Search Documents

By W. M. McKewan, R. G. Olsson

In order to improve the understanding of the iron oxide reduction mechanism, the rate of equal molar diffusion of hydrogen and water vapor was measured through disks of porous iron and alumina. The measuretneizts were made at atmospheric pressure at 800°, 900- , and 1000°C. It is shown tint the reduction of dense hematite pellets with hydrogen at these temperatures and at atmospheric pressure is to a great extent limited by gaseous diffusion between the bulk-gas phase and the iron-wustile interface. THE investigation of the reduction of iron oxides with hydrogen has been the subject of numerous papers. Although the effects of temperature, pressure, and gas composition on the rate of iron oxide reduction have been studied, the actual mechanism of the reduction process has not been definitely determined. As a means of improving the understanding of the mechanism, the rate of equal molar counterdiffusion of hydrogen and water vapor was measured through porous iron and porous alumina disks at reduction temperatures. The alumina was used as a basis of compari-son because its pore structure is homogeneous and independent of temperature. The porous iron was prepared by the reduction of dense hematite disks with hydrogen at the temperature of the subsequent diffusion experiment. The hematite disks were made from pellets that were identical to those used by McKewan1,2 in his study of iron oxide reduction with hydrogen. In these investigations the weight loss and rate of movement of the various interfaces were measured as a function of the reduction temperature and gas composition. With these reduction data and the presently reported diffusion data it is possible to determine the importance of H2-H2O transport between the bulk-gas phase and the Fe/FeO interface to the reduction of dense hematite. APPARATUS AND PROCEDURE A porous iron or alumina sample was held in the base plate of a sealed canister containing porous granular wustite, as illustrated schematically in Fig. 1. The canister was suspended from an automatic recording balance in a vertical tube furnace through which flowed hydrogen and water-vapor mixtures of known composition at atmospheric pressure (0.96 atm). Hydrogen from the gas stream diffused through the porous sample, reducing the wustite in the interior of the canister. The water vapor that was formed diffused back to the gas stream. The rate of diffusion was determined from the recorded weightloss data. The furnace, automatic balance, and gas-metering equipment have been described previously.2 The main body of the canister and the tubing extension were made of stainless steel while the base plate was made of high-purity iron. The main body of the canister was % in. in diam. It held approximately 6 g of porous granular wustite that was prepared by reducing 0.1- to 0.2-cm-diam specular hematite particles at 900°C with an H2-H2O mixture of a composition near the iron-wustite equilibrium value. The upper end of the 1/8-in.-diam tubing extension was sealed with a segment of plastic tubing and a tubing clamp. The temperature at the top of the furnace was sufficiently high so that no water vapor condensed inside the extension. In the experiments with porous iron, iron oxide samples were prepared from reagent-grade hematite that was pressed and sintered in a manner previously described.' The resulting pellets had a density of 5.15 ± 0.05 g per cu cm. Each pellet was centerless-ground

Jan 1, 1967

By Spencer S. Shannon

The lanthanide elements from lanthanum (atomic number 57) to lutetium (71) plus yttrium (39) are called the rare-earth elements; scandium (21) is chemically similar to yttrium and the lanthanides, but differs in occurrence. The rare-earth metals were divided into three categories by the chemist, Berzelius, in the early 1800s; however, modern usage defines only two groups. The cerium group is named after the most abundant -element and comprises lanthanum (57), cerium (58), praseodymium (59), neodymium (60), promethium (61), samarium (62), europium (63), and gadolinium (64). Traces of natural promethium were discovered in apatite in Finland (Erametsa, 1965). The yttrium group, also named after its most abundant representative, comprises terbium (65), dysprosium (66), holmium (67), erbium (68), thulium (69), ytterbium (70), and lutetium (71). Yttrium most closely resembles holmium in chemical properties, and occurs most commonly with the heavy lanthanides. The rare-earth minerals may be divided into cerium-group, yttrium-group, or mixed-group classes. A number of rare-earth minerals contain thorium and uranium, but these are variable in content and are not essential to the composition of the minerals. In monazite, a mineral that is a principal source of rare earths, the worldwide average content of thorium oxide is 7.2 % ; however, varieties of monazite contain as little as 0.001% and as much as 31.5% thoria. Monazite is the chief ore of thorium and, until recently, thorium has been the main product; the rare-earth metals were in fact byproducts. However, because of the great demand for rare-earth metals by the petroleum refining and the iron and steel industries since the early 1970s, the roles have been reversed so that thorium is now the byproduct. Uses A 9 to 1 mixture of yttrium and thorium oxides is used for high-intensity incandescent lamps and for high-temperature-resistant windows and lenses. Yttrium oxysulfide and orthovanadate, doped with europium oxide, are used in color television tube phosphors. Yttrium, as well as cerium, praseodymium, and samarium, is alloyed with cobalt to form strong permanent magnets. It hardens magnesium alloys and retards the oxidation of iron-chromium alloys. Yttrium-iron garnets are used for transmitting low microwave frequencies. Yttrium-aluminum garnets are used as host crystals for lasers and as artificial gems. Yttria also forms strong, stable, high-temperature refractories. Gadolinium-gallium garnets are used in substrate wafers on which bubble-memory films are deposited. Rare-earth chlorides, particularly of lanthanum, neodymium, and praseodymium, are used as catalysts for petroleum cracking. Mischmetal is used for lighter flints and to improve the ductility and impact strength of iron and steel alloys. Mischmetal also reduces the fatigue resistance of magnesium and aluminum alloys. Rare-earth oxides are used for polishing glasses and lenses. Individual or specific combinations of high-purity oxides are used as additives in glass to maintain or change its color, dispersion, or refractive index. High-purity oxide combinations are also used to color tile and to opacify porcelain enamel. Rare-earth fluorides and oxides are used in carbon-arc electrodes to provide incandescent white light. Lanthanum or gadolinium oxysulfide phosphors, activated with terbium, are used as x-ray screen intensifiers. Hydrogen can be stored by sorption on lanthanum-nickel alloys (Anon., 1979). Thorium232 is bombarded with slow neutrons in breeder reactors to create fissionable thorium233 for nuclear fuel cells. The 330-MW, high-temperature gas-cooled reactor at Fort St.

Jan 1, 1983

By G. L. Kehl, Emilo Jaraiz F., J. S. Brett

The transformation of eutectoid beryllium bronze has been quantitatively investigated at 550° and 592°C, the temperature region where the products of p decomposition are a fine lamellar eutectoid and a coarse lamellar aggregate which replaces the fine eutectoid with prolonged annealing. Metallographic evidence indicates that the coarse lamellar aggregate forms preferentially in the most densely lamellated regions of the fine eutectoid and favors the hypothesis that the development of the coarse lamellar aggregate in the fine eutectoid is due to the occurence of a cellular segregation reaction. WHEN eutectoid beryllium bronze (Cu-94 pct, Be-6 pct) is isothermally transformed at high temperatures in the and y region after quenching from the fl field, the principal initial decomposition process is G one of growth of approximately spherical nodules composed of a number of lamellar colonies of the a and y phases. After the initial reaction has proceeded substantially or completely, depending on the transformation temperature, a second reaction occurs wherein the fine lamellar eutectoid is replaced by a coarser lamellar aggregate composed of the same oand yphases.' This reaction is not simply a spheroidization of the initial fine eutectoid but the nucleation and growth of a coarser, structurally different, and more stable distribution of the @and yphases. Fig. 1 illustrates the replacement of the initial fine lamellar structure by a coarse lamellar aggregate. The a phase is the dark mottled constituent; the light constituent the y phase. The phase diagram for the copper-rich end of the Cu-Be system2 is shown in Fig. 2. The a phase has the face-centered cubic structure characteristic of copper-rich solid solutions. The B phase is a disordered body-centered cubic structure, while the y phase is body-centered cubic, ordered (CsC1, B2 type). A. viswanathanS investigating Debye patterns of Cu-6 pct Be discovered that a transitory phase appeared on very rapid quenching from the /3 region which was absent when the quenching velocity was moderate. The phase could be assigned a body-centtred cubic structure with a lattice parameter of 2.876. Tempering at 100°C for 2 hr after quenching resulted in complete disappearance of the phase. The work of Fillnow and Mack' is the only previously published study of the isothermal transformation of eutectoid beryllium bronze. Their study elucidated the nature of decomposition at various subcritical temperatures in an exploratory fashion. The purpose of the research reported in this paper was principally to obtain quantitative information on the isothermal decomposition of the fl phase and to clarify the relationships existing between the fine lamellar eutectoid and the coarse lamellar aggregate. EXPERIMENTAL PROCEDURE The material used in this investigation was an almost eutectoid Cu-Be alloy bar furnished by D.J. Mack. The alloy had been melted under a protective carbon cover and centrigugally cast into a graphite mold preheated to 490 "C. Segregation was minimized by violent agitation during melting and pouring. The analysis of the casting was 93.85 pct Cu, 5.60 pet Be with traces of Si, Mg, Mn, Co, and Al. To determine the minimum soaking time necessary to insure specimen homogeneity, a number of specimens were held in the P region at 788OC for times fron 1 min to 12 hr and isothermally transformed at 550°C. Specimens betatized less than 12 min exhibited partial transformation at times shorter

Jan 1, 1961

By H. S. Price, D. A. T. Donohue

The system of equations describing displacement of a hydrocarbon liquid by a hydrocarbon vapor in a porous medium where mass transfer takes place between the phases is solved numerically for a variety of gas injection processes. Even though the method of solution is quite general, only systems with three hydrocarbon components are considered. Computer simulations of displacement processes wherein mass transfer between phases is both considered and neglected are compared, and it is shown that neglecting mass transfer can give pessimistic displacement efficiencies. INTRODUCTION The role of the gas displacement process in the recovery of petroleum has been subjected to a series of detailed analyses; as a result, a number of predictive models have been published in the literature. However, because of major simplifying assumptions, most of these models do not completely represent the physical system. As a result, the effect of making the simplifying assumptions is unknown. Therefore, a complete representation of this process — one without major simplifying assumptions —should lead to a fuller understanding of the process, and perhaps to methods of improving it. The general method of developing a model for two-phase fluid flow in a porous medium is to solve simultaneously the continuity equation, the energy equations and the equation-of-state for each phase under the prescribed initial and boundary conditions. For an isothermal system, the energy equations reduce to the momentum equation. Darcy's law. However, since natural gas is the vapor state of the reservoir liquid, interphase mass transfer may take place with concomitant changes in both the intensive and extensive thermodynamic properties of each phase. It is this phenomenon that has often been omitted in previous mathematical models. An additional relation, then, which accounts for mass transfer between the phases, must be included with the other equations to specify a complete model. Completely formulating the equations to be solved is not a difficult task1 but obtaining their solution has been intractable up to now. Availability of large-memory, high-speed digital computers now makes an attack on this formidable problem possible. This paper presents a preliminary study of the problem. Since this investigation is intended to be exploratory, it is restricted to the linear, horizontal, isothermal, two-phase viscous flow of oil and gas in an oil reservoir. In the early development of predictive models of this process, the reservoir system was considered as a unit and various forms of the material balance equation were proposed.2-4 Pressure and saturation gradients were then added in the Buckley-Leverett model.5 The Buckley-Leverett formulation considered the fluids to be incompressible; thus, the mathematical model reduces to a steady-state system. In the 1950's, studies incorporating numerical techniques were being published.6-9 These mathematical models differed in the efficiency of finite difference techniques, the inclusion or exclusion of capillarity or the number of space dimensions considered. To solve these nonlinear, partial differential equations, each phase was considered to be homogeneous with time; therefore, mass transfer between phases was neglected. The effect of mass transfer on the gas displacement process was first reported by Attra. 10 He simulated the one-dimension flow system by a series of cells in each of which the fluids were equilibrated during a time step. In addition, the pressure throughout the system during each time step was predetermined and constant-phase velocities were calculated according to the Buckley-Leverett incompressible fluid flow model. Welge et al.11 developed a model for the displacement of oil by an enriched gas where composition is considered to be a dependent variable. Fluid

By R. D. Mollison, C. F. Fogarty

Sulfur is widely distributed in nature. It is present in the earth's crust, the ocean, the meteorites that come to us from cosmic space and in practically all animal and plant life. According to Clarke,9 the earth's crust contains 0.06 pct sulfur. Large quantities of free or combined sulfur are found in coal, natural gas and petroleum. Mineral waters contain sulfates and hydrogen sulfide. Sulfur is rather plentiful in the crust of the earth; however, only under special circumstances can it be produced profitably. Sulfur is one of the cheapest raw materials used by industry; and, therefore, the economic feasibility of a given deposit is strongly dictated by the law of supply and demand on local as well as world-wide levels. The forms which are commercially important are elemental sulfur or brimstone, and the sulfides such as pyrite (FeS2), pyrrhotite (FenSn+1), chalcocite (Cu2S), sphalerite (ZnS), and galena (PbS); the sulfates such as gypsum (CaSO4,2H2O), anhydrite (CaSO4), and kieserite (MgSO4,H2O). Elemental Sulfur Elemental sulfur is found in many localities, generally in solfataras and gypsum type deposits. The solfatara deposits are found commonly in the neighborhood of active or extinct volcanoes as in Italy, Japan and Chile, or fumaroles associated with mineral springs such as the Mammoth Hot Springs in Yellowstone Park. Here the sulfur is deposited in tufas or other porous host rocks. This type of sulfur deposit probably results from the oxidation of hydrogen sulfide or the reaction of hydrogen sulfide with sulfur dioxide. Most of the world's supply of elemental sulfur comes from the gypsum-type deposits. Here the mineral occurs as either crystalline or amorphous sulfur in sedimentary rocks in close association with gypsum and limestone. This association is characteristic and occurs in almost all the great gypsum beds of the world, although sulfur is not always present in quantities of economic importance. Various theories have been advanced to account for this association. Bischof5 suggested that the sulfur came from hydrogen sulfide which resulted from the reduction of calcium sulfate by carbon or methane in accordance with the following reactions: CaSO4 + 2C= CaS + 2CO2 CaS + C02+ H2O = CaCO3 + H2S CaSO4 + CH4= CaS + C02+ 2H20 2H2S + 02= 2H20 + 2S All of the sulfur-bearing domes on the Gulf Coast have calcium sulfate in great quantity in the cap. They all show the presence of hydrocarbons. The oxygen for the final reaction could have been supplied by circulating ground waters. The principal objection to this theory is that temperatures of 700° to 1000°C are needed to reduce the sulfate to sulfide with carbon compounds. The geologic evidence is that the temperature of the sulfur-bearing domes of Texas did not exceed 100°C. Proponents of the theory say that geologic time or a catalyst replaced temperature. According to another theory the sulfur in the salt domes is the result of bacterial action. Sulfate reducing bacteria have been detected in sulfur cores and in the formation water issuing from salt domes. It has, therefore, been suggested that these bacteria converted the sulfate to sulfide which subsequently was converted to elemental sulfur.

Jan 1, 1960

By L. Zwell, H. A. Wriedt

X-ray Lattice parameter and bulk density measurements were made at room temperature on solid solutions of nitrogen in purified a, iron, containing from 0 to 0.053 wt pct N. When nitrogen is dissolved in a, iron, the fractional increase in unit cell volume (X-ray diffraction) and the fractional increase in volume per gram of iron (bulk density measurement) are the same within experimental error. The two sets of results when averaged show that the unit cell edge of a, iron increases linearly by 3.2 X 10-2 A per wt pct N dissolved and that the partial gram-atomic volume of nitrogen at infinite dilution in a, iron is the same as it is in nitrogen-martensite, that is, 5.90 cm3. RECENT reviews17' of literature dealing with the lattice parameter of ferritic iron-nitrogen alloys indicate that the dilating effect of dissolved nitrogen on the bcc unit cell of a iron is not known with confidence. Five investigations3-7 either revealed no effect of nitrogen or were inconclusive. Among other investigations, where quantitative data were obtained, the results of Osawa and Iwaizumi8 indicate too large an effect, and those of Eisenhut and Kaupp9 show the lattice parameter of ferrite varying with the nitrogen content at concentrations far beyond the known solubility limit. It is not clear in Burns'10 data what value should be used for the lattice parameter of nitrogen-free ferrite in calculating the dilation. Burdese11 shares with Burns the shortcoming that the iron-nitrogen alloys were solution-treated and quenched with undissolved nitride present. The consequence is that the un- certainties in the solubility limit1 are added to those in the lattice parameter measurements when the variation of lattice parameter with nitrogen content is computed. For a system of such widespread interest, we felt that a new investigation was merited. Both X-ray diffraction and bulk density measurements were used to determine the dilation of the , a iron lattice by dissolved nitrogen. EXPERIMENTAL PROCEDURE Material. The bulk density and X-ray diffraction experiments were both made with specimens of a purified iron (denoted as "B iron")- from Battelle Memorial Institute. The impurity contents were as follows: As, C, Cu and Pb—50 ppm; Ag, Al, Co, Ga, 0, Ti-11 to 50 ppm; B, Be, Ca, Cd, Cr, Mg, Mn, Mo, N, Ni, S, Sb, Si, Sn, V, W-10 ppm or less. The vacuum-cast ingot was hot-forged and annealed. Pieces of the forged stock were machined and cold-rolled to give strip stock 0.08 and 0.002 in. thick for density and for X-ray measurements, respectively. Preparation of Specimens. Starting with a piece of the cold-rolled iron stock, the general sequence of operations, after an initial recrystallizing anneal, was to measure the density or lattice parameter, nitrogenize, remeasure the property, age or denitrogenize, and again measure the property. Duplicate analyses for nitrogen were made by a modified Kjeldahl method on portions of the actual density specimens and on pieces nitrogenized to equilibrium alongside the X-ray specimens. Annealing of the density specimens was performed by sealing the pieces with the as-rolled surfaces removed by filing into evacuated "Vycor" capsules and treating for 1 hr at 750°C followed by furnace cooling. (TO check the effect, if any, of annealing procedure, a specimen also was

Jan 1, 1962

By W. A. Wood, H. L. Wain, R. I. Garrod

The mechanical behavior of recrystallized chromil~m of high purity has been studied, principally in torsion and to a lesser extent in tension, at temperatures between —196oand 350oC. Depending upon the conditions of test, the material may show brittle or ductile behavior or an intermediate or subduc-tile state having some of the characteristics of each. This latter state existed at temperatures between approximately ±50°C and was characterized by a) extensive creep at stresses well below the normal fracture stress, b) nonelastic loading/unloading effects during creep, c) strain softening under cyclic loading, and d) final failure of a brittle type. Suggestions are made on the dislocation processes and interactions which give rise to subductile behavior The ductile-brittle transition in bee metals has been studied mainly by tension and bend tests. These methods, however, favor crack propagation which may follow too closely on initiation for detailed study of the transition itself. For work of this nature, therefore, other modes of deformation less favorable to crack propagation may be preferable. This paper describes a study of the ductile-brittle transition in chromium which is based mainly on torsional testing although a few subsidiary experiments were made in tension. It appears to reveal at the transition an intermediate state that cannot properly be described as either brittle or ductile. Torsional tests on chromium have been made by other workers1 but not, as here, primarily for study of this intermediate state. EXPERIMENTAL The chromium, in the form of swaged rod, was prepared by techniques already described.' The particular material used was one in which the main impurities were 0.03 wt pet 0 and 0.006 wt pet N and one in which transition from ductile to brittle states in torsion conveniently fell at about room temperature. For torsion, test specimens were from 5/16-in.-diam rod to provide test portions 1-1/4 in. long by 7/32 in. diam, a twist of 1 deg thereby corresponding throughout this paper to 0.0015 surface shear. The specimens before test were annealed for 2 hr at 1200°C in vacuo, which left them with a re-crystallized grain size of about 0.01 mm, and then electropolished. They were tested under dead-weight loading in an apparatus in which they could be surrounded by a furnace or cooling chamber, tests in practice being made at various temperatures between -196" and +350°C. For tension tests, cylindrical specimens were prepared in a similar manner and tested at room temperature under dead-weight loading. RESULTS (TORSION) Subductile State. The state described above as intermediate between brittle and ductile may be perhaps best defined by reference to torque/twist curves at various temperatures. These are grouped in Fig. 1. Below about -50°C the material was brittle, in the sense that it exhibited little plastic deformation under stress and fractured by cleavage along planes of maximum resolved tension, which in torsion produces the well-known helical type of fracture. The deformation is typified by the curves for -196" and -150°C in Fig. 1; it shows a slight but progressive deviation from linearity above a certain torque, here about 50 lb-in., until fracture occurs at about 95 lb-in. A feature to which it is desired specially to call attention is that under none of the loads did the specimens show significant creep.

Jan 1, 1964

By R. D. Nelson, F. E. Bowman

Evidence has been found for a (010)a?(111)B[102]a /,11[341]/B crystallographic relationship between the monoclinic a and B phases of plutonium during the a?B transformation. The results of an X-ray diffraction study, where [010] fiber textured a samples were used in the absence of suitable single crystals indicate that the (OIO)a planes become (111)B planes upon transformation under near-equilibrium conditions. The transformation strain along the fiber axis, which was the [010] direction, was measured dila-tomekically; the measured 8.5 pct expansion compares favorably with the 8.44 pct expansion in the in-terplanar spacing represented by the (010)a?(111)B relationship. From plots of the atom positions in each of the related planes, a correspondence was deduced between the [102]a, direction and the [341]B direction. Further analysis of the two lattice structures in the light of this relationship revealed a rotation about the [102] direction of 1 deg 43 min and a slight shearing in this same direction of about 30 min. THIS paper discusses the (B crystal structure of plutonium and the orientation relationship existing between the monoclinic a and B phases during the a?ß transformation. The kinetics of the a?ß and (3 — a transformations have received extensive consideration, and because of the crystallographic complexity of these phases, the question of the mechanisms by which these transformations occur is especially intriguing. Nelson and Shyne1 evaluated the existing experimental evidence and concluded, from the indirect evidence available, that both the ß ? a and a ? ß transformations occur by a martensitic process. Their data reveal the anisotropic nature of these transformations which suggests the existence of specific crystallographic relationships between the parent and product phases. In this paper, we are concerned with the confirmation of the existence of such a relationship resulting from the a ? ß transformation and the derivation of the crystallographic details necessary to specify it. EXPERIMENTAL RESULTS X-ray diffraction and dilatometric data were obtained from samples of a plutonium having a [010] fiber texture. These cylindrical specimens, approximately 1 cm in diam, were prepared by transforming the ß phase to a under the influence of a uniaxially applied compressive load.' The [0l0] direction is parallel to the direction of applied stress; it is also perpendicular to the (010) planes. This correspondence between the plane normal and the direction having the same indices is, in the monoclinic a plutonium structure, restricted solely to this (010)[010] combination. Such a specimen was mounted in an evacuated, elevated temperature specimen holder on an X-ray dif-fractometer so that the diffracting surface was perpendicular to the fiber axis. The a diffraction pattern, Fig. 1, taken at about 115ºC, revealed the predominance of the (020) reflection. This monoclinic, P 21/rn space group yields no (0k0) reflections when k is odd. The temperature was raised slowly to 160°C to effect the complete transformation to the phase; then it was lowered to 120°C so that a diffraction pattern of the ß could be obtained near the a = ß equilibrium temperature for direct comparison with the a at the same temperature. The (3 diffraction pattern, Fig. 2, obtained under these conditions showed a (222) reflection relatively much more intense than in the random pattern. The other reflections appearing with sig-

Jan 1, 1970

By A. L. Labbe, J. J. Donoso

Hard-won experience in the operation of smelting plants has pointed the way to the most efficient design and economical operation of a baghouse system for recovery of metallurgical fumes. This paper treats of the principles governing bag filtration and the factors most directly affecting bag life. Methods for temperature conditioning of smoke previous to filtering are described and the evolution of bag shaking mechanisms is brought up to date. THE history of the bag filter process, as applied to the recovery of metallurgical fumes, goes back to 1876, when the Lone Elms Works of Joplin, Missouri, erected a two-section baghouse for filtering fumes from Scotch Hearth lead smelting furnaces. By modern standards this installation was crude, but the basic operating principles remain essentially the same today. Great progress, however, has been made in the mechanization of the process by the use of devices for mechanically and automatically cleaning bags of adhering fumes, in the use of instruments for recording and controlling the variables affecting baghouse operation, and in the conditioning of the smoke previous to filtering. The principles governing bag filtration of fumes were investigated in 1929 by A. J. Seitz of American Smelting and Refining Co., and he arrived at the following conclusions: 1. Pressure on Bags at Constant Volume: The rate at which the pressure builds up in a bag with constant volume is directly proportional to the time, with the same kind of smoke and dust burden (fig. 1). 2. Pressure on Bags for Change in Volume: With equivalent smoke and dust burden, the bag pressure increases with the square of the increase in volume. The rapid increase in pressure is due to (1) increase in volume, (2) increase in amount of dust on the bag, and (3) more intense packing of the dust at higher velocity (fig. 2). 3. Effect of Intensive Filtering on Pressure: Since the pressure builds up directly as the square of the volume, with the same smoke and dust burden, it is necessary to shake the bags in that increased ratio, and vigorously, to keep the pores of the bag open and pressure down. This increases the wear on the bags and the dust losses. 4. Effect of Shaking on Dust Losses: The losses are in direct proportion to the frequency of shaking because the loss takes place immediately after shaking, before the bag seals itself. Tests show that with hand shaking the last 20 pct of the removable dust requires seven times more shaking per unit weight of dust than the first 80 pct. 5. Effect of Fineness of Dust on Losses: The fineness of the dust particle increases the loss in two ways: (1) When the bag is clean a greater percentage of it will pass through before the bag seals itself; (2) fine material penetrates farther into the bag pores, building up pressure faster and necessitating more shaking, thereby increasing the loss. The physical principle of operation of the bag filter is simply the separation of solids from a gaseous carrier through a porous medium, and is analogous to the filtration of solids from liquid carriers. Basically, the mechanics of the process are as follows: Fume-laden gases drawn from the operating fur-

Jan 1, 1951

By A. W. Demmler

RECENTLY, Chaudron,&apos; Montariol,2 and their co-workers published the results of their studies on zone-refined aluminum. They found their material to be capable of recrystallization at —50°C, but gave no data as to the percentage reduction or time required. Their material was found to be practically non-work hardening at room temperature, but after 96 pct cold work at a low temperature and storage in liquid nitrogen it was found to recrystallize to coarse grains in less than 3 hr at 20°C. Recently, a study was made of the room temperature recrystallization characteristics of zone-melted aluminum. An ingot 14 in. in length, with a 3hx3 in. cross section, was made in an extremely high purity graphite boat under an atmosphere of dried commercial argon. It was made by first passing the molten zone along the ingot of 99.99+ pct A1 15 times. At this point, the most impure 3 in. (the end toward which the eutectic forming impurities migrated) were replaced with more of the original starting material, and 15 more traverses were made. Each traverse of the zone along the ingot required approximately 3 hr. Three ingots were prepared in this identical fashion and the chemical analyses were made spec-trographically on two of these ingots, rather than on the one used in this investigation. The analyses were made at 1 in. intervals along the ingot, in duplicate. Over the purest 5 in. of the ingot, which were most important in this investigation, there was found an average composition of <0.00004 pct Cu, <0.0003 pct Fe, <0.0001 pct Si, and <0.0001 pct Mg. In addition, the following elements were not detected spectrographically even in the more impure end of the bar: manganese, zinc, nickel, chromium, titanium, vanadium, lead, tin, boron, beryllium, bismuth, gallium, zirconium, cadmium, antimony, cobalt, and molybdenum. The original ingot was given several cold reductions, with intermediate anneals in order to refine the grains. Owing to the extreme length resulting and the ease of deforming the material plastically, it was cut into eight equal lengths and identified as shown in Fig. 1, with the highest numbered section at the purer end (that enriched with peritectic formers). Section 6 was used in the exploratory work and was found to be of exceptionally high purity, giving more rapid rates of room temperature re crystallization than any previous aluminum studied at the Alcoa Research Laboratories. This fact suggested that the entire midsection of the ingot might be of very high purity. Accordingly, section 4 was chosen for the next study. A portion of it was rolled to cold reductions of 10, 25, 40, 60, 75, and 90 pct at room temperature, and the re-crystallization of each specimen was followed by X-ray pinhole transmission photographs. The other portion received the same treatment, except that both the specimens and the rolls were maintained at 160°F in the process of rolling. The latter ortion was retarded in its recrystallization as compared to the former, probably due to the stress relief effect of the warm rolling. Both of these portions of the fourth section were found to recrystallize at a considerably slower rate than did the sixth section.

Jan 1, 1957

By F. F. Craig

A series of both welter and gas puttern Hoods was made in the laboratory to study the oil recovery performances of .such operations. These tests were contlrrctt~tl on consolidated sandstone models, using oil. water, and gas. The model floods were scaled to reprotlrrce field performance under gas arid water five-spot injection. X-ray shadowgraphs permitted observation of the gross fluid movement within the models. A method was developed for applying the mobility ratio concept to water flooding and dispersed gas drives in a five-spot well pattern. The area1 sweep efficiency. tit breakthrough for dispersed gas drives is much higher than previorsly expected, Iying in the range of 50 to 100 per cent. A method is presented for predictitig the water-oil ratio performance of five-spot pattern water flood., in uniform sands. This method is verified experimentally for the cotidition of 120 free gas initially present and for va1ues of gas saturation normally encountered in fields following depletion operations. Prodrrction perfort?zut~cc for pattern gas injection is also predictable by this method. INTRODUCTION In field pattern hater flooding or dispersed gas injection operations, the displacing fluid (water or gas) is injected and oil is produced through wells which are, area-wise. small openings in a large container or rescrwir of oil. As a result, not all of the area between the injection and producing wells is necessarily contacted by the injected fluid by the time it first reaches the producing wells. The question arises in predicting oil recovery. as to what traction of the pattern area involved is contacted by either the injected water or gas due to the relative position of the injection and producing wells. This is the areal sweep efficiency. It is also desirable to know how well arrangement affects the oil production performance. A solution to this problem has been attempted by many means. Mathematical analysis¹,²,³, and electrolytic models&apos;, have been used to establish a breakthrough areal sweep efficiency of 73 per cent for a five-spot pattern in which the ability of the oil to flow ahead of the invading fluid is equal to the ability of the invading fluid to flow in the invaded zone. All of these studies simulate only one of many field conditions. Improved studies of areal sweep efficiency at breakthrough were made using the fluid mapper5, poten-tiometric models" and X-ray shadowgraph techniques. In these it was possible to study the effect of variations in mobility of the injected and displaced fluids, and so to cover a wide range of field conditions. The limitation of these studies is that, with these models, it was not possible to simulate the saturation gradient behind the flood front when oil is displaced by gas or water. In the most recent published technical paperS on the subject, a method was presented for predicting the oil recovery performance after breakthrough in a five-spot pattern water flood. The method involved correlations which were obtained experimentally using miscible fluids. One limitation of this work was that a saturation gradient, usually found in immiscible fluid displacement, was absent in these studies. Also the laboratory studies did not cover the situation of a water flood following oil recovery by depletion drive. as is the situation in most field water floods. The tests reported in this paper were made using oil. water, and gas, thus eliminating the simplifications of former studies. Also reported are laboratory studies on

Jan 1, 1956

By R. E. Carter, C. Wagner, F. D. Richardson

By means of inert markers of radio-platinum, it has been shown that cobalt metal oxidizes by out-ward diffusion of cobalt atoms through the oxide. Oxidation rates have been measured at various temperatures and oxygen pressures and have been found to agree with the rates calculated from the Wagner equation and the authors&apos; values for the diffusion coefficient of cobalt in the oxide. The distribution of radio-cobalt in growing oxide loyers has been accurately measured and found to be different from that predicted from the Wagner oxidation theory. Attempts have been made to measure the change of lattice parameter of the oxide with composition. SEVERAL investigators have shown that cobalt metal oxidizes according to the parabolic law,1-3 but no detailed study has been made of the oxidation mechanism. Cobaltous oxide has a metal-deficient lattice, but the defect concentration which is dependent on the oxygen pressure is only approximately known.&apos; From the similarities in the structures of "CoO" and "FeO" and the rate laws governing the oxidation of cobalt and iron, Gulbransen- as suggested that cobalt, like iron," oxidizes by diffusion of cobaltous ions through the oxide layer. To substantiate this hypothesis, he has attempted to measure the oxidation rate of cobalt as a function of the oxygen pressure but has been able to report only that the rate depends on a "small" power of the pressure. On the other hand, Preece," Valensi,&apos; and Arkharov&apos; all have suggested from indirect evidence that oxygen diffuses through the COO to the metal-oxide interface. The present authors, in a previous paper,&apos; have shown that the rate of diffusion of cobalt in cobaltous oxide is dependent on the oxygen pressure. In that investigation, they also found that cobaltous oxide disks made by complete oxidation of cobalt metal were porous at their centers (Fig. 5L, ref. 4). Both these facts strongly suggest that oxidation of the metal proceeds via outward diffusion of cations. In order to establish the mechanism unequivocally, oxidation experiments were made with inert radioactive platinum markers, and the dependence of oxidation rate on oxygen pressure was measured. In addition, an attempt was made to determine the form of the cation vacancy gradient, which the marker experiment showed must exist across a growing oxide layer. This was done by depositing radioactive Co on the surface of a cobalt disk and then measuring the tracer distribution across the oxide layer produced by partial oxidation of the metal. Finally, an X-ray examination was made in an attempt to find the expected change of lattice parameter of COO with oxygen pressure. Experimental The apparatus and materials used were substantially the same as those previously described by the authors.4 Marker Studies: The use of inert markers to follow oxidation reactions was first attempted by Pfeil" in 1929, and radioactive markers have recently been used by Davies et al.&apos; In the investigation reported here, the markers were applied as an (NH4)2PtCI6 slurry in several thin streaks across both faces of four disks of cobalt metal 1 mm thick and 14 mm in diameter. The disks were then oxidized almost to completion at 1200°C in pure oxygen. After oxidation, they were mounted and sectioned and auto-radiographs were taken to locate the markers. Oxidation Rate: The oxidation rate of cobalt was measured at 1148°C at oxygen pressures ranging from 0.0055 to 1.0 atm and at 1000°, 1148", and 1350°C under 1 atm of oxygen. The rate was deter-

Jan 1, 1956

By Paul A. Flinn, Jean-Marie Robert Genin

The MCssbauer effect was used to study the distribution of carbon in Fe-C alloys of high carbon content during room-temperature aging. In freshly formed rnartensite the carbon distribution is approximately random; carbon clustering occurs dun&apos;ng aging. In the retained austete the carbon atoms are isolated, suggesting an efiective repulsion; and no rearrangement during room-temperature aging is evident. The kinetics of the carbon clustering in martensite has been studied in detail at 0" . 10". and 20°C. The time and temperature dependence observed is sinzilar to that reported for a variety of other aging effects, such as resistance change, hardness increase, and recovery of internal friction. The stabilization of the martensite kransformation also appears to be related to the clustering effect. DESPITE extensive efforts since the early days of Reaumur, the mechanism which provides the strengthening of steel remains controversial in many cases for several reasons: 1) The structure of as-quenched martensite is not well-determined. 2) Experimental methods capable of distinguishing between various hardening mechanisms are not well-developed. 3) The temperature of formation of many low-alloy martensites is so high that the martensite formed during quenching may be already tempered to some extent before any observation. Among all the hardening phenomena, the most puzzling one occurs at room temperature, where no structural changes have been detected by the usual methods of X-ray diffraction or electron microscopy. However, a new and more sensitive technique became available with the discovery of the MBssbauer effect. This effect makes possible the detection of changes in the local environment of iron atoms in solid solution. It has been extensively used in the study of substitutional alloy systems, for example, Fe-Al,1 Fe-Si,2,3 Fe-Rh,4 and Fe-Ni.5 Making use of the possibility of obtaining new structural information, we undertook an investigation of the aging of high-carbon Fe-C martensite to follow the structural changes involved in the aging at room temperature. Preliminary results6 showed that a clustering of the carbon atoms occurs with time. A systematic study of the kinetics of the process showed a striking similarity to the kinetics of stabilization of the marten-sitic transformation, thus suggesting further investigation of the relationship. EXPERIMENTAL TECHNIQUE To eliminate difficulties with the aging of martensite prior to the first experimental measurements, we needed an alloy with an M, temperature not above room temperature. Other investigators7 were misled by results obtained on alloys which transformed above room temperature and underwent structural changes prior to the first Mossbauer measurements. Winchell and cohen8 dealt with this difficulty by using a third element, nickel, to depress the MS below room temperature. The presence of nickel did not seriously interfere with hardness or resistivity measurements, but it would complicate the interpretation of the Mossbauer data by increasing the variety of iron environments. We chose, therefore, to obtain the necessary lowering of the M, simply by increasing the carbon content. After the first quench to room temperature, our specimens are retained austenite, which we later quench into liquid nitrogen. The martensitic transformation takes place suddenly, so that the as-quenched condition of the samples is retained, since the temperature is low enough to prevent any carbon diffusion. A Massbauer spectrum at 77°K can be taken and analyzed; after an appropriate up-quenching to the aging temperature, a new Mossbauer measurement at 77°K can be made. Fig. 1 shows a typical cycle of experiments. The samples were foils 25 p thick of high-purity

Jan 1, 1969

By A. M. Gaudin, C. S. Chang

Adsorption was measured for barium ion and laurate radical, using radioactively marked agents, over wide range of concentrations. Laurate adsorbed in absence of barium fails to float. With barium, flotation-effective laurate coating needs not exceed 5 pct of monolayer. Barium adsorption then is several fold larger. No barium laurate coating is obtained. IN general, fatty acids or their alkali salts do not cause clean quartz to float. However, the presence of multivalent ions, such as the alkaline-earth metal ions and heavy-metal ions, can activate quartz and thus make it respond to soap flotation. The mechanism of activation and soap flotation of quartz has been studied.&apos;-&apos; The problem was attacked by making flotation tests rather than by careful adsorption measurements on suspensions of ground quartz in solutions containing the activator and the collector. Attempts have been made to determine the adsorption of barium ion and calcium ion on quartz. The results have only qualitative value as the analytical methods were not adequately precise. Artificial radioactivity and progress in radioactivity detection have introduced a new analytical tool, which can have a sensitivity several orders of magnitude greater than that of other methods."-" In the experimental work described in this paper the radioactive tracers, barium 140 and carbon 14, were employed. Lauric acid was synthesized, having a radioactive carbon atom and was used with Ba" to study the adsorption of barium and laurate ions from aqueous solution on ground quartz. Flotation tests, using the vacuum flotation technique,&apos; were run in conjunction with the adsorption experiments. The object of this investigation was to understand better the reaction mechanism of barium activation and soap flotation of quartz. Methods and Materials Quartz Sample Preparation: Lumps of hand-picked quartz, washed free of stains, were reduced in size to —20 mesh in laboratory crushers. The product was boiled in concentrated hydrochloric acid to remove the abraded iron. The cleaned product then was ground dry in a laboratory porcelain mill, using siliceous pebbles, to pass through a 200 mesh screen. The ground product was deslimed by sedimentation at 37 microns. This —200 mesh +400 mesh material was subjected again to boiling with concentrated hydrochloric acid, followed by washing with distilled water and further desliming. The cycle was repeated until no trace of iron could be detected in the wash liquor. During the final washing, the pH of the wash water was checked to insure the complete removal of the acid from the mineral. The quartz then was rinsed with conductivity water. The resulting product was dried in a drying oven and stored in mason jars. The impurities (spectrographic) were as follows: Al, 0.01 to 0.001 pct; Li, Mg, Mn, Na, each less than 0.001 pct; Fe and Cu not detected. The specific surface of the quartz sample was determined by the krypton gas adsorption method.&apos; The average of two measurements was 881 sq cm per g. The calculated specific surface for 37/74-micron quartz particles, using a surface factor of 1.96; is 900 sq cm per g. This is in good agreement with the measured value of 881 sq cm per g. Beta-Counting Method: The radioactive isotope of barium used in the experimental work was barium 140. It has a sufficiently long half-life, 12.8 days, emits high-energy beta particles (up to 1.0

Jan 1, 1953

By A. M. Gaudin, C. S. Chang

Adsorption was measured for barium ion and laurate radical, using radioactively marked agents, over wide range of concentrations. Laurate adsorbed in absence of barium fails to float. With barium, flotation-effective laurate coating needs not exceed 5 pct of monolayer. Barium adsorption then is several fold larger. No barium laurate coating is obtained. IN general, fatty acids or their alkali salts do not cause clean quartz to float. However, the presence of multivalent ions, such as the alkaline-earth metal ions and heavy-metal ions, can activate quartz and thus make it respond to soap flotation. The mechanism of activation and soap flotation of quartz has been studied.&apos;-&apos; The problem was attacked by making flotation tests rather than by careful adsorption measurements on suspensions of ground quartz in solutions containing the activator and the collector. Attempts have been made to determine the adsorption of barium ion and calcium ion on quartz. The results have only qualitative value as the analytical methods were not adequately precise. Artificial radioactivity and progress in radioactivity detection have introduced a new analytical tool, which can have a sensitivity several orders of magnitude greater than that of other methods."-" In the experimental work described in this paper the radioactive tracers, barium 140 and carbon 14, were employed. Lauric acid was synthesized, having a radioactive carbon atom and was used with Ba" to study the adsorption of barium and laurate ions from aqueous solution on ground quartz. Flotation tests, using the vacuum flotation technique,&apos; were run in conjunction with the adsorption experiments. The object of this investigation was to understand better the reaction mechanism of barium activation and soap flotation of quartz. Methods and Materials Quartz Sample Preparation: Lumps of hand-picked quartz, washed free of stains, were reduced in size to —20 mesh in laboratory crushers. The product was boiled in concentrated hydrochloric acid to remove the abraded iron. The cleaned product then was ground dry in a laboratory porcelain mill, using siliceous pebbles, to pass through a 200 mesh screen. The ground product was deslimed by sedimentation at 37 microns. This —200 mesh +400 mesh material was subjected again to boiling with concentrated hydrochloric acid, followed by washing with distilled water and further desliming. The cycle was repeated until no trace of iron could be detected in the wash liquor. During the final washing, the pH of the wash water was checked to insure the complete removal of the acid from the mineral. The quartz then was rinsed with conductivity water. The resulting product was dried in a drying oven and stored in mason jars. The impurities (spectrographic) were as follows: Al, 0.01 to 0.001 pct; Li, Mg, Mn, Na, each less than 0.001 pct; Fe and Cu not detected. The specific surface of the quartz sample was determined by the krypton gas adsorption method.&apos; The average of two measurements was 881 sq cm per g. The calculated specific surface for 37/74-micron quartz particles, using a surface factor of 1.96; is 900 sq cm per g. This is in good agreement with the measured value of 881 sq cm per g. Beta-Counting Method: The radioactive isotope of barium used in the experimental work was barium 140. It has a sufficiently long half-life, 12.8 days, emits high-energy beta particles (up to 1.0

Jan 1, 1953

By J. G. Y. Chow, S. B. McRickard

The tensi1e properties of Ferrovac iron have been studied from 4° to 300°K. The stress required for macroscopic yielding was found to he constant below approximately 50°K. The effect of mechanical twinning on this low -temperature stress plateau was investigated. The onset of twinning occurs in this iron between 130° and 150°K and depending on its previous thermal history the twinning-stress curue may drop below or remain above the vield-stress curves as the temperature is lowered. Twinning has been shown to initiate slip in quenclzed iron at low temperatures. In no instances, however, did the onset of twinning alter the continuity of the yield stress -tempwature curve. Our data shows that carbon inhibits twinning and slip at low tem-peratures. This observation nay be used to explain the ductile-to-brittle transition in iron. The effect of fast neutron irradiation on yielding and embrittlement in iron and Fe-C alloys is offered as supporting evidence for this viewpoint. THE mode of yielding in iron at low temperatures was studied in an attempt to find an expression based on a single mechanism to describe the thermal dependence of the yield stress of iron. There are two types of inflections observed in the variation of the yield stress with temperature in iron and Fe-C alloys. The first is associated with ductile behavior and consists of a region extending 50" to 100°K above absolute zero in which the yield stress is independent of temperature. The second is observed in more brittle materials such as Fe-C alloys and irradiated iron and consists of an abrupt discontinuity in the yield curve as the temperature is lowered through a ductile-to-brittle transition point. The temperature dependence of the yield stress for iron with four grain diameters as found in this study is shown in Fig. 1. To varying degrees all the curves appear to flatten or approach an asymptotic value as the temperature is lowered below 50°K. Several other investigators1,2 have observed a plateau in the yield stress of iron and steel at low temperatures and in 1956 Louat3 presented a theory which contained an explanation for this behavior. In a subsequent exchange with Erickson and Low4&apos;5 who attributed the plateau to the onset of mechanical twinning Louat8 showed that twinning first occurs in iron and steel tested in tension at temperatures as high as 140°K which is well above the observed plateau in yield stress. Furthermore he pointed out that both twinning and slip are basically dislocation processes and that with modified parameters his original theory still applied when deformation is initiated by twinning. Variables which affect the ductile-to-brittle transition in iron are test temperature, strain rate, composition and grain size.7 LOW,8 Hahn et al.,9 and Hull10 have provided evidence which links brittle fracture at a given temperature with the specimen grain size and the onset of twinning. In fact, Hull equates the brittle fracture stress to the twinning stress. On the other hand brittle fracture has been observed in the absence of twinning and priestnerl1 has given a fracture criterion which is valid whether or not fracture is preceded by extensive twinning. The data presented here clarify the role of twinning in the low-temperature deformation of iron. Strong evidence is given that the amount and distribution of interstitial impurities such as carbon are of

Jan 1, 1965

By M. E. Wadsworth, J. R. Lewis, J. M. Quets

Samples of snythetic magnetite were reduced in hydrogen at various partial pressures and temperatures. The reaction mas found to be surface controlled and directly proportional to hydrogen partial pressure over the temperature range studied (400° to 1000°C). A transition in the mechanism occurred at approxirnately 590°C. This has been attributed to a change in the slow step of the reduction reaction resulting from the presence of stable wüstite at higher temperatures. Below 590°C the heat of activation for the reduction was found to be 14,700 cal per mole and it was 3,200 cal per mole above 590°C. THE reduction of the oxides of iron has been a subject of study and interest for many years. Edstrom1 has reviewed the work up to 1953 and his findings provide much basic information concerning details of the reduction of hematite (Fe2O3 ) and magnetite (Fe3O4) with both H2 and CO. He concluded that below 600°C the reduction of both hematite and magnetite was essentially identical, since the rate was controlled by a surface reaction at a magnetite gas interface and the iron formed was very porous. The decrease in the reduction rate for both hematite and magnetite immediately above 600°C was attributed to the formation of a stable wüstite phase across which diffusion was very slow. The wide difference in reduction kinetics for hematite and magnetite above 600°C was explained in terms of the character of the wüstite formed. The rate of magnetite reduction increased slowly with temperature beyond the minimum immediately above 600°C and rates equivalent to those observed at 550°C were not obtained until the temperature was increased beyond 850oC. Edstrom and Bitsianes2 studied the solid-state reduction of magnetite, the reaction of which can be written (4x-3)Fe + Fe3O4—4 FexO [1] where x is between 0.83 and 0.95. The rate was found to be controlled by the kinetics of transport of iron ions through the wüstite phase. Bogdandy and Riecke3 studied the kinetics of reduction of small grains of iron oxide in hydrogen and qualitatively attributed the slow step in the reduction process to the diffusion of hydrogen and water vapor through pores. McKewan4 has analysed the data of Joseph,5 Stalhane and Malmburg,6 and Lewis7 and has demonstrated that the kinetics of reduction of both hematite and magnetite are controlled by surface reactions and also that the variation in surface area during reduction must be accounted for. McKewan was able to correlate the reduction data by the equation rodo[1-(1-R)1/3] = Kt [2] where ro is the initial particle radius, do is the density of the iron oxide, R is the fraction reduced at time t, and K is a rate constant. The applicability of Eq. [2] for temperatures above 600°C where a stable wüstite phase is present, indicates the slow step in the over-all kinetics does not result from diffusion unless diffusion occurs laterally along the oxide metal interface or through a wüstite layer of constant thickness. Diffusional control through a layer of wüstite is unlikely, however, in view of the pressure effects demonstrated by Tenenbaum and Joseph,&apos; Diepschlag,9 McKewan,10 and the results of the present study. McKewan has demonstrated a linear rate dependence on the hydrogen partial pressure over the temperature range 400" to 1050°C for the reduction of hematite.

Jan 1, 1961

By Joseph L. Gillson

BRAZIL has had an industry based on ocean beach deposits of heavy minerals containing monazite, zircon, rutile, and ilmenite for well over 40 years, but except at the very earliest period, prior to 1906, and again during World War 11, has this industry been at all comparable in size with similar operations in other countries. Limiting factors have been neither a lack of reserves nor lack of markets (except for zircon). Although poor local transportation and shipping facilities have handicapped the development in Brazil, these conditions were perhaps equally bad (when mining operations started) in the Indian State of Travancore, and in New South Wales and Queensland, Australia, in which states the principal production of beach deposits of heavy minerals has occurred. The outstanding restraints on the Brazilian industry have been the lower quality of the Brazilian minerals, the relative small size of individual deposits that were known until recently, the lack of interest of Brazilian investors in mining ventures, and the unfavorable climate for investment of foreign capital under Brazilian mining law. The lower quality of the minerals is indicated by the fact that the Brazilian monazite carries only 5 to 6 pct Tho2*, and the ilmenite 561/2 pct TiO2, whereas the corresponding Travancore minerals carry 9 pct Tho, and 60 pct TiO, respectively. The Brazilian zircon is a dirty brown color (which can be removed readily) as compared with the gleaming whiteness of the Australian zircon. An inadequate market for the abundant zircon that will be available in any operation in Brazil is certainly a heavy restraint, since otherwise it could be an important byproduct. The oxide of zirconia, baddeleyite, that has come from Brazil is from other sources.&apos; Since the Brazilian beach sands carry only a little rutile, that mineral has not been available as a valuable byproduct to help finance the operations. Substantial tonnages of rutile have been exported from Brazil. The sources of this mineral are stream placers and residual deposits over gneisses in the States of Goyaz, Minas Geraes, Ceara, etc. (Leonardos,&apos; and Chambers". With these handicaps, Brazilian production from beach sands has been marginal, and there has been only one consistent producer. This is a company, originally French, which was called Companie de Franco-BrazilliCne, but, with the downfall of France in 1940, became Brazilian under the name Monazita e Ilmenita do Brasil ("Mibra"). This company has operated several deposits in the vicinity of Guara-pary, in the State of Espirito Santo. Its office and plant has been at Guarapary. Recently a company called, "Fomil" (Fomento Monazita-Ilmenita) started operations. This company was organized by the Foote Mineral Co. of Philadelphia, and such share as a foreign company can hold under Brazilian law has now been acquired by the Lindsay Light and Chemical Co. of Chicago. When the writer went to Brazil in the fall of 1940, he found that no general survey of the beaches had been made except for a thorough study of part of the area by Abreu.4 The paper by Miranda6 had not then been written. The federal Geological Survey and Department of Mines knew only of the existence of the deposits in Espirito Santo south of Vitoria, and had a hazy idea that others might be found north of Vitoria. One deposit in Bala was known in Rio, but the larger one at Guaratiba was not known, although a Frenchman had prospected

Jan 1, 1951

By Joseph L. Gillson

BRAZIL has had an industry based on ocean beach deposits of heavy minerals containing monazite, zircon, rutile, and ilmenite for well over 40 years, but except at the very earliest period, prior to 1906, and again during World War 11, has this industry been at all comparable in size with similar operations in other countries. Limiting factors have been neither a lack of reserves nor lack of markets (except for zircon). Although poor local transportation and shipping facilities have handicapped the development in Brazil, these conditions were perhaps equally bad (when mining operations started) in the Indian State of Travancore, and in New South Wales and Queensland, Australia, in which states the principal production of beach deposits of heavy minerals has occurred. The outstanding restraints on the Brazilian industry have been the lower quality of the Brazilian minerals, the relative small size of individual deposits that were known until recently, the lack of interest of Brazilian investors in mining ventures, and the unfavorable climate for investment of foreign capital under Brazilian mining law. The lower quality of the minerals is indicated by the fact that the Brazilian monazite carries only 5 to 6 pct Tho2*, and the ilmenite 561/2 pct TiO2, whereas the corresponding Travancore minerals carry 9 pct Tho, and 60 pct TiO, respectively. The Brazilian zircon is a dirty brown color (which can be removed readily) as compared with the gleaming whiteness of the Australian zircon. An inadequate market for the abundant zircon that will be available in any operation in Brazil is certainly a heavy restraint, since otherwise it could be an important byproduct. The oxide of zirconia, baddeleyite, that has come from Brazil is from other sources.&apos; Since the Brazilian beach sands carry only a little rutile, that mineral has not been available as a valuable byproduct to help finance the operations. Substantial tonnages of rutile have been exported from Brazil. The sources of this mineral are stream placers and residual deposits over gneisses in the States of Goyaz, Minas Geraes, Ceara, etc. (Leonardos,&apos; and Chambers". With these handicaps, Brazilian production from beach sands has been marginal, and there has been only one consistent producer. This is a company, originally French, which was called Companie de Franco-BrazilliCne, but, with the downfall of France in 1940, became Brazilian under the name Monazita e Ilmenita do Brasil ("Mibra"). This company has operated several deposits in the vicinity of Guara-pary, in the State of Espirito Santo. Its office and plant has been at Guarapary. Recently a company called, "Fomil" (Fomento Monazita-Ilmenita) started operations. This company was organized by the Foote Mineral Co. of Philadelphia, and such share as a foreign company can hold under Brazilian law has now been acquired by the Lindsay Light and Chemical Co. of Chicago. When the writer went to Brazil in the fall of 1940, he found that no general survey of the beaches had been made except for a thorough study of part of the area by Abreu.4 The paper by Miranda6 had not then been written. The federal Geological Survey and Department of Mines knew only of the existence of the deposits in Espirito Santo south of Vitoria, and had a hazy idea that others might be found north of Vitoria. One deposit in Bala was known in Rio, but the larger one at Guaratiba was not known, although a Frenchman had prospected

Jan 1, 1951

By B. L. Averbach, Morris Cohen, S. A. Kulin

The martensitic transformation can be initiated by elastic stresses at temperatures above M. in a steel containing 20 pct Ni and 0.5 pct C. Shear strains and normal tensile strains acting on a potential habit plane promote the transformation but compressive strains oppose it. THE strain sensitivity of the martensitic transformation has long been recognized. It is now well known that martensite formation can be induced by plastic deformation at temperatures below, and not too far above, the M, point.&apos; However, the exact role of elastic vs. plastic strains and of the concomitant stresses has proved to be a very elusive matter. Many investigators2-&apos; of the steel hardening reaction have made use of the stresses resulting from volume changes to account for such observations as the existence of retained austenite and its variation across the section of a bar, the change in the amount of retained austenite with quenching rate, and the self-stopping nature of the transformation when the cooling is stopped. The effect of applied strain as an independent variable has been studied in 70 pct Fe-30 pct Ni alloys by Scheil7 and McReynolds.8 Some data are also available for lithium and Li-Mg alloys,9 Cu-Zn,10 Cu-Sn and Cu-A1 alloys," and aus-tenitic stainless steels."-" It has been found that martensite formation can be induced isothermally, even at temperatures above M,, by mechanical deformation of the parent phase. The competitive nature of plastic yielding by slip and by the martensitic reaction has been depicted by Scheil.7 Basically, Scheil postulated that: 1—at temperatures not too far above M, (where austenite is less stable than martensite), a critical resolved shear stress (within the elastic range) is required to promote the transformation to martensite; 2—at and below M,, the austenite lattice becomes mechanically, as well as thermodynamically, unstable and shears over spontaneously into martensite without the application of external stress; and 3—at temperatures sufficiently far above M8, the critical resolved shear stress for martensite formation increases to a level above that required for slip, and plastic flow then supersedes the transformation when external stress is applied. Scheil&apos;s concepts were tested by McReyno1ds8 ho found no change in the elastic moduli (measured both statically and dynamically) of 71 pct Fe-29 pct Ni alloys in the vicinity of the M, temperature. Since the moduli did not approach zero or become negative on cooling to M,, it was concluded that the austenite lattice does not become mechanically unstable at M2, as postulated by Scheil. McReynolds also reported that M, is not raised by elastic stresses. Accordingly, plastic deformation was considered to stimulate the transformation by generating martensite nuclei in the distorted regions of the parent phase. The above issues with regard to the role of applied stress require clarification, if a basic understanding of the martensitic transformation is to be obtained. For example, in the reaction-path theory,&apos;"," it is postulated that strain embryos exist in the austenite that provide part of the activation energy for the nucleation process. These embryos are visualized to be regions of localized strain in which the atoms in the austenite lattice are displaced part way along the path to their ultimate positions in the martensite. Consequently, it would

Jan 1, 1953