By Lei Wang, Jianjun Wang, Lingen Luo, Zhengbang Li

Dearsenication in molten steel was studied by adding Ca-Fe Alloy-based arsenic removal agent. In order to improve the utilization rate of Calcium Iron Alloy and improve arsenic removal ratio, [O] is less than 0.0005% and [S] is less than 0.0035%, Al is added into the molten steel. In the processes of adding CaO-Al2O3 based alkalinity slag for arsenic removing in molten steel (initial arsenic content is 0.0080%), arsenic removal ratio reaches 50% when Ca-Fe Alloy addition amount is 18%. During the arsenic removal experiment, adding Rare Earth promotes the arsenic removal reaction and makes the arsenic removal more effectively.

Jan 1, 2015

By S. Neogy, M. Gupta, D. Srivastava, V. Kain, S. Roychowdhury, R. C. Prasad, G. K. Dey

"Austenitic stainless steels are an important material of construction for Boiling Water Reactors (BWR). These stainless steels are amenable to strengthening by strain hardening. Various deformation modes at different test temperatures and strain become active. In the present investigation type 304LN stainless steel was used in the annealed and strain hardened condition. Thin foils were prepared from gauge section for transmission electron microscope (TEM) investigation after tensile testing at room temperature and at 288°C. TEM investigation reveals that twinning is the major mode of deformation for the tests done at room temperature while dislocation cross-slip is the major mode of deformation at higher temperature. Stacking faults were also observed to a limited extent. The extent of twinning was much higher for the tests done using the rolled material. The formation of martensite in the stainless steel due to straining was investigated by the analysis of selected area diffraction patterns.IntroductionAustenitic stainless steels (type 300 series) are an important material of construction in Boiling Water Reactors (BWR). These stainless steels cannot be heat treated but can be strengthened by cold working [1]. Nitrogen alloying of these stainless steels result in high strain hardening rates and higher strength without any loss in toughness [1]. Stress Corrosion Cracking (SCC) in BWR of these types of stainless steels have been attributed to surface strain hardening and strain hardening ofregions adjacent to constrained weldment [2].The test temperature [3, 4], prestrain [5] and nitrogen level [5] has been reported to affect the deformation mechanism during tensile testing. Byun et al. [3] have reported the formation of martensite, dislocations, stacking faults and twinning during tensile deformation, the extent of each depending on the test temperature. Strain localisation has been reported to occur during tensile deformation in irradiated stainless steels [ 6]. The behaviour of rolled material during tensile testing is similar to that of irradiated material to a large extent [3]. Austenitic stainless steels are low stacking fault energy (SFE) materials in which various types of microstructures have been reported to form during tensile deformation and the strain is also highly heterogeneous in nature in these stainless steels which aides SCC in BWR environment to a large extent [7]. During cold working of austenitic stainless steels second order twinning has also been reported [8]. Knowledge about the deformation mechanisms operative in the strain hardened austenitic stainless steels during tensile testing at different temperatures is essential to understand the material deformation behavior and the present study aims at enhancing the existing understanding."

Jan 1, 2011

By Carla Lupi

Zinc electrowinning from sulfate solutions is the traditional industrial method to produce SHG zinc. Over the past few years several efforts have been done to improve process efficiency in order to reach high productivity with low energy requirement. The latter aim can be pursued both by means of a hard purification of the electrolyte and reducing the anodic voltage. This work is a comparative study of the results obtained in several previous researches on zinc electrowinning from both sulfate and chloride solutions. Zinc electrowinning tests on industrial sulfate solution have been carried out by using Pb alloy anodes and by adding organic depolarizers such as ethanol, acetic acid or ethylene glycol. Experiments on chloride solutions, obtained by purification of zinc exhausted electrolyte, have been performed by using DSA anodes and by testing the effect of additives such as TEACI and TBAC\. Comparing the best results obtained with the two methods it can be highlighted that a high quality zinc is electrowon in both cases with comparable energy requirements.

Jan 1, 2000

By N. El-Kaddah, A. D. Patel, T. T. Natarajan

The phenomenon of particle migration in a conducting fluid under an applied electromagnetic force field finds its application in selective sorting of minerals and more recently in the removal of inclusion from molten metal. This paper deals with the analysis of the expulsion force and the flow around a spherical particle in crossed uniform electric and magnetic fields in .infinite and in confined medium. Analytical solutions will be presented for the electrk and magnetic fields as well as the induced flow at the limit of zero Hartmann number. The flow around the particle was investigated numerically at low and high values of Hartmann number. It will be shown the magnetic field has almost no effect on the velocity field when Hartmann number is less than 1.0. At higher Hartmann numbers the damping effect of the magnetic field was pronounced in the direction of the applied current. It is concluded that Hartmann number has little effect on the net force on the sphere particle.

Jan 1, 1999

By W. Dresler

Design details of a 100 kVA DC electric-arc reduction furnace are described. The furnace is equipped with a 610 mm (24 inch) diameter graphite crucible hearth. A 76 mm (3 inch) diameter top graphite electrode is used as a cathode. The current passes through the bottom of the crucible and is carried to a bottom plate (the anode) by conductive magnesia carbon bricks. The furnace can be operated up to a maximum of 120 V, 1800 A, and presently 100 kW. The start-up operating experiences and metallurgical results of one reduction test with a Montana chromite containing 38% Cr2O3 are discussed.

Jan 1, 1994

By P. E. Nolan

The disproportionation of carbon monoxide is an important aspect of reduction processes, in the production of carbon filaments for composites, and in the removal of CO from CO,. It can also be a hindrance, causing carbon fouling of equipment and metal dusting. The reaction is thermodynamically favored at lower temperatures, but it occurs slowly. Catalysis of the reaction by transition metals has been examined. A materials science approach to the selection of a catalyst material and of optimum operating conditions is being taken in the present work. Of particular interest is characterization of a catalyst that can be repeatedly regenerated to prevent deactivation in long term use. Experimental data on a less studied catalyst, ruthenium, are reported.

Jan 1, 1992

By John E. Litz

The Denver Process is a chemical/metallurgical process for treating radioactive or mixed wastes by extraction and concentration of the radioactive and/or hazardous component(s). The process was developed at bench scale, evaluated at pilot scale, and will be implemented at full scale to remediate a low-level radioactive sludge. Six unit operations comprise the process: feed handling, leaching, solvent extraction, electrodeposition, precipitation, and tailing preparation. Unit operation design may be modified to tailor the process for varying feed stock composition. Radioactive or mixed waste is reacted with aggressive reagents in an aqueous phase, solubilizing targeted components. These components are then selectively extracted and concentrated in subsequent steps. Waste solids and solution exit the process as non-hazardous non¬radioactive waste. Dehydration of aqueous waste by submerged combustion eliminates aqueous discharge.

Jan 1, 1994

By Vinicius Alves Gomes, Jean Igor Margem, Thallis Cordeiro, Frederico Muylaert Margem, Roberto Faria Jr., Sergio Neves Monteiro, Marina Rangel Margem

Natural fibers are attracting the interest of engineering sectors owing to specific advantages such as lightweight and lower cost as well as for their inherent condition of being renewable, biodegradable, recyclable and neutral with respect to CO2 emission. In particular, the fiber extracted from the malva plant stem is nowadays recognized as one of the strongest lignocellulosic fibers. However, the thermal properties of the malva fibers have yet not been fully investigated. The present work had as its objective to investigate, by photoacoustic spectroscopy and photothermal techniques the thermal properties of diffusivity, specific heat capacity and conductivity of a pressed malva fibers sample. The results revealed that these fibers showed a superior thermal insulation capacity.

Jan 1, 2015

By D. Y. Wang, G. Y. Sha, X. L. Shen, D. R. Gu

The study of the volatilization kinetics of zinc and lead in pellets made of zinc-leadbearing dust mixed with coal powder, in a nitrogen atmosphere and at a temperature range between 1100 °C and 1300 °C, shows that the reduction temperature has a significant effect on the volatilization rates of zinc and lead, and that both the particle size of the coal powder and the extra carbon content has no effect on the volatilization rates. The obtained activation energies for the volatilization of zinc and lead are 79.42kJ/mol and 88.74kJ/mol respectively. The volatilization rate of zinc is controlled by the reaction between the zinc oxide and carbon monoxide while that of lead is controlled by the lead evaporation reaction, and the diffusion of gaseous lead through the gas boundary layer covering the surface of the reduced liquid lead.

Jan 1, 2000

By Bart Blanpain, Muxing Guo, Zhuangzhuang Liu

In order to stabilize free lime in the basic oxygen furnace (BOF) slag to achieve high value products, quartz sand and other additives are injected into slag. However, the current hot stage slag stabilization does not work in case of slag (before treatment) with a liquid fraction lower than 90%, where the slag containing solid particles is too viscous. Therefore, it is essential to understand how solid phases affect the viscosity of the slag system. In this study, the industrial BOF slags were investigated with respect to the correlation between volume fraction of solid phases and its viscosity. Slag viscosity was measured with a rotating type viscometer at temperatures below the liquidus. The volume fraction of solid phases was quantitatively calculated with FactSage. The Einstein-Roscoe equation was employed to predict the viscosity of BOF slag.

Jan 1, 2016

By S. Shrivastava

A structure based model has been developed for the prediction of viscosities of K20-B20, melts. These melts exhibit an anomalous behavior of viscosity with continuous variation in B203 content. A maximum and a minimum are observed at low temperatures, which disappear on raising the temperature above the softening range. The addition of K20 to the borate melts causes two opposing phenomena: (1) depolymerization effects and the related breakdown of network structure resulting in the formation of singly bonded oxygens, which weakens the structure and hence causes a decreases in viscosity, and (2) the formation of four coordinated borons (BO4 tetrahedra) which strengthen the structure leading to an increase in the viscosity. The structural changes taking place in these melts on varying the temperature and the alkali content have been reviewed and are incorporated in developing this model. The predicted values are in excellent agreement with the experimental values over the whole temperature and composition range.

Jan 1, 1992

By Guoqiang Lv, Xi Yang, Wenhui Ma

Cast multicrystalline silicon ingots are widely used in photovoltaic manufacturing. A key issue to achieve high solar cell efficiencies is to attain an optimized temperature field during directional solidification (DS) process. This paper reports numerical investigation of multicrystalline silicon (mc-Si) ingot production using two major types of DS furnace. Specific examination is made on thermal distribution, interface shape and stress field. Evaluation is performed for the applicability of thermal system design to reduce thermal stress, improve crystal quality and enhance energy efficiency. The effects of procedure parameters and geometric configuration on temperature distribution are discussed as well to provide the viable solutions for systems optimization.

Jan 1, 2015

By Zhucheng Huang, Zhikai Liang, Lingyun Yi, Tao Jiang

"In this study, reduction of iron ore pellets was carried out at 800-950°C by simulating the atmosphere of typical coal gasification gas. The effects of temperature, gas composition and reduction degree on swelling were investigated respectively. Reduction degree was obtained according to the weight loss records. And volume changes of pellets during reduction were evaluated by infrared photography. Results showed that the pellet swelling increased with temperature and decreased slightly with hydrogen content in the reducing gas. The swelling peaked when reduction degree reached about 40% and then decreased to be stable finally. The microstructures of pellets during reduction were examined by reflected light microscope and relatively rational explanations were proposed for their swelling behaviors.PrefaceDirect reduction iron is an important and indispensable raw material for high-purified and high-quality steel in the electric furnace smelting. Gas-based shaft furnace direct reduction process has very strong competitative ability; however, this technique requires natural gas as reducing agent, so its development has been restricted by gas source and area. Compared with gas-based reduction method, coal based reduction method has the disadvantages of higher production cost and lower productivity. In China, coal resources are abundant and coal gasification technology is mature, and the development of coal gasification shaft furnace direct reduction process is promising. [1] The gasification methods of fixed bed method (Lurgi method), fluidized bed method (Undok method), airflow bed method (Texaco coal water slurry method and Shell dry powder coal method) have been put into use successfully. These syngas generated by different methods can meet the actual production requirement of shaft furnace. However, the compositions of the effective reduction gas in the syngas are quite different. The ratios of hydrogen and carbon monoxide (H2/CO) of Undok or Shell coal gas, Texaco coal gas and Lurgi coal gas are 0.4, 0.6~ 1.0 and 1.6~2.3, respectively. [2] In the coal gas direct reduction process, the swelling behavior of iron ore pellets is various due to the differences of the gas composition, reduction temperature and reduction degree, and it seriously affects the normal operation ofDRI production. [3-9] Therefore, the research on the swelling behavior and its mechanism of iron ore pellets in direct reduction were carried out in this paper."

Jan 1, 2013

In accordance with the new concept described in the paper presented at the TMS annual meeting in 1989, 1 a new zinc cellhouse was constructed and successfully operated. The new concept was proposed in order to reduce energy requirements and to mechanize the electrode handling in the cellhouse. Major modifications involved the use of an electrode unit consistfog of assembled anodes and cathodes with frame bodies between each cathode and anode. The space between a cathode and an anode could be halved by this unit structure. In this paper actual operation data are summarized and discussed in comparison with the calculated figures.

Jan 1, 1990

By Jacques Magnaudet, Julie Cranga, Didier Huin, Pascal Gardin

"With the aim of controlling steel grade in steelmaking reactors, IRSID and IMFT are developing a numerical description of the evolution of bubbles in the vicinity of a liquid steel/ slag interface. The objective is to identify the main parameters affecting the hydrodynamics of the various phases. The goals of the present paper are:• To describe the numerical technique developed to predict the multi phase flow including bubbles, liquid metal and slag layer.• To analyze the influence of the absolute pressure on the bursting of bubbles in a RH degasser. Validation is given by comparison with results available in the literature. The major point concerns the distinct behaviors observed whether the pressure is low or high.• To study the influence of the properties of the slag layer (thickness, viscosity and interfacial tension) on the entrainment of liquid metal in the wake of the bubble and on the nature of the projections from the bath surface.IntroductionMost of secondary steelmaking processes use gas stirring for homogenization, removal of nonmetallic inclusions or decarburization under reduced pressure. The bursting of gas bubbles at the metal or slag layer surface produces a beneficial ejection of metal droplets in the low pressure atmosphere, provided that there is no violent projection, which may have detrimental effects on the process.Our objective is to develop a numerical tool to study the phenomena occurring in the vicinity of the bath surface, in particular bubble bursting under reduced pressure and entrainment of metal in the slag layer. In this paper we report the first conclusions of our study. In the first section we describe the numerical model used to describe the three-phase flow and the expansion of the gas bubbles under the effect of the ferrostatic pressure. The second section is devoted to the study of pressure effects on bubble rise and bursting. The third section reports some computational results about the rise of a gas bubble through the interface between the two liquids."

Jan 1, 2001

By Du Sichen, S. Seetharaman, Wei Liu

"The viscosities of two-phase mixtures are of great importance in the modelling of the fluid flow in metallurgical processes. For example, in steel making and refining, the intimate mixing of metal droplets in the slag phase requires a consideration of the effective viscosities for the mixture. The present work was aimed at an understanding the phenomena underlying the viscous flow in a two-phase mixture with widely differing viscosities.Emulsions of silicone oils of known viscosities (345mPa.S and 1010mPa.S at 293K) with small amounts of water evenly distributed in the same were prepared by subjecting the mixture to uniform stirring using a magnetic stirrer. The viscosities of these emulsions were measured at constant temperature by rotating cylinder method using Brookfield Digital Rheometer. The uniformity of the preparation of the emulsions was confirmed by the reproducibility of the results. Th7 measured viscosities were generally found to be independent of the torque under the experimental conditions so that the two-phase mixture could be considered as a Newtonian liquid. The variation of viscosities with temperature and the effect of addition of a surface-active substance were also studied in this work.The measured viscosities were found to be· higher than those of both pure water and silicone oil. The experimental viscosities were found to increase with increasing concentration of water. The influence of surface tension on the viscosities was examined by adding surfaceactive agent to the mixtures. The result is discussed and compared with theoretical models developed by Einstein, Taylor and Oldroyd."

Jan 1, 2000

By A. Rawat

The removal of oxyanions of arsenic present in mine process water and drinking water to a regulatory level is a challenging problem. Recently a patented adsorbent lanthanum oxide has been developed which has shown strong specificity for the anions of arsenic. In this paper the kinetic and thermodynamic aspects of arsenic adsorption on to lanthanum oxide are discussed. Adsorption tests were performed at different temperatures using synthetic solutions of arsenic of varying concentrations. From the kinetic data and adsorption isotherms thermodynamic properties such as Gibb's free energy, standard enthalpy of adsorption, standard entropy, isosteric heat of adsorption and activation energy were determined. The results showed that temperature had a positive effect on the rate and degree of adsorption:The activation energy decreased with increase in the initial concentration thus indicating solute-solute interactions in the system. Also, the isosteric heat was found to decrease with increase in the adsorption density implying a heterogeneous adsorbent surface.

Jan 1, 1998

By Rodríguez M. Esperanza

The efficient performance of Pachuca tanks is strongly linked to the suspension of mineral particles, which results from the motion of the liquid caused by injected gas rising, in general, through a central draft tube. This study reports a computational investigation on the effect of operating and design parameters on the suspension of particles. By extending the classical 2-phase drift-flux model to compute the gas hold-up, the three-phase (water-air-particles) system was simulated as consisting of a variable-density liquid plus the solid particles. These two phases were treated as interpenetrated continua using an Eulerian approach to set a turbulent recirculating flow model in 2-D and transient state. The model predicted adequately the measured critical superficial air velocity, uc, needed for maintaining particle suspensions, in pulps with 10-50 wt% solids. Additionally, the model was used to investigate the operation of industrial size reactors, obtaining results that agree well with the general trends reported in the literature, and highlighting important differences with respect to laboratory-scale reactors.

Jan 1, 2009

By N. Coone

By exploiting the results of solidification modelling foundries can enhance the quality and reduce the cost of their casting processes. However not enough information exists on the thermal boundary conditions, which control the transfer of thermal energy stored in liquid metal to the mould via the metal/mould interface during solidification. This is quantified by the heat transfer coefficient (h.t.c.). An experimental and numerical study was carried out to find the magnitude and variation of the h.t.c. in cylindrical castings during the solidification of grey cast iron in green sand moulds. The h.t.c. values were calculated using a time marching solution to the inverse heat conduction problem. The variation of h.t.c. with metallostatic head was analysed. There is a wide scatter in green sand thermal properties due to the large number of variables involved in mould manufacture including green sand compaction and water content. The sensitivity of the calculation to uncertainties in the thermophysical properties of the green sand was evaluated. Keywords: Heat transfer coefficient, grey cast iron, sand moulds. inverse technique

Jan 1, 2003

By P. F. Stratton, M Huggahalli, N Saxena

"Several studies have been carried out to determine how the optimum atmosphere conditions in the heat treatment of metals can be established for a given product by using different gas injectors and varying atmosphere flow rate and composition. The most common approach taken to gain insight into furnace atmospheres has been to use commercial computational fluid dynamics codes and examples of their use are shown. However, the complexity of these codes, the difficulty in establishing boundary conditions, their cost and computational demands limit their usability in solving day-to-day production problems.A simplified, web-based model of a furnace atmosphere is described where the conservation equations are solved to determine the composition profiles of the atmosphere in the furnace. Although the model is restricted in scope to certain types of furnace, it is shown to give better results than CFD when boundary conditions are uncertain. The application of the model to the understanding of existing furnace conditions and to determining ways of optimising the use of gases are discussed. IntroductionThe important role of protective atmospheres during heat treatment of metals, furnace brazing of assemblies and soldering of printed circuit boards is well established. The atmosphere in the furnace prevents air ingress and oxidation of the parts, helps flush away any flux or binder from braze and solder pastes and provides an important mode of heat transfer [1]. In a batch furnace having typically one or two gas injectors, the gas utilisation and process can be optimised by minimising air leaks and mantaining atmosphere homogeneity with fans or other atmosphere circulation techniques. In a continuous furnace, however, atmosphere optimisation is more difficult as furnace inlets and exits can also let in air. The atmosphere requirements of different stages of heat treatment, brazing or soldering vary [2]. Achieving these atmospheres in different sections of the open-ended furnace is a relatively complex task. Methods such as atmosphere zoning and the use of physical curtains and gas injectors have evolved with time, though it is hard to predict how effective these techniques will be for a given furnace and process. Experts in the field tend to rely on experience and rules-of-thumb rather than scientific method to achieve the required results."

Jan 1, 2001