By G. K. Manning, W. E. Few

T has been known for some time that both'inter-granular carbide and intergranular oxide phases cause brittleness in molybdenum. Parke and Ham' indicated that 0.0025 pct 0 present in molybdenum after solidification from the melt was sufficient to induce intergranular brittleness during forging. However, material containing 0.06 pct C could still be forged. However, adding this amount of carbon to insure deoxidation causes the formation of carbides on freezing. These carbides are precipitated at grain boundaries, and Rengstorff and Fischer' have shown they have an unfavorable effect on the room-temperature ductility of molybdenum. Take? in 1928 proposed that the solubility of carbon was a constant value of 0.30 pct from room temperature up to 1800°C. In 1935, Sykes, Van Horn, and Tucker' obtained X-ray data suggesting that the solid solubility of carbon in molybdenum was between 0.07 and 0.09 pct at temperatures from 1500" to 2100°C. The a-solubility line for carbon was included in the Mo-C diagram given in the Metals Handbook as a tentative line based on the data of Sykes, Van Horn, and Tucker. In order to determine the partial phase diagrams for these systems, it was necessary to construct a high-temperature furnace suitable for heat treating molybdenum at temperatures up to 4000°F. A molybdenum resistance furnace was built for this purpose in which samples could be heat treated in a purified atmosphere and quenched from any desired temperature.' Experimental Work Solubility of Carbon: Arc-cast molybdenum supplied by the Climax Molybdenum Co. and 18-gage molybdenum wire samples produced by powder metallurgy at the Fansteel Metallurgical Co. were used in determining the a-solubility line for the MO-C system. The cast molybdenum contained 0.032 pct C initially. Two lots of 18-gage wire were used, one containing 0.011 pct C and the other 0.005 pct C initially. All material contained a carbide phase as received. Fig. 1 illustrates the carbides found in the untreated material. Heat treatment in a purified hydrogen atmosphere was found to reduce the carbon content in the as-cast molybdenum. Purified argonT also decarburized molybdenum samples at temperatures above 3500°F; however, the carbon content remained constant during heat treatment in purified argon at lower tem- peratures. The argon was purified by passing it over titanium at 750 °C and then through a magnesium perchlorate drying tower. The hydrogen was purified by passing it through a commercial hydrogen deoxidizer, followed by a drying tower. Specimens having different initial carbon contents were heat treated in argon at 3500°F for periods ranging from 5 min to 5 hr and were analyzed for carbon. Samples of the same final carbon content had the same microstructures regardless of time at temperature. Furthermore, a gradient between center and surface in the amount of undissolved carbide particles present was never observed. It was concluded that at these low carbon levels, and at the high temperatures involved, diffusion proceeds so rapidly that the specimen is always substantially homogeneous in carbon content, in spite of the gradual loss in carbon. Based on the above findings, the following procedure was used to determine the carbon-solubility limit at 3000°, 3500°, and 4000°F. At each of these temperatures, a number of samples were heat treated, as shown in Table I, and rapidly cooled to room temperature. Since the samples lost carbon in proportion to the length of time heated, a series of samples were obtained of varying carbon contents. By use of a rapid cooling rate, the phases present at the high temperature were retained at room temperature. All samples were examined microscopically. Those found to contain either no excess carbide phase or only a very small amount were then analyzed for carbon. The samples actually analyzed for carbon

Jan 1, 1953

By E. W. Filer, R. P. Smith, L. S. Darken

The solubility of nitrogen gas in purified iron and low alloy steels is determined for the y region (930° to 1350°C). The diffusivtiy of nitrogen is estimated from the rate of approach to equilibrium. The investigation of aluminum-killed steels, held in nitrogen, discloses precipitation of aluminum nitride, the solubility of which is determined. ALTHOUGH several investigations of the solu-bility of nitrogen gas in y iron have been reported, all have made use of the method adopted by Sieverts in his classic work, whereby the solubility is determined by the pressure or volume change of the gas. The agreement between different investigators* is rather poor, particularly as compared to the self-consistency of results of several individual investigators. The present report represents a portion of our investigation of the equilibrium of nitrogen and nitrogenous atmospheres with iron and steels. The method adopted in this temperature region (910" to 1400°C) consists of holding the specimen in gaseous nitrogen, quenching (or cooling), and determining the nitrogen content by direct analysis (solution in acid followed by distillation and titra-tion of the ammonia).** Up to 1050°C a 20 in. vertical wire-wound (Kan-thal) furnace was used; this was wound in three sections so that by proper adjustment of relative currents, and use of a modulator1 and a commercial controller (using a chromel-alumel control couple), a zone almost 6 in. long could be maintained uniform within a few tenths of a degree. Since the temperature coefficient of the nitrogen solubility is low, the full precision was not utilized and a variation of l° to 2" was tolerated; a variation of a similar amount also occurred occasionally between the beginning and end of the experiment. At higher temperature a vertically mounted, tubular Globar furnace and control unit was used; the zone of uniformity (l° to 2"C) was here limited to about 2 in.; fluctuations with time were comparable to those in the wire-wound furnace. Reported temperatures were measured by use of a platinum-platinum-rhodium thermocouple, which was frequently com- pared with a similar standard couple which was calibrated at the gold and palladium points and also compared with one certified by the Bureau of Standards; error from this source is believed to be less than 1 "C. Nitrogen gas from a commercial cylinder was mixed with slightly over 1 pct H by use of a gas mixer described previously.' This mixture was passed over hot copper and through ascarite and phosphorus pentoxide to remove oxygen and water vapor. The purified gas contained 1.05 pct H. This procedure was adopted to prevent the formation on the specimens of oxide film, which is well known to be nearly impervious to nitrogen; its success was attested by

Jan 1, 1952

By N. J. Grant, W. R. Opie

THE amount of hydrogen that will dissolve in lead has been considered negligible. However, a limited number of measurements made recently using apparatus built for determining hydrogen solubility in aluminum alloys' indicate that liquid lead will hold a small but appreciable amount of hydrogen in solution. The apparatus used was similar to that developed by Sieverts.' This consists of a bulb to hold the molten metal, a gas burette for introducing a measured quantity of gas into the bulb and a manometer for measuring the gas pressure in the bulb. Measurements are made by introducing enough of an insoluble gas (helium) to fill the system at a given temperature and pressure, thereby determining the hot volume of the bulb. This gas then is pumped out and hydrogen is introduced until the same pressure is reached, the metal being maintained at the same temperature while in contact with each gas. The difference between the volumes corrected for pressure is then the hydrogen solubility. A more detailed account of the procedure can be found in refs. 1 and 2. The lead was melted in an alundum crucible by induction heating to provide uniform temperature and an important stirring effect. The metal was the purest obtainable, 99.999 + , prepared especially by the research department of the American Smelting and Refining Co. Measurements were made by approaching the equilibrium value from high and low temperatures during the constant pressure runs, and from high and low pressures when the temperature was held constant. Thus a number of measurements were made on each of two large samples which weighed 336 and 398 g. The gases were purified as .described in ref. 1. The effect of temperature on the solubility was studied with the pressure held constant at 760 mm of Hg. To show the effect of pressure, solubility measurements were taken at two constant temperatures, 600" and 900°C. Results The effect of temperature on hydrogen solubility is shown in Fig. 1. The curve representing the data is parabolic, as are plots of hydrogen solubility vs. temperature for other metals and alloys (aluminum,' copper," and iron,& for example). Fig. 2 shows the relationship that exists when the solubility is

Jan 1, 1952

By C. Wert, P. Bunn

Determination of the solid solubility of gases in metals is usually done by one of two methods. The first is an additive method, in which measurement is made at temperature of the maximum amount of gas absorbed by an initially degassed piece of the metal. Gas additions are made until the dissolved gas first comes into equilibrium with a compound. This method is most useful at relatively high temperatures where the amount of gas absorbed is relatively large and where equilibration of the dissolved gas with the gas atmosphere can be achieved in a relatively short time. The second is a precipitation method. A supersaturated solution of the gas in the metal is held at temperature until equilibrium is established between the gas atoms in solution and a compound. The quantity of dissolved gas is then determined by some physical measurement which is sensitive only to the gas in solution. This method is generally useful in low temperatures. This paper describes measurement of solubility of nitrogen in tantalum whereby measurements at low temperatures using internal-friction methods are plotted together with existing measurements at high temperatures. The solubility is thereby known from less than 0.5 at. pet at 350°C to near 13 pet at 2300°C. Several measurements have been reported of the solubility of nitrogen in tantalum. These are collected in Fig. 1. Three single determinations by Ke,1 Andrews,2 and Brauer and zapp3 are plotted along with a series of measurements by Vaughn, Stewart and schwartz4 and Gebhardt, Seghezzi, and Fromm.5 Although not much doubt exists about the solubility being in excess of 10 at. pet above 2000°C, the solubility indicated at low temperatures depends on whose data are selected as being most reliable. The variation is enormous, being at least an order of magnitude at 500°C. Accordingly, a measurement was begun to examine this discrepancy. The method of measurement finally selected was that of internal friction. A solid solution of nitrogen in tantalum was prepared by heating a tantalum wire in a dilute at-

Jan 1, 1964

By A. U. Seybolt

The solubility of oxygen in a iron has been determined in the range between 700° and 900°C. The solubility is a function of temperature and varies from about 0.008 pct oxygen at 700°C to atureandabout 0.03 pct at 900°C. The heat of solution is approximately +15,500 cal per mol. AS pointed out in a recent paper by Kitchener et al.,1 there has been a lack of agreement among many investigators even as to the order of magnitude of the solid solubility of oxygen in the various forms of iron. This lack of agreement is attributable in large part to the difficulties in the determination of a small oxygen solubility; but because the problem has remained so long unsettled, it also indicates a lack of interest which is rather surprising when the demonstrated importance of small amounts of soluble nonmetallic impurities in iron is considered. The work of Kitchener et al. apparently leaves the solubility of oxygen in iron in a satisfactory state, but no attempt was made to investigate the solubility in a iron. The solubility of oxygen in a iron is actually of greater interest, since it is in this form that iron and mild steels are employed ordinarily. That the effect of oxygen in iron is of more than theoretical interest has been well established by Fast,' and more recently by Rees and Hopkins," who demonstrated that oxygen in the range between 0.0008 and 0.27 wt pct has a pronounced effect upon the mechanical properties. Previous Work and Methods Used To report in detail the literature relating to the solubility of oxygen in a iron would require an inordinate amount of space. For those interested in reviewing this work, a bibliography4-13 of the more significant papers is appended. In general, two methods of studying this problem have been used. One is the gas-metal equilibrium method where the H2O-H2-Fe or the CO2-CO-Fe equilibria have been used. The other is the more direct approach of the oxidation of thin strips of pure iron by packing in mill scale or by air or gaseous oxygen at some desired temperature. In this method oxygen is allowed to oxidize the surface and then to diffuse inward until saturation is obtained. In the gas-metal equilibrium method the oxygen dissolved in solid iron at a given temperature is proportional to the ratio of the water vapor-hydrogen pressures or the CO2-CO pressures over the sample for small ratio values. If the ratio becomes higher than a critical value, then an oxide phase makes its appearance (the solution becomes supersaturated). In principle, it is possible to use a series of H2O/H2 or CO2/CO ratios and to find by analysis the corresponding amounts of oxygen in solid solution at constant temperature. At the point where a very small increase in the gas ratio (increase in oxidizing powder) produces a large increase in oxygen content, the solid solubility limit is reached. Alternately, if the critical ratio is known, it is possible to use the procedure of Kitchener et al.1 and to use a ratio which is near but below the critical one. The solubility corresponding to this lower ratio will not be the saturation solubility at the temperature employed, but the saturation solubility can be calculated by multiplying the measured solubility by the critical ratio over the ratio used. However, in the case where oxygen gas is the oxidizing medium, the saturation solubility is not a function of pressure, providing the pressure exceeds the dissociation pressure of FeO in equilibrium with iron. This is 1.2x10-16 mm at 800 °C, according to Dushman." As pointed out by Darken17 in discussing the FeO phase diagram, most of the possible errors tend to yield high values of oxygen solubility. For example, one circumstance which evidently caused the reporting of many high values was the use of finely divided or powdered iron in the gas equilibrium method. Because of the large surface area of such a sample, and the likelihood of some surface contamination if only by exposure to air, the results tended to be high. The direct oxidation method which was used in this work has the advantage in that it is simple and direct, but it suffers from one disadvantage: equilibrium can only be approached from the low oxygen side. The important factors to be kept under control are the following: 1—use of high purity iron to avoid internal oxidation (oxidation of readily

Jan 1, 1955

By A. U. Seybolt

Since the time this topic was originally treated in 1954, more recent French3,1 work has been published making it advisable to repeat the earlier oxygen solubility experiments, but using iron of a higher purity. Upon repeating oxygen saturation experiments with zone-refined iron, it was found that the oxygen solid solubility was at least an order of magnitude less than previously observed. SINCE the publication of an earlier paper1 (1954) on this subject by the present author, several contributions on this topic have appeared. Meijering2 in 1955 attempted to reconcile recent conflicting solubility data, without reaching any definite conclusion. sifferlen3 (1955) found that iron of high purity appeared to absorb a quantity of oxygen (0.005 to 0.025 pct) approximately proportional to the structural imperfections present, such as polygonization and grain boundary area. However, he also indicated that purity itself was a significant factor. He concluded that very pure iron nearly free of lattice imperfections would have essentially zero oxygen solubility. His second paper4 (1957) supported this contention since a zone-melted iron containing initially 0.0007 pct O analyzed only 0.0006 pct 0 after prolonged soaking at 850°C with an FeO layer on the surface. Because of the discrepancy between the results of Ref. 1 and those of Sifferlen, it seemed desirable to attempt to resolve this disagreement. EXPERIMENTAL PROCEDURE AND MATERIALS The experimental method used by sifferlen3,1 was essentially the same as that of Ref. 1. In this technique thin iron strip with a surface layer of FeO is soaked for prolonged periods at an elevated temperature in order to saturate the iron with oxygen. After two days at temperatures near 800° to 900° C, one would expect that the iron would be in equilibrium with the surface FeO. In the work reported in Ref. 1 there was evidence that two days holding at 8000to 900°C was more than sufficiently long for saturation. Sifferlen used 48 hr at 850°C. Because of the evidence presented by Sifferlen that the apparent oxygen solubility is a function of iron purity, three grades of iron were used as indicated in Table 1. The Bureau of Standards wire was used only for resistivity tests, while the other two irons were used for saturation-analysis tests of the type described above.

Jan 1, 1960

By J. Chipman, H. A. Wriedt

DURING the past twenty years, a considerable background of knowledge has been built up on the chemical behavior of oxygen in liquid iron. Little is known regarding oxygen in liquid nickel or the effect of nickel as an alloying element on the behavior of oxygen in liquid steel. The solubility of oxygen in liquid iron was determined by Fetters and Chipman' and, more precisely, by Taylor and Chipman.' The Ni-NiO eutectic was placed by Merica and Waltenberg"' * at 1438°C and 0.24 pct 0, and this point has been confirmed by others." O It was reported by von Bohlen und Halbach and LeitgebelT that nickel and its oxide are miscible in all proportions at 1600°C, but this report is discredited by observations of others. The melting point of NiO according to von Wartenberg and ReuschV s 1990°C. Approximate values of oxygen solubility at several temperatures were reported by Hensel and Sc0tt.O The data of Krupowski and Balickil0 are inconsistent with those of Hensel and Scott and indicate a solubility less than half that found in the present study. For oxygen solubility in Fe-Ni alloys under pure iron oxide-nickel oxide slags, only the scattered data of von Bohlen und Halbach and LeitgebelT are avail- able. The careful work of Bardenheuer and Brauns" involved silica-saturated slags. The equilibrium between Fe-Ni alloys and iron oxide-nickel oxide slags was studied by zur Strassenu and by Jander and Senf,u but no oxygen analyses were reported. Oxygen in Pure Nickel Apparatus and Nlethod: Samples were taken with a "Taylor sampler" from a bath of molten electrolytic nickel held under an air atmosphere in a magnesia-lined 30 lb induction furnace. Saturation of the melt with oxygen was effected partly by the addition of chemically pure black nickel oxide and partly by the air atmosphere. Samples were taken only when there was a clearly visible oxide phase present. To avoid contamination of this oxide phase, the silica-sheathed Pt—Pt-10 pct Rh thermocouples, by means of which temperatures were measured, were immersed in the melt for the minimum time consistent with accurate reading. Samples and temperature readings were taken only after the furnace had been

Jan 1, 1956

By D. G. Westlake, D. T. Peterson

The saturation solubility of thorium dihydride in thorium was studied by saturation of samples and subsequent analysis. The solubility increased from about 1 at. pct at 300°C to above 20 at. pct at 800 °C. Over this temperature range the log of the solubility was a linear function of the reciprocal absolute temperature for thorium of good purity. The heat of solution of thorium dihydride was found to be 7.9 kcal per atom of hydrogen in crystal bar thorium and 6.6 kcal per atom of hydrogen in Ames thorium, The important effect of hydrogen on the physical and mechanical properties of many metals is receiving increasing recognition. The basic physical and chemical data necessary to help explain the observed effects of hydrogen on the mechanical proper ties of metals are all too often not available. The solubility of hydrogen in thorium metal was determined to provide a portion of this basic data for the thorium-hydrogen system. The absorption of hydrogen by thorium metal and the formation of thorium hydrides was studied by several investigators, beginning in 1891, and their work is summarized in Gmelin's Handbuch.1 No effort was made to determine the extent of solid solubility in the metal in these early investigations and the impure metal available made interpretation of the results uncertain. Nottorf2 reported the results of a careful study of pressure-composition isotherms for the thorium-hydrogen system. The principal interest in this work was in the composition and dissociation pressures of the thorium hydrides. Mallett and campbel13 reported the pressure-composition isotherms for the thorium-hydrogen system up to the composition of thorium dihydride. The saturation solubility of thorium dihydride in thorium was reported to be 13 at. pct at 650°C and 23 at. pct at about 900° C. Mallett and Campbell used thorium metal which had been prepared by the calcium reduction of thorium tetra-fluoride or thorium oxide. The results obtained with thorium of these two types agreed within the experimental error. PROCEDURE AND MATERIALS Procedure—The method used to determine the solubility was to saturate a sample of thorium with hydrogen and analyze a portion of the saturated sample. This method was chosen rather than a determination of pressure-composition isotherms since it was much less time consuming and could be applied at temperatures at which the equilibrium hydrogen pressure was too low to measure. The

Jan 1, 1960

By L. M. Pidgeon, K. T. Aust

There has been considerable interest in the possible use of titanium in magnesium alloys.' Zirconium has shown some promise in this connection2 and its general similarity with titanium suggests that the latter might act in a similar manner. A literature survey revealed that quantitative data on the Mg-Ti system was unavailable. Several patents3 have claimed that titanium additions from 0.2 to 4 pct to magnesium alloys were possible, but no mention was made as to the form in which the titanium existed in the alloy. Kro114 succeeded in introducing only traces of titanium into magnesium by bubbling TiCl4 through the metal under argon or by reacting it with sodium titanium fluoride. The application of theoretical data given by Carapella5 based on Hume-Rothery's principles, involving atomic size factor, crystal structure, valency and the electro-chemical factor, suggests that a Mg-Ti alloy is a favorable case, and the system appeared to warrant experimental examination. Experimental Procedure and Results THERMAL ANALYSIS If titanium is appreciably soluble in magnesium, a change in the melting point of the magnesium might be detectable using standard cooling curve methods. Magnesium was melted in graphite crucibles under an argon atmosphere, the assembly being enclosed in a silica tube. Graphite thermocouple protection tubes served also to stir the melts. The apparatus was very similar to Fig 1, with the addition of a refractory and baffle system to prevent undue heat losses from the top of the crucible. Chromel-alumel thermocouples were calibrated using Al of 99.97 pct purity. Dominion Magnesium Limited sup- plied redistilled high purity magnesium of the analysis given above. Titanium was added in three different forms: 1. Titanium powder —100 mesh, from the Titanium Alloy Manufacturing Co., Niagara Falls, N. Y. 2. Sheet titanium from the U.S. Bureau of Mines, produced by Mg reduction of TiCl4. 3. Magnesium —50 pct titanium master alloy from Metal Hydrides Inc., Beverly, Mass. The melting point of the high purity magnesium used was measured experimentally as 651.0°C. More than a dozen tests were conducted using titanium from the three sources referred to above, in calculated additions up to 20 pct titanium, at temperatures between the melting point and 1000°C and holding periods up to 6 hr. In no case was evidence obtained of solubility of titanium in magnesium, using inverse-rate and time-temperature curves. The melting point of the magnesium was unchanged within the accuracy of measurement, namely -+0.5°C; and no other thermal arrests were detected. Metallographic investigation of the thermal analysis billets indicated that the titanium additions were apparently mechanically entrapped in the magnesium in segregated areas. Consequently, these samples were not analyzed for titanium. The master alloy proved to be a mechanical mixture of titanium particles in a magne- sium matrix. These results indicated that the titanium solubility, if such existed, could not be obtained by the usual thermal methods. X RAY DIFFRACTION INVESTIGATION In an effort to detect solubility of titanium in magnesium, samples were investigated using both the Debye-Scherrer and the Focusing Back-Reflection methods. Filings from samples of the thermal analysis billets and from pure magnesium were annealed in argon one hour at 350°C to relieve mechanical strain. Measurements made of the interplanar spacings showed no difference between the Mg-Ti samples and pure magnesium. The interplanar spacings could be measured to within 0.0002A, and the greatest variation found was 0.0004A, in the back-reflection method. The diffraction lines for magnesium were not shifted by the titanium additions indicating that the solid solubility of titanium in magnesium is of a very low order—less than 0.5 pct. From both diffraction methods, a d or interplanar spacing of 0.817A was obtained for the redistilled high purity magnesium. This latter value is not given in the standard X ray diffraction cards for magnesium metal or vacuum distilled magnesium. Theoretical calculations for a close-packed hexagonal space lattice for magnesium indicate that the planes {2134) should give a line which was found. The relative intensity for this reflection at 0.817A is slightly less than that at 0.870k for magnesium. SOLUBILITY OF TITANIUM IN LIQUID MAGNESIUM The Mg-Mn system was examined by Grogan and Haughton6 who were

Jan 1, 1950

By A. L. Mowry, John T. Norton

Isothermal sections of the pseudo-ternary carbide systems TiC-VC-ZrC, TaC-VC-ZrC, and NbC-VC-ZrC have been examined. The sections contain an inverted U shaped two-phase field whose maximum extent is 77 molecular pct for Tic, 64 pct for TaC, and 51 pct for NbC. lsoparametric lines were determined which show the curvature of the single-phase field and the direction of tie lines in the two-phase field. It was not possible to show any relationship between atom size and the extent of the two-phase field. REVIOUS work' on the solubility relationship of several pairs of refractory cubic monocarbides from the group Tic, ZrC, VC, NbC, and TaC has shown that, with the exception of the system VC-ZrC, they all form continuous series of solid solutions. It was demonstrated that the limited solubility in the case of VC-ZrC system was primarily a question of the size factor, the size difference between vanadium and zirconium being greater than the limiting value of about 15 pet. It is interesting to consider the results of combining these isomorphous carbides in groups of three and to determine the isothermal section of the pseudo-ternary diagram at, for instance, 2000°C, a temperature that will assure an equilibrium structure in a reasonable length of time. In the ternary systems where the three pairs form complete solid solution series, it is probable that the isothermal ternary section would be a single- phase field, although this is not necessarily the case. However, if one pair of carbides has a very limited solubility, then there must be a two-phase field of some extent, and it is the purpose of the present work to examine the extension of this field and to determine if it can be related to the nature of the third carbide. This condition is fulfilled if the VC-ZrC pair, which has only limited solubility, is combined with Tic, TaC, or NbC. The relative sizes of the metal atoms undoubtedly play a role in the extent of the single-phase field, and the values obtained from the pure carbides, assuming close-packing between metal and carbon atoms and a carbon atom diameter of 1.54A, are

Jan 1, 1952

By J. T. Norton, A. L. Mowry

The monocarbides of the A subgroup elements in the fourth and fifth group of the periodic table in addition to being hard and refractory are of special interest in that they are isomorphous in crystalline structure. They are cubic with a sodium chloride type structure in which the metal atoms are essentially close packed in a face-centered cubic arrangement with the carbon atoms placed in the interstices between. Interstitial structures of this close packed type were first investigated systematically by Egg1 and he gave the rule for their formation, stating that the radius ratio of the nonmetal to the metal atom should not exceed the value of 0.59. The carbides of interest are those of titanium and zirconium of the fourth group and vanadium, columbium and tantalum of the fifth group. Table 1 shows the radius ratio using the Goldschmidt radii for 12 coordination for the metal atoms and the diamond radius for the carbon atom. It will be noted that while there is considerable variation in the size of the metal atom, in all cases the ratio is smaller than the limit of 0.59 placed by Hägg. It has been known for some time that these cubic carbides are soluble in one another, at least to some extent or, in other words, the metal atoms can be replaced, one by another without destroying the stability of the structure. Since the stability of these close packed interstitial substances appears to depend more upon geometry than upon the exact chemical nature of the atoms involved, it is of interest to examine the possibilities of replacement in these carbides in some detail. Hume-Rothery2 has pointed out the importance of the difference in size of solute and solvent atom as a factor in limiting the solubility in simple binary solid solutions. Largely on an empirical basis, he states that if the difference in size between solvent and solute atom is more than 14-15 pct of the solvent atom, the range of solubility is very restricted. The atom size was based on the distance of closest approach in the elements involved. While there is some question as to how one should calculate the size of the metal atom in the carbide structures, reference to Table 1 will show that zirconium is the largest and vanadium the smallest of the group and that the difference is about 15 pct. The Ti-Zr difference is about 9 pct and the others are smaller. Thus one would predict that if the size factor controls the solubility, all of the pairs except VC-ZrC would have wide or complete solubility whereas this latter pair is on the border line and might have restricted solubility. The purpose of the present investi- gation was to examine the solubility of the several pairs of carbides by heating them together until equilibrium was established and then examining the product by X rays. Previous Work Agte3 and his associates prepared various transition metal carbides and determined the melting points of binary mixtures. He concluded from the shapes of the melting point curves that there was extensive solubility in the case of the cubic carbides. Umanskii and his colleagues made an investigation of a number of pairs of the cubic carbides, using X rays and plotted lattice parameter vs. composition curves for the systems TaC-Tic, CbC-Tic, TaC-ZrC and CbC-ZrC. All pairs showed a continuous series of solid solutions. The first two pairs gave a linear relation while the latter two showed a negative deviation from Vegard's law. Kiefer and Nowotny, in a paper which became available after the present work was well advanced, investigated the binary pairs of the five cubic carbides by means of X rays. Relatively few points were obtained and results indicated that in some cases, at least, equilibrium was not reached at the temperatures used. The results indicated that solubility in the VC-ZrC system was not complete. All of the results of previous investigations indicated the desirability of a more detailed study. Materials The raw materials used were mono-carbides of titanium, zirconium, vanadium, columbium and tantalum and were the purest which could readily be obtained commercially. Spectrographic qualitative analysis showed that the CbC and TaC contained less than 1 pct

Jan 1, 1950

By J. T. Norton, A. L. Mowry

S. J. SINDEBAND*—(1) Discussing the properties of the powders used, Mr. Rostoker mentioned a silicon powder as being between 150 and 325 mesh. We always had much difficulty in measuring particle size of silicon powder by screen analysis, because of its tendency to agglomerate. I would be interested in the method used to measure these particle sizes. (2) Mr. Rostoker maintains that the measurement of magnetic properties is more accurate in determining complete homogenization of an alloy, than is the X ray diffraction technique. I wonder whether this is really true. Even when diffusion is complete, magnetic properties will change during continuation of the heat treatment, due to change in density and pore shapes, as has been demonstrated by Mr. Rostoker himself. Which effect is faster, the diffusion of the alloy components or the attainment of final density, will, in my opinion, depend very much on initial material and sintering conditions used. For magnetic applications, of course, the magnetic measurements are most suited for determining the point at which equilibrium conditions are reached. (3) I was glad to see that Mr. Rostoker had used sample sizes which are similar to those I had used previously, and I believe that ring samples of about 2 in. od will become more or less standard samples for the determination of magnetic properties of powder metallurgy products. I should like to ask how the density was changed for the samples on which the effect of porosity was investi- gated, and, further, why the sintering temperature used for this series of experiments was so low. It is somewhat surprising that a 24-hr treatment at 850°C acts so much more to spheroidize the pores than a treatment for 1 hr at 1100°C. But the effect seems to be indisputable. I have made an investigation of the influence of sintering temperature for longer times on the maximum permeabilities of iron powder compacts which was presented at the International Powder Metallurgy Conference in Graz, in 1948, and I hope that these results will be published here within a short time. The results of this investigation are confirmed by Mr. Rostoker's findings that the change of time from 1 to 24 hr changes the permeability behavior considerably in the direction as indicated by Polder and Van Santen for spheroidiza-tion of pores. I do not quite understand Mr. Rostoker's explanation of the influ-

Jan 1, 1950

By Allan Martin, R. A. Swalin

Diffusion rates of manganese, aluminum, titanium, and tungsten in nickel were measured at temperatures between 1100° and 1300°C. Activation energies, Q, and values of the frequency factor, Do, were calculated for each system. Values of Q were found to be within 15 pet of that for self-diffusion of nickel in agreement with present theories of diffusion. ONE of the most interesting problems in diffusion concerns factors governing the order of diffusion coefficients of various solutes in a common solvent metal at low solute concentrations. An early suggestion by Rhines and Mehl' was that diffusion coefficients might each approach that of the self-diffusion coefficient of the solvent itself. Later Thomas and Birchenall' pointed out correlations between the order of the diffusion coefficients and the freezing point depressions of the solvent by the various solutes. Other correlations have been sought. To settle this question it seems likely that much more data will be needed and, in particular, data collected at low solute concentrations. This type can be obtained by special analytical techniques as well as by use of radioactive tracers. The following study was made of diffusion of manganese, aluminum, titanium, and tungsten in a common solvent, nickel, at relatively low solute concentrations: 1—Production of alloys of nickel with manganese, aluminum, titanium. and tungsten at concentrations of the order of 1 atomic pet. 2—Use of pressure-welded diffusion couples in cylindrical form. 3—Diffusion anneals in the temperature range of 1100" to 1300°C. 4—Lathe sectioning of the diffused couples. 5—Spectrophotometric analyses of lathe turnings for the solute being studied. 6—Calculation of the diffusion coefficient for each of the solutes as a function of temperature. 7—Interpretation of results with current theories of diffusion. Experimental Work Materials—Two types of nickel were used in this research. The grade designated as Vacuum melted Mond nickel was used for all diffusion systems except the Mn-Ni system for which the Vacuum melted electrolytic nickel was used. Analyses of the two grades are given in Table I. The manganese used in making alloys was 99.9 + pet pure, aluminum 99.99 pet pure, titanium 99.9 pet pure, and tungsten of C.P. grade powder. Alloys used in this investigation were prepared by melting in vacuo or under a low pressure of argon. After melting, all heats except those of nickel-manganese were poured into a cylindrical copper mold 3 in. long and 1 in. ID. In the case of nickel-manganese, the alloys were solidified in the melting crucible. For nickel-aluminum heats alumina crucibles were used and for all other heats, zirconia crucibles.

Jan 1, 1957

By Roger A. Gregg, Barry J. Piearcey

MANY of the nickel-base superalloys developed recently for use in the as-cast condition exhibit a massive "white-etching" constituent1 in the inter-dendritic regions. Commercial alloys in this category are SM 200,* IN 100, INCO 713, and Nicrotung. The appearance of a similar microconstituent in nickel-rich Ni-A1-B alloys has been reported by Schijbel and Stadelmaier. Their investigation revealed that this constituent was the binary eutectic of the terminal nickel-base solid solution and the inter metallic based on Ni3A1. This binary eutectic is degenerate and NhA1 is the major phase. At lower temperatures the eutectic composition lies within the NkA1 phase field and under equilibrium conditions is single-phase NisAl. Taylor and F&apos;loyd3 have shown that in Ni-Al-Cr alloys containing at least 8 at. pct Cr, liquid compositions which solidify by the eutectic reaction in the nickel-rich portion, precipitate nickel-base solid solution and NiAl rather than nickel-base solid solution and NkA1 in the binary Ni-A1 system. Since the nickel-base alloys contain chromium in excess of 8 at. pct and are further alloyed with one or more of the elements titanium, cobalt, molybdenum, or tungsten, it is possible that the eutectic could contain NiAl rather than NisAl. In addition, Benson4 has reported that in low-nickel austenitic high-temperature alloys, which possess Ni/(Al + Ti) atomic-weight ratios <18.0, the Ni (Al, Ti) phase may precipitate from the melt during solidification. Since SM 200 and similar high-temperature materials were developed from alloys which were designed for solution treatment, the appearance of a eutectic would indicate that the limit of solid solubility has been exceeded. The purpose of this note is to confirm that the massive white constituent in the complex nickel-base alloys investigated is based on the binary eutectic Ni + NbAl and that the limit of solid solubility need not be exceeded to produce it, in common with other observations of cast alloys. Successive polishing of a sample of SM 200 showed that, in agreement with Schobel and Stadelmaier, particles of the constituent were spherulitic and in particular were a) situated between cored dendrite arms, Fig. 1, and b) nucleated at the surface of dendrites, Fig. 2. The Ni/(Al + Ti) atomic-weight ratios for the nickel-base alloys which were observed to contain the massive eutectic constituent in the interdendritic regions are 12.1 (Nicrotung), 9.2 (IN loo), 19.5 (INCO 713), and 14.5 (SM 200). However, the results of X-ray analysis of these alloys in the as-cast condition failed to reveal the presence of the Ni (Al, Ti) phase. An electron microanalyzer was therefore employed to analyze the composition of this constituent in SM 200. The results of analyses of representative particles are as follows5: 8.4 at. pct Ti, 8.8 at. pct Co, 5.5 at. pct Cr, 0.9 at. pct W, 12.8 at. pct Al, and 63.6 at. pct Ni. Assuming that

Jan 1, 1964

By F. Weinberg

The distribution of solute during the progressive solidification of dilute Sn-Ag alloys was determined in both solid and liquid as a jbnction of growth rate, rod diameter, temperature gradient, and solute concentration, using radioactive tracer techniques. The results indicated that partial mixing occurs in the liquid during freezing for most of the conditions investigated, approaching complete mixing for larger rod diameters (>2mm) and slow growth rates. Measured solute distributions were fitted to distribution functions based on diffusion controlled solute transport in the liquid state, by treating the normal solute diffusion constant and distribution coefficient as variable solute transport and segregation parameters. Values of these parameters were determined for the growth conditions investigated. Observations were made to determine whether mixing in the liquid was primarily due to volume changes in freezing or to differences in density between solute and solvent. The former effect was investigated using a selected Sn-Bi alloy as a solvent with zero volume change on fusion, and the density effect was studied using vertical solidifications of Sn-In and Sn-Ag alloys, systems having, respectively, very small and large differences in density between solute and solvent. The result indicate that mixing in the liquid cannot be primarily attributed to either volume changes or density differences. THE solute distribution in progressively solidified rods of dilute alloys, in which there is complete mixing in the liquid, is given by the expression1 where C, is the solute concentration in the solid at the point where the fraction g of the material has solidified, C, is the initial solute concentration and k is the equilibrium distribution coefficient. If it is assumed that there is no significant con-vective mixing in the liquid, then the solute distribution in the initial portion of a semi-infinite rod has been calculated to be2 where t is the time from the start of freezing and x1 is the distance in the liquid ahead of the solid-liquid interface at time t. Expressions [1] and [2] describe the limiting cases of solute distribution in the liquid, i.e., complete mixing, or no convective mixing; in practice it might be expected that the solute distribution would be somewhere between these two cases. pfann3 has suggested that Eq. [I] is applicable for partial mixing, as well as complete mixing, if an effective distribution coefficient k1 is used instead satisfactorily describes solute distributions in rods of magnesium, n-g, and b-sb6 alloys that were progressively solidified from the melt without mechanical mixing. The values of kl were observed to depend on the growth rate4-6 and the temperature gradient.6 The purpose of the present investigation was to measure solute distributions in both the solidified rods and the melt as a function of the solidification variables, and to determine to what extent the observed solute distributions could be described by the above theoretical expressions, keeping in mind that expressions [2] and [3] have been derived solely for the case of diffusion controlled solute transport in the liquid and are not theoretically applicable to

Jan 1, 1963

By K. G. Davis, P. Fryzuk

WEINBERG,&apos; in an investigation of solute distributions along unidirectionally solidified rods of dilute silver in tin alloys, concluded that, for rods of 2 mm diameter or larger, a very high degree of convective mixing takes place in the melt ahead of the advancing interface. Suggested causes for this mixing were (1) thermal convection, (2) convective currents set up by changes in fluid density associated with concentration gradients, and (3) currents set up by changes in volume during freezing. Evidence was presented that causes (2) and (3) were not primarily responsible for solute mixing. Further, convective mixing took place in horizontal rods with temperature gradients as low as 6°C per cm, putting doubt on the importance of thermal convection. In the present work, convective mixing is examined in melts with known initial solute distributions. The absence of a moving solid-liquid interface eliminates convection caused by volume changes on solidification. In the first experiment, three silica tubes 2 mm in diameter and approximately 20 cm long were filled with an alloy of 100 ppm Ag in tin (99.999 pct purity), placed adjacent to one another in a horizontal furnace, and solidified from one end at 1 cm per hr. A110, a Y emitter, was used as tracer. A few centimeters at the start of the rod were left un-melted, to determine the initial concentration Go. After solidification was complete, one sample was removed. The hot furnace was then brought back to

Jan 1, 1965

By J. J. Kramer, W. A. Tiller, G. F. Bolling

The temperatures of solid-liquid interfaces have been measured during the growth of Sn-Pb alloy crystals which exhibited a cellulur substructure. A simple descriptive theory was used in combination with this data and the other measurable growth variables to predict some features of the solute segregation such as the intercell excess concentration and the depth of cell grooves during freezing. The effective distribution coefficient at the tip of a cell, a, was predicted and experimentally found to vary in the range, 1 >a > k0. At the lower limit, the severe segregation that must arise between dendritic cells was substantiated by various observations such as the existence of a second Phase even for alloys of only 0.2 wt pct Pb. ThE cellular morphology of a solid-liquid interface is known to coincide with the formation of a zone of constitutional supercooling ahead of the interface during growth.&apos; The occurrence of various cell structures, (two-dimensional cells, regular cells, dendritic cells), has been quantitatively investigated,&apos;2,4 but the segregation of solute which arises as a consequence of this mode of growth has only been examined qualitatively. An indirect method of obtaining the solute concentration at the tip of a cell cap during solidification has been de-

Jan 1, 1963

By F. Weinberg

Measurements have been made of solute segregation during dendrilic growth by using radioactive solute elements and ,measuring the activity of den(12-ites cut from decanted specimens. This has been done for both lead awl tin based binary alloys contaitzing the following solute additions: Ag, T1204, was dependet on ko, the equilibrium distribution coefficient in the following way Fay k &apos;c 0.1, C/C 0.6; for k0 >0.1. 0.6 <c,/c,< I. Qualitative obse?-vations were madc of dendritic segregation, by using autoradiographic techniques, for the Sn + Ag110 and Sn + Tlo4 systems. The observation were found to he in general agreement with the measurements ofCA/Co. Autoradiographic were also obtained of scctiolccl delzr11-iie stalks. These indicated that the stalks had a substructure, dclileated by solute corzetlt?atio?zs nlolg the substructure walls. A new dendrite growth direction <JI2> is reported for tila. SOLUTE segregation in dilute binary alloys has been investigated by Pfann,&apos; Smith, Tiller, and Rut-ter,&apos; and others. They considered the case of a slowly advancing plane solid interface, and derived expressions for the distribution of solute in both solid and liquid during solidification. To determine these expressions, they assumed no diffusion in the solid and either complete mixing in the liquid:&apos; or diffusion controlled solute movements in the liquid without any convective mixing.&apos; The present investigation considers solute segregation during dendritic growth, in which case the solid-liquid interface is not plane, and the growth rates are rapid. Segregation under these growth conditions has not been treated mathematically, because of the relative complexity of the system. It has been suggested by Chalmer, on the basis of preliminary results, that an alternative to the diffusion and heat flow controlled conditions during growth is &apos;diffusionless" dendritic growth in which solid is formed with the same composition as the liquid. He suggests this type of growth may depend upon a solvent-solute relationship that permits some solid solubility without excessive increase in internal energy, as is the case for solutions of tin in lead. On the other hand, Montariol,4 and others, have shown experimentally that some segregation does occur during dendritic growth in metals using etching and radioactive tracer techniques to indicate the concentrations of the solute. The present investigation was undertaken to determine, both qualitatively and quantitatively, the extent of solute segregation associated with dendritic growth in a series of binary alloys, as a function of solute concentration. PROCEDURE The solvent materials used were Vulcan Electrolytic tin (99.997 pct purity) and Tadanac lead (99.998 pct purity). The solute materials were Zn, Sn, and Sb (better than 99.998 pct purity), Ag and Co (99.5 pct purity), and T1 (Fisher "purified" metal sticks). Activation of the solute metals was carried out in the reactor at Chalk River, Canada. Master alloys were prepared by induction heating from the radioactive solute metal and the pure solvent, under argon, in graphite crucibles. Pieces of these alloys were then added to the solvent to give the required solute concentration. Dendrites were grown in essentially the same manner as that described by Weinberg and Chalmer, , in which controlled orientation single crystals were grown dendritically in horizontal graphite boats, and the liquid decanted. The crystals were grown and decanted in an atmosphere of tank argon. Before decanting, a sample of the liquid was drawn up in a glass tube and allowed to solidify rapidly. The orientations of the single crystals were such that <loo> was parallel to the growth direction, and (100) in the horizontal plane for lead, and [1101 and (110) respectively for tin. With these orientations long dendrite stalks formed along the bottom of the boat in the dendrite direction (<100> for lead and [I101 for tin) from which secondary branches grew. Only these secondary branches, which grew freely in the liquid from the dendrite stalk to the liquid surface, were used in the measurements. Accordingly, effects due to substrates and oxides on the surface of the liquid need not be considered. In order to measure the solute concentration C, of the dendrites, individual dendrite stalks were cut from the decanted specimens, remelted, and formed

Jan 1, 1962

By E. W. Cawthorne, R. I. Jaffee, C. M. Craighead

SOLUTION of a solid metal or alloy in a molten metal bath is used daily in melting operations, extractive metallurgical processes, and in brazing. It is generally recognized that temperature, time, agitation, and the composition of the solute metal and the solvent bath all affect solution rate. However, there is little information available in the literature on the kinetics of the process or the relative effect that these variables have on solution rate. In connection with an aluminum brazing study, data on the solution of aluminum in an A1-Si* bath to promote rapid solidification. The chemical analyses were made on drillings taken from the cast plates. The results of this work are listed in Table I. The thermal-analysis data were obtained on 200 gram samples cooled at approximately 1.5" per min. A calibrated chromel-alumel couple was used. The thermal arrests were recorded autographically on a General Electric photoelectric potentiometer recorder. The instrument was calibrated to 22.5 pct. The thermal emf was bucked with a Leeds and Northrup semiprecision potentiometer so that 1 mv represented the full scale of the GE recorder. Referring to Table I, it will be noted that the analytical results tend to be lower than the intended compositions by about 0.3 pct Si in the higher ranges. In view of the known difficulties in obtaining accurate silicon determinations by wet analysis when the silicon content is high and in view of the care that was employed in weighing and preparing the alloys, the intended compositions are believed to be more accurate than the analyses. Furthermore, when the thermal-arrest data are plotted against the intended compositions, a smooth curve is obtained, as shown in Fig. 1. This is not the case when the data are plotted against the analytical results. It will be noted from Table I that the 12.5 pct Si alloy (melt 4) showed a primary arrest at 577.6"C and the eutectic at 576.l°C. The metallographic examination of this chill-cast plate sample showed a small amount of primary silicon. These results, Fig. 1, place the eutectic at slightly less than 12.5 pct Si and are in rather good agreement with the unpublished Hanford data. In all of the subsequent work, the composition of the A1-Si dipping baths was determined by thermal analysis (spread between the primary arrest and the eutectic temperature) employing 12.5 pct Si and 577.2 °C as the composition and temperature of the eutectic. Material Preparation and Selection of the Techniques: At the beginning of this work, it was anticipated that, owing to oxide film present on the surface of the aluminum, difficulty would be encountered in obtaining rapid uniform wetting of aluminum specimens dipped in the A1-Si bath. The following etchants were investigated as possible methods of providing a thin uniform oxide film on the specimen surface: 1—phosphoric acid (H³O4), 2—fluoboric acid (HBFI), 3—sodium hydroxide (NaOH), and 4—hydrofluoric acid (HF). Tests with sheet .specimens (2x½x0.06 in.) of 2s aluminum prepared with these etchants indicated that the fast uniform wetting required for this work could not be obtained if any oxide film existed on the specimen surface. Tests were then conducted by dipping similar specimens etched in 5 pct NaOH and given a thin

Jan 1, 1956

By W. A. Jr. Slippy, E. P. Dahlberg, R. B. Reed-Hill

A large room-temperature mechanical-hysteresis effect under cyclic tensile loading was observed in zivconium specimens prestrained at 77°K so as to form large numbers of (1121) twins. The observed hysteresis loss was a maximum when the prestrain was just under 1 pct It also depended strongly on the maximum applied cyclic stress, but only moderately on loading rate and temperature (-72°to 100°C). The phenotnena have also been studied in terms of the elastic aftereffect where the data has been found to cotlforln closely to the functional relationship between strain and time, c = -RT/a In tank ft. t to)/Zr, for strains cts large as about 10-4 This eyication can be derived directly from the strain-rate equation There may be important commercial implications to the present discovery since it appears that within rather wide limits it may be possible to obtain any desired magnitude of damping capacity in zirconium melal. The damping propevties may also be given directional characteristics. It is shown that the observed anelaslic phenomena can he explained on the assumiplion that they are the resuilt of stress-induced twin-boundary movements in which the average twin increases its thickness by only a few percent. In polycrystalline zirconium, a grain is least favorably oriented for slip when its basal plane, containing the (1130) slip directions, lies nearly perpendicular to the principle normal stress. Mechanical twinning is favored by this orientation and under simple tensile deformation at room temperature the primary twinning mode is {1012).&apos; The (1012) twinning shear is small (0.17) so that, during deformation, twin growth does not greatly enhance ductility. At 77°K, on the other hand, the predominant twinning mode shifts to {1121), and many thin (1121) twins can form at small strains.&apos; Twins thus nucleated can grow readily during subsequent room-temperature deformation and permit easy deformation in unfavorably oriented grains. In addition, the (1131) twinning shear is large: 0.63. These facts have lead to a process&apos; for greatly improving the room-temperature ductility of zirconium when it contains a sizable fraction of grains with basal planes nearly normal to the stress axis. Optimum results are obtained by slightly less than 1 pct prestrain. The effect is large so that a 50 pct elongation increase is readily attained. A large room-temperature mechanical-hysteresis effect has also been observed in zirconium specimens prestrained at 77°K. The present paper is concerned with some aspects of this effect which the experimental observations strongly indicate is primarily the result of strain-induced {1121) twin-boundary movements. This clearly suggests that mechanical twins formed by plastic deformation can cause anelastic effects similar to those previously observed2 for annealing twins and twins associated with phase transformations. EXPERIMENTAL PROCEDURES All specimens were prepared from arc-melted sponge zirconium plate stock as previously described,3 which has a preferred orientation with basal planes aligned parallel to and uniformly distributed around the rolling direction. Both lonti-tudinal and transverse tensile specimens, with axes parallel and transverse, respectively, to the plate rolling direction, were cut from this plate. In a longitudinal specimen most grains are favorably oriented for slip, while in a transverse specimen a large fraction are unfavorably oriented. Prestraining at 77°K was performed in two ways. In one, annealed zirconium plate stock was cooled in liquid nitrogen and then rolled in the transverse plate direction to strains varying from 0.5 to 12 pct. Cylindrical 1/8-in.-diameter by 1-1/4-in.-gage-length tensile specimens were machined from this material. In the other, previously machined tensile specimens were prestrained in tension at 77°K between 0.2 and 3.8 pct. Type FA 25-12 SR4 strain gages were cemented to all specimen gage sections. All tests were performed on an Instron testing machine of 10,000-lb capacity. EXPERIMENTAL RESULTS Fig. 1 shows a typical two-cycle room-temperature stress-strain diagram for a specimen prestrained 0.65 pct by rolling at 77°K. The maximum stress in both cycles was 14,500 psi. Note that in the first cycle the loading and unloading curves are unsymmetrical so that a residual strain, er, remains after unloading. In the second cycle the stress-strain curves form a nearly symmetrical hystere-

Jan 1, 1965