By B. Nowak

For sources with an iron-to-vanadium ratio of far above 1, it is proposed to leach in acid and to oxidize under autoclave conditions. During this oxidation process, it is experimentally shown that divalent iron contained in this solution will be oxidized to trivalent iron, whereas free acid contained will be consumed by this reaction. In case no acid is present or already fully consumed, a solid consisting of ferric compounds and an iron-vanadium-co-precipitate will form that can be filtered from the solution. If choosing the right reaction conditions, this filter cake has an iron-to-vanadium ratio of close to 1, whereas the liquid remainder is almost vanadium free. This precipitate, identified as FeVO4, 1.1 H2O, can be processed by conventional technologies such as caustic leaching, or probably salt roasting or reduction with aluminum, yielding common marketable products.

By Robert Hanson, Mayur K. Patel

"Pneumatic conveying pipelines are used throughout a variety of industries, from food processing/packing to power generation plants, as an efficient means of transporting materials between storage and processing points. In general, different phases of pneumatic conveying exist when material is conveyed from point A to point B in a pipeline. This depends on the operating pressure and the material conveyed. Lean phase conveying exists when pipelines are operated at high airflow rates, relatively low pressures, inducing sufficient turbulence for particles to become entrained in the air stream. Thus, particles are conveyed along the pipelines at velocities in the range of IS-2Sm/s. Generally, the initial capital costs for lean phase system is low, however the running costs are high. The opposite is true for dense phase, high-pressure systems. In considering either conveying system, it is important that the rate of erosion of the pipeline be considered when designing such a system, since it is the rate of erosion that dictates the lifetime of components. In general, the high level of erosion occurs for lean phase flows, where high impact velocity contribute substantially to the rate of erosion as well as other processes such as particle breaking, if the particles are friable. This would lead to poor quality of material, not normally desirable. On a positive note, the process of erosion is used in other applications, which benefits from this process, e.g. abrasive guns.The failure, by puncture, of pneumatic conveyor bends in industry causes several major problems. Two of these are: (a) escape of the conveyed product causing health and dust hazard and (b) repairing and cleaning up after punctures necessitates shutting down conveyors, which will affect the operation ofthe plant, thus reducing profitability.The paper reports on modelling strategy used in the development of a modelling framework and the initial validation phases of the models incorporated within. The modelling framework encompasses Computational Fluid Dynamics (CFD) related engineering tools, based on Eulerian (gas) and Lagrangian (particle) approaches, to represent the two distinct conveyed phases, to represent the erosion process which is used to ascertain the lifetime of conveyor bends."

Jan 1, 2001

By Krzyszof Borowiec

With the aim of determining the thermodynamic conditions for sulfation of impurity elements, in particular magnesium, in titaniferous slags the equilibrium gas composition for the sulfation reaction: MO + so2 + 1/2 02 = MS04 has been studied by an EMF technique with a solid zro2 + Cao electrolyte. Here M denotes the impurity elements: Mg, Ca and Mn, and the following _oxide systems have been studied: Ti02-MgO-Fe2 o 3 , Ti02-MnO-Mn2 o 3 , and Ti02 -CaO-Si02 , all in the . temperature range 700-1000ºc. Reproducible EMF values were obtained by adding small amounts of -Na2so4 to the oxide-sulfate mixture. From the observed results the Gibbs energy of formation of the phases Mg 2Ti04 , MgTi03 , MgTi 2o 5 , MnTi03 , CaTi03 , and CaTiSio5 , as well as the activity of MgTi05 in the solid solution with Fe2Ti05 have been calculated. The results show that, from a thermodynamic viewpoint, sulfation of these impurities in titaniferous stags i:s favorable- at around and below 800ºC.

Jan 1, 1985

By Feng Liu

A thermal upgrading process by which nickel value can be concentrated in a ferronickel alloy is a possible alternative to treat Sudbury pyrrhotite (Po) tailings with nickel content of 0.5–1.5 wt%. The basis of this process is precipitation of Ni from Po at high temperature once Fe/S ratio in the iron-deficient Po is shifted towards stoichiometric or near stoichiometric FeS (troilite) either by the addition of iron and/or the removal of sulfur. For the iron addition route, the reaction between elemental iron and nickeliferous pyrrhotite to produce ferronickel alloy and Ni-depleted iron sulfide phase plays a critical rule. In this paper, the formation mechanism of ferronickel alloy was investigated using the diffusion couple technique to better understand the nickel diffusion behavior in the iron and sulfide phases.

By W. D. Riley

Engineered Scavenger Compounds (ESCs), developed by the U. S. Bureau of Mines I are a novel class of compounds that can selectively recover a desired element from 'a solid or molten alloy. Lithium titanate (Li2Tip7 or Li20' 3TiO.) is being used as an ESC to recover lithium (Li) from Aluminum-Lithium (AI-Li) alloys. X-ray diffraction measurements have shown that lithium titanate undergoes a phase change from an orthorhombic structure to a hexagonal structure. This change is due to the incorporation of Li in the matrix of the material and the effect of temperature. Although both of the structures are metastable, the hexagonal phase that forms during the scavenging of Li from AI-Li alloys appears to be the more stable phase. Recovering Li from the ESC by electtodeposition does not cause the structure to revert to the orthorhombic phase. Both the orthorhombic and the hexagonal structures of Li.Til07 have similar scavenging capacities for Li. This paper proposes a new mechanism for the phase transformation.

Jan 1, 1991

By Katsutoshi Inoue

Pectic acid gel crosslinked with epichlorohydrin was found to have very high selectivity to lead(II) and iron(III) ions over zinc(II) ion compared with commercial weakly cation exchange resins containing the same carboxylic functional groups, suitable for removing small amount of impurity metal ions from waste zinc plating solutions. In order to lower the cost, new adsorption gel was prepared from orange juice residue containing pectic acid by crosslinking with epichlorohydrin, which was also found to be suitable for removing these impurities. Further, very cheap adsorption gels was prepared not only from orange but also from apple juice residues by a simple method through just saponificating pectin substances contained in these residues into pectic acid by calcium hydroxide followed by water washing and drying. These adsorption gels exhibited excellent adsorption behaviors for removing the impurity metal ions away from zinc.

Jan 1, 2003

By Wang Jia, Chai Li-yuan, Zhang Jin-Long, Peng Bing, Zhang Qiang

"Electrolytic manganese dioxide (EMD) residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick for the utilization of the residue from EMD production. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity. The results showed that the calcined residue had capability of solidifying toxic metals and exhibited perfect strength after treated in the optimal parameters of EMD residue below 50%, temperature at 1000-1100°C, time3-5h, and semi-quenched at 600°C1 InstructionSolid clay-brick holds the leading position among building materials for a very long time in China. The traditional technique of making clay-brick has the drawbacks of backward process, simple facilities and single product. Since Chinese Reform and Opening-up, urban-rural construction and real estate have been booming with the rapidly development of national economy and science technology. The problems of ruining fertile land, environment contamination and high energy consumption in the traditional technique of clay-brick making have not been solved yet. On the other hand, more than 7 billion tons of industrial wastes are accumulated over years which occupies over 6.7 million hectares filed and causes serious environmental problems[1-31. Strategy present in ""The Chinese Agenda of the 21st Century"" required the production of wall materials less energy conservation, land saving and waste recycling.Coal gangue[4-9l, fly ash[I0- 13l, sludge from waste water treatment and tailings of gypsum, pyrite, copper mine, high silicon containing iron, asbestos and ects [l4-lSJ are the solid wastes used for brick making around the world. There are two kinds of process for brick making, high temperature sintering and low temperature steam curing[19•201. Although the technology of two brick making made great progress and got widely application in construction field, no precedent for preparing sintering-bricks with EMD residue as materials occurred in China because of its complicated processing technics and lack of sufficient practical experience to guarantee the bricks' quality.In this study, EMD residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity."

Jan 1, 2011

By Chao Li, Shuai Wang, Hongxu Li, Lifeng Zhang, Xie Yang

The method of chloride-hypochlorite leaching has the advantages of short process, low pollution and higher in reaction rate compared with the traditional leaching method. In this research, NaCl - NaClO solution is used to leaching gold from a refractory gold concentrate, and the influence of NaCl and NaClO concentration, reaction time to the leaching rate were investigated in this experiment. The raw materials and the leaching residue were characterized by a series of analysis methods such as XRD, XRF, SEM and EDS. Results indicate that the leaching rate and the desulfurization rate can be achieved at 96.26% and 98% with most optimum conditions as follows: NaCl concentration 50g/L, NaClO concentration 200g/L, Liquid-solid ratio 10:1, the best reaction time was 150 mins. And these conditions should be guaranteed pH<8.0, ORP>900mV.

Jan 1, 2015

By Robert D. Rogers

The demand for phosphate will continue into the future, because phosphate is currently irreplaceable as a plant nutrient and in many chemical applications. Phosphate is not recycled, so the supply must be replenished through a process of mining and purification. Numerous microbial isolates. obtained from the environment were screened find those which demonstrated the greatest promise of solubilizing PO4 from the ore of interest. Screening was accomplished in a step wise manner an agar plate bioassay, shake flask studies, and semi continuous growth conditions. It was found that with the proper conditions of nutrient supply and solution pH; the bacteria and. fungus used in the semicontinuous process were able to solubilize in excess of 80% of an Idaho rock phosphate ore (RP) within nine days. A significant amount of solubilization occurred within the first six days. There was a &apos;reasonable correlation between the occurrence of soluble Ca and PO.4 during the processing of the RP thus providing evidence that the RP was being disintegrated by the organisms. In all cases, HPLC analysis of the solutions in which PO4 had been. extracted from RP showed that organic acids, which have been implicated as the mechanism of solubilization, were present.

Jan 1, 1991

By Guan-zhou Qiu, Shui-shi Liu, Yu-feng Guo, Tao Jiang

"The preparation of high-quality synthetic ruitle from electric furnace titanium slag was systematically investigated by activation roasting followed by acid leaching process. The results showed that impurities such as Ca and Mg in titanium slag can be effectively removed and TiO2 grade of the product was markedly improved by the process. High-quality synthetic rutile containing 88.54% TiO2, 0.42% (CaO+MgO) was obtained under the conditions that roasted with 7.5%(wt) H3PO4 at 1000 oC for 2h, followed by two-stage leaching in boiling dilute sulfuric acid for 2h. Mechanism studies showed that anosovite solid solution and silicate minerals were reacted with phosphoric acid in the roasting process. As a result, titanium components in titanium slag turned into rutile (TiO2) and impurities were transformed into acid-soluble phosphate and quartz.IntroductionWith the gradual depletion of natural rutile and the rapid development of titanium industry in China, the natural rutile reserves cannot satisfy the requirement for production of titanium pigment and titanium sponge. Ilmenite is, therefore, becoming main raw material for titanium industry. However, because of its low TiO2 grade, it generally requires preconcentration to titanium-rich material such as titanium slag or synthetic rutile [1-3].Ilmenite resources are extremely rich in Pan-xi area of China, which account for 90.54% of total ilmenite reserves in China [4]. The titanium slag produced by electric smelting of ilmenite concentrate has high contents of Ca and Mg, and is not suitable as a raw material for chloride process and titanium sponge production. Therefore, upgrading titanium slag to prepare raw material suitable for chloride process and titanium sponge production has important significance for the development of China's titanium industry."

Jan 1, 2011

By Xiao-hui Fan, Li-shun Yuan, Xu-ling Chen, Wei Lv, Min Gan, Yi Wang

"As the amount of ferrous scrap increases every year, it becomes more and more urgent to deal with this iron-bearing resource properly. This paper puts forward a method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing), and these cold-bonded pellets can be used as coolant in a converter. The influence on the pellets qualities by using different kinds of chloride as rust agents is studied, and results show that the strength of cold-bonded pellets increases significantly by using a combination of the three kinds of chloride -NaCl,MgClz,FeCh, their best dosages are 1.2%, 0.2%, 0.1% respectively. Other iron-bearing materials also have an effect upon the pellets strength, by adding 5% iron powder and maintaining for 48h, the compressive strength of the clumps surpass 2500N/A, dropping strength surpass 4 times/ A, and 10% iron slag or 20% steel slag can replace 5% iron powder while obtaining the comparative quality. The influence of different ratios of three ferrous scrap (converter mud, iron scale and dust) is further studied, and results show that when the ratio is 30% : 30% : 40%, the pellet strength reaches the maximum. After maintaining for 24~48h, the clumps can meet the mechanical as well as the physical-chemical requirements as BOF steelmaking refrigerant.IntroductionGreat amounts of converter mud, dust and iron scale are produced in steel production process. These materials are of great values, and their accumulation not only leads to environmental pollution, but also wastes the precious resources, which restricts the sustainable development of the steel industry [1,2] The main approach at present to dealing with the ferrous scrap is to add them into sintering. But in this way, the utilization factor of sintering and the quality of sinter decline while the energy consumption increases [3].Therefore, more advanced and efficient technology is needed to make the best of these iron resources. Cold consolidation of ferrous scrap is a simple process that has many advantages such as less investment, quicker effect, lower energy and lower cost [4-5] But the conventional maintaining period is too long, usually up to four-six weeks, and the pellet strength is low. Therefore, the key points of the cold-bonded pelletizing are to develop a new adhesive [4,5] to shorten the natural maintenance cycle and to improve the strength of the pellets. A method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing) is brought forward, and these cold-bonded pellets can be used as coolant in converter. After maintaining for 48h, these cold-bonded pellets can satisfy the mechanical requirements to replace the converter coolant [6]."

Jan 1, 2013

By SIMON TIMBILLAH

The chalcopyrite-molybdenite (Cu-Mo) flotation industry is increasingly turning to organic depressants as suitable replacements for inorganic reagents, such as NaHS, due to environmental and safety concerns as well as high consumption rates of the inorganic reagents. This presents an opportunity for improvements or design and synthesis of alternative reagents. Disodium carboxymethyl trithiocarbonate (Orfom® D8) depressant is an organic depressant with a carboxylate group on one end and a trithiocarbonate group at the other end. Fundamental results are shown regarding the interaction of the Orfom® D8 depressant in the bulk flotation of a Cu-Mo concentrate from an operating North American mine. Cyclic Voltammetry on pure copper and Fourier Transform Infrared Spectroscopy (FT-IR) and X-ray Photoelectron Spectroscopy (XPS) measurements on pure chalcopyrite with Orfom® D8 depressant treatment are also reported. Through such characterization techniques a potential adsorption mechanism of Orfom® D8 on the mineral surface was identified and its depressant characteristics in the Cu-Mo flotation systems explained.

By K. A. Brunk

Newmont&apos;s research, operations, history and experience with pre-treatment of preg-robbing carbonaceous ores are described, with emphasis on the chemistry, physics and kinetics of chlorine treatment. Present operations, control strategy and projected changes are also described, including a summary of the adsorption of chlorine into pulps and off-gas scrubbing. Conditions of chlorination have been optimized by the use of Eh-pH diagrams of the gold-chlorine-water system, and have resulted in significant increases in gold recoveries and decreases in chlorine consumptions.

Jan 1, 1987

By Nobuo Takahashi

Effective solvent extraction media have been investigated for purification of rare earths. At first, a quaternary ammonium compound was studied. The counter anions of rare earths and organic dielectric substances were tested to improve separation factors,. And second, crown ethers were selected for extractant. Several diluents of crown-adducts were tested to improve solubility and distribution coefficient as well as the counter anions of rare earths. Especially, in the presence of strong reducing agents, highly selective extraction of europium from other rare earths was observed. The third extactnts were ß -diketones. Presence of organic dielectric substances was very effective to improve separation factors. Though those. three groups of extractants were suitable for mutual separation of light rare earths, alkyl esters of alkyl-phosphonic acids were suitable for mutual separation of heavy rare earths because of their high separation factors. To keep proper pH value was necessary for acidic extractants, so control method of the solution pH was studied with high molecule insoluble amines or salts of those.

Jan 1, 1995

By N. L. Piret

In copper smelting minimization of solid waste generation is receiving increased attention with more stringent environmental legislation and lower disposal space availability. Copper smelting slags generally being valorizable, solid waste generation is attributed to the presence in the feed of unvalorizable impurities which do not report to the slag and to the unavoidable formation of contaminated dilute acid solutions which need neutralization. As to unvalorizable impurities, solid waste minimization is achieved by rejecting them in the highest possible concentration. Dilute acid is mainly due to the formation of SO3 in the smelter gases and to the discard of decopperized bleed-off electrolyte. Its generation is substantially lowered by preventing SO3 formation, by converting the dilute acid to a valorizable product, e.g., by thermal decomposition for H2S04 recovery or by precipitation as chemical gypsum, and by suitable treatment of the bleed-off electrolyte for impurity removal. Industrial processes are evaluated and alternatives are discussed.

Jan 1, 1994

By J. K. Brimacombe, I. V. Samarasekera, B. G. Thomas

"Mathematical models have been developed for the processing of static cast steel ingots and are app1ied to investigate the mechanisms for the formation of panel cracks. Panel cracking is an intermittent but persistent defect that causes affected steel ingots to be scrapped. A two-dimensional, finite-element, heat-transfer model was formulated and employed to calculate the temperature distribution in both large and small steel ingots during the various processing stages from initial casting to the start of rolling, including solidification, cooling in the mold and in air, reheating in the soaking pit, and subsequent air cooling. The stress state in the ingot arising from the calculated temperature variations was then determined. This involved the development of a transient, elasto-visco-plastic, finite element, thermal stress model, including the effects of phase transformation volume changes and kinetics creep, and temperature-dependent, mechanical properties. The results of the mathematical model predictions of temperature and stress were then used to determine the mechanisms and to suggest solutions for two different types of panel crack formation. Mid-face panel cracks apparently form during air cooling when the mid-face surface temperature is between the Arl and 500~C. Off-corner panel cracks appear to initiate internally during the early stages of reheating but do not propagate to the surface until much later. IntroductionPanel crack formation in static-cast steel ingots is a defect that has been plaguing the steel industry for several decades. Although the problem is intermittent, it is also serious since affected ingots must be scrapped. Panel cracks are manifested as two distinct types of cracking problems. ""Mid-face"" panel cracks are found exclusively in small, 2 to 6 ton, medium carbon steel (0.3 to 0.7% C) ingots and usually exhibit a single, continuous, longitudinal crack down the center of one of the ingot faces as shown in Fig. l (l). ""Off-corner"" panel cracks often form roughly oval, discontinuous crack patterns on the wide faces of large, 20 to 30 ton ingots as seen in Fig. 2 (2). They affect only low carbon steels (0. l to 0.2% C) with high manganese content. Both defects affect only aluminum-treated steels and are caused by a combination of intermediate temperature ductility loss involving aluminum-nitride precipitation and thermal stress generation. The ductility problem has received a good deal of attention which was the subject of a recent review (3). The present study was undertaken to investigate the thermal stress aspects of the problem through the development of mathematical models of heat transfer and stress generation in static-cast steel ingots. The ultimate objective was to elucidate the mechanisms of formation for both types of panel crack and to evaluate possible solutions to the problem."

Jan 1, 1986

By Ali Hasham

Reduction rates of FeO in CaO-SiO2-Al2O3 slags by Fe-C melts have been investigated experimentally at 1723 K. The rates were estimated using experimentally determined CO(g) evolution rates. Flash X-ray images were employed to visualize the behavior of the melt-slag interface during the reactions. The influence of melt interface was examined by conducting two types of experiments - (i) dropping one (or several) Fe-C droplet(s) weighing 2 g into the molten slag bath, and (ii) dropping a small amount (10-30 g) of slag onto a Fe-C melt weighing 400 g. The rates from both types of experiments were compared and analyzed to determine the rate limiting steps. It was established that neither the carbon transport in the Fe-C melt, nor the transport of gas species in the gas film adjacent to Fe-C melt was responsible in limiting the reaction rate. It is possible that the slag phase mass transport may be controlling the initial reduction rate in the droplet experiments. However, a, different mechanism was responsible in limiting the reduction reaction when the overall %C in the droplets fell to about 2-3.

Jan 1, 1992

By Kafui Nyavor

The indirect, and the direct contact mechanisms of bacteria oxidation of sulfides were studied using Thiobacillus ferrooxidans and pyrite. The aim was to determine which of the two generally aeeepted mechanisms played a dominant role, if any, during acid mine drainage (AMD) formation from the oxidation of sulfide minerals. The results show that at a pH of 4.5 where T. ferrooxidans are quite active, but where initial chemical oxidation of pyrite to Fe2+ is limited, the bacteria were unable to directly oxidize pyrite to any significant extent. Whereas, in the presence of Fe2+, T. ferrooxidallS assisted oxidation of pyrite by the indirect mechanism was observed and sustained over the pH and Eb range where the bacteria is active. The results lead to the conclusion that the direct contactmechanism of pyrite oxidition by T. ferrooxidans is insignificant. The predominant, and possibly the only, pathway involves the indirect bacteria oxidation of available Fe2+ to Fe3+, which in turn oxidizes FeS2 to generate additional Fe2+ and acidity in a cyclic process.

Jan 1, 1996

By P. Maraboutis

Iron removal by precipitation as jarosite from Fe-Ni-Co sulfate solutions, (synthetic or real, resulting from laterites leaching) has been investigated. Precipitation was carried out at 95 C, and at an initial pH 1.6, which was either kept constant with CaCO3 or Li2CO3 additions, or left to drift with the evolution of the reaction to lower values. The precipitation of K-, NH4- and Na- jarosite was initially examined using synthetic solutions. In all cases, hydronium ions were incorporated into the precipitate as well. Residual iron in solution was lower (0.2-1 g/1) and equilibrium was achieved faster (within 4-8 h) when precipitating K¬jarosite at constant pH, using CaCO3 for neutralization. Nickel and cobalt losses were small. Na- jarosite precipitation was also studied from real solutions with high initial iron content, under constant pH=1.5, controlled with CaCO3 additions, and it was shown that low residual iron concentration in solution (0.3-0.5 g/1) can be achieved again, with relatively small nickel and cobalt losses. The thickening and filtration characteristics of the precipitates were excellent in all cases examined.

Jan 1, 1988

By R. W. Charles

The Los Alamos National Laboratory, under the sponsorship of the U.S. Department of Energy; is involved with laboratory and field experiments to assist in development of the Hot Dry Rock concept of geothermal energy. The field program consists of experiments in which hot rock of low permeability is hydraulically fractured between two wellbores. Water is circulated from one well to the other through the fractured hot rock. Our field experiments are designed to test reservoir engineering parameters such as heat-extraction rates, water-loss rates, flow characteristics including impedance and buoyancy, seismic activity, and fluid chemistry. Laboratory experiments were designed to provide information on the mineral-water reactivity encountered during the field program. Two experimental circulation systems tested the rates of dissolution and alteration during dynamic flow. SOlubil ity of rock in agitated systems was studied. Moreover, pure minerals, samples of the granodiorite from the actual reservoir, and Tijeras Canyon granite have been reacted with distilled water and various solutions of NaCl, NaOH, and Na.CO.. The results of these experimental systems are compared to the observations made in field experiments done within the hot dry rock reservoir at a depth of approxi-mately 3 km where the initial rock temperature was 150 to 200°C.

Jan 1, 1981