By Forrest K. Pence

BENTONITE deposits are known to occur in Texas within the Jackson group of formations. This group represents the uppermost Eocene age sediments found in the coastal plain area of Texas. It outcrops across this area of the state in a narrow band of some 4 to 20 miles width. The outcrop pattern roughly parallels the present Gulf of Mexico shore line and is some 100 miles inland from the Texas shore, Fig 1. The principal bentonite deposits are found in the areas where this outcrop pattern cuts across the south-central Texas counties of Karnes, Gonzales, and Fayette. In these deposits, the better quality bentonite is found in the lower or bottom layers of the volcanic ash deposits in which they occur. Some of these better quality bentonites develop very light colors upon firing and therefore justify their being classified as "white firing." The deposits in Karnes and Gonzales Counties apparently occur in commercial quantity, whereas the white firing strata so far uncovered in Fayette County have been too thin to be classified as yet as "commercial." A study of the ceramic properties of the weathered ash in Gonzales and Karnes Counties was reported in 1941.1

Jan 1, 1949

By Axel Hultgren

IN ingots of silicon-killed carbon steel made without addition of - aluminum, transparent spherical or nearly spherical inclusions, up to about 0.15-mm diameter, are generally present. They may be glassy or crystallized, wholly or partially. In steels of high carbon contents they consist of silica,4,12 in steels of lower carbon contents arid, in consequence, higher oxygen contents, of iron-manganese-silicate with higher iron and manganese contents the lower the carbon content. Small silicate inclusions, about 0.01 mm or smaller, may occur, just as sulphide inclusions do, in portions that have been the last or nearly the last to freeze,10,12,17 this location being verified by primary etching.10 Hence, it may be concluded that they have separated from liquid steel that has become enriched in oxygen through segregation during freezing. Silicate inclusions with a diameter larger than about 0.02 mm appear, at least in ingots of moderate size, to be distributed at random in relation to the primary structure and therefore may be assumed to have existed as droplets in the liquid steel before freezing started at the point in question. The average size of such large inclusions has been found to increase toward the axis17 and their amount to increase from the top downward in the axial region .2,10 It has been assumed that this accumulation is a result of the droplets being brought down by the slowly settling metal crystals.2 It has been suggested that large silicate inclusions generally form,6 or may form," by coagulation of smaller ones, or by small drops being caught by larger ones during the rising of the latter.9 The occasional occurrence of a large inclusion surrounded by a swarm of small ones has been taken as a proof of this mechanism but, as suggested later, may be explained in another way. It has been pointed out that an inclusion droplet in the liquid steel may grow at the expense of an adjacent one, which implies diffusion of soluble inclusion-forming elements in the liquid steel.15 Further, it has been pointed out that, on cooling in ladle or mold, the metal-silicate equilibrium is displaced in the direction of separation of silicate. Thus inclusions may grow in size and amount.2,3,8,12,13,17,19,20 The exposure of the liquid steel to the oxygen of the air during tapping and pouring, and the consequent reaction, has been mentioned as a source of the formation of inclusions19,20 but this possibility has not received particular attention. Further, the admixture of furnace slag during tapping' or of refractory material from various sources1,20 has been considered. The inclusions due to the latter may be recognized, however, through their resistance to hydrofluoric acid, imparted by the alumina content. Silicate inclusions, are often referred to as. the natural and inevitable product of reaction on adding silicon or silicon

Jan 1, 1948

By A. D. Hughes

A relatively small area in Malaya, about 200 miles long by 40 miles wide, is the most important source of tin in the world. Some tin is recovered in other parts of the peninsula. Of the tin mined, 98 pct is recovered from alluvial deposits. From 1935 to 1941 the average annual world production of tin was 190,000 tons. The average annual production from Malaya during the same period was 62,000 tons or about one third of the total. Other producing countries, in order of importance, were the Netherlands East Indies 34,000 tons, Bolivia 30,000, Belgian Congo, Nigeria, Siam, Burma, China, and a few others with smaller amounts. The serious shortage of tin during the war period was due to the fact that the Japanese were occupying Malaya, Netherlands East Indies, Siam, Burma, and China which, together, formerly were producing 65 pct of the world supply.

Jan 1, 1949

By W. L. Penberthy, H. J. Ramey

Experimental work on the combustion oil recovery process has consisted of both laboratory and field studies. Although field experiments are the ultimate test of any oil recovery process, they are costly, time consuming and difficult to analyze quantitatively. Laboratory combustion tube experiments can be opertzted far more rapidly and cheaply, but are subject to scaling and interpretation problems. This paper points out some important design problems, operational criteria and considerations in2portunt to interpretation of results. An analytical hcut model of movement of a burning front axiully along a cylinder with heat loss through an annular insulation was developed. The result was used to identify steady-state temperatrrre distributions both ahead of and behind the burning front, with and without heat loss. Results indicate potential operating limitations on the minimum burning front rielocity (or air flux) which may be used for any given combustion tube. Results also enable estimating the effective thermal diffusivity and over-all heat loss from experimental data and thickness of the brnning zone. Resu lts of operation of a combustion tube constructed recently verify this preliminary theory in the region immediately ahead of and behind the burning front surprisinRly well. INTRODUCTION Many field and laboratory studies of the forward combustion oil recovery process have been conducted since the early publications of Kuhn and Kochl and Grant and Szasz2 in 1953 and 1954. In view of the complex and costly nature of this type of investigation, it is not surprising that no complete theory of the nature of the forward combustion Drocess is yet available. However, gross effects are understood well enough that reasonable design procedures are available for planning field operations. Nelson and McNeil 3,4 have published two comprehensive papers concerning design procedures. One major consideration in planning field operations is the fuel concentration at the burning front. Fuel concentration controls air requirements — an important cost factor in forward combustion. Although fuel concentration can be estimated from field test results by various methods, results are subject to great uncertainty in view of natural limitations on experimental observations. Nelson and hlcNeil4 recommend that fuel concentration be determined from laboratory combustion tube studies. Fuel concentration is only one of many important factors which can be studied by combustion tube experimentation. An obvious goal of imporrance must be development of a comprehensive theory of the forward combustion process. If a theory of this process can be established which matches controlled laboratory experimentation, it should be possible to apply this theory to field operating conditions with some confidence. Laboratory combustion tube studies have already yielded important information concerning the combustion process. However, details concerning the design, construction and operation of combustion tubes are rare. Combustion tubes used by various investigators vary in size, length and mode of operation. Therefore, one purpose of this paper is to present considerations important to design, construction and operation of a combustion tube. In regard to previous combustion tube studies, attention is called to Refs. 1 through 9. These references describe a wide variety of equipment types and present a great deal of pertinent experimental data. In general, combustion tubes usually consist of thin-walled stainless steel tubes containing an oil sand pack mounted within a pressure jacket. Provisions have often been made to heat the tube ex tern a lly by separately controlled heaters to reduce heat losses. This step usually permits operation at low air fluxes (air rate per square foot burning front surface) similar to those encountered in field operations. Burning is usually conducted from the air inlet end of the tube to the outflow end. The tube orientation used has been vertical or horizontal. For vertical tubes, burning has been conducted vertically downwards. As a result of laboratory studies, many of the

Jan 1, 1967

By L. F. Porter, G. J. Dienes

The effect of netltron irracliation on mart ensite transformation in the iron-nickel system was studied by means of electrical resistance and magnetic induction measuremertts. Irradiation lowers the M8 temperature of the allay, causes changes in the electrical and magnetic properties of the high-temperature phase which indicate either an accelemtion of phase separation or a clustering of nickel, and enhances strain recovery on specimens partially transformed to martensite prior to irradiation. Possible mechanisms to account for the effects; are discussed. 1 HERE is a good deal of evidence to indicate that neutron irradiation is capable of affecting phase changes in metals and alloys. While the mechanism of the effect often is not well understood, such studies hold promise of improving our understanding not only of irradiation damage but also of the phase changes involved. To date systematic and detailed investigations have been made of the influence of nuclear radiation on order-disorder transformations in the copper-gold, nickel-manganese, and copper-zinc system, and on precipitation reactions in the copper-iron, nickel-beryllium, and copper-beryllium system.' These solid-state reactions are diffusion controlled and the results can be explained largely on the basis of enhanced diffusion due to the presence of irradiation produced vacancies. Reversion of low-temperature eutectoid phases to the high-temperature phase has been observed in the fissionable uranium-molybdenum and uranium-niobium systems.2 Here it is necessary and logical to postulate a displacement spike mechanism to account for the effect. The only case of irradiation induced diffusionless transformation in metals is the allo-tropic transformation of p to a tin reported by Flee-man and Dienes. 3 They found that neutron irradiation markedly decreases the incubation time for transformation, but the mechanisnl is not well understood. Another diffusionless transformation which one might expect to be influenced by neutron irradiation is the martensite transformation. This transformation is known to be sensitive to strain, structural hardening, and the presence of imperfections.6,7 Since the transformation is diffusionless, one also

Jan 1, 1960

By Charles M. Brown, Russell Franks, W. O. Binder

Occasionally in the application of the austenitic chromium-nickel steels to corrosive conditions, failures have occurred by cracking without serious general over-all attack of the metal. As pointed out by Foyt and Scheil(1),2 and by Scheil, et al.(2) as well as by Hodge and Miller(3), the stress-corrosion failures that have occurred have been limited in number, and have taken place only when the steels were exposed to certain corrodents. These investigators have stated that while stress- corrosion cracking can be intergranular in nature and originate at the grain boundaries of the austenitic chromium-nickel steels, it can also take place in trans- granular fashion. They have shown that the cracking may be either initiated at the grain boundaries and may propagate along grain boundaries for some distance and then suddenly extend across grains, or it may begin in a transgranular fashion and suddenly proceed along grain boundaries until the cracking stops. Their data further show that when austenitic stainless steel is subject to intergranular attack, stress will concentrate and cause cracking in service. These investigators have studied the effect of the metals titanium and columbium which are added to the steels to impart immunity to intergranular attack, and molybdenum which is added to improve resistance to general corrosion.

Jan 1, 1945

Jan 1, 1910

By Frank C. Schrader

Page Introduction.............................. 196 Geology of the District......................... 196 Ore Deposits of the District....................... 198 Gcncral Description........................ 198 The Cerbat Mountains Group................... 199 General Description...................... 199 Tennessee Mine....................... 203 Midnight Mine........................ 203 Mineral Park........................ 204- Golconda Mine........................ 204 Other Ore-bearing Districts.................. 205 Lost Basin District ...................... 205 The Black Mountains Group.................... 206 Tom Reed-Gold Road District...................... 208 General Dcscription........................ 208 Development........................... 209 Topograplly............................ 210 Geology.............................. 210 Ore Deposits........................... 213 General Dwcription...................... 213 Zones.......................:....215 Structure of Ore Shoots.................... 217 Gold Road Mine ......................... 218 General Description...................... 218 Geology........................... 218 Ore Deposits......................... 219 Tom Reed Minc......................... 222 General Description..................... 222 • Ore Deposits.......................... 222 Development......................... 223 Character of Ore....................... 224 Other Mines........................... 224 Fields Similar to the Ton1 Reed-Gold Road District......... 227

Jan 1, 1917

By S. D. Strauss

The marketing of nonferrous metals and of the ores and concentrates from which these metals are recovered is a fascinating trade, international in character, sensitive to every change in the economic tide, and complex in its organization. Each individual metal has its own marketing mechanism; no two are exactly alike. The differences sometimes are a matter of tradition rather than of necessity, but usually they have developed because of the very nature of the problems of producing or consuming the individual metal. This description, because of limitations of space, can do no more than indicate the major aspects of the trade and touch lightly on the marketing structure of each metal. The dictionary states that a market is a "meeting of people for selling and buying." In the case of nonferrous metals this meeting may occur on a half-dozen different occasions between the time the ore has been first mined and the time the refined metal is available for use by industry; or it may not occur at all until after the metal itself has been rolled, drawn, stamped, cast, or forged into a useful semifabricated shape. To illustrate: A Chilean miner may sell his small ore production to a custom mill, which produces concentrates that are sold to an ore dealer, who finances the shipments of the concentrates to a United States custom smelter, which buys these' concentrates for conversion into blister, which is subsequently refined into electrolytic copper and sold. Conversely, much of the production of aluminum is in the hands of integrated concerns that mine bauxite, convert bauxite to alumina, smelt the alumina to produce aluminum, and then fabricate the aluminum into semifinished or even finished products before title to the material changes hands for the first time. Some nonferrous ores are not converted into metal at all but are sold by the miners or dealers directly b the ultimate consumers. A good example would be chrome ores used by the chemical industry. And of course a substantial part of the commerce in nonferrous metals is in scrap, which is the reconversion into useful form of metals that have long since been mined and smelted. Thus, one-third of all the lead used in the United

Jan 1, 1959

By S. R. Zimmerley, S. F. Ravitz

High-grade cobalt concentrates were produced from the complex Blackbird ore with very good recovery in continuous pilot-plant operations in which a low-grade bulk cobaltite-pyrite flotation concentrate was roasted in a multiple-hearth furnace to oxidize the pyrite selectively. The cobaltite was floated from the resulting calcine.

Jan 1, 1950

By R. J. S. Brown, B. W. Ganison

A new logging method has been developed, based on measurement of the nuclear magnetism of formation fluids. The nuclear magnetism log (NML) is the only log that responds solely to formation fluids. It operates equally well in both oil-base and water-base muds and in empty holes, and can be used in all kinds of formations except strongly magnetic ones. Two separate NML measurements can be made, one of which provides a continuous formation fluid curve. This fluid curve is called the free fluid log (FFL) and is believed to indicate a minimum effective porosity in most formations. The FFL not only delineates fluid-containing zones, but provides an excellent correlation curve that can be obtained under conditions where conventional correlation logs are ineffective. Preliminary tests indicate that the second kind of NML measurement may help distinguish oil and water zones and provide information concerning permeability and wettability. (The FFL itself appears to provide some information on permeability.) The second kind of NML measurement requires stopping the logging tool for a short time opposite a zone of interest and taking more extensive NML data that can be displayed as nuclear magnetic relaxation curves. In some instances, oil and water saturations for the region immediately adjacent to the borehole can be read from these relaxation curves. INTRODUCTION In 1946, Bloch, Hansen and Packard and Purcell, Torrey and Pound3 independently announced the successful demonstration of the phenomenon of nuclear magnetic resonance. During the past 13 years, there have been many applications of nuclear magnetic resonance, including applications to the study of chemical structure and to the measurement of magnetic field strengths. Preliminary experiments on the feasibility of using nuclear magnetism measurements in well logging were made independently by California Research Corp. and Varian Assoc., the Varian work being sponsored by the Byron Jackson Tools, Inc. Since then a cooperative research program on nuclear magnetism logging has been carried out by the Byron Jackson Div. and Research Center of Borg-Warner Corp., and California Research Corp., subsidiary of Standard Oil Co. of California. The use of nuclear magnetism in well logging is of special interest because it offers a way of making direct measurements on the hydrogen in the formation fluids and not on the rock matrix. Within the past 1 1/2 years, successful measurements have been made with a research model logging tool in wells in California, Tex as, Utah, Louisiana and Wyoming. NUCLEAR MAGNETISM SIGNALS Polarization, Relaxation and Precession Many atomic nuclei possess magnetic moments and spins; that is, they are similar in some respects to bar-magnet and gyroscope combinations. Molecules and their nuclei are subject to thermal motion, which has a scrambling effect, tending to leave as many nuclear spins oriented in any one direction as in any other. However, if a magnetic field is applied, the magnetic nuclei tend to align in the direction of the field. The scrambling and aligning forces compete with each other, with the result that a few more spins are oriented parallel to the field than in other directions. This gives a net magnetization, or polarization, which is directly proportional to the strength of the applied magnetic field (aligning influence) and inversely proportional to the absolute temperature (scrambling influence). When the magnetic field in, or temperature of, a liquid sample containing protons is changed, the new equilibrium value of proton polarization is not established immediately but requires an amount of time which depends on the nature of the hydrogen-containing materials. The process of approaching the equilibrium value of polarization is called relaxation.'.' Polarization is a vector quantity, and the components parallel to and perpendicular to the magnetic field must be considered separately. Relaxation of the component parallel to the field is called "thermal relaxation", or "longitudinal relaxation", and the corresponding time for this component of non-equilibrium polarization to decay by a factor of e (natural log base) is denoted T. The relaxation of the perpendicular component is called "transverse relaxation", and the corresponding relaxation time is denoted T,. The potential energy of a magnet in a uniform field depends on the angle the magnet makes with the field; therefore, a change of the component of net polarization parallel to the magnetic field involves an exchange of energy between the spin system and the thermal motion of the molecules, leading to the term thermal relaxation for the relaxation of this component. Suppose we subject a sample to a strong magnetic field at right angles to the earth's field for a time greater than TI. A polarization, thus, is established at right an-

By H. S. Martin

ALTHOUGH it was known some years ago at the- Utah Copper Co. mills that fine grinding improved flotation recoveries, no accurate data were available until recently as to just how far the grinding could be carried economically. In 1923 the ultimate degree of fineness for flotation feed was supposed to be about 10 per cent. on 65 mesh, with approximately 55 per cent. through 200 mesh, which meant that most of the mineral would pass 100 mesh. At this time Garfield and Wilfley tables were used ahead of flotation and a good deal of the coarse mineral removed prior to the ball mill regrind. Shortly afterwards, mill-scale tests developed the fact that on a feed containing not over 10 per cent. +65¬mesh material flotation alone would give a copper recovery equal to that obtained by the combination of tables and flotation, but that on much coarser feed the recovery with flotation alone was lowered. This was at a time when all the sulfide minerals were floated if possible, so that the only requisite was to grind fine enough to free the mineral from gangue. EARLIEST USE op MICROSCOPIC EXAMINATION OF TAILINGS As early as 1921, the writer had attempted to determine by chemical analysis the relative proportions of copper minerals in tailings from an ore that made extremely poor flotation results. Chemical analysis was not satisfactory or conclusive, and samples of these tailings were sent to the U. S. Bureau of Mines Station at the University of Utah for micro-scopic examination. The question at that time was to determine, if possible, which copper minerals had been lost and why, but R. E. Head, in his report, revealed other interesting data. He said in part: Briefly stated, the mineral particles or grains may be classified into separate groups as follows: 1. Free grains of pyrite, chalcopyrite, chalcocite and bornite, respectively, which contain no other included sulfides; 2. Grains in which all three of the copper sulfides are represented (the core may he of chalcopyrite, partially altered to bornite, these two minerals being entirely surrounded by a shell of chalcocite); 3. Grains composed of equal amounts of bornite and chalcocite or chalcopyrite and chalcocite.

Jan 1, 1929

By B. J. Harlan

THE trying times experienced by the steel industry during the past four years have emphasized the necessity of producing pig iron at the lowest possible cost. The trend in both design and operation of blast furnaces has been toward this end rather than securing maximum production from a unit or group of units. In the following discussion the trend in design of stacks and auxiliary equipment will be taken up before operation is considered. Although few furnaces have been constructed in the past few years, the trend is definitely toward larger furnaces with a hearth diameter of 24 or 25 ft. Such a furnace is very flexible, being able to produce efficiently any desired daily tonnage between 500 and 1000 or more. The detail of the design of furnace stacks, with the exception of the top, has changed little in recent years.

Jan 1, 1934

Jan 1, 1928

By Carl Pierce

The writer of this article has not attempted to write a technical paper; on the contrary, he has tried to express in "steel-plant English," for steel men, a viewpoint drawn from his practice and experience. It is not his thought that it shall be taken as the "last word" in the making of this class of steel, or that good rimming steel cannot be made by any other practice. The paper was written to serve as the basis of a discussion from which it is hoped much benefit may be derived. The paper deals only with rimming steel made by the open-hearth process, and with the lower carbon steels, such as sheet and tin bar, rivet stock, skelp, etc., although good rimming steel as high as 40 to 50 carbon can be made by having good open slags and giving proper attention to working and tapping temperatures. Definition of Rimmed Steel Rimmed steel is sometimes called open or effervescing steel to differentiate it from killed or partly killed steel. It is steel made by a process which permits the free escape of gases from the metal in the molds. In passing up through the metal, the gases keep it in a rolling action from the walls of the mold inward. The top of the ingot rims in as the metal chills and the walls of the ingot get thicker, the center part remaining fluid until it reaches a pasty condition when it is covered with a cast-iron cap. The Charge In making up a charge for rimming steel, clean stock of a known composition must be selected, special attention being given to the analysis of the materials. The silicon in good rimming steel must be eliminated to a trace, therefore it is advisable to have a uniform amount going into the charge. Too much silicon gives a raw melting heat from which rimming steel is unlikely to result. For this reason a charge containing not to exceed 40 per cent. pig iron and 60 per cent. scrap, with no iron ore, is preferred to the Monell type of charge in which as high as 65 to 70 per cent. pig iron is used with a proportional amount of iron ore for the removal of the excess silicon and carbon. The silicon content of pig iron varies so much from day to day in the average blast-furnace practice that there is danger of getting too much of this element in the latter mixture when

Jan 1, 1926

By William G., Pariseau

There are important phenomena in rock and soil mechanics that cannot be explained in terms of theories of homogeneous, isotropic materials. Subsidence of strata about mine openings is an example. In-situ stress measurements in nonisotropic sedimentary, and metamorphic rocks is another. Patterns of joints, faults, fractures, and similar geologic features impart directional mechanical properties to rock masses that are locally isotropic or anisotropic. On the geologic scale, the non-homogeneity of composite rock masses may, in certain instances, be dealt with as homogeneous anisotropy. The mechanics of large rock masses can, therefore, be expected to involve considerations of anisotropy. The source of the anisotropy is not relevant. Once the scale of observation is selected and the material is defined accordingly, the analysis of stress and deformation proceeds without regard to the numerical values of the material constants. There are also important phenomena in rock and soil mechanics that cannot be explained in terms of linear elasticity, theory. For the mechanical description of anisotropic geologic materials capable of de- forming beyond the limit of purely elastic strains, a plasticity theory is required.

Jan 1, 1972

By H. R. Hanley

THE characteristics of alloyed anodes and their influence on the products of electrolysis and power consumption have been noted previously in the literature.1 This paper presents data in continuation of the subject given in an earlier paper by the authors.2 As noted in the authors' previous paper, the objectives of this work are the reduction in the cell voltage and the purity of the cathode product resulting from the use of alloyed lead anodes. The fundamental facts developed in the previous paper were: (1) that the presence of a small amount of calcium lowers the anode potential approximately 50 per cent. below that of pure lead; and (2) that thallium when present to the extent of 4 per cent. rendered the anode practically stable, thereby lowering the contamination of the cathode by lead to a very insignificant amount. The specific features determined in this recent work are as follows: 1. The lowest limit of calcium in the lead which will still give maximum lowering of the anode potential. 2. The characteristics of the thallium-calcium-lead anode. 3. The characteristics of the silver-calcium-lead anode. 4. The characteristics of the thallium-silver-calcium-lead anode. It was determined that 0.1 per cent. calcium in the anode was sufficient to lower the anode potential approximately 50 per cent. Table 1 shows the characteristics of alloyed anodes tested. The anode composed of 0.1 per cent. calcium, 4 per cent. thallium, and 95.9 per cent.

Jan 1, 1931

By I. J. Polmear

Earlier work revealed that small amounts of silver (< 0,l at. pct) may exert a marked effect on the structure and aging characteristics of certain a1loys based on the Al-Zn-Mg system. Silver additions have now been made to other age-hardening aluminum alloys, and significant effects have been observed in the Al-Mg system and in several Al-Cu-Mg and Al-Mg-Si alloys. Similarities exist between the behavior of alloys from all four systems, notably that in each case silver stimulates nucleation of an intermediate precipitate which forms when the alloys are aged in the medium temperature range (-120" to 220°C). The mechanism for this effect is uncer- IT has been shown that small additions of silver (<0.1 at. pct) may have a marked effect on the structure and age-hardening characteristics of tain although it is suggested it originates in a preferred affinity between magnesium and silver atoms. There is evidence to indicate that the effects of silver are unique to that element. It is suggested that silver atoms interact with vacancies during low-temperature aging of Al-4 pct Cu and certain Al-Cu-Mg alloys. Silver had little effect on Al-8 pct Zn aged at any temperature. Preliminary observations indicate that silver may have interesting effects on the strength properties of Al-Mg alloys, md a the commercial Al-Cu-Mg alloys designated as 2024 and 2618. many alloys based on the Al-Zn-Mg* system.1"&apos;*

Jan 1, 1964

ALTHOUGH the refining period of the heat is generally defined A as starting after the charge has been completely melted, it may more properly be considered as beginning with the first efforts to facilitate the shaping up of the slag and the making of corrective additions for the control of slag or metal composition. Such actions may be initiated during the latter half of the lime boil. The early part of the refining period may, then, in essence overlap the latter part of the melting period. The primary aims of the refining period are: (1) to reduce phosphorus and sulfur from the steel bath to levels safely below the maximum contents specified; (2) to eliminate carbon to a specified level as rapidly as possible and still allow time for proper conditioning of the slag and attainment of the necessary bath temperature; and (3) to have the heat ready for tapping or furnace deoxidation, with slag in the proper physical and chemical condition, and with carbon and oxygen contents and the temperature of the steel at the proper levels for the composition and grade of steel being produced. The particular conditions that fulfill these aims are distinctly different, depending upon whether the steel is to be finished according to fully killed semikilled, or rimming practice and also depending upon the carbon range specified. Regardless of the type of charging practice employed, the object of the refining period is to produce repeatedly the desired finishing and tapping conditions for the grade of steel being produced. The variations and proportions of raw materials used in the charge may cause some variations in the degree of control required during refining, but not in the method of control. The refining period can therefore be discussed from a viewpoint largely independent of charging and melting practice. SHAPING UP THE SLAG In the first helper&apos;s vocabulary, refining practice consists in

Jan 1, 1964

By Henry Rawdon

Cold-working is generally considered as a process of hardening metals. Diamet-rically opposite statements concerning the applicability of the scratch-hardness method in the testing of cold-worked metals, particularly after severe deformation, which exist in the technical literature led to the study of the results which are summarized in this paper. A series of metals, of which copper, iron and tin are used as illustrations here, were cold rolled to a definite degree without any intermediate annealing and the hardness determined by both the scratch and Brinell methods. The results indicate that the metal hardens rapidly during the initial stages of deformation; however, after a certain stage, which corresponds to a rather definite microstructure, the metal becomes softer and in its final form may be softer than the metal in its initial stage. As part of the study of the scratch-hardness method for metals and alloys in cooperation with one of the technical committees of the American Society for Testing Materials, the authors devoted considerable time to the study of the changes in hardness of metals when cold rolled. Various seemingly contradictory statements in the technical literature concerning the applicability of the scratch-hardness method to such cold-rolled materials were among the principal reasons for the investigation, the results of which are in part presented here. The effect of cold deformation, at least in moderate degrees, on the hardness as measured by the Brinell and other common methods is so well known that further reference is unnecessary. Concerning the scratch hardness of cold-worked metals, Martens and Heyn state&apos; that hardness, whether measured by the ball-pressure method (Kugeldruck) or by the scratch method (Ritzverfahren), will be increased by cold deformation. Jeffries and Archer give a seemingly diametrically opposite view. They state,2 that "the sclerometer (indicating scratch

Jan 1, 1924