By Robert A. Colten, Frederick C. Hull, Robert F. Mehl

It is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth.l,2 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in I939.3 Two types of process were described: (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures; and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth. Both cases are met in the formation of pearlite from austenite (Fig. I);2,4 the former, occurring near the knee of the S-curve, has been named "grain-boundary transformation," and the latter, occurring at temperatures near Ael, has been named "group-nodule transformation." In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important1,2 to obtain data on the rate of nucleation and the rate of growth of pearlite. Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the factors that affect hardenabil-ity; when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite.2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature, and the degree of homogeneity of the parent austenite. The studies are restricted chiefly to plain carbon commercial steels." Previous Data on Rate of nucleation and rate of Growth Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Meh1,l and by Dorn, De Garmo and Flanigan.2, It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc.), austenite grain size, and mode of formation of pearlite at the temperatures given. Except for the approximations of Mehl and the work of Dorn, austenite grain size was disregarded, though it is well known

Jan 1, 1942

By J. K. Stanley, R. F. Meel

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

By R. F. Meel, J. K. Stanley

The recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are emp1oyed.l Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystal- lization is not a heterogeneous reaction within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress. 4,5 The theory of recrystallization is not in advanced state; if recrystallization data were obtained in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert mcasurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now available for the case of three-dimensional recrystallization (recrystallization of

Jan 1, 1942

By J. T. Eash, N. B. Pilling

As a group, the alloys of iron, nickel and carbon are, in application, one of the most versatile of the ferrous alloy family, and while many investigations have been made of their properties and structure only a few attempts have been made to show the microstructural relation over a wide range of composition. It is neccssary at once to be clear about the kind of structural relation with which we are concerned. The equilibrium diagram provides quantitative data regarding structural make-up and its variation with temperature, but equilibrium structures often are far different from the technologically significant ones. This is particularly true of steels and cast irons, and some of the most important cornponents of their structure may have no place in the diagram of equilibrium. The fugitive phases that result from transFormation are dealt with in a highly detailed and descriptive manner in. the S-curves originated by Bain. The present effort lies in a still different field, which is to portray the relation between sweeping changes in composition and in resultant structure, under controlled but nonequilib-rium conditions of thermal treatment. The Guilletl diagram presented in 1903 was the initial attempt at such a correlation and frequent references to this diagram can be found in the literature even though later work has shown it to require considerable modification. Kase2 published in 1925 a diagram that was based upon observations of furnace-cooled melts: At low carbon contents this diagram agreed fairly well with experience in showing pearlite to exist in alloys containing up to 6 per cent nickel, and completely austenitic steels at 24 to 28 per cent nickel. At high carbon contents, however, irons were indicated as being martensitic at around 2 per cent nickel and austenitic at 12 per cent nickel; these interpretations are open to serious question. Based upon experience with steels and cast iron, Wickenden3 suggested a diagram that agreed fairly well with Kase's in the steel range but which presented a wide departure from it in the higher-carbon, high-nickel regions. In its broad picture, the Wickenden diagram is an approach to "practical" structures. Reference may be made at this point to the efforts of Marsh5 to construct an iron-nickel-carbon equilibrium diagram by the coordination of scattered data, which are described at length in the monograph cited. None of these preceding attempts has appeared to meet the need for an exposition of the structural sequence that is encountered in traversing the nickel-steel nickel-cast-iron range under what might be called ordinary departures from equilibrium. ExperimentaT. Conditions Since the intent has been to establish structures developed under arbitrary conditions, experimental details have perhaps more than usual importance. Three of these conditions should particularly be noticed: (I) the material was cast and not subjected

Jan 1, 1942

By J. T. Eash, N. B. Pilling

As a group, the alloys of iron, nickel and carbon are, in application, one of the most versatile of the ferrous alloy family, and while many investigations have been made of their properties and structure only a few attempts have been made to show the microstructural relation over a wide range of composition. It is neccssary at once to be clear about the kind of structural relation with which we are concerned. The equilibrium diagram provides quantitative data regarding structural make-up and its variation with temperature, but equilibrium structures often are far different from the technologically significant ones. This is particularly true of steels and cast irons, and some of the most important cornponents of their structure may have no place in the diagram of equilibrium. The fugitive phases that result from transFormation are dealt with in a highly detailed and descriptive manner in. the S-curves originated by Bain. The present effort lies in a still different field, which is to portray the relation between sweeping changes in composition and in resultant structure, under controlled but nonequilib-rium conditions of thermal treatment. The Guilletl diagram presented in 1903 was the initial attempt at such a correlation and frequent references to this diagram can be found in the literature even though later work has shown it to require considerable modification. Kase2 published in 1925 a diagram that was based upon observations of furnace-cooled melts: At low carbon contents this diagram agreed fairly well with experience in showing pearlite to exist in alloys containing up to 6 per cent nickel, and completely austenitic steels at 24 to 28 per cent nickel. At high carbon contents, however, irons were indicated as being martensitic at around 2 per cent nickel and austenitic at 12 per cent nickel; these interpretations are open to serious question. Based upon experience with steels and cast iron, Wickenden3 suggested a diagram that agreed fairly well with Kase's in the steel range but which presented a wide departure from it in the higher-carbon, high-nickel regions. In its broad picture, the Wickenden diagram is an approach to "practical" structures. Reference may be made at this point to the efforts of Marsh5 to construct an iron-nickel-carbon equilibrium diagram by the coordination of scattered data, which are described at length in the monograph cited. None of these preceding attempts has appeared to meet the need for an exposition of the structural sequence that is encountered in traversing the nickel-steel nickel-cast-iron range under what might be called ordinary departures from equilibrium. ExperimentaT. Conditions Since the intent has been to establish structures developed under arbitrary conditions, experimental details have perhaps more than usual importance. Three of these conditions should particularly be noticed: (I) the material was cast and not subjected

Jan 1, 1942

By Blake M. Loring

Recently the S-curves for 30 to 40 alloy steels have been pub1ished.l.2 These steels show individual characteristics, which make each additional S-curve of great interest. There are important differences in the mechanism of the transformation process, the type of transformation product, and the influence of alloying elements. Steels of the same general alloy composition may possess such variable characteristics with regard to the length of time of isothermal transformation that an S-curve for each heat of steel may be desirable. In the present work the isothermal transformation of a steel having the following composition and grain size was studied: 0.29 per cent carbon; 0.21 manganese; 0.026 phosphorus; 0.017 sulphur; 0.056 silicon; 1.45 chromium; 3.25 nickel; austenite grain size, 7. The progress of the isothermal transformation was followed by several different methods, including hardness measurements, dilatometer observations, and examinations of the microstructure. It was not expected that these methods would be in precise agreement.3 Accordingly, the changes in microstructure and hardness were given additional weight in determining the initial stage of transformation and the dilatometer measurements were relied on in estimating the completion of the process. The beginning of transformation was indicated by I per cent of transformation products and the end of transformation by about 99 per cent. The reproducibility of the various methods in the ranges of highest sensitivity was checked by several observations at each time and temperature. The steel used in this investigation was annealed for 24 hr, at 925°C. Macroetching revealed no serious segregation. The specimens for the metallographic and hardness investigations were 1¼ by ½ by ? in. Wires attached to the samples were used for handling. instead of tongs, to avoid chilling. The specimens were heated at 845°C. for ½ hr. and quenched into constant-temperature salt baths held at various temperatures from 205' to 650°C. The time required to transfer the specimens was found to be about 1½ sec., and nearly 5 sec. more was required for them to come to the temperature of the bath. After various lengths of time in the constant-temperature baths the specimens were quenched in water at 2I°C. The specimens were cut in half for the metallographic examination, to provide a surface free from decarburization. To determine the beginning and end of the transformation the percentage of transformation determined metallographically and by hardness was plotted against time. A planimeter was used in the metallographic determination. The hardness and metallographic determinations made at room temperature were confirmed reasonably well by dilatometer measurements taken during the process of transformation at the various temperatures. Two dilatometers were used to

Jan 1, 1942

By Blake M. Loring

Recently the S-curves for 30 to 40 alloy steels have been pub1ished.l.2 These steels show individual characteristics, which make each additional S-curve of great interest. There are important differences in the mechanism of the transformation process, the type of transformation product, and the influence of alloying elements. Steels of the same general alloy composition may possess such variable characteristics with regard to the length of time of isothermal transformation that an S-curve for each heat of steel may be desirable. In the present work the isothermal transformation of a steel having the following composition and grain size was studied: 0.29 per cent carbon; 0.21 manganese; 0.026 phosphorus; 0.017 sulphur; 0.056 silicon; 1.45 chromium; 3.25 nickel; austenite grain size, 7. The progress of the isothermal transformation was followed by several different methods, including hardness measurements, dilatometer observations, and examinations of the microstructure. It was not expected that these methods would be in precise agreement.3 Accordingly, the changes in microstructure and hardness were given additional weight in determining the initial stage of transformation and the dilatometer measurements were relied on in estimating the completion of the process. The beginning of transformation was indicated by I per cent of transformation products and the end of transformation by about 99 per cent. The reproducibility of the various methods in the ranges of highest sensitivity was checked by several observations at each time and temperature. The steel used in this investigation was annealed for 24 hr, at 925°C. Macroetching revealed no serious segregation. The specimens for the metallographic and hardness investigations were 1¼ by ½ by ? in. Wires attached to the samples were used for handling. instead of tongs, to avoid chilling. The specimens were heated at 845°C. for ½ hr. and quenched into constant-temperature salt baths held at various temperatures from 205' to 650°C. The time required to transfer the specimens was found to be about 1½ sec., and nearly 5 sec. more was required for them to come to the temperature of the bath. After various lengths of time in the constant-temperature baths the specimens were quenched in water at 2I°C. The specimens were cut in half for the metallographic examination, to provide a surface free from decarburization. To determine the beginning and end of the transformation the percentage of transformation determined metallographically and by hardness was plotted against time. A planimeter was used in the metallographic determination. The hardness and metallographic determinations made at room temperature were confirmed reasonably well by dilatometer measurements taken during the process of transformation at the various temperatures. Two dilatometers were used to

Jan 1, 1942

By R. W. Gurry

In the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and III0°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon conteDt of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched, The mean result of concordant ments-—taeats-is-^that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C .(i755°F.) and 1.89 per cent at III0°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutec-toid temperature (738°C. or I360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature II35°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. Experimental Procedure The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.' In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (I6°F.) but at a given location the temperature remained within +o.5°C. (o.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (I760°F.) and III0°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with toluene; this quickly produced on the

Jan 1, 1942

By R. W. Gurry

In the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and III0°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon conteDt of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched, The mean result of concordant ments-—taeats-is-^that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C .(i755°F.) and 1.89 per cent at III0°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutec-toid temperature (738°C. or I360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature II35°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. Experimental Procedure The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.' In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (I6°F.) but at a given location the temperature remained within +o.5°C. (o.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (I760°F.) and III0°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with toluene; this quickly produced on the

Jan 1, 1942

By R. W. Gurry

When a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, yet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. Experimental Procedure Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;' it suffices to state here that the carburization lasted about I40 hr. at 760°C. (1760°F.) and 44 hr. at iiio°C. (2030°F.), these periods being long enough-—on the basis of the calculations presented later—to ensure that the specimen was about 99.9 per cent saturated at each temperature. The specimen was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully carburized specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

By R. W. Gurry

When a steel in the austenitic state, with all its carbon in solution, is maintained, at constant temperature, in contact with a gas that removes the carbon from the surface, yet without otherwise altering the composition of the steel, the change in weight of the specimen, after any period of exposure, is a direct measure of the amount of carbon it has then lost. The purpose of the present paper is to show how, by application of established mathematical reasoning based on the fundamental diffusion law and on certain postulates, this loss of weight yields a complete picture of the distribution of carbon throughout a specimen of regular shape after any period of exposure, with all the accuracy required in any practical occurrence of decarburization. Precisely the same is true for the gain in weight during the reverse process of carburization, or for the gradual gain or loss of any element, so long as the steel comprises only a single phase at temperature, provided always that the experimental conditions conform to the postulates. The change in carbon content from surface to center of the specimen is always continuous, when everything is in solution, even though under the microscope the decarburized zone (or carburized rim) may appear to be sharply defined. The experimental procedure is described and some typical results are presented, which are then interpreted by application of the diffusion law. Experimental Procedure Initially an endeavor was made to follow the gain of weight during the process of carburization in a hydrogen-toluene atmosphere, but it was soon found that the specimen became coated with graphite, which could not be removed without some loss of metal; therefore it was decided to continue carburization until the steel was saturated throughout, to remove all graphite from the surface of the specimen, and then to follow the loss of weight during decarburization in a moist hydrogen atmosphere at the same temperature as that used for carburizing. The carburizing procedure has been described in an earlier paper;' it suffices to state here that the carburization lasted about I40 hr. at 760°C. (1760°F.) and 44 hr. at iiio°C. (2030°F.), these periods being long enough-—on the basis of the calculations presented later—to ensure that the specimen was about 99.9 per cent saturated at each temperature. The specimen was a cylinder about 3.8 cm. long and 0.475 cm. in diameter; the materials were carbonyl iron, a commercial low-metalloid iron, and a steel with 3.6 per cent nickel and the usual proportion of other elements. The fully carburized specimen, after cooling at the top of the furnace tube, was placed in a lathe and sandpapered to remove all graphite; then the diameter was measured with a micrometer caliper, and the initial weighing (corresponding to complete saturation) was made. By means of a

Jan 1, 1942

By William L. Fink, H. R. Freche

The constitution of the aluminum-cobalt alloys has been the subject of relatively few investigations. Brunckl analyzed the residue which remained after treating the 17 per cent cobalt alloy with dilute hydrochloric acid. The results of the analyses indicated the existence of a compound Co3Al13. Guillet2 published a liquidus for the aluminum-cobalt system which contained two maxima corresponding to CoA16 and CoAl2 and two eutectic points at 30 and 74 per cent Co. The most extensive investigation of the system was carried out by Gwyer13 whose results are summarized in Fig. 1. It will be noted that at the aluminum end there is a suppressed eutectic at 644' C. By extrapolation of the duration of the eutectic arrest to zero, the composition of the compound was placed at Co3Al13. Another thermal arrest was noted at 550" C., which Gwyer attributed to a peritectic reaction. The present investigation of the aluminum end of the aluminum-cobalt system is the eleventh of a series dealing with the constitution of aluminum-rich alloys prepared from electrolytically refined a1uminum.l Preparation of Alloys.—The alloys used in this work were all prepared from electrolytically refined aluminum, the analysis of which is shown in Table 1. In preparing some of the alloys, metallic cobalt (98 to 99 per cent) was used either directly or in the form of an intermediate alloy, the composition of which is given in Table 1. In order to obtain alloys of higher purity, cobalt was introduced into some of the alloys by means of chemically pure cobaltous chloride which was readily reduced by the aluminum. A small electric furnace with nickel-chromium heating elements was used in the preparation of the alloys. Chemical Analysis.—An analysis sample from each melt was chill-cast in the form of a plate 3/16 in. thick. In all cases the casting temperature was well above the liquidus. Cobalt was determined electrolytically in all alloys containing more than 0.05 per cent cobalt and by the nitroso-

Jan 1, 1932

By E. H. Dix

The work of Merical and other investigators indicates that the phenomenon of age-hardening in alloys of the duralumin type is primarily dependent upon the variation in the solubility of copper with temperature. In addition to copper, however, these alloys contain small amounts of magnesium, silicon, manganese and iron, which may affect the age-hardening either directly or indirectly. The effect of these elements on the solubility of copper and on the manner in which this solubility varies with the temperature is of considerable interest, therefore. The effect of magnesium is of especial interest because apparently it exerts a marked effect on the natural or room-temperature aging of alloys of the type described.2 A series of investigations3 has been in progress in the research laboratories of the Aluminum Company of America to determine the functions * Metallurgist, Aluminum Research Laboratories. f Metallurgical Division, Aluminum Research Laboratories. Formerly with Metallurgical Division, Aluminum Research Laboratories. 1 P. D. Merica, It. G. Waltenberg and H. Scott: Heat Treatment of Duralumin. U. S. Bur. Stds. Sn. Paper 347 (1910). 2 M. Gayler: Constitution and Age-Hardening of Alloys of Aluminum with Copper, Magnesium, and Silicon in the Solid State. Jnl. Inst. Met. (1922) 28, 213. W. Fraenkel: Vergutbare Aluminiumlegiengen. Ztsch. Melallkunde. (1920) 12, 427. E. H. Dix, Jr.: Note on the Microstructure of Aluminum-Iron Alloys of High Purity. Proc. Amer. Soc. Test. Mat. (1925) 26, Pt. 2, 120. E. H. Dix, Jr. and H. H. Richardson: Equilibrium Relations in Aluminum-copper Alloys of High Purity. Trans. A. I. M. E. (1926) 73, 560. E. H. Dix, Jr. and W. D. Keith: Equilibrium Relations in Aluminum-manganese Alloys of High Purity. Proc. Inst. Met. Div., A. I. M. E. (1927) 315. E. H. Dix, Jr. and A. C. Heath, Jr.: Equilibrium Relations in Aluminum-silicon and Aluminum-iron-silicon Alloys of High Purity. Proc. Inst. Met. Div., A. I. M. E. (1928) 164. E. H. Dix, Jr. and F. Keller: Equilibrium Itelations in Aluminum-magnesium Alloys of High Purity. Proc. Inst. Met. Div., A. I. M. E. (1920) 351. E. H. Dix, Jr., F. Keller and R. W. Graham: Equilibrium Relations of Aluminum-magnesium Silicide Alloys of High Purity. Trans. A. I. M. E., Inst. Met. Div. (1931) 404. W. L. Fink and K. R. Van Horn: Constituents of Aluminum-iron-silicon Alloys. Trans. A. I. M. E., Inst. Met. Div. (1931) 383.

Jan 1, 1932

By William L. Fink, Kent R. Van Horn

Zinc is one of the effective elements introduced to enhance the strength of aluminum. This strengthening is principally attributable to the high solid solubility of zinc in aluminum and the pronounced variation of solubility with temperature. Consequently an accurate determination of the solid solubility curve is desirable. The solid solubility relations have been studied by numerous investigators. Shepherd1 first established the existence of a solid solution region at the aluminum end of the diagram (-v phase) by specific volume and microscopic determinations. Bauer and Voge12 published a constitutional diagram which showed the limits of solid solubility as determined by thermal and microscopic methods. Hanson and Gayler3 presented the aluminum-zinc diagram which is now most generally accepted (Fig. 1). Chill-cast samples were given thermal treatments designed to obtain equilibrium conditions, quenched, and microscopically examined. The solubility was placed between 15 to 20 per cent at 60" C., 20 to 22 per cent at 140" C. and 36 to 38 per cent at 270" C. Sander and Meissner decidedly modified the limits of the -y phase field of Hanson and Gayler's diagram by using similar methods on chill-cast specimens annealed for a shorter period of time. Tanabe,s utilizing dynamic hard-ness, electrical conductivity and dilatometric measurements of specimens at temperature, obtained values comparable to Hanson and Gayler's at room temperature, but appreciably lower at higher temperatures. Nishimura6 concluded from age-hardening results of aluminum-zinc alloy chill castings, which had been quenched from 400" to 500" C., that the solubility of zinc in aluminum at room temperature is less than 5 * Metallurgical Division, Aluminum Research Laboratories. 1 E. S. Shepherd: Aluminum-Zinc Alloys, Jnl, phys. Chem. (1905) 9, 504. 2 0. Bauer and 0. Vogel: Aluminum-Zinc Alloys, Int. Jn1. Melallog. (1916) 8, 101. 3 D. Hanson and M. V. L. Gayler: A Further Study of the Alloys of Aluminum and Zinc. Jnl. Inst. Met. (1922) 27, 267. 4 W. Sander and K. L. Meissner: ZII~ Kenntnis der Konstitution der Aluminium-Zinklegierungen. Ztsch. f. Metallkunde (1922) 14, 385. 4 T. Tanabe: Studies in the Aluminum-Zinc System, Jnl. Inst. Met. (1924) 32, 415 6 H. Nishimura: On the Age-Hardening of Aluminum-Rich Al-Zn Alloys. Mem. Kyoto Imp. Univ. (1924) 3, 133.

Jan 1, 1932

By Cyril Stanley Smith, W. Earl Lindlief

A study of the mechanical properties of the alloys of copper and silver led to the discovery that the solubility of silver in copper was greatly different from that generally supposed, therefore some work was done to determine the solubility with greater accuracy than had previously been achieved. After the work had been completed, two papers were published' giving solubility figures which agreed closely with one another and with the work described herein. A detailed comparison of that work with the present will be given later. Preparation of Allots The copper used in making the alloys was electrolytic ingot of high purity. The silver was prepared by precipitation as chloride from nitric acid solution, followed by fusion of the washed precipitate with sodium carbonate and potassium nitrate. This method gives metal containing at least 99.99 per cent silver. The copper was first melted under charcoal in a small electric resistance furnace and the silver added as pure silver, it being unnecessary to make any intermediate alloys. After thorough stirring the metal was poured into a mold of suitable form. The alloys contained between 0.008 and 0.015 per cent of oxygen. Small amounts of oxide were visible under the microscope, but it is not believed this would have much effect on the results. Copper-silver alloys are notorious for segregation, consequently a few experiments were carried out to find a form of casting with as little segregation as possible. A mold 6 in. long and 1/2-in. dia. was first used, and an alloy nominally containing 5 per cent silver was cast in it, while some of the same alloy was poured directly into water to obtain the maximum rate of cooling possible. Analyses were made both on this sample and on turnings from the top and bottom of the 1/2 in. dia. cast-ing, the turnings being separated into three parts according to the position

Jan 1, 1932

By Walter R. Hibbard, Cyril Stanley Smith

IN 1929 one of the authors1 determined the constitution of copper-silicon-manganese alloys contailling over go per cent copper. Through a combination of circumstances the presence of the copper-silicon kappa phase was overlooked in both binary and ternary systems. In the binary system the omission has already been rectified.2,3 To establish the limits of this phase in the ternary system, the samples that had been heat-treated at the time of the original research have now been re-examined, using more careful technique. Full details of the compositions used and the temperatures and times of heat-treatment are to be found in the earlier paper.2 The etching reagent now used to distinguish the kappa phase had the following composition: hydrogen peroxide (30 vol.), 2o c.c.; water, 25 c.c.; 20 per cent potassium hydroxide solution, 5 c.c.; ammonium hydroxide (0.90 sp. gr.), 50 c.c. 'I'able I lists the newly observed structures. In virtually every case the constituents are the same as those previously recorded, except where kappa is now shown to be present as a result of the improved etching technique. X few other changes will be noted (No. 138 at 450°C., No. 147 at 550°C., Nos. 153 and 149 at 75o°C.). The change from liquid to beta in equilibrium with kappa in No. 137 at 800°C. is based upon newly heat-treated samples. The alloy is very near the solidus at 800°C. and probably there was a slight error in the old heat-treatment temperature. The isothermal phase diagrams shown in Figs. I to 6 were reconstructed on the basis of the new studies. The presence of manganese does not greatly change the composition limits of the kappa phase or cause the K-a + Y change to occur at a markedly different temperature. There is some uncertainty regarding the range of existence of beta, for alloys were not spaced very closely in composition. The proposed diagrams, however, are in accordance with the available experimental data and with the dictates of the phase rule. Theoretically necessary fields with no experimental points are delineated by dotted lines. The alpha boundaries at all temperatures are shown together in Fig. 7. This includes also some additional points on the alpha boundary at 300' and 350°C., which were obtained as a result of electrical-conductivity measurements. Two series of seven alloys with increasing manganese content but with silicon constant at 1.90 + 0.03 per cent or 2.42 ±. 0.05 per cent were cast in ingots of 3-in: diameter. These were hot-rolled, homogenized and drawn to wire, finished at 0.08-in. diameter with a 61 per cent reduction of area following annealing at 700°C. Conductivity determinations were made before and after annealing for 30 days at 300°C. or 21 days at 350°C. Figs. 8 and 9 show the change of conductivity produced by this annealing, plotted against manganese

Jan 1, 1942

By Walter R. Hibbard, Cyril Stanley Smith

IN 1929 one of the authors1 determined the constitution of copper-silicon-manganese alloys contailling over go per cent copper. Through a combination of circumstances the presence of the copper-silicon kappa phase was overlooked in both binary and ternary systems. In the binary system the omission has already been rectified.2,3 To establish the limits of this phase in the ternary system, the samples that had been heat-treated at the time of the original research have now been re-examined, using more careful technique. Full details of the compositions used and the temperatures and times of heat-treatment are to be found in the earlier paper.2 The etching reagent now used to distinguish the kappa phase had the following composition: hydrogen peroxide (30 vol.), 2o c.c.; water, 25 c.c.; 20 per cent potassium hydroxide solution, 5 c.c.; ammonium hydroxide (0.90 sp. gr.), 50 c.c. 'I'able I lists the newly observed structures. In virtually every case the constituents are the same as those previously recorded, except where kappa is now shown to be present as a result of the improved etching technique. X few other changes will be noted (No. 138 at 450°C., No. 147 at 550°C., Nos. 153 and 149 at 75o°C.). The change from liquid to beta in equilibrium with kappa in No. 137 at 800°C. is based upon newly heat-treated samples. The alloy is very near the solidus at 800°C. and probably there was a slight error in the old heat-treatment temperature. The isothermal phase diagrams shown in Figs. I to 6 were reconstructed on the basis of the new studies. The presence of manganese does not greatly change the composition limits of the kappa phase or cause the K-a + Y change to occur at a markedly different temperature. There is some uncertainty regarding the range of existence of beta, for alloys were not spaced very closely in composition. The proposed diagrams, however, are in accordance with the available experimental data and with the dictates of the phase rule. Theoretically necessary fields with no experimental points are delineated by dotted lines. The alpha boundaries at all temperatures are shown together in Fig. 7. This includes also some additional points on the alpha boundary at 300' and 350°C., which were obtained as a result of electrical-conductivity measurements. Two series of seven alloys with increasing manganese content but with silicon constant at 1.90 + 0.03 per cent or 2.42 ±. 0.05 per cent were cast in ingots of 3-in: diameter. These were hot-rolled, homogenized and drawn to wire, finished at 0.08-in. diameter with a 61 per cent reduction of area following annealing at 700°C. Conductivity determinations were made before and after annealing for 30 days at 300°C. or 21 days at 350°C. Figs. 8 and 9 show the change of conductivity produced by this annealing, plotted against manganese

Jan 1, 1942

By Cyril Wells, Robert F. Mehl

The purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2o C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made2. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsenl that variations as great as 30' C. exist in the reported data on the A3 temperatures in iron-carbon alloys. Fortunately, the Aa temperature in pure iron is now known to be 910" C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato5 on both hypoeutectoid and hyper-eutectoid steels. Esser made a dilatometric and magnetic study of iron and iron-carbon alloys containing 0.06 to 0.86 per cent C, for which a high purity is claimed. Presumably the electrolytic iron was reasonably pure, but the alloys contained considerable impurities, on the average totaling 0.35 per

Jan 1, 1937

By C. O. Burgess, W. D. Forgeng

The results of an investigation of the ternary system iron-chromium-silicon were reported in 1936 by the present authors.l Partly for the sake of theoretical interest, and partly because of the possible commercial importance of these alloys, the present investigation was undertaken to determine the effect of some of the commoner elements likely to occur, deliberately or otherwise, in such alloys if made on a commercial scale. The elements thus added were carbon, nickel or manganese. The alloys studied were, therefore, parts of quaternary systems. This investigation was concerned primarily with the effect of these additional elements on the alpha-iron phase and the boundary between this phase region and the alpha plus sigma two-phase region. The sigma phase is a ternary solid solution based upon the compound FeCr. The work was performed mainly by X-ray methods, but a number of microscopic examinations were also made and are reported. While isolated alloys in the composition ranges studied may have been discussed in metallurgical publications, no systematic investigation of any assistance to us was found. Of the earlier work, the investigations on the iron-chromium-carbon system and on the chromium carbides by Westgren and his coworkers2'3 enabled us to identify the carbide phase. Several articles appeared after the present experimental work had been completed. Lucas and Wintrup4 determined the solubility of carbon in molten iron-chromium-silicon alloys. Tofaute and his coworkers5'6 have made detailed studies of the iron-chromium-carbon system, which will be referred to later. Materials and Methods Materials.—The iron, chromium and silicon used were essentially the same as those used in the investigation of the ternary system.l The

Jan 1, 1938

By C. O. Burgess, W. D. Forgeng

The results of an investigation of the ternary system iron-chromium-silicon were reported in 1936 by the present authors.l Partly for the sake of theoretical interest, and partly because of the possible commercial importance of these alloys, the present investigation was undertaken to determine the effect of some of the commoner elements likely to occur, deliberately or otherwise, in such alloys if made on a commercial scale. The elements thus added were carbon, nickel or manganese. The alloys studied were, therefore, parts of quaternary systems. This investigation was concerned primarily with the effect of these additional elements on the alpha-iron phase and the boundary between this phase region and the alpha plus sigma two-phase region. The sigma phase is a ternary solid solution based upon the compound FeCr. The work was performed mainly by X-ray methods, but a number of microscopic examinations were also made and are reported. While isolated alloys in the composition ranges studied may have been discussed in metallurgical publications, no systematic investigation of any assistance to us was found. Of the earlier work, the investigations on the iron-chromium-carbon system and on the chromium carbides by Westgren and his coworkers2'3 enabled us to identify the carbide phase. Several articles appeared after the present experimental work had been completed. Lucas and Wintrup4 determined the solubility of carbon in molten iron-chromium-silicon alloys. Tofaute and his coworkers5'6 have made detailed studies of the iron-chromium-carbon system, which will be referred to later. Materials and Methods Materials.—The iron, chromium and silicon used were essentially the same as those used in the investigation of the ternary system.l The

Jan 1, 1938