In the systems Mo-Fe-C, Mo-Co-C, and Mo-Ni-C the phase boumdaries of the cubic Ij carbides were determined at 1000°C and the variation of the lattice parameter with composition was measured. In the system Mo-Fe-C a single ternary carbide, Mo3Fe3C, was observed. In Mo-Co-C and Mo-Ni-C two new n phases of the type M12C were found: Mo6C06C and Mo6Ni6C. At 1000°C they coexist with the M6C phases MO3-4,CO3-2C and Mo3-4Ni3-2C, respectively. Mo3C03C and Mo4C02C are not separate phases but parts of a single M6C phase region, and the same is true of Mo3Ni3C and Mo4Ni2C. THE n carbide structure type has been known since it was determined by westgren' in 1933, yet reliable information on phase compositions of this type is ap-parently scarce. The following selection of suggested formulas illustrates the extent of the confusion con-cerning compositions: W2-3Fe4-3C,1W6Fe6C,2 W2_4Fe4-2C,3 (W,Fe)6C,4 Tj.-W4Co2C and nz-W6Co6C,5 n1-W3Co3C and n2-w4Co2C,5 W3C03C and w6Co3C2,7 MO3Fe3C,8n2-M04Fe2C,9 (MO,Fe)6C,4 MO3CO3C,8 n2-MO4CO2C.9 Many of these compositions obviously overlap, some disagree in carbon content. The use of the designations 77, and n2 is not consistent. There is uncertainty whether two carbides M6C coexist or whether there is only one M6C with a wide range of substitution of one metal for the other. The existence of M12C seems questionable altogether if one ignores the results of a neutron diffraction study of W6Fe6C supporting that particular metal to carbon ratio.'' More reliable information is available for the iso-typic oxides studied by Nevitt,11 Nevitt, Downey, and orris," and Meussner and carpenter.l3 That n car-bides and oxides are structurally identical, particularly with respect to the location of the metalloid atom, has been demonstrated clearly by Stadelmaier and Meussner14 and also by Parthe, Jeitschko, and sadagopan.15 Therefore the present paper, which attempts to establish the phase boundaries of n defini-tively for three carbon systems, has implications for the whole family of filled Ti2Ni types. EXPERIMENTAL PROCEDURE The samples were prepared in two stages. Pellets weighing 3 g were compacted from powders of the elements and presintered in a closed tube of fused silica that had been evacuated to lO-4 mm Hg. This was fol- lowed by arc melting the sintered samples under argon. Remelting the button once was sufficient to produce homogeneous specimens. The metal powders had the following minimum purities in wt pct: molybdenum 99.5, iron 99.0, cobalt 99.7, nickel 99.9, graphite 99.94. Carbon determinations by the gas volumetric method were obtained from thirty-one of the one hundred samples in the annealed condition. They were limited to compositions that were critical to placing a boundary line in the isothermal sections. The carbon losses were comparatively low and averaged less than 1.5 at. pct. For annealing, the samples were sealed in tubes of fused silica evacuated to 10-4 mm Hg. The annealing schedule was 20 hr at 1250°C followed by 150 hr at 1000" ±10°C. For the water quench the silica glass tubes were broken mechanically to speed the quench. The specimens were examined in the as-cast and annealed condition by standard metallographic techniques. Some of the as-cast and all annealed samples were studied by X-ray diffraction using a 114.6-mm powder camera with filtered Co radiation. The lattice parameters of the n phases were determined by graphic extrapolation to 8 = 90 deg on a plot against sin2 8. It is estimated that the maximum error in the lattice parameters is ±0.002A.. The phase fields were determined by the disappearing phase method, relying on X-rays for phase identification and on microscopy to detect small amounts of a phase. RESULTS Pertinent information on the binary side diagrams has been summarized by Hansen and Anderko16 and Elliott17 and will not be discussed further. Photomicrographs documenting the equilibria at 1000°C have been selected to avoid redundancy due to the similarity of the three systems. Thus there will be only one picture showing an equilibrium with Mo2C, and so forth. Molybdenum-Iron-Carbon. An isothermal section of most of the Mo-Fe-C system at 1000°C is shown in Fig. 1. No attempt has been made to distinguish between a and y iron or to determine their phase boundaries. A conspicuous absence is the phase Fe2 1Mo2C6 with the Cr23C6 structure, supporting the suggestion by Krainer4 that it decomposes by annealing at high temperatures. The only ternary phase is found in a narrow range around Mo3Fe3C (MO43Fe43C14). A microstructure with a two-phase mixture of Mo + n is seen in Fig. 2. The variation of the lattice parameter of n with the estimated composition is shown in in Table IA. The phase diagram does not agree with the results of Kuo9 who reported n2-Mo4Fe2C. Our lattice parameter Varies from 11.095A at the iron-rich end to 11.140Å at the molybdenum-richoend of the phase field whereas Kuo9reported 11.26Å for Mo4Fe2C. We are in agreement with the older work

Jan 1, 1970

P. H. Dudley, Yew York, N. Y. (communication to the Secretary*) :—The characteristics of Professor Home's metallurgical papers are, that he is able, from the mass of confusing evidence on the subject, to make an analysis and present hypothetical and essential principles in concrete form for consideration and discussion. I can appreciate, from the practical side of the subject, the labor of collecting and investigating the data which was essential to prepare the paper. Much of it necessarily came from material of preceding years of manufacture in which time was allowed for chemical reactions of the re-carburizer, and for the elimination of the oxidation-products before teeming the ingots. This practice gave a favorable time-element to free the metal from slag and other impurities— a requisite condition for the production of sound steel in the ingots. But, in allowing them to become cold before they were charged into the furnace, a subsequent time-element entered as a detrimental factor in the development of the pipe or shrinkage-cavities, which gave an ingot-structure deficient in soundness, at least in the upper portion. (The term slag is used in a general rather than in a strictly technical sense.) Traces of manganese sulphide are often associated with manganese silicates in the same thread or seam, and at other places they are separate and distinct. Interpretations from material thus manufactured must be made with due allowances for the methods of fabrication and the requirements of service. The only way we now have to estimate what the degree of soundness of the ingot-structure was, in the early foreign and American manufacture of steel rails, is by examination of the worn and failed material after years of service. We must remember also that the poorest material was long since consigned to the scrap-heap without any full record of its history. The rails from a given ingot cannot now be identified ; and in many

Jan 1, 1909

By R. G. Bowman

DISCUSSIONS of processes for the manufacture of white lead generally open with the statement that white lead is the oldest chemical pigment known to man. This fact is of more than historical interest; in the light of the present extensive use of white lead, ii indicates that the .compound possesses characteristics that make it unique among white pigments, and superior to all ;in its particular field. A greater variety of processes have been proposed for manufacturing white lead than for any other one chemical compound. Only a few of these processes have come into commercial use, however, and a large part of the present production here and abroad is made by the process used in ancient times. The outstanding disadvantages of the old process are that it is slow and laborious, affords no control of the product, and yields at best an impure material lacking in uniformity. Improved processes, sometimes classed all together as "quick processes," have had as their main object the shortening of the time required. Most of them accomplish this and some have yielded a superior product as well, but only two or three are now in use commercially. For centuries the manufacture and mixing of paints has been treated as an art, and the practice has been much influenced by tradition and precedent. There is a reluctance to abandon old materials for this purpose, and as few new uses for white lead have been developed, the adoption of the quick processes has been slow. The electrolytic production of white lead is not-new, a large number of processes and forms of apparatus have been proposed and patented within the past 25 years, all directed toward the, production of white lead, wholly or in part, by electrolysis. One or two of these processes were tried commercially but proved unsuccessful.

Jan 9, 1925

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The room-temperature microhardness of as-grown and annealed MoaC single crystals was measured on the (0001), {2110), and1012) planes using Knoop and Vickevs indenters at loads ranging front 25 to 1000 g. The orientatimz dependence of hardness with respect to crystal axes was also studied. The average random hardness of as-grown crystals was determined to be 1520 kg per sq nm. Annealing to 2000°C decreased. the average hardness by 150 units. An increase in hardness after annealing at 2200 ;C was noted. Optical and electron microscopy revealed slip and twin traces on all planes studied, as produced by mi-cvohavdness indentations. Basal (0001)(2i10) slip was determined to be the primary slip system and was substantiated by electron transmission microscopy. A secondary {1010)(2110) slip was produced by mi-crohardness indentations. The lattev also produced twinning- of the {10i2)[0001] type, as proven by electron diffraction. Electrical resistivity and elastic-modulus anisotropy were found and correlated with hardness anisotropy and Mo2C crystal structure. Elastic-modulus values were obtained by microhard-uess and ullrasonic methods. Bonding mechanism of Mo2C is discussed. ROOM-TEMPERATURE microhardness indentations are useful for studying hardness anisotropy, slip, and twinning in brittle materials. Slip has previously been produced in this manner in and WS~~.~ Recently, the authors5 reported slip of the {10i0)(11~0) type produced by high pressure and microhardness indentations on hexagonal TiBz (c/a = 1.066) single and polycrystals. This slip system was also reported by French and ~homas' and Taka-hashi and ~reise~ for hexagonal WC (c/a = 0.976) crystals. These results suggest that prismatic rather than basal slip is favored in hexagonal nonmetallic materials having a c/a ratio considerably less than the ideal (1.633). Buerger precession and cylindrical X-ray rotation patterns were previously' taken on cleaved sections of the Mo2C single crystals studied in this work. Th~y were found to be hexagonal MoaC with a. = 3.0233A, co = 4.7344A, and C/O = 1.5660. The latter ratio is close to that of the beryllium metal (c/a = 1.57), which slips primarily on the (0001) plane: but also slips on the (1010) planes.'0 ~irconium" (c/u = 1.59) and titanium12 (c/o = 1.59) deform mainly by slip on nonbasal planes which contain a close-packed direction. This is due to the fact that for these two metals the initial resolved shear stress for slip on the (10i0) prismatic planes is lower than that on the (0001) plane. The prominence of basal rather than prismatic slip in metals of high c/o ratios is shown by cadmium (c/a = 1.89), zinc (c/a = 1.86), and magnesium (c/a = 1.62) which deform mainly by basal slip. However, in case of the latter, by stressing magnesium crystals in tension or compression parallel to the basal plane, slip on (10i0) planes can also be produced.13 Several hardness values for polycrystalline Mo2C are reported in the literature: Biickle ' and Samsonov'~ give a value of 1800 and 1479 kg per sq mm, respectively, at a 100-g load; and Kieffer and Benesovsk~'~ report a value of 1950 kg per sq mm at a 50-g load. ~ott'~ reports a Vickers hardness value of 2000 kg per sq mm, with the load unspecified. A Rockwell A hardness value of RA = 88 has also been reported.'' In the present work, for comparison with single-crystal Mo2C hardness values, a Khnloo value of 1600 It 150 kg per sq mm was found on 99.6 pct pure and 99 pct dense hot-pressed Mo2C. This work was undertaken partly to explain the considerable differences in hardness values reported for polycrystalline Mo2C. EXPERIMENTAL The Mo2C single crystals investigated were prepared by a Verneuil-type process using an electric arc by the Linde Co. of the Union Carbide Corp.lg The largest specimens grown were boules 7 mm in diam by 40 mm in length. The crystals had an average density of 9.04 g per cu cm, with a Mo + C content of 99.8 wt pct. The major impurities were: 100 ppm each Na, Zr, and Ca; 85 ppm 0, 55 ppm Fe, and 10 ppm each Cr and Ta. The crystals were found to be carbon-poor, the average carbon content being 5.73 wt pct (stoichiometric value is 5.89 pct). The molybdenum content was found to be 94.08 pct, which is nearly stoichiometric. Electron-microprobe traverses of selected specimens were done with a Phillips-AMR microanalyzer. Thin-film and carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to optical and electron-optical studies, specimens were mounted in Lucite and polished on a vibratory polisher using diamond-paste grades ranging from 9-1 p and Linde A powder for up to 48 hr. Dilute nitric acid was used for thin-section polishing and chemical etching for 1-15 min. Electrical-resistivity measurements at room temperature were taken with a Rubicon bridge, using gold contacts. For hardness measurements, a Tukon Microhardness Tester Type FB with Knoop and Vickers indenters was used. Measurements were taken at loads ranging from 25 to 1000 g; however, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Indentations of cracking classes 1 and 2 only were considered for hardness determinations.20)21 (There are six cracking classes, ranging from "class 1" for a perfect inden-

Jan 1, 1967

By Charles Y. Clayton

The shank, to give good service, should not upset nor should it cause excessive wear on the various parts of the machine. To fulfill these requirements, the steel must have a certain hardness—that is, resistance to deformation. The hardness is expressed in conventional terms, as Brinell or scleroscope number. Before deciding on the hardness that is proper, several factors should be considered; the most important are: type of drill steel used (whether hollow or solid), length of steel, nature of ground, air pressure, and hardness of hammer or anvil block (usually 600 Brinell). These are not all, but they are the most cogent ones. Without doubt, it would be better to use a shank that is too soft than one that is too hard. Most satisfactory service will be obtained from shanks that are just hard enough to resist any tendency to upset. To express the proper hardness in terms of Brinell numbers would mean a great many tests over a long period of time, or a study of drill steels that are being used successfully in the various districts. To obtain some information along this line, the persons making this investigation requested, a number of companies to send to them drill shanks that had been given the usual treatment at that mine. The results of the hardness tests are given in Table 1. The hardness values given in Table 2 are those of shanks known to have been quenched in water and drawn. These results show that where water quenching and drawing are in vogue the hardness is rarely under 400 Brinell.

Jan 1, 1923

By Charles Y. Clayton

The shank, to give good service, should not upset nor should it cause excessive wear on the various parts of the machine. To fulfill these requirements, the steel must have a certain hardness—that is, resistance to deformation. The hardness is expressed in conventional terms, as Brinell or scleroscope number. Before deciding on the hardness that is proper, several factors should be considered; the most important are: type of drill steel used (whether hollow or solid), length of steel, nature of ground, air pressure, and hardness of hammer or anvil block (usually 600 Brinell). These are not all, but they are the most cogent ones. Without doubt, it would be better to use a shank that is too soft than one that is too hard. Most satisfactory service will be obtained from shanks that are just hard enough to resist any tendency to upset. To express the proper hardness in terms of Brinell numbers would mean a great many tests over a long period of time, or a study of drill steels that are being used successfully in the various districts. To obtain some information along this line, the persons making this investigation requested, a number of companies to send to them drill shanks that had been given the usual treatment at that mine. The results of the hardness tests are given in Table 1. The hardness values given in Table 2 are those of shanks known to have been quenched in water and drawn. These results show that where water quenching and drawing are in vogue the hardness is rarely under 400 Brinell.

Jan 1, 1923

By T. A. Rickard

The earlier paper (Trans., xx., 463) describing this Victorian mining district, to which the present is supplementary, was mainly confined to the consideration of the "saddle-reefs," as scientifically the most interesting and economically the most important of the

Jan 1, 1893

A. Blainey (Ministry of Supply, Atomic Energy Research Establishment. Hnrtoell. England)—With ref- erence to the published work of Hausner et al. on the powder metallurgy of zirconium, it will be of interest to summarize briefly the results of preliminary work we have carried out on this subject at A.E.R.E., Harwell. For the early experiments we used zirconium

Jan 1, 1953

By John C. Osmond

One of the least known geologic regions in the U.S. is the area now called the Basin and Range Province. It is paradoxical that so little geologic information has been compiled for a province that has yielded billions of dollars worth of metals and is currently producing a small amount of oil. Regional stratigraphic studies of parts of this large territory have been published only recently, and regional structural interpretations of even parts of the province are rare in the literature. This, of course, does great injustice to the earliest workers: Gilbert, Russell, Le Conte, Spur, Louderback, and others, who recognized the area as distinctively different from the rest of North America. Their simplified picture of the structure of the ranges and the province as a whole is the groundwork for present understanding and has never been superseded. Since their early works, however, geologic data from the province has consisted largely of detailed reports of widely scattered mining districts. Each district has been described as though it were an island in an unknown sea.

Jan 3, 1960

By R. G. Bowman

Discussions of processes for the manufacture of white lead generally open with the statement that white lead is the oldest chemical pigment known to man. This fact is of more than historical interest; in the light of the present extensive use of white lead, it indicates that the compound possesses characteristics that make it unique among white pigments, and superior to all in its particular field. A greater variety of processes have been proposed for manufacturing white lend than for any other one chemical compound. Only a few of these processes have come into commercial use, however, and a large part of the present production here and abroad is made by the process used in ancient times. The outstanding disadvantages of the old process are that it is slow and laborious, affords no control of the product, and yields at best an impure material lacking in uniformity. Improved processes, sometimes classed all together as "quick processes," have had as their main object the shortening of the time required. Most of them accomplish this and some have yielded a superior product as well, but only two or three are now in use commercially. For centuries the manufacture and mixing of paints have been treated as an art, and the practice has been much influenced by tradition and precedent. There is a reluctance to abandon old materials for this purpose, and as few new uses for white lead have been developed, the adoption of the quick processes has been slow. The electrolytic production of white lead is not new, a large number of processes and forms of apparatus have been proposed and patented within the past 25 years, all directed toward the production of white lead, wholly or in part, by electrolysis. One or two of these processes were tried commercially but proved unsuccessful. Process The Sperry process, used by the Anaconda Lead Products Co., is the invention of Elmer A. Sperry, and was worked out to a commercial basis at the East Chicago plant. It resembles, in a general way, earlier methods, but embodies the features that make it possible to operate

Jan 1, 1926

By Royal Jackman

Two comprehensive papers have appeared regarding the forms of copper that occur in smelter slags, one by Frank E. Lathe1 and the other by C. G. Maier and G. D. Van Arsdale.2 These authors comment on other published results and draw conclusions from their own investiga-tions. The development of X-ray examination of minerals and improve-ment in high-power microscopic methods make it possible today to get additional evidence by means that were not available to earlier investi-gators. The present work was confined to reverberatory slags obtained from five different plants. Some definite conclusions were reached regarding the forms of copper present in these slags. In most cases these agree with some of the findings of Maier and Van Arsdale but new methods of attack were used in the investigation.

Jan 1, 1933

By P. B. Knuckey, D. Littleford

The Kalengwa mine, situated in a remote area of Zambia in Central Africa, has presented some unique problems to the planners engaged in developing the deposit. This small, high grade copper deposit contains some 1,688,000 tons of ore at a grade of 9.3% contained copper. Of this 362,000 tons is classified as high grade ore at 27.2% Cu, the coarse fraction of which can be fed directly to converters; 733,000 is classed as intermediate grade ore averaging 6.3% Cu, and 593,000 tons classed as low grade ore containing 2.1% Cu. The geology of the deposit and the establishment of the mining operation is fully described. A concentrator is being built at Kalengwa to treat the high grade fine product, intermediate, and low grade ore, whilst the coarse high grade ore will be trucked to the Copperbelt smelters for direct smelting. Details of metallurgical processing are given. The decision to truck the coarse high grade ore to the smelters on the Copperbelt necessitated the construction of a new 200-mile road, the setting up of a fleet of heavy ore transport trucks and associated equipment. The remoteness of the area from established communication facilities on the Copperbelt necessitated the provision of radio communications between Kalengwa and the head office at Kalulushi, and the establishment of a regular mine air service. The paper also describes the training of an unsophisticated local population in the operation of heavy plant and machinery, the establishment of the township, and the provision of health services.

Jan 1, 1972

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938

By J. Ruzicka

IN creep testing, material is subjected to a constant load, preferably at a constant temperature, and its rate of deformation is measured. The method of loading can be of various types but in this paper only creep testing under tensile load will be considered. The ordinary tensile test is essentially a comparison test in conditions that frequently bear little or no relation to those under which the test material is to be used in service. The purpose of creep tests is to measure the strength of the test material at slow rates of deformation that more nearly approach the rates realized in service. One purpose of this paper is to illustrate that the creep test, in addi-tion to its value as a service test, is superior to the ordinary tensile test as a sensitive tool for the comparison of certain metals in investigative testing. The other purpose is to describe equipment having distinctive features of design that make it especially suitable for such tests. Representative data obtained with this equipment on a group of rolled zinc-base materials are given. These data are compared with those from practical comparison tests of the creep type on weatherstrip fabri-cated from the same group of materials. The comparison illustrates the value of the fast creep test and of the equipment.

Jan 1, 1937

By A. L. Fentress, P. R. Bucky

The purpose of this paper is to present a scientific method for determining the proper span and shape of roof for safe and economical mining; at present, these two vital factors wherever pillars are left to support the roof are determined by local practice or general experience. To develop the method described here, experimental laboratory work was done. The arch adopted was a segment of a circle, a flat roof being considered an arch with an infinite radius. Hitherto, arches have been used underground without the background of stress analysis that generally precedes arch construction on the surface. In many cases results have not been as expected, because of the lack of knowledge of the factors affecting its strength and behavior. A theoretical and experimental study of arches should furnish information that will make it possible to design safe and economical surface structures as well as underground openings. For example, on the subject of mine drifts and tunnels, the present idea is that arching their backs increases their strength; this paper will indicate that this is not always true, and if it can be shown that under certain conditions arching becomes unnecessary an economic saving will result. In room-and-pillar work a question may arise as to whether arching the roof and gobbing the excavated material will result in timber saving, and a decrease in the dangers from falls of roof. It is to be distinctly understood that each mine must be treated as an individual problem, and that answers to these questions and many others can now be found after experimental laboratory data have been obtained. Mine-Arch Structure Fig. 1 shows the elements that affect the strength or behavior of the experimental arch. They are the span, crown thickness, radius of curvature, rise and restraint. The restraint in all cases was made sufficient to cause the arch to fail without displacing the restraining sides. Fig. 2a is a photograph of a model arch prepared for testing in the centri-

Jan 1, 1934

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By G. P. Connell, R. E. Gilmore, J. H. H. Nicolls

The purpose of this paper is to suggest a procedure for indicating the dividing line between noncaking coals and those that have weakly caking properties. A laboratory agglomerating test as an aid in classifying weakly caking coals is outlined and its merits in comparison with the standard agglutinating method advanced by the U. S. Bureau of Mines are discussed. No attempt, however, is made to discuss in detail either the different methods for determining "caking" and "agglutinating" indices or the various systems of classification. Two methods, differing somewhat in procedure, have been employed and recognized as suitable for determining the caking or agglutinating values of coals; namely, those in which an inert material such as sand, electrode carbon, etc., has been mixed with the coal before being heated, and those in which the coal is carbonized alone. In all such methods, the coal with or without the inert material is in the finely divided state and the index or value sought is derived from the examination of the residue after heating in a closed crucible or other container. The procedure outlined by Selvig, Beattie and Clellandl is the most recent representative of the method using sand as inert material, while the agglomerating test described below is representative of the method in which the coal is carbonized alone. The standard volatile-matter determination affords a means for observing the coking properties of a coal, and this has been described by Rose2 as the simplest of all coking tests. According to him, "the resulting coke button will indicate whether the coal is noncoking, feebly coking or strongly coking," despite the fact that "almost every condition in this test is at variance with large-scale carbonizing practice." Lessing,3 the

Jan 1, 1934

By R. Woods

INTRODUCTION Gaudin (1), considered that "the mechanism of mineral collection is the central problem of flotation theory". From their work on adsorption phenomena in flotation for more than fifty years (2), Gaudin and his co-workers have made major contributions to the elucidation of this mechanism, a fact acknowledged by their contemporaries in the field (e.g. (3)). Their investigations in a number of areas, e. g. demonstrating that submonolayer quantities of adsorbed collector species can induce flotation, or identifying the influence of substances which can activate or depress (1), have helped to provide the basis for and the development of a theory to account for the interaction between mineral and collector. It was established in the late fifties (4) that the presence of oxygen is a prerequisite for the flotation of metal sulfides with thiol collectors. This fact rendered inadequate the concept of simple ion adsorption being responsible for rendering these minerals hydrophobic. The requirement for oxygen has been explained (1) in terms of this species being a component in chemical reactions between the sulfide surface and the collector. Gaudin has been instrumental in identifying the products of chemical reactions at sulfide minerals (1, 5), a line of work which has been continued particularly by Finkelstein and co-workers in South Africa (6). In presenting a detailed mechanism of the mineral-collector- oxygen interaction, it has often been considered that the mineral surface [must] first be oxidized to a metal oxy-sulfur species which

Jan 1, 1976