Search Documents

By L. F. Mondolfo, B. E. Sundquist

The undercooling associated with the nucleation of the secondary phase from the liquid by the solid primary phase was studied in sixty binary alloys by means of a hot-stage microscope. It was found that in a system of a and ß, a usually nucleates ß at low undercoolings, but ß does not nucleate a, except possibly at undercoolings approaching homogeneous nucleation. This behavior can be explained in terms of relative interfacial energies and shows that crystallographic disregistry is only a minor factor in heterogeneous nucleation from metallic liquids. PREVIOUS experimental work1-6 on nucleation of solids from liquids has shown that normally nucleation is heterogeneous, and that small solid particles present in the liquid are responsible for the nucleation. These experiments and the theory that has evolved from them have made apparent that there is a "characteristic undercooling" associated with the nucleation of the solid from a given liquid by a given impurity. Little is known, however, about the chemical and structural relationships between the nucleating agent and nucleated solid that control the effectiveness of the nucleating agent in catalyzing the nucleation, as measured by the required undercooling. A review of the literature has yielded seventeen undercoolingsL-6 for the nucleation of solid from liquid metals by "known" nucleating agents. All values come from experiments in which the metal studied was divided into a number of particles (10 to 300 pin diam.) much larger than the number of extraneous impurity particles so as to obtain a large number of particles free of foreign nucleating catalysts. Known nucleating agents are then introduced by coating the droplets with particles or a thin film of the catalyst. Six of the seventeen undercooling values referred to cases where, for various reasons, the identity of the nucleating species was not at all certain. Another six cases involved nucleating agents with a crystal structure that was not known. Four other cases involved undercoolings listed as greater than or equal to undercoolings which were very likely those for homogeneous nucleation. One investigation3 involved adding to droplets powdered oxides, carbides, and so forth that were doubtlessly covered with adsorbed oxide or nitride films. The highly variable nature of these films resulted in highly variable undercooling (as was also found in preliminary work in this investigation). It is apparent that the information on heterogeneous nucleation in liquid metals is too limited to give rise to any definite conclusions on the nature of the catalytic process. With these problems in mind a new method was

Jan 1, 1962

Note Any member who desires to be designated as being "Available for Consulting Work" can arrange it simply by sending a written request to the office of the Secretary of the Institute The following list of members is primarily arranged geographically, with secondary consideration to political subdivisions arranged alphabetically First, the states of the United States , then other North America, in order Alaska, Canada, Mexico, the West Indies, and Central America Then cones South America, Europe, Africa, and Asia, each including the near by islands associated with those continents Australia, the islands to the north, and the Pacific islands except Japan are grouped together under Oceania The various countries are indexed on the preceding page NORTH AMERICA UNITED STATES ALABAMA America -Dyar, G C Anniston -DePriest, S H Klugh, B G Lefforge, J W Auburn Poor, R S Bankhead -Armstrong, W D Bessemer -Beck, A IV, Jr Carnes, D Chabot, L S , Jr Creveling, J C

Jan 1, 1952

By J. C. Jaeger, G. A. Wiebols, N. G. W. Cook

It is usual practice in engineering to design a stable structure by ensuring that the stresses in the elements of the structure are always less than their strength, which may be defined as the yield stress, the ultimate stress, or the fatigue stress, according to the type of the load. Such restrictive design is not practical in the design of underground excavations since the rock surrounding such structures is usually failed, but only occasionally does this give rise to instability of the structure. Thus, while the usual criterion for the design of a stable structure is certainly sufficient, it is not necessary for underground excavations. A proper understanding of the conditions necessary for stability is vital to the useful application of rock mechanics knowledge to the design of underground structures. Most tests on the properties and strength of brittle rocks are disrupted at or near maximum load by the rapid release into the specimen of energy stored in the resilience of the testing machine. This is in contrast with a phenomenon, which may be observed frequently, where the rock immediately surrounding an excavation is both failed and subject to stress. By postulating a complete stress-strain curve for rock, it can be shown that failure is unstable or stable, depending upon whether the stress-strain curve of the rock lies inside or outside the stress-strain characteristics of the applied stress. Stability is, therefore, a function of the stiffness of the system applying the stress relative to that of the failing rock. Many workers have established that the strength of rock specimens under a lateral hydrostatic confining stress varies linearly with confining stress, in a way which may be expressed by the equation CT=Co+K[o]3

Jan 1, 1972

By C. W. Gennet

Announcement was made in the spring of 1926 that the Boston & Maine R. R. Co. had contracted with the well-known German steelmakers, Messrs. Fried Krupp, for the manufacture of 15,000 tons of basic open-hearth steel rails at the Rheinhausen Works, for delivery to Boston, Mass. The manufacture of rails in the United States has for many years been almost a national pride, and as this feeling is chiefly the result of a long-time liberal and consistent patronage of American rails by American railroads, it is not strange that this somewhat unusual announcement should arouse more than ordinary interest. Since the end of the World War, the importation of foreign rail has been fairly large, principally because the newly created economic conditions have rendered some American competition more difficult, but the tonnage imported, for the most part, has been made up of small orders for miscellaneous use; and the contract referred to constitutes the largest single importation of foreign rail in over ten years. In 1915, the Algoma Steel Co. of Sault Ste. Marie, Canada, supplied the Illinois Central R. R. with 30,000 tons of rails,' and various other American roads with smaller amounts. In 1902, 1903 and 1904, large tonnages of rail from abroad were purchased, the Louisville & Nashville R. R. alone obtaining 30,000 tons from German mills. It is the object of this paper to present, in what is believed to be a new and concise form, figures showing the production and consumption of rails in the United States, and to record some of the testing and inspection results of the recent Krupp rails; also, to direct attention to two quite unique departures from American practice that were regular features of the Krupp process and which are worthy, it is thought, of careful study. Production and Consumption of Rails in the United States Table 1 shows the tonnage of rail produced in the United States and the amount imported, exported, and consumed by years since 1849. That, evidently, was the first year of record, for the statistics of the American Iron and Steel Institute and its predecessor, the American Iron and

By C. O. Burgess, W. D. Forgeng

DESPITE the increasing interest in and the technical importance of iron-chromium-manganese alloys, very little published information is available regarding their constitution. F. M. Becket's paper1 in 1930 represents the first correlated effort in the field of these alloys. The paper served particularly to draw attention to the commercial possibilities of iron-rich alloys containing chromium and manganese in balanced proportions. The duplex structure of alloys within the commercial range was briefly discussed, but exposition of their structural constitution was necessarily limited because the physical properties and corrosion resistance of the alloys were the main subjects of the paper. Both prior to and following the publication of F. M. Becket's paper, and at his instigation, an extensive investigation of the constitution of iron-chromium-manganese alloys of commercial purity was in progress at the Union Carbide and Carbon Research Laboratories, Inc. The present paper is based on the results of that investigation. In the last few years, investigations covering various portions of this alloy system have also been made in Europe. W. Koester briefly mentioned the effect of annealing on chromium-manganese steel2 and later3 constructed approximate sections of the iron-chromium-manganese equilibrium diagram. M. Schmidt and H. Legat14 even more recently studied this system, and their article and conclusions are of interest as representing an entirely independent study of a number of iron-chromium-manganese alloys. Koester's sections are shown in Fig. 1. The figures summarize the effect of manganese additions to iron alloys containing 5, 10, 15 and 20 per cent Cr as well as the effect of increasing chromium content on iron alloys containing 3, 8, 20 and 30 per cent Mn. These diagrams, within their composition limits, substantiated in some measure the results of our investigation. However, in our work some differences as regards the position of the mixed alpha-gamma fields were found as compared to Koester's work, and we were able to detect the presence of

Jan 1, 1938

By E. P. Pfleider, W. G. Pariseau

This paper reports the theoretical and experimental results of an analysis of ore pass drawdown as a problem in soil plasticity. The method of analysis developed appears to be a promising technique of investigating the mechanics of fragmented materials. A reconstructed plasticity theory brings experiment and theory into reasonable agreement, and hence may provide the foundation needed for rational ore pass design. The gravity-induced movement of broken rock through ore passes is an economical method of transporting fragmented materials through large vertical distances in underground mines, provided the ore pass is well designed. Unfortunately, the design procedures now followed do not very often result in ore passes that function properly. On the one hand, the huge accumulation of empirical data pertaining to the movement of materials in gravel bunkers, storage bins, deep grain silos and other structures that have features in common with ore passes remains uncorrelated. On the other hand, there is a dearth of experimental data substantiating theoretical models of material behavior. Consequently, reliable generalizations encompassing the broad spectrum of problems involved have not been forthcoming. AS an initial step towards improving the situation, a detailed case study of two-dimensional ore pass drawdown was made. The mechanics of the process were analyzed theoretically as a problem in soil plasticity and tested experimentally through observations of a laboratory ore pass model. THEORY Taylor1 defines a soil as a "mass commonly considered to consist of a network or skeleton of solid particles, enclosing voids of varying size." Broken rock in an ore pass is such a material. In plasticity theory this material is replaced by an idealized substance that deforms elastically up to some state of stress at which slip or yield occurs,2 For com-pressive states of stress, the Mohr-Coulomb criterion is a satisfactory yield condition. After the yield point is reached, the ideal soil deforms in accordance with the concept of plastic potential.4 Under plane strain conditions the governing equations separate into a system of stress equations and a system of velocity equations.' Only stress variables appear in the stress system. The velocity system, however, contains a stress variable. The two systems are, therefore, coupled. Both systems are hyperbolic, and each has two real, distinct families of characteristic curves that coincide according to the classical theory of ideal soil plasticity. The

Jan 1, 1969

By G. F. Loughlin, C. H. Behre

THE DEVELOPMENT OF CLASSIFICATION WHAT is the use of a classification of mineral deposits? From the days of Agricola, the founder of the science of ore deposits, successive authors on the subject have attempted classifications, none of which have attained unanimous indorsement of miners, engineers, or geologists. The miner and engineer naturally have little regard for a classification that does not help them to find ore. Mining geologists may share this feeling, and deplore the overemphasis that may be placed on classification by their academic brothers. Apparent effects of such overemphasis may be reflected by students or new graduates who have grown to think that each deposit must fit perfectly into some pigeonhole of the more or less arbitrary scheme that has been drilled into them. Diversity in mineral deposits as in other natural phenomena, however, is too great to be fully expressed in the usual tabular classification, and experience is essential for the appreciation of the value or usefulness of a classification. The succession of classifications has closely followed the growth of the science of mineral deposits and reflects that growth, as well perhaps as the limited or comprehensive viewpoint of each proponent. The earliest classifications were based on metal content, and were superseded by those based mainly on form of deposit. Source of materials also became a basis, and was followed by physical and chemical conditions and processes. In spite of this development it is interesting to note that in many of the latest reports on mining regions the authors adopt special classifications suited for their particular districts. Some of these, like the earliest classifications, are based primarily on metal content, and others are most conveniently based on form, and it may be convenient to modify these by reference to source of material or temperature of deposition. Some, including the writers, after noting these different usages, have refused to worry much over classification as an ultimate objective, but,

Jan 1, 1933

By Oliver Smalley

Except for the work of Guillet, who conducted a systematic investigation on the zinc-replacing value of nickel in brass, and extended his investigation with a view to developing commercial high zinc content nickel brasses, the author does not know of any other systematic research on the subject. The most promising commercial alloys and their physical properties obtained by Guillet are given below: These test results scarcely justify the use of such quantities of so expensive a metal, and could have been obtained from ordinary commercial brass. For purposes of comparison, the physical properties of ordinary brasses, ranging from 70 per cent. to 50.1 per cent. Cu in both the cast and normalized1 conditions are included in 'Table 1. These incidentally furnish a useful standard of the properties of castings and of rolled, extruded and forged brass when correctly annealed. A close study of some of the well-known special brasses containing nickel reveals a series of alloys which bewilder by their complexity, and me can only hazard a guess at the function and commercial value of each of the many elements used.

Jan 1, 1926

By C. Stansfield Hitchen

THE introduction of the logarithmic sector method of quantitative spectrography by Scheibe and Neuhäusser in 1928, and the subsequent .modification and improvement of the method by Twyman and Simeon, would seem to have marked yet a further advance in quantitative spec-trum analysis and its industrial application, inasmuch as it offers a simple means of eliminating some of the uncertainties inherent in the older methods based upon mere visual comparison of line intensities. In their recent admirable review of the position and capabilities of industrial spectroscopy, Brownsdon and van Someren1 say: Ways and means of facilitating the comparison of line-intensities so as to give them numerical values are helpful, and of these a logarithmic sector rotating in front of the slit appears to he one of the most promising; . . . the success recently experienced by the author in using this method for the examination of steels and solutions of metallic salts prompted him ,to investigate its possible use in estimating the impurities commonly present in crude and refined tin. The results of this investigation are submitted in the present paper. Details of a number of spectrographic analyses of tin for various impurities have already been published. Thus, Schweitzer2 describes the spectrographic examination of tin for lead, bismuth and cadmium, and was able to distinguish between such atomic percentages as 0.01, 0.05, 0.10, 0.30, 0.60, 1.20, 3.00 and 10.00. Negresco3 investigated the bismuth content of tin over a range of from 0.0005 to 35 per cent. Meggers, Kiess and Stimson4 compare spectrographic and chemical analyses of tin metal for copper, lead, iron, zinc, silver, nickel and bismuth. They stress also the value of spectrum analysis in the examination of tin used for boiler plugs, where the requirements that only minute quantities of impurities shall be present render the chemical analysis both tedious and difficult.

Jan 1, 1933

By C. W. Goodale

I. INTRODUCTION. In the summer of 1909 the Boston & Montana reduction department of the Anaconda Copper Mining Co. completed a new flue system, at a cost of about $1,100,000, and -is this includes the largest and highest chimney in the world, and some new features of flue construction, a description will be of interest. At the Spokane meeting of the Institute in September, 1909, a brief mention was made of this flue system, in discussing Mr. Brunton's presidential paper on the Progress of Metallurgy in the West, and a promise was given that when a long enough time had elapsed, so that operating results could be given, a paper would be offered. The smelting plant includes blast furnaces, MacDougall roasters, gas-fired reverberatories, and converters.

Jan 8, 1913

By B. J. Shaw, R. Kossowsky, W. C. Johnston

High purity (99,95) Ni-51 wt pct cr eutectic alloy was unidirectionalty solidified at rates of 0.1 to 8 in. per hr. The resulting material was characterized by large grains, approximately 0.5 mm in cross section and extending through almost the entire length of the specimen, parallel to the growth axis. The eutectic structure of specimens the growth at -1/3 The per hr consisted of a continuous nickel-rich phase and chrome -rich lamellae approximately 2 thick, spaced about apart. Specimens were tested in compression at temperatures ranging from —196 to 850"C over which range the 0.2 pet yield strength dp -creased from 160,000 p si to 35,000psi, respectively. Swaging to 40 pet reduction in area, followed by a 30-min anneal at 1000c to remove residual cold work, increased the 0.2 pet yield to 260,000 psi at -196°C, dropping to 35,000 psi at 850°C. The increase in strength was attributed to a residual cell structure. The strength of the alloy could be rationalized by the simple rule of mixtures if one assumed that additional strength is derived front a size effect characterized by is petch equation IN recent years there has been increasing interest in dispersion and second phase strengthening in materials needed for high-temperature applications. inm role of structure on the mechanical The of such alloys has been well established of such some extent accounted for theoretically. and to of how the strengthening mechanisms due to fibers and lamellae operate has been reduced to its fibers form by the fabrication of composites of strong rods unidirectionally aligned in a From work on tungsten-fiber-reinforced copper, for example, it was established that the "Rule of Mixtures" could explain the strengthening.12 " some what more sophisticated technique for introducing strong fibers into copper matrix was used by Hertzberg strong Kraft3 who unidirectionally solidified the copper-chromium eutectic. The use of unidirectionally fied eutectics has advantages in that there are no matrix-fiber wetting problems and fine fibers are automatically aligned and uniformly fiber However, one Is restricted to a specific volume fraction of the second phase. Nevertheless, even though the volume fraction is fixed, the rod or lamella thickness, , can be varied by controlling the freezing interface velocity. Alternatively, the grown material may be worked down by swaging or rolling. Embury and Fisher, " using this approach, drew down pear lite in iron and studied the mechanical properties iron and that the yield strength, oy, was properties.proportional They that d was the wire diameter. It could be inferred that was also proportional to but the work hardening had to be taken into consideration at the same time. By varying the growth rate of the cadmium-zinc lamellar eutectic, Shaw'1 showed that was proportional to without the introduction of work hardening and suggested that the lamellar interface itself contributed to the strengthening of the composite. In this investigation we have evaluated the mechanical properties of the unidirectionally solidified fec-bec eutectic Ni-Cr. This eutectic was selected because it presented the possibility was selected beca temperature, and high corrosion resistant alloy, and also represented a hard-soft phase combination with two completely different slip systems. Specimens were tested in compression and tension up to 850°C and a detailed study of the micro structure as a function of plastic strain and temperature was carried out by light and electron microscopy. It was shown that the composite strength tested in compression can be accounted for by the simple rule of mixtures if one allows for an additional term representing the effect of Intereprese EXPERIMENTAL PROCEDURE 1) Unidirectional Solidification. Fig. 1 is a schematic drawing of the apparatus used to produce 0.2 in. diam by 12 in. long alloy ingots. The crucible tube is alumina, containing the charge which has been is swaged, or machined to 0.195 in. diam. The lower end of the tube is immersed to 0 .195in in.d iam. The upper end is supported by a 10 mil nichrome wire which lowers the crucible mil nic hr the] wire at a prescribed rate. Surrounding the furnace is a graphite susceptor into which a control thermocouple is inserted. The furnace is insulated with fiberfrax and enclosed in a quartz tube. There is a sliding seal at the bottom around the crucible and one on the top so that an atmosphere may be used for the sample and suscep tor. The power for the furnace is supplied from a 10-kw, 450 kc generator. The skin depth (the skin depth at which the field falls to l/e of its value at the outer surface) for graphite (p = 10 (j-ohm-cm) is 0.1 in. at this fre-

Jan 1, 1970

Part 1. Coal Part 2. Industrial Minerals

Jan 3, 1977

By Ira Joralemon

THE Ajo copper district is in the heart of the Arizona desert, near the western boundary of Pima county. Gila Bend, the nearest railroad point, is 43 miles north of the camp, and the little Mexican border town of Sonoita is 30 miles south. Between Gila Bend and Sonoita, Ajo is the only settlement save for one or two small cattle ranches and the uncertain villages of nomadic Papago families. The Little Ajo mountains rise a few hundred feet above wide desert valleys, beyond which are lava mesas. The camp itself lies at an elevation of about 1,900 ft. above sea level, in a little basin on the east side of the range, separated from the open desert by low hills. In the center of the basin the brilliantly iron and copper stained rocks of Copper mountain rise 150 ft. above -the village. Many varieties of cactus and low desert bushes cover the hills, while in the large valleys there are clusters of mesquite paloverde, and ironwood trees which furnish limited amounts of fairly good fuel. A scanty supply of water is obtained from wells in the desert and from prospect pits in the camp. The nearest abundant source of water is the Gila river, 50 miles north of Ajo. (See Fig. 1.) HISTORY OF THE AJO DISTRICT The Ajo, next to Santa Rita, New Mexico, is claimed to have been the first copper district in the Southwest worked by Americans. In the '60's or even earlier high-grade native copper and cuprite Ore was mined from shallow surface workings and hauled by bull team 400 miles across the desert to San Diego. From there it was carried in sailing ships to Swansea, Wales. Later, the ore was hauled to Yuma, floated down the Colorado river to the Gulf Of California, and shipped to Swansea. Bat-infested old workings and the massive axles of the bull carts are shown to prove the truth of the stories.

Jan 8, 1914

SLAG composition, slag constitution, reactions in slag, and reactions between slag and metal-in other words, the physical chemistry of slags-are matters of great importance to the open-hearth operator, whether or not he makes use of any detailed knowledge of them. Although this is a relatively young branch of the science of steel- making, much progress has been made; however, much remains to be learned, and many of the statements that can be made at present are probably--or even certainly-subject to future change. Nevertheless, the physical chemistry of slags is sufficiently developed to provide a reasonably secure basis for real understanding of steelmaking reactions. FUNDAMENTALS OF SLAG CONTROL By way of introduction, some time is spent in this chapter on effecting an easy transition from some of the more "practical" manifestations of slag to discussions couched in the more formal language of physical chemistry. This necessitates a certain amount of repetition, but it is felt that the purpose of the chapter is best served in this way. Reactions in the metal phase have products that find their way into the slag and are important components thereof; they are discussed in detail in the preceding chapter. Some substances distribute themselves Between slag and metal in definite fashion, and others are found only in the slag. Their reactions are a large reason for this chapter. Limitations of Slag Control. The open-hearth process is essentially oxidizing and cannot be otherwise operated. (Oxygen gradients in the furnace, the mechanism of oxygen inflow, and similar subjects are discussed in Chapter XIX.) As shown in the calculations of material and heat balances for the charge (see Chapter XV), from 25 to 50 lb. of oxygen will flow from air or combustion gases into the charge or molten bath during the heat for each ton of liquid steel

Jan 1, 1944

By W. Wanjokow, H. O. Hofman

In the metallurgical treatment of most metallic sulphides it is usually necessary to carry on a roasting-operation. In some cases the raw ore will have to be roasted; in others the intermediary product, matte, produced in smelting the ore; again, both ore and matte may have to be subjected to oxidation at elevated temperatures. Most metallic sulphides, when given an oxidizing-roast, pass through the state of sulphate before they are converted into oxides. All metallic sulphates are completely decomposed by heat, with the exception of those of lead and bismuth, but the temperatures at which decompositions take place vary with the metals. Some metallic sulphates are converted directly into oxides, others first form basic salts. Alkali-earth sulphates show a behavior similar to that of metallic sulphates, while alkali sulphates do not part with their sulphur trioxide even at elevated roasting-temperatures. The older data on the decomposition of metallic sulphates by heat are only approximations. Thus Kerl' gives the order in which metallic sulphates are decomposed with increasing temperatures as (Ag2, Fe, Cu, Zn, Ni, Co, Mn, Pb) SO,. More recent statenlents give definite temperatures and modify the formerly accepted order of decomposition. But the temperatures given by various observers do not agree. The reasons for this are to be found mainly in the method and manner of carrying out experiments. Four methods have been used: 1. Heating in an evacuated tube; 2, heating in a tube closed at one end, without air-cur-

Jan 1, 1913

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

By J. E. Burke, C. W. Mason

In attempting to study precipitation from a tetragonal lattice, using solid solutione of bismuth in tin, it was found that although a Widmanstätten pattern is observed1,4 only a qualitative analysis of the orientation relationships is possible, because of the unusual structural changes that accompany the precipitation process. Microscopical Studies Alloys were made from Chempur tin (Standard samples 42b and 426, National Bureau of Standards), and bismuth (Kahl-baum C.P.) by melting weighed quantities together under palm oil, stirring well, and castilig in a heated graphite mold. The polishing and etching techniques employed largely govern the visibility of the structural changes. The preliminary surfacing operations were similar to those recommended by Villela and Bergekoff,5 through Behr-Manning 3/0 abrasive papers, lubricated by a solution of paraffin in kerosene. A rough metallographic polish was next given, using a thin cotton cloth charged with relevigated alumina (maximum particle size of about 4µ) and soap solution; repeated etching and polishing served to remove disturbed metal. For high-power examination better preparation was necessary. It was found that on such soft metals the threads of the fabric, rather than the abrasive, cause most of the scratching. Cotton outing flannel, which had been brushed so that the nap lay down, was fairly satisfactory, but a heavy grade of silk velvet (not the noncrushable kind) was found to be better, especially after some use. A better procedure was as follows: The metal lap was warmed slightly, and a 4-in. circle of woolen broadcloth was cemented to its center by a thin film of melted paraffin. The broadcloth was then moistened with water, and a 30 to 40 per cent solution of sodium hydroxide heated to about 50°C. was poured over it, allowed to stand for I to 2 min. and then washed off. It was neither necessary nor desirable to remove all the sodium hydroxide from the cloth, since its etching action aided in the removal of the flowed layer from the sample. The cloth was then charged with a paste of the relevigated alumina in water. Since this lap did not remove deep scratches, it was necessary previously to polish the specimen on some material such as the silk velvet. The sodium hydroxide softens and partly gelatinizes the woolen lap covering, permitting a scratch-free polish, but its action continues, and the cloth deterioratcs after about 24 hr. This is not serious, because a new lap can be prepared in about 5 min., and only small pieces of cloth are used. Etching with a strongly acid solution of ferric chloride was found satisfactory for removing the flowed layer. For the final etching, the most satisfactory reagent was that of Tafls,7 the formula for which is: FeC13.6H2O, 2 grams; HC1, 5 c.c.; H2O, 30 c.c.; C2H5OH (95 per cent), 60 C.C. This etchant reveals differences in com-

Jan 1, 1942

R. S. Shoemaker: Our first question is, is there a need for a grizzly before a primary crusher? What is its effect on crusher capacity and crusher maintenance? Is it worth the extra capital cost in a crusher installation? Vincent: ASARCO has a grizzly at Mission. Utah Copper uses grizzlies ahead of their gyratories. There is some quite abrasive ore at Mission, an argillite type of rock, which has a work index of 16.5 to 20, which is getting up toward the taconite classification. We get a life of 12- 16 million tons per set of concaves or per mantle with the grizzly ahead of the crusher. At Duval Corp., some 6 miles to the south of Mission, their crusher installation on a good, hard rock does not have a grizzly, and the last information I had is they get a life of about 2 ½ -3 million tons on their mantle and concave. At Silver Bell, our other copper unit in Arizona, they do not have a grizzly ahead of the gyratory and there they get a life of about 5-6 million tons. At Utah Copper, which we all know is a fairly soft ore, relatively speaking, they get a life of 24-27 million tons with grizzlies ahead of the crushers. I think a grizzly has a very definite effect on the life of the mantle and the concaves. As far as a jaw crusher is concerned, I think that usually it is desirable to have a grizzly if it is properly designed, which means it is self- cleaning. Otherwise I would not like to see one in the circuit.

Jan 9, 1967

By C. H. Mathewson

ABOUT fifty pages of Henry M. Howe's profound treatise, "The Metallography of Steel and Cast Iron," are devoted to twinning with special reference to the origin, nature and general significance of the Neu-mann bands in ferrite. Howe believed with Osmond and Cartaud1 that the Neumanns are mechanical twins and his careful observations leave no doubt that these straight-sided narrow bands habitually occur parallel to trapezohedral planes of form {211}. Attempts to develop the structure of the bands by various methods so that their identity could be established beyond question have not been conspicuously successful. Howe thought that they deflected slip bands. Some of the etching figures which have been developed within and adjacent to Neumann bands support the contention that they are twins. A good example of this effect in ferrite containing 0.6 per cent. of nickel and 1.3 per cent. of phosphorus, originally due to Harnecker and Rassow,2. was reproduced in the 1928 lecture before the Institute of Metals Division on twinning in metals.3 In this case, the sides of the figures might represent the traces of cubic planes laid bare by etching a properly oriented grain of ferrite, twinned along a plane of form 12111. Our own observations in this direction may be represented by Fig. 1 which shows in a deeply etched cavity in the boundary region between a Neumann band and the original crystal two small crystal surfaces which resemble the faces meeting at a reentrant angle in the simple cube twinned along a bisecting plane of form {211} as sketched in Fig. 2. Rosenhain and McMinn4 in 1925, after a careful study of slip bands in ferrite containing Neumanns previously produced by shock, concluded

Jan 1, 1928

By A. M. Gaudin, A. F. Taggart

Flotation of ores is a practical utilization of the energy that resides in the surfaces of solids and liquids. The best known manifestation of this energy is called surface tension; an equally important, though less apparent, phenomenon is adsorption. This paper reviews some of the recent investigations of these phenomena, and gives the results of certain experiments performed by the authors. Surface tension is a manifestation of energy having its seat at the bounding surface between the adjacent phases of a multiphase system. Thus, at the interface between a liquid and a gas, or between two immiscible liquids, or between a solid and a gas or a liquid, there are forces capable of doing work, their magnitude depending on the nature of the adjacent phases and the extent of the bounding area. These surface forces are inappreciable when the ratio of surface to volume of the adjacent phases is small, but they become powerful when this ratio becomes large, as it does when one of the phases is highly dispersed. Froth flotation, which consists in buoying solids heavier than water to the surface of water by means of gas bubbles, utilizes the force of surface tension to attach the solid particles to the gas bubbles and again to maintain the floating mass of bubbles as a more or less persistent froth at the surface of a pulp for a sufficiently long time to allow its removal. It follows from the second law of thermodynamics that the potential energy of a system in equilibrium is a minimum. Therefore a multiphase system, tending toward equilibrium, will arrange itself in such a way that the total energy of the interfaces will be the least possible. This end can be accomplished in two ways: by a change in shape that will reduce the interfacial area; by a change in the nature of the surface layer in

Jan 1, 1923