Search Documents

By C. A. Zapffe

BOTH the foundryman and the theoretical metallurgist are now generally agreed that the anomalous "rising" or "bleeding" of certain ferrous castings of killed metal is primarily attributable to hydrogen. How and why the phenomenon occurs, however, have not been made clear. The following discussion is intended to harmonize foundry experience with metallurgical theory so that the foundryman may possibly improve his ability to prognosticate whether a certain casting may bleed or not. BLEEDING, RISING, AND PIPING The "rising" to be discussed here is not to be confused with the action in rimming ingots as a result of the carbon-oxygen reaction, although a conclusion will be drawn that may apply to the art of controlling the rimming action. Only killed metal is considered, which includes both steels and irons. In Fig. I, three killed, chill-cast ingots are shown: a porous ingot whose evolution of gas during late stages of solidification has ejected metal through the top; an ingot in which moderate gas evolution during solidification has lifted the mushy central metal, i.e., it has "risen"; and, third, a sound ingot with good piping characteristics. The first type is referred to as "bleeding," and generally infers that a solid skin had first formed through which the liquid metal later erupted. There is no fundamental distinction between bleeding and rising in reference to killed metal.* POROSITY Hydrogen appears as a cause of bleeding because the gas evolution simultaneously leaves a porosity of a type traceable to hydrogen. Twenty years ago, Melmoth1 noted that killed steel that rose unexpectedly in the mold, if returned while liquid to the furnace and heated further under a reducing lime slag, would again rise in the mold; but that if the ingot were allowed to solidify and was then remelted no rising occurred. A critical quantity of the responsible gas is therefore removed by the rising action. Melmoth associated rising with high silicon (0.7 to 0.9 per cent) and concluded that silicon increased gas absorption. Because silicon is a strong deoxidizer, oxygen must, therefore, be eliminated from consideration of the three common gases in steel-oxygen, nitrogen, and hydrogen. Butterworth2 later decided that pinhole porosity was caused by gases dissolved in the metal and that hydrogen was obtained from steam in the mold. Allen's classical work on copper castings,3 soon followed by

Jan 1, 1942

By J. F. Smith, J. E. Davison

The heat capacity of CaMg2 was measured over the temperature interval, 4.8° to 287°K, by the technique of low-temperature adiabatic calorimetry. Heat content measurements were performed with a drop calorimeter over the temperature interval, 273" to 673°K. From these data the thermodynamic functions, (FT - H0)/T, ST - So, and & - Ho, were evaluated. A third-Law calculation of the standard entropy of formation of CaMg2 yields a value of -0.25 * 0.06 cal per (°K g-atom) , and the free-energy function derived from this study when combined with existing equilibria data yields a value for the standard enthalpy of formation which is in agreement with direct calorimetric enthalpy measurements. The accompanying paper' shows that the enthalpy of formation of CaMg2 has been determined with good precision by three different calorimetric techniques.'-= TWO independent determinations of the Gibbs free energy of formation of CaMg2 have also been made; both determinations were based on vapor pressure measurements, being in one case hydrogen vapor pressures over ternary Ca-Mg-H alloys4 and in the other case magnesium vapor pressures over binary Ca-Mg alloys.5 The present determination of heat capacity of CaMg2 below room temperature and of the heat content of CaMg2 above room temperature was undertaken to provide supplementary data. These data are useful in their own right but can in addition be used to evaluate an entropy of formation for CaMg2 which, because of the interrelation of free energy, enthalpy, and entropy, can be used as a check of the self-consistency of the composite of the presently available information. LOW-TEMPERATURE HEAT CAPACITY The heat capacity of CaMg2 was measured over the temperature interval 4.87° to 286.64°K in an adiabatic calorimeter. The physical details of the calorimeter and the experimental procedure for measuring the heat capacity of a specimen have been adequately described by Gerstein et a1.6 The source and purity of the calcium and magnesium are described together with the methods of sample preparation and chemical analyses in the accompanying paper.' Results of chemical analyses of the material which was used in the present investigation are shown in Table I. These analyses show that, on the basis of the published phase diagram,7 the heat capacity sample contained a slight excess of a calcium while the heat content sample contained a slight excess of magnesium. However, in both cases the excess was small, and X-ray diffraction patterns showed reflections which were without exception attributable to CaMg2. The sample which was used for heat capacity measurements weighed 69 g while the sample container and addenda weighed 132 g. The sample was in the form of annealed powder, 50 to 60 mesh, and was sealed into the sample container under 0.1 atm of helium. Copper fins inside the sample container facilitated thermal equilibrium of the powdered Sample. Time intervals of the order of 10 min were required for thermal equilibration, and such times are normal for this calorimeter regardless of the form of the sample. The observed heat capacities were corrected for the small excess of a calcium through use of the heat capacity values tabulated by Hultgren et a1.8 The corrected heat capacities are tabulated as a function of temperature in Table II. The free-energy function and the absolute entropy of CaMg2, which were calculated from the experimental heat capacity data, are listed in Table 111. A smooth curve was fitted to a plot of the experimental values of the heat capacity and in only two instances above 30°K did the plotted points deviate from the curve by more than 0.2 pct. Below 10°K the deviation of several of the points was as much as 50 pct. These large percentage deviations were attributed to the small value of the heat capacity and to the low sensitivity of the platinum resistance thermometer in this temperature range. The deviations in the region of 10°to 30°K were less than 5 pct. Although the percentage deviations of some of the low-temperature measurements are large, the actual value of these deviations is small since the magnitude of the heat capacity in that temperature range is small. The error in the value of the third-law entropy at 298.15°K was estimated to be less than 0.01 cal per (°K g-atom). A value of -0.25 ±0.06 cal per (°K g-atom) was obtained for the standard entropy of formation at 298.15°K from the relation:

Jan 1, 1969

By F. A. Olson, J. S. Cho, M. E. Wadworth

An infrared study of the states of hydration of MgSO4 revealed a hitherto unreported metustable dehydration state in the temperature range just below that of the stable anhydrous salt. Infrared, thermogvavimetric, and X-ray studies indicated that the state had bisulfate and hydroxide characteristics. A formula fitting all of the experimental evidence is hydrogen-bonded Mg(OH)HSO4, or possibly the chemically equivalent 1/2 Mg(HSO4)2. Mg(OH)2 Infrared spectra of the 7, 6, 1, and OH2O states of hydration are given as well as the spectra of the newly found state which is called the bisulfate state in this paper. Thermogvavimetric studies as a function of water-vapor pressure gave an enthalpy value of 16 cal per mole, and 25 eu for the conversion of the bisulfate state to that of the anhydrous salt. The free energies of the transition varied from 1.76 to 0.18 kcal per mole as the transition temperature varied from 279° to 336°C. The bisulfate state is believed to be of importance in catalytic dehydration phenomena using MgSO4 and may be of interest because of properties in sulfating reactions differing from those of the monohydrate. Also, an analogous state may exist as a hydration state of other sulfates. ANHYDROUS magnesium sulfate is a catalyst with a high degree of specificity for the dehydration of secondary alcohols.1'2 The only product obtained at the usual operating temperature range of 360" to 400°C other than the corresponding olefin is water. Thus, the bonding of water to the anhydrous salt as well as an understanding of the hydration states of MgSO4 became of interest in attempting to understand the catalytic mechanism better. In the process of this study using infrared, X-ray, and thermogravimetric analyses a dehydration state not previously reported was found. Proof of its existence, the nature of the state, and its role, if any, in the catalytic mechanism then became of interest. This paper is concerned principally with the first two aspects of this problem. Magnesium sulfate forms many hydrates, of which the monohydrate and heptahydrate (Epsom salts)3 are most important. Other hydrates4 are known with 1-1/4,5 l-1/2, 5 2, 4, 5, 6, and 12 H2O's. The hydrates with 1-1/4, 1-1/2, 2, 4, and 5 HzO's are unstable. The anhydrous salt is very stable thermally and has a strong affinity for water. It can be heated without additional decomposition to about 800°C.' At 900°C noticeable decomposition takes

Jan 1, 1964

By AIME

NEW YORK'S largest hotel, the Pennsylvania, will be filled with mining and oil men and metallurgists the third week of February when some 3000 AIME members, their wives, and guests will gather for the Institute's 1948 Annual Meeting-its 166th general meeting. Except for the usual Sunday afternoon and evening sessions of the Mineral Industry Education Division at the Columbia University Men's Faculty Club, the big assembly will be under one top and members will not this year have to consult compass and map to find their next session. Possibly enervated by the stupendous effort of the Anniversary Celebration last spring and the plethora of highly successful fall meetings, the various committees have been a trifle slow in arranging their social and technical programs, but in mid December as we go to press there is already much to report indicative of substantial fare and high interest. The definite timetable schedule will appear in the February M&M.

Jan 1, 1948

By R. E. Shinkosk

This paper outlines the development of a program for increasing the life of woolen bags used for filtering Dwight-Lloyd gases by treating the bags and gases with hydrated lime. Methods and apparatus are described for determining alkalinity of dusts, acidity and breaking strength of bag cloth. Procedure and results, based on several years of operation, are presented. DURING 1939, additional facilities were constructed in the Dwight-Lloyd Blast Furnace and Baghouse departments at the Selby, California, Plant of the American Smelting and Refining Co. In order to handle adequately the increased volume of gases from the resultant increase in production, it was necessary to increase gradually the amount of water used for cooling gases ahead of the sinter machine baghouse. As a result of this increased water cooling, the average bag life dropped from 27 months in 1939 to 14 months in 1941. (Table I). This drop in life meant an increased. bag cost, as well as lower recovery of dust and some curtailment of operation. During 1941, it was found new bags showed as high as 0.3 pct acidity* after two weeks of opera- tion and as much as 2.0 pct acidity after some months of operation. This high acidity was present in spite of the fact that free oxide or relative alkalinity of the unburned dust ran from 5 to 6 pct. In view of these circumstances, a twofold program was started in Nov. 1941.t Part one of this program consisted of vigorously dipping all new bags in a weak lime solution, containing 50 lb of hydrated lime per 50 gal of water. Part two consisted of feeding fine, dry, hydrated lime into the gas stream intake of the sinter baghouse fan. Apparatus for feeding this lime is shown in fig. 1. All baghouse chambers are shaken in rotation about once each hour. On alternate hours, the baghouse operator places 50 lb of hydrated lime (one sack) into the lime feeder, starts feeder and immediately starts the bag shaking machinery. The rate at which lime is fed is set to coincide with the approximate time necessary to shake all sinter bag-house chambers, or about 15 min. It is felt this method of lime addition is most effective for getting lime into the woolen bag fabric. The amount of lime so fed averages about 600 lb per day. The amount of lime fed per day is varied to keep a minimum relative alkalinity of 9 pct in the unburned sinter dust. A daily dust sample is taken for alkalinity by allowing dust to accumulate in a sample pipe over a 24-hr period. This sample pipe, placed in any chamber cellar, is 2 in. in diam, 4 ft long, is sealed on the inner end, and capped on the outer end. It has a 1/2 in. slot cut for 18 in. along the tip end. This slot faces upward and allows the pipe to fill gradually with dust as bags are shaken. Breaking strength of bags has, in most cases, been the deciding factor in bag replacement. Bags that normally test 100 psi breaking strength when new are replaced when they test under 35 lb. The method for determining breaking strength is shown in the description accompanying fig. 2. Since the start of the liming program in 1941, bag life has increased from 14 months to an average of over 23 months, with a consequent material decrease in bag cost per year. Acidity, as per cent sulphuric acid, may be determined by means of a Beckman pH meter as follows: From a piece of bag cloth. which has been thoroughly cleaned of dust, a 5 g sample is weighed on a balance. Cut the sample into fine pieces and place in a 400 cc beaker. Add 100 cc (measured) of distilled water and stir vigorously. Filter on suction funnel, holding cloth pulp in beaker with a stirring rod. Wash cloth sample and filter wash water four additional times, each time with 20 cc distilled water, the last time squeezing cloth pulp over funnel. Discard pulp and rinse funnel and filter paper. Pour wash solution jnto measuring graduate and make up to exactly 300 cc with distilled water. Place into clean 600 cc beaker and measure the pH on meter. The per cent acid in bag cloth is read from the following table:—

Jan 1, 1951

By G. A. Parks, C. Kovacs

The xanthate flotation of chrysocolla can be improved by preheating the ore to 500° to 600°C. Addition of water vapor reduces the preheating temperature required. The temperature range of flotation improvement correlates well with the range over which dehydroxylation occurs. This observation is consistent with changes in the structure and properties of the mineral as detected by measurement of solubility, D.T.A., T.G.A., X-ray diffraction, and infrared absorption and with recently proposed explanations of chrysocolla flotation. A brief experiment by one of the authors several years ago showed that exposure of chrysocolla to high temperature water vapor resulted in increased recovery by subsequent xanthate flotation. Recently renewed interest in flotation and thermal properties of chrysocolla1-5 prompted further study of this effect and more detailed reporting.6 This paper explores the response of pure chrysocolla recovery in Hallimond tube flotation tests to the time and temperature of exposure and to changes in the water vapor pressure. Brief attention is paid to the effects of such treatment on accessory minerals. A single experiment with flotation of chrysocolla from an ore is reported. MATERIALS Chysocolla from Inspiration, Gila County, Ariz. was crushed in a porcelain mortar, cleaned of visible and magnetic impurities, and screened to obtain -48 +65 mesh (Tyler) material for flotation test work. The clean material contained 28.5% Cu and was identified as chrysocolla by comparison of X-ray diffraction, D.T.A., and infrared absorption data with that reported for similar materials by others.4,5,7 Samples of malachite and chalcopyrite, prepared in a similar way, were also identified by X-ray diffraction. The sources of these materials are unknown. A sample of chysocolla-bearing oxidized copper ore from Pima, Ariz. was crushed and dry ground for thermal activation and subsequent flotation. PROCEDURES Activation: The apparatus used for exposure of materials to high temperature water vapor is illustrated in Fig. 1. The furnace temperature was controlled to ±5°C Water vapor pressure was controlled by pre-saturating a nitrogen carrier stream with water in an adjustable thermostatted saturator (multiple bubbler). A water manometer and capillary orifice flow meter were used to measure nitrogen flow rates for activation and for subsequent Hallimond tube tests. Gas flow rate and temperature were adjusted prior to introduction of samples. Exposure time was measured from the moment of introduction of the sample to the furnace, hence includes an initial drop below the control temperature. After heating, the samples were removed from the furnace and stored at room temperature in air. Representative samples of activated materials were examined by X-ray diffraction and infrared absorption.

Jan 1, 1967

By J. S. Bowles

THE martensite transformation in lithium, dis- covered by Barrett,' has been studied extensively by X-ray techniques by Barrett and Trautz,² and Barrett and Clifton.V he present paper reports the results of an investigation into the metallographic characteristics of lithium martensite. Such an investigation has not been carried out before. The spontaneous transformation in lithium consists of a change from a body-centered cubic to a close-packed hexagonal structure with the hexagonal layers in imperfect stacking sequence." As far as is known at present, this transformation can be regarded as being crystallographically equivalent to the body-centered cubic to close-packed hexagonal transformation that occurs in zirconium,5 although stacking errors have not been reported in zirconium. From a study of the orientation relationships in zirconium, Burgers5 as proposed that the martensite transformation, b.c.c. to c.p.h., occurs by a heterogeneous shear on the system (112) [111]. The crystal-lographic principle underlying this proposal is that the configuration of atoms in the (112) plane of a b.c.c. structure is exactly the same as that in the (1010) plane of a close-packed hexagonal structure based on the same atomic radius. The pattern in 2v2 both these planes is a rectangle d X 2v2d where v3 d is the atomic diameter. Thus a close-packed hexagonal structure can be built up from a body-centered cubic structure by displacing the (112) planes relative to each other.* This mechanism leads to orientations that can be described by the relations: (110)b.c.e. // (0001)c,p.h.; [111]b.c.c. // [1120]c.p.h Observations confirm these relations. In zirconium, Burgers' measurements indicated an angle of 0" to 2" between the close-packed directions, while Barrett's measurements on lithium indicated an angle of 3". According to the Burgers' mechanism, the martensite habit plane for this transformation would be expected to be the (112)b.c.c. plane, for this plane would not be distorted by the transformation. One of the purposes of this investigation was to find out whether the observed lithium habit plane agrees with this prediction of the Burgers' mechanism. Experimental Procedure Materials: The lithium was from the same purified ingot used by Barrett and Trautz.² The Bridgman technique was used to produce single crystals. To maintain a temperature gradient in the melt, during the production of these crystals, it was necessary to use a steel mould with a wall thickness of only 0.015 in. Metallographic Techniques: Lithium specimens could be given an excellent metallographic polish by swabbing them gently with cold methyl or ethyl alcohol.? The best results were obtained with methyl alcohol saturated with the reaction product, lithium alcoholate. With higher alcohols the reaction became progressively slower and the attack became an etch pit attack rather than a polish attack. Butyl and amyl alcohols were used for macroetching. After polishing, it was necessary to remove all traces of alcohol from the specimens; otherwise, on subsequent quenching in liquid nitrogen, the alcohol froze to a glassy film. The alcohol was removed with dry benzene. The benzene in turn had to be removed before quenching, but since it does not react with lithium it could be allowed to evaporate. The specimens could then be quickly quenched before they began to tarnish. This operation could be carried out in air on all but excessively humid days when it was advisable to use an atmosphere of dry nitrogen or argon. For examinations at room temperature, the specimens could be transferred directly from the benzene bath into a bath of mineral oil. In mineral oil the specimens oxidized slowly by the diffusion of oxygen through the oil but the structure remained visible for about an hour. Lithium Martensite: Specimens prepared in the manner described above transformed spontaneously to martensite with an audible click when quenched into liquid nitrogen; i.e., M, was above the boiling point of nitrogen (77°K). The disparity between this result and the M, temperature of 71°K, found by Barrett and Trautz, is probably to be attributed to the large grain size and freedom from mechanical deformation of the specimens used in the present work. The relief effects produced by the transformation did not disappear when specimens were quenched from liquid nitrogen into mineral oil at room temperature. This permitted the microstructures to be studied at room temperature where, of course, the martensitic phase was no longer present. Typical micrographs of lithium "martensite" made at room temperature are reproduced in figs. 1, 2, and 3. As anticipated by Barrett and Trautz, the microstruc-

Jan 1, 1952

By B. Post, F. W. Glaser

Three borides of zirconium have been reported: ZrB,l ZrB2,2,3 and ZrB12, 4 The phase relationships, ranges of stability, and some physical properties of these compounds are described. THE zirconium borides differ considerably from one another, particularly with respect to their relative stabilities at high temperatures in the presence of carbon.4,5 ZrB2 is extremelv stable at all temperatures (to the melting point) in contact with carbon. Both ZrB and ZrB12 tend to decompose at elevated temperatures when carbon is present in excess of about 0.5 pct. ZrB forms ZrB2 and ZrC, and ZrB12 decomposes to form ZrB2 and a boron-carbide phase. In the ZrB12 preparation, boron present in excess of that needed to form ZrB2 reacts with carbon, if present, to form carbides, in preference to forming the higher boride. Similar instability of borides, other than diborides of the transition metals of the 4th and 5th groups of the periodic table, has been reported.5,6 special precautions had, therefore, to be taken to minimize carbon contamination in the preparation of ZrB and ZrB12. Reactions below 1400°C were carried out by heating powdered mixtures of zirconium hydride and boron in quartz tubes in a hydrogen atmosphere. For temperatures above 1400°C, reactions were carried out in graphite molds. Carbon contamination from the molds was minimized by employing extremely rapid heating rates to reduce carbon diffusion into the body of the specimen, and by subsequent "shaving" of sample surfaces that had been in contact with the graphite dies. A heating rate of about 2000°C per min was obtained by heating the dies (by direct conduction), using a current of 40,000 amp. Although this type of heating cycle apparently allowed little time for "homogenization," close approximations to equilibrium conditions were usually obtained as a result of the very strongly exothermic reactions between zirconium hydride and boron at elevated temperatures. Reproducibility of results in repeated runs under varying conditions was taken as a reasonable indication that equilibrium conditions had been effectively achieved. Quenching was accomplished by rapidly immersing the entire die, containing the reaction products, in water. Specimens could also be cooled at controlled rates by adjustment of the rate of flow of water through the water-cooled copper electrodes in contact with the graphite dies.

Jan 1, 1954

By G. H. Bishop

The kinetics of the inter granular penetration and embrittlement of [100] tilt boundaries in 99.998 pct pure nickel upon exposure to bismuth-rich Ni-Bi liquids have been determined in the temperature range from 700° to 900°C. The kinetics of penetration are parabolic in time at constant temperature over most of the temperature range. In a series of 43-deg bicrystals the rate of penetration is anisotropic with respect to the direction of penetration into the grain boundaries. In lower-angle bicrystals the penetration rate is isotropic. The rate of penetration decreases with tilt angle at 700°C. The activation energy for penetration in the 43-deg bicrystals is 42 kcal per g-atom independent of direction. It is concluded that the intergranular penetration and embrittlement in the presence of the liquid proceeds by a grain boundary diffusion process and not by the intrusion of a liquid film. This was confirmed by a determination that the kinetics of penetration and embrittlement were the same in the 43-deg bicrystals upon exposure to bismuth vapor under conditions such that no bulk liquid phase would be thermodynamically stable. WhEN solid metals are exposed to a corrosive liquid-metal environment, the grain boundaries are sites of preferential attack. Depending on the temperature, the composition of the liquid, and the composition, structure, and state of stress of the solid, a number of modes of attack are possible. This paper reports a study of the kinetics of intergranular penetration and embrittlement of high-purity nickel bicrystals upon exposure to bismuth which, together with an earlier study by Cheney, Hochgraf, and Spencer,&apos; demonstrates that there are at least two modes of intergranular attack possible in the Ni-Bi system. In the study by Cheney et al., columnar-grain specimens of 99.5 pct pure nickel were exposed to liquid bismuth presaturated with nickel in the temperature range 670" to 1050°C. They found that the majority of the boundaries, which were predominantely high-angle boundaries, were penetrated by capillary liquid films, the attack proceeding by a process which will be termed grain boundary wetting. This process occurs in a stress-free solid when twice the liquid-solid surface tension is less than the surface tension of the grain boundary,* i.e., when 2yLs < YGB In this case the penetration of the grain boundary by the liquid occurs at a relatively rapid rate, resulting in the severe embrittlement of a polycrystalline solid. Grain boundary wetting is a common mode of intergranular attack in systems in which the lower melting component is relatively insoluble in the solid, but the solid has an appreciable solubility in the liquid, for example, the Ni-Bi system, Fig. 1. In systems of this type at temperatures above the range of stability of any intermetallic phases, once the liquid is saturated with respect to the solid so that no gross solution occurs, chemical gradients are small, and surface tensions become major driving forces for attack, provided the solid is stress-free. The results of Cheney et al. appear to be typical of those encountered when grain boundary wetting occurs.&apos; Capillary films were observed in the boundaries after quenching from the exposure temperature. The mean depth of penetration increased linearly with time, and the activation energy for the process was found to be 22 kcal per g-atom. In a study of the Cu-Bi system Yukawa and sinott4 found that the depth of penetration of bismuth into high-purity copper bicrystals of orientations from 22 to 63 deg of tilt about (100) at 649°C ranged from 0.05 to 0.25 in. after a 12-hr anneal. This corresponds to a linear rate of 6 to 15 X 10~6 cm per sec. At the same reduced temperature of 0.68 the rate for the Ni-Bi system&apos; was 7 x lo-&apos; cm per sec. In another study of the Cu-Bi system, Scheil and schess15 determined the kinetics of grain boundary wetting in hot-worked commercial rod. While there were several complicating factors present in this study, there is general agreement with the above results. The kinetics of penetration were linear, the activation energy was 20 kcal per g-atom, and at 650°C the rate of wetting was 2 to 5 x 10-6 cm per sec. The rate of wetting in the A1-Ga system6 is somewhat

Jan 1, 1969

By A. U. Seybolt

The solubility limit of oxygen in columbium has been determined in the range between 775&apos; and 1100°C by means of lattice parameter measurements and microscopic examination. The solubility is a function of temperature and varies, in the range given above, from 0.25 to 1.0 pct O, respectively. BECAUSE of the marked deleterious effect of oxygen upon the mechanical properties of some of the transition metals, it is desirable to know something about the solubility of oxygen in these metals. The brittleness caused by oxygen in solution is particularly marked in the case of the group VA elements, vanadium, columbium, and tantalum. The solubility of oxygen in vanadium has already been reported in an earlier paper,&apos; and Wasilewski2 has given a value (0.9 wt pct) for the solid solubility of oxygen in tantalum at 1050°C. Brauer3 in 1941 investigated the Cb-0 system up to Cb2O5, but made no real effort to investigate the extent of oxygen solubility in the metal. He made the observation, however, that this solubility must be less than 4.76 atom pct (0.86 wt pct) oxygen. This estimate was made from X-ray diffraction results on the alloys CbO, CbO, and CbO; all alloys consisted of the terminal (Cb) solid solution plus CbO, but the last alloy containing 4.76 atom pct 0 showed only three very weak CbO lines. It is surprising that Brauer, by examining only three alloys, arrived at an estimate of the solubility which agrees very well with the results to be reported herein. Experimental Procedure A columbium strip obtained from Fansteel Metallurgical Products was cut into strips, 0.020x1/2x2 in. Two holes, about 3/16 in. in diameter, were made near the ends of the strips in order to hold them against a flat steel block for mounting in a General Electric X-ray spectrometer for lattice parameter measurements. The same holes were used to hang the specimens inside a fused silica vacuum furnace tube which was part of a Sieverts&apos; gas absorption apparatus. The apparatus and method of adding oxygen gas has been previously described.1 According to the supplier, the columbium obtained had the analysis given in Table I. After degreasing the samples, approximately 0.001 in. was etched from each side of the samples in order to remove possible surface impurities from the last rolling operation. For this purpose the following cold acid pickle was found satisfactory: 8 parts HNO3, 2 parts H2O2 and 1 part HF. Various Cb-O compositions were obtained up to 0.75 wt pct O by the gas absorption and diffusion technique. After the sample had absorbed all the oxygen gas added at 1000°C, an additional 24 hr was allowed for homogenization. This treatment appeared to be adequate, as shown by the linearity of the lattice parameter-composition plot. More concentrated alloys were prepared by arc melting mixtures of Cb and Cb2O5 since it was very time-consuming to make Cb-0 alloys in the neighborhood of 1 pct O, or over, by the diffusion method. When the flat strip specimens were used, they were ready for the X-ray spectrometer after cooling from the Sieverts&apos; apparatus. The cooling rate obtained by merely allowing the hot fused silica furnace tube to radiate to the atmosphere (when the furnace was lowered) was sufficiently fast to keep the dissolved oxygen in solution. Arc-melted alloys were reduced to —200 mesh powder in a diamond mortar, wrapped in tantalum foil, sealed off in evacuated fused silica tubes, and then heat treated as indicated in Table 11. The fused silica tubes were quickly immersed in cold water without breaking the tubes after the heat treatments. The tantalum foil prevented reaction between the fused silica and the sample; there was no reaction between the powdered samples and the foil at 1000°C, but some trouble was experienced at 1100°C. At this temperature level a reaction between the sample and the foil was sometimes observed, which resulted in erroneous parameter values. Experimental Results Hardness Tests: Since most of the X-ray samples were in the form of flat strip, it was convenient to obtain Vickers hardness numbers as a function of oxygen content. Compared to the V-O case,&apos; oxygen hardens columbium much more slowly, presumably because of the larger octahedral volume in colum-bium (about 12.0 compared to 9.3Å3 in vanadium), hence, requiring less lattice strain for solution. The plot of VHN vs wt pct O is shown in Fig. 1.

Jan 1, 1955

By Robin O. Williams

Robin 0. Williams (Oak Ridge National Laboratory)— The authors have questioned the degree to which the coherency strains between the iron-rich and chromium-rich phases are isotropic as proposed in Ref. 5 on the basis of the difference between the elastic properties of the two phases. The relative magnitude of the stresses is determined by the moduli as shown by Eqs. [2], [3], and [4] of Ref. 34. However, the moduli of the two phases have no direct bearing on the uniformity of either the stress or strain within either phase. The idea that the strains are isotropic within each phase (but normally of different magnitude and always of different sign) is based entirely upon the experimental observation that X-ray line broadening has not been detected even when the particles become rather large. It has not proven possible to grow the particles sufficiently large that they lose coherency. Based upon this lack of line broadening one can estimate an upper limit for the nonuniformity of the strains within each phase as follows. It is considered possible to detect line broadening if it is as great as 10 pct of the separation of the K, doublet for the (211) line using chromium radiation. The doublet separation would correspond to a total strain of 0.0017 such that the total variation of lattice parameter relative to the average lattice is now k0.05x0.0017 or something less than ± * For the present case the strain in each phase is roughly 0.002 such that the variation of strain within a phase will not exceed 5 pct. It is stated that the expression derived for strengthening for the hydrostatic straining as observed in this system would substantially overestimate the magnitude due to dislocation flexure. This is contrary to the conclusion reached in the original paper34 for the present range of particle sizes. What is the lowest temperature at which a has been observed to form in this alloy? M. J. Marcinkowski, R. M. Fisher, and A. Szirmae (nutlzors&apos; reply)— -Williams&apos; arguments based on X-ray findings for a chromium-rich precipitate and an iron-rich matrix strained to a common lattice parameter are certainly convincing. This being the case, there are no shear components of strain associated with the precipitate-matrix aggregate to interact with the shear components of the dislocation stress fields, contrary to the opinion expressed by the present authors. On the other hand, the present authors, in spite of this error, did not expect the shear interactions to be significant. The chief objection to Williams&apos; model in the present case is that the various segments of the dislocation line are assumed to pass from one potential valley to the next independently of neighboring segments. This is only true for a highly flexible dislocation line, i.e., one whose radius of curvature is something less than the center to center distance between precipitate particles which amounts to about 90A in the present alloy. In order to maintain this curvature, an externally applied shear stress of at least 230,000 lb per sq in. would be required or about four times the observed stress. It is therefore concluded that the dislocation lines move rather rigidly through the lattice. This being the case, the forces on the dislocation resulting from the hydrostatic interaction between the stress fields of the edge-dislocation components and the precipitate particles should average out to zero; that is particles above the below the slip plane produce forces on the dislocation of opposite sign and therefore will cancel when averaged over the entire length of the dislocation. On the other hand, since the dislocation is not perfectly rigid, Williams&apos; model may lead to some strengthening, but far less than that predicted. A second and equally serious objective to using Williams&apos; strengthening model for the present alloys is that profuse wavy slip due to the motion of screw dislocations played a predominant role not only in the unaged alloys but in the fully aged ones as well. Since the screw dislocation has associated with it only shear components of stress the hydrostatic strengthening model no longer applies. In view of these arguments the present authors must reject Williams&apos; model of strengthening as being pertinent to the present alloy system. The present authors have made no detailed study of the lowest temperature at which a forms in the quenched ferritic alloys. None was ever observed n the alloys aged at 500°C so that forma-tion must occur at temperatures higher than this and was therefore not a factor in the present study.

Jan 1, 1965

By D. R. Miller

Internal friction and elastic modulus variations in electrorefined titanium, iodide refined titanium, and alloys of the latter material with oxygen, nitrogen, aluminum, and zirconium were investigated. No oxygen peak was detected with electrorefined titanium but, provided precautions were taken to prevent increases in background damping, an oxygen peak at about 410°C could be resolved with each of the other materials. An additional partially resolved peak was observed at 500°C in a Ti-N alloy. An anomaly in the variation of rigidity modulus with temperature was observed. Possible mechanisms for the formation of any oxygen peak have been discussed. PRATT, Bratina, and Chalmersl investigated the internal friction of commercial purity titanium and alloys of this material containing 1.5, 3.5, and 4.5 at. pct O. With commercial titanium the internal friction curve consisted of two components, a background which increased steadily with temperature and a peak at about 600" C which was due to grain boundary relaxation. In the Ti-O alloys, however, an additional internal friction peak was observed at 430" to 450°C and, since this peak increased in height as the oxygen content was increased, it was thought to be associated with the presence of oxygen. The diffusion of oxygen in titanium at temperatures between 300" and 500° C is believed to have marked effects in its tensile properties2&apos;3 and the present internal friction measurements were undertaken to obtain further information on this diffusion, using material of higher purity than that of Pratt et d. and an apparatus of very much greater sensitivity. In the course of the investigation a number of important limitations on the work of Pratt et al. were revealed and results have been obtained which emphasize the need for ensuring that in this type of experiment, internal friction is independent of strain amplitude and that the values obtained are reproducible. 1) MATERIALS AND APPARATUS The basis material from which the majority of the specimens was prepared was iodide-refined titanium, the major impurities in which were oxygen and nitrogen—the metallic impurities being present at concentrations less than 0.001 at. pct. The hardness of this material after arc melting, forging, and swaging to rods 1/4 in. diameter was Dph = 110. Specimens 10 in. long and 0.020 in. (0.51 mm) diameter were prepared from these rods by further swaging and wire drawing and were finally annealed in vacuo (5 x 10-6 mmHg) for 24 hr at 800°C. The oxygen alloys were prepared from iodide-

Jan 1, 1962

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth, W. L. Finlay

Titanium with up to 7.5 pct Al forms single-phase a alloys that are work hardening, not heat treatable, and ductile as welded. The high aluminum Y phase alloys are not usefully ductile, despite their low hardness, but they have excellent oxidation resistance and hot hardness. LITTLE has been published on the effect of aluminum on the mechanical properties of titanium, despite the fact that two of the first four commercial alloys released by titanium alloy producers contained aluminum as an important alloying ingredient. These were both a-ß type alloys, one containing 4 pct A1 and 4 pct Mn and the other containing 3 pct A1 and 5 pct Cr. However, neither of these alloys reflects the true alloying nature of aluminum, since each contains important amounts of the ß-stabilizing addition, manganese or chromium. In a previous publication on the constitution of Ti-A1 alloys,&apos; the authors showed that aluminum had a high solubility in a titanium and was strongly a stabilizing in nature. About 25 wt pct A1 is soluble in a titanium at room temperature. With as little as 5 pct added aluminum, the a transus temperature is increased from 882" to 970°C, and the correspond- ing ß transus to 995°C. The first intermediate phase in the Ti-A1 system is the ordered face-centered tetragonal TiAl phase, which extends from 34 to 46 wt pct Al. The present paper presents hardness data over the entire titanium-rich region of the system, through the TiAl phase, and mechanical property data on the alloy range capable of being fabricated. Methods of Investigation The materials used and general preparation of alloys, as well as experimental techniques used in the investigation of Ti-A1 alloys, have been adequately described.&apos; Briefly, the preparation consisted of arc-melting the desired amount of high purity aluminum (99.99 pct purity) and iodide titanium (maximum hardness 100 Vickers, as deposited) together on a water-cooled copper hearth under a partial pressure of argon. The resulting button ingot was of such form that it could be fabricated without further treatment. All work was done using ingots weighing 10 to 15 g, which were hot-rolled to strip form whenever possible. Tensile samples were 3.25 in. long, 0.5 in. wide, and 0.040 in. thick, with a reduced section 1.25 in. long by 0.250 in. wide. The gage length used was 1 in. Electrical strain gages mounted on the

Jan 1, 1954

By A. E. Bellis

The problem of heat treating high-speed steel becomes more and more important as the design of cutters becomes more and more complicated in increasing the efficiency of mechanical operations. Hundreds of dollars&apos; are spent in the design and manufacture-of milling cutters of special form ,for rapid production of duplicate or interchangeable parts, and then, as the heat treatment is faulty on the one hand, or scientifically executed on the other, the tool fails after a few operations, or its efficiency is greatly increased. The practical operation of giving these complicated tools the right temperature necessary to bring out the best cutting qualities, and at the same time bring the tool out "clean," is a difficult: one and calls for no small amount of skill. In order to be on the safe side, the average tool hardener uses a temperature much too low to give the best results with the high-speed steel he uses. In the case of cutters which are finished to a given diameter before hardening, it is impossible to grind the tool after hardening, so that it is essential that the surface be-protected from oxidizing or de-carbonizing. It is the aim of this paper to describe some experiments on hardening high-speed steel, in which metallographic means were used to determine the correct hardening temperatures. The accompanying table and plates show the results of hardening experiments on five different high-speed steels. The analyses for carbon, tungsten, chromium and vanadium of each steel are given in the accompanying table. Six specimens from the same bar :of each: kind of steel

Jan 1, 1917

By Arthur Notman

TO present some idea of the magnitude of the gold-mining industry of Canada and the world, the records of 106 gold-mining companies currently paying dividends have been studied. Forty of these are in Canada, and 37 on the Rand in South Africa, these being all the straight gold-mining companies that paid dividends in the two areas in 1938. None of the base-metal companies that produce gold as a by- product, or even as a major fraction of the value of their total product, have beezl included. In addition, a group of 29 similar companies from Southern Rhodesia and the Gold Coast in Africa, India, Australia, Manchuria, Philippine Islands, the

Jan 1, 1939

By AIME AIME

THE Seventh International Petroleum Exposition and Congress to be held in Tulsa, Okla., Oct. 4 to 11, inclusive, in true western spirit promises to be bigger and better than ever. The Exposition has become an established institution. It gives opportunity to petroleum engineers, technologists, and operators to see each year at one place what the tool makers and machinery manufacturers have to offer which is new or better. It has truly become a place "where men, methods and machinery meet." It is also a convenient focus for technical meetings of various kinds devoted to petroleum and natural gas problems. &apos;The Petroleum Division of the A. I. M. E. has for several years held its chief fall meeting at Tulsa just preceding the opening of the Es- position. This year our meeting will be on Oct. 2 and 3 and it will be held as usual at Hotel Mayo. The Mid- Continent Oil and Gas Association will, as usual, hold a meeting during the Exposition and this year the Petroleum Division of the A. S. M. E. will hold a three- day session, Oct. 6-8, in the auditorium on the Esposition grounds. In all, six technical sessions are planned by this Society, and aside from reports of committees some 20 technical papers are to be presented. Members of the Institute should attend its own meeting and stay over for as many days as possible for the other meeting at which they will hear and see much of helpful interest.

Jan 1, 1930

THE exhibits of mining equipment at the AMC Metal Mining Convention and Exposition will be the largest and most diversified ever shown to the metal and nonmetallic mining industry. Over 795 leading manufacturers have been assigned a total of 36,130 net sq ft of exhibit space - 49 pct more than the last such exposition. Following is a partial listing of exhibitors, the products they will show, and their representatives.

Jan 8, 1950

By Paul Sterling

The general impression regarding the preparation of merchantable anthracite is that it is confined to a colossal, grimy structure, called a " coal-breaker." This name is a misnomer; for the desired result is not to break the coal, but to prevent its being broken. Preparation may be said to begin at the face of the chamber, with the mining and loading of the coal. Local conditions vary, not only ill the same field or basin, but also in the same mine, so that there is no fixed empirical rule governing the method of blasting or cutting coal. Tests should be made, when possible, to determine the explosive, or the mechanical coal-cutter, which will produce the largest percentage of what are locally known as " lump " and " prepared sizes " of anthracite. The prepared sizes are those mostly consumed for clomestic purposes. All other sizes might be called by-products of the anthracite industry; for they are not especially desirable, being the degradation resulting from the mining and handling of a brittle or laminated material. Being low in volatile combustible matter, anthracite burns most successfully when nearly of a uniform size, permitting the easy passage of air through the voids. This accounts for the large number of sizes into which the coal is separated. Table I. gives the various sizes, the diameter of ring over and through which each size is made, and the usual purpose for which it is employed.

Jan 1, 1912

By Murray Kaufman

Using en; 41 for a base alloy, 15 modifications were made in sheet form. The elements Al, Ti, C, Mo, Co, and Cb were varied. The effects on the phases formed and their temperature dependence, the aging characteristics, tensile and stress-rup- ture properties, and weld cracking were determined. The A1-Ti content and balance is the most important factor influencing the major sCrengthening phases [Ni,Ti and Ni,(Al, Ti)] and, consequently, mechanical properties. THE mechanical properties, fabricating and joining characteristics, dimensional stability, and so forth, of alloys containing secondary phases are largely determined by the phases present, their distribution, and their temperature dependence. The phases in the basic ternary and quaternary Ni-Cr-Al-Ti combina- tions have been investigated thoroughly.&apos;* The phase behavior of many commercial nickel-base alloys has been determined also. In some cases, for example U500, 5 the effect on mechanical properties has been found. However, little systematic work has been done to clarify the action of each of the important alloying elements in controlling the phases formed in complex commercial alloys and their behavior. The effect of molybdenum on the carbides formed in M252 was investigated by Beattie and verSnyder.6 Application of the results provided by that work

Jan 1, 1963

By M. Gensamer, B. Lustman

A recent paper described, by means of stereographic pole figures, the preferred orientations produced by cold-rolling low-carbon steel of automobile-body grade. It was found that the surface of the sheet exhibited a deformation texture significantly different from the texture possessed by the inside of the sheet. Efforts to produce the surface texture by buffing a sample exhibiting the normal or inside texture, using a copper lap, have not been successful. In view of the data collected by Kurdjumow and Sachs2, it was suggested that the surface texture might be the result of partial recrystallization of the normal or inside texture. The recrystallization texture of cold-rolled mild steel was studied by Goss3, but he did not use the pole-figure method, so that his conclusions were in need of verification. For these reasons the work reported in here was undertaken. It had two objectives: (1) to study the general behavior of cold-rolled mild steel on recrystallization below the critical temperature Al, and (2) to attempt experimentally a demonstaration of the genesis suggested above for the surface texture in cold-rolled steel. The material was that used by Gensamer and Mehl, cold-rolled to 97.5 per cent reduction in thickness. Fig. 1 is an X-ray pinhole photo-gram of this material, taken with the beam transmitted perpendicular to the plane of the sheet, using a molybdenum target at 35 kv. with no filter. It is typical of the inside texture, but in it the deformation texture is better developed than in the samples that showed a well developed difference between the inside and surface samples. Specimens from this sheet, which was 0.005 in. thick, were annealed for 5 min. at various temperatures in a lead bath. After about 0.0005 in. had been etched from both surfaces, X-ray photograms were prepared, using the technique described in the earlier paper1. Figs. 2 to 6 are photograms of the annealed sheet, at 566, 571, 577, 580 and 650" C. (1050&apos; to 1202" F.), in order. Fig. 2 shows that 5 min.

Jan 1, 1937