By Lawrence H. Van Vlack, Otta K. Riegger

Periclase-type oxides were examined microscopically after being exposed to siliceous liquids. The rate of grain growth was found to be inversely proportional to the grain diameter. Grain growth proceeds more rapidly at higher temperatures, but is retarded by increasing liquid contents. aMag-nesiowiistites with higher MgO contents grow less rapidly than those with higher FeO contents. The growth rate is reduced by the presence of a second solid phase. The silica-containing liquid penetrates as a film between the individual magnesiowus tite grains. This is independent of time, temperature, amount of liquid, or the MgO/ Fe0 ratio. When present, olivine and spinel-type phases can provide a solid-to-solid &apos;&apos;bridge" between magnesioustite grains. THIS paper presents the results of a study of the microstructures of periclase type oxides in the presence of a silicate liquid. The purpose was to learn more about the effect of service factors such as 1) time, 2) temperature, and 3) liquid content upon A) grain growth, and B) liquid location among the solid grains. This study was prompted by the fact that periclase refractories are known to have very little solid-to-solid contact when the phases which are present are limited to periclase and liquid. Such a micro-structure gains industrial significance because it permits fracture during service when stresses are applied at high temperatures. The details of ceramic microstructures have not received extensive attention. This is in contrast to the extensive attention given to a) the phase relationships pertaining to refractory compositions, and b) the details of the microstructures of comparable metallic materials. A brief review will be made of the pertinent phase relationships and microstructural considerations in general, as well as of refractory compositions. a) Phase Relationships. This investigation was limited to those compositions in which (Mg, Fe)O was the solid phase. MgO and FeO form a complete series of solid solutions. Pure MgO has the name of periclase. The related FeO structure is called wustite. Both have the NaC1-type structure: however, wustite possesses a cation deficiency so that the true composition is Fe<10 even in the presence of metallic iron. The phase relationships involving solid (Mg, Fe)O and a silicate liquid are shown in Fig. 1. In this case. the liquid is saturated with (Mg, Fe)o. There-fore its SiOz content is below that encountered in orthosilicate liquids. As a consequence the liquid phase specie:; are primarily the following ions: and 0-&apos; plus occasional Fe+ ions. Two features are of importance: a) the liquid contains relatively small species and b) the liquid contains large quantities of the same species as the solid. viz., Fig. 2 shows the system, FeO-SiOz, which will be used in some of the discussions that follow. This diagram is the right side, vertical section of Fig. 1. Here, as pre\iously, the composition at the FeO end of the diagram is nonstoichiometric, varying from Feo.950 when the liquid oxide is in contact with the solid iron, to about Fe 0, when the solid oxide is in equilibrium with an atmosphere of equal proportions of CO and C02 at the solidus temperature. The Fe/O ratio will be maintained in wustite in the presence of SiO,. However, the FeM/Fe++ ratio in the liquid will be lower because of the effect OIF the SiO, on the activity of the FeO. With the addition of MgO to wustite, the over-all composition (IvZg, Fe)@, has a value of x lying between 0.9 and 1.0 when the COz/CO ratio is 1.0&apos;. b) Microstructures. In general, published attention to refractory microstructures has been directed toward the phase analyses that accompany compositional variations. This is illustrated by Harvey6 in his work on silica brick and by wells7 in his work on periclase brick. In each case, a series of altered zones is encountered which provides a sequence of phase associations. If due consideration is given to reaction kinetics, such an examination reveals phases that are compatible with equilibrium studies. Admittedly, however, it is often necessary to determine more complicated polycomponent systems to account for all the phases present.8 Relatively little attention has been given to microstructural geometry in ceramic materials. Certainly less attention has been given to this aspect of ceramic microstructures than to the size, shape, and distribution of the constituent phases in metals. Burke has pointed out that the grain size of oxides follows the same growth rules as for metals, viz.,

Jan 1, 1962

By E. T. Turkdogan, P. Grieveson

STAFF: Editor, Gerhard Derge Acting Editor, Paul G. Shewmon Carnegie lnstitute of Technology Sc hen ley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: Karl L. Fetters, President; J.S. Smart, Jr., Past-President; R. C. Cole, Vice President; R. L. Hennebach, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: W. 0. Phil-brook, Chairman; H. L. Bishop, R. C. Cole, J. N. Hobstetter, W. A. Krivsky, E. R. Morgan, F. C. Langenberg, R. E. Lund, Paul Queneau, L. L. Seigle, R. L. Smith, and T. &apos;4. Wainwright. Review and selection of manuscripts is under the supervision of the following Publications Committes: Extractive Metallurgy Division: R. E. Lund, Chatrmon; M. E. Wodsworth, Vice Chairman; D. H. Baker, Jr., G. M. Bell, R. E. Groce, W. A. Krivsky, R. A. Lewls, Charles O&apos;Neill, A. W. Schlechten, R. E. Shinkoskey, and W. W. Stephens. Iron and Steel Division: T. V. Wainright, Choirman; H. L. Bishop, R. E. Boni, T. E. Dancy, C. W. Murphy, Johonnes M. Uys, J. B. Wagstaff, and R. G. Ward. lnstitute of Metols Division: J. N. Hobstetter, Chairman; P. A. Beck, J. J. Becker, G. F. Bolling, J. O. Brittain, J. 8. Clark, R. S. Davis, A. E. Dwight, R. W. Fountain, L. R. Girifalco, J. C. Gurland, H. S. Kclish, E. L. Harmon, J. J. Heger, A. A. Hendrickson, L. Himmel, J. P. Hirth, H. H. Johnson, Jr., R. R. Nosh, T. N. Rhodin, R. H. Richman, H. C. Rogers, W. Rostoker, C. Sherby, C. W. Spencer, L. Slifkin, J. K. Stanley, R. Steinitz, H. C. Stumpf, and R. Swolin. Published bimonthly by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc., 345 East 47th Street, New York 17. N. Y. Telephone PLaza 2-6800. Subscription $30 per year for non-AIME members in United States and North, South, and Central America; $32, foreign; $7.50 for AlME members. Single copies, $6.00, single copies foreign, $6.50. The AlME is not responsible for any statement made or opinion expressed in its publications ... Copyright 1962 by the American lnstitute of Mining, Metollurgical. and Petroleum Engineers. Inc. . . . Registered cable address, AlME New York . . . Indexed in Engineering Index, lndustriol Arts Index, and Chemical Abstracts . . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 224, Number 6.

Jan 1, 1962

By J. H. Swislzer

TWO-LIQUID miscibility gaps have been found to exist in both the CaO-SiO, system above 1705 and the Cr,03 system above 2200"c. Glasser and 0sborn3 studied the extension of these miscibility gaps into the Ca0-Si0,-Crz03 ternary system and reported that the two-liquid region is not present at temperatures below the monotectic temperature of 1705°C in the CaO-SiO, system. The present authors, in connection with other work on surface-tension measurements and foam stabilities in the same ternary system,4 observed that the miscibility gap exists at temperatures as low as 1600°C. A brief experimental study was devoted to deter- mining tie-line positions in the two-phase region. The technique used was to obtain a separation of phases at 1600°C, then to quench-in the high-temperature phases and obtain a chemical analysis of each phase. It was necessary to take special precautions in obtaining a phase separation because of a tendency toward emulsification of the two liquids. The procedure followed is described in the schematic drawing in Fig. 1. A small platinum crucible containing several pinholes on its sides was placed inside a larger platinum crucible. An excess of Crz03 was placed in the outer crucible, together with a prefused binary CaO-Si02 mixture, and the Cr203 was allowed to diffuse through the pinholes and saturate the same binary CaO-SiOl mixture in the smaller crucible. After equilibration at 1600°C, the inner crucible contained only the lighter liquid (liquid A) saturated with Cr203. The outer crucible contained layers of both liquids. Experimental data were obtained by analyzing the entire contents of the inner crucible and only the bottom layer of the larger crucible (liquid B). The upper layer of the outer crucible was not suitable for chemical-analysis purposes because dispersions of the second phase sometimes were found in the samples. The technique is described in more detail in Ref. 4. The same method was used by Grieveson and urkdoan&apos; to study a miscibility gap in sulfate-ferrite melts, where the liquids were difficult to separate because of similarities in density. In addition to the phase-separation experiments, a few others were conducted to obtain information

Jan 1, 1964

By J. E. Ostberg, G. Phragmen, A. Hultgren, S. Wohlfahrt

Detailed study was made of a number of rimming ingots, both low and high carbon, and especially upon effects of superimposed air pressure. Requirement to suppress core bubbles is between 10 and 15 atm; at 6.5 atm freezing was in semikilled manner and at 3 atm, steel was of rising type. Probable mechanism of freezing under various conditions is discussed. AN earlier paper&apos; reported an investigation made by a committee for studying rimming steel ingots appointed by Jernkontorets in Stockholm. The present paper is the outcome of some further work done by the same committee. Since the characteristics of ordinary rimming steel are connected closely .with the amount of gas liberated during freezing and since this amount of gas is governed by the pressure, it was considered of interest to ascertain in what manner and to what extent definite pressures applied to the top of the liquid steel in the mold would affect the solidification process and the consequent structure of a rimming steel of ordinary composition. The experiments were made at the Domnarfvets Steel Works. The steel was made according to normal practice in a 4-ton Rennerfelt electric furnace. Ferromanganese was added in the furnace; no aluminum was added, with one exception. Analyses of the four heats are given in Table I. The top-poured ingots measured about 12 in. sq x 48 in. and weighed about 1300 lb. One or two ingots of each heat were allowed to solidify under pressure, using a special device for admitting compressed air to the upper closed part of the mold, as shown in Fig. 1. A heavy plate sealed with asbestos was bolted to the top of the mold. The plate had a tapered aperture for pouring. Immediately after pouring the hole was closed by a wedged plug, and compressed air was admitted through a hole in the plug. Because of some delay in applying the plug, full pressure was not reached immediately. The pressure was adjusted to the desired value as indicated by a manometer. In order that the interior of the ingot might have the benefit of the pressure, the freezing of the top crust was delayed by a refractory lining applied to the top part of the mold, Fig. 1. Ingots were also cast from each heat without applied pressure, and with and without refractory lining at the top. Axial sections of ingots were cut either of the whole ingot or of some part of it of special interest; sections were polished and usually etched.&apos; To facilitate description of structures the following terms may be used for different types of ingots solidified under gas evolution: 1. Box-hat or boot-leg ingot: Abundant gas evolution during casting and during rimming; no rim holes. 2. Normal rimming ingot: Lively gas evolution during rimming; usually rim holes in lowest part of

Jan 1, 1952

By Donald J. Knight

HEAT Treatment at 1500&apos; F of a mild steel containing 0.1 pct C, in an atmosphere which is oxidizing to both carbon and iron, results in the progressive oxidation of the metal surface with little or no change in the carbon content of the underlying metal. Further heat treatment of the scaled metal in either a neutral atmosphere or in a vacuum may or may not result in the decarburization of the metal depending upon the physical nature of the scale. It is apparent that if a continuous layer of oxide is present on the steel surface, the reaction OScale + Cmetal Cogas cannot progress since the SO formed gas would be unable to leave the oxide/metal interface. Thus, in order for the reaction to progress, the oxide must be cracked or porous. Vacuum heat treatment at 1500" F of samples with a thick continuous oxide scale showed no decarburization of the steel. However, when cracks were introduced mechanically into the scale prior to the vacuum heat treatment notable decarburization of the metal resulted and a structure as shown by Fig. 1 obtained, i.e., reduction of the crack walls to ferrite. With reference to the diagram of Fig. 2, it would appear that a mechanism of the following type takes place. Carbon atoms arriving at an oxide/metal/void interface, such as &apos;A&apos;, Fig. 2(a), can combine with oxygen atoms from the scale and leave the reaction site as Cogas thereby reducing the oxide to metal. On a greatly magnified scale, Fig. 2(b),this will appear as a ferrite projection along the crack wall. Carbon atoms entering this projection can react with oxygen atoms at point &apos;C&apos;, which is a new interface, and so on leading to a progressive growth of the ferrite along the crack wall and to the surface, Figs. 2 (c) and 1. It would appear that the only means by which thickening of the ferrite film can take place is by a diffusion of oxygen through the ferrite film to react with carbon at the newly formed ferrite/ void interface. Since the diffusion rate of carbon is reportedly much greater than that of oxygen, and since there is a low probability factor of oxygen and carbon atoms arriving simultaneously at the same site on the ferritehoid interface, there will be a tendency for more rapid lengthening than thickening of the ferrite layer, as is observed.

Jan 1, 1962

By H. Kosmider, P. Coheur

New processes of blowing with an oxygen-enriched air or gas mixtures of oxygen and steam allow the steelmaker to produce, in a basic converter, a rimmed steel low in nitrogen (0.0020 pct), phosphorous (0.020 pct), and sulphur (0.020 pct). The physical properties (ductility) of the new steels are excellent. Furthermore, from the point of view of economy, these new methods of blowing offer outstanding possibilities. THE natural occurrence of geological deposits of iron ore and local economic circumstances led European blast furnace men to work large quantities of lean iron ore with a phosphorus content as high as 0.5 pct. The iron obtained from these ores generally contains 1.5 to 2.1 pct phosphorus, 3.6 to 3.9 pct carbon, 0.3 to 0.6 pct silicon, 0.04 to 0.08 pct sulphur, and 0.3 to 1.2 pct manganese. To produce steel from this pig iron, the steelmaker has at his disposal several processes. One of the simplest and most economical is the pneumatic process developed by S. G. Thomas in 1879. This process of steelmaking, called the Thomas process, consists of blowing through the bottom of a basic bessemer converter and is used widely in Western Europe, as shown in Table I. Due to the development of tonnage oxygen plants, this process has become more important because the use of oxygen offers new possibilities of steel manufacture. Not only may the quality of the steel be improved, but liquid pig iron also may be used, the composition of which does not meet the heat requirements of the blow with atmospheric air. It is not intended to present here a detailed scientific discussion of the basic bessemer process but rather to discuss briefly its industrial possibilities in the case of rimmed steel and when blowing with atmospheric air, oxygen-enriched air, or gas mixtures of oxygen and steam. This paper is based on the current practice at Klockner-Hüttenwerk Haspe&apos;s steel division, and at six Belgian and Luxemburg steel works. The latter are members of the Liege section of the C.N.R.M. (National Institute for Metallurgical Research) and are: ARBED, John Cocker-ill, Esperance-Longdoz, HADIR, Miniere et Metal-lurgique de Rodange, and Ougree-Marihaye, most of which are working with tonnage oxygen plants.&apos; In order to avoid any misunderstanding, it should be noted that most of the techniques to be men- tioned, or similar ones, are used currently at many steel plants in Western Europe. Background The basic converters used in Europe have a capacity of 17 to 65 tons of steel, and are similar in shape to the one in Fig. 1. The lining is brick or rammed dolomite and has a life of 250 to 500 blows. The bottom is rammed dolomite and has a life of 40 to 80 blows. As far as we know, the type of blast used does not appear to have any influence on the life of the lining. Bottom life, on the contrary, depends very much upon the composition of the blast. It is only when

Jan 1, 1955

By H. M. Otte

Certain choices for the shear elements of the inhomogeneous distortion in the phenomenological theory of martensite formation are examined for their agreement with crystallographic and X-ray data of iron alloys. The assumption that the shear elements must represent slip or twinning systems characteristic of bcc metals is found to covey all observations, even when a small uniform dilatation is taken into consideration. In bct martensite, (011) becomes a possible twinning or faulting plane, in addition to {112), and qualitatively similar X-ray line broadening is to be expected from both. The basic concept inherent in the current theoriesl-4 of the formation of martensite is that the interface between the parent (austenitic) and product (martensitic) phase is an invariant strain plane (i.e., one that is undistorted and unrotated). Experimental evidence that the interface is of such a nature is available in certain transformations2&apos;5&apos;6 but for the transformation in iron alloys direct observation has not proved enlightening. Internal strains resulting from the formation of the small martensite platelets within the parent austenite matrix7 make it difficult to produce the desired evidence. Indirect evidence, however, such as the continuity of scratches in passing from untrans-formed to a transformed region, strongly indicates that the habit plane in iron alloys is an invariant strain interface. The scatter in habit planes in a given specimen8 would suggest that internal stresses have a slight but definite influence. On the other hand, composition changes which affect the lattice parameter can alter the habit plane appreciably, and by an amount greater than the scatter.&apos; The success of the theories depends on the choice made for the "inhomogeneous distortion" or "complementary shear&apos;&apos; in the analysis and also on the choice for the parameter 6 representing a small uniform dilatation. In the approach developed by Wechsler, Lieberman, and Read&apos;," it is implicitly assumed that 6 is unity. In the case of iron alloys, all observations cannot be explained without varying either the inhomogeneous distortion or 6 . Bowles and Mackenzie3 considered only the effect of varying d. They found it difficult to reconcile the wide scatter of habit planes with the theory and were forced to the conclusion that it may also be necessary to consider variations or different choices of the inhomogeneous distortion. Wechsler and Read" considered a limited number of possible choices for the inhomogeneous distortion, but no variation in 6, though this could easily have been introduced if so desired. It is the purpose of the

Jan 1, 1961

By J. T. Norton, J. G. McMullin

The ternary system of gold-silver-copper is characterized by a solid solubility gap and a two phase region in which copper-poor and silver-poor phases coexist. At about 30 pct gold, the two phases become mutually soluble at temperatures below the melting temperature. As the gold content is increased, the solubility temperature of the alloys decreases until at about 80 pct gold, the two phases are soluble down to the lowest temperature at which the alloys will recrystallize. Although the general form of the two phase region is known, its boundaries do not seem to have been investigated extensively. In an X ray diffraction study, Masing and Kloiberl have outlined the boundaries of this two phase field at 400 and 750°C. Using only microscopic techniques, Pickus and Pickus2 determined a vertical section of the ternary diagram showing the 14 kt alloys (58.3 pct gold). These two reports are riot in complete agreement. It has been shown3 that some of the ternary alloys are susceptible to age hardening and that the hardening is caused by the separation of a homogeneous alloy into two phases at the aging temperature. While the gold-copper binary system is an outstanding example of super lattice formation, Hultgren4 has shown that a few per cent of silver added to gold-copper destroys the tendency for ordering. Because of the age hardening possibilities of these alloys, it seemed advisable to investigate the boundaries of the two phase field more in detail using an X ray diffraction method, so as to permit a better understanding of the aging phenomena and enable predictions as to the behavior of other alloys to be made. This is especially true for the 18 kt alloys (75.0 pct Au) at the lower temperatures since they are known to exhibit age hardening. Twelve ternary alloys were prepared having the compositions shown in Table 1 and graphically in Fig 1. The gold used was fine gold bars supplied by Handy and Harmon. The silver was a bar of high purity silver from the U. S. Bureau of Standards. The copper was a bar of vacuum-treated, high conductivity copper from the National Research Corporation. The pure metals in the form of powder were weighed out in proper proportions and melted in graphite in a high frequency induction vacuum furnace. They were heated to 1100°C and slowly cooled. The ingots were then removed from the crucible, inverted, returned to the crucible and remelted. This remelting procedure was intended to reduce segregation in the ingots. After remelting, the ingots were checked for weight loss. The weight loss in each ten gram ingot was held to less than 25 mg. The remelted ingots were cold rolled and then given a homogenizing heat treatment of 16 hr at 760°C to remove any remaining segregation. Powder specimens were prepared by cutting the ingots with a fine file, one half the required amount of powder being taken from each end of the ingots. When the X ray diffraction pattern showed any difference in lattice constant between the ends of the ingot, the ingot was remelted and given an additional homogenization treatment. All powder samples were sealed in evacuated pyrex tubes for heat treatment. Ordinary pyrex proved satisfactory for temperatures up to 650°C but above that temperature it was necessary to use a special high temperature pyrex glass. Annealing at temperatures below 500°C was done in a salt bath whereas for temperatures of 500°C and above an electric muffle furnace was used. In both furnaces the temperature control was ± 5°C. In all annealing treatments samples of cold worked powder were placed in a furnace which was already at temperature. In this manner the specimens recrystallized directly to the equilibrium structure for that temperature. Time at temperature was selected so as to allow complete recrystallization, but very little grain growth. Specimens were quenched from the annealing temperatures by breaking the pyrex tubes in cold water. X ray diffraction photograms were made of all the heat treated powders using copper radiation and a Phragmen

Jan 1, 1950

By J. T. Norton, J. G. McMullin

E. R. JETTE*—The way this ternary was developed there are two directly determined points on each of the iso-thermals except the 700° isothermal, where I believe there is only one. How were the end points determined, and what was the basis for it? Whose work formed the basis for the silver copper line ? M. B. BEVER †—At most temperatures the authors determined three points of the isothermal line. For example it can be seen from Fig 3 and 4 how three points for the 600°C contour line were obtained. The authors took two additional points for each temperature from the copper-silver binary diagram contained in Hansen&apos;s volume on constitution diagrams. It is correct that the 700°C contour line is based only on one point in the ternary field which was found by a slight extrapolation of Fig 4. R. I. JAFFEE*—Are the tie lines representing phases in equilibrium parallel to the silver-copper boundary ? M. B. BEVER—Are you asking that as a matter of principle ? R. I. JAFFEE—I assumed that would follow from principle. I wonder if that is in accordance with the authors&apos; ideas too. M. B. BEVER—I do not believe the authors obtained any information on the tie lines in the two-phase field. Of course, in the limiting case of very low gold contents the tie-lines approach to the silver-copper boundary, but generally in the two-phase field I do not think that the tie-lines have to be parallel to the boundary. E. R. JETTE—I am quite sure they do not have to be parallel. You cannot tell from this work in which direction they go. E. A. GULBRANSEN*—Were any pycnometric measurements made to check the lattice parameters of the alloys ? M. B. BEVER—I did not hear any-

Jan 1, 1950

By d&apos, John C. Entremont

Pure iron was inductively melted in small refractory crucibles and optical pyrometer and immersion thermocouple readings were simultmzeously taken. The resulting emissivities of the liquid iron surface obtained were found to be greatly affected by both the gaseous atmosphere and geometrical changes in the physical setup. Quantitative values for these effects are indicated. FOR many applications in both the laboratory and plant, optical pyrometry is still the best means of measuring temperatures in the incandescent range. A prerequisite in evaluating the correct temperature is a good value of the emissivity of the surface. To obtain the emissivity from the tabulated values of the literature can be very confusing and often far from correct. There are many reasons for these difficulties, and it is not within the scope of this paper either to enumerate or to discuss them all. Its purpose is to show quantitatively how several factors affect the apparent emissivities obtained from experimental measurements on liquid iron surfaces. The black body is the reference state for the quantitative values of emissivities and is defined1 as a body which absorbs all radiation incident on it, reflecting none; such a surface emits more radiation per unit area per unit time than any surface which reflects any radiation, and is given a value of unit emissivity. All bodies having reflective power thus have emissivities less than unity and are considered nonblack or grey bodies. The ratio of the radiant energy emitted by the flat, nonblack surface to that of a perfectly black surface of equal area and temperature is the emissivity of the surface. The above definitions are applied to flat, polished, opaque surfaces, very seldom encountered in actual measurements, and for this reason many authors have suggested that the word "emittance" be used for real bodies rather than emissivity. The emittance has reference to the material and its configuration rather than to its properties in the idealized state. Recent observations of molten iron in a small refractory crucible indicate that not only the configuration of its surface but the geometrical arrangement of its surrounding and the nature of the surrounding atmosphere have a pronounced effect on the emittance. Neglect of changes in such conditions may lead to errors as large as 40°C at 1600°C. Thus it is suggested that the term "apparent emissivity" be used and that it be recognized that its value pertains to a particular experimental arrangement only. As a result of not recognizing these differences in emissivities, which are obtainable from changes in the physical setup of an observation, many investigators have incorrectly quoted their values as those of the emissivities of particular materials rather than as an apparent emissivity for their particular arrangements. As a consequence, values of the emissivity of liquid iron ranging from 0.3 up to 0.55 are found in the literature. In an effort to establish an accurate optical temperature scale for liquid iron solutions in which de-oxidation studies were to be carried out, it was observed that the temperature relationship, obtained by simultaneously taking immersion thermocouple

Jan 1, 1963

By N. A. Gokcen, M. N. Dastur

In metallurgical process industries a knowledge of true melting and casting temperatures is very essential for increasing the operating efficiency as well as improving the quality of the finished product. Optical pyrometers are widely used for the purpose because of their cheapness and ease of operation. It is an unfortunate fact, however, that this mode of measuring temperature entails a source of severe error inasmuch as with all non-black bodies, the temperature observed is always below the true temperature owing to deficient emissive power. Hence, the need for emissivity correction arises. In 1913 Bidwell1 obtained emissivity values of 0.36-0.48 for a temperature range of 1520-1800°C. He measured the true temperature of molten iron by sighting into a carbon cavity immersed in the iron under an atmosphere of hydrogen. In 1914 Burgess2 determined the emissivity of a smooth surface of liquid iron free from oxide to be 0.37 under an atmosphere of hydrogen. He claimed to have attained an accuracy of within 5°C at 1500°C with an optical pyrometer using monochromatic light. He reported that no difference appeared to exist between the emissivities of pure iron and of steels containing considerable percentages of carbon, nickel or manganese; nor was there any appreciable variation of emissivity with temperature from 1530 to 1571°C. Wensel and Roeser3 found an elnissivity value of 0.4 for temperatures above 1375°C for cast iron. The average emissivity value for carbon steels reported by Leiber,4 odd,5 Hase6 and Umino7 range from 0.4 to 0.45. Knowles and Sarjant8 made an extensive study of emissivity of molten iron and steel over a wide range of workshop and laboratory conditions. Observations of true temperature were made with immersion thermocouples, and correlated with apparent temperatures indicated by optical pyrorneter readings taken on the pouring stream as it passed over the lip of the crucible. The emissivity of Armco iron was shown to be of the order of 0.4, rising slightly with increasing temperature. But for plain carbon steels containing up to 1.0 pct carbon the emissivity was shown to fall slightly with increasing temperatures. The results of their investigation are in agreement with those of Guthmann.9 Naeser,10 Spencer," Todd5 and Hase6 in regard to the relation between emissivity and temperature for plain carbon steels. However, Goller12 has found a rise of emissivity with increasing temperature for the same steels. Results of several investigations are given in Fig 1. Measurement of True and Apparent Temperatures The necessity for an accurate optical temperature scale for liquid iron in studies of gas-metal equilibria led to this investigation. Experimental measurements were carried out in the induction furnace used by Dastur and Chipman13 in their studies of the reaction of hydrogen with oxygen in liquid iron. The furnace as modified for this work is shown in Fig 2. The atmosphere of the furnace was a mixture of purified argon with hydrogen containing a small controlled amount of water vapor. Gases were preheated by means of a platinum-10 pct rhodium resistance coil. The stream of hydrogen sweeping across the surface of niolten iron vir-

Jan 1, 1950

By H. M. Kraner, R. C. Devries, K. H. Gee, E. F. Osborn

On the basis of liquidus measurements in the system COO-Mg0-Al2O3-Sio, and previously published data, diagrams have been constructed at 5 pct Al2O3, intervals from 5 to 35 pct Al2O3,. Liquidus temperatures and primary phase fields are shown. The optimum composition of a blast furnace slag for a given alumina content is indicated. At the optimum point, ordinary slags will be entirely liquid and will have maximum desulphurization potential and minimum viscosity. The relation of optimum composition of slags to the "plateau region" of the liquidus surface, and the application of these data on synthetic quaternary slags to actual slag compositions are discussed. Index of refraction of glasses is given as well as composition, temperature, and phase data for each mixture. THE usual blast furnace slag, as a first approximation, can be considered a mixture of the four oxides, CaO, MgO, Also,, and SiO,. Systematic, extensive data for the quaternary system, CaO-MgO-A1,0,-SiO, is therefore required for the understanding of the properties of such a slag as a function of composition and temperature. With sufficient data, it should be possible to fix unequivocably the relative amounts of lime, magnesia, and silica required for a given alumina content to result in a slag composition having optimum properties. Other constituents, such as FeO, MnO, Ti02, and S, have an effect on the properties of a slag, but as long as they are present in small and approximately constant amounts they produce only a second-order effect superimposed upon the major changes in properties of slags determined by the relative amounts of the four major components. Viscosity and desulphurization data have been reported for mixtures approaching blast furnace slags in composition, but systematic liquidus data have not been obtained. Inasmuch as a slag must be all liquid in order to be most effective as well as practicable, clearly the temperature above which a mixture is all liquid (liquidus temperature) is a type of data needed. Such data have been obtained through the study of 446 compositions and are pre- sented in this paper along with a discussion of their bearing on the optimum composition of blast furnace slags. For an orderly presentation of the data, the quaternary system is viewed as a tetrahedron with one component at each apex. Fig. 1 shows a tetrahedron representing the system Ca0-Mg0-A1,0,-Si0,. The base is the ternary system Ca0-Mg0-SiO,, A1,0, is the top apex, and the front face, the system CaO-

Jan 1, 1955

By F. W. Luerssen, J. F. Elliott

F LUSHING the early slag from a stationary open Fhearth having a high percentage of hot metal in its charge is necessary in order to remove silica from the system. The flush slag is strongly oxidizing and is somewhat acidic. It has, however, considerable capacity to extract phosphorus from the bath and it also removes considerable manganese. It seems probable that factors which control the distribution of phosphorus and manganese between slag and metal in the refining period also should be dominant in the flush and postflush periods. Several studies, as summarized elsewhere,1,2 support the viewpoint that conditions closely approaching equilibrium for these elements are rather readily established during the refining period. Over the years these studies have repeatedly demonstrated that 1—high slag v01ume, 2—low bath and slag temperature, 3—basic slag, and 4—strongly oxidizing slag favor rapid elimination of phosphorus from the bath to the slag. They also show that the following conditions favor retention of manganese in the bath: 1—low slag volume, 2—high bath and slag temperature, 3— basic slag, and 4—minimum oxidizing power of slag. When it is considered that the flush slag often carries as high as 75 pct of the manganese charged and only 25 to 60 pct of the phosphorus charged, it is evident that in removing silica much manganese is sacrificed but phosphorus removal is far from conplete. Because of overriding circumstances, this is accepted in most operations and actually it is considered to be inevitable. This may account for the fact that little attention has been paid to conditions affecting the elimination of phosphorus and manganese in the flush slag. A recent study of the behavior of various charge oxides has developed considerable information on the flush and postflush periods. Because the data are felt to be of general interest, they have been brought together and Presented in this paper. The object is to show the various factors in the flush and postflush periods which influence elimination of phosphorus and manganese. Physical Conditions During and After Flushing Physical conditions existing during the flush vary from plant to plant, from shop to shop, from furnace to furnace, and even from heat to heat. They are strongly influenced by the physical and chemical character of the charge oxide which is ordinarily necessary to provide sufficient oxidizing power early in the heat. Invariably the period is characterized by a vigorous reaction between the principal re-actants: the hot metal being added and the charge oxide. During the flush, it is probable that the slag acts to some extent as an oxidizer; but, because of the critical influence of the behavior of the charge oxid&apos;e on flushing action, it seems apparent that the oxide itself is the dominant oxidizer. Fig. 1 shows the course of two heats which were selected as being typical of the group studied. Heat A was charged with 55 pet hot metal, based on the total metallics charged, and heat B had 57 pct hot metal. As indicated in Table I and Fig. 1, the melt-down slag, which is not usually voluminous and which is principally FeO, expands greatly in volume and will show rather high levels of SiO2, MnO, and P2O5 very soon after the beginning of the hot metal addition. Simultaneously, large volumes of CO are liberated which cause violent mixing of slag and metal. It is of interest to note that the time required to bring carbon down to a low level is very much longer than that required for the removal of silicon, manganese, or phosphorus. At the end of flush, carbon in the bath is still approximately 2 pct. When strongly reducing hot metal is brought into contact with strongly oxidizing conditions within the furnace! it is probable that the rate of mass transfer to the slag (and atmosphere) of silicon, manganese, phosphorus, and carbon initially depends principally on the rates at which the two participating phases are brought into contact That is, it depends on the nature of the various reactions. Later in the flush period, when the scrap is virtually all dissolved and the action of the bath has settled down to a steady and somewhat gentle boil, it is likely that other factors, such as the transfer of oxygen across the slag-metal interface, become dominant. The temperature of the slag-metal system is far from uniform. Heat is being driven by the flame down through the slag. Bubbling and surging of the metal also frequently brings portions of the bath in contact with the flame. At areas of contact between the ore and liquid metal, or slag and liquid metal, the oxidizing reactions generate much heat. On the other hand, scrap is being melted which tends to absorb large quantities of heat. Because the liquid bath is high in carbon, the steel scrap is brought into solution rapidly. This can proceed at a rather low temperature; and until much of the scrap has been taken into solution, the bath temperature would not be expected to increase appreciably. Consideration of these factors leads to the conclusion that during the flush period the slag should be rather hot and the bath relatively cold. Both observation and temperature measurements bear this out. Experimental Data The extended program of charge oxide evaluation permitted study of the widely varying conditions existing during the flushing period. Slag and metal analyses and bath temperatures reported herein (Tables I and 11) were obtained toward the latter portion of the work. Four different types of charge oxide, sinter, two types of hydraulic cement-bonded soft ores, and a pyrobonded agglomerate were used in the study. Although the heats reported were from only one 205 ton furnace, they show variations in flush slag analyses all the way from 25 pct FeO, which is typical with the use of a hard natural charge ore, to 45 pct FeO which resulted when a very poorly agglomerated fine ore was used. The physical behavior of the flushes showed a correspondingly wide variation from well controlled reactions to violent surges following periods of inac-

Jan 1, 1956

By H. Larson, J. Chipman

The ferrous and ferric oxide concentrations of slags, expressed as j = Fe+++/(Fe+++ + Fe++), have been established through gas-slag equilibrium at 1550°C in a range of oxygen pressure of 10-I to 10-9 equilibriumatm. The value of j is increased by basic additions (BaO, CaO, MgO, MnO) and decreased by acidic oxides (SiO2 and TiO2). Oxygen pressure is shown graphically as a function of composition for slags which are analogous to those at the slag-gas interface of the open hearth furnace. THE progress which has been made in recent years in understanding the chemistry of metallurgical slags has been based largely on studies of slag-metal and slag-gas equilibria. There is a considerable body of knowledge which is applicable to reactions occurring at the slag-metal interface in open hearth steelmaking. There is little information concerning reactions of the slag with the furnace atmosphere and hence little basis for an understanding of the transfer of oxygen, sulphur, or hydrogen between gas and slag. The oxygen pressure of the open hearth atmosphere is normally of the order of 10-1 to 10-3 atm which differs by several orders of magnitude from that of about 10" atm at the slag-metal interface. The chemical properties of the slag, for example, the ratio of ferric to ferrous iron and the ability of the slag to hold sulphur in solution, are greatly affected by changes in oxygen pressure. This investigation was undertaken to enlarge our knowledge of the effect of oxygen Pressure on steel-making slags. Using air or controlled mixtures of CO a CO2 a range of oxygen Pressures from 10.&apos; to 10.&apos; was covered. Review of the Literature There are only a few references in the literature which pertain directly to this investigation. The most important is that of Darken and Gurry1,2 on the system iron-oxygen. This work included the determination of the phase diagram of the system and also a study of the field of homogeneous melts and their oxygen pressures. Their apparatus and procedure were very similar to that used in this study. Iron oxide was melted in a platinum crucible under an atmosphere of CO2:CO, CO2:H2, H2O, CO2, air or O2 depending upon the partial pressure of oxygen desired. After equilibrium was reached, the sample was quenched and analyzed for ferrous and ferric oxide. By appropriate calculations these authors were able to determine the oxygen and iron activities in the various slags, heats of formation of the oxides of iron, and heats of solution of iron and oxygen in the liquid slags. In a subsequent paper&apos; the same authors made a less thorough investigation of the effects of additions of lime and manganese oxide on the composition of iron oxide melts. Only a few experiments were made and those in a narrower range of temperature and oxygen pressure. Darken&apos; has investigated the fusion temperature of iron oxide in contact with silica under various atmospheres. He found that the temperature changes from 1120° to 1447°C as the gas composition changes from CO2/CO equal to 20.8 to pure oxygen. A comprehensive paper by White" predates the work of Darken and Gurry. The decomposition of ferric oxide into oxygen and lower oxides of iron was studied from 1000° to 1650°C and under oxygen pressures from 2 to 76 cm of mercury. The effect of

Jan 1, 1954

By W. M. Wojcik, R. F. Kowal

Oxygen and sulfur distributions in commercial, 5-ton ingots of killed, medium carbon steel are described. Oxygen distribution is found to vary with deoxidation practice. Irregular distribution of oxygen within ingots makes necessary special precautions in sampling of rolled products for analysis of oxygen. Oxygen distribution is discussed in terms of recently published solidification concepts which had been successfully applied to simpler cases of segregation. These concepts have been found inadequate to explain observed oxygen distributions. Convective movements of the liquid metal, as determined by tracer elements, are shown to be capable of accounting for the observed distributions of oxygen. IN an effort to explore the origin of surface and subsurface imperfections in pierced steel products, a study of oxygen and sulfur segregation was made on ingots cast in open-top and hot-top molds. The results of our previous investigations1"3 have indicated the importance of the location and amount of oxide inclusions in an ingot. Inclusions close to the surface of the ingot have been found to contribute greatly to the formation of imperfections in the surface of finished products. This study of the effects of deoxidation and casting practice on segregation and the resulting oxygen distribution in ingots was initiated to determine the parameters controlling the location of inclusions in an ingot. Segregation of solute elements during solidification of low-melting binary alloys has been studied in the past.1, 5 Formation and growth of inclusions in iron melts have been studied under specific conditions."- In spite of these and other recent studies,10-12 segregation during solidification of commercial, killed steel ingots is not well understood. Consideration of solidification rates, of segregation during solidification of the chill, dendritic, and central zones, and of material balances for the segregated elements has indicated that a simplified theoretical solidification model is not adequate. However, the observed high oxygen contents in localized volumes of the dendritic zone can be rationalized if additional effects of convection currents in the ingots, precipitation, and rapid growth of new phases are considered. EXPERIMENTAL PROCEDURE Steelmaking and Processing. A group of nine killed. medium carbon steel heats having compositions listed in Table I have been studied. The deoxidation and mold practices used were varied to give a wide range of steel oxygen contents. The amounts of aluminum added to the ladle and the ingot casting practices (hot top and open top) were the main variables. The steel was made by a duplex practice in 160-ton tilting basic open-hearth furnaces. All nine heats were top-cast into 24 by 24 in. big end down, fluted molds, to a height between 60 and 76 in., using both open tops and exothermic hot tops. The deoxidation practice and the tapping and teeming details for each heat and ingot studied are given in Tables II and III, respectively. Hot-top practice is indicated by the letter H following the heat designation. Furnace and ladle temperatures were measured by standard disposable-tip, Pt/10 pet PtRh thermocouples. Teeming-stream temperatures were obtained as described by Samways et al.,13 by immersing a Pt/10 pet PtRh thermocouple, covered by a silica sheath, into the teeming stream under the nozzle. The output of this thermocouple was recorded with Leeds & Northrup Speedomax potentiometer. Calibration of the latter thermocouples was based on the freezing point of a pure iron/oxygen alloy (2795°F). The accumulated errors of measurements were within ±10°F. The thermocouple measurements were supplemented in this investigation by continuous recording of a ratioing, two-color pyrometer (Shawmeter), protected from smoke by a blast of clean air within the sighting tube, and calibrated to read with better than ±10°F accuracy. Following teeming of three heats, P, R, and T, tracer elements were added to the steel in the molds to obtain a record of the progress of solidification. As soon as the teeming stream was shut off, a 0.010-in.-thick steel can containing a mixture of crushed standard ferro-titanium and ferro-vanadium (0.05 pet of each alloy element) was plunged into the middle of the steel pool to a depth of 6 in. In about 30 sec no indication of the can or its contents remained. The surface of the open-top ingots solidified in 20 to 30 sec. A study of liquid metal movement and the precipitation of oxides was facilitated materially by use of the tracer technique as titanium has a low distribution coefficient between solid and liquid steel while vanadium has a high distribution coefficient.

Jan 1, 1965

By Henry A. Wriedt, John Chipman

Equilibrium in the reaction of hydrogen gas with oxygen in liquid nickel, iron, and their alloys has been studied at temperatures of 1500° to 1700°C. The equilibrium con^stant, 0/p, [% O], is greater in nickel then in iron by a factor of 45 at 1594 C. In the alloy steel range, the activity coefficient of oxygen is slightly increased by the presence of nickel. NICKEL is more resistant to oxidation than is iron, in both the solid and the liquid state. The solubility of oxygen,&apos; however, is greater in nickel than in iron. The two metals and their liquid alloys constitute an interesting series of solvents in which the chemical behavior of oxygen can be studied by methods similar to those used for liquid iron.&apos; Experimental Method The furnace assembly, including the tube for preheating the entrant gas, was the same as that described by Gokcen and Chipman. " controlled mixture of water vapor, hydrogen, and argon preheated to approximately the melt temperature impinged upon the surface of the liquid metal. The charge, weighing about 35 g, was held in an alumina crucible at constant temperature in the gas stream for a prolonged period, then quenched in a stream of cold helium, sampled, and analyzed for oxygen by the vacuum fusion method. The temperature of the liquid metal was measured by a Leeds and Northrup optical pyrometer which had been checked against a similar instrument certified by the National Bureau of Standards. The freezing point of electrolytic iron in hydrogen, taken as 153j°C, was used for frequent checks. This point and the emissivity determined by Dastur and Gokcen" established the transmissivity of the optical system. The emissivities of Fe-Ni alloys at 1535" are known from the experiments of Smith and Chipman,h nd it was assumed that the variation with temperature is parallel with that of iron. Recorded temperatures are probably accurate within k5"C. Preparation of Gas Mixtures—Since the ratio H,O:H, had to be much higher for nickel than for iron, it was found convenient to construct two separate systems for gas preparation. In both cases, the ratio of argon to the sum of the other two gases was at least 4, the proportion of hydrogen and water vapor being varied to produce H,O:H, ratios from 0.2 to 70. The primary purpose of the argon was to diminish the errors caused by thermal separation&apos; in the gas phase. In addition, its presence lowered the saturation temperature required for a given H,O:H, ratio and minimized the difficulty of preventing condensation. Both systems were modifications of the one used by Dastur and Chipman.&apos; For H,O:HI ratios greater than 2, welding-grade argon purified by passage over magnesium chips at 620°C was mixed with hydrogen produced in the electrolytic cell shown in Fig. 1. The design was based on a cell used by Bodenstein and Pohl," the important features of which area nickel wire cathode and sodium hydroxide solution as the electrolyte. The rate of hydrogen evolution was controlled by a calibrated ammeter and a rheostat in the circuit, the current efficiency being taken as 100 pct. Precise control of the argon flow rate at about 300 ml per min was achieved by means of a capillary flowmeter having a controlled pressure drop. The molar flow rate was measured volumetrically before each run, and a constant flowmeter setting was maintained thereafter. The A-H, mixture passed through a water saturator of the type previously described," the saturation temperature being maintained automatically with a fluctuation of k0.04"C. The tube between saturator and furnace was heated by a resistance winding. The system was of all Pyrex construction with the exception of the stainless steel tube containing magnesium chips. This was connected with the glass tubing at the upstream end by

Jan 1, 1957

By B. M. Larsen, T. E. Brower, J. W. Bain

A mass of circumstantial evidence is presented to indicate that the main source of alloy losses in open-hearth tapping is oxidation by air, with the steel apparently reacting with an amount of oxygen equivalent to about 30 times its own volume of air. The effect is erratic from heat to heat, depending largely on turbulence and distance of free fall of the stream of liquid metal. THIS paper reports another phase in a general study of oxidation in the open-hearth, various aspects of which have already been discussed in previous papers.1,2,3 It is based on experiments conducted on commercial, basic open-hearth furnaces at various times when opportunity offered, beginning about 1938, in an attempt to determine the mechanism and measure the amount of air oxidation during the flow of the tapping stream through the air into a ladle. This effect is closely connected, not only with alloy losses and control of chemical analysis, but possibly with various questions regarding inclusion content and steel quality and with a true picture of the deoxidation of steel in general. Thus it is believed that discussion of a large part of the results to date may be of assistance to others who are studying problems related to deoxidation or to steel cleanliness and quality. The literature reveals that strangely little attention has been devoted specifically to the effect of pouring steel through open air. Bardenheuer and Henke4 in 1939, in a paper devoted largely to overall losses of manganese in the basic open-hearth, reported that for a number of heats tapped into a tilted ladle held just beneath the runner so that the maximum distance of drop of the stream through the air was held to less than about 30 in., there was in most cases almost no loss of manganese from furnace to ladle. Hultgren,5 in 1945, showed that in high-carbon basic electric steel deoxidized in the furnace and containing no large inclusions as it left the furnace, large silicate inclusions, often rich in manganese oxide, were present in samples dipped from the pool in the ladle; also that the rise in content of large inclusions (above 0.01 mm dim) was greater when the metal stream was made to spray or flow in a turbulent manner. Our interest in this phase of oxidation in the open-hearth was first aroused by a study of alloy efficiencies on ladle additions. The frequency curves of manganese efficiency (net recovery of metal added in ladle) given in fig. 1 are of interest in this connection. Lowest, and also most variable (47 to 95 pct), recovery was in low-carbon heats having no coal additions to the ladle, progressing upward to a maximum average and least variable (82 to 97 pct) recovery in high-carbon heats killed with aluminum and silicon. Both coal additions and higher carbon contents in the tap stream, as well as additions of silicon and aluminum, help to lower the amount of manganese loss. But the most interesting point is the amount of manganese oxidized in many heats tapped at 0.50 to 1.06 pct carbon. It has been shown in a previous paper3 that the amount of oxygen in the tap stream in such heats is very small, usually below 0.01 pct, too small to oxidize any appreciable amount of manganese. Also, the fact that manganese should be oxidized at all in a metal solution containing such more stable oxide-forming elements as aluminum and silicon is an indication of some rather intense oxidizing effect such as could be caused by reaction with the air during ladle filling. Oxygen Balances from Tap Stream to Teeming Stream: Data in the form of alloy efficiencies, such as those shown in fig. 1, are not a proper measure of such a general oxidation effect. Having available

Jan 1, 1951

By E. T. Turkdogan

This is a compilation and a critical review of the data on the Fe-Ca-0 ternary system. Using the results on the reductiorz-equilibria, an oxygen potential diagram is drawn for the greater part of the system. A number of univariant systems and invariant points, not determined experimentally, are evaluated by making use of the theorem on univariant curves intersecting at an invariant point. The formation of solid solutions and ternary compounds and the crystal structures of some of the phases in the composition-diagram are given for a feu! temperatures. DURING the past thirty years there has been a continued interest in the study of the Fe-Ca-0 system. A detailed literature survey made by white1 in 1943 indicated that further work was required to clarify the phase relationships; in fact, the work carried out in the subsequent years, reviewed by Burdese2 in 1954, made a valuable contribution to a better understanding of this subject. Most of the data were obtained by the step-wise reduction of mixtures of iron oxides and calcium ferrites. However, there is some uncertainty about the phase relationships in this system, arising mainly from insufficient use of thermodynamic concepts in the construction of phase diagrams. In this paper an attempt is made to establish the invariant points from the available data. OXYGEN POTENTIAL DIAGRAM Schenck and coworkers3,4 were the early investigators who studied part of this system by the step- wise reduction method and suggested the formation of two ternary compounds, CaO.FeO.Fe2O3 and 2Ca0.5Fe0.2Fez03, the latter being referred to as point X. They also deduced from their results that the phases Y (8.74Ca0.32.5Fe0.8.74Fe2O3 and Z (2.02CaO-97.98FeO) were formed near the w?stite corner of the system. Martin and voge15 postulated the existence of the compounds CaO.9FeO and 4Ca0.3Fe3O4; the former is very close to the composition of point Z and the latter to that of CaO.FeO-Fe2O3. The most valuable contribution to the presen knowledge on this system was made by Cirilli and Burdese6-8 who showed by X-ray and chemical anal yses that there were two ternary compounds, CaO-Fe0.Fe2O3 and CaO.3FeO-FezO3; the former is the same as that suggested by Schenck et al. and the latter is close to their point X. The results of Cirilli and Burdese show that the phases Y and Z postulated by Schenk et al. are solid solutions of calcium oxide in w?stite. In most of the above-mentioned reduction-equilibria measurements carbon monoxide-carbon dioxide mixtures were used and in a few cases hydrogen-water vapor mixtures were employed. Using the

Jan 1, 1962

By W. D. Forgeng, R. L. Folkman, D. C. Hilty

The solubility of oxygen in molten Fe-Cr alloys has been determined at 1550° , 1600°, and 1650°C for alloys containing up to alloyshasbeenabout 50 pct Cr and found to decrease as chromium increases to 6 pet and then to increase gradually. Phase relations in the Fe-Cr-0 system at steelmaking temperatures have been evaluated and two previously unreported oxides have been identified. OPERATIONS in the melting and refining of chromium steels are dependent to a major degree on the reactions of chromium and iron with oxygen and are primarily directed toward controlling and modifying these reactions to secure maximum advantage in the utilization of chromium. Although fairly effective practices have been developed empirically, understanding of the specific reactions is limited. Moreover, the ability of molten steel to dissolve oxygen that subsequently precipitates as oxide inclusions during solidification is well known, so that clarification of the effect of chromium on the nature and mechanism of formation of these inclusions is desirable. Study of the problem indicated that increased knowledge of the fundamental Fe-Cr-0 system is essential to further technical and economic improvement. Consequently, an investigation of the influence of chromium on the solubility of oxygen in molten iron and of phases and phase relations in the Fe-Cr-0 system was undertaken at the Metals Research Laboratories of the Electro Metallurgical Co. as part of a general program on the effective utilization of chromium in chromium steel production. Experimental Procedure All of the experimental runs made during this investigation were carried out in the rotating crucible induction furnace which has been described in detail in a previous publication.&apos; In review, the principle underlying this furnace is that rotational forces in the crucible cause the molten metal to assume a concave shape in such a manner that the slag is contained in the molten metal cup, thereby minimizing slag/crucible contact and subsequent reaction. Practically all of the heats were melted in commercial-quality magnesia crucibles of the type usually furnished for laboratory induction furnaces. All of the runs were made under an argon atmosphere after the furnace chamber had been degassed. Bath temperatures were controlled by Pt—Pt-10 pct Rh thermocouples. The basic furnace charge consisted of a premelted 12 to 15 lb electrolytic iron slug which had been cast to a shape convenient for fitting into the rotating furnace crucible. A typical analysis of the electrolytic iron slugs is given in Table I. For certain runs, it was desirable to melt down charges containing high initial chromium contents. In these cases the chromium was added to the electrolytic iron during the premelting operations. Chromium was added to the rotating furnace bath in the form of electrolytic chromium of the analysis given in Table 11. In all of the constant temperature runs, the standard procedure was to melt down the electrolytic iron or alloy slug under vacuum, admit argon to slightly greater than atmospheric pressure, and adjust rotational speed to develop a well formed "cup" on the bath surface. The melt was then saturated with oxygen by an addition of ferric oxide and the temperature of the bath adjusted to within +5°C of the desired level. At this point the heat was permitted to come to equilibrium prior to sampling or further addition. This time interval was varied from 15 min to 2 hr but generally was about 20 min. After sampling, the desired chromium addition was made and the bath again equilibrated prior to subsequent sampling. This cycle of addition and sampling continued for the duration of the run which lasted from 4 to 8 hr. At the end of this period, power was shut off and the bath allowed to solidify in the furnace. Quenched metal samples were taken from the equilibrated melts by means of the "Taylor sampler" which has been described by Taylor and Chipman.&apos; Before being submitted to chemical analysis, all samples were carefully examined for surface slag occlusions and cold shuts. Later in the study, each sample was radiographed and examined metal-lographically in cross-section to determine the presence of internal defects. On the basis of these examinations, sound and apparently clean specimens were selected from the Taylor samples for chemical analysis.

Jan 1, 1956

By S. R. Goodman, Hsun Hu, R. S. Cline

The quenching technique has been used to study phase relations in the composition area 2FeO.SiO2-FeO-SiO2-MnO.Si02-ZMnO.SiO2 of the system iron oxide-manganese oxide-silica under strongly reducing conditions such as exist in a gas mixture consisting of equul parts of carbon dioxide and hydrogen. Liquidus and solidus temperatures of most mixtures in the composition area studied are in the range of 1173° to 1345°C. EQUILIBRIUM relations existing among the oxides of iron, manganese, and silicon are of particular interest in two areas of steelmaking: slags and ingot inclusions. Mixtures of these oxides represent about 90 pct of the slag in the acid steelmaking process, and so dominate the chemistry of the whole refining process. These constituents also play an important role in the early slags existing at the time of the "lime boil" in the basic open hearth process. If these slags are liquid, they "wet" the lumps of lime rising from the bottom of the bath, and react with them. A liquid slag rich in CaO is then formed at the very beginning of the refining. Because the temperature is still low, all conditions for a good dephosphoriza-tion are fulfilled at this stage of the operation. Metal deoxidized with ferromanganese or silico-manganese is likely to contain, as inclusions, phases made up from among the oxides of iron, manganese, and silicon. A knowledge of stability relations existing among the phases present in this system, therefore, enables one to predict the hardness of the inclusions encountered. Moreover, because the shape of the inclusions in steel has a profound influence on the physical properties of the metal, it is important to establish whether or not the oxidic material is present as liquid or crystalline phases during heating and rolling of the steel (-1150 to 1350°C). A knowledge of melting relations in synthetic mixtures of iron oxide, manganese oxide, and silica will give a clue to these problems. Methods for determining such relations and the results obtained are described iln this paper. I) PREVIOUS WORK A number cf previous studies have dealt with the three "binary"* systems bounding the system iron oxide-mangar,.ese oxide-silica. The system iron oxide-silica was studied by Bowen and shairerl in 1932. Their data were obtained by equilibration of mixtures in contact with metallic iron. Phase relations for the system iron oxide-silica ill atmospheres of different oxygen pressures car1 be derived from data on the system FeO-Fe2O3-SiO2 as determined by Muan.2 The diagram shown iri Fig. l is a section of this system in an atmosphere of CO2 and H2 in ratio 1:l. The system manganese oxide-silica has also been the subject of several investigations. Most of the early studies suffered from a lack of proper control of the atmosphere under which the equilibrations were carried mt. Phase diagrams for the system at two well defined levels of oxygen pressures have been determined recently. Glasser3 determined stability relations in an atmosphere consisting of carbon dioxide and hydrogen in ratio 5:1, diagram Fig. 2, and Muan4 studied phase relations in the system in air.

Jan 1, 1962