By E. M. Norris

Phosphate deposits are distributed widely over the earth's surface. Of the known areas of deposit, eight fields are of particular interest because of their vast reserves of high grade phosphatic material and the volume of their production that goes to the world's great consuming areas. These fields, in the order of their present economic importance, are situated respectively in Florida, French Morocco, Kola Peninsula of U.S.S.R., Tunisia and Algeria, Tennessee, Montana-Idaho-Wyoming-Utah, Ocean and Naru Islands in the Gilbert group, and in Egypt. The Rocky Mountain deposits have a comparatively low ranking in the phosphate trade of today, but this field contains one of the largest known reserves of phosphatic material, associated with which are recoverable trace minerals, which are of increasing importance in our national economy. The first discoveries of phosphate rock in the western states were recorded in Cache1 and Rich2 counties in Utah, respectively in 1889 and 1897. Mining operations were begun on these deposits near Montpelier, Idaho, in 1906. During the latter year geological studies of the phosphate beds were started by Weeks and Ferrier of the U. S. Geological Survey. These studies have been continued to the present day by a distinguished roster of the Survey's technicians. As a result of this systematic exploratory program, the Survey has published a series of bulletins, papers, and maps, which provide the mining public with a comprehensive study of the exposed

Jan 1, 1949

By S. Y. Ogawa

The effects of sulfur (up to 0.1 pet) on the deformation and fracture characteristics of iron, in cast form, were studied at strain rates up to 100 pct pcr sec and at temperatures of 1600o to -3300 oF. The effects of oxygen and manganese additions on the behavior of Fe-S alloys were studied under comparable test conditions. Brittle fracture characteristics, evident at all strain rates, resulted from the presence of the liquid iron sulfide phase at grain boundaries. Ductility could be restored in three ways: solution of the sulfide in solid y iron at higher temperatures, spheroid-zzation of the liquid sulfide, and increase. in the melting point ot the sulfide. THE literature shows that most previous studies of deformation and fracture at hot working temperatures have been based on measurements of energy absorption, reduction of height in forging upset tests, torsion tests of bar or wire samples, and so forth,' but that relatively few tension tests have been used at high temperatures and strain rates. The present work was initiated to study the ef- fects of temperature, strain rate, composition, and structure on the deformation and fracture characteristics of iron, utilizing cast specimens tested in tension. As in a previous study,' strain rates up to 100 pct per sec were chosen for the temperature range 1600° to 2400° to provide data which might be useful in the interpretation of the deformation and fracture behavior of steels under hot working conditions. The previous work was with Fe-P solid solution al10ys;2 this work is concerned with Fe-S alloys, and with the effects of oxygen and manganese additions. MATERIALS AND PROCEDURE Cast tes! specimens were employed throughout, since most of the difficulty during hot working occurs in the initial breakdown of the ingot. Alloy Systems. Ten 25 lb. heats containing sulphur were prepared. Of these, three had manganese additions, and two had oxygen additions. The sulfur content varied from 0.023 to 0.10 pct. Manganese contents were intended to be ten to twenty times the sulfur content of the particular alloy. Oxygen, being more difficult to control in small melts, was varied by the amount of solid deoxidizer added, but poor control of the oxygen content was experienced in most instances. Table I shows the chemical analyses of the heats. Melting and Casting. Electrolytic-iron chips were melted by high frequency induction in a prefired, clay-graphite crucible lined with rammed magnesite.

Jan 1, 1962

By R. P. Abendroth

This study is concerned with the kinetics of selective oxidation of chromium in a commercial Fe-Cr-Ni alloy. Selective oxidation of chromium in this alloy, by use of a low oxygen-potential atmosphere, leads to the formation of a compact, protective layer of Cr2O3. This layer serves to protect this alloy from gross scaling when it is subsequently exposed to severe oxidizing conditions at high temperature. The interaction of low oxygen-potential atmospheres close to equilibrium with Fe-Cr and Ni-Cr alloys has been studied by others."' These studies werk concerned with the surface-structure variations under slightly oxidizing conditions. NO detailed study was made of the oxide scale formation kinetics, however. The alloy samples were cut from 0.012-in.-thick sheet, with an apparent surface area of 7.1 sq cm. These sheet samples were abraded through 4/0 metallographic paper, and washed in alcohol and acetone. The analysis of the sheet alloy is (in weight percent): 42 pct Ni, 5.5 pct Cr, 0.09 pct C, 0.18 pct Al, 0.36 pct Si, 0.26 pct Mn, balance Fe. The weight gain vs time data were obtained with a 2-g capacity fused-silica spring—cathetometer system. The spring deflection was optically magnified ten times before being read by the cathetometer. A sensitivity of about 0.01 mg was attainable. The spring was enclosed in a water jacket maintained at 60°C to minimize the effect of temperature changes. The sample was suspended from the spring with a fused-silica hangdown and was positioned in the thermal center of a mullite furnace tube. Sample temperature was read with the aid of a thermocouple placed outside the mullite tube and an inside vs outside temperature calibration. Temperature change during the course of a run was ±0.25°C, with a temperature gradient of less than l.O°C over the length of the sample. Total temperature uncertainty was no more than ±3.0°C. Alignment difficulties between the hangdown and radiation shields in the furnace tube required that the sample be positioned in the furnace when cold, and heated with the furnace until the temperature stabilized at the desired point. This required 5 to 6 hr, and was carried out in Matheson ultrahigh-purity hydrogen. Oxidation was started, after evacuation, by introducing a hydrogen-water vapor mixture, obtained by saturating hydrogen with water vapor at 31.00o ± 0.02oC. Oxidation was continued for 90 min. Gas flow was 300 ml per min during heat up and oxidation. Since only several milligrams of oxide are formed on each sample, chemical analysis of the oxide is difficult. A representative analysis is: 80 pct Cr2O3, 5 pct Fe2O3, 3 pct Al2O3, 4 pct MnO, 7 pct SiO2, 1 pct or less NiO. X-ray diffraction analysis of the oxide as formed on the alloy gives rhombohedra1 Cr2O3, and barely distinguishable amounts of a cubic spinel phase, and possibly AlZOs and SO2. The identification of these latter two compounds is by no means certain. The spinel phase could be based on iron or manganese as these elements are present in significant amounts in the oxide. The results of the kinetic studies using 31°C dew-point hydrogen-water vapor mixtures were found to conform to a parabolic rate law. In many cases the parabolic plot consisted of two intersecting straight lines, defining an early and a late rate for a particular run, and in the other cases the parabolic plot consisted of one straight line for the entire run. The slopes of the various straight lines were determined by the method of least squares. Reproducibility of the data was good enough for multiple runs at the same temperature such that the value given for the rate constant is the average for two or more closely similar values, rather than widely varying values of the rate, where more than one determination is indicated in Table I. The exhibition of only one or of two rate constants during a run can happen at the same temperature. Thus, Table I shows that at 11'74°C a single rate constant was obtained from one sample, while other samples oxidized at the same temperature gave an early and a late rate constant. It should be noted that the single rate constant corresponds very closely with the early rate constant. This is also true at 1153°C. The time at which the late rate started to appear was variable, usually occurring 20 to 40 min after oxidation had started.

Jan 1, 1964

By Nestor Torres-Acuña, Fathi Habashi

Metallic copper of purity equal to commercial electrolytic copper is deposited during the anodic dissolution of technically available white metal, Cu2S, in m acidic solution of' copper(II) sulfate as electrolyte and copper sheets as cathodes. The process may be applied on commercial scale since it has the advantage of by passing the converting and poling steps, decreasing pollution problems due to SO, and recovering the sulfur of the white metal in the elemental form. The anodic dissolution is believed to take place in three steps: The working conditions that lead to 98 pct cathodic current efficiency are: 30 gpl Cu2+ and 100 gpl H2SO4 in electrolyte, current density 1.0 amp per sq dm, and tetnperature of bath 40°C'. DURING the smelting of copper, nickel, lead, and zinc sulfide ores, large amounts of sulfur dioxide are produced. Because the release of this gas in the atmosphere causes pollution problems, many attempts were made in the past for its recovery either in liquified form or processed to sulfuric acid. Although these two forms of sulfur are the usual forms that are consumed by the chemical and metallurgical industries, their storage and transport usually raise economic problems. It was realized, long ago, that a process by which sulfur can be recovered directly in the elemental form would be most attractive. Elemental sulfur is easily stored and transported, and is readily converted to SO2, H2S, or H2SO4 when needed. Processes aimed to recover the metals from their sulfide ores, and at the same time by-product sulfur in the elemental form, were recently reviewed.' As early as 1882, Marchese2 patented a process in which a matte having the composition: Cu 15, Pb 14, Fe 41, and S 25 pct was electrolyzed. According to cohen3 the process was applied on a pilot scale by the Aktiengesellschaft fur Bergbau-, Blei-, und Zinkhiitten-betriebe at Stolberg, Rheinland, Germany. The process was unsuccessful, however, owing to the contamination of the electrolyte during electrolysis. Studies in this field were reported by Bernfeld4 and Egli.5 Borchers et a1.6-8 developed the process further by using white metal (Cu 78.2 pct, S 19.6 pct) instead of the matte, and a pilot plant was operated by the Mansfeldschen Kupferschiefer Co. at Eisleben, German~.~ It appears, however, that the process never went into commercial operation. Further studies in this direction were carried out by Russian workers.10-23 The International Nickel Co. of Canada erected a pilot plant at Port Colborne in 1951 to apply the process to nickel matte which is essentially pure nickel sulfide."'- 26 Full-scale plant went into operation at the Thompson Refinery in Manitoba in 1964.27 In this method nickel sulfide matte is melted and cast into anodes analyzing 76 pct Ni and 20 pct S with small amounts of copper, cobalt, and iron. These anodes are then electrolyzed in an aqueous solution of NiS04 at pH 4. Further work on this method was reported in the literature.28-31 In this paper, experiments on the anodic dissolution of white metal in aqueous copper sulfate solution are reported. EXPERIMENTAL White metal, Table I, obtained from The Anaconda Co., was cast in form of anodes 10 by 7.5 by 1 cm, Fig. 1. The anodes are mechanically strong and do not break easily; when polished they gave a shiny gray metallic appearance. From the chemical composition shown in Table I, it can be seen that the atomic ratio Cu:S corresponds approximately to the formula CU2.06S. The copper in excess to the formula Cu2S is most probably present as a separate phase since metallic copper could be seen under the microscope, Fig. 2. Fig. 3 shows the X-ray diffraction pattern of white metal which matches fairly well with that of reagent-grade Cu2S.

Jan 1, 1969

By James R. Cudworth

OUR colleges and universities have met many difficulties during the past year. From a period of small enrollments and depleted faculties, the educational institutions have passed quickly to a period of the largest enrollments in their history with inadequate facilities and staffs. The results of the shortsighted policy of the Selective Service system which drained the technical schools and universities of many of the students who were potential teachers are now being felt. The movement of faculty members into positions in industry during the war years has resulted in many of them forsaking permanently the educational field for the higher salaried positions they now occupy. Competition is keen between the educational institutions, and between the institutions and industry, for technically trained men. Dean Holbrook's statement in last year's annual review that he thought it would take three or four years to restore our engineering departments to their former level in quality of instructors is even more convincing today. Somehow, the institutions must not only reach their former level in quality of instruction but they must also increase the quantity of their staffs to meet the demands of the ex-service men and the high school graduates for engineering education. The enrollments in the mineral industry fields of mining, metallurgical, geological, petroleum, and ceramic engineering, although greatly increased, are not expanding as much as in the more widely known fields of electrical, mechanical, aeronautical, and civil engineering. In fact, many educators are tremendously worried about the segregation of so many young men in a relatively few fields while the needs of others will remain unanswered.

Jan 1, 1947

By G. A. Beske, P. Hilsch, J. Wulff

The effects of the growth precipitates on the su-perconduching properties of an Al- 15 al. pel Zu alloy have been studied using magneization, transition lem-perature, and residual resistivity measurements. Aging at 230C for 1/2 to 11 he produces an increase in Hfp, Ike field of first penetration, and tut increase in trapped flux. The upper critical field, Hc2 remains constant for such aging tunes. Aging at 200°C produces a decrease in Hfp and an increase in trapped flux. The transition temperature remains constant at Tc - 1.227° ± 0.02°K for aging at 220°C for tims of from 1/2 to 10 hr, and for aging at 200°C it remains constant at Tc. = 1.18° i 0.02°K for times from 1/2 hv to 26 hr. The observed behavior indicates that the superconducting matrix when aged at 220°C behaves tike a type U su-perconducior, but when aged at 200°C behares like a type I superconductor. The magnetization changes after aging can be attributed to the growth and clutnge in distribution of the precipitate in a matrix of fixed composition. IT has been realized for some time that the superconducting properties of alloys are highly structure-sensitive. This is evident in the work of Mould and Mapother1 who examined the properties of an aluminum alloy. Precipitation effects have also been briefly mentioned in other studies.2-4 Bonnin and coworkers5 have observed a sharp inc rease in trapped flux in an A1-Mg alloy when the residual resistivity reaches a value that indicates it is a type II superconductor. Recently Blanc, Goodman, and Nemoz5p have reported on precipitation effects in A1-Ag alloys. Detailed studies of precipitation in Pb-Sn and Pb-Cd alloys made by Livingston6 serve to show that the upper critical fields are enhanced by quenched-in solute. Furthermore. at various stages in the precipitation process? the upper critical field is determined largely by the remanent solute. The observed magnetic hysteresis and trapped flux in such alloys result from the interaction between precipitate and the flux filaments in the mixed state. The flux trapping appears to depend largely on the precipitate distribution and is greater if the superconductor is type II than if it is type I. To examine the effect of precipitation in another alloy system, particularly one in which the composition of the superconducting phase does not change significantly during the course of precipitation, the Al-Zn system seems interesting, especially in view of the transition temperature and resistivity studies of Chiou and seraphim.' Furthermore, the recent detailed electron-microscope studies of an Al-Zn alloy by Richards and Garwood8 provide a guide for relating superconducting properties to changes in structure. For these reasons, magnetization, transition temperature, and residual resistivity measurements for varying times of heat treatment at two temperatures were made with a -15 at. pct Al-Zn alloy. The results are reported in this paper. I) EXPERIMENTAL The alloy used was prepared by Cominco Products Inc. from 99.9999 A1 and 99.999 Zn. It was chill-cast, swaged, and drawn to 0.125-in.-diam rod. The analyzed composition was 15.6 at. pct Zn (31.1 wt pct). A jeweler's saw was used to cut the 0.125-in.-diam rod into the 0.875-in. lengths needed for magnetization measurements. The ends of the cylinders were slightly beveled to remove the sharp edges. A portion of the original 0.125-in.-diam rod was drawn into 0.010-in.-diam wire and used for transition temperature measurements. Specimens were suspended from wires within a vertical furnace during heat treatment. All were homogenized at 500°C for a minimum of 3 days and subsequently solutionized for times in excess of 6 hr. The solutionizing temperature was held constant to +3°C. Individual specimens were homogenized, quenched, and aged several times and no effects indicating loss of zinc were noted. The suspended specimens were quenched by cutting the wires and allowing the specimens to fall into a silicone oil bath held at the aging temperature. They were then isothermally transforked by aging in the same bath used for quenching. After aging for the required time (approximately 10 min aging was necessary before the upper critical field reached a fixed value), they were briefly (1 to 2 sec) dipped into an acetone bath at room temperature to remove adherent oil and then immediately transferred to liquid nitrogen where they remained until inserted into the helium bath (usually within an hour). The temperature of the aging bath was held constant to +3°C for longer aging times. The cryostat used for the measurement of superconducting properties consisted of outer and inner dewars for liquid nitrogen and liquid helium, Stokes 6-in. booster diffusion pump and Stokes Model 212 mechanical pump, temperature controller to measure and control the temperature of the helium bath, and a superconducting solenoid with inserted search coils to provide the magnetic field and measure the magnetic moment of the specimens. A schematic diagram of the cryostat is shown in Fig. 1. An ultimate temperature of 0.85°K was reached with this apparatus. The temperature controller used is similar to the one described by Blake and chase.' A 0.5 pct Allen-Bradley carbon resistor and a nichronle heater (200

Jan 1, 1968

By W. D. Robertson, J. -P. Briant, M. Gell

The distribulion of dislocatiorls genevnted during the propagalion of hydrogen-induced cracks in Fe-Si cryslcrls was studied as a funclion of temperature f-110o lo 243°C) and silicorz conlenl (3.1 and 4.2 pct). It zoas found that the clislocntiotl densily and the size of the plctslic zone increased with increasing tempevalnre and decreasing silicon conlent. Furtheruvzove, there was a correlcrtion in the dislocalion patterns formed around cracks that propagated at different tempevattrt-es in cvyslals of diffevent silicon contents such that a 1 pcl itlcverise in silicon content was equivalent to a lemperaluore redziclion of approximately 120°C. The experimenlal YeSnllS were compaved with the results of an elastic-plastic wodel that relates the size of the pluslic .zone to the cvack length, internal pressure, and yield stress. it was found that the clzunges in the dislocctlion cryrays with lemperature and combosition can be e-kplaincd by the lemperatrnre and composilion dependence of the yield stress. An wmtsual feature of this study was the observation of low -temperature noncrystrrllogruphic cracks. PLASTIC relaxation can occur at the edge of a moving crack by the operation of pre-existing dislocation sources or by the creation of new sources in a region of perfect 1attice.l'2 The amount of relaxation in a given crystal depends on the crack velocity and the temperature, and can determine whether a crack propagates in a brittle or a ductile manner.1-3 Tetelman and Robertson4 observed microcracks m Fe-3 pct Si single crystals that formed on (100) planes by the precipitation of hydrogen gas during electrolytic charging at 23°C. The plastic deformation accompanying crack propagation was observed in the form of dislocation etch pits and an extensive analysis has been made of the size, shape, and crystallography of the dislocation arrays5-7 This paper describes the effect of temperature on the plastic deformation generated around hydrogen-induced cracks in Fe-3.1 pct Si and Fe-4.2 pct Si single crystals. The observations are compared with the results of an elastic-plastic model for yielding around a crack containing an internal pressure. 1) EXPERIMENTAL PROCEDURES The composition of the materials used in this study are given in Table I. Single crystals of alloy A and the 4.2 pct Si alloy were grown by the strain-anneal method; crystals of alloy B and the 5.1 pct Si alloy were cut from an ingot grown from the liquid. he ~ingle-cr~stal metallographic specimens had a Cross section of 0.100 by 0.050 in. with a length of at least 3/8 in. Specimens were annealed for 3 hr at

Jan 1, 1968

By B. F. Tillson, C. M. Haight

I. General Remarks..........................723 1. Location............................723 2. Characteristics of the Orebody..................725 (a) Mineralogical (b) Shape, Strike, Dip, Size, Etc. (1) Ore (2) Country Rock 3. Historical Sketch........................725 11. Mining Method..........................726 1. Outline of Methods Now in Operation............... 726 (a) Stopes (b) Fill . (c) Pillars (d) Slices (e) Transportation (f) Miscellaneous 111. Mining Operations........................727 1. Shaft..............................727 (a) Sinking (b) Dimensions and Equipment, Sketches (1) Size, Inclination. Direction, Etc. (2) Timbering (3) Stations (4) Track (5) Hoisting Equipment (a) Skips (b) Engines and Ropes (c) Idlers (d) Man Cars (6) Loading Pockets (a) Operating Figures (7) Headframe

Jan 1, 1918

A regular general meeting of the Canadian Mining Institute will be held in Vancouver, B. C., on Nov. 26-28. The Council extends a cordial invitation to all members of the American Institute of Mining and Metallurgical Engineers to attend.

Jan 11, 1919

By J. E. Cannaday, R. J. Austin, R. K. Saxer

PREVIOUS investigators have determined activation energies and have postulated various controlling mechanisms for creep.'-' Recently Barrett et 01.I5 have suggested, as the result of their work with cadmium, that the apparent activation energies for creep (AHc) above 0.5 T, could be correlated by means of activation energies for self-diffusion (AHSD) and modulus of elasticity functions: AHC = AHSD - (5RT/E) dE/dT. The wide disparity of apparent activation energies previously obtained with nickel compared to those reported for other fcc metals and the desire to test the postulate of Barrett el al. prompted this study. The as-received 17.5-mil nickel wire used during this work assayed 99.87 pct pure, Table I. X-ray analysis indicated that the wire was in a stress-re- lieved state and metallographic examination revealed an equiaxed grain size of approximately 0.01 mm. Specimens degreased in acetone and cut to 1-1/2 in. lengths were tested in a cam-mechanized constant-stress creep machine. A vacuum of at least lo-5 mm Hg was maintained during all tests. Stresses were applied when thermal equilibrium was established. When a measurable (at least 0.5 pct) secondary creep was observed, the temperature was pulsed to a higher temperature. Pulsing time varied from 30 sec at 480°C to 2 min at 1300'C and above. Slopes of creep curves were determined after the initial acceleration in the strain rate had subsided and steady-state creep was achieved. To confirm the results obtained, additional tests were performed incorporating a temperature pulsing method suggested by sherby. In this method the load was removed during temperature pulsing and reapplied after thermal expansion had occurred. No appreciable differences in results were obtained. Tests were performed over a wide range of temperature (470" to 1310°C) and stresses (250 to 17,000 psi). The expression was used to calculate activation energies. In this expression T1 and T2 are the initial and final temperatures, and el and i2 are the creep rates at T, and T2. The variation of the apparent activation energies with the mean test temperature calculated by means of Eq. [I] are shown in Fig. 1. The mean test temperature (Tmean) was calculated from the relationship

Jan 1, 1967

By A. Perry Thompson

I- GeneRal Distribution, AppeaRance, and Relations ........ 563 11. Data fRom MicRoscopic Examination............... 568 1. Criteria for Distinguishing Primary from Secondary Minerals...... 568 2. The Leonard Vein Filling..................... 574 Quartz............................ 575 Pyrite............................ 575 Enargite............................ 576 Covellite............................ 578 Bornite............................ 581 Chalcocite........................... 583 Chalcopyrite.......................... 586 3. The Fault-Vein Covellite..................... 587 The Speculator Ore........................ 587 The East Gray Rock Ore.....,.............. 589 4. Other Occurrences of Covellite.................. 591 111. Conclusions........................... 592 1. The Replacement of Minerals..................592 2. The Character of Mineralizing Solutions .............. 594 I. General Distribution, Appearance, and Relations Mining in Butte has seldom encountered covellite in commercial quantities. The notable occurrences, extending vertically and laterally perhaps several hundred feet, presented scattered, bladed lenses of this mineral in a matrix of quartz, pyrite, enargite, bornite, and chalcocite. But under the microscope covellite is seen to be widespread in the Butte ores, though in such small quantity that megascopic examination will not discover it. In early mining operations covellite was found in the Gray Rock vein, a member of the Blue vein system. As described by Sales,' it persisted as an occasional ore mineral, associated with quartz, pyrite, tetrahedrite, bornite, chalcocite, and minor amounts of sphalerite, from the 700-ft. to the 1,200-ft. level of the East Gray Rock and Diamond mines. Crushed quartz-monzonite and later quartz completed the vein filling between

Jan 1, 1916

By R. C. Schmidt, B. E. Kennedy

The Mont Klahoyo magnetite deposit is located about 600 km (373 miles) northwest of Abidjan, Ivory Coast. During an exploration period ending in 1977 an international joint venture group investigated the deposit and proved reserves of 670 Mt (739 million short tons) grading 36% iron. The deposit occurs at the northeast end of the Baoubly-Kiriao chain of Precambrian iron formations with associated amphibolites, pyroxenites, and gneisses of the Liberian Shield. The ore body is represented by a highly metamorphosed banded quartz-magnetite iron formation with alternating beds of iron silicates and quartz-magnetite. Amphibolite-pyroxenites and sillimanite-cordierite-garnet gneisses form hanging and footwall rocks. The iron formation has been folded into an elongated, overturned 2-shaped major drag fold with axes trending and plunging approximately northeast. Beds are vertical or dip steeply to the southeast. The ore zone has an average thickness of 130 m (427 ft) and outcrops intermittently over a distance of approximately 5.5 km (3.4 miles). Based upon detailed studies of drill cores and the results of ore dressing test work, eight stratigraphic units, identified as K- 1 to K-8, are recognizable in the iron formation. Four interbedded units are low grade silicate zones (silicate facies) while the remaining quartz-magnetite units are oxide facies, representing the important Mont Klahoyo deposit ores. Ore-bearing "K" units are subdivided further into 11 ore types, based upon their specific lithologies, iron content, and concentration characteristics. Identification of these ore types proved particularly useful to mine planning and flowsheet design. A cap of oxidized material overlies the primary quartz- magnetite iron formation, but no enrichment has occurred. It is thought that the Mont Klahoyo iron formations were deposited chemically in a volcanic environment as a siliceous iron formation with volcanism the primary source of iron and silica. Metamorphism converted the siliceous iron formation to a coarse-grained, quartz-magnetite-silicate iron formation.

Jan 1, 1983

By F. L. Bosqui

The history of the development of gold metallurgy in South Africa is divisible into two periods: That preceding the introduction of the cyanide process on a commercial scale in 1890; and the 24 years intervening between that important event and the present time. The period between the discovery of the banket reefs of the Witwaters-rand and the year 1890 was one of phenomenally rapid progress in mining development, but of no special interest to the metallurgist, There were no strikingly original or distinctly local advances in the treatment of gold ores. Californian practice in stamp milling and amalgamation prevailed, in mills ranging in equipment between 5 and 50 stamps, operating within a wide range of efficiency, and under the trying conditions usually encountered in a new and isolated field. The somewhat incomplete records of gold output of that period show that in December, 1887, there were 20 producing companies in the Witwatersrand district, of which 10 had mills, the largest being of 20 stamps. The only official record of returns for May, 1887, was that of the Wemmer mine, whose modest achievement with a 5-stamp mill was 100 tons crushed, producing 887 oz. 3 dwt. of gold. This is interesting in view of the present-day output of this field, which in 1913 reached 8,430,998 oz. The rapid increase of production during this first period (May, 1887, to January 1891) is shown by the following summary for the year 1890:1 Total tone crushed.................................. 702,828 Number of stamps in operation....................... 1,046 Average number of tons crushed per stamp per day..... 2.36 Yield of gold, ounces................................ 494,817 Yield per ton, pennyweights.......................... 13.36 The stamp duty ranged between 11/2 and 4 tons per day, according to weight of stamp, fineness of screen, and operating skill available. The prevailing weight of stamp was about 900 lb., and the screen, 900 meshes to the square inch.

Jan 1, 1916

By W. Gundaker, F. C. Schwerer

Natural chromium-bearing spinels (chromites), which are used as refractory materials in basic steelmaking, are the only commercially important chromium ore and are also encountered as difficult-to-separate contaminants in ore deposits of potential economic value. Techniques for characterization and separation of ore materials frequently are dependent on the magnetic properties of the constituent minerals. An experimental program was initiated to explore the effects of temperature and of simple mechanical and thermal treatments on the static magnetic properties of several ore-grade natural chromites. Studies of the temperature dependence of the magnetic properties showed that the natural chromites, which are dilute in the magnetic ions Fe and Cr, order magnetically only at cryogenic temperatures. However, mechanical treatment in the form of crushing produces a magnetic component that is ordered at room temperature and that is of sufficient strength to alter magnetic-separation characteristics. The additional magnetic component apparently is associated with surface structures which develop during crushing and disappear after heating to above about 500°C. Preliminary studies indicate that this surface structure enhances the susceptibility of the chromite grain surfaces to gas reactions at moderate temperatures.

Jan 1, 1976

Through the courtesy of Mr. J. H. Batcheller, we are able to give the following extracts from a letter written by Mr. Caetani: It has been a nice idea of yours to collect for me all those scraps of news I received a few days ago and to send me such a long interesting letter. In four years war I have had practically no news. Burch wrote several times but several of his letters were lost and so mine. I believe I even wrote to you. Much has changed since our last days in Telluride; here and there many have disappeared. Of myself I will tell you in a few words: for a year I was in Cadore(?), where I had the good luck to do to the others what they wished to do to me, and had good luck on my side. Then I went to Macedonia for 5 months, did little fighting but lost my faithful fellow officer and companion.

Jan 6, 1919

By Cuppam Dasarathy

The incidence of liquid inzmiscibility in binar)) indium alloys has been theoretically analyzed on the basis of the Hildebrand-Alott equation. Bedictions of miscibility or otherwise Imve in general been found to agree with those phase diagrams that are already publislzed in the literature. Out of a total of 27 systems, where either the complete phase diagrams are published or liquid immiscible behavior is reported, the Predictions agree with the experimental data in 25 systems, the exceptions being the Te-In and Ni-In systems. According to the equation, liquid immiscibility is also indicated in the binary alloys of indium with K, Rb, Cs, Na, Sr, Ba, Ti, Zr, V. Nb(Cb), Ta, W, U, Re, Ru, Rh, Os, and Ir. RECENT investigations by the author have shown that indium when alloyed with iron, chromium, and cobalt shows liquid immiscible behavior.1"3 The Fe-In phase diagram shows a wide range of compositions where the liquids are immiscible.4,5 No intermediate phases are present in this system. No precise information is available about the extent of liquid immiscibility in the Co-In system. However, it is certain that there is a range of compositions where the liquids are immiscible and that there are two or three intermediate phases,376 in the system. Liquid immiscibility is also strongly indicated in the Cr-In system and no evidence was obtained in the brief investigation to indicate the presence of intermediate Cr-In phases.2 The present paper deals with a theoretical analysis of binary alloys of indium with certain elements of the periodic table and indicates the systems where liquid immiscibility may be expected. The incidence of liquid immiscibility in binary systems has been theoretically examined by many workers and many excellent papers are available on the subject. In this paper, the alloy systems are examined on the basis of the more recent ideas proposed by Mott.7,8 It has been claimed8 that the Mott parameter predicts the incidence of miscibility or otherwise with reasonable accuracy and consistency. BACKGROUND TO MOTT&apos;S APPROACH Hildebrand applied his immiscibility rule for non-polar liquids to various alloy systems.9 The basis of this rule is that the equation for the excess free energy of formation of a liquid solution is rather similar to the theoretical expression for the energy of mixing of a regular solution. He postulated that when the heat of mixing is sufficiently high, separation into liquid phases will occur and the condition for complete CUPPAM DASARATHY is at the Research Centre, British Steel Corporation, (South Wales Group), Port Talbot, Glamorgan, Great Britain. Manuscript submitted March 12, 1969. IMD miscibility was shown as where VA and VB were the atomic volumes of the components A and B, and ?EV the energy of vaporization of the component. The term (?EVA/VA)1/2 was regarded as a measure of the binding energy of the component A and was called the L&apos;solubility parameter" 8A. On this basis immiscibility occurs when 1/2(VA+VB)(bA-bBf > 2RT [2] Apparently, however, there were several inconsistencies in that according to Eq. [2] several systems known to be miscible in the liquid state were predicted as immiscible. MOTT&apos;S ANALYSIS ~ott&apos;" regards that the reason for the inconsistencies arising out of Hildebrand&apos;s equation was largely due to the electrochemical attraction between the two elements, not being considered. Hence, Eqs. [I] and [2] were modified by taking into account the electro-negativities of the two elements XA and XB, and Mott arrived at an equation for immiscibility, i(VA + VB)(6A - aB)2 - 23,Q60n(XA - XBf > 2RT [3j which can be written as i **&£*&* >&apos;*°™- &apos;• HI T being the melting point of the more refractory component of the system. In Eq. [4], the numerator was called the Hildebrand term, the denominator, the electronegativity term, and their ratio, the Mott number. Mott observed that if the Mott number of a given binary system was greater than the maximum number of Pauling bonds which the two metals could form, then liquid immiscibility could be expected. The maximum number of bonds formed by a given metal was considered to be directly related to the number of bonding electrons available, i.e., to its maximum valency. Since the valencies of the elements considered vary from 1 to 6, Mott assumed that if the ratio of the Hildebrand term to the electronegativity term was >6, then immiscibility could be expected. On the contrary, if the ratio is <1, the metals should be miscible. Further, the alloying behavior is not only influenced by the valencies of the two elements but also by the relative atomic sizes that influence the types of packing and hence the coordination number. Mott considers that on average the maximum number of near neighbors of unlike atoms is 6. Thus, on both valency and size factor considerations, Mott concludes that the maximum number of bonds&apos; possible in any system was 6, this being the upper limit of the Mott number for miscibility. In considering the alloying behavior of systems with Mott numbers between 1 and 6, Mott plotted the num-

Jan 1, 1970

By Charles L. Mantell, Kurt Straler

The hydrogen reduction of Cr2O3 to chromium metal was found to be feasible at very low water-vapor concentrations, corresponding to dew points of -38° to -24°C, over a temperature range of 1130" to 1490°C. Hydrogen reduction under these conditions was predicted by the calculated equilibrium curves which also indicated that CrzOs is reduced directly to chromium without forming the intermediate oxide, CrO. This reduction path was confirmed by X-ray diffraction analysis. The percent reduction of Cr2O3 at each reaction temperature was constant with time, suggesting an inhibiting effect of water vapor. A small increase in the residual water-vapor concentration of a single temperature, 1490°C, strongly retarded the rate of reduction This effect was expressed by an empim&apos;cal equation which indicated a direct relationship between "distance from equilibrium" and the rate of reduction. me effect of temperature over the range of 1130" to 1490°C was expressed in an Arvhenius plot of log rate vs reciprocal absolute temperature. From this curve the apparent enthalpy of activation was found to be 29,600 cal. Based on the hypothesis that the rate of reductiun is contvolled at the oxide-metal interface, an over-all rate equation consistent with the experimental data and the thery of absolute reaction rates was formulated. A simplification of this expression to an Arrhenius equation was justified by the overriding effect of temperature on the rate of reaction for the minimum water-vapor concentration range. MOST of the metals in Subgroup V1 of the periodic table can be prepared commercially by direct reduction of their oxides by hydrogen or carbon monoxide, at temperatures considerably below the melting points of both the metals and their oxides. Chromium is an exception, being generally reduced from its ore, Cr2O3 . FeO, by silicon in an electric arc furnace which operates above the melting point of the Fe-Cr alloy or above the melting point of chro- mium if a chromium oxide be the starting material. In reduction of chromium oxide by hydrogen, either reduction does not occur at all or the rate of reduction is extremely slow. Theoretical considerations based on the high, exothermic, free energy of formation of Cr2O3 compared to the oxides of the other Subgroup VI metals, molybdenum, tungsten, and uranium, would also suggest a slow rate of reaction and a high activation energy. Interest in the direct gaseous reduction of fine-powdered ores in fluidized beds was considered justification for examination of this reaction. In order to develop a basis for a continuing study of the commercial feasibility of the direct gaseous reduction of chromite, a study of the kinetics of the reduction of Cr2O3 with hydrogen was undertaken. To the authors&apos; knowledge no accurate kinetic data for this reaction have been obtained. Neither has an activation energy been determined nor has an attempt been made to establish a mechanism of reaction. LITERATURE Maier10 compared the data of I. Y. Granaat,6 H. von Wartenburg and S. Aoyama, and G. Grube and M. Flad7 with that derived from calorimetric and ther-modynamic properties for the equilibria for the reduction of Cr2O3 with hydrogen. These results, plotted as the log of the equilibrium constant vs absolute temperature for the reduction of Cr2O3 and the intermediate oxide, CrO, to chromium, show agreement between the differently derived data. In both cases the equilibrium constants were extremely low. Maier showed that, over a temperature range of 1000° to 2000°K, Cr2O3 is more readily reducible than CrO. Granat assumed that CrO was preferentially formed from Cr2o3 above 1100°C. Grube and Flad&apos;s analysis of their reaction products in the 895" to 1000°C range indicated the coexistence of only Cr2O3 and chromium. The hydrogen reduction of the other Subgroup VI metals, molybdenum, tungsten, and uranium, shows that reduction of the higher oxide proceeds through all of the intermediate oxides before being reduced to the metal. Since evidence pointed to an anomaly in the reduction behavior of Cr2O3, the authors investigated the reduction path of Cr2Os.to chromium. This was done theoretically with more recently available free-energy data and experimentally by X-ray diffraction analysis. This work reinforces Maier&apos;s conclusion.

Jan 1, 1964

By Chas. A. Ashburner

The occurrence of oil- and gas-springs in the State of New York has been a fact of historical record since 1627, when the existence of the Cuba oil-spring was first recorded. The utilization of natural gas at Fredonia in 1821 attracted the attention of the public to the possibility of obtaining an illuminating gas by digging and drilling into the rocks. No active search was made, however, for oil or gas by the drilling of wells until after the discovery of commercial oil in Pennsylvania in 1859. In 1862 a well was drilled at Bradford, McKean County, Pennsylvania, but a few miles south of the New York state line, to the depth of 200 feet, in search of the oil-sand which had been found at Titusville, Oil City, and at other points in Western Pennsylvania. Immediately subsequent to this, other wells were drilled in search

Jan 1, 1888

By T. W. Smoot

Bentonites are composed chiefly of montmorillonites which are clay minerals generally distinguished from other clay minerals by their surface activity and extremely fine particle sizes. The uses of bentonite are many and varied, depending principally on one or more of the following characteristics: 1) Thixotropy, 2) Dispersion, 3) Plasticity, 4) Swelling, 5) Surface area, activity, ab- and adsorbtive properties. Some of the major uses of bentonite are briefly reviewed as are the mineralogical and physical properties. The uses of X-ray diffraction, differential thermal analysis and other tests for physical properties are reviewed as to their uses in evaluation. In the past 40 years, the industrial uses of bentonite have grown to include many applications. The physical and chemical properties of bentonites are such that they can be used as catalysts, adsorbants, plasticizers, binders, drilling muds, and pelletizers. Not all bentonites, however, can be used for all of these purposes and some are probably of little or no value for any use. The purpose of this paper is to briefly review the mineralogical, physical, and chemical characteristics and variations of bentonites. The determination of these characteristics and their uses in industry are also reviewed so that these determinations can be used as guides for evaluation. DEFINITION OF BENTONITE The word bentonite, as used in this paper, refers to a clay material, usually (but not necessarily) the result of the in-place-weathering of volcanic ash. Its mineralogical composition is dominated by the clay mineral montmorillonite and generally carries other clay minerals and silica minerals as the major &apos;impurities&apos;. For this discussion, such a definition is justified since most of the economic uses of bentonite~ depend upon the physical and chemical characteristics of the montmorillonite minerals involved. The terms montmorillonite and bentonite have been used almost interchangeably in industry although the latter is much more commonly used. Therefore, where montmorillonite is discussed, it should be understood that the major feature of a bentonite is the subject. STRUCTIJRE OF MONTMORILLONlTE The economic importance of bentonites is generally based on one or more of the following characteristics of montmorillonite: 1) high-thixotropy and easy dispersion in water, 2) high-plasticity, 3) swelling properties, 4) large surface area/unit mass, 5) high surface activity, and 6) adsorptive properties. To understand these properties, an appreciation of the structural scheme of montmorillonite is helpful. Montmorillonite IS one of the three-layer clay minerals composed essentially of hydrous aluminum silicates. The essential building blocks of these layered silicate:; are: 1) silica tetrahedron composed of a silicon atom surrounded by four oxygen atoms, and 2) aluminun (iron, magnesium, etc.) octahedral unit that, ideally, has one of these atoms surrounded by six hydroxal units. Fig. 1 is a diagrammatic sketch of the montmorillonite structure. In the montmorillonite structure, the tetrahedron are pointed inward and attached to the octahedral units so that the O= atoms replace the hydroxal units where they are bonded; hence two-thirds of the hydroxal units

Jan 1, 1962

By Arthur Bell

(San Francisco Meeting, September, 1915) . PRIOR to 1908 the oil production in the State of California, had been almost entirely a heavy fuel, oil, with a high flash point, hut changed within a-short period to a large percentage of refining oil with a low flash, by reason of the coming in of the Santa Maria field, the Midway field, and the increased production of the Fullerton field. This is clearly shown in the following tabulation of California&apos;s production: Year Barrels . Below -20° Be, Above 20° Be,, Per Cent_ Per Cent. 1905 48,307,000 90 10 1910 77,698,000 SO 20 1912 90,075,000 6o 31 1914 10:3,600,000 47 53 The bringing in of these high percentage&apos;s of light oil with their dangerous low flash and the increasing demand for the refined products necessitated the devising of some cheap and efficient means of quickly separating the lighter elements either in the field or at the main distributing points; also it became necessary to remove the excessive percentage of water which many of the light oils carried in emulsion.

Jan 9, 1915