Search Documents

By Ji-He Wei

Keywords: stainless steel, AOD refining, side and top combined blowing, mixing characteristics, water modeling The fluid mixing characteristics in the bath during the side and top combined blowing AOD (argon-oxygen decarburization) refining process of stainless steel have preliminarily been investigated on a water model unit of a 120 t AOD converter. The geometric similarity ratio between the model and its prototype (including the side tuyeres and the top lances) was 1:4. On the basis of the theoretical calculations for the parameters of the gas streams in the side tuyeres and the top lances, the gas blowing rates used for the model have more reasonably been determined. The influence of the tuyere number and position arrangement, and the gas flow rates for side and top blowing on the characteristics has been examined. The results demonstrated that the liquid in the bath underwent vigorous circulatory motion during gas blowing, without obvious dead zone in the bath, resulting in a well mixing effectiveness. The gas flow rate of the main tuyere had a governing role on the characteristics, a suitable increase in the gas flow rate of the subtuyere could improve mixing efficiency, and the gas jet from top lance could make the mixing time prolong. Corresponding to the oxygen top blowing rate specified by the technology, a roughly equivalent and good mixing effectiveness could be reached by using six side tuyeres with an angle of 27 degrees between each tuyere, and five side tuyeres with an angular separation of 22.5 or 27 degrees between each tuyere. The relationships of the mixing time with the gas blowing rates of main-tuyeres and sub-tuyeres and top lance, the angle between each tuyere, and the tuyere number have been obtained.

Jan 1, 2005

By Jeffrey D. Winterton

Keywords: Copper, ion exchange, sulfonic acid, bis-picolylamine, ion exchange modeling, ion exchange kinetics As part of an investigation into the feasibility of using ion exchange resins to recover copper from aqueous waste streams generated during the manufacturing of semiconductor devices, the uptake of copper onto two ion exchange resins was investigated. The resins studied were DOWEX G-26, a standard gel type sulfonic acid resin, and DOWEX M4195, a macroporous chelating resin with a bis-picolylamine functional group. The equilibrium and kinetic behavior of the uptake of copper were investigated over a range of copper concentrations with constant sulfate concentration and different levels of acidity. The homogeneous structure of the G-26 resin yields equilibrium relationships that fit the Langmuir equation, and equilibration times of less than 30 minutes. The uptake behavior of M4195 is complicated by the need to absorb co-ions to maintain electroneutrality, resulting in uptake profiles that change character with increasing copper concentrations, and extended equilibration times.

Jan 1, 2005

By Tsunehisa Nishimura

Stable operation of the blast furnace needs adequate control of the lower part. To clarify the behavior of the lower part of the blast furnace with accurate consideration of the property of slag and its flow characteristic, a new mathematical model has been developed. Using this model, the effects of the change of operational conditions on the behavior of the lower part of the blast furnace were studied. Further, means to control of the lower part of the blast furnace, especially effective means to maintain adequate temperature, were discussed. And desirable slag property and composition, especially the method to control FeO concentration dripping from the bottom of the cohesive zone to avoid a decrease in temperature of the lower part of the blast furnace was estimated.

Jan 1, 2006

By Zhan Jing

Keywords: thermodynamic, Ni-Co alloy powders, composition, fibrous The mathematics model of Ni(II)-Co(II)-C2O42?-NH3?H2O-H2O of thermodynamic equilibrium system has been developed theoretically according to the law of conservation of mass and the law of simultaneous equilibrium, and the logarithm concentration-pH (log[Me2+]T-pH) diagrams of this system have been made. The effect of ligand and pH value was studied. Two issues in coprecipitation route to synthesize fibrous nickel-cobalt alloy precursor powder, com-position and morphology which are a first priority, are addressed based on thermodynamic analysis and experiments. The results show that suitable pH value range of coprecipitation of nickel ions and cobalt ions in theory can be obtained to maintain fibrous, excellent compositonal homogeneity and stoichiometry in coprecipitation products. Experimental demonstration is also carried out.

Jan 1, 2005

By Christophe Thiébaut

Keywords: Pyrochemistry, Salts Treatment, Distillation The pyrochemical purification of metal generates spent salts. When this metal is an actinide such as plutonium, the slags cannot be discarded and are thus disposed in nuclear facility. In order to handle with these slags, the decision has been taken to reduce stored quantities. The development of a pyrochemical treatment is in progress in the CEA Valduc centre. The feed salt, typically composed of various Pu and Am species contained into monovalent or divalent chloride matrix, is first oxidized to convert the actinides into oxides. Then the chlorides are separated from the actinide oxides by vacuum distillation. Temperatures higher than 750°C for monochloride salts mixture NaCl/KCl and higher than 1100°C for divalent CaCl2 base salts, are required to produce an industrial flow of vaporization. Inactive qualification of the process for NaCl/KCl base salt has been carried out with lanthanide surrogates. Then, a pilot equipment, called distillator has been designed and built for production-scale distillation of NaCl/KCl and CaCl2 oxidized plutonium salts. Industrial flows of vaporization have been obtained with this pilot equipment : about 4 g/cm²/h for NaCl/KCl at 800?900°C and 1 Pa, and more than 1,5 g/cm²/h for CaCl2 base salts between 1000?1200°C at 0.1 Pa. The last step, now in progress, is the integration of the distillator into a glove box.

Jan 1, 2005

By Elaine Araújo

Since the ancient times, clays were used as decolorant material for various types of oils. These clays were called ?decolorant clay?. They have the property to decolor dye materials present in mineral oils, plants and animals. Biofuel is a fuel derived from biomass of live organisms. As biodiesel is produced from renewable sources, the generation of employment due to industrial scale production may cause a reduction in the dependence on foreign diesel importing, as well as the reduction of air pollution by the addition of biodiesel to diesel. This study aimed to develop a technological process to decolor post- consumption oil to be applied as biofuel. The results were characterized by techniques of XRD (X-ray diffraction), X-ray fluorescence and FTIR (Fourier Transform Infrared). It was observed that the post-consumption oils presented a higher decoloration result after treatment with the Brazilian clay.

Jan 1, 2009

By Qingzhu Li

The brewing industry byproduct, spent grain (SG), was evaluated for its ability to adsorb Ag(I) from aqueous solutions. Ag(I) adsorption was dependent on solution pH, contact time, adsorbent dose, initial Ag(I) concentration and temperature. The kinetic data were well described by pseudo-second-order kinetic model, indicating that chemical adsorption was the rate-controlling step. The equilibrium data followed Freundlich isotherm rather than Langmuir isotherm, suggesting heterogenity of the adsorption sites on spent grain. Ag(I) desorbed from Ag(I)-loaded spent grain was also evaluated in this study. HCl, NaOH, Na2S2O3 and ultrapure water were chosen as eluants and desorbed Ag(I)-loaded spent grain for 30min, Ag(I)-loaded spent grain desorbed in 0.1M Na2S2O3 exhibited higher elution efficiency as compared with other eluants. The results indicated that application of spent grain for adsorption and recovery of silver from aqueous solutions was feasible.

Jan 1, 2009

By Ryo Sasai, Takeshi Itakura, Haruki Imaizumi, Hideaki Itoh

"Emission of industrial wastewater containing harmful oxoanions is one of the serious problems on account of its toxicity and the environmental pollution, especially caused by boric, phosphinic, arsenic and antimonic species. In this study, we developed a novel treatment technique of such polluted-water by hydrothermal mineralization. The treatment is “Geomimetic” method for precipitating oxoanions in aqueous media as natural ore resources by using hydrothermal treatment with calcium salts mineralizer. The treatment made it possible not only to detoxify the polluted-water, but also to recover the calcium minerals such as Ca2B2O5·H2O, Ca5(AsO4)3(OH), etc. Concentration of each ion in treated-water was lower than that of effluent standard in Japan. Moreover, the residual concentration of each ion was independent of the initial concentration, but it depends only on the solubility of the formed mineral under hydrothermal condition. Therefore, the hydrothermal treatment could be recommended as one of the treatment techniques of polluted-water.IntroductionVarious oxoanions such as boron and arsenic oxo-anions have high toxicity against human health and the environment. They are important resources, however, for plating or advanced material manufacturing industries[1-3], from which the wastewater containing these oxoanions is generated every day. An appropriate treatment is often required for industrial wastewaters to attain national effluent standards of Japan (NESJ, B: 10 mg/dm3, As: 0.1 mg/dm3). On the other hand, there is no production of arsenic and boric resources in Japan, and they are expected to be recycled. Therefore, the establishment of a system for the removal and recycling of arsenic and boron from wastewaters is of global significance.Several methods to remove them from aqueous media have been already reported by using adsorption[4], electro-coagulation[5], membrane separation[6-8] and biological techniques[9]. However, these methods have the following problems because of their stability in water. (1) Removal yield is low, especially for tri-valent arsenite ion (AsIIIO3 3-) and borate ion. (2) The applicable concentration range is narrow. In addition, the used adsorbents or collected residues after treatments are sill hazardous wastes, so that they must be treated by a proper method. But, it is very difficult to convert them to recyclable resources at most industrial plants. These problems are caused by the difficulty to recover these oxoanions as stable solid precipitates with low solubility in water. The establishment of recycling system of these hazardous compounds will be one of the world-important issues, especially, in Japan, which is poor in natural resources. On the other hand, compounds that contain high arsenic concentrations and are insoluble in water, are often found in natural minerals, for example, as haidinglite (Ca(AsO3OH)·(H2O) or Johnbaumite (Ca5(AsO4)3(OH)). This fact suggests that nature has an ability to produce insoluble As-bearing minerals. Similar phenomena can be found in case of boron, antimony, etc."

Jan 1, 2008

By Pinai Mungsantisuk

Keywords: Pd-Ni alloys, Pd-Fe alloys, Pd-Co alloys, Magnetostriction, Magnetic Properties The presence of congruent melting minima, the occurrence of ferromagnetic transition over a large composition range, and FCC type crystal structure make Pd-Ni, Pd-Co, and Pd-Fe based systems attractive candidates in our search for materials with no rare-earths, large low-field magnetostriction, and good mechanical properties. The presence of paramagnetic-ferromagnetic transition over a broad range of composition also provides opportunity for fundamental studies. In this work, we have examined the magnetic and magnetostrictive behavior of Pd-Ni, Pd-Co, and Pd-Fe alloys over the entire composition range. Alloy sample rods were prepared by arc melting and casting. X-ray diffractometer was used to obtain lattice parameter data. Magnetostriction was measured along the rod axis using strain gages. Magnetic properties were measured using a vibrating sample magnetometer.

Jan 1, 2005

By Adriana Gómez

White dross is a result of the aluminum oxidation during its primary production and is mainly composed of metallic aluminum, Al2O3, with minor amounts of AlN and some other oxides. Because of the great variety of phases, the quantitative characterization is complicated. This work shows a quantitative method to determine the main phases of white aluminum drosses by means of X-ray diffraction (the Rietveld method). Nowadays the Rietveld method is maybe the most useful method for obtaining quantitative phases information in multicomponent mixtures, this method permits relatively quick quantitative phase analysis by fitting the calculated X-ray diffraction profile with the observed one. The analysis were done using powder with a grain size less than 45 µm; to obtain the suitable material size the aluminum dross was grounded by ten minutes, several times. The grounded material was screened, and the material smaller than 45 µm was taken to quantitative XRD analysis. Keywords: Rietveld Method, Characterization, Aluminum dross.

Jan 1, 2005

By Purushottam Kumar

Keywords: Magnetostriction, magnetic properties, Pd(Fe,Co,Ni) single crystals Fe-Pd, Co-Pd and Ni-Pd alloy systems show appreciable magnetostrictive strains that are of interest for sensor applications. These systems exhibit congruent melting minima. In this work the magnetic and magnetostrictive behavior of congruent melting Fe-Pd, Co-Pd, and Ni-Pd compositions have been examined. The alloys examined include Fe-54.9 at.-% Pd, Ni-45.4 at.-% Pd, and Co-45 at.-% Pd. The paper describes the growth of bulk single crystals of these alloys using Czochralski technique. X-ray diffractometer was used to obtain rocking curves that were used to determine the [001] crystal direction. Magnetostriction in [001] direction was measured using strain gages. Magnetic properties were measured using a vibrating sample magnetometer. Ni-Pd showed the highest magnetostriction values among the congruent melting compositions. Magnetic and magnetostrictive behaviors of these alloy single crystals are presented.

Jan 1, 2005

By Murat Baydogan

Effect of retrogression and reaging treatment on hardness and stress corrosion cracking resistance of 7075 aluminum alloy was investigated. As received 7075 alloys in T6 temper condition were retrogressed at 170, 220, 240 and 380°C for different durations between 15 s and 60 min. Subsequent reaging was made at the T6 aging condition. Treated materials exhibited higher hardness and better stress corrosion cracking resistance than T6 temper in a wide range of retrogression temperature and time. The highest hardness was obtained after retrogression at 170°C for 210 s followed by reaging, corresponding to 20% hardness improvement. Improvement in stress corrosion cracking resistance of the alloy by as much as 85% was also observed. In this paper, improvements in hardness and stress corrosion cracking resistance are discussed on the basis of the microstructural changes during retrogression and reaging treatment.

Jan 1, 2006

By Pengfu Tan

A program ?SlagVis? has been developed to simulate the liquidus temperature, phase compositions and viscosities of ZnO-CaO-SiO2-Al2O3-?FeO? slag, such as Imperial Smelting Furnace (ISF) slag and lead blast furnace slag, combined with F*A*C*T slag database and the mathematical model of slag viscosities based on a modified Urbain formalism. The modeling results have been validated by a number of measurements. The effects of slag compositions on viscosities of ISF slag and lead blast furnace slag have been simulated and discussed.

Jan 1, 2005

By I. Gaballah

Jarosite contains up to 15 % of heavy metal compounds 'HMC'. The current waste disposal methods will not be allowed in the near future due to new environmental regulations and pollution risks. For these reasons, thermal treatments of raw or decomposed jarosite, in controlled atmospheres, were investigated. The aim of these treatments is to decontaminate the jarosite and/ or to recover the HMC for recycling. According to physico-chemical characteristics of the samples, the thermal treatments in controlled atmospheres N2, CO+N2 and C12+air lead to the extraction rate that vary from 93 to 98 %. Heavy metal compounds were separated by cooling the gaseous phase. The treatments' residue was almost free from HMC. Between 700 "C and 800 "C, the chlorinating treatment was successful of eliminating more than 97 % of HMC contained in four different samples.

Jan 1, 1999

By Guangqing Zhang

The paper presents results of a systematic study of synthesis of titanium oxycarbide and its chlorination. Titanium oxycarbide was produced by carbothermal reduction of titania in hydrogen, argon and helium. Formation of titanium oxycarbide started at 1200°C in all gases. The reduction was the fastest in hydrogen. Formation of titanium oxycarbide in hydrogen was close to completion in 120 min at 1300°C, 60 min at 1400°C and less than 30 min at 1500°C. Reduction in argon and helium progressed at a similar rate and reached 90-95% after 300 min at 1400-1500°C. The chlorination of titanium oxycarbide was ignited at 150-200°C. Chlorine partial pressure and gas flow rate strongly affected the chlorination rate. Chlorination of titanium oxycarbide produced with carbon to titania molar ratio 2.5 at 235-400°C was close to 100% in 30 min.

Jan 1, 2009

By Juliana Gutiérrez-Paredes

Keywords: Slag, chromium oxide, recovery, stainless steel Experimental and theoretical work was performed to estimate the effect of slag basicity and amount of reducing agents on the reduction of chromium oxide from the slag which interacted with molten steel at 1600°C. The slag system contained CaO, MgO, SiO2, CaF2 and Cr2O3 together with Fe-alloys (Fe-Si and Fe-Si-Mg). The CaF2 and MgO contents in the slags were 10 mass % each; Cr2O3 was 25%. The amount of the ferroalloys ranged from 12.5 to 50 g per 100 g of slag. The (CaO+MgO)/SiO2 ratio was held at 1 and 2. The Cr yield was determined using both Fe-alloys as reducing agents. Some estimations were made to determine the theoretical effect of temperature, slag basicity, (CaO+MgO)/SiO2, and amount of reducing agents in the slag on the chromium recovery. The FACT (Facility for the Analysis of Chemical Thermodynamics) computational package is used to determine the equilibrium between the slag and molten steel.

Jan 1, 2005

By Sergio Neves Monteiro

This work had as its objective the characterization of a waste material, steel slag, generated from an integrated steel plant, with a view to its recycling and incorporation into red ceramics fabrication. The characterization was performed in terms of chemical composition by X-ray fluorescence (XRF), particles size distribution, X-ray diffraction (XRD), thermal analysis (DTA/TG) and scanning electron microscopy (SEM). The results indicate that the steel slag presents high amount of Ca, Fe, Mg and Si. The weight loss of the steel slag at temperatures above 800oC is associated with calcium carbonate decomposition. The coarse particle size of the steel slag is inadequate for its direct recycling into red ceramic fabrication. It is necessary to screen or to grind the waste. As a possible solution, it is suggested that screening or grinding the steel slag to a convenient particle size distribution would allow its successful industrial incorporation into red ceramics products.

Jan 1, 2006

By Ryan Walton

The Flash Converting Furnace at Kennecott Utah Copper converted over 465kmt of high-grade matte in 2002 but was restricted due to low matte production to 395kmt in 2003. This paper presents updated operational performance data and describes improvements implemented since the mid 2001 rebuild. Matte burner feed distribution, silica and arsenic impacts on settler lime-based slag operability, blister laundering, uptake/boiler accretion control, and dust sulfation will be discussed, as well as current development requirements dictated by operational imperatives and furnace modification plans.

Jan 1, 2005

By Oliver Zach

To know as much as possible about the condition of the refractory material (lining thickness, slag layer, build ups, ...) in an high temperature furnace is very important due to the safety and economic impacts. The new CONSCAN system offers the possibility to measure the inner surface of an furnace, and based on this results to calculate the thickness of the refractory lining, slag layer, build ups,.... The CONSCAN System provides this results as figures and graphics. This system is also working under hot conditions so it is not necessary to cool down the furnace. Based on these results the process control and the refractory lining concept could be optimized for maximum campaign life of the furnace.

Jan 1, 2006

By Thomas Weyand, Thomas Claridge, Dale Nickels

"This paper addresses the initial results of a project to evaluate the suitability of copper mining tailings as raw material for the production of structural products using PMET’s patented technology. Preliminary testing indicated that high performance structural products were possible using these materials. A demonstration scale project produced approximately 1,500 bricks in various colors. These products fall under under ASTM C- 73 and were found to present properties suitable for severe weather applications. Although the products in this project were of typical brick dimensions, other products are possible, for example concrete block substitutes or pavers. These products from the PMET process are commercially known as Brixx. This paper will provide operational details of the production process, mineralogy and mechanical properties of the products.INTRODUCTIONPMET has developed process technology that can convert various siliceous waste materials into competent structural products. This technology is the subject of US patent # 6,068,803. In general, the process consists of mixing lime, water and the major feed stock, pressing to form a “green” shape, and curing the product in an autoclave for 6 hours with saturated steam at ~200oC. The curing process forms Tobermorite, which acts as a crystalline binder. Freeport-McMoRan approached PMET to see whether mine tailings from the Sierrita mine, containing significant amounts of clay, might be a suitable feed material for the production of structural products. “Brixx” is the commercial term used to describe the resultant structural product formed in the test work. This paper is a preliminary evaluation of a technology that is being considered by Freeport-McMoRan. This report is not an endorsement by Freeport-McMoRan of the process or products, nor is it a commitment to use this technology."

Jan 1, 2008