By J. Bruce Wagner, Roger L. Levin

Lattice-parameter measurements have been carrzed out at room temperature on undoped and on chromium-doped wustite as a function of oxygen concentration. Results may he expressed by for the undoped uustite. These data are in agreement with and extend the work of' Jette and Foole. The present results are consistent with the cation vacancy model. for metal- deficil wuslite, both undopen and doped. SEVERAL investigators have made room-temperature lattice-parameter measurements on wustite as a function of composition. Jette and Foote used these measurements to determine the phase limits of wustite. Willis and Rooksby and Benard have also measured the lattice parameters of wustite at room temperature, but their values of a. vary considerably from those of Jette and Foote. In conjunction with Studies' on the transition from surface-controlled heterogeneous reactions involving CO-C02 oxidation of metals, lattice-parameter measurements on undoped and chromium-doped wiistite have been performed. These studies are especially needed to clarify conflicting data of previous authors, to extend the data to the stability limits of wiistite as determined by Darken and urr,6 which include a larger range of existence than that found by Jette and Foote, and to test by X-ray means the role of chromium as a vacancy producer in wiistite.

Jan 1, 1967

By Alexander L. Field

IN a previous paper,' the experimental methods used and some of the results obtained in an extensive investigation of steels containing zirconium were described. The present paper considers in greater detail one of the most interesting of these effects, namely, the elimination of " red shortness" and the occurrence in steel of a compound of zirconium and sulfur. A consideration of the actual percentages of zirconium, manganese, and sulfur in numerous steels in the light of behavior during rolling has led to new conclusions of the most practical import regarding the reciprocal relationships of these elements. The microscopic examination of high-sulfur steels containing zirconium has also been productive of interesting results. Before discussing the experimental data in question, it may be stated, briefly, that the rettetion between zirconium and sulfur in molten steel may be represented by the simple equation, Zr + 25 = ZrS², and that the zirconium sulfide thus formed occurs in the finished steel in the form of gray-colored inclusions, closely resembling manganese sulfide and, like the latter, exhibiting plasticity at rolling temperatures. Molten steel containing zirconium retains such a negligibly small amount of oxygen in solution that the foregoing reaction goes to completion. Hot-rolling Properties of High-sulfur Steels with and without Zirconium The chemical composition of twenty-eight steel ingots embracing eleven heats made in a basic-lined electric furnace is shown in Table 1. The practice followed in the manufacture of these high-sulfur steels was described in the previous paper. Table 1 also gives the behavior of the

Jan 1, 1924

By Harry V. Welch

Early in the development of the art of metallurgy, it was noted that a distinct difference existed in the character, collection possibility and health hazard of the "smoke" from lead furnaces and those from copper plants. Zinc-plant fumes, although not so detrimental to health, were closely allied in nature to those of the lead works. In Cottrell plants, there are sufficiently distinct differences in operation and amount of construction between those for lead and copper to justify their consideration under separate headings; therefore, while the application of the process at copper-reduction works was covered by the writer some two years ago in the Transactions1,† this discussion will confine itself more distinctly to "fume" collection. General information on the process has been presented in numerous articles and by many authors: Cottre112, Schmidt3, Bradley4, Anderson6, Labbe6, Shiga7, Rathbun8. "Fume" may be defined as material, metal or nonmetal, elemental or compound, evolved as a vapor from a furnacing or chemical reaction and condensing, chilling or reacting within the gas stream to yield a solid form, and in this definition liquid particles are solids in a sense as distinguished from gases or vapors. Such condensed particles are of minute form, on the order of "smoke," and, for example, on the order of a few hundredths of 1 micron (1 micron = 1/25,000 in.) to perhaps 3 microns, with agglomerates, in relatively small proportions of many particles. Metallurgically typical fume products are lead compounds, oxides, carbonates and sulphates; elemental zinc, more commonly encountered as a fume particle of zinc metal with a surrounding "skin" of zinc oxide; arsenic, both metal and oxide and some of its more complex salts such as added sulphates as found in flue dusts; antimony, more particularly its oxide forms; and elemental sulphur, sometimes a troublesome product, in Dwight-Lloyd sintering-plant fumes. These products, particularly the elemental or lower oxide forms, have relatively appreciable vapor pressures at the existing operating temperatures as reported by Welch and Duschak9, Ingold10, Johnstonll, Millar12,13.

Jan 1, 1937

By H. A. Stacy

THE ability of galvanized sheet steel to withstand severe bending is of very great importance as relates to all such sheet material which, in service, is not used in the flat condition in which it is purchased. A "bend-test" clause is found in, all specifications for material of this kind. In the attempt to draw up a specification for galvanized sheet steel the subcommittee of the Federal Specifications Board having this work in charge, soon found that there was a surprising lack of published data and apparently very little available from manufacturing sources upon which to sustain or reject the various requirements embodied in the tentative specification which, in turn, had been based largely upon other specifications submitted to the subcommittee for this class of material. Specifications from 25 sources were received; 10 Government specifications, 10 from private users of such material, and five from manufacturers. The main points raised were: (1) The minimum mandrel thickness, expressed in terms of the thickness of the sheet tested, over which sheets with different weights of coating can be bent 180°, without serious damage to the coating; (2) the minimum radius of curvature on the inside of the angle in 90°-bends in such material; (3) effect of double seaming on the coating; (4) uniformity in the thickness of coating over a sheet, particularly as relates to the results of bend tests. In view of the uncertainty existing, it was considered very desirable for the subcommittee to conduct a series of tests in order to secure reliable information.

Jan 10, 1926

By Edward A. Loria

Vanadium is one of the materials being considered for use in fast-breeder nuclear reactors. It is a good heat conductor and nearly transparent to radiation, properties regarded as ideal for nuclear fuel containers. The problem has been the metal lacks ductility needed for forming. In our program at Reno Laboratory the effects of the U.S. Bureau of Mines (previous affiliation) the effects of oxygen, nitrogen, and carbon have been reported21,22 nd most recently the effects of boron and boron with carbon.23 The continuing study by the Ames Laboratory of the effects of hydrogen, the most subtle and fugitive element in its relationship to structure and properties, is commendable. The solubility of oxygen, nitrogen, and hydrogen in vanadium (and other bcc metals as well) is related to material purity. With the available limit on metal purity and the interaction (clustering) of hydrogen with the other interstitial and substitutional elements present in their base metal, would the authors comment on the tolerance of hydrogen in relation to oxy- gen that will avoid intergranular fracture and above what content or how seriously harmful in oxygen at various carbon levels? Understanding the true effects of hydrogen (and other interstitial impurities) in vanadium depends on knowledge of the amount present under various conditions and its distribution between various possible positions. Significant amounts of hydrogen may be in "thermo-dynamic" solution, but not as individual atoms in interstitial positions. It may be in grain boundaries, in subgrain boundaries, in vacancies, or in dislocations. Some of the hydrogen may be paired or in complexes with impurities in substitutional solid solution in vanadium. This makes the analysis of the effect of hydrogen vastly more difficult. It should not be expected that hydrogen in grain boundaries will affect slip in the same manner as hydrogen in interstitial positions, nor will the complexes react to heat treatment the same way as hydrogen in dislocations. It is gratifying that the authors have quoted results from two of our inestiations,' but neglected one2' which applied the Petch theory to electrorefined vanadium of high purity and analyzed the effects of oxygen, nitrogen, and carbon on the ai and ky values obtained by the extrapolation and grain size methods. Details can be found in the paper. Briefly, we obtained a ui value of 10,300 psi (t = 5150 psi) at 273°K. The metal also exhibited profuse twinning with high ductility at 123" and 77°K. Nitrogen was more effective than oxygen in increasing ui, the increase being about twice as much for the same impurity level. Carbon additions resulted in only minimal changes in Ui. The corresponding ky increased as oxygen and nitrogen increased, with nitrogen being more effective. Carbon additions resulted in little change. Although the difference in yield strength of vanadium was explained on the basis of the Cottrell-Bilby model of the tearing away of dislocations from the impurity atoms,

Jan 1, 1970

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

W. 0. HOTCHKISS,* Madison, Wis.-When we began to do geological field work in the Lake Superior region, we found a correlation in existence, and, as youngsters, accepted all that as settled. Both Mr. Allen and I, since that time, have seen a great many things that were not apparent nor visible to Van Hise, and those who worked with him; we realize now that the correlation was not final and that much remains to be determined concerning geology of the Lake Superior region. My attitude on this matter is that we should not publish an amended correlation as a final thing. We should avoid, in every way possible, foreclosing the minds of those who follow us in working in the geology of this region. As a matter of fact, no correlation can be final at present, because facts and data are accumulating so rapidly that every classification must be immediately modified to fit further observation. Consequently, my attitude in this matter would be, instead of saying that the iron formations of the Lake Superior region are all Middle Huronian, to say that there may be three Huronians-or four or five- we do not know. I believe it is better policy to hold to our present correlation. I do not believe there is any economic benefit to the mining man or the geologist working on problems relating to explorations for iron ore, that cannot be just as well solved by maintaining our present correlation, with a. wholesome idea of our lack of knowledge and the necessity for further detailed work. Then, if any new horizons are discovered in any particular range, the minds of the investigators will not be foreclosed because some one has said that all the iron formation is in the Middle so that there is no use looking elsewhere for it. There is use looking elsewhere, in many cases, as the ore deposits become exhausted.

Jan 1, 1920

[ ]

Jan 1, 1938

By T. F. McCormick

THIS year, 1950, is the golden anniversary of the construction and operation in this country of a tube mill for the sole purpose of fabricating aluminum alloy tubing. For a short period prior to the beginning of this mill, aluminum alloy tubing was obtained from foreign sources or produced in mills fabricating other metals. Indeed, it was a very short period because aluminum itself was a newcomer in the field of metals. The first sheet rolling mill had been in operation just eight years and a rod rolling mill for the production of wire and cable had been functioning one year. The first tube mill for aluminum was built by the Aluminum Co. of America in May 1900 and started production with four draw benches and five men, including the mill superintendent. The building itself was a lean-to attached to a sheet-rolling mill at New Kensington, Pa. The cost of equipment, including the draw benches, dies, mandrels, and other tools, was about $5000. This figure seems absurd in the present day but nevertheless it was questioned at that time whether or not such a large sum should be spent to embark on a new and uncertain venture. The initial production system for the new mill consisted of casting round hollow ingots in a tilting-type iron mold, reducing the ingots to bloom size outside the plant, and finally drawing to size on the draw benches. This method of producing aluminum alloy tubing survived just two years, as blooms of satisfactory quality were not obtained consistently. It was superseded by the cupping method in which a 24-in. diam circle cut from a rolled plate was formed into a tube bloom using first a small cupping press and then a push bench. It was stated that tubing so produced was limited to a maximum diameter of 2 3/4 in. and to wall thicknesses varying from 12 to 24 gage. However, for the first time all the operations were performed at one plant and the result was a quality product. Later larger cupping presses and push benches were obtained and the method continued to be the principal one for aluminum alloy tubing for almost a quarter of a century. During the interim the use of a Alan Mannesmann -type billet piercer was explored and it was used to some extent, but failed to produce consistently a smooth inside surface suitable for drawing with aluminum alloys. Experiments started during the latter stages of World War I in the production of tube blooms with a hydraulic extrusion press, led to the use of this type of equipment to make tube blooms for further drawing during a change-over period extending from 1925 until 1930. At this time the cupping method was discarded completely. From these humble beginnings, the aluminum alloy tubing business expanded until well over six million pounds were produced in a single month in the United States during World War II. The major portion of this production was in strong alloys which did not appear in the tubing picture until 1022, when 17S alloy tubing was introduced for aircraft construction.

Jan 1, 1951

By R. L. Stegman, M. R. Achter

Nickel, fatigued in vacuum, shows intragranular crack initiation and growth at low temperatures. An increase in temperature initially prolongs fatigue life due to a more homogeneous distribution of slip. With a further temperature increase, the mode of failure undergoes a transitiotz to intergranular crack initiation with concurrent recrystallization which results in a shorter life. The transition temperature varies with bending strain and specimen purity. UNTIL recently, very little work has been done on the effect of temperature on the mechanism of fatigue and the resultant variation in fatigue life. Except for mild steel, where strain aging raises the strength at moderate temperature, fatigue lives had been shown to decrease with an increase in temperature. In their review article, Allen and Forrest' summarized the work of McCammon and Rosenberg and of Forrest and Mann on the fatigue of copper from -269" to 325°C. The fatigue life vs stress curves remained roughly parallel over this temperature range, the fatigue strength decreasing progressively with increasing temperature. When testing was done in vacuum, the present authors' found the results for nickel were different from those quoted above. Initially, the fatigue lives increased with temperature and then decreased as a grain boundary mode of failure was observed. The initial increase was attributed to a more homogeneous distribution of slip, a condition which was not as conducive to crack initiation as the bunching of slip lines observed at 20°C. Ronay, Reimann, and wood3 observed a similar change of slip line distribution in brass, tested in air, with rising temperature. Our previous observations were based on preliminary work with relatively few specimens, fatigued at comparatively low strains. To learn more about the mechanisms, the present investigation was undertaken for the purpose of studying systematically this effect over a wider range of strains and as a function of purity of the nickel. EXPERIMENTAL PROCEDURES The testing equipment, procedures, and specimen geometry have been described elsewhere.' An optical technique to measure bending strains was used as de-

Jan 1, 1968

By I. Fatt

This paper proposes the network of tubes as a model more closely representing real porous media than does the bundle of tubes. Capillary pressure curves are derived from network models and pore size distributions are calculated from these curves. In this way is shown the difference between the true and calculated pore size distributions when the capillary pressure curve is used to obtain pore size distribution for porous media. INTRODUCTION Despite the technological importance of the laws governing flow through porous media, many of these laws have not yet been clearly formulated. This is especially true of the laws governing multiphase flow. The static properties, such as the capillary pressure curve, are also not at present interpretable correctly in terms of the pore size distribution and other structural properties of porous media. In the absence of any well founded theoretical description of fluid flow through porous media, many empirical descriptions have been proposed. In addition to the strictly empirical flow equa- tions, some equations have been developed rigorously from simple geometrical models of the pore spaces. These equations are only as valid as is the model used in their development. The two models used in the past, the sphere pack and the bundle of tubes, have been too simple, and as a result, the equations derived from them have failed to predict the observed properties. Agreement between theory and observation has been achieved for these models by inserting parameters of doubtful physical significance. The work to be reported here was undertaken in the belief that the study of a model more closely resembling most real porous media than does the sphere pack or bundle of tubes would yield useful information concerning the structure of real porous media and the relation between structure and flow properties. There was no intention of developing any calculational procedures, as for example calculating relative permeability from capillary pressure data. The objective of the study was instead to develop a better qualitative understanding of the relation between the various measurable properties of porous media. The model chosen for study is the network of tubes in which each tube represents a pore space in the porous medium. Microscopic observations leave no doubt that sandstones and clastic carbonates are three-dimensional irregular networks of irregularly shaped pores. The irregularity of these structures makes any accurate theoretical study of their properties impossible. Results from an oversimplified model such as the bundle of tubes are worthless when applied to real systerns. The sphere pack model, on the other hand, not

Jan 1, 1957

By B. G. Klugh

The present paper represents a preliminary investigation of the ultimate structure of iron-bearing materials which have been subjected to heat treatment for the purpose of agglomerating the fines, or for chemical changes, or for both. Primarily, the object of this inquiry was to determine the relation of the microstructure of each of these materials to its specific susceptibility to the action in the blast-furnace. It is hoped that this small contribution will serve as a nucleus to a line of research that will throw some light upon the debated questions involved in blast-roasting. Thus far the investigation has been conducted along lines of analogy of known principles, rather than through the application of any well-defined system of microscopic petrography. This is obviously due to the fact that we are dealing with ma-terials which are the artificial products of a new art, rather than with the natural materials from which the essence of the pure science has been evolved. In the limited time allowed for this research, it has been conducted upon those materials the chemical content of which allows of their use commercially in the blast-furnace. The following microphotographs are arranged in the order of the degree of complete fusion to which the mass in question has been subjected, in effectively binding the particles together. A very notable fact here clearly demonstrated is that the degree of fusion to which the material has been subjected is inversely proportional to the reducibility of the product. The characteristic of the material under consideration to which reducibility is almost universally attributed call be progressively traced in the following arrangement, through the identity of the obvious microscopic constituent. Furthermore, the degree of fusion to which a bod? has been subjected is recorded in the presence of resultant products of fusion in that body. Such readjustment is generally apparent

Jan 1, 1914

By S. B. Twiss, P. R. Basford

The relationship between areas of iron powders, briquettes, and sintered compacts and tensile strength has been determined. It has been found necessary to distinguish between two types of areas which exist in such powders—a macroscopic area due to the shape and size of particles and a microscopic area due to pores and cracks in the surface. Only the macroscopic area, specifically the area due to particle irregularity, contributes to tensile strength; the microscopic area cannot be forced into contact with adjacent particles ond does not participate in bond formation. Of the two methods of area measurement employed in this study—permeability to liquids and gas-phase adsorption—only the former is useful for determining the roughness factor. A measure of this roughness, (area measured by permeability to liquid) -f- (orea of powder with the same size distribution, but made up of spherical particles), is shown to be uniquely related to tensile strength at constant density. The other important factors in determining the strength of sintered-metal compacts are the density and presence or absence of surface oxide. THE manufacture of metal parts by the process of powder metallurgy is an important and rapidly growing industry. Progress has been rapid and continuous, largely because of the excellent research in the field. Nevertheless, the process remains inherently complex and empirical. Several investigators have shown that the properties of the final compact must depend on many variables; namely, shape,' size distribution,"-" nd compositiona of the original particles, the pressure necessary to compress to the desired density, the density of the compact, the time and temperature of sintering, and so on. Through the application of some new techniques to the study of powders and compacts, and the correlation of a number of observations of known variables, the present paper attempts to clarify and simplify the underlying theory of the powder-metallurgy process. Any theory must start with the obvious fact that the strength of a compact, its most useful property, is due to the formation of welded areas between adjacent particles, and attempt to deduce what effect other variables will have on (a) the area and (b) the intrinsic strength of these welds. Such welded areas can be demonstrated by electron micrographs, as in Fig. 1. It was believed that (a) could be most directly studied by means of surface-area measurements on the original powders and on the compacts made from them; the area decrease should be related closely to the welded area. A representative group of eleven iron powders from commercial sources, and made by a variety of processes, was chosen for this study. In addition to the surface-area measurements, correlations were established between the tensile strength and all the known variables which might possibly affect it. The results are quite unexpected. They indicate that the situation is much simpler than the authors had anticipated. The strength of the sintered compact is determined, indeed, by no more than three variables; viz., the irregularity of the original particles, the density of the compact and, in exceptional cases, the amount of surface oxide. All three had been recognized previously as having some effect on the tensile strength, but in the absence of the special techniques and interpretations to be developed here, there could be no suspicion that they were the only relevant variables. Materials and Methods Material—All the iron powders were commercial products obtained from the Amplex Division of Chrysler Corporation. Powders A, B, C, and J were very pure electrolytic iron. Powder D was made from oxidized scrap reduced by heating with an excess of cast iron. Powder E was a high-grade iron ore reduced by hydrogen. Powder I was prepared by atomizing molten cast iron in an air blast, quenching the droplets in cold water, and crushing the coarse powder. Mill scale (oxide) is added and the mixture heated to reduce the high carbon content. The other powders were all prepared by reduction of iron oxides, such as mill scale. They

Jan 1, 1959

By A. H. Geisler, R. F. Mehl, C. S. Barrett

The mechanism by which the supersaturated solid solution of 20 per cent silver in aluminum decomposes has been reported in two previous publications.1'2 The analysis of streaks in Laue photograms showed that thin platelike particles (the so-called Guinier-Preston aggregates) form upon matrix planes in the early state of decomposition.1 The size of these particles is larger, the higher the temperature at which they form in accordance with nucleation theory;³ at all temperatures they increase in size with aging.2 When they have grown thick enough to afford three-dimensional diffraction, powder X-ray photograms show that the structure is not that of the equilibrium precipitate but that of a transition lattice . Sincc this is also platelike in shape and also lies upon the (III) matrix planes with the [IIO] direction in the matrix parallel to the [II.O] direction in it seems likely that the original platelet particles are merely in an early stage of formation, and thus finely dispersed. The atomic spacing and pattern on the (00.1) plane in y' are identical with those on the (111) matrix plane to which it lies parallel, and since comparable directions in the two planes are parallel, the lattices are thus coherent at the interface; an analogous coherence has been found in aluminum-copper alloys.3 The structures y' and y are both close-packed hexagonal and are oriented alike; they differ only in interatomic distances. Consequently, y' is regarded as y strained from its ordinary dimensions by the lattice coherency between it and the matrix.2 The lattice movements that transform the matrix to the equilibrium precipitate appear to be very simple.2 The mechanism of precipitation in this system is simpler and is more precisely known than that in any other system hence the system should be a profitable one for the difficult task of correlating property changes with structural alterations. The present report provides additional studies on powder X-ray diffraction from alloys of 10 per cent, 20 per cent and 30 per cent Ag, and presents the correlation of crystallographic changes with changes in microstructurc, Brinell hardness and electrical resistivity of the three alloys. Preparation of Samples and Experimental Procedure The preparation of the 20.2 per cent Ag alloy has been described2 Alloys containing 9.9 and 29.7 per cent Ag were prepared from 99.97 per cent A1 and 99.99+ per cent Ag using a similar procedure. Rolled

Jan 1, 1943

By R. F. Mehl, C. S. Barrett, A. H. Geisler

The mechanism by which the supersaturated solid solution of 20 per cent silver in aluminum decomposes has been reported in two previous publications.1'2 The analysis of streaks in Laue photograms showed that thin platelike particles (the so-called Guinier-Preston aggregates) form upon matrix planes in the early state of decomposition.1 The size of these particles is larger, the higher the temperature at which they form in accordance with nucleation theory;³ at all temperatures they increase in size with aging.2 When they have grown thick enough to afford three-dimensional diffraction, powder X-ray photograms show that the structure is not that of the equilibrium precipitate but that of a transition lattice . Sincc this is also platelike in shape and also lies upon the (III) matrix planes with the [IIO] direction in the matrix parallel to the [II.O] direction in it seems likely that the original platelet particles are merely in an early stage of formation, and thus finely dispersed. The atomic spacing and pattern on the (00.1) plane in y' are identical with those on the (111) matrix plane to which it lies parallel, and since comparable directions in the two planes are parallel, the lattices are thus coherent at the interface; an analogous coherence has been found in aluminum-copper alloys.3 The structures y' and y are both close-packed hexagonal and are oriented alike; they differ only in interatomic distances. Consequently, y' is regarded as y strained from its ordinary dimensions by the lattice coherency between it and the matrix.2 The lattice movements that transform the matrix to the equilibrium precipitate appear to be very simple.2 The mechanism of precipitation in this system is simpler and is more precisely known than that in any other system hence the system should be a profitable one for the difficult task of correlating property changes with structural alterations. The present report provides additional studies on powder X-ray diffraction from alloys of 10 per cent, 20 per cent and 30 per cent Ag, and presents the correlation of crystallographic changes with changes in microstructurc, Brinell hardness and electrical resistivity of the three alloys. Preparation of Samples and Experimental Procedure The preparation of the 20.2 per cent Ag alloy has been described2 Alloys containing 9.9 and 29.7 per cent Ag were prepared from 99.97 per cent A1 and 99.99+ per cent Ag using a similar procedure. Rolled

Jan 1, 1943

NEW MEMBERS The following list comprises the names of those persons who became members during the period Mar. 10, 1916 to Apr. 10, 1916. ALLEN, P. R., Pres., McAlester Coal & Coke Co., Knight Templar Bldg., McAlester, Okla. BERNARD, CLINTON PERCIVAL, Min. Engr., Care Forminiere Mission Kasai, Tschikapa, Congo Belge, W. Africa. CARPENTER, GEORGE 0., Vice-Pres National Lead Co. St. Louis Mo. CLARK, WILLIAM ANDREWS, JR., Min. Engr., Pres., Elm Orlu Mining Co., Butte, Mont. CLAYTON, CHARLES YANCEY, Asst. PrOf. of Metallurgy and Ore Dressing, Missouri School of Mines, Rolla, Mo. COHEN, JULIUS MILTON, Mgr. Croesus Gold Mines, Ltd., Matheson, Ont., Canada. CRAMER, WILLIAM BRONSON, Met. at Concentrator, Old Dominion Copper Min. & Smelt. Co., Globe, Ariz. DAHL, SIMEON H., Mill Supt., Messina Transvaal Dev. Co., Messina, Transvaal S. Africa.

Jan 5, 1916

By E. H. Bunce, E. C. Handwerk

The inherent difficulties of zinc smelting arise from the fact that metallic zinc is volatilized at the reducing temperature of zinc oxide and thus is liberated in the form of a vapor. This vapor must be subsequently condensed to obtain metallic zinc, first in molten and eventually in solid form. Zinc vapor is sensitive to oxidation not only by air but by combustion gases containing carbon dioxide. It is, therefore, necessary to carry out both the reduction and the condensation operations in a closed system consisting of an externally heated muffle with attached condenser from which extcrnal oxidizing agencies are excluded. However, the reoxidation of zinc vapor cannot be entirely prevented by excluding external sources of oxidation. Internal sources of oxidation are necessarily present when oxidic zinc ores are reduced by a carbonaceous reducing agent. The reduction reactions themselves involve, first, the production of carbon monoxide in an amount at least equal in volume to the zinc vapor produced in the reaction, and, second, the formation of carbon dioxide. Not all of the carbon dioxide is reduced again to carbon monoxide by the excess carbon in the time available, and the slightly oxidizing condition, which results, seriously affects the efficiency of the condensation of the zinc vapor to the metallic state. In the past the difficulties arising from these causes have limited practical zinc smelting on an industrial scale to the use of small retorts equipped with small condensers. The retorts had to be small, because a closed refractory container capable of excluding oxidizing gases from the heating chamber surrounding the retort could not be built in large dimensions. The size was also limited because ordinary refractories when thin enough to conduct heat readily are not capable of sustaining a heavy load of charge at high temperature. Moreover, a loose charge of zinc ore and carbonaceous reducing material such as fine anthracite coal or coke breeze is a poor conductor of heat, thus limiting the cross section of the retort. The operation of these small retorts requires arduous

Jan 1, 1937

By AIME

One of the operations of the J. L. Shiely Co. is quarrying in a hard granite gneiss with intrusions of gabbro or trap. During the winter of 1948-1949 the quarry ramp was lowered about 30 ft and during the 1949 season practically all drilling was done from the quarry floor, developing a face from 72 to 83 ft for the entire quarry area. The performance and cost table shows our record for 1948 and 1949.

Jan 1, 1950

By N. D. Shutler

This paper describes a numerical mathematical model of the steamflood process that depends on fewer restrictive assumptions than models previously reported. The solution, however, is obtained economically. Example calculations are presented that, on comparison with experimental results, tend to validate the model. Results that expose certain process mechanics are discussed. The model describes the simultaneous flow of three phases — oil, water and gas — in one dimension. It includes the effects of three-phase relative permeabilities, capillary pressure, and temperature- and pressure - dependent fluid properties. Interphase mass transfer of water-steam is allowed, but the oil is assumed nonvolatile and the hydrocarbon gas insoluble in the liquid phases. The model allows heat convection in one dimension and two-dimensional heat conduction in a vertical cross-section spanning the oil sand and adjacent strata. The hydrocarbon-steam gas composition is tracked, but the effect of gas composition on water-steam phase behavior is neglected. The model is solved numerically in three separate stages. The three-phase mass balances are solved simultaneously using Newtonian iteration on nonlinearities occurring in the accumulation terms. The energy balance is solved separately by noniterative application of the alternating-direction implicit procedure. Separate solution of the composition balance is accomplished by straightforward solution of the finite difference equations. The method of effecting nonsimultaneous, stable solution of the mass and energy balances is the key to the success of the model. INTRODUCTION Mathematical tools as well as laboratory and field experiments are necessary to help us understand the complex steamflood process. A mathematical model can expose process mechanics and show the relative importance of process variables, but this ability is often limited by restrictive assumptions. Most known models of steam processes,l-5 with the exception of the model of Gottfried,6 are "simplified" in that they involve analytic approximations and require many restrictive assumptions. The primary utility of these methods lies in the routine use as an aid in engineering design. By contrast, the comprehensive model presented here is numerical and requires far fewer restrictive assumptions. It finds its primary utility as a research tool. It serves as an aid in understanding the nature of the process, in interpreting laboratory experiments and in evaluating and developing simpler mathematical models for engineering design. The major reason why previously presented models have been confined to the "simplified" class is evidenced by the one published exception. In 1965, Gottfried6 presented a numerical model for the combustion process of which the steam process is a subset. The result is a comprehensive tool (though it neglects capillarity and two-dimensional heat conduction) that is troubled with convergence problems and that requires 2 to 3 hours of IBM 7094 time to complete a calculation. Though our present model does not simulate combustion, it does consider capillarity and two-dimensional heat conduction and it overcomes the convergence and computer-time problems. MATHEMATICAL DESCRIPTION OF STEAMFLOODING FLUID FLOW The equations employed to describe three-phase fluid flow are of a familiar form. Darcy's. law provides expressions for the velocities of the three phases (oil, water and gas), which, when combined with oil, water and gas mass balances, give the partial differential equations governing flow of the

Jan 1, 1970