combined Grashof number

Jan 1, 1968

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.&apos; Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler&apos;s saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.&apos; A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By Joseph M. Jacisin

Fatigue tests were conducted on 2017-T4 alumium in alloy in an u1lrcthig.h vacuum of 2 x 10-lo Torr and in air. The vatio of vacuum-to-air faligue life for this ~malerial varied Jrom 3.5:1 at a strain of 2.5 X 1O-3 ill. pegr in. to 8:l at a strum of 3.3 x X ill. per 171. Sotlze pvelivtlinary data were also obtained on the faligue life of the alumirnum alloy in a dvy-nitrogen atmosphere. A dark deposit observed on the fracture surfaces of the aiv-tested specimens was identified as oxides of tr~angarzese and magnesium This observalion, and the close correlalion betaveen results obtained in vaCuum and dry-nitrogen environtments, tend to confirm that air stvongly influences the fatigue mechanism by a covrosion process. THE fatigue life of certain metals is known to increase when the atmospheric pressure is reduced. Gough and Sopwith1-2 postulated that this is due to a joint chemical and mechanical process operating in air at the surface of the metal with oxygen and water vapor playing significant roles. Wadsworth and Hutchings3 observed that aluminum is mainly affected by the presence of water vapor. Very little information is available on the fatigue properties of structural aluminum alloys in a vacuum environment. This report describes work performed on 2017-T4 aluminum alloy in an ultrahigh vacuum (2 x 10-loTorr) and in air. Some preliminary data are also presented on the fatigue life of the alloy in a dry-nitrogen environment. 1) EXPERIMENT 1.1) Test Material. The material tested was commerciaT 2017-T4 aluminum alloy which, in addition to aluminum, has an approximate composition of 4 pct Cu, 1 pct Fe, 0.8 pct Si, 0.5 pct Mg, 0.5 pct Mn, plus smaller amounts of other elements.* Some typical naturally age to a substantially stable condition. Specimens were then machined from these rods and ground to a No. 8 microfinish. In order to minimize variation in material characteristics, specimens were made from rods procured from the same lot. 1.2) Apparatus. The apparatus and test specimen used in the fatigue tests are shown in Fig. 1. The device utilized a single-cantilever beam with rotating-bending loading. Bending stress was applied to the fatigue test specimen by placing a spacer beneath the bearing support, thereby providing a constant deflec-

Jan 1, 1968

By Pradeep K. Rohatgi, Clyde M. Adams

An analysis of heal conduction in the freezing of a solution has been performed. The case considered is the semi-infinite mass of solution, bounded by a con-stant-temperature plane with one-dimensional heat flow, Numerical cooling rate and freezing rate distributions hare been calcutated for the particular case of unidirectional freezing of aqueous solutions against. a cold copper chill. The solution at each level parallel to the chill surface is subjected to a spectra of frcezing rates; the freezing rate is inilially lour., passes through a maximum, and then decreases until solidification is camplete. Arange and maximum freeeing rates are inversely proportional to the square of distance from the chill surface. The temperature of the chill surface in contact with the solution remains constant during solidification. Experimentally, it is observed that deudrite sparing increases linearly with distance from the chill surface; in the light of heat -flow analysis this means that the dendrile spacing is imersely proportional to the square root of the maximum freezing rate. SOLIDIFICATION of liquids is accompanied by rejection of latent heat at the solid-liquid interface. The over-all rate of liquid to solid transformation is governed by the rate of heat extraction. Analysis of the heat transfer in the liquid during freezing is important since it determines the freezing rate and resulting structure. A considerable amount of work has been done on metallic systems since solidification is frequently a major step in processing metals. Unidirectional freezing from heat sinks has been treated by several investigators.1-4 Much of the work has been limited to the simpler case of substances such as pure metals which freeze isothermally at a unique transformation temperature. In this case the thickness of the solid zone y, next to a chill surface. is a parabolic function of the time. 8. where a and b are constants. Eq. |1| is a close approximation giving the progress of solidification for the case in which there is a small but finite thermal contact resistance at the interface between the freezing liquid and the chill.&apos; It has been used with some success in connection with large steel ingots4 when the therma1 contact resistance is negligibly small (as is the case when water is brought into contact with the metal chill). The constant, b. becomes zero and Eq. [l] is then exact. even when the thermal properties of the chill and the freezing liquid depend on temperature. Analysis of unidirectional solidification of solutions is more complicated since the latent heat is evolved over a range of temperatures. Next to the all-solid zone in contact with the chill surface there is a solid plus liquid zone in which solidification takes place. Although the equations presented are considered quite general the numerical and experimental results are for freezing of aqueous solutions from a copper chill. I) EXPERIMENTAL PROCEDURE Solutions of potassium chloride, sodium chloride. and lithium chloride have been used. These solutions form a eutectic: a typical phase diagram is shown in Fig. 1. A solution at its liquid us temperature is poured into a tygon tube mounted on a relatively large copper chill. The chill is immersed in a freezing mixture of dry ice and acetone at -70°C. A thermocouple connected to a high-speed recorder was mounted near the top of the chill to measure the fluctuation in the temperature of chill surface in contact with the solution. In this system the progress of solidification can be visually observed through the tygon tube. After the specimens freeze to a desired height they are removed from the copper chill and stripped from the tygon tube. Longitudinal and transverse sections are cut from the specimen for micrographic examination. Specimens in the form of a thin slice are mounted on a transparent glass slide by freezing small drops of water around the periphery. They are then polished on a series of emery papers; the final finishing is done on a soft tissue paper. A Leitz Biological microscope was used for structural observations; photography was

Jan 1, 1968

By Nicholas J. Grant, Joseph T. Blucher

High-purity aluminum and an Al-10 pet Zn alloy zvere tested in axial fatigue from 80" to 900oF, at struzn vales of 5 and 150 pct per min, at a strain amplitude of 1 pcl. Cycles to failure were recorded as well as the load per cycle during the entive test. Several grain sizes were examined in each material. Examination was made of modes of deformation, initiation and growlh of&apos; cracks, and vecovery mechanisms such as srbgrain formation and boundary migration. Strain rate effects on cycles to failure are first observed ahoi&apos;e 50O0F, the highev vate vesulting in longer lije. Crack initiclion at room temperature may be truns-or iutercrystalline but fructures are transcrystalline. Abore 600&apos;F, crack iniliation and growth ave largely inlercvystalline. Boundary wzigratiotz to 45-deg positions is observed above 70Oo F, and fractrrves are a combination of grain bol~ndary voids and cvacks. It is only in recent years that studies of deformation and fracture which prevail in fatigue at elevated temperatures have attracted significant attention.&apos; Of such studies considerably less attention was given to high strain-low strain rate fatigue. Moreover, the majority of high-temperature fatigue studies were performed at conventional machine speeds (1000 to 10,000 cpm). As it is well-demonstrated in uniaxial creep-rupture series, at high strain rates, even at high temperatures, metals undergo work hardening with little or no attendant recovery or recrystallization thus the nature of deformation and fracture which is observed is similar to that encountered at lower temperatures.&apos;-" Thus, for example, fatigue testing of a stainless steel at 750°F does not involve high-temperature deformation processes,2 and might more correctly be termed "fatigue testing at an elevated temperature". It was the purpose of this work to study deformation and fracture in fatigue as a function of low strain rates and temperature, selecting conditions which would result in grain boundary sliding, migration, fold and subgrain formation, and intercrystalline cracking in high-purity aluminum and a high-purity A1- 10 pct Zn alloy. Grain size was an additional variable. Extensive studies of the deformation and fracture behavior of these aluminum materials in simple creep had been done in the authors&apos; laboratory, and were to serve as a basis of comparison for the observed effects in fatigue:&apos;-&apos;&apos; the range of the creep test temperatures was 80° to 1150oF. MATERIALS AND EXPERIMENTAL PROCEDURE The compositions of the 99.99 pct pure A1 and the A1-10 pct Zn alloy are shown in Table I. Button-head specimens, with a liberal fillet, of 0.20 in. diam and of gage length 0.40 in. were machined from wrought bar stock. The ratio of 2:l gage length to diameter was selected after preliminary tests showed that a shorter length gave a shorter life, probably due to end effects, and after evidence of buckling in longer gage length specimens. After machining, the specimens were chemically polished to remove the worked outer layer, and were subsequently heat-treated to stabilize the selected grain sizes. Both the high-purity aluminum and the A1-10 pct Zn alloy were heat-treated to produce grain diameters of approximately 0.5 and 2 mm in each case. These grain sizes are referred to in the text as fine and coarse grain, respectively. One lot of the high-purity aluminum was heat-treated to produce a still coarser grain size in which the cross section was occupied by 2 to 3 grains. This structure is referred to as very coarsegrained. After heat treatment, the specimens were again electropolished. To avoid complications of both stress and strain gradients in the cross section of the specimen, a hydraulic, axial fatigue machine was designed and built. A button-head specimen, 1/2 in. diam at the head, was firmly gripped in a split-type holder free of any play in the grips. The test temperatures varied from 80" to 900°F. The strain amplitude in all of the reported tests was 1 pct for a total strain amplitude of 2 pct. The strain range was set by precision micrometers and measured by a precision dial gage. Constant strain rates of 5 and 150 pct per min were selected so that high-temperature type deformation and fracture would occur in the higher-temperature tests5,6 The strains and strain rates must be regarded as nominal values because they are based on the original specimen dimensions, which changed significantly as a result of necking and crack propagation, as can be observed from Fig. 8. For the elevated-temperature tests, a thermocouple was inserted into a well in the head of the specimen; the selected temperatures could be maintained with less than ± 5oF fluctuation during the entire test. To avoid changes in grain size before the test, specimens were heated to the test temperature in less than 15 min; similarly, they were cooled to room temperature after fracture with an air blast to avoid or minimize recovery or recrystallization. During the fatigue tests, load vs strain curves were recorded by a strain gage load cell for each fatigue cycle. In addition, the maximum values of load amplitude were recorded for the entire test.

Jan 1, 1968

By N. J. Grant, B. C. Giessen, M. Morris

The slvuclures of alloys in the system In-Bi have been investigated after (levy vapid queuching from the mell (splat cooling) to -190°C. Tuo-phase fields could be suppressed over most of the tota1 concentvalion range; five melastable phases a1, a2, ?, ?1. and ß exisl, of which four have simple elementtike structures. For example, ß has the A5 struclure of white till. Crystal-tographic data and coordination numbers for these phases aye given, as well as addilional information on the equilibrium diagram, where a new phase In5Bi3 teas found. THE phase diagrams of binary combinations of B elements from the groups B2, B3, B4, and B5 are usually of a simple type and show considerably fewer intermediate phases than combinations of these elements with A metals, transition metals, or the B1 noble metals. Aside from phases such as the typical B3-B5 compounds with the ZnS-B3 structure type, few stoichiometric phases are known; among them are In2Bi and 1nBi.l Nonstoichiometric phases include ß (In-Sn), a1, (In-Pb), and the tin-rich ? phases in the In-Sn, Cd-Sn, and Hg-Sn systems.&apos; The first two phases have a close relationship to indium, while the latter group are known to be structurally related to a Sn. Thus, there are generally no immediate experimental data for the correlation of the crystal structures of B metals and B metal combinations with certain monotonously varying parameters, such as the valence electron concentration (VEC), or the average atomic size. Such parameters have been recognized as structure determining, e.g., for the transition 4 Sn — y phase,2,3 where nonintegral valence electron concentrations are encountered. It should be possible to extend such correlations to other binary systems, if nonequilibrium single-phase alloys could be produced over broad valence electron concentration ranges, and if their crystal structures could be regarded as being imposed by their electronic states. It has been shown in the case of the tin-rich 7 phases3 that alloy phases with typical crystal structures can be produced in B metal alloys rapidly quenched from the liquid to -190°C by the splat cooling technique due to Duwez,3-8 and reviewed in Refs. 5 and 6. The In-Bi system was selected because it extends over a valence electron concentration range in which several metastable, nonstoichiometrir phases could be expected to occur. Further, the low melting points of the known intermediate phases, In2Bi and InBi, Fig. 1(a), indicated low binding energies and thus possibly low driving forces for the formation Of the equilibrium structures. EXPERIMENTAL TECHNIQUES AND RESULTS The preparation of the quenched foils followed the practice described in Ref. 3. Master alloys were produced by melting of indium (99.97+) and bismuth (99.99+) in evacuated Vycor capsules or in an inert gas arc furnace; quantities of 20 mg were splat-cooled onto copper and silver substrates held at - 190°C; and crystal structures and lattice parameters were determined on a GE XRD-5 diffractometer using Cu Ka, radiation at -190°C and at room temperature. The duplication of each run with both substrates permitted the elimination of overlap of the substrate diffraction pattern and that of the investigated substance. The XRD patterns were usually taken from sin2 " = 0.03 to 0.35; the substrate was used as a means of internal calibration. The fractional accuracy of the lattice parameters of metastable phases is approximately 10-3 In the following, all percentages are in atomic percent. The stable and metastable phases found after rapid quenching to -190°C are listed in Table I, together with estimated concentration ranges and crystallographic data. The investigated alloys and phases present in them are given in Table 11. Except for the region between indium with 33 and 50 pct Bi, where a revision of the equilibrium phase diagram became necessary to include a new stoichiometric phase In5Bi3, the diffraction patterns taken after heating to room temperature agreed with those expected from the phase diagram, Fig. l(a). This suggests that the new nonstoichiometric phases are not stable at room temperature, thus following the observations made for the y phases based on tin.3 Results concerning the equilibrium phases In2Bi and In5Bi3 and the revision of the equilibrium phase diagram which is made necessary by the inclusion of In5Bi3 will be treated first. The Crystal Structure of In2Bi. Makarov7 had identified In2Bi as belonging to the AlB2-C32 type ; however, in a later paper the structure was revised.8 In2Bio was found to be of the Ni21n-B8ß type,21 with a = 5.496A, c = 6.57.9A, and N = 6 atoms per unit cell.9 This crystal structure was confirmed in the present work; definite evidence for the doubling of the c axis, as compared to the A1B2-C32 type, and for the proposed order structure, was found in the powder pattern. The observed lattice parameters agree well with those of Ref. 8; those measured at -190°C are given- in Table I. The Crystal Structure of In5Bi3. A new, equilibrium, intermediate phase was identified in slow-cooled, as-cast alloys; it was identified as In5Bi3. The structure has been worked out by Giessen and Grant;" lattice parameters at -190°C are given in Table I. This phase is probably identical with "In3Bi2", produced by vapor deposition techniques, but not recognized as an equilibrium phase by Palatnik et a1.11 After completion of the present work, the existence of In5Bi3 has also been demonstrated by superconductivity measurements on In-Bi alloys.20

Jan 1, 1968

By T. G. Nilan

Steels containing 0.4 and 0.8 pet C have been transformed isothermally at pressures up to 34 kbuv. Decomposilion mechanisms are so intimately related to phase equilibvia that, as the equilibria shift under high pressure, the microstruclures of the decomposition producls change, maintaining at pressure the same correspondence between a given phase equilibrium and a given microstructure as a1 1 atm. A bainitic unicvo-structure occurs in these steels at high pressure that IS observed only at 1 aim abole 1.4 pct C. This strrrcl111,e 1s ruliorzalized in terms of the effect of pressure on the transformation to lower bainite. The pressuve depetlderlce of the kinetics of pearlile formation is descrihed by an absolute rule theory amalysis. The activation volume for the transformation is 7 cu cm per mlole, which is indicative of a phase-interface transformation-rate cotntrol mechanism. This fortmulation, when expressed in terms of known solule effects on the energelics of tvansformation, gives promise of explaining the effects of alloying elemenls on hnrden-abilily, particularly that of &apos;coball. KINETIC processes in solids are functions of the primary thermodynamic variables of state: composition, temperature, and pressure. Until the development of high-pressure techniques&apos; that permitted the generation of sustained high pressure at high temperatures, metallurgical studies of such reactions were largely limited to isobaric conditions at atmospheric pressure. The data so obtained, and theoretical deductions based on these data, were necessarily incomplete For the particular case of austenite decomposition, a knowledge of the phenomenology of the reaction in terms of all the state variables should lead to a clarification of the process. This deeper understanding should facilitate a decision between conflicting theories that have been proposed to rationalize these phe- nomena. An analysis, derived from an understanding of the transformation mechanisms, may aid in the optimization of alloy steel development. The first studies of the effect of pressure on transformations in steel were made by Kulin et al. in 1952.&apos; In a study of the influence of applied stress on mar-tensite formation in a 30 pct Ni steel, they found that the martensite start (M,) was depressed 8°C per kbar* by hydrostatic pressure. Jellinghaus and Friedewold3 were apparently the first to investigate the effect of pressure on isothermal transformations above the Ms. They found that the bainite transformation rate in a 1.2 pct C, 3.8 pct Mn steel was reduced by a factor of 3 by a hydrostatic pressure of 4 kbar. In both of these investigations,2,3 the M, of the steels studied was below room temperature. Austenitizing and quenching were done at atmospheric pressure, followed by the decomposition of the metastable austenite under pressure. The maximum temperature at pressure in the bainite study3 was 350°C. Until the advent of the present high-pressure devices, it was not possible to conduct isobaric high-pressure heat treatments from austenitizing through isothermal decomposition and quenching. The exploitation of high pressure as a variable in metallurgical studies was greatly advanced by the apparatus and techniques developed by Hall4 and co-workers. Utilizing these techniques, Radcliffe et a1.5 and Hilliard6 etermined the pressure dependence of phase equilibria in the Fe-C system. Hilliard and cahn7 examined the pearlite transformation rate in an AISI 1080 steel and also in a high-purity 0.92 C Fe-C alloy at 1 atm and at 34 kbar and found a 700-fold reduction in rate at pressure in the 1080 steel but only a fivefold reduction in the high-purity alloy. In agreement with the shift of phase equilibria under pressure, the microstructures were hypereutectoid at 34 kbar pressure, whereas they are eutectoid at 1 atm. Determination of the effect of pressure on carbon diffu-

Jan 1, 1968

By Hiroshi Oikawa, R. G. Blake, A. G. Guy

An equatzon has been derivedfor conveniently calculatzng the couvse of homogenzzation in a three-corviDonent solid solutiorz. The necessary assumptions are that the initial distributions of concentration are sinusoidal and that the four interdiffusion coefficients are constant. Employed in the deriuation were the Laplace transform and the fouter Fourier sine transfovwz. The final equation is shown to be in good agveetnent with the experimental results of Kirkaldyet al. on Cu-Sn-Zn alloys. COMMON boundary conditions for representing physical problems are those of the finite solid and of the infinite solid. Many metallurgical phenomena, however, have the geometrical form of a finite pattern reproduced throughout an infinite solid. Precipitation within a uniform matrix and segregation during solidification are examples. The purpose of this treatment is to show that a convenient and useful mathematical analysis is possible in those cases in which the finite pattern can be approximated by a sine function. The particular topic to be considered here is the elimination of segregation by diffusion, but the mathematical model has applicability in many other areas. It should be recalled that the mathematical solution of a typical problem involving a finite solid, such as diffusion into a thin layer, is quite involved.&apos; Various types of solutions are used depending on the degree of advancement of the diffusion process and on the initial conditions. A step function is the simplest initial condition, but even in this case the general solution has the form of an infinite series. Kirkaldy et a1.2 have

Jan 1, 1968

By A. G. Preban, R. J. De Angelis, J. B. Cohen, P. Gordon, D. C. Brillhart

Changes in stored energy, resistivity, density, X-ray line broadening, and dislocation arrangements (from transmission electron microscopy) have been mensured on copper specimens shock-loaded at 75 to 435 kbars. The stored energy in shock-loaded copper and changes in density and resistivity are larger than those after conventional deformation. A high density of twins makes an appreciable contribution to all the measured quantities. Dislocation densities rise to values of 1011 lines per sq cm at the highest pressure. The resistivity, density, and X-ray In a study of the effects of shock loading on copper, changes in stored energy, resistivity, density, hardness, lattice parameter, line broadening, and dislocation structure have been examined after subsequent annealing of specimens shocked to various pressures. This paper presents certain aspects of the data, taken by two groups, one at the Illinois Institute of Technology, and the other at Northwestern University, and compares the changes in these properties, and what they indicate about the effects of shock deformation. measurements yield dislocation densities in substantial agreement at all pressures, after correcting for the effects due to the twins. At the higher pressures, electron microscopy yields dislocation densities that are lower by a factor of about 5 to 10. Dislocation densities from stored -energy measurements are high; this finding can be rationalized by the consideration that the deformation twin boundaries present are largely incoherent. There is no evidence for homogeneous dislocation nucleation during shock loading. Shock loading any metal or alloy, such as copper, causes a large increase in yield strength, with dimensional changes of the order of only a few percent."&apos; Other properties have not been extensively studied, but this result clearly indicates the importance of examining the substructure. Previous studies of the substructure of conventionally deformed specimens have been made using electron microscopy,3-6 X-ray diffraction,7,8 and etch pitting.9,10 The dislocation density can reach values of about 10" per sq cm; and the dislocations are arranged in cells approximately 0.15 in size. The substructure varies widely, however, from point to point in the specimen. The substructure of explosively loaded copper consists of cells of about the same dimensions6,11 but their size is more uniform.6 Profuse twinning occurs12,13 and the twins are often too small to be detected optically.6,13 The boundaries outlining these twins appear to be incoherent.14 There is now ample evidence 13-15 that twinning is a strengthening mechanism in fcc metals but this is only part of the strengthening effect in shock-loaded copper.* From the twinning systems which operate in shock-loaded single crystals,13 and from changes in texture on shock loading,17 it has been shown that both the

Jan 1, 1968

By A. J. Strauss

The solubilily of lead in PbS as a funclion of lemperature has been investigated by means of Hall coej&apos;icient (RH) measurentents OIL samples prepared by annealing and quenching Bridgman-grourz single crystals, which contain excess lead incorporated during /heir growth from the mell. For sufficiently long annealing times and sufficiently rapid quench rules, the samples obtained consist of n-lybe PbS snturated with In the semiconducting compounds PbS, PbSe, and PbTe, the point defects associated with the presence of lead in excess of the stoichio metric composition are shallow donors. The defects associated with the presence of excess nonmetal are shallow acceptors. lead at the annealing teuiperatiire, together luilh a dispersed second phase of lead microprecipitates. Due to the retrograde solubility of lead, the measured free carrier concentration (n = l/eR77) decreases with decreasing annealing tewperature (T) from- 2.4 X 10 em-3 for 1l85OK to 1.3 X 1018 cm-3 for 623°K. The dala are well-represented by the equation n =(1.08 x 102) exp[ - (0.37 ev.)/kT] cm-3 For most undoped samples of these compounds, the carrier concentration at room temperature and below is determined primarily by the stoichiometry, since the concentration of either excess lead or excess non-metal is large compared to the concentrations of intrinsic carriers and electrically active impurities. Therefore the dependence of composition in temperature and partial pressure can be investigated by means of Hall coefficient measurements, even though the deviations from stoichiometry do not exceed 0.03 at. Pct

Jan 1, 1968

By N. A. Gjostein

The real and apparent dependence of the surface self-diffusion coefficient, Ds, of gold on crystallo-graphic orientation has been investigated by isolated scratch smoothing and grain boundary grooving experiments. No systematic variation of Ds with orientation was found along the [100] zone. In view of the experimental scatter in these results, however, only aniso-tropy ratios, p, greater than -1.3 would be detectable. Anomalously low values of Ds were found on the [0ll] and [110] zones when the diffusion direction lies along (the scratch or grain boundary groove is perpendicular to) these zones. By comparing these results with a previous y plot study of gold, it is hypothesized that this is not an intrinsic diffusivity effect, but rather it results from a decreased driving force for mass transfer at orientations where the y-plot curvature is negative and appreciable in magnitude relative to y. The characteristics of this type of anisotropy do not appear sEVERAL investigations1-7 have dealt with the anisotropy of the surface self-diffusion coefficient, Ds, of metals as measured by the decay of single or multiple to be in agreement with the hypothesis of fast diffusion along ledges in the surface structure. In certain cases the Fourier method of determining Ds, described in Paper I of this series9 was compared with the second moment analysis in order to determine whether or not the method of analysis affects the anisotropy ratio. While the type of analysis does influence the magnitude of the anisotropy ratio, this effect is not associated with the shape of the profile, but rather is connected with the iterative volume diffusion correction used in conjunction with the second moment analysis. It is further demonstrated that the volume diffusion correction can be too large by either method when the y-plot curvature effect is large. Certain orientations exhibit an unusual temperature dependence of Ds ; this is discussed in terms of the y-plot curvature effect and/or the influence of impurities on Ds . scratches in the surface. Depending on the system investigated, both large1"3&apos;6&apos;7 and small4&apos;5 anisotropies in Ds have been found. Although adsorbed impurities undoubtedly play an important role in determining the magnitude of the anisotropy,8 there are other factors that can give rise to an apparent anisotropy in Ds, thus obscuring the true nature of an intrinsic anisotropy in

Jan 1, 1968

By K. A. Jackson, J. D. Hunt

The discussion by Tammann and Botschwar of the transition from eutectie grouth to denrdritic plus eu-tectic growth is reviewed and applied to metallic eutectic systems. Using expevimental data on the geowth rate of the Pb-Sn eutectic, and an extrapolalion of dendritic growth rate in tin and Sn-Pb alloys , qlcantitatice prerlictiotls of the extent of the eutectic region in tin-vich Sn-Pb alloys are made. There are no experimenta1 measuvements available for detailed comparison with these predictions. EUTECTIC structures form over a small range of compositions. The theory of lamellar growth presented by Jackson and Hunt&apos; indicates that it is in principle possible to have eutectic growth over almost the complete range of compositions between the two solidus lines. This does not occur in practice. Alloys far from the eutectic composition grow dendritically followed by a eutectic as shown in Fig. I. The transition from a eutectic to a dendritic plus eutectic interface cannot be predicted from constitutional undercooling arguments because constitutional undercooling always exists ahead of the eutectic interface.&apos; Reasonable predictions can, however, be made using arguments originally put forward by Tammanl. and Botschwar.3 These and later workers&apos;"*6 carried out extensive experimental investigations of the extent of the eutectic range in organic materials. They concluded that the structure formed, eutectic or dendrites plus eutectic, depended on which structure grew faster at the given undercooling. This is, of course, equivalent to the structure which grows with the smallest undercooling at a given growth rate. In this paper, we will discuss these ideas briefly and then apply them to predict quantitatively the range of eutectic growth in tin-rich Pb-Sn alloys. The temperature dependence of the growth rates of dendrites and eutectic for a typical metal alloy of eutectic composition is shown schematically in Fig. 2(a). The growth rate for the eutectic increases more rapidly with undercooling than those of the dendrites because of the short diffusion path maintained in the eutectic, see Fig. 1. For an alloy off the eutectic composition on the A-rich side, the growth rates shift as shown in Fig. 2(b). The liquidus temperature of the a phase increases, that of the 3 phase decreases, and the temperature of zero growth rate for the eutectic does not change. The curves, particularly the dendritic ones, change shape as well, but for our purposes the principal effects occur because of the change in liquidus temperatures.3-6 In an isothermal system, only a dendrites will grow above TE, Fig. 2(b). If the temperature is below TE, and both phases have nucleated, a dendrites will grow ahead of the eutectic at

Jan 1, 1968

By J. J. Demo

The effect of aluminum additions on the coating vale and corrosion resistance of Cr-Fe diffusiou coalings on a mild steel substvate has been studied. Aluminum additions up to 2 wt pct increase the chromium penetration rate while further additions retard it. The apparent cor$lict between these data and metallogyapkic ineasurements, which show a continuially increasing coaling thickness with aluminum addition, is discrissed. Compavisorz of corrosion resistance on the basis of equal thickness of tlre entire coating measured mnetal- ALTHOUGH ferrous metal articles are cheap and widely used, they are often quickly degraded by corrosion. To prevent or slow down the corrosion process, lographically is misleading; equal thickness of the cor-rosion-resistant portion of the coating is a bette.v basis of conzpavison. Inter difision coefFicients for Cr-Al-Fe coatings of different aluminum content have been detevmined and found to dary logarithmically when plotted againnst chromium concentvation. A general method of calculating diffusion profiles for different lrealment limes and surfuce coucentralions IS described. many types of coating are applied to steel.&apos; Among these are diffusion coatings, formed by high-temperature diffusion of selected elements into the surface, which then becomes the coating Diffusion coatings are metallurgically bonded to the substrate and show a continuously varying concentration gradient from surface to substrate. Generally, these coatings have the advantage of adhering to the substrate upon deformation of the composite. Moreover, when chromium is one of the diffusion elements, a mild steel substrate

Jan 1, 1968

By B. J. Bayles, J. A. Ford, M. J. Salkind

Unidirecltonally sulidijied AL-A13Ni was found to exliibit excellent microstructural stability to 508°C. Above this temperature the transverse micvostructure coarsened in a manner analogous to "Ostwald Ripening", but the A13Ni whiskers did not spheroidize or foreshorlen. The coarsened whiskers reinforced the matrix as effectirely as the finer whiskevs and no reduction in room-temperature tensile strength mas noled after exposure for 90 hr at 96 pel 0-1 the absollite melling temperature of the eulectic. The slability was auribucted to the presence of low-index (and presurrlably lor-energy) cvystallographic interjaces between phases. The driving force for microstructural coursening was presumed to be the reduction of interfacial energy between the phases. Finer micvoslructures were found to coarsen more rapidly than those which weve imitally coarser. FIBER-reinforced metals have been shown to exhibit good short-time tensile properties at elevated temperatures.1-4 However, many elevated-temperature applications require long-time property retention which dictates the necessity for microstructural stability. Two types of instability are common to fiber composities. The first, chemical instability, is due to chemical reaction between the matrix and the relnforcing phase. Petrasek and weeton5 have shown that chemical reaction between tungsten wire and several copper alloy matrices resulted in degradation of the reinforcing phase and reduction in strength of the composite materials. Kreider and Leverant4 have noted similar behavior for boron-reinforced aluminum above 400°C. The second type of instability arises in systems in which the phases are essentially chemically stable with respect to each other and is characterized by spheroidization and/or agglomeration of the reinforcing phase. parratt6 has reported this type of degradation to occur relatively rapidly at moderate temperatures for nickel and cobalt alloys containing whiskers of silicon nitride, aluminum oxide, and silicon carbide and has identified it as "physicochemical" instability. Although both types of instability are the result of the differences in the chemical potential between the fibrous phase and the matrix, they may be differentiated by the fact that the second type, "physicochemi-call&apos; instability, results in little or no net change in the composition or amount of each phase present. It does, however, result in a morphological change which profoundly affects the strengthening mechanism. Chemical interaction. on the other hand, results in a change in the composition and amount of one or more of the phases present, or the appearance of a new phase. In the latter case, the appearance of the mi-crostructure, that of a fibrous phase aligned in a matrix, may remain essentially unchanged, but the chemical degradation of the fiber results in markedly reduced composite strength. This investigation was initiated in an attempt to evaluate the microstructural and related mechanical property changes of a whisker-reinforced eutectic composite after elevated-temperature exposure. The composite system chosen for this study was the uni-directionally solidified A1-A13Ni eutectic which Lemkey. Hertzberg, and Ford7,8 demonstrated to behave as a whisker-reinforced composite. The microstructure of the unidirectionally solidified material consists of aligned needles of A13Ni in a matrix of aluminum. EXPERIMENTAL PROCEDURE Eutectic ingots having a nominal composition of 6.2 wt pct Ni were produced by melting 99.99+ pct A1 and 99.99 pct Ni in recrystallized alumina crucibles in an argon atmosphere. The analyses of the starting materials are listed in Table I. These master heats were cut up? melted by induction heating, and unidirectionally solidified vertically in 1/2 -in.-ID. 6-in.-long graphite crucibles, in a dynamic argon atmosphere. Therma1 gradients in the liquid were determined by measuring the temperature in the melt as a function of apparatus travel distance, as discussed by Kraft and Albright.9 The rate of solidification was assumed to be equal to the uniform rate at which the crucible assembly was withdrawn from the furnace. Ingots representative of nominal growth rates of 2, 5, and 11 cm per hr were produced and the solidification parameters are summarized in Table 11. Ingots used for met allographic analysis were pre-

Jan 1, 1968

By F. R. Brotzen, L. D. Whitmire

Single crystals of high-purity molybdenum were de-formed at temperatures from 195°to 473°K, and the effect of deformation on the electrical resistivily was deler-mined. To separale the resislivity components of point and line defecls some cryslals were annealed at 473°K. The vale of resislivily increase wilh strain was nearly linear and was strongly dependent upon the deformation temperature. Point dejects are annealed out without any effect on the flow stress. At low temperatures the flow stress is a linear function of the square root of the resistivity increase attributable to dislocations. ELECTRICAL-resistivity measurements have been used successfully to gain information on structural changes in metallic materials. During plastic deformation the electrical resistivity rises because of electron scattering from newly created lattice defects. Such measurements lend themselves, therefore, to corroborating results from direct observation of lattice defects and, to a certain extent, to correlating defect densities and distribution with mechanical properties. Published information on research with single crystals of the bcc metals of Group VI, particularly molybdenum, is still limited. Yet, molybdenum single crystals of relatively high purity can be readily prepared by electron-beam-melting techniques. Furthermore, some valuable information on the defect structure of deformed crystals by direct observation is available. Lawley and Gaigher,1 for example, have examined dislocation configurations in deformed molybdenum crystals by means of transmission electron microscopy. Their results revealed that the dislocation density and distribution were strongly dependent upon the deformation temperature. These findings differed from those by Keh and weissmann,2 who found that the average dislocation density in polycrystalline iron deformed between 138° and 298°K depended only on the degree of strain and not on the deformation temperature. Martin3 and peiffer4 showed that point defects introduced in polycrystalline molybdenum by cold work can be eliminated by annealing at a relatively low tempera-ture. In view of their work it became apparent that resistivity measurements of suitably annealed crystals could disclose changes in their dislocation structure and contribute to the understanding of the work hardening of molybdenum crystals. EXPERIMENTAL PROCEDURE Crystals were grown by electron-beam zone melting5,6 of 0.062-in.-diam molybdenum rods (99.99 pct) supplied by General Electric Lamp and Wire Division, Dover, Ohio. The crystals, about 4 in. long, were prepared by using five zone-refining passes at a speed of about 6 mm per min in a vacuum of about 5 X l0-6 Torr. The resistivity ratio of the crystal, p(4.Z°K)/p(273°K), was generally near 10-3. These crystals were used as tensile specimens of uniform diameter in the "as-grown" condition. They were oriented for maximum shear on the (011)[111] slip system (Schmid factor >0.49). The specimens were held in spherically seated Templin-type grips so as to minimize bending. Samples were deformed on an Instron machine at a strain rate of about 5 X 10-5 sec-1 in an isopentane bath with dry ice at 195°K, in ice water at 273°K, and in a vegetable-oil thermostat at 373° and 473°K. The temperature in the latter was maintained constant within +2°K. Resistance measurements were carried out with a Kelvin double bridge. The resistance of the potential leads was kept low by using large-diameter wires outside the low-temperature bath. Many of the resistance data were checked by measurements made with an ac bridge. Current and potential leads were spot-welded to the specimens. The distance between the potential leads, about 3 in., was also considered to be the gage length for the strain measurements. Diameter and gage length of the samples were measured optically with an error of less than 2 pct. These measurements were used also to insure that the deformation had been uniform over the gage length of the specimen. Resistivity changes were then determined from the resistance measurements at 4.2°K assuming constancy of volume. In the course of a test, the crystal diameter, gage length, and resistance at 4.2°K were determined first in the initial state and subsequently for various amounts of elongation.

Jan 1, 1968

By W. D. Robertson, J. -P. Briant, M. Gell

The distribulion of dislocatiorls genevnted during the propagalion of hydrogen-induced cracks in Fe-Si cryslcrls was studied as a funclion of temperature f-110o lo 243°C) and silicorz conlenl (3.1 and 4.2 pct). It zoas found that the clislocntiotl densily and the size of the plctslic zone increased with increasing tempevalnre and decreasing silicon conlent. Furtheruvzove, there was a correlcrtion in the dislocalion patterns formed around cracks that propagated at different tempevattrt-es in cvyslals of diffevent silicon contents such that a 1 pcl itlcverise in silicon content was equivalent to a lemperaluore redziclion of approximately 120°C. The experimenlal YeSnllS were compaved with the results of an elastic-plastic wodel that relates the size of the pluslic .zone to the cvack length, internal pressure, and yield stress. it was found that the clzunges in the dislocctlion cryrays with lemperature and combosition can be e-kplaincd by the lemperatrnre and composilion dependence of the yield stress. An wmtsual feature of this study was the observation of low -temperature noncrystrrllogruphic cracks. PLASTIC relaxation can occur at the edge of a moving crack by the operation of pre-existing dislocation sources or by the creation of new sources in a region of perfect 1attice.l&apos;2 The amount of relaxation in a given crystal depends on the crack velocity and the temperature, and can determine whether a crack propagates in a brittle or a ductile manner.1-3 Tetelman and Robertson4 observed microcracks m Fe-3 pct Si single crystals that formed on (100) planes by the precipitation of hydrogen gas during electrolytic charging at 23°C. The plastic deformation accompanying crack propagation was observed in the form of dislocation etch pits and an extensive analysis has been made of the size, shape, and crystallography of the dislocation arrays5-7 This paper describes the effect of temperature on the plastic deformation generated around hydrogen-induced cracks in Fe-3.1 pct Si and Fe-4.2 pct Si single crystals. The observations are compared with the results of an elastic-plastic model for yielding around a crack containing an internal pressure. 1) EXPERIMENTAL PROCEDURES The composition of the materials used in this study are given in Table I. Single crystals of alloy A and the 4.2 pct Si alloy were grown by the strain-anneal method; crystals of alloy B and the 5.1 pct Si alloy were cut from an ingot grown from the liquid. he ~ingle-cr~stal metallographic specimens had a Cross section of 0.100 by 0.050 in. with a length of at least 3/8 in. Specimens were annealed for 3 hr at

Jan 1, 1968

By David J. Mack, Dennis R. O’Boyle

The mechanical properties of three polycrystalline intermediale Phases that have the y bvass structure were measured in compression between 400° and 900°K. At the lower testing temperatures— termed Region I— no plaslic deformalion occurred prior to brittle fracture. A1 higher temperatuves— lermed Region III—the three phases deformted plaslically for all strain rules from 1.5 to 36.0 x 10-4 sec-1. The homologous temperature for the inilialion of plaslic flow increased in the same order as tile atomic size difference between atoms in each plmse (0.50Tmp for y AgZn, 0.62Tmp for y CuZn, and 0.76 Tmp for y CuCd). The increased flow resistance oj. y CuCd above 0.50Tmp is explaitzed in terms of the more random arrangement of copper and cadmiwn atoms on the laltice sites of&apos; the y bvass slrilctlire. Plaslic deformation of the three intevmiediate phases in the smooth plaslic flow region appears to be controlled by oacancy-induced dislocation climb. RESULTS are reported in this paper on the mechanical properties of three binary intermediate phases having the complex cubic y brass structure (D82, 143m) containing fifty-two atoms in the unit cell. The structure of the prototype y brass phase, y CuZn, was first analyzed by Bradley and Thewlis&apos; based on the X-ray work of Westgren and Phragmen.2 The y brass structure can be visualized as an arrangement of twenty-seven body centered cubes (3 by 3 by 3) into a unit cell containing fifty-four atoms. From this cell the center atom and the four corner atoms are removed and the remaining fifty-two atoms are slightly displaced, resulting in the y brass structure. Approximately thirty-five binary intermediate phases that have an electron to atom ratio of 21:13 have been reported to form the y brass structure. The three y brass intermediate phases selected for this study are formed from elements in groups IB and IIB of the first and second long period. Each compound exists over a composition range that includes the stoi-chiometric composition A5BB (Cu5Zn8, Ag5Zn8, Cu5Cd8). y CuZn (a0 = 9.944A) has solubility limits extending from 57 to 67 at. pct Zn at 500°C apd melts peritecti-cally at 834°C; y AgZn (a0 = 9.326A) has a solubility range from 58 to 63 at. pct Za and melts peritectically at 661°C. y CuCd (a, = 9.596A) melts congruently at 563°C and has a maximum range of solubility extending from 58 to 64 at. pct Cd. In order to minimize coring and microporosity during solidification, the composi- tion of the compounds that form peritectically (y CuZn and y AgZn) was chosen so that the temperature difference between the liquidus and the solidus is only a few degrees centigrade. In selecting y brass compounds for this study, phases were avoided that contained a transition element or that had an electron to atom ratio greater than 1.70. Hume-Rothery et a1.3 has observed that, when the electron to atom ratio of y brass intermediate phases exceeds 1.70, atoms begin to drop out of the unit cell to maintain a constant electron to unit cell ratio. EXPERIMENTAL PROCEDURE Each of the three intermediate phases was prepared from elements having a purity >99.999 pct. Only trace quantities of impurities (<0.0001 pct) were detected by spectrographic analysis of the four elements. A master alloy of each compound weighing approximately 130 g was prepared by melting the elements in evacuated sealed quartz tubes heated in an electric furnace. Specimens having the desired diameter for the mechanical property measurements were obtained by remelting the master alloy in a Vycor tube under argon and drawing specimens from the melt into 4-mm-diam quartz tubes. To obtain a smooth surface on specimens drawn from the melt, the inside of the quartz tube was coated with a thin layer of graphite formed by thermally decompositing acetone. All specimens were imbedded in sealing wax and cut to the proper length with a diamond-impregnated cut-off wheel. The individual specimens (4 mm diam by 8 mm long) were then sealed in evacuated Pyrex tubes and homogenized at 500°C for 72 hr. Chemical composition, variations over the length of the rod (10 cm long) were generally less than 0.2 pct and the analyzed composition differed from the desired composition by less than 0.5 pct.4 Metallographic evaluation of the specimens after homogenization showed no evidence of a second phase in any of the compounds. The average grain size of the specimens after homogenization was 1 to 2 mm. All mechanical property measurements were carried out in an argon atmosphere using a compression apparatus described previously.5 Prior to applying the load to the specimen, the test apparatus was evacuated, back-filled with argon, and heated to the test temperature for 20 min to establish thermal equilibrium. EXPERIMENTAL RESULTS Mechanical properties measured as a function of temperature and strain rate for each of the three y brass phases were similar. From room temperature to the ductile-to-brittle transition temperature, only elastic deformation was observed prior to fracture.

Jan 1, 1968

By K. A. Johnson, F. H. Ellinger, C. C. Land

The Pu-La alloy systenz has been studied by thertnal, tnzcrographic, and X-ray diffraction methods. It is churacterized by a liquid miscibility gap, a maximum solubility of about 20 ut. pct PM in y lanthunum and 19 at. pct PI* in 0 lanthanum, very little soluibility of lanthanum in the plulonium allotropes, and the absence of intermediate phases. THE existence of immiscible liquids in the Pu-La system has been reported by Schonfeld.1 A tentative phase diagram based on the results of thermal-analysis experiments has been constructed by Poole et a1 2 This diagram shows a liquid immiscibility loop with a monotectic at 77 at. pct La and 846°C. 7 lanthanum is shown to dissolve 20 at. pct Pu and to decompose by an inverse peritectic reaction (y La = L , + p La) at about 82 at, pct La and 833°C. The ß lanthanum solvus was not determined, but the thermal work indicated a maximum solubility of 16 at. pct Pu in ß lanthanum. The present investigation has defined the solubility limits of plutonium in y lanthanum and 0 lanthanum, and, with the exception of minor discrepancies, has verified the results of Poole et al. 1) EXPERIMENTAL The electrolytic plutonium melting stocks were better than 99.9 wt pct pure, the main impurities being 90 ppm Fe and 50 ppm W. The lanthanum melting stocks, supplied by Research Chemicals and the Cerium Metals Corp., were about 99 wt pct pure, the main impurity detected by our spectrochemical analysis being 2000 ppm Fe. The components for each alloy button (-5 g) were weighed on an analytical balance and were melted together in a conventional arc furnace. If no significant weight loss occurred during melting, the as-weighed

Jan 1, 1968

By R. C. Gifkins, K. U. Snowden

The value of the index n in power ktivs for the stress sensitivity of minimum creep rale at lead is derived front results drawn from lite literature and from previously unpublished nork on commercial (99.99 pel) and high-purity (99.999 pel) lead polycryslalline and hi crystal specimens. In tests al 0.5Tm (22 to 50&apos;C) for slvesses below 250 psi, n fulls to mily for poly-cr,yslullirle specimens, single crystals, and bicrystals, and toy grain boundary sliding in bicrystals. Between 250 and 500 psi there is a tyansilion range and, for the polycrystalline specimens al least, u high-stress regime for 500 to 1500 psi where n is 5 or 6. These results are such that none of the suggested stress taws can he used to extrapolate to very loir stresses. Meclianisms for deformation in Ike grains and toy grain boundary sliding in the low-strcss regime are outlined. In particular, the mechanism for grain boundary sliding involves sliding controlled by diffusion from tensile to compressire Ledges. predictions based on this model give promising numerical agree-nicul with experiment. II is suggested that the mechanism for grain boundary sliding may he important in other circumstances, e.g., in creep of ceramic materials or superplaslicity, because it can operate with lille or no dislocation aclirity. WhEN the stress dependence of secondary creep rate is represented by a power law the values taken by the stress exponent n are found to vary between 1 and 7, see, c.g., Garofalo.&apos; In Eq. 1 11 u is the applied stress and A a constant. The case for accepting values of v = 1 rests principally upon tests at high temperatures (>0.9Tm) and there have only been isolated tests at lower temperatures (rather than plots of creep rate against stress) for which the creep rates are such that some form of Nabarro-Herring creep with n = 1 is applicable. Hanson5 and Greenwood and cole6 plotted creep rate against stress for tests made in the vicinity of 0.5Tw, and found a "creep yield", so that below a certain low stress the creep rate was linearly related to stress: these observations appear to have been subsequently ignored. Various models have been proposed which agree with a large body of experimental results in which n equals -5 at high stresses (e.g., weertman7 and McLean8). Various alternatives to Eq. [1] have been proposed principally as a means of unifying creep data, but sometimes, it seems, in order to obviate the necessity for assuming a series of regimes of deformation associated with the various values of n; further refer- ence to these will be made in the section on stress laws. This paper calls attention to extensive results which show n = 1 for the creep of lead at room temperature (0.5 T,). RESULTS Fig. 1 is a composite diagram based on figures in the literature6,9,10 with additional results obtained by the present authors and their colleagues11,12 in the course of a number of investigations not directly concerned with stress sensitivity. In Fig. 1 In creep rate is plotted against In stress. The curves show results for two kinds of material. Lead I is of commercial purity (99.99 pct Pb) and lead IT a specially refined material, hydrogen-purified to remove oxygen; it contains 99.999 pct Pb. Curve A is for lead I in polycrystalline form (grain diameter 0.02 to 0.05 cm) at room temperature (22&apos; to 26°C). Curve B1 is for lead I, polycrystalline, tested at 50C. Curve B2 is for lead 11, polycrystalline (grain diameter 0.02 cm), tested at room temperature (22 O- Curves C to F relate to tests made of bicrystals of lead 11: all of the same nominal orientation ("Y" in Ref. 12). Curves C and V are for creep within the component crystals of the bi crystals at 22°C (AB and CD in Fig. 2). Curve E is for creep measured in a gage straddling the boundary, approximately 0.15 mm either side (BC in Fig. 2). Curve F shows rates of grain boundary sliding (as distinct from strain rates in the other curves), obtained by averaging the offsets of six marker lines on the bi-crystal boundaries. The principal feature of the results is that the stress sensitivity falls into two distinct regimes, according to whether the stress is below approximately 250 or above 500 psi (there is a transitional range between 250 and 500 psi). The new result is that below -250 psi two of the curves (A and BI) give a value of n 1, and the other curves also drop below n - 2 to -1.5 but do not extend to low enough stresses to show clear evidence of n 1. At very high stresses the curves tend to give values of n - 6, as previously determined in other investigations. Curve R2 for the high-purity lead in polycrystalline form at room tenlperature almost merges with B, and thus gives new significance to the values for stresses of 150 and 200 psi; previously&apos;3 these points had seemed to fall away from the curve of slope -3, but they now can be seen as almost completing a transition to n = 1. It should be noted that there was originally considerable apparent scatter in the results for the high-purity lead. However, this was found to be associated with annealing conditions or variations in residual content of oxygen and curve B2 was constructed using the highest rate (i .e., the rate for the purest lead) determined for each stress during the course of various investigations over the years: altogether, some forty tests were used in constructing curve R2.

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

Aclivilies of magnesium in liquid Alg-Si alloys have been delermined between 5 and 60 at. pcl Si, close to the melling point of Mg2Si, by an improved isopieslic melhod. Silicon specinrens, held in alumina crucibles and graplrile conlainevs of special design, were healed in a letrlpevalure gvadient and equilibrated with mag-nesilcrrl rapor in a closed lilanium system. The ther-madynamic Junctions were calculated and compared with the thermodyuamic properties of the other three mg- Gvoup IVB systems. Lattice paramelers of three Mg2X compounds were measured. The bonding in the Mg2X compounds is largely covalent with small and uarying amounts of metallic and ionic conlvibutions. The Mg-Si phase diagram1 has one congruent melting compound, Mg2Si, of essentially stoichiometric composition, two eutectics, and very limited terminal solid solubilities. Little information is available on the thermodynamic properties of this system. The free energy of formation of Mg2Si has been determined by the Knudsen cell technique2 in the range 572" to 680oC, by the transportation method3 between 858" and 950oC, and by the electromotive-force method4 in the range 400o to 600°C. Kubaschewski and villa5 and caulfield6 have measured the heat of formation of Mg2Si. An electromotive-force study of magnesium-rich liquid alloys was recently published by Sryvalin el al.7 The present investigation was undertaken to complete a general survey of the thermodynamic properties of the homologous series of Mg-Group IVB systems, i.e., Mg-Pb,a9,Mg-Sn,10,11 mg-Ge,12and Mg-Si. An isopiestic technique, previously developed for similar measurements on liquid Mg-sn11 and Mg-Ge alloys,12 was modified for the Mg-Si system. Specimens of the nonvolatile component, silicon, were contained in dense alumina crucibles placed inside covered graphite crucibles which were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure. The alumina crucibles prevented contact between the highly corrosive liquid Mg-Si alloys and graphite. The graphite cruci- bles effectively preserved the high-temperature equilibrium composition of the liquid alloys containing highly volatile magnesium on termination of the experiments during the quench to room temperature. EXPERIMENTAL PROCEDURE Silicon of semiconductor-grade purity (E. I. du Pont de Nemours and Co., Brevard, N.C.) and 99.99+ pct Mg (Dominion Magnesium Ltd., Toronto, Canada) were used. Graphite crucibles with press-fitted lids were machined from high-density (1.92 g per cu cm) rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The alumina crucibles had a purity of 99.7+ pct (Triangle RR grade, Morganite, Inc., Long Island City, N.Y.). In preliminary runs the liquid alloys were contained in graphite crucibles following the exact procedure developed for the Mg-Ge system.&apos;2 These runs failed due to appreciable reaction between the molten Mg-Si alloys and graphite, and the results have been discarded. The procedure was then modified and the Mg-Si alloys were subsequently held in alumina crucibles. For most of the runs alumina crucibles of known weight and approximately 6.3 mm ID, 12.5 mm height, 1.0 mm wall thickness were loaded with weighed amounts of silicon and encapsuled in tightly covered weighed graphite crucibles 5/16 in. ID, 2 in. helght, 3/32 in. wall thickness). The graphite crucibles were machined from rods which were 85 pct of the theoretical density. These crucibles were therefore sufficiently porous so as to permit magnesium vapor to effuse through the silicon under the experimental conditions of approximately 970O to 1220°C and 1 day equilibration time. However, negligible magnesium was lost from the crucible during the quench due to the slow effusion rate through the pores of the graphite. The inner alumina crucible prevented the liquid alloys from contacting the graphite, and the very tightly fitting graphite crucible lids served to retain any magnesium vaporizing from the alloys inside the crucibles during the quenching step.12 The loaded silicon-alumina-graphite cells were positioned, one above another, on a 16-in.-long titanium thermocouple well and tied securely to the titanium tube with thin molybdenum wires held in grooves around the circumference of the graphite crucibles. A thin (0.005-in.) molybdenum strip prevented contact between the graphite crucibles and the titanium. This assembly was lowered into a titanium reaction tube (la in. ID, 16 in. long, $ in. wall thickness) closed on one end which contained a 11/2-in.-long cylinder of magnesium at the bottom. The inner titanium thermocouple well was positioned eccentrically in the large tube because of the eccentric mounting of the cells on the well. Appropriate modifications of the titanium cap"&apos;12 were made to join the inner and outer titanium

Jan 1, 1968