By N. A. D. Parlee

The diffusion rate of hydrogen in liquid iron has been measured by a gas-liquid metal diffusion cell technique. The diffusion cell was formed by immersing an alumina tube containing hydrogen gas at 1 atm in a bath of stagnant liquid iron. The change in the composition of the melt in the cell was determined by measuring the rate of absorption of the gas in the cell. The appropriate solution to Fick's second law was used to examine the data and calculate diffusivi-ties. The absorption of hydrogen in stagnant pure liquid iron has been found to be diffusion-controlled. The results show that the chemical diffusion coefficient, D, of hydrogen in pure iron in the range of 1547" to 1726°C can be represented by the following Arrhenius relation: D(sq cnz per sec) = 3.2 x X exp(- 3300 i 1800/RT) where the uncertainty in the activation energy corresponds to the YO pct confidence level. Oxygen in the melt (above 0.015 pct 2) increased the apparent rate of absorption of hydrogen. The importance of diffusion data on liquid metals for predicting the rates of certain metallurgical processes has been recognized for a long time. Moreover, these data are much needed to test and develop theory for diffusion in liquid metals. Despite this practical and theoretical interest, however, relatively little reliable information about diffusion in liquid metals is available in the literature. This is particularly true for gas components such as hydrogen, oxygen, and nitrogen in liquid metals, where almost no data on chemical diffusion coefficients are to be found. This is probably due to a multitude of experimental difficulties particularly associated with high-temperature melts. In an effort to fill this gap in information, a research program was undertaken to study the diffusivities and rates of solution of gases in liquid metals. This paper presents the results of a study of the diffusion of hydrogen in liquid iron. EXPERIMENTAL METHOD Two methods for the study of the kinetics of dissolution of gases in liquid metals are being employed in this laboratory. Both involve the measurement of the volume of gas absorbed by the melt as a function of time and as such both avoid the uncertainties involved in chemical analyses of quenched samples for relatively small amounts of gas. In the first method, the gas dissolves in an inductively stirred melt and, in the absence of a slow surface reaction, the results are often interpreted in terms of mass transport across a liquid "boundary layer" between the homogeneous gas phase and well-stirred part of the melt. Other interpretations of the results of such experiments have also been described in the literature.1'5 In the second method a gas-liquid metal diffusion cell is used.' The gas dissolves in a cylindrical column of stagnant liquid metal and, in the absence of a slow surface reaction, the results are interpreted in terms of a non-steady-state diffusion solution to Fick's second law. The weakness of the first method is that while it gives information on the mechanism of absorption by stirred melts it yields an overall rate constant which even in the simplest cases depends on the nature and the thickness of the "mass transport layer" or "boundary layer". It yields no values of diffusion coefficients. The second method was used in this research because in many cases it is possible to determine the diffusion coefficient of the gas component in the liquid metal. In this research it has been utilized to measure diffusion coefficients of hydrogen in liquid iron. The apparatus used was essentially the same as that described by Mizikar, Grace, and par lee but certain modifications have been introduced to meet the elevated temperatures and special conditions of this research. Fig. 1 is a schematic drawing of the apparatus and Table I gives the identification of various parts in this figure. The diffusion cell, shown in detail in Fig. 2, was formed by immersing an impervious alumina tube (hereafter called absorption tube) in a bath of pure liquid iron contained in an alumina crucible. Two types of tubes were used, Morganite triangle RR and McDanel AP35. The crucible was contained in a vertical impervious alumina combustion tube (32 mm ID by 914 mm long) which was closed at both ends by water-cooled brass heads employing O-ring compression seals, Fig. 1. A protection tube enclosing a Pt, 5 pct Rh-Pt, 20 pct Rh thermocouple was introduced through the lower end of the combustion tube

Jan 1, 1968

By K. Osseo-Asare

The presence of carbonaceous matter in gold ores presents a two-fold problem: (1) The poor release of gold from the carbonaceous matrix and (2) the uptake of dissolved gold by the carbonaceous leach residues. A critical review is presented of the published information from various parts of the world pertaining to the nature of the carbon-containing components of these ores and their different roles in the gold extraction process. Included in this paper are new results based on the authors' research on carbonaceous ores from the Prestea goldfields of Ghana. Methods for isolating and characterizing the carbon-containing materials are given and a discussion is presented of the interaction of the carbonaceous ores as well as the fractionated components with aurocyanide solutions. Emphasis is on basic physico-chemical phenomena, investigated with the aid of X-ray diffraction, infrared spectroscopy, adsorption, and electrophoretic mobility studies.

Jan 1, 1984

By S. Whinery

In these times of sharp rivalry, both as to price and quality, among the makers and venders of engineering explosives, it is often desirable to be able to determine the relative energy or value of the various explosives offered for sale, in order to purchase intelligently ; or, having contracted for a large amount of an explosive of a certain standard quality, to be able to ascertain if the manufacturer keeps his product up to the specified standard. The simple and inexpensive apparatus described below was devised by the writer while engaged on the improvement of the Tennessee River, at MuscleShoals, under the direction of' Major W. R. King, U. S. Engineers, in the summer of 1879. It answered the purpose so well that it is thought that a brief account of it may be of interest to other engineers. It consisted, essentially, of an old blacksmith's anvil and a common striking hammer, such as is used for driving rock-drills. The anvil was placed face downward on solid, level ground. In what was then the top of it, a vertical hole, one and one-fourth inch in diameter and about one arid three-fourths inch deep, was made with a ratchetdrill. The surface of the anvil immediately around the drill-hole was made as true and smooth as possible with a file. Next, a new striking-hammer, weighing nine pounds, with a turned and true face, was selected ; and a handle, eleven feet long and about one and a half inches in diameter, was fitted into it so that it

Jan 1, 1886

By J. W. Spretnak, G. W. Powell, J. H. Bucher

Tlze room-temperature tensile fracture oj smooth, round specitnens of three ultrnhigh- strength steels tempered to a wide range of strength levels was studied by means by light and electron-microscopic examination of the fracture surfaces. The fracture of AISI 4340 and 300 M at all the strength levels studied, and H-11, except after tempering at 1200° and 1300°F, occurs in three stages. The initiation of fracture is internal (except in some lightly tcmpeved specimers in which fracture is initiated at surface flaws), and is nucleated largely by separation at metal-second phase intevjaces. TIze voids grow and, coalesce to form a crack. When the crack has reached a sufficienl size, rapid propngutio~z ensues. Failure in this stage of fracture usually occurs by dimpled rupture of inicroshear stefis. In the case of H-11 tempered in the 1125° to 1300°F range, fracture in the shear steps is predominantly by concentrated deformation without void formation. The termination of fracture is usually occomplished by the formation of a shear lib in which fracture occurs by shear dimpled rupture. In the case of H-11 tempered at 1200° and 1300°F, no shear lip was obserued, and the radial elelments extend to the surface—a true termination slage does not exist. ThE tensile fracture of several metals and alloys has been investigated.2-4 In the case of polycrystal-line materials, cup-cone fracture usually results. The mechanism of cup-cone fracture may be summarized as follows.5 Cavities are formed in the necked region of the specimen. They usually are initiated by inclusions or second-phase particles. The cavities extend outwards by means of internal necking, and a crack lying about perpendicular to the length of the specimen is formed in the necked region. Subsequent crack growth occurs by the spread of bands of concentrated plastic deformation inclined at an angle of 30 to 40 deg to the tensile axis. Cavities are formed in the bands of concentrated deformation. The deformation bands zigzag across the bar with the net result that mac-roscopically the crack extends about perpendicular to the specimen axis. The final separation, or cone formation, appears to occur by continued crack propagation along one of the deformation bands out to the surface of the specimen. The micromechanics of the tensile fracture of ultrahigh-strength steels have not been thoroughly investigated. Larson and carr6,7 studied the tensile-fracture surfaces of AISI 4340 with a low-power microscope and reported that three stages of fracture could be observed in general. A centrally located region characterized by circumferential ridges, an annular region characterized by radial surface striations, and a peripheral shear lip were found. It was first pointed out by 1rwin8 that the central region is very probably one of fracture initiation and slow growth, and that the annular, radially striated region is one of rapid crack growth. Presumably the crack grows slowly, assuming roughly a lenticular shape, until it is large enough for the initiation of rapid propagation. In this investigation, it was attempted to determine the fine-scale aspects of the room-temperature tensile fracture of some ultrahigh-strength steels, and to relate the variation in fracture mode with microstructure. The steels studied were AISI 4340, 300M, and H-11 tempered to a wide range of strength levels. I) EXPERIMENTAL PROCEDURE The compositions of the steels studied are given in Table I. The steel was received in the form of hot-rolled bar stock 5/8 to 1 in. in diameter from which oversized specimens were machined and heat-treated. The heat treatments employed are given in Table 11. Subsequent to heat treatment, the specimens were ground to the final dimensions and stress-relieved by heating for 1 hr at 350°F (with the exception of the as-quenched steel). Standard smooth round specimens of 0.252-in. diameter and 1-in. gage length were tested in a Tinius Olsen Universal Testing Machine using a cross-head speed of 0.025 in. per min. The relatively coarse aspects of the fracture topography were determined by light-microscopic examination of sections through the fracture surface of nickel-plated specimens. A direct carbon-replication technique9 was used in the electron-microscopic study of the fracture surfaces. The replicas were examined in the electron microscope, and stereo pairs of electron micrographs were taken. The stereo pairs were then examined using a Wild ST4 Mirror Stereoscope. Carbide and inclusion particles extracted in the replicas were analyzed by selected-area electron diffraction. II) EXPERIMENTAL RESULTS The mechanical testing data are summarized in Table 111. The values reported are the average of

Jan 1, 1965

By D. Weinstein

The high temperature mechanical properties of stainless steels after fast neutron irradiation are discussed in the light of effects caused by lattice dattmage and effects caused by helium generated from n,a transmutations. Embrittlement at high temperatures is due to helium accumulation at grain boundaries and to cavity formation and proPagation along grain boundaries. Following from the embrittlement mechanism, it is suggested that when deformation occurs by mechanisms associated with super plasticity, helium ac-curnulation at boundaries should be attenuated and cavities, if formed, should be nonpropagating. As the mean free Path between interphase boundaries of a two-phase Fe-Cr-Ni alloy was decreased, the degree of superplastic deforrnation at 870°C increased, as vneaszired by total elongation and by the expottent m = a log 'a/a log 'i. This alloy and type 304 stainless steel were cyclotron irradiated in an a-particle beam to a helium concentration of -1 x 10 atom He per atom. The stainless steel specimen was embrittled, but the ductility of irradiated two-phase Fe-Cr-Ni alloys correlated with the values of. m during 'defor-malion. The .finest grained, helium-injected specimens that deforrned with highest m values exhibited the largest elongations to ,fracture. These results could be correlated with metallographic observations of cavity behavior: the propensity for intergranular propagation was lessened as the m value increased. It is concluded that superplastic deformation is ef-fectizle in attenuating helium embrittlement at elevated temperatures. One of the principal problems associated with development of fast breeder reactors is application of alloys such that suitable fuel cladding results. Stainless steels and other Fe-Cr-Ni alloys, because of highly acceptable nuclear characteristics, represent the primary materials for this component, and an exhaustive research and development effort is being conducted. The main deficiency of these materials has been a severe loss of ductility at high temperatures after fast neutron irradiation. An extensive body of mechanical property data and microstructural observations has provided an adequate phenomenological description of embrittlement; in conjunction with transmission electron microscopy studies, a reasonably acceptable embrittlement mechanism has been obtained. Following from this mechanism, it is suggested in the present work that ductility would be enhanced if deformation could occur by mechanisms associated with the phenomenon of superplasticity. Experiments to test this hypothesis have been conducted, and the results are presented and discussed in this paper. IRRADIATION EMBRITTLEMENT AT HIGH TEMPERATURE Austenitic stainless steels have been irradiated to accumulated fast neutron fluences of 1020 to 1022 nvt at temperatures between 60" and 600°C. Specimens that have been exposed to these conditions and subsequently tensile tested at temperatures between 600" and about 900°C exhibit approximately 5 pct total elongation to fracture.'-3 For unirradiated specimens receiving a nearly identical thermal exposure, total elongation at these test temperatures is about 45 pct. Examination of irradiated specimens has shown that fracture propagation is entirely intergranular. These phenomenological aspects of irradiation embrittle-ment at elevated temperatures are well known and are not generally disputed. Although the explanation of this phenomenon has been controversial, a mechanism for ernbrittlement has emerged that accounts reasonably well for the observed mechanical behavior. The controversy resulted primarily from an indeterminate role of neutron-in-duced lattice damage, if any, and a presumed, but experimentally unverified, contribution to embrittle-ment from helium generated by n,a transmutations. Recently, Holmes and coworkers4 have conducted experiments that separate these effects, and the results are instructive in formulation of the ernbrittlement mechanism. Holmes el al.4 irradiated type 304 stainless steel in EBR-I1 to a fluence of 1.4 x 1022 nvt (E > 0.18 mev); the irradiation temperature was 538" * 48°C or, in terms of absolute melting point, 0.49 * 0.03 T,. After irradiation, tensile tests were conducted at temperatures of 21" to 870.C, the specimens first being annealed for 30 min at each test temperature. In addition, thin sections of irradiated specimens were annealed for 1 hr at identical temperatures, electro and examined by transmission electron microscopy. Thus, for a given temperature, it was possible to correlate mechanical properties with the defect structure. At room temperature, the yield stress of irradiated specimens was a factor of 2.5 higher than unirradi-ated specimens exposed to an equivalent thermal history. Electron microscopic examination of the irradiated specimen revealed a high density of lattice damage in the form of Frank sessile dislocation loops and polyhedral voids. Holmes et al.4 concluded that the presence of this defect substructure caused the increase in yield stress and that after irradiation in a fast neutron flux at 0.49 Tm, substantial lattice dam-age persists. Annealing at progressively higher tem-

Jan 1, 1970

By R. I. Jaffee, R. M. Evans

IN recent years, the interest in liquid metals as heat-transfer media for power plants has been very great. The possibility of the development of nuclear power plants has increased this interest and served as the impetus behind much research on low melting metals and alloys for such purposes. The principal reasons for consideration of liquid metals as heat-transfer media lie in their high thermal conductivity and consequent high heat-transfer coefficients, stability at high temperatures, and the high ranges of temperature possible. The element gallium possesses some of the requisite properties for a heat-transfer liquid. It is a unique material, having a low melting point and a high boiling point. Pure gallium melts at 29.78oC, and suitable alloying will produce a metal which melts below room temperature. The boiling point is about 2000°C. As it is a liquid metal, the heat-transfer characteristics would be good. Gallium is not now readily available, due in part to a lack of uses for the metal. Nevertheless, it is not a rare element, and a sufficient supply of gallium exists to permit its consideration for this use. Since gallium has some promise as a heat-transfer liquid, owing to its unique properties, research on the subject was carried on at Battelle Memorial Institute at the request of the Bureau of Ships, U.S.N. The research had as its objectives the determination of the effect of alloying on the melting point of gallium, and the study of the corrosion of possible container materials. In this research, alloys were found which had significantly lower melting points than pure gallium, but none which simultaneously fulfilled other additional requirements, chiefly the corrosion problem. Neither was it found possible to reduce the melting point of certain otherwise suitable alloys appreciably by small additions of gallium or gallium alloys. The results gave little hope that gallium alloys can be developed which enhance the good properties and minimize the undesirable characteristics of elemental gallium. Thus, gallium now appears less promising than other metallic heat-transfer media. The experimental thermal-analysis techniques used in this work have been described.' Experimental Results As a first approximation, the development of low melting gallium alloys was based on alloying elements suitable for use in a nuclear power plant, which also lowered the melting point of gallium. Information from the literature, summarized in Table I, indicates that. tin, aluminum, and zinc are the only suitable elements which cause a lowering of the melting point of gallium. Indium and silver also lower the melting point of gallium, but are of little interest for use in nuclear power plants. Of the elements reported not to lower the melting point of gallium, there is some ambiguity on the behavior of copper. Weibke3 obtained solidus arrest temperatures of 29°C for Cu-Ga alloys from 60 to 90 pct Ga, 0.8C lower than the generally accepted melting point. This may be the effect of a eutectic close to gallium, or, more likely, the result of impurities, or experimental error. The seven elements listed in Table I whose effects were not known were of potential interest if they lowered the melting point of gallium. Their effects were determined experimentally for this reason. Binary alloys containing nominally 2 pct of each of these elements were prepared in the form of 2-g melts by placing the components in a graphite crucible and holding them in an argon atmosphere at 370°C for 5 hr. These melts were then subjected to thermal analysis. In all cases. the solidus temperature was the melting point of gallium. Since these elements (As, Ca, Ce, Mg. Sb, Si, and T1) did not lower the melting point of gallium, they were not considered further as components of a eutectic-type alloy. Ga-Sn-Zn Alloys Preliminary considerations of this system for low-melting alloys were encouraging. All three binary systems were of the simple eutectic type. The composition and melting points of the eutectics were as follows: Sn-9 pct Zn (199°C), Ga-8 pct Sn (20°C), and Ga-5 pct Zn (25°C). Therefore, the probability of a ternary eutectic was high. For reasons to be discussed later, aluminum could not be used as an alloying constituent, leaving the Ga-Sn-Zn system as the only one of interest for low-melting gallium-

Jan 1, 1953

By H. T. Green, R. M. Brick

True stress-strain data on alloys of pure iron with up to 2.4 pct Al were obtained in the temperature range +100° to —185°C. Alumi-num was found to reduce yield and flow stresses of iron at low temperatures but to have little or no effect on ductility. The effects of temperature and composition on strain hardening are discussed. SEVERAL independent studies of the behavior of high purity iron binary alloys at low temperatures are now in progress in attempts to evaluate systematically the variables affecting the low temperature brittleness of ferritic steels. This paper reports the results of one such investigation in which the tensile properties of aluminum and aluminum plus silicon ferrites were measured from 100" to —192°C. True stress-natural strain data have been obtained in order to evaluate as many as possible of the parameters which describe the behavior of the materials involved. In comparable studies at the National Physical Laboratory in England, iron and iron alloys of high purity have been produced' and tested at subat-mospheric temperatures.' True stress-natural strain curves were obtained there also. The purest iron contained 0.0025 pct C and 0.001 pct O and N. Even this, as normalized at 950°C following hot rolling, showed little ductility at -196°C. The grain size was ASTM No. 3, and the room-temperature yield strength was 17,800 psi (which seems too high for pure iron). Some of the NPL irons contained considerably more oxygen and demonstrated intergran-ular fracture at —196°C. The authors2 carefully differentiated between intergranular fractures associated with excessive oxygen content and transcrys-talline cleavage with little ductility encountered at —196°C in the purer material. The cleavage stress was half again as great as that associated with inter-granular fracture. Test Material, Preparation, and Procedures Of a number of Fe-A1 alloys produced, eight were considered to be sufficiently pure for testing. Partial chemical analyses (Table I), low observed yield points, and high ductilities indicate these alloys to be comparatively pure for vacuum-melted irons of sizable ingots, 5 Ib or more. To produce the binary Fe-A1 alloys, electrolytic iron was melted in air, cast into slabs, and rolled to strips 0.010 in. thick. These strips, joined into a continuous ribbon and wound into 2 1/2 in. diameter spools, were subjected for four weeks to a moving atmosphere of purified dry hydrogen in a stainless-steel tube at 1050" to 1150°C. Charges of these spools were melted in beryllia crucibles under good vacuums (1 micron), and aluminum (99.97 pct Al) was added to the melts. Compositions of these alloys are recorded in Table I. The ingots were hot forged and then cold rolled at least 65 pct to 3/8 in. rods which were vacuum annealed to the desired grain size, approximately ASTM No. 4, prior to machining into tensile test bars. All tensile specimens had gage sections 1 in. long, with a fillet of 1.5 in. radius to the shoulder. Gage diameters were 0.250 in, except for a few rods where additional cold work required use of a 0.200 in. gage section. After machining, 0.002 in. was removed from the gage diameter using 240, 400, and 600-grit metallo-graphic papers. The final polish with 600 grit left the fine scratches running in the longitudinal direction. By this means, surface metal strained during machining was removed. A few specimens heat treated after machining were similarly reduced 0.004 in. to remove any material affected chemically by the atmosphere during heat treatments, as is discussed in a later section. Tensile tests of the eight alloys at constant temperatures from +100° to —185°C were performed in apparatus which has been described." The essentials include a double-walled insulated metal vessel which contained the liquid heat-transfer medium surrounding the test specimen. A constant temperature was maintained by means of a pyrometer which regulated the pressure of dry air driving liquid air through a copper coil. Temperature variation was less than ±2°C during a specific test. For axial straining, two lengths of case-hardened chain, terminating in simple shackles, loaded the specimen through threaded grips. The lower grip bar passed through a hole in the bottom of the test vessel to which it was joined by a thin-walled

Jan 1, 1955

By Rodney P. Smith

The diffusivity of carbon (0.1 wt pct C) in Fe-Nz alloys (0 to 100 pct Ni) has been determined for the temperature range 860° to 1100°C. As a function of nickel content, the diffusivity has a maximum near 60 pct Ni (the maximum diffusivity being about 1.3 times that in the absence of nickel); the activation energy has a maximum between 40 and 50 pct Ni and a maximum between 80 and 90 pct Ni. The difference between the minimum activation energy and that in iron is about 3000 cal pev g-atom; Do has a minimum between 40 and 50 pct Ni and a maximum between 80 and 90 pct Ni. The results cannot be rationalized by an approximate thermodynamic treatment. THE diffusivity of carbon has been determined in a number of iron alloys over a limited concentration range. It seemed desirable to investigate a system which allows an extended range of alloy composition within a single-phase region. The Fe-Ni system is ideal in this respect, in that all alloys from 100 pct Fe to 100 pct Ni are fee in a convenient temperature range.&apos; The carbon diffusivity was determined by a decar-burization method. The experimental procedure was identical with that used to determine the diffusivity of carbon in y Fe-Co alloys.2 The experimental data are given in Table I. A small correction (order of a few percent) has been made to the measured carbon loss to correct for the carbon lost from the ends of the cylinders.&apos; Since the diffusivity of carbon varies with carbon content the measured diffusivity is an average value for a carbon content between zero (surface) and that at the center of the sample at the end of the decarburization periods. In making the correction in D to 0.1 wt pct C it is assumed that the measured D corresponds to the arithmetical mean of the carbon content at the surface and at the center of the sample at the end of the decarburization period.3 Since this correction is small (<4 pct in D) and since for our decarburization times the changes in carbon content at the center of the sample was small the mean carbon content could have been taken as half the initial value. It is further assumed that the change in D with carbon content for the alloys is the same as that for the diffusion of carbon in iron. From the data of Wells, Batz, and Mehl4 and of smith5 the correction of D from the mean carbon content to 0.1 wt pct C is 0.3 (0.1 - mean wt pct C). The results for iron are given in Ref. 2. Within the experimental error log Do.l%C for each alloy is a linear function of 1/T; the constants for the equation determined by the method of least squares are given in Table I. The deviations of the experimental points from the least-squares line are of the order of 2 pct in D. A comparison of our results for the diffusivity of carbon in nickel with those of other investigations is shown in Fig. 1. The lower curve in Fig. 1 is a linear extrapolation of values calculated* from the equation of Diamond6 for the relaxation time (temperature range 100° to 500°C). The results indicate a small increase in the activation energy over the temperature range 100° to 1400°C; however, it is difficult to say whether the change in Q is real or experimental error. Certainly the change in Q is less than the variation of 5 kcal per g-atom in the diffusivity of carbon in a iron.6 The experimental data for all the alloys are plotted in Fig. 2. As a function of nickel content the diffusivity has a maximum near 60 wt pct Ni at all temperatures investigated and possibly a minimum between 80 and 90 wt pct Ni for temperatures below 1000°C. The activation energy, Q, and log Do are plotted as a function of the nickel content in Fig. 3. Due to the limited temperature range of our experiments neither Q nor Do can be determined precisely; the activation energies appear to be consistent to ±0.3 kcal per g-atom; however the deviation from the absolute values may be considerably larger, see Table II. The Do values probably have little significance. The solid line for Do in Fig. 3 represents the values required to reproduce the experimental values for D when Q has values represented by the upper solid line The diffusivity of carbon may be expressed in terms of the mobility B22, the activity coefficient r2,

Jan 1, 1967

By R. M. Waterstrat

The phases occurring in the V-Mn system were studied by means of X-yay diffraction and metallo-paphic techniques, using are-melted alloy specimens annealed in the temperature range 800° to 1150°C and quenched. The bcc solid solution extends at 1250°C all the way from vanadium to 6-manganese. Below 1050°C the a-phase is formed, and the terminal a-manganese phase is stabilized up to about 900°C by vanadium in solid solution. IN the only previous general survey of the V-Mn system Cornelius, Bungardt and Schiedtl reported the existence of three intermediate phases corresponding to the approximate compositions VMn,, VMn, and V5Mn. The phase VMn8 has recently been identified as a o phase2 but the alloy VMn was found to have a bcc structure2 corresponding apparently to the vanadium solid solution rather than to the large cubic unit cell reported by Cornelius et al. 1 Subsequent work by Rostoker and Yamamoto3 has shown that the vanadium-base bcc solid solution extends to at least 15 pct Mn at 900°C. An alloy corresponding to the composition VMn, was examined by Elliott,4 who reported that the as-cast sample as well as samples annealed at 1200o and 1300°C had bcc structures, but that annealing at 1000°, 800") and 600°C produced two phases. One of these phases was apparently the bcc solid solution and the other resembled the o phase structure. Hellawell and Hume-Rothery5 established the phase relationships in manganese-rich alloys above 1000°C, and showed that the o phase in this system is replaced by the 6 Mn (bcc) solid solution at temperatures above 1050°C. These results suggest that a continuous bcc solid solution may exist above 1050°C between vanadium and 6 Mn. The present investigation was undertaken in order to develop more complete information in regard to this system. EXPERIMENTAL METHODS The alloys used in the present work were prepared by arc-melting electrolytic manganese having a minimum purity of 99.9 pct and vanadium lumps with a purity of 99.7 pct. The major impurities present in these metals were carbon, nitrogen, and oxygen and this would account for the small percentage of nonmetallic inclusions observed metal-lographically. The arc-melting was at first performed under a helium atmosphere and it was necessary to keep the melting times as short as possible in order to minimize the loss of manganese by vaporization. It was later found that the evaporation of manganese was considerably reduced when the melting was done under argon atmosphere. The final composition of each alloy was calculated by assuming that the total weight loss during melting was due to evaporation of manganese. Compositions which were calculated in this manner agreed reasonably well with the results of chemical analysis, as shown in Table I. Spectrographic analysis revealed the presence of contamination by tungsten, but in no case was the percentage of tungsten greater then 0.4 at. pct. The specimens were in each case broken in half and the fractured section was examined visually and microscopically for evidence of inhomogeneity. Each specimen was homogenized at temperatures near l100°C, as shown in Table I. After this treatment most specimens consisted of large columnar grains of the bcc vanadium solid solution. The etchant used in most of the metallographic work consisted of 20 pct nitric acid, 20 pct hydro-flouric acid, and 60 pct glycerine. It was found that this etchant would clearly delineate the phases present in these alloys although it does not produce any striking contrast between the phases. For certain manganese-rich alloys, a 1 pct aqueous solution of nitric acid was used. This etchant gave a brown color to the a-manganese phase, whereas the o phase was virtually unattacked and appeared very light as shown in Fig. 1. The etchants used by Cornelius et a1.l were found to produce spurious effects in some of these alloys. In particular, the vanadium-rich alloys etched in hot sulfuric acid often appeared to consist of two phases when both X-ray diffraction and etching with the glycerine-acid mixture indicated the presence of single phase bcc solid solution. A few percent of what appears to be an oxide or nitride phase was found at the grain boundaries and in the interior of the grains, especially in the vanadium-rich alloys. All alloys were annealed in sealed silica tubes containing 1 atm of pure argon and these tubes were then quenched in cold water. Although some manganese loss occurred during annealing, the loss seemed to be confined to the surface of the speci-

Jan 1, 1962

By W. M. Baldwin, J. T. Brown

The effect of hydrogen on the ductility, c, of SAE 1020 steel at strain rates, i, from 0.05 in. per in. per rnin to 19,000 in. per in. per rnin and at temperature, T, from +150° to —320°F was determined. The ductility surface of the embrittled steel reveals two domains: one in which and the other in which The usual "explanations" of hydrogen embrittlement are in accord with the first of these domains only. THE purpose of this investigation was a fuller A characterization of this of the investigation effects of varying temperature and strain rate on the fracture strain of hydrogen-charged steel. To be sure, it is known that low and high temperatures remove the embrittlement that hydrogen confers upon steels at room temperature,1 * see Fig. la and b, and that high strain rates have a similar effect,&apos;-&apos; see Fig. 2a, b, and c. However, the general effect of these two testing conditions on the fracture ductility of hydrogen-charged steels is not known, i.e., the three-dimensional graphical representation of fracture ductility as a function of temperature and strain rate is not known—only two traverses of the graph are available. The need for such a graph is not pedantic. To demonstrate this point, Fig. 3a, b, and c shows three of many three-dimensional graphs, all possible on the basis of the two traverses at hand. The important point (as will be developed in the Discussion) is that each of them would indicate a different basic mechanism for hydrogen embrittlement. It will be noted that the four types of ductility surfaces in Fig. 3a, b, and c may be characterized as follows: Material and Procedure Tensile tests were made at various temperatures and strain rates on a commercial grade of % in. round SAE 1020 steel in both a virgin state and as charged with hydrogen. The steel was spheroidized at 1250°F for 168 hr to give the unembrittled steel the lowest possible transition temperature. The steel was charged cathodically with hydrogen as follows: The specimen was attached to a 6 in. steel wire, degreased for 5 min in trichlorethylene, rinsed with water, and fixed in a plastic top in the center of a cylindrical platinum mesh anode. The assembly was placed in a 1000 milliliter beaker containing an electrolyte of 900 milliliters of 4 pct sulphuric acid and 10 milliliters of poison (2 grams of yellow phosphorous dissolved in 40 milliliters of carbon disulphide). A current density of 1 amp per sq in. was used which developed a 4 v drop across the two electrodes. All electrolysis was carried on at room temperature. Temperatures for tensile tests were obtained by immersing the specimens in baths of water (+70° to + 150°F), mixtures of liquid nitrogen and isopen-tane (+70° to —24O°F), and boiling nitrogen (-240" to-320°F). Specimens were tested in tension at strain rates of 0.05, 10, 100, 5000, and 19,000 in. per in. per min. The 0.05 and 10 in. per in. per rnin strain rates were obtained on a 10,000 lb Riehle tensile testing machine, the 100 in. per in. per rnin rate on a hydraulic-type draw bench with a special fixture, and the 500 and 19,000 in. per in. per rnin rates on a drop hammer. The fracture ductility of hydrogen-charged steel at room temperature and normal testing strain rates (-0.05 in. per in. per min) is a function of electro-lyzing time, dropping to a value that remains constant after a critical time.&apos;* Under the conditions of • The hydrogen content of the steel continues to increase with charging time even after the ductility has leveled off to its saturated value.&apos; this research the saturated loss in ductility occurred at approximately 30 min, see Fig. 4, and a 60 min charging time was taken as standard for all subsequent tests. After charging the steel with hydrogen, the surface was covered with blisters. These have been described by Seabrook, Grant, and Carney.&apos; The original diameter of the specimen was not reduced by acid attack, even after 91 hr. Results The ductility of both uncharged and charged specimens is given as a function of strain rate in Fig. 5, and as a function of temperature at four different strain rates in Fig. 6. These results are assembled into a three-dimensional graph in Fig. 7. It is seen that the locus of the minima in the ductility curves of the charged steels divides the ductility surface into two domains. At temperatures below the minima,

Jan 1, 1955

By David Turnbull

IN isothermal recrystallization processes, new crystals generally grow into the matrix until they impinge upon other new crystals or an external surface, at constant linear rates G. Before impingement the perceptible course of growth can be described by the equation: 1 = G(t-7) C1I where, G = dl/dt, 1 is a crystal dimension measured in a constant direction, t is the time, and 7, the nucleation period, is a positive intercept on the time axis. Fig. 1 is a schematic representation of I as a function of time for a recrystallizing grain. G is dependent upon temperature, driving energy (strain or surface energy), relative grain and boundary orientations, but is generally independent of time. The frequency of nucleation, fi, (time" volume") can be defined by the equation: N = 1/fV [2] where ? is the mean nucleation period and V is the volume of the specimen that has not recrystallized. The kinetics of primary and secondary recrystallization generally can be described satisfactorily in terms of the parameters N and G only.&apos;-" After recrystallization is complete the average grain size 7 increases with time by "normal grain growth;" didt, the average rate of grain growth, is strongly time dependent and has not yet been precisely related to G for the motion of the individual grain boundaries constituting the system. It has been suggested4* " that the elementary act in grain boundary migration is closely related to the elementary act in grain boundary self-diffusion. Although the distance of atom movement in the two processes may be somewhat different, there is reason to expect that the activated states may be very similar, so that the free energy of activation for grain boundary migration should be of the same order of magnitude as for grain boundary self-diffusion. Therefore, it is desirable to develop a satisfactory basis for comparing data on self-diffusion and grain boundary migration and to make such comparisons where possible. Theory The formal theory of grain boundary migration rates is analogous to the theory for the rate of growth of crystals into supercooled liquids reviewed elsewhere 6-8. Boreliuss has shown that the latter theory describes, within the theoretical uncertainty, the growth of selenium crystals into supercooled liquid selenium. Motto and more recently Smolu-chowski" have derived expressions for the rate of boundary migration in recrystallization. The treatment to be presented is similar to Mott&apos;s excepting that the formalism of the absolute reaction rate theory will be used. The atomic mobility, M, in grain boundary migration is defined by: G = -M6p/6x where p is the chemical potential per atom and x is the coordinate measured in the direction of grain boundary movement. Let AF be the free energy difference per gram atom on the two sides of the boundary and k the thickness of the boundary. For RT>>AF the potential gradient across the boundary (6p/6x) is essentially linear and it follows that: SF/8x = - aF/N\ [4] where N is Avogadro&apos;s number. According to the Nernst-Einstein equation, M is related to a diffusion coefficient, Do, for matter transport in grain boundary migration by the equation: M = Da/kT [5] Substituting eqs 4 and 5 into eq 3 gives the basic relation between Do and G: G = DoaF/\RT [6] Do values may be calculated from experimental values of G from eq 6 and directly compared with the coefficient of self-diffusion within the crystal, DL, or the grain boundary self-diffusion coefficient D,. However, a more convenient, though equivalent, basis for comparing atomic mobility in grain boundary migration and self-diffusion is through the constants of the absolute reaction rate theory. According to this theory diffusion coefficients may be written:" D = k2(kT/h) exp [-AF,/RT] 171 aFa, the free energy of activation, is related to the measured energy of activation, Q, by the equation: AFA = Q - T aSx - RT [8] where aSa is the entropy of activation. Substituting eqs 8 and 7 into eq 6 gives: G = ek(kT/h) (aF/RT) exp [(AS,,)C/R] exp C-Qc/RTI C91 where the subscript G refers to boundary migration. The relationship between the driving free energy and the free energy of activation in boundary migration is indicated schematically in Fig. 2. Experience indicates that the variation of G with temperature can be described by: G= Go exp [- Qc/RT] [10] where Go and Qc are generally temperature independent over wide ranges of temperature. Comparison of eq 9 with eq 10 gives:

Jan 1, 1952

By F. Forward, H. Veltman, A. Vizsolyi

Activities of oxides in the ternary FeO-MnO-SiO system are calculated from data on the binaries, using the Gibbs -Schuhmann method. These activity data are used, together with thermodynamic relations, to calculate the contents of oxygen, silicon, and manganese in liquid iron, and the composition of the corresponding oxide phases in equilibrium with it. Excellent agreement was found between calculated and experimental metal compositions, indicating that thermodynamic methods, such as those presented, can supply useful data on slag-metal equilibria, and are therefore capable of wider application. When molten steel containing oxygen is treated with a deoxidizer, the product of the reaction is composed of the oxides of the deoxidizing elements together with more or less iron oxide. This assemblage of oxides is presumably very close to equilibrium with the melt since it is formed directly from elements dissolved in it. Therefore, it is likely that metal analyses corresponding to a given oxide phase composition are calculable with considerable precision where sufficient information is available on activities in both phases. The present study was made to test this hypothesis in the case of deoxidation by silicon and manganese. Here experimental data on the relationship among oxygen, silicon, and manganese in the metal phase are available, as are activity data for the MnO-SiO2, FeO-SiO2, and FeO-MnO binary systems. A further objective was to demonstrate in a specific example how gaps in the data may be filled by judicious interpolation, and how the Gibbs-Schuhmann method is applied to obtain activities in ternary systems. The rigorous derivation of the latter, requiring considerable facility in handling partial differential equations, tends to mask the real simplicity of the method, and repel the very engineers and experimenters who would benefit the most from its use. I) GENERAL PROCEDURE Deoxidation of steel with silicon and manganese results in the formation of two phases, metal and oxide. The number of components is four—Fe, Mn, Si, and 0. The phase rule then gives the number of degrees of freedom: If temperature and pressure are fixed, 2 deg of freedom remain. Consequently, it suffices to fix the concentration of two of the components of the system for all the concentrations to be determined and, at least in principle, calculable. The practical problem is then to discover a straightforward method of calculation with a minimum of trial and error solutions. The type of reactions to be dealt with are like the following: Si (in steel) + 2 O(in steel) = SiO2(in oxide phase) The standard free energy of this reaction is readily obtained from the literature, so that the equilibrium constant can be calculated by the expression: Since the metallurgist is concerned with percentages rather than activities, a real solution requires information that will permit activities to be converted to concentrations. This information is fairly adequate for the elements dissolved in molten steel, but is not available for the FeO-MnO-SiO2 oxide system. Therefore, the first step in this study was to find the relation between activity and concentration for the three oxides making up the system. The next step was the calculation of slag and metal compositions that are in equilibrium with one another. As shown by the phase rule, it is sufficient to assume the values of two composition variables in order to calculate the rest. But which two are picked makes a vast difference in how difficult the calculation turns out to be, so that it is necessary to make preliminary trial of several routes to find the easiest one. A convenient method is to begin with the slag, and to pick FeO concentration and that of one of the other oxides. Starting with the relation between oxygen dissolved in the liquid steel and FeO in the slag permits a good first estimate to be made of the oxygen content of the steel in equilibrium with FeO, because the iron content being fairly close to 100 pct, Fe has an activity close to unity. Using this first estimate of oxygen activity, approximate values of the manganese and silicon contents of the melt are readily calculated from the appropriate equilibrium constants. A minor correction for the depar-

Jan 1, 1963

By Larry Kaufman

A useful method for estimating the entropy of NaCl type compounds has been developed by combining the Debye theory of specific heat with the Lindemann formula. This method pemnits calculation of the entropy from a knowledge of the atomic weight, atomic volume, and melting point of the compound. Comparison of the calculated and observed entropies of 35 NaCl type compounds over a wide temperature range yields good agreement thus establishing the usefulness of the method. Application of the method to other crystal types is also discussed. KUBASCHEWSKI~ has suggested a useful method of estimating the enthalpy of formation of inter-metallic compounds from a knowledge of the crystal structure, lattice parameter, and heats of sublimation of the component elements. This method is quite valuable in predicting the tendency for compound formation in a given system and is of particular value in considering systems for which no experimental data are available. In order to supplement the enthalpy calculation afforded by Kubschewski&apos;s method, it would be of value to be able to estimate the entropy of compounds so that the entropy and free energy of formation could be evaluated. Although a considerable body of such data determined by calorimetric and equilibration techniques exists at present, the difficulty of making such measurements (particularly at high temperatures) and the ever increasing number of new compounds which are of interest make the desirability of such a computational method clear. This paper deals with a method for calculating the entropy of a compound from a knowledge of the atomic weight, atomic volume, and melting point. Since these data are generally easier to determine and therefore more readily available than thermo-dynamic data, they should provide an additional tool in estimating the stability and reactivity of compounds at high temperatures. I) THE ENTROPY OF PURE METALS As a first approximation, the specific heat of a pure metal can be represented by a sum of terms where C,($/tI is the vibrational specific heat calculated on the basis of the Debye theory, lo4 TC, (0/T) is an approximation to the Cp - C, correction. T is the electronic specific heat, and Cp (p) is the magnetic specific heat. Although the Debye theory does not provide a complete description of the vibrational specific heat, i.e., the Debye temperature 0 is not a constant, it does provide a good approximation when used properly. Blackman6&apos;7 has written several reviews on this subject discussing the different values of 0 determined by various methods (specific heat, X-rays, elastic constants, electrical resistivity, and so forth), as well as the observed temperature dependence of 0 with T. In the present case the 0 in Eq. [I] naturally refers to the specific heat 0. The variation of Debye 0 (as determined from specific heat measurements) with temperature is observed to exhibit its most radical behavior at very low temperatures. At higher temperatures the 8 values are observed to become more nearly constant. Blackman6&apos;7 has presented the variation of 0 with temperature for several metals. His tabulation is reproduced in Table I. Reference to Table I shows that above a certain temperature level, 0 remains fairly constant. The value of 0 which is most useful in computing the specific heat, and hence the entropy, is the value of 0 in the range 0/6 « T « 0. In 1910, Lindemann&apos; suggested a relation for estimating Debye 0 values. According to this formula, where V is the atomic volume, T is the melting point in &apos;K, M is the atomic weight, and CL is a constant. Mott and Jones9 present this formula and state that there is at present no satisfactory theoretical explanation, but that it does have an empirical basis. By using the valuesof 0 in Table I along with known1&apos; values of M, T, and the molar volume VM, where the Lindemann constant can be evaluated. This

Jan 1, 1962

By J. T. Norton, N. J. Grant, I. S., Servi

Coarse grained high purity aluminum was tested in creep at temperatures of 400° to 1200°F to develop subgrain structures. Measurements of subgrain size, distribution, and rotation were made from X-ray diffraction patterns. Subgrain size and distribution were checked metallographically and the size was compared with average slip band spacing. The slip family was determined for several specimens. THE interest and research recently evident abroad in the role of subgrain formation and polygon-ization as a contribution to the creep of metals at elevated temperatures is deserving of greater attention in this country. Such metallic subgrains can be defined as macroblocks existing within the grains. The general observation has been that the macro-blocks which belong to the same grain have a maximum difference in orientation of a few degrees. In spite of the considerable amount of work that has been done since Jenkins and Mellorl observed the "division of existing crystals into smaller units when deformation occurs at an annealing temperature," the subject of subgrain formation is only now receiving truly active discussion and investigation. The existence of subgrains has been revealed by metallographic methods, as in the work of Jenkins and Mellor,1 and by X-ray methods, first applied to this problem by Homes.&apos; Hirst3 and Calnan and Burns4 applied the back-reflection Laue technique to the study of coarse grained specimens. Wood et al.5 and Greenough and Smith&apos; examined the ring obtained with a back-reflection camera for the study of fine grained specimens. In addition to the above, the transmission technique was used by Wood.6 A special technique was developed by Guinier and Tennevin8 in order to improve the resolution. Metallographically, the subgrains have been observed directly on the surface of deformed specimens by Wood et al.,3 or have been made evident on repolished surfaces by applying a suitable etching reagent. The latter technique, first suggested by Lacombe and Beaujard,9 was then improved by Wyon and Crussard.10 Subgrains can be formed in single crystals after small amounts of bending followed by heating after this cold work, or during deformation at elevated temperatures. The first phenomenon was analyzed by Cahn11 for the simple case of pure bending followed by annealing. Cahn suggested a mechanism of subgrain formation based on the dislocation theory and called this phenomenon "polygonization." He extended this mechanism to the more complex case of local bending, such as the bending which may occur when a polycrystalline specimen is deformed in tension. Cahn&apos;s suggestion was later found quite consistent with the results obtained by Dunn and Daniels." An explanation has been presented recently regarding the formation of subgrains during deformation at elevated temperatures by Chang and Grant.&apos;" In general, there are two schools of thought on the subject. One, according to Wood et al.,5 is that subgrain formation is a mechanism of deformation which is operative under certain conditions in the same way that the slip process is the mechanism of deformation which is operative under other conditions. The boundaries between the subgrains undergo a viscous flow which contributes substantially to the deformation of the material. The second, according to Cahn,13 Wyon and Crussard,10 and Chang and Grant,18 is that subgrain formation is the effect of simultaneous deformation and annealing and is,

Jan 1, 1953

By Louis R. Hodell

WHEN the drilling of an oil well is completed a permanent opening from the reservoir to the surface must be provided. This is done by lining the hole with pipe, commonly known as casing. In the past, all but a small amount of casing has been run in the hole and joined by threads and couplings. Recently, however, in California, Texas, and Oklahoma, there has been a definite tendency &apos;to adopt -the welded joint for the following reasons: (1) Plain end casing for welding may be bought for 15 per cent less than thread-and-coupled casing; some of this is offset by the cost of welding the pipe in the hole but a respectable net profit remains.

Jan 1, 1937

By Frederick T. Williams

The purpose of this paper is to discuss the relative merits of the large 31/8-in. machine and the small 2 1/4-in. tappet machine in driving development-headings; and although the data here presented were obtained from cross-cut headings alone, experience has shown that the results are equally true in drifting, raising and winzing. Recently we drove two parallel cross-cuts through the same formation, using a 3 1/8-in. machine at the breast of one crosscut, and a 2 1/4-in. machine of the same make at the breast of the other. The results of this work afforded an ideal comparison, since in both cases the headings were advanced through rock practically of the same hardness and breaking-properties, the amount of sludging was equal, and there was no difference in the condition of the steel or the machines, the air-pressure or the experience of the operating crews. Some operators in the Cripple Creek district contend that there is ground which cannot be handled with the small machine, the holes being too small to contain enough powder to "pull " the ground, etc. The results obtained in working the property of the Portland Gold Mining Co., however, show that the ground worked by them does not fall in this class. During a period of two years there have been driven, with the small machine, 4 miles and 308 ft. of development-headings, through a diversity of ground, including Pike&apos;s Peak granite (a coarsely porphyritic type of granite), highly indurated andesitic or pho-nolytic breccia, true massive andesite, trachytic phonolyte, tuffs, and along dikes of decomposed basalt and hard phonolyte. In every instance a satisfactory record was made. The headings here describe? mere driven through highly indurated andesitic breccia, having a hardness of from 5.2 to 7.2 and a sp. gr. of from 2.2 to 2.8. The action of the breccia under the drill was not materially different from that of ordi-

Jan 1, 1907

By E. B. Hunt

Paraffin deposition has been studied in the laboratory under conditions simulating deposition in well tubing. A theoretical analysis has been made of the cooling of the oil and the precipitation of paraffin from the oil as it flows up the well tubing and through surface flowlines. It is proposed that paraffin deposits are initiated by the precipitation of paraffin directly on or adjacent to the pipe wall and grow by diffusion of paraffin from solution to the deposit. This mechanism is consistent with laboratory and field observations, and has proved useful in the design and interpretation of laboratory paraffin-deposition tests. Tests have been made of the effect of plastic pipe coatings and chemical additives on paraffin deposition. INTRODUCTION Paraffin deposits which form in well tubing and surface flowlines interfere with production and must be removed. Over the years much progress has been made in developing and improving methods of removing these deposits after they form. Much less progress has been made in developing methods of preventing or inhibiting the formation of paraffin deposits. This is due, it is believed, to the lack of knowledge of the mechanism of paraffin deposition, the absence of satisfactory laboratory testing methods and the difficulties in evaluating the results of field tests of preventive treatments. The present investigation was undertaken to elucidate the mechanism of paraffin deposition and to develop suitable laboratory tests for studying the inhibition of paraffin deposition in well tubing and surface flowlines. Current theories on the mechanism of paraffin deposition have been evolved from field observations, from laboratory studies of various factors which might be involved in paraffin deposition, and from laboratory paraffin-deposition tests.1-9 Paraffin deposits have been formed in the laboratory by immersing a cold finger into a hot wax-oil solution and by flowing hot wax-oil solutions through cooled pipe or over cooled plates. These laboratory conditions differ in important features from field conditions, and the observed deposition behavior is not entirely field-like." Thus, there is reason to question the field applicability of the results of these tests. The present investigation was undertaken to determine how to perform and interpret laboratory paraffin-deposition tests to obtain information on the inhibition of deposition in the field. The paraffin problem in the broadest sense encompasses the formation of any predominantly organic deposit in well tubing, surface flowlines and other equipment in contact with crude oil or gas. The present investigation was limited to paraffin deposition involving the precipitation of paraffin wax from solution by cooling and its concentration in a deposit on a cooled surface. This probably excludes its applicability to those problems arising from asphaltic-base crudes, but not those arising from paraffin-or mixed-base crudes. This also excludes its applicability to emulsion and congealing oil problems which are often included as part of the paraffin problem. The phenomenon of cooling appears to be the controlling factor in paraffin deposition involving the precipitation of paraffin wax and its concentration in the deposit. Deposits of this type are usually found in the field only where cooling occurs. Early in this laboratory investigation, it was not found possible to form deposits under constant temperature conditions from a wax-oil slurry, either by steady flow through pipe or by gas-lift up a pipe. Thus, the investigation was limited to situations involving cooling. THEORY The relationships involved in establishing the temperature profiles in an oil stream as it flows up well tubing with a linear (geothermal) pipe-wall temperature distribution or through surface flowlines with essentially constant pipe-wall temperature are presented in the Appendix. The relationship between radial distance in the pipe and the rate of cooling of the oil is then combined with a relationship between cloud point and rate of cooling to develop the pattern of formation of a wax cloud in the oil. The following discussion of paraffin deposition under various laboratory and field conditions is based upon this development which is presented in the Appendix. PARAFFIN DEPOSITION IN SURFACE FLOWLINES The average temperature of the oil coming out of a well is somewhat higher than the ground temperature. Thus, the oil continues to cool on its trip through the surface flowline, and wax deposition can occur. The temperature distributions calculated from Eq. A-4 are given in Fig. 1. As can be seen, almost all the cooling occurs in the first 500 ft from the wellhead. In addition, the radial temperature gradient near the wall decreases rapidly with distance and becomes very small after a few hundred feet. Thus, growth of a paraffin deposit would be expected to decrease rapidly with distance from the wellhead and become negligible after a few hundred feet, since growth is dependent on concentration gradient. Wax precipitation and diffusion of wax to the already

Jan 1, 1913

By Charles E. Wait

The old laboratory at the School of Mines was among the notoriously bad ones, being situated in apartments of the main collegebuildings not originally intended, and conspicuously unfit, for the use to which they were put; while, as in many of our schools and colleges, the assaying was done in the basement of the college. Prominent among the disadvantages of such an arrangement are insufficient light, poor ventilation, and little or no provision to carry off offensive gases. It is not my intention now to present a complete description of this building. I wish merely to call attention to a few points in its construction and equipment, which may prove of interest to those who contemplate erecting buildings for snch work, and who may be, as we were in this instance, limited as to funds. In this laboratory every room is well lighted; all rooms used by students are well ventilated, and are provided with closed hoods for

Jan 1, 1887

By Maynard H. Jameson

Earlier investigations of the potential-drop-ratio method of electrical prospecting have indicated that under suitable conditions this method is well adapted to the location of formation boundaries in stratified ground. A description of this development was given several years ago by H. Lundberg and Th. Zuschlag.l The curves published by these authors for the potential-drop-ratio variation above a horizontal contact indicated a definite relation of the position of the curve peak to the depth of the interface. The theory underlying this relation was subsequently studied by Z. Mitera in greater detail,&apos; and the theoretical deductions were compared with the results of tank experiments. The investigations available at this writing were confined to studies of horizontal formation boundaries. It is the purpose of this paper to extend the scope of the previous work to the problem of dipping layers. Theory Consider the case of three media of different resistivities, whose interfaces are not parallel. If a point-source is located in one of these interfaces, its images do not lie in a straight line, but on the circumference of a circle whose center is at the hypothetical junction of the interfaces. R. F. Aldredgea determined the relation that exists between the degrees of dip of the two interfaces and the distances between the various images and the point for which the potential is to be found. As seen in Fig. I, three media of resistivities PO, p1, and p2 are involved, and the source I is located at the interface of the media Coo) and (p1). The perpendicular depth of the lower interface is h, 0 is the dip, R is the distance between source I and potential point P, and r is the distance between the images and that point. To distinguish between images lying above the ground interface and those below, the notation "odd" and "even" images will be employed; images below the ground interface will be termed "odd" and those above "even." The following relations govern the distances between either kind of images and the potential point: EvEn Odd Ta — R r1 - [rl] - [RS + 4h(h + R sin 01½ r, = [r] =. [R1 + 4h cos 0)2(h + -R sin 0)1½ ri - [r3] ={r3} [R* + 4h(4 cos2 0 - i)1 (h + R sin 0)l½ r4 = [r4] = [R2 + 4h(4 cos $ cos 30)1 (h + R sin 0)]½ r, — [r4] - [R2 + 4h(4 cos9 R cos 20 + cos 48)2 (h + R sin 01½ I RI + 4h[2 cos 30(4 cos2 0 - I)12 (h + R sin 8)1 ½ rn - [r4] - [R2 + 4hlf(cOs 0)18(h + R sin R)l½ As previously pointed out, the images of the source are on the circumference of a circle. If the angle of dip is 0, the angle measured from the horizontal to the first image is 28; to the second image it is 48, and so on. Since the limit of the reflecting interface is at its outcrop, the last possible

Jan 1, 1946