Jan 1, 1942

By T. D. McKinley

Theory, operational characteristics, and indicated precision and accuracy of analytical methods based on vacuum extraction, equilibrium pressure, and combustion approaches are reviewed. At the present time vacuum extraction at 1400°C and the equilibrium pressure method are recommended for determination of hydrogen in titanium and titanium-rich alloys. UNTIL a few years ago the role of hydrogen in titanium was an unknown factor with regard to its effect on the physical and mechanical properties of the metal. However, following the work of Jaffee and othersa-" it is now generally acknowledged that hydrogen has a degrading effect on titanium and its alloys. The chief manifestations are a decrease in impact strength in -systems and delayed cracking in a-ß systems. Since hydrogen does have a de- grading effect on titanium it is essential to control it within tolerable limits. It then follows that procedures for quantitative estimation of hydrogen are a primary requirement for the industry. For greatest benefit these methods should be simple, rapid, and precise. In addition to having these virtues, methods must be easy to duplicate in both equipment and technique to gain widespread use. After inherent accuracy has been established, the, required precision to make a method acceptable is dependent largely on the nature of the work at hand. Ability to obtain a representative sample has a pro-

Jan 1, 1959

By K. M. Rolls, F. W. Reuter, J. Wulff

The superconducting behavior and microstructural characteristics of a nominal Nb-40 wt pct Ti-0.239 wt pct O alloy were studied as a function of ther mo -mechanical processing treatment. Critical current density us applied transverse magnetic field was obtained for 0.010-in.-diam wires at 4.2°Kin steady fields 14 to 110 kG. Both optical metallogvaphy and transmission electron microscopy were used to delineate the micros tructures of the same wires. It wan found that a 1-hr 500°C precipitation heat treatment after cold drawing to final size led to the highest critical current density. Heat treatment at 600°C also led to a high critical current density, but the precipitate differs in kind and form from that at 500°C. The resistire critical field was also found to be sensitive to precipitation heat treatment since the effective composition of the superconducting phase changes. This is discussed in terms of the oxygen in interstitial solid solution. Two types of high-field superconducting wire are at present used in the construction of high-field superconducting solenoids. These types are solid-solution alloy wire such as Nb-Zr and Nb-Ti and composites of the brittle inter metallic compound Nb3Sn. The latter generally have a high super cur rent-carry ing capacity which is difficult to vary if properly made. The supercur rent- carry ing capacity of the former can be varied drastically and often predictably by suitable thermomechanical processing treatments. In general, the critical current density Jc of the solid-solution type of alloy is increased by cold work and by additions of interstitial elements along with aging heat treatments. The imperfections which result are be-iieved to be responsible for the observed increase in Jc. In 1962 Kneip and coworkers1 found that the critical faurrent density of Nb-Zr alloys could be increased by proper heat treatment preceded and followed by cold work. Betterton and coworkers2 using a Nb-25 at. pct Zr alloy found that small additions of oxygen or carbon enhanced the effect of this heat treatment. They suggested that the interstitials present aided precipitation in the alloy, leading to a filamentary structure with superior properties. If the precipitation heat treatment was omitted, interstitial additions had a negligible effect on Jc. wong3 showed that higher heat-treatment temperatures lowered Jc. Walker and co-workers,4 who studied microstructure (by transmission electron microscopy) as well as superconductivity, found that the Jc anisotropy introduced by cold rolling was itself affected by heat treatment. They were unable to clarify the relation between microstructure and critical current density, although evidence of precipitation was indicated. More recent investigation of Nb-Zr alloys,5,6 besides showing that structural defects and fiber ing due to cold work and precipitation serve to raise Jc, also elucidate important optically observable microstructural changes which occur upon precipitation. In these reports, coarsening of the microstructural features was found to decrease Jc. Vetrano and Boom,7 who studied Ti-20.7 at. pct Nb, found that Jc was increased to a maximum by a 415°C, 3-hr heat treatment following quenching from 800°C and cold working. Heat treatments can also affect the resistive critical field Hr. Final-size heat treatments of Nb-Zr wire can lower Hr drastically if gross phase decomposition occurs5'* or moderately if the effects of cold work are eliminated without changing significantly the composition of the phase of interest.3,5,6,8 The percentage of oxygen which can be added to Nb-Zr alloys to enhance Jc is limited by the difficulty of subsequent cold drawing. Since Nb-Ti and Ta-Ti alloys in contrast can tolerate appreciably higher percentages of oxygen, it was decided to investigate the superconducting behavior of various alloys in these systems. The present paper describes the results of adding oxygen to a nominal 40 wt pct Nb alloy as a function of thermomechanical treatment. I) EXPERIMENTAL PROCEDURE A small alloy ingot was prepared from high-purity niobium, iodide, crystal-bar titanium, and Nb2O5 powder by arc melting on a water-cooled copper hearth in a gettered argon atmosphere. The ingot was turned and remelted fourteen times to insure homogeneity. After final melting and rapid cooling, it was machined round to 0.415 in. diam, jacketed in stainless steel, and cold-swaged to 0.117 in. diam. The jacket was removed and swaging continued to 0.051 in. diam followed by wire drawing in carbide dies to 0.010 in. diam. Although it was intended that about 1500 ppm O (by weight) be added, inert gas fusion analysis indicated a 2390 ppm 0 content, apparently due to additional oxygen pickup in the arc furnace. Even so, the alloy was sufficiently ductile to be cold-worked to greater than 99.9 pct reduction

Jan 1, 1967

By J. Szekely, V. Stanek

Heat and gas flow interactions in nonisothermal packed beds were examined in the paper. A study was made of the response of the system to a step or pulse change in the inlet gas temperature, with a fixed value of the overall pressure drop across the bed. Under these conditions the heat flow and fluid flow transients are coupled because the convective heat transfer rate is alfected by the mass flow rate of the gas which, in turn, for a fixed pressure drop will depend on the temperature profile in the system. The Problem was stated in terms of differential equations, which were integrated numerically. The parameters used in the computation were so chosen to reflect the operation of the stack region of blast furnaces and sinterbeds. The computed results showed that the pressure drop-flou1 relationships and the rate of progress of the temperature fronts (waves) were strongly interrelated and were also markedly affected by variations in particle size and in void fraction. MANY metallurgical processes involve the contact of solid particles with a gas stream in a packed bed arrangement under nonisothermal conditions. Examples are shaft furnaces, regenerators, pebble heaters, and the sinter process. Although the heat and mass transfer aspects of packed bed processing have been extensively studied, the associated flow phenomena and in particular the effects of nonisothermality on the flow, have received little attention to date. :In fact, most of the previous workers considered the flow rate of the carrier gas time invariant and independent of the heat or mass transfer processSzekely and carr2 have shown that the pressure drop-flow relationships in nonisothermal packed beds may be strongly affected by the temperature profile within the system. These authors have devised a method for relating the pressure drop to flow for a given temperature profile. thus providing an extension of the Ergun equation to steady nonisothermal systems. Finally, in a recent paper willmot3 examined the response of regenerators to externally imposed changes in the gas flow rate. Both these investigations were somewhat specialized since, in general, neither the temperature distribution nor the gas flow rate may be regarded as truly independent variables, thus the heat transfer and the fluid flow problems have to be solved simultaneously. The work reported here is divided into two parts: in Part 1 the general formulation is given and a detailed discussion is presented of fixed bed systems. Part is devoted to systems in which a gas and particulate solids are contacted in a counter flow arrangement. FORMULATION Consider a nonisothermal fixed packed bed, extending from through which a gas is flowing. The problem is to develop a relationship between pressure drop and gas flow (with the gas flow being the dependent variable) and to evaluate the rate at which a change in the gas temperature, imposed at the inlet, travels through the system. Let us consider an infinitesimal section of the bed and establish differential heat, mass, and mechanical energy balances over this region. In addition, relationships are needed describing the temperature dependence of gas density (equation of state) and the temperature dependence of viscosity. These may be written as: where c, and are constants. It is noted that in this formulation we neglected any temperature gradients within the solid particles, thus assuming these to be either sufficiently small or of sufficiently high thermal conductivity to meet this condition. The justification and consequences of this assumption will be mentioned in the discussion.

Jan 1, 1970

By George J. Young

Jan 1, 1911

Jan 1, 1942

By H. J. Rose, J. J. S. Sebastian

When coal is stored under ordinary conditions, progressive changes take place in its chemical and physical properties. These changes are largely caused by the reaction of atmospheric oxygen with the coal substance. Although this "oxidation" or "weathering" occurs slowly in the case of high-rank coals, it is nevertheless a matter of considerable importance, since even a small amount of oxidation may affect the value of coal for carbonization purposes. Coal storage is a necessity at all carbonizing plants. In normal times there are about 5,000,000 tons in storage at by-product coke ovens and gas retorts in the United States, as compared with an annual throughput of about 75,000,000 tons. In other words, the average coal reserve at such plants is slightly less than one month's supply. However, owing to the cost of storage and recovery, coal is usually left in stockpile for as long a time as the management thinks advisable. Storage for six to eight months is common practice and is, in fact, a necessity at certain plants which obtain their coal by water routes that are closed during winter months. Modern by-product coke ovens operate continuously, and they are not cooled down from the time that they arc put into operation until they are shut down for rebuilding—perhaps 20 years later. This continuous operation is imposed by silica-brick construction and high operating temperatures. It is therefore obvious that coke plants must at all times maintain an adequate supply of stored coal, in order to prevent a failure in supply from any cause whatever. Thus when strikes or other emergencies threaten, abnormally large coal stocks are accumulated and held at coke and gas plants. Many of these plants have been forced, at some time or other, to use coal that has been stored for several years. Such coal may fail to coke at all, or it may produce a dirty appearing, weak coke of reduced value. The yields of salable by-products may also be distinctly lowered. However, it must not be assumed that slight oxidation or heat effects are always injurious. Certain high-volatile coals produce a stronger, blockier

Jan 1, 1930

By R. Maddin, N. Ujiiye

ALTHOUGH the cold-rolled texture for body-centered-cubic metals and alloys is well known (see, e.g., Barrett'), the pole figure representing the texture may be interpreted in two ways. It may be regarded as consisting of several ideal preferred orientations with an associated spread (a view which is shared among several investigators2), or it may be regarded as consisting of two sets of continuous preferred orientation also with an associated spread."." Recently, Chen and Maddin7 noted a stable (001) [loo] end orientation for molybdenum single crystals rolled at low rates of reduction provided the initial rolling. orientation" was close to the cube ori-

Jan 1, 1957

By T. PH. D. Egleston

THE origin of gold both in placer deposits and in veins, and especially the origin of nuggets, has been the subject of repeated discussions and investigations, which have been recently brought to my attention by several extremely interesting specimens sent to me for examination, and more especially by the one exhibited at the meeting of the Institute in February, 1880.* In the year 1874 I made some examinations of the hydraulic mines of Califor¬nia, and was very much struck with the distribution of the gold throughout these deep placers, which were almost invariably poor on' the surface, while gradually growing richer towards" the bed¬rock. The constant presence of fossil wood, and the large quantity of organic matter contained even low down in these beds, was also remarkable. Not being satisfied with the various theories advanced to account for the formation of these deposits, I began an investiga¬tion early in the year 1879 on the conditions of solubility of gold and the causes of the loss in working gold ore in a large way: The researches which I have undertaken show that gold must be considered a soluble rather than an insoluble metal, and that the conditions of solution are such as will be found anywhere where gold is likely to occur, and the solution may take place even under the ordinary cir¬cumstances of surface drainage, and may be going on freely even where the presence of gold has never been suspected, and that there are causes enough in nature to produce the solution of the gold in sufficient quantities to account for all the phenomena of both the vein and placer formations. The general theory with regard to the formation of these placer deposits and nuggets has been that they were the result of the de¬struction of pre-existing- vein-matter, which does not accord with the facts as shown in the deep placer deposits. The gold in such case would be distributed in layers of unequal richness throughout * Transactions of the American Institute of Mining Engineers, vol. 8, p. 451.

Jan 1, 1881

By Glenn R. Zellars, J. P. Morris

The carrier gas method was used to measure the vapor pressure of copper over liquid copper and Fe-Cu alloys. From these results, the activity of copper in the alloys was determined at 146°, 1550°, and 1600°C. Calculations of the activity of iron were made from the results for copper. The activities of copper and iron show strong positive deviations from Raoult's law. KNOWLEDGE of vapor pressures of liquid metals has both practical and theoretical value. Fuming of metal baths is directly related to vapor pressure, and the data should bc particularly important to the technology of vacuum metallurgy. Theoretical applications include determinations of heats of vaporization, heats of solution, and activity coefficients in alloys. Methods for measuring vapor pressures of metals have been reviewed by Speiser and Spretnak.' High-vacuum procedures, such as the Langmuir and Knudsen methods, have been used most widely in recent years. However, these methods are not applicable to vapor pressures greater than lo-' mm Hg and often cannot be used in the temperature range of greatest interest. The purpose of this investigation was to develop a procedure for measuring vapor pressures of pure metals and alloys that would be applicable to pressures greater than lo-' mm Hg. The transportation or carrier gas method has been used. Copper was chosen for the initial work because its vapor pressure has been established fairly well and the reliability of the technique could be ascertained. Applicability to alloys was studied by determining the vapor pressure of copper over liquid Fe-Cu alloys. Experimental Procedure The tests were carried out in a graphite-spiral resistance furnace. The charge consisted of 50 g of metal contajned in a covered sintered-alumina crucible 1/2 in. deep and 13/8 in. ID. Two sintered-alumina tubes led from outside the furnace to within the crucible, passing through close-fitting holes in the crucible cover and radiation shield. The arrangement of the crucible and the two alumina tubes is shown in Fig. 1. The small-bore tube (1/16 in. ID by 5/16 in. OD) served as the inlet for the carrier gas. The tip of this tube touched the metal surface and the flow of gas imparted a rippling motion to the metal. In this manner the gas was brought into close contact with the metal and became saturated with metal vapor. In most of the tests the flow rate of the carrier gas was 560 ml per min, measured at room temperature. Approximately half of this saturated gas was allowed to escape from the crucible through the second alumina tube (3/16 in. ID by 5/16 in. OD) and was discharged to the atmosphere through a

Jan 1, 1957

By E. J. Efsic, C. M. Wayman

The fcc to bcc y to a transformation in an Fe-24.5 at. pct Pt alloy was studied and found to be martensitic. Large martensite plates are formed in this alloy which are ideal for crystallographic studies; the Ms temperature is about -5°C. Ordering of the parent phase prior to transformation to martensite causes a pronounced lowering of the Ms temperature. For the first time in the case of alloys of iron, measurements of the habit plune, orientation relationship, and magnitude and direction of the shape stvain have been obtained on preselected martensite plates. It is shown that by measuring the initial and displaced (as a result of the shape strain) positions of three or more non-parallel fiducial scratches on one reference surfice the maguitude and direction of the shape strain and the state of distovtion at the parent-mavtensite interface can be determined with a reasonable degree of accuvacy. The agreement between the phenomenolog-cal crystallographic theory of martensitic transformations and the experimental results habit plune, orientation relationship, and nlagnitude and direction of the shape strain) is essentially perfect, and is thought to be the best reported to date for iron alloys. THE comparatively few investigations on binary Fe-Pt alloys have been concerned with magnetic properties, ordered phases, and the equilibrium diagram itself. Various investigations have shown that the equilibrium diagram is of the open y field type; in addition there is a peritectic transformation, a minimum melting point, and three ordered phases: Fe3Pt, FePt, and FePt3. The results of a number of investigators1-6 have shown that the temperature dependence of the y to a (and reverse) transformation in iron-rich alloys is reasonably well-established. The Fe3Pt phase was first noted by Kussman and Rittberg,7 and its existence was later confirmed by Franklin et al,8 Steijn and Donahoe,9 and Berkowitz et al.10 The FePt phase was reported by Isaac and amman' and later confirmed by a host of others.3,6,7,12,13 Kussman and Rittberg7 noted the existence of the superlattice FePt3. Prior to 1956, the 1 to a transformation in iron-rich Fe-Pt alloys was termed "irreversible". In 1957 Klokholm and Donahoe" termed this transformation martensitic, presumably because of its occurrence at temperatures well below those where diffusion normally takes place. This observation served as a point of departure for the present investigation, and in the very early stages of the work to be discussed it was readily verified that the y to a transformation in iron-rich Fe-Pt alloys is indeed martensitic. Quite large martensite plates exhibiting the well-known surface tilt were observed. These plates are ideal in the sense that the boundaries between the parent and product phases were usually very straight. It thus appeared that Fe-Pt martensites would be ideal for crystallographic studies, and this was the purpose of the present investigation. Details of the crystallography of martensitic transformations (particularly for iron alloys) and the phe-nomenological crystallographic theories15-l7 have been discussed many times and thus will require very little elaboration here. The end result of these theories, given in matrix form, is

Jan 1, 1968

By Hsun Hu, R. S. Cline

The annealing behavior and the mechanism of re-orientation during recrystallization of iodide titanium cold-rolled 94 pct have been studied in detail. Results indicate that recrystallization occurs by the nucleation and growth of new grains, as in other common metals. Recrystallization nuclei form by the coalescence of subgraim, and the change in texture as a result of recrystallization is largely due to selective growth among the nuclei formed. The annealing of titanium is characterized by a wide range of overlap of the various stages of the annealing process, which may be responsible for a range of activation energies observed, and for the apparently gradual change in the annealing texture as a function of time or temperature. The deformation and recrystallization characteristics of titanium and zirconium are very similar. In cold-rolled strip, the deformation texture consists of two symmetrically oriented components, each having the basal plane laterally tilted at about 30 deg from the rolling plane and the [1010] direction parallel to the rolling direction. Upon annealing for recrystallization, the change in texture can be described, for simplicity,* as rotations around [0001].2'6'8 According to McGeary and Lustman,' recrystallization occurs in zirconium through normal growth of the subgrains, which they called "domains", without the nucleation of new grains; and the magnitude of rotation around the [0001] axis increases gradually during the progress of recrystallization. If these conclusions were true, the mechanism of recrystallization in zirconium would be basically different from that in most metals, since it is commonly known that recrystallization with reori-entation always involves the migration of high-angle boundaries. In an attempt to clarify the situation, the mechanism of reorientation during recrystallization in iodide titanium cold-rolled 94 pct was studied in detail. The structural and textural changes upon annealing at various temperatures were examined by optical and transmission-electron microscopy, X-ray pole figures, pole density distribution measurements, and micro-beam techniques. EXPERIMENTAL PROCEDURE Material and Specimen Preparation. An iodide titanium crystal bar was are-melted and solidified in a cold-hearth crucible under a purified argon atmosphere. The solidified ingot had dimensions of approximately 3 by 1/2 by 3 in. One face of the ingot was somewhat uneven, but was as clean and shiny as the remaining parts of the ingot. Large grains with a Widmanstatten internal structure were clearly shown on the shiny surfaces, indicating the occurrence of P — a transformation upon rapid cooling from the melt. Analysis of the are-melted ingot indicated C 0.033, N 0.010, H 0.013, 0 0.002 in weight percent, and traces of iron, copper, and silicon as detectable impurities. The ingot was cold-rolled -40 pct to 0.300 in. thick with a reduction of 0.005 in. per pass. The defects on the uneven side of the ingot were then removed by machining. This reduced the thickness to 0.285 in. The piece was then recrystallized by annealing at 800°C for 1 hr in a fused silica boat charged into a fused silica tube furnace under a vacuum of 10~5 mm Hg. To refine the grain size, the recrystallized metal was again cold-rolled 40 pct to 0.170 in., then annealed at 700°C for 1 hr. These treatments yielded a strip with a uniform equiaxed grain structure, having a penultimate average grain diameter of 0.04 mm and a hardness of approximately 90 Dph. Final rolling reduced the thickness from 0.170 to 0.010 in., corresponding to a reduction of 94 pct. The strip was rolled in both directions by reversing end for end between passes. Surface lubrication was provided by oil-soaked pads attached to both rolls. Specimens of 1 in. length (for X-ray examinations) and +in. length (for hardness and microstructure examinations) were cut from the rolled strip, and a width of & in. was cut from the edges of each specimen by a jeweler's saw. These specimens were then etched in a solution of 10 cu cm HN03, 5 cu cm HF, and 50 cu cm H,O to 0.008 in. thick to remove the surface metal, as well as the distorted metal at the saw cuts, prior to annealing or measurements. To minimize any surface reaction with the atmosphere, all specimens were kept in an evacuated desiccator. Isothermal Anneals. All annealing treatments were conducted in vacuum in a fused silica tube furnace as described earlier. The temperature of the furnace was controlled to within *2"C. The specimen was placed in a fused silica boat, then pushed into the hot zone of the furnace. It took about 5 to 6 min for the specimen to reach the furnace temperature. After the specimen was held at temperature for a desired length of time the boat was pulled to the cold zone of the furnace; the heating-up period was excluded from the isothermal annealing time. Thus, the uncertainty in annealing time is higher for very short anneals, but negligible for long anneals.

Jan 1, 1969

By A. M. Gaudin

The study that is presented here was undertaken in order to condense information concerning comminution, and covering a great variety of conditions, into one or several rules which would be of use in the development of a systematic theory as well as in many directly practical ways. As the result of this work, the following conclusions appear justified: 1. Rocks may be classified, from the point of view of comminution, into two general classes which are (a) structurally homogeneous, and (b) structurally heterogenous. Structurally homogeneous rocks are those in which fracture takes place through grains and grain boundaries alike; heterogeneous rocks are those in which fracture passes in preference through grain boundaries. 2. If a sized product composed of structurally homogeneous rock grains is crushed, a product results in which the relation between the percentage weight of grains of various sizes and these sizes themselves follows a definite law. This is not true of structurally heterogeneous rocks. 3. Ball milling with structurally homogeneous rocks, and under certain conditions, presents exceptions to this rule. 4. In ball milling with structurally homogeneous rocks, there exists a critical ratio of size of feed to size of balls, above which the machine operates essentially by surface wear, and below which it operates essentially by breaking across the body of the particle. 5. In ball milling, with structurally homogeneous rocks, and when the size of feed grains exceeds the critical size, the particles worn off are of a substantially definite size which depends upon the ball size. 6. In the case of a typical heterogeneous rock, such as Manhattan schist, particles are crushed in such a way that there is a greater proportion of grains of the size that is the average grain-size of the rock than there would be in that range of size with a structurally homogeneous rock. This has been found to be true with all the crushers tested. 7. Different methods of crushing produce grains of different shapes. 8. The importance of sizing the — 200-mesh portion of a crushed product, in crushing-efficiency investigations, has been greatly under-

Jan 1, 1926

By H. C. Chao, W. F. Hosford, L. H. Van Vlack

The negative "plastic Poisson's ratio" suggested in earlier studies of Mus deformation is analyzed, and the results are verified experimentally with NaCl crystals. In the early stages of deformation where the primary {110}(110) slip predominates, compression along. the [001] direction produces contraction along the lateral [011] direction plus a compensating expansion along. the [100] direction. With additional strain, the primary slip is supplemented by secondary {111}(110) slip so that the above contraction diminishes and a more typical deformation appears. THE shape change of bee and fee crystals deformed by compression or tension along [011] has been analyzed in some detail and shown to be responsible for the development of peculiar microstructures in [011] fiber textured polycrystals of these metals.1'3 This paper concerns the unusual shape change accompanying [011] compression of NaCl crystals. It is the direct outgrowth of an earlier investigation of the deformation of manganese sulfide inclusions in steel.3,4 In that investigation, cylindrical specimens of steel containing small oriented crystals of MnS were prepared by powder metallurgy and plastically compressed. The flow of the inclusions was determined relative to that of the steel by sectioning the composite and measuring the length-to-width ratio L/W of the inclusion and diameter-to-height D/H ratio of the steel cylinder on the plane of section. These L/W ratios, normalized by dividing by the initial LO/WO ratio of the inclusion, were compared with the normalized D/H ratio of the steel cylinder. Of particular interest here are the deformation characteristics of an inclusion oriented with [Oil] parallel to the compression axis. When measurements were made on sections parallel to the (100) plane of the inclusion, the L/IV ratios were only slightly in excess of unity, indicating a high apparent hardness of the [011] criented inclusion. However, measurements on a (011) plane of section resulted in L/W ratios which were much larger, Fig. 1. These observations prompted an analysis of the strains resulting from slip in an MnS crystal compressed along [011.]. CRYSTALLOGRAPHIC ANALYSIS Manganese sulfide has the NaCl crystal structure, and the predominant slip system is {110}(110). A secondary system, {111}(110), has also been reported.= {110}(110) Slip. When a crystal is subject to a uni-axial compressive stress 011 along [011], four slip systems, (101)[101.], (101)[101.], (110)[i10], and (110) [ 110], will be equally stressed with a shear stress t = 0.2 011 while the other two {110}( 110) systems will be unstressed. The normal strain En along any reference axis n resulting from slip is given by Schmid's law: en = S COS ?in COS in ?i 111 where ?in and +in are the angles between n and the i slip direction and n and the i slip plane normal, respectively, and where ?i is the shear strain on the i slip system, For the four active slip systems above, the cos ?in cos +in terms are all equal when the reference axes are the [011] compressive axis, [011] and [ 100]. Eq. [I.] therefore reduces to en - cos ?n cos +ny [2] where y =S?i for all slip systems. Substituting the appropriate angles, Eon = 0.25? 110 eon - 0.25y110 [3] €100 = -0.50y 110 The interesting feature of Eqs. [3] is that they predict that the strains in the [011] and [011] directions, resulting from {110}(110) slip, are equal and of the same sign. Thus when a crystal is compressed along [011], it will contract along the lateral [oil] direction

Jan 1, 1967

By N. R. Adsit

THE B-Ni system was chosen for this study because of the great interest being shown in boron-fiber-strengthened composite materials. Boron fibers were obtained from Texaco Experiment, Inc. They average 4.2 mils in diam with a 0.5-mil tungsten wire in the center. In order to make the diffusion couple, the fibers were included in the nickel matrix by electroforming. The samples were placed in a preheated furnace for the desired temperature and length of time. Sectioning and polishing the samples revealed concentric rings as shown in Fig. 1. The average penetration distance, X, was calculated by measuring the radius of the second phase (the white shell in Fig. 1) and subtracting the original radius. The second phase was identified as NiB by X-ray diffraction. This allows the kinetics of the formation of the phase NiB to be calculated by Eq. [I], which is taken from offman:"

Jan 1, 1967

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. 'These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness' when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.' In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By A. U. Seybolt, R. A. Oriani

The pressure and composition of the solid solution of nitrogen in chromium has been investigated as a function of temperature. The partial molal heat of solution, the activity of nitrogen in solid solution, and the partial molal free energy have been computed. The enthalpy of three reactions is summarized: N + 2Cr(3) = Cr2N(4), H° = —28,500 cal per mol 1/2N2(p) + 2Cr(8) = Cr2N(3)1 ?HO = —23,500 cal per mol 1/2N2(p) = N, ?H° = 5,000 cal per mol. WORKERS who have investigated the problem of the preparation of ductile chromium have been concerned with the effects of minor amounts of impurities upon this refractory metal. In particular, gaseous impurities such as oxygen and nitrogen have been suspected of causing trouble because of many known cases where brittleness in transition elements has been definitely traced to these elements. In order to evaluate the possible effects of the nitrogen impurity in chromium, it appeared desirable to learn something of the dependence of the nitrogen solubility upon temperature and pressure. Previous Work Maier3 in 1942 in his treatise on sponge chromium reviewed the thermodynamics of the chromium nitrides Cr2N and CrN, both of which are well-estab- lished compounds, but which apparently have not been studied in much detail. Maier presented some free energy-temperature expressions for the reactions 2 Cr,N = 4 Cr + N2 [1] and 4 CrN = 2Cr2N + N2 PI based mainly on the work of Satoh2 and Sano." Pearson and Ende3 in 1953 briefly reviewed the thermodynamics of Cr-N using the same data available to Maier, and also derived a free energy-temperature expression for reaction 1. Of the two nitrides mentioned previously, the present investigation was only concerned with Cr,N, since this nitride is in equilibrium with the metal phase, at least over most of the temperature range, Blix4 in 1929 established the structure of Cr2N (close-packed-hexagonal) by X-ray diffraction methods, and indicated that its homogeneity limits extend from 11.2 pet to 15.1 wt pet N. At a temperature of 1200°C, 38 mm Hg from the Maier expression and 43 mm Hg from the Pearson

Jan 1, 1957

By AIME AIME

MOST recently elected to the limited group of Honorary Members in the A.I.M.E. is the distinguished Australian metallurgist, Guillaume Daniel Delprat. His citation reads: "in recognition of his distinguished achievement as metallurgist, engineer, and administrator in the production of ferrous and nonferrous metals," Mr. Delprat's ability and experience in both the ferrous and nonferrous fields at once distinguishes him from most of his professional brothers. Mr. Delprat's nativity was neither Australian nor English, for he was born in Delft, Holland, in 1856, and educated in Amsterdam. At the age of 22 he went to Spain, as metallurgist for the Tharsis Sulphur and Copper Co., Ltd. Afterwards he spent some time with the Bede Metal and Chemical Co., which had mines in both Spain and Norway, and of which company he became general manager. Other positions of responsibility held by Mr. Delprat before he went to Australia included the managing directorship of the Cordova Exploration Co., with properties in Spain and Canada; of the Rincon Silver-Lead Mining Co., in Spain; and of the Deloro Gold Mines, in Canada.

Jan 1, 1936

By Robert Glass Cleland

THE MEMBERS of the Phelps-Dodge, Phelps-James co- partnership differed widely from one another in certain aspects of temperament and personality; but in one thing Anson Phelps, William Dodge, and Daniel James were fundamentally alike. They were all bred in the English Puritan tradition. Their creed, moreover, was the stern, militant, uncompromising creed of John Calvin and John Knox. The present generation, harshly intolerant of such a creed, has little understanding of the authority it exercised on the thinking and conduct of its adherents or of the contributions that those same adherents made to human welfare and social progress. The men who accepted its authority "were characterized by a blend of strong individualism and an equally strong sense of social duty, and they submitted their own souls to the same searching scrutiny that they applied to their business ledgers." To all three of the immediate founders of Phelps Dodge, their religion was the most real and important thing in life. It was with them day and night, in joy and sorrow, in loss and prosperity, in their most trivial personal affairs, in business transactions of the greatest moment. It was with

Jan 1, 1952

By Robert T. Howard, Morris Cohen

IT has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkin1 has shown that the compositions of two coexisting phases in a a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanalysis.3 Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantitative way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of, this research could not be treated satisfactorily by other quantitative tools, such as specific volume,4 magnetic,5 dilatometric,6 electrical resistance7 or x-ray measurements.8 It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. LITERATURE SURVEY Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-