Search Documents

By A. W. Dana, F. J. Shortsleeve, A. R. Troiano

The phenomenon of flake formation which may occur during cooling or room temperature aging of large steel sections is caused by a combination of hydrogen and stress. As such, the transformation characteristics of austenite in a particular section play a major role in the occurrence of flakes. Isothermal and continuous cooling studies demonstrated that flake formation is particularly sensitive to nature, distribution, and relative proportions of the microconstituents in the cooled sections. In the absence of transformation stresses, abnormally high hydrogen contents could be tolerated without flaking. Flakes were not found in the absence of transformation stresses. No correlation existed between average hydrogen content and flake formation where cooling stresses were low. Hydrogen in the steel was a necessary but not sufficient condition for flake formation. DESPITE a long history of laboratory and commercial investigations, the mechanics of hairline crack or flake formation in large steel sections remains unresolved. Recent publications1-5 emphasize that flaking is still a serious problem.* immediate cause of flaking is the pressure exerted by entrapped hydrogen gas that collects in small internal cavities or voids during cooling. When the temperature of steel is low enough to preclude extensive plastic flow, the cavity pressures cause local brittle fractures (flakes). 2—The microsegregation and transformation stress theory. According to this theory, flaking results from stresses arising from the volume changes accompanying the formation of martensite and/or low temperature bainite after a large portion of the section has transformed at elevated temperatures. The proponents of the hydrogen theory suggest that stresses from other sources may be additive to the stresses produced by hydrogen and may, in some cases, provide the increment of stress necessary to produce flakes. However, the critical aspect of this theory is that no stress, except that produced by hydrogen pressure, is believed to be sufficient in itself to produce flakes. For practical considerations, this means that the only safe thermal cycle is one that reduces the hydrogen content to some low critical level below which flaking will not occur regardless of the state of transformation. On the other hand, the transformation stress theory does not rule out the embrittling effect of hydrogen. This theory simply proposes that flaking does not occur in the absence of transformation stresses. With the transformation stress theory as a basis, commercial antiflaking cycles would be designed to complete the transformation of austenite prior to cooling to ambient temperatures. Both of these theories appear compatible with industrial experience. Antiflaking cycles, such as cooling at extremely conservative rates or soaking for periods of time in the upper subcritical temperature ranges prior to cooling to ambient temperatures, may allow the following: 1—diffusion of hydrogen out of the section and, as a consequence, reduction of the hydrogen content to some safe minimum value (hydrogen pressure theory) and 2—complete decomposition of the austenite at rela-

Jan 1, 1956

By P. Bardzil, J. Gurland

An experimental study of the variation of transverse-rupture strength with composition Anexperimentaland grain studysize has shown that the strength reaches a maximum for values of the mean free path between carbide particles of 0.3 to 0.6 microns. The fracture oforiginates in and proceeds through the carbide grains mainly. Impact strength and hardness also were recorded. MOST of the physical properties of sintered carbides vary linearly with composition. The transverse-rupture strength, however, shows a unique behavior. As the amount of binder metal is varied from 6 to 25 pct by weight, the strength at first increases; then, between 15 and 20 pct Co, it reaches a maximum of nearly 400,000 psi, and finally decreases with further additions of binder metal. This behavior of the transverse-rupture strength has been reported, among others, by Englel and Sandford and Trent.' The significance of these observations has not been discussed in the literature. That it may be of more than specific importance is indicated by the very similar variation of strength with composition encountered in other systems sintered in the presence of a liquid phase, such as Tic-Ni3 and Fe-Cu.' Experimental Details All compacts were prepared and sintered according to normal industrial practice. The average diameter of WC grains and the mean free path between grains were measured on metallographically prepared samples by a method of linear and planar analysis sing the relations where d is the average diameter of dispersed grains; Nl is the number of noncontiguous grains intersected on a metallographic plane by a line of unit length; N, is the number of noncontiguous grains per unit area; P is the mean free path between grains of dispersed phase; and f is the volume fraction of dispersed phase. Approximately 1000 grains were counted on each sample. For each composition d2 was plotted against P, the resulting straight lines serving as a check on the measurements. The distribution curves of the WC powders of different average diameters were homologous, and no attempt was made to influence the grain size by blending powders, adjusting the sintering conditions, or otherwise altering the particle size distribution. Densities were measured by differential weighings in air and water. The degree of densification did not vary consistently with either composition or grain size. The density is influenced by slight amounts of impurities, specifically by 0.1 to 0.2 pct Fe which enters the powders during ball milling. As an illus- -tration of the experimental variations, a number of measured densities are listed in Table I. They are expressed in percentage of theoretical density, as calculated from the published X-ray densities of WC and Co.' For the purpose of determining the transverse-rupture strength, rectangular test specimens (3/16x 3/8x3/4 in.) were broken by loading at the center of a 9/16 in. span. The average strength of five or more samples is reported for each composition and grain size. The compacts were ground on two parallel surfaces only. The load was applied at an average rate of 6,800 psi per sec. Since the elongation after fracture of the alloys is very small, it was assumed that the compacts deform elastically to failure and the fracture stress was calculated by the conventional beam formula. The data for one alloy are presented in Table II as an example of the results and scattering ranges encountered. The precision of the test, as measured by the average difference between duplicates, is of the order of 15,000 psi. The results are strictly comparable only to compacts prepared and tested in the manner described and of similar chemical composition and grain size characteristics. Unnotched Charpy specimens were used for impact testing. Each point represents the average of 3 to 20 samples, the larger number being used in an attempt to determine the influence of grain size. Considerable scatter was encountered, the range from lowest to highest value often amounting to 30 pct of the impact strength. The hardness is reported as a Ra reading, using a 60 kg load with diamond brale indenter. Compositions are given in weight percent.

Jan 1, 1956

By E. C. W. Perryman

The recovery and recrystallization characteristics of superpurity aluminum have been investigated using electrical resistivity, X-ray line breadth, and hardness measurements for the former and the micrographic method for the latter. The three different properties recover at different rates and have different activation energies. The recrystallization results agree well with Avrami&apos;s theory and furthermore indicate that the perfect subgrains formed during recovery are not the nuclei for re-crystallization. WHEN a metal is plastically deformed, its physical and mechanical properties generally undergo considerable changes and by subsequent annealing these changes are partly or wholly annihilated. Thus, a recovery process can be discussed, taking this term in its general sense. In practice, however, there is reason to discriminate between two apparently different processes, one most easily followed at low temperatures, in which the properties return to an almost constant value between that of the cold worked and fully annealed material, and a second process in which the properties return to their original values before cold working and which is accompanied by the formation and growth of new grains having an orientation different from that of the matrix. In this paper the word recovery will be taken to mean the changes in some property as a function of annealing time which occur either without the appearance of new grains or under conditions such that the new re-crystallized grains are very small (= 2 microns), are very few in number, and substantially do not affect the property being measured. This definition is rather abitrary, for it will depend upon the sensitivity of the technique used for the observation of new recrystallized grains, which in the present work was about 1 to 2 microns. However, it is helpful to use the term recovery in this sense and to reserve the term recrystallization for the processes of nucle-ation and growth of new grains in the cold worked matrix. Although considerable work has been done on recovery and recrystallization, most workers have based their study on the measurement of one or perhaps two parameters. Since very small amounts of impurities have such a profound effect on the recrystallization characteristics of a pure metal, it becomes extremely difficult to correlate one piece of work with another. With this in mind, the present work on recovery and recrystallization was done on the same material. Experimental Procedure Material Used and Fabrication: The composition of the superpurity aluminum used throughout this investigation was 0.002 pct Cu, 0.003 pct Fe, 0.003 pct Si, and <0.001 pct Mg. The ingot was hot rolled to 0.250 in., annealed, and cold rolled to 0.034 in. A large number of reductions and intermediate anneals were carried out so as to produce material with a minimum of preferred orientation and maximum homogeneity. For the recovery part of the investigation, the final cold reduction was 20 and 80 pct and for the recrystallization part, 20 pct. After each pass in the cold rolling process, the material was quenched in cold water in order to keep the rolling temperature as near room temperature as possible. Annealing Procedure: For the recrystallization work, specimens 1x1 in. were cut from the 0.034 in. cold rolled sheet and a hole was drilled in each through which a wire was threaded to support it in the salt bath. The temperature of the salt bath was controlled to +2°C and the time taken for a specimen to reach temperature was approximately 5 sec. These 1 in. squares were then divided into three groups, one of which was given 5 min at 318°C and another 2 hr at 244°C. These treatments were such that recovery was almost complete and a well defined subgrain structure produced. Separate specimens of each group were annealed for different times at 301°, 318°, 355°, and 373°C, i.e., three specimens for each annealing time. The delay between finish of cold working and start of annealing was about 1 hr. For the recovery work, strips 0.062 in. thick were cut from the cold worked sheet, annealed, and then given the last cold rolling operation. This was done for each annealing temperature. By this means it was possible to minimize the delay between cold working and annealing. In general, all measurements were carried out within 1 hr of the last cold rolling operation. Annealing at low temperatures was done in an oil bath the temperature of which was maintained constant to +1°C. Electrical Resistivity Measurements: Strips 20x0.5x0.05 in. were machined and the electrical resistance measured using a Kelvin double bridge. Measurements were made in an oil bath maintained at 20rt0.1°C. The same specimen was used for the complete isothermal annealing curve.

Jan 1, 1956

By B. N. Das, P. A. Beck

THE o phases have a complex tetragonal structure with Lo/ao = 0.52 and 30 atoms per unit cell.1 A large number of such phases are now known to occur in various binary systems of the transition elements and they exhibit the following typical features: 2,3 The composition of binary o phases is variable, ranging from approximately A4B to ABI. With only a few exceptions, in the o phases the A-ele-ment comes from the V- or Cr- group of the periodic table, while the B-elements are from the Mn-, Fe-, Co-, or Ni- group. In the first long period the corresponding o phases of the V- and Cr-series have approximately the same compositions. However, as the B-element changes from Mn to Fe to Co to Ni, the mean composition shifts monotonously toward higher A-contents.2-4 For example, if the mean compositions of the various o phases with vanadium are compared with each other, the composition shift mentioned above becomes plainly visible: V 30Mn0 80 Vo.45Feo..,, Vo .,Coo. 45 and Vo.5Nio.3. Similiar composition shifts, although not the same composition values, were observed in u phases formed by second and by third long-period transition elements.3&apos;4 This behavior, very characteristic of o phases, is in rather sharp contrast to the usually quite well-behaved stoichi-ometry of the Laves phases. In the latter, the AB2 stoichiometry predominates, with A the large atom and B the small atom.= The p phase occurs in the four binary systems of Mo or W with Fe or Co. On the basis of their crystal structure determination, Arnfelt and westgren6 ascribed to the p phase in the Co-W system the ideal composition W,Co7. Since all four binary pphases have nearly the same composition, it would seem quite plausible that some definite stoichiometry such as A6B7, might be characteristic of this phase, as AB2 is of the Laves phases. On the other hand, it has been noted,7 that the phases occur at average electron concentrations near to those at which the various cr phases are found. Also, it has been pointed out by Shoemaker and associates8 that structurally the a phases and the p phases are somewhat related to each other; both of these structures may be described in terms of suitable stackings of quasi-hexagonal layers&apos;of atoms. By studying a suitably chosen ter- nary phase diagram, one might expect to be able to find out which one of the two conditions, the analogy with the o phase or the constant ratio between the number of large atoms and the number of small atoms in effect governs the behavior of the p phase. Several isothermal sections of ternary systems containing o phases have been investigated. In all cases where two binary o phases occur, these were found to be connected b a more or less straight ternary o phase field.7&apos; &apos;10 Such elongated o phase fields were also found in ternary systems in which only one of the limiting binaries is known to contain o phase. In this manner a latent o forming tendency could be detected and the virtual composition of a "binary o phase", which does not actually occur as such was approximately determined by extrapolation. The behavior of the phases, including their composition shift, is analogous to that of the classical electron compounds, as described by Hume-Rothery.11 In order to decide whether the p phase is essentially a "size compound" like the Laves phases, where a fixed stoichiometric ratio is quite generally maintained between the "large atoms" and the "small atoms", or whether the p phase is typically an "electron compound" in the same sense as ois, it was decided to investigate an isothermal section of the Mo-Mn-Co system. The Mo-Co system12 and the Mo-Mn system13 each are known to have a binary o phase. It could be therefore expected that a ternary o phase field will connect these two binary cr-phase fields. The p phase is known to occur in the Mo-Co system. If the p phase should turn out to form an elongated phase field extending deep into the ternary system, the following considerations mighto apply. The atomic radius of manganese (1.314for C.N.12) is between the va,lues for Mo (1.40Afor C.N.12) and for Co (1.26Afor C.N.12). If it is assumed that p is a "size compound", and that Mn is substituting for the smaller Co atoms in the p-structure in the ternary system, the y-phase field might be expected to extend parallel to the Mn-Co binary line. If Mn is substituting for the large Mo atoms in the p-structure, the p-phase field may be expected to extend parallel to the Mn-Mo binary line. On the other hand, if the p-phase turns out to be an "electron compound" like o, the ternary p-phase field should extend parallel to the ternary o -phase field connecting (Mo,Mn)owith (Mo, Co) a

Jan 1, 1961

By C. G. Dunn, F. W. Daniels, M. J. Bolton

IN recent investigations1. a data on relative grain boundary energies in silicon iron have been obtained. The present investigation is a continuation of this work along similar lines for the purpose of obtaining additional information on boundary energies. One aim has been to extend the data for a (110) series, which was formerly studied,&apos; to small differences in orientation, since a recent theory3,4 based on a dislocation model of grain boundaries predicts a E. ? (A-ln ? )* form of energy curve for small differences in orientation. Another aim has been to provide data for a (100) series—all grains having (100) planes parallel with the surface of sheet speci-mens—and to compare the results with the predicted form of energy curve. Finally, information on the nature of approach to equilibrium conditions was to be obtained through observations on the movements of grain boundaries. Recently published papers2,3,5 have treated the mathematical problem of expressing equilibrium conditions for grain boundaries for the general case when boundary energy depends upon boundary orientation. The equilibrium equations, which relate equilibrium angles and grain boundary -free energies, contain additional terms that express the variation of energy with boundary rotation. It has been necessary in the present investigation, however, to neglect these additional terms since no data for their evaluation were available. Dropping the additional terms leads to the following approximate equations which were used: E12/sin ?3 = E18/sin?2 =E28/sin?1 or those of the form: E28 + E13 cos ?3 + E12 cos ?2 = 0 Experimental Procedure Except for sample F1, all specimens were made from two lots of silicon iron called C and L respectively. The compositions of these are listed in table I. In the preparation of 12 three-grain specimens for the present investigation, a controlled grain growth technique, which has been described previously,&apos; was used. After preparation, the specimens were notched at the boundaries to shorten them as a means of providing more rapid approach to equilibrium in the anneals. Initial grain boundary angles were determined from micrographs taken at X500. Seven anneals, totaling about two days at 1300°C and two to four days at 1400°C, were run in an atmosphere of pure dry argon as described in a previous paper.&apos; Boundary changes generally could be followed without metallographic surface preparation, because thermal etching occurred during the anneals. These observations indicated angle changes of as much as 35" in some instances, with the major changes occurring during the first anneal. Annealing was discontinued when the angles reached stationary values. Fig. 1 gives a schematic diagram for purposes of defining crystallographic and boundary directions for three grains with common plane parallel with the sheet. Differences in orientations (expressed by A) are the angles between [00l] directions. They can be calculated with the aid of the ?&apos;s. The grain boundary angles can be calculated from the w&apos;S. Results Results are given in table 11. Types of crystal-lographic planes refer to those parallel with the sheet. Orientations are given in terms of [00l] direc-tions as shown in fig. 1. Except for grain 3 of specimen H6, which was unintentionally tilted 7" out of a (100) plane, all grains generally were within 1" or 2" of the plane specified. The directions of boundaries were measured generally to within 1" on both upper and lower surfaces, and the average direc- tions were determined for use in calculating the grain boundary angles. Variations in grain boundary directions refer to deviations from average directions. Boundaries near the junction point for all specimens generally were very close to perpendicu-

Jan 1, 1951

By K. T. Aust

The relative interfacial energies of symmetrical tilt boundaries in silver of greater than 99.999 pct purity were measured as a function of orientation difference 0 between 9° and 36° about <001>. The results are in good agreement with the dislocation model of the grain boundary. The energy vs H curve may be represented by the Shockley and Read equation in the form Eoe (0.55—In 8). READ&apos; has indicated that an ideal experimental method of testing the predictions of the dislocation theory of the grain boundary would be to measure the interfacial energies of symmetrical tilt boundaries between face-centered-cubic grains that have a common <001> axis, as a function of orientation difference 0. The misfit H should be defined by a rotation of each grain through an angle of H/2 away from the boundary. Such boundaries might be expected, from geometrical considerations, to be made up of a series of edge dislocations, at least for small values of 0. Energy vs H relationships for tin&apos; and lead:&apos; were previously obtained for an asymmetrical tilt boundary separating two grains in which generally only one grain was rotated about a <001> specimen axis through an angle of H away from the boundary, the other grain remaining fixed. It is possible, however, that the boundary atoms in tin and lead may have attained a symmetrical position, in relation to the orientations of the grains on either side of the boundary, during equilibrium annealing. The two sets of measurements on silicon ferrite&apos; were somewhat better suited for comparison with theory, since the boundaries were symmetrical tilt boundaries in which the axis of relative rotation was <110> in the first series and <l00> in the second; but this alloy has a body-centered-cubic structure. Although the grain boundaries in silver" were symmetrically tilted, the axis of relative rotation was not a simple crystallographic direction, and it varied from boundary to boundary. Although the above measurements were in good agreement with the Shockley and Read equation,"&apos;: it appeared desirable to carry out experiments under the ideal conditions specified by Read.&apos; Consequently, the relative energies of symmetrical tilt boundaries in silver between grains that have a common <001> axis were measured. The technique of equilibrating grain boundaries in oriented tricrystals was used rather than the less satisfactory thermal groove method previously employed for silver bicrystals." Experimental Details and Observations The solidification and seeding techniques, described previouslyh for growing tricrystals of controlled orientations, were used to prepare tricrystal specimens from silver of greater than 99.999 pct purity. The silver was obtained from American Platinum Works, Newark, N. J., in the form of poly crystalline rods 10 cm long and 7 mm in diam. These rods were then cold worked by rolling or drawing them into suitably shaped blanks. Single crystal seeds and tricrystals were grown in a high purity graphite boat by means of a movable furnace with globar heating elements. The graphite boat was enclosed in a Vycor tube, which was first evacuated to about l00/u Hg and then filled with a static argon atmosphere. The maximum temperature outside the Vycor tube was 1250°C. A typical tricrystal specimen of silver is shown in Fig. 1. Grains B and C were grown from seed crystals with a <001> specimen axis or longitudinal direction parallel to the direction of growth and with another <001> direction perpendicular to the surface. Each of the two seed crystals was rotated 18" about the <001> specimen axis but in opposite directions away from the boundary. A symmetrical tilt boundary, therefore, separated grains B and C with an orientation difference 8 of 36" about <001>. Grain A in Fig. 1 was grown from the middle seed with a <110> direction parallel to the specimen axis and with a <001> direction inclined at 45&apos; to the surface of the specimen. The interfaces sepa-

Jan 1, 1957

By H. C. Theuerer

EVEN the highest purity silicon available for semiconductor use contains significant amounts of donors and acceptors, usually aluminum, phosphorus, and boron. Aluminum and phosphorus can be removed from silicon by adaptations of the zone refining techniques&apos; widely used with germanium. Removal of boron, however, has been a difficult problem. The approximate distribution coefficient for boron in silicon is 0.8, so that while zone refining is possible, it is not very effective in any reasonable number of passes. It has been found, however, that boron can be effectively removed from silicon by treatment of a liquid zone with hydrogen and water vapor. Starting with 40 ohm-cm, n-type silicon, use of zone refining coupled with hydrogen

Jan 1, 1957

By H. C. Fiedler

It was recently shown with 3.3 pct Si-Fe containing 0.026 pct S and 0.06 pct Mn that the extent of secondary recrystallization to a cube-on-edge texture is determined by the cooling rate from the solution temperature of the manganese sulfide inclusions.1 With a rapid cooling rate, many small inclusions rather than a few large ones are formed, which leads to increased restraint to normal grain growth and more complete secondary recrystalliza-tion. Strip samples 12 mils thick, rolled from 1-in.-thick slabs that were cooled at 130°C per min

Jan 1, 1964

By B. D. Cullity

A distribution of residual stress after plastic elongation is proposed, in which the bulk of the material is strained in compression and a very small portion in tension, This distribution is shown to account both for the X-ray observations and for the effect of plastic straining on magnetic losses in silicon steel. The regions left in compression are tentatively identified with the interiors of the sub-grains revealed by the electron microscope. THIS paper is concerned with the general problem of the nature of the residual stress which is produced in metals by plastic elongation. A particular stress distribution will be suggested which accounts for the main X-ray diffraction observations which have been made. It will also be shown that certain magnetic measurements made on silicon steel can be understood in terms of this stress distribution. X-RAY OBSERVATIONS Uniform straining of a crystal lattice (macro-strain) causes a diffracted X-ray beam to shift its position, and nonuniform straining (microstrain) causes line broadening. If a bar of metal is plastically elongated in the longitudinal x direction and then unloaded, diffracted X-ray lines are observed to be both shifted and broadened.&apos;-= Although the observed line shift indicates the presence of macro-strain, experiments have shown that no macrostrain, in the usual engineering sense of the term, exists.5"7 For example, removal of a layer from one surface of a stretched and unloaded bar does not produce curvature in the remainder of the bar 5&apos;7 Fig. 1 shows the variation of lattice strain in the x direction, as determined from X-ray line shifts, with the applied stress in the same direction. The curve ABC is the normal stress-strain curve of the material, AB being the elastic portion and BC the plastic. In the elastic region AB, the strain measured by X-rays, called the lattice strain, and the strain measured mechanically are both proportional to the applied stress, and both return to zero when the applied stress is removed. Above the elastic limit the lattice strain would be expected to continue to increase along the line BD. Actually, it increases less rapidly with respect to stress, or even decreases, as shown by BE. If the applied stress is then decreased, the lattice strain decreases along EF, which is parallel to AB. As a result, there is a compressive residual lattice strain FA after unloading. STRESS DISTRIBUTION. Since a stretched and unloaded bar does not contain macrostress, it follows that the observed line shift must be due to a special distribution of mi-crostress. Such a distribution is shown in Fig. 2, which shows the variation of the stress u, across a stretched and unloaded bar. The material is assumed to consist of two kinds of regions: regions C, stressed more or less uniformly in compression, comprising the bulk of the volume of the material and responsible for the observed diffrac-

Jan 1, 1963

By R. C. Nelson, T. L. Weaver, A. I. Michals

This paper describes the design and performance of an apparatus for making continuous nondestructive resistance measurements throughout a spool of fine wire. Highly reproducible results on clean and graphite coated tungsten and rnolybdenum wires from 1 to 9.5 mil are presented. A linear relation between resistance and wire weight (per standard length) was obtained on clean wires, but only on those coated wires with very uniform coatings. Results indicating a correlation between tensile strength, hardness, and resistivity are reported. THE increasing demand for greater uniformity in fine tungsten and molybdenum wires destined for use as mandrels, grids, and coils in radio tubes and as filaments in light bulbs has rendered inadequate the standard (sampling) approach to the control of wire diameter and other physical properties. This ap-

Jan 1, 1961

By F. V. Lenel

Resistance sintering under pressure is a method of hot pressing in which a powder compact is subjected to pressure and simultaneously heated by passing a low voltage high amperage current through it. Equipment for this process is described. Its basic characteristics such as resistance requirements for powders and compacts, temperature distribution in compacts, and gas reactions during resistance sintering are discussed. Examples of the sintering process in compacts made of a single metal or an alloy powder and in compacts made of mixtures of powders are presented. Potential commercial applications of the process are evaluated. THE usual sequence of operations in commercial powder metallurgy is to compact metal powders in a die at room temperature and sinter the compact subsequently without applying pressure while the compact is in the sintering furnaces. In hot pressing, on the other hand, the compacting and the sintering are combined. The loose powder, or in many cases a cold formed compact, is inserted into the die which is held at the hot pressing temperature, the compact is left in the die until it attains its temperature, and then pressure is applied and maintained for a given length of time. The die may be heated by surrounding it with a suitable furnace, by high frequency induction heating, or by passing current through the die. In hot pressing, compacts of high density and good mechanical properties can be produced in a relatively short time. One of the principal difficulties in hot pressing is the lack of suitable die materials which will have adequate strength at the hot pressing temperature. This difficulty can be overcome at least partially by heating only the material to be hot pressed without heating the die directly. This can be done by passing a low voltage high amperage current through the material and simultaneously subjecting it to pressure. Either loose powders or compacts can be hot pressed by this method in which the desired temperature is produced by the power dissipated in the metal powder. This method of hot pressing has been termed "electrical resistance sintering under pressure." The most significant differences between this operation and conventional hot pressing are: 1—The sintering times are very short, usually a fraction of a second and at most a few seconds. 2—The powder and die are initially cold. 3—Heat is generated within the powder itself and not conducted in from the die. 4— The pressure used is high. 5—Cooling following sintering is rapid, amounting to a quench. Resistance sintering of metal powders under pressure has been suggested repeatedly. In 1933, G. F. Taylor&apos; proposed an apparatus which consisted of an insulating tube made of glass, or a ceramic filled with the powder to be pressed, and plungers above and below the powder. The powder was to be heated by passing an electric current through it and pressure was then applied. The apparatus was intended principally for hot pressing cemented carbides. Although the principle of resistance sintering under pressure is clearly shown in this patent, few details are given. A sintering period of a second or a fraction of a second, which is terminated by the operation of an inertia switch, is mentioned but no values for current density are mentioned. Low pressures, such as atmospheric pressure or a somewhat higher pressure exerted through a lever, are suggested. W. D. Jones&apos; discussed electrical resistance sintering under pressure and proposed using resistance welding apparatus for this purpose. In a patent issued in 1944, G. D. Cremera described a method of electrical resistance sintering under pressure using resistance welding apparatus which was to be applied mostly to nonferrous metals such as copper, brass, bronze, and aluminum. Current densities of 400,000 amp per sq in., sintering times of 1 and 2 cycles of 60 cycle current, and pressures of 5 to 10 tsi are proposed. Cremer suggested using an

Jan 1, 1956

By R. J. Block, G. H. Kehl

IN order to investigate the possibility of a spontaneous low-temperature transformation, resistivity measurements were made on a sample of eutectoid beryllium- copper. A cast specimen of 5.965 pct Be, 94.035 pct Cu was homogenized at 650°C for 22 hr, furnace cooled to 550°C, and held for 2 hr to allow the 0 - a ß-a+? reaction to proceed. In an attempt to refine the ß grain size, the specimen was then reheated to 620°C, held

Jan 1, 1960

By J. P. Hirth, C. S. Hartley

A simple graphical technique is presented for rapidly determining the ratio of resolved shear stress on slip systems in single crystals to the applied stress (Schmid factor) for various simple states of stress. Master plots are presented which, when used in conjunction with an appropriate stereo-graphic projection, allow one to determine the Schmid factor for all slip systems in a crystal of given orientation. It is shown that one such plot suffices for simple tension or compression, flex-ural bending, and biaxial compression, while a combination of two different plots must be used for torsion and simple shear. STUDIES of the deformation behavior of single crystals are most valuable when the applied stresses are resolved onto the various slip systems of the crystal. A careful study of the available slip systems and proper selection of the state of stress used and the specimen orientation can then yield quantitative information about the probability of specific dislocation reactions, the strength of barriers to plastic flow, and the mechanisms of yielding and flow in general. It is the purpose of this work to analyze some common states of stress used in deformation studies and to present a simplified way of determining for these cases the ratio of the resolved shear stress on the slip systems to the applied stress (Schmid factor). I) CALCULATIONS We first define two orthogonal coordinate systems: one based on the specimen geometry (a right circular cylinder of radius, R, is considered here) and one based on the particular slip system of interest. The unit vectors and angles specifying the two coordinate systems and the relationship between them are listed in Table I. The relationships among the various angles and unit vectors are shown on a stereographic projection in Fig. 1. The transformation matrix between the (XI X2 X3) and (x&apos;1 x&apos;2 x&apos;3) system is x1 x2 x3 X&apos;1 a11 al2 a13 x&apos;2 a21 a22 a23 x&apos;9 a31 a32 a33 where in this case the direction cosines aij are given by a11 a12 a13 aij = a21 a22 a23 a31 a32 a33 sin 0 cos F cos 0 sin F cos 9 = -cos 0 cos F sin 0 sin F sin 6 [1] 0 -sin F cos (p In terms of Eq. [I.], the stresses sij, referred to the slip system, are determined from oij, referred to the specimen axes, by1,2

Jan 1, 1965

By L. F. Mondolfo

An aluminum-copper 4 pct Cu alloy aged at room temperature for times increasing up to 78,000 hr was annealed at 170°C and the hardness and electrolytic potential determined during retrogression and subsequent aging. It was found that there is a change of behavior with increasing time of aging at room temperature which indicates that, given sufficient time, retrogression disappears and the room-temperature aging tends to progress directly into the high-temperature aging. WHEN an age-hardenable alloy is aged at low temperature after proper quench, changes of properties and structure take place. If this material is then heated to a temperature higher than the previous one, but still well below the solution-treatment temperature, the properties and structure changes produced by the low-temperature aging disappear and the material apparently reverts to the as-quenched condition, ready to undergo aging from the start. This phenomenon is termed reversion or retrogression. First discovered by Cayler3l it has been extensively investigated, as shown by the number of publications listed in the bibliography. From all the information available the following facts emerge: 1) All aeg hardenable alloys can be retrogressed.9 13, 19) 24, 33, 41, 42, 44, 47, 53, 54, 61, 63, 64, 66, 73, 78 2) All the properties changes that take place during aging at low temperature can be retrogressed to a smaller or larger extent.4,5,7,12,19,32,49,50,57,58,60,67,75,76 67, 75, 76 3) Retrogression requires that the temperature be well above the preliminary aging temperature. If the difference between the two temperatures is small, Little or no retrogression takes place.7,20,32,33,41,49 57. 65 4) The larger the difference between the preliminary aging and the retrogression temperature, the faster and more complete is the retrogression.20, 33, 41, 48, 65, 67 5) Retrogression can be produced several times in the same alloy.23, 35,41,57,59 6) The amount of retrogression that can be obtained depends on the aging temperature. Alloys aged at the lower temperatures can be retrogressed the most. The higher the preliminary aging temperature the less retrogression can be produced.20,25,33,37,44,49,54,58 7) Appreciable retrogression after aging at elevated temperatures is possible only if the preliminary aging has lasted a short time. After a certain time of aging at high temerature retrogression does not take place any more,:5,6,9,10,11,21,40,58 8) During retrogression the Guinier-Preston zones redissolve and disappear. The other precipitate

Jan 1, 1960

By M. S. Hunter, D. L. Robinson

An extremely fine subgrain structure found in aluminum and aluminum alloys is shown and a method for revealing this structure is described. The appearance and some of the characteristics of this structure are described and the possible significance of subgrain structure in terms of chemical, electrochemical, and metallurgical processes is considered. GRAINS and grain boundaries, which constitute the principal manifestations of the crystalline aggregates known as metals, play such an important part in determining the characteristics and properties of metals and alloys that their nature and behavior have long been of much concern to the met-allographer. Many investigators have speculated on the possible existence of a finer structure within the usual grain structure and, through X-ray diffraction and metallographic techniques, have revealed evidence that such finer structures exist. Among these structures are the mosaic blocks and domains described by Burgers1 and others in their contributions on crystalline structure and the dislocation theory, the small units associated with polygoniza-tion described by Cahn,2 and the intragranular blocks revealed more recently by Lacombe and Beaujard.3 his paper describes some novel methods for clearly revealing a very fine granular substructure within the usual grains of pure aluminum and aluminum alloys. It also compares the characteristics and behavior of this subgrain structure with those of the ordinary grain structure and gives some examples of the manner in which this substructure may influence the characteristics of aluminum alloys. Metallographic investigations of aluminum and its alloys have dealt extensively with the functions and behavior of grains and grain boundaries and have evolved a definite concept of the relation between grain structure, orientation and physical, mechanical, chemical, and electrochemical behavior. During the examination of etched samples, a roughening or mottling of the body of certain grains has occasionally been observed. Such roughening obviously represented differential attack by the etching solution, but its true significance was not at first realized. It is now known that this roughening probably rep- resented a subgrain structure, although the particular etching treatments used were not capable of revealing this subgrain structure clearly. Also, in practically all cases, the subgrains were apparently far too small to be resolved by the light microscope. Recently, a method has been developed for revealing clearly the subgrain structure of most aluminum alloys. This method is somewhat unique in that it eliminates much of the usual tedious mechanical polishing and the attendant danger of a surface layer of flowed metal and at the same time is simple, rapid, and effective. It involves the use of the Alcoa R5 Bright Dip, a patented chemical polishing treatment licensed by Aluminum Co. of America. This treatment produces a bright, highly polished surface at least the equal of any mechanical polish and also etches the subgrain boundaries as well as the ordinary grain boundaries to reveal both the grain and subgrain structure simultaneously. Metallographic specimens to be examined are taken through the customary grinding and polishing operations used for aluminum alloys.&apos; The usual care required in the final polishing operation to prevent a flowed surface layer and to obtain a high polish is not necessary, however, because any flowed layer is eliminated and a high polish is produced by the final immersion in the Alcoa R5 Bright Dip. Depending on alloy type, this dip takes from a few seconds to about 3 min, after which the sample is rinsed well, blown dry, and is ready for examination. The substructure can be revealed by some of the usual metallographic methods such as electropolish-ing or mechanical polishing and etching but no method has been found which is the equal of the new chemical polishing treatment. Mechanical polishing followed by the usual metallographic etching is not entirely satisfactory for revealing this substructure, probably because of the flowed surface layer resulting from the mechanical polish. If the usual etching methods are prolonged sufficiently to remove this layer, the specimen surface becomes quite rough and the substructure is not defined clearly.

Jan 1, 1954

By H. Herman, M. E. Fine

Kinetics of reversion and reformation of GP I were studied resistometrically in Al-1.7 at. pct Cu. The reversion process is over in roughly 1/2 minute at 205 "C irrespective of the amount of primary aging. After reversion the occurrence of an incubation time before reaging begins has been substantiated. The reaging kinetics is drastically accelerated by plastic deformation to the specimen. An incubation time is observed only if the specimen is aged before reversion. The incubation time and the effect of plastic deformation indicate that nucleation of GP I is heterogeneous. Simple clusters of copper atoms apparently do not act as nuclei for GP I. AFTER quenching aluminum-rich copper from the solid solution range, Guinier-Preston zones of the first kind, GP I, form very rapidly at room temperature. The rate, largely controlled by the concentration of vacancies, is initially most rapid1 (that is, at the time of the first measurement: 1/2 min) and decreases with time. The nucleation is thought to be athermal. If after aging for several days the GP I is dissolved by reversion at 205°C, according to measurement of Young&apos;s modulus an incubation period is observed before GP I begins to form on subsequent aging.2 Yet if the reversion is carried out immediately after quenching, both resistivity3 and modulus changes2 show no incubation effect. The zones which form after reversion have the same structure as those which form after the quench.4 Because of entropy considerations and also the short diffusion time, the solid solution after reversion, 2 min at 205°C, is probably more highly clustered than at the original solution treating temperature, 520" to 550°C. It appears most reasonable to associate with nucleation the incubation time observed on reaging after reversion. A simple cluster of copper atoms, many of which are presumed to be present after reversion, is then not a sufficient nucleus for GP I; a GP I nucleus must contain something in addition to a cluster of copper atoms. The purpose of the present note is to give some additional experimental information concerning the incubation time and rates of reaging after reversion. The existence of the incubation time has been verified by measurement of another property, the electrical resistivity. Acceleration of reaging after reversion by plastic deformation has also been investigated. In acl.dition, the kinetics of the reversion process itself was studied. EXPERIMENTAL Electrical resistance was measured by the poten-tiometric four probe method. The 1.7 at. pct Cu alloy was furnished by the Aluminum Co. of America in the form of 1/2 in. rod. The major impurities reported by Alcoa were Fe (0.002 wt pct), Si (0.003 wt pct), and Mg (0.001 wt pct). Specimens for measuremenl of resistance were prepared by rolling to 0.010 in., cutting 2 by 0.2 in. pieces, rolling the middle pclrtions of these to 0.005 in., and splitting the 0.010 in. sections up to the reduced central section to form current and potential leads. Aluminum extension wires insulated with ceramic tubes were spot welded to the leads. The specimen was supported by the lead wires. The whole specimen assembly was annealed at 500" C in an air furnace for more than 12 hr and then aged at room temperature. This was done to assure quick and complete resolution during subsequent solution treatments. These were carried out in Houghton&apos;s "430 Temper Salt" at 520&apos;C for 1 hr. Unless otherwise specified, quenching was accomplished by quickly transferring the specimen from a salt pot to 25°C water. Aging was carried out in a 3 liter dewar of distilled water, rotated and stirred. The temperature was controlled to +0.01°C with a thermomercurial regulator in conjunction with a transistorized relay

Jan 1, 1962

By E. P. Abrahamson II

The effect of transitiorz element bitzary solid solution additions upon the recrystallization temperature of columbium has been investigated. The elements Mn, Fe, Co, Ni, W, Re, and 0s OWY the yecystallization tempel-aturye, while Ti, V, CY, zr, Mo, Ru, Rh, Pd, Hf, Ta, W, Ir, and Pt mise it. A correlation is kloted between the rate of chatzge of recyystallization tewaperature with atomic hercent solute and the free atom electron configuration of the solute element. The work of Abrahamson and Grant1 has indicated a correlation between the free atom ground-state electron configuration and the change in brittle-ductile transition temperature per atomic percent solute in chromium base alloys. A similar correlation was observed for the change in the recrystallization temperature of iron base alloys by Abrahamson and Blakeney and Abrahamson. It was also observed that the limit of rapid change in recrystallization temperature also Correlated with the electronic configuration of the free solute atom. A further study by Abrahamson4 established the generality of the phenomenon by yielding similar results for vanadium base dilute alloys. It has been inferred that a peri- odicity might be expected with changes in the free atom electron configuration of the solvent element. This study is the third set of transition base metal systems to be studied. It is the object of this and further studies on transitional metal systems to detect any systematic variations in the observed correlation which might contribute to the understanding of the electron interactions which are evidently exhibiting themselves. PROCEDURE All alloys were made using 99.9 pct Cb with 0.030 Ta, 0.016 0, 0.0025 H, 0.003 Mo, 0.021 Fe, 0.005 C, and 0.002 N. The solute elements were 99.9 pct pure. According to the published binary phase diagrams5 and metallographic examinations at X750, all additions were in solid solution. The alloys were arc melted and remelted 6 times in the form of cubic 400-g buttons under an argon atmosphere. They were then hot forged at 1200oC to 0.6-in. diameter, annealed for 3 hr at 1200o under argon, and furnace cooled. The specimens were then machined to 0.400 -in. diameter. Grain size was checked and found to remain essentially constant at 150 i 30 grains per sq mm. The specimens were then cold swaged to 0.187-in. diameter, yielding 46 i 1 pct cold work. All alloys were chemically analyzed for the major solute. Analyses of random samples indicated that the impurity content remained at the values of the starting material. Tungsten contamination was held to 0.007 pet.

Jan 1, 1962

By E. P. Abrahamson II

The effect of transition element binary solid-solution additions upon the recrystallization temperature of vanadium has been investigated. Cr, Fe, Co, Ni, Mo, Ru, Rh, Os, and IY lower the recrystallization temperature, while Ti, Mn, Zr, Cb, Pd, Hf, Ta, W, Re, and Pt raise it. The majority of elements have their greatest effect in less than 0.15 at. pet. Both the rate of change of recrystallization temperature with atomic percent solute and the limit of initial linearity are found to Correlate with the free atom grozdnd state outer electron configuration of the sollte element. THE work of Abrahamson and Grant1 and Abraham-son and Blakeney2 has shown that the solute&apos;s elec- tron configuration appears to be a prime determinant of both brittle-to-ductile transition and recrystallization temperature in dilute binary alloys. It has also been shown by Abrahamson3 that the limit of linearity, i.e., the limit of initial linear change of recrystallization temperature with atomic percent solute, is also a function of the electron configuration of the solute in iron base alloys. Because of the systematic nature of the solute electron configuration correlation, it is to be expected that some systematic variation might be observed upon changing the solvent. Thus, this study of recrystallization in vanadium base alloys is the first of a series aimed at defining the role played by the electron configuration of solute in determining the recrystallization characteristics of dilute transitional alloys. PROCEDURE All alloys were made using 99.8 pct V containing 0.011 C, 0.024 N, 0.08 0, 0.006 H, 0.035 Ta, and

Jan 1, 1962

By E. P. Abrahamson II

The effect of transition elements which form binary solid solution upon the recrystallization temperature of zirconium has been investigated. All additions raised the recrystallization temperature. A correlation is obtained between the logarithm of the rate of change of recrystallization temperature with atomic percent solute and the free atom ground state electron configuration of the solute element. ThE work of Abrahamson, et al., on dilute binary solid-solution alloys indicated a correlation between the free-atom ground state electron configuration of the solute and either the brittle-ductile transition or recrystallization temperature. These studies were carried out on bcc base materials. The implication is that the outer s and d electrons of the solute are the prime determinant of the absolute rate of change of recrystallization or transition temperature. Furthermore, the limit of linearity has been shown to be a function of solute electron configuration for recrystallization in iron and vanadium. To date no Complete systematic recrystallization study of dilute binary zirconium base alloys has been made. It is the purpose of this study to note whether the change in solvent structure from bcc to hcp will influence the correlation. It was also desired to learn more of the role of the electron configuration of the solvent on recrystallization temperature. PROCEDURE All alloys were made using 99.87 pct Zr with 0.01 Cr, 0.04 Fe, 0.006 Hf, 0.003 Mg, 0.003 Mn, 0.003 N, and 0.080 0 (132 BHN). The solute elements were 99.9 pct pure. According to the published binary phase diagrams6 and metallographic examinations at X750, all alloys used were solid solutions. The alloys were arc melted and remelted six times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot pressed at 950°C to 0.450 in., upset pressed to 0.350 in., and annealed at 800°C for 1 hr. The specimens were then Blanchard ground to 0.250 in., removing 0.050 in. from each side. The grain size of the material at this stage was found to be 8000 100 grains per sq mm. The specimens were then cold rolled to 0.130 in. and cold pressed to 0.125 in., yielding 50 1 pct cold work. All alloys were then chemically analyzed for the principal addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The rolled sheet was cut into 6.75 by 0.25-in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was 250o to 900°C over the 6-in. length, recorded continuously by six thermocouples resting on each specimen. Control was 3oC, accomplished at the hot end. The recrystallization temperature was determined metallographically using polarized light. The criterion chosen was the point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be 3°C. RESULTS Three different pure zirconium specimens were tested, and the recrystallization temperature was

Jan 1, 1962

By Donald Warren, J. F. Libsch

HIS investigation originated as a result of a pre-vious experimental study&apos; of the magnetic properties of Fe-Co alloys fabricated by the powder metallurgy technique. Densities of powder compacts prepared for the magnetics investigation varied from 7.45 to 7.70 g per cu cm or from 93 to 95 pct of the experimental value of 8.08 g per cu cm for a fused alloy of the same composition.&apos; While this range of density is considered sufficiently high for most applications, the highest possible density is to be desired for maximum magnetic properties. By applying a technique similar to the one described above to a pure electrolytic iron powder, Rostoker³ was able to achieve a density of 7.895 g per cu cm, which is the highest density ever reported for sintered iron. While Rostoker&apos;s work involved the sintering of an elemental powder rather than a mixture, it was believed that higher densities should also have been obtained for alloys using the above technique because of the recoining operation and the high sintering temperature. Consequently, it was decided to investigate the various factors affecting the density of this alloy with the idea that such a study might lead to higher densities and, as a result, powder alloys having magnetic properties identical with those of the fused alloys. It was believed that the principal reason that near-theoretical densities for the powdered alloy were not obtained was the interference of gases with the normal sintering mechanism. When present during the sintering operation, gases can exert several harmful effects: they can remain on the particle surface and interfere with surface diffusion and plastic flow; they can be released and, under certain conditions, expand the void spaces through gas pressure; or they can remain trapped in the pores and exert a hydrostatic pressure that retards elimination of the pores. Jones,4 Rhines,5 Goetzel," and others have given the effect of gases in the sintering of powder compacts an extensive treatment. Among the more important sources of gases in the sintering process are dissolved gases, adsorbed gases, air entrapped during pressing, and gaseous products of chemical reactions. During sintering adsorbed gases are partly released at a relatively low temperature, while those gases entrapped during pressing cannot escape until their pressure is increased sufficiently through increasing temperature to expand the interpartjcle openings. The remaining adsorbed gases, gaseous reduction products, and dissolved gases produce a similar effect at the higher temperatures. If, in the sintering process, gas evolution occurs after the interpore channels have been sealed, an exaggerated expansion of the void spaces results. This is particularly true if the temperature is high enough for extensive plastic flow. In his fabrication of powder bars from tantalum, Balke7 had to consider the effect of adsorbed hydrogen and provide for its escape during sintering by limiting the compacting pressure to a maximum of 50 tons per sq in. The effect of gases entrapped during pressing was first noted by Trzebiatowski8 when he found that gold and silver powders decrease in density with increasing sintering temperature if pressed at 200 tsi, while they exhibit the usual increase when pressed at 40 tsi. Recent investigators9-11 have also noted that entrapped gases have an effect on the expansion of copper compacts during sintering. Proper provision for the escape of gaseous products of reduction must be made in order to avoid deleterious effects. Myers" states that in the sintering of electrolytic tantalum powder, the temperature was gradually raised to 2600°F with a pause at 2000°F to permit reduction of the oxides. Experimental Details For the present study, 50 pct Co-50 pct Fe compacts in the form of circular disks 1½ in. in diam and 0.15 in. thick were fabricated by the pressing and sintering of a mixture of the elemental powders. It was decided to follow the sintering process by means of liquid permeability measurements, because it was thought that such measurements might serve as a measure of relative pore sizes, as well as a possible indication of the point at which most of the interpore channels become sealed. However, since the permeability as measured by the flow of a liquid, such as ethylene glycol, does not give an absolute indication of the point where the pores have become isolated, a method for determining the percentage of pores connected to the surface was set up. As an additional cross check on the permeability measurements, metallographic methods were used to study the relative pore size. Finally, the property of ultimate interest, the density, was measured. Raw Materials: The powders used consisted of an annealed, 99.9 pct pure, —150 mesh grade of electrolytic iron powder, and a 98 pct pure, —200 mesh grade of reduced and comminuted cobalt powder. The cobalt powder was not further processed either by hydrogen reduction or annealing. The screen analyses for the iron and cobalt powders are given in Table I, while the chemical analyses for each type of powder are listed in Table 11. Table 111 gives the hydrogen loss measurements for the powders according to the M.P.A. Standard Method and for a higher temperature as well. Preparation of Compacts: Equal amounts of the elemental powders were mixed by rotation for 1 hr and then pressed into compacts approximately 0.15

Jan 1, 1952