By R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-C and Fe-Ni solid-solution alloys has been investigated at 25°C. It is found that the rate of solid-solution strengthening is dependent upon the strain at which the yield stress is measured, the macroyield stress being much more concentration-dependent than the microyield stress. In fact the addition of nickel does not lead to any increase in the microyield stress of iron. The primary effect of increasing the carbon or nickel content is to increase the slope of the stress-strain curve in the microyield region; this effect has been correlated, by means of transmission electron microscopy, with a decreased ability of the dislocations to cross-slip. It is concluded that the Mott-Nabarro theory is a good description of true solid-solution hardening in these and other iron-base alloys. A.LL theories of the solid-solution strengthening1-4 indicate that the flow stress of an alloy increases both with solute concentration and "misfit" between the solvent and solute atoms. The functional relationship between strength, solute concentration, C, and misfit depends upon the particular theory. Mott and Nabarro1,2 and Schoeck and Seeger3 both predict a linear increase in strength with concentration, while Fleischer4 indicates that the strength should be proportional to C1/2; there are in the literature experimental observations to support both these compositional dependencies.1'8 The experimental evidence used to support the theories is the change in macroscopic yield stress (strain, e, = 10-3) with composition. However, recent investigations have revealed that solid-solution strengthening in a Cu-Al single crystals7 and in Fe-V polycrystal-line" alloys depends upon the strain at which the flow stress is measured; a flow stress in the microplastic range (e = 10-6 to 10-5) is much less concentration-dependent than the macroyield stress. Since the theories of solid-solution strengthening are concerned in particular with the stress to move a dislocation in a dislocation-free matrix, they should only be compared with microyield-stress data; it will be shown that in a material deforming homogeneously the microyield stress (e = 10-6) is approximately the stress to move through the matrix those dislocations which have been nucleated by stress concentrations such as particles or grain boundary ledges.9-11 In contrast, the macro-yield stress is more complex in that it is affected by several phenomena: dislocation multiplication, dislocation interactions, and the ease of propagating slip across grain boundaries. For example, it is experimentally observed that when long-range order12'13 or solute effects10 restrict cross alip the grain boundary

Jan 1, 1967

By Gerhard Derge

METALLURGISTS have used borax as a fluxing agent traditionally, but until recently elemental boron has played an insignificant role as an alloying element. Neither the metal nor its compounds have been regarded as important metallurgical materials and there is a surprising lack of knowledge concerning their metallurgical behavior. The new applications to steelmaking of both boron and borates, which arose in part from wartime incentives and restrictions, have been seriously handicapped by this lack of data. For example, rasorite, a naturally occurring sodium borate, has been shown to be an effective substitute for aluminum as a ladle deoxidizer in rimming steels.1 Likewise, the effectiveness of boron as an alloying agent has been demonstrated, 2,3 giving deep hardening when used in restricted amounts. The exploitation of both of these uses has been retarded by the difficulty of attaining suitable metallurgical control. Recognizing that the most important information required was a knowledge of the equilibrium between boron and oxygen dissolved in liquid iron, Gurry4 calculated this relation from the best thermal data available. However, estimates of the entropy of melting of boron, the activity coefficient of boron in liquid iron and the activity coefficient of B203 in slag were involved, and experimental work on this problem was obviously desirable. The experiments to be described were planned to establish the boron-oxygen relations in liquid iron and to demonstrate at the same time the ferroborate slag compositions in equilibrium with various amounts of oxygen in liquid iron. Accordingly, slags containing varying proportions of iron and boron oxides were held in contact with molten iron, and samples of both slag and metal were analyzed. The limitations upon the accuracy of the data will be considered, but in a practical sense the oxygen levels that can be attained in iron by iron borate slags, and the amounts of boron in iron at these oxygen levels were established. EXPERIMENTAL PROCEDURE No entirely suitable refractory was found for the mixtures of iron oxide and boron oxide used as slags. Crucibles of silica, magnesia, Ramix, beryllia, and zirconia were all tried unsuccessfully. The most satisfactory method discovered for handling them was the rotating-crucible technique, which creates a parabolic crucible of liquid iron 5,6 Even this was not entirely successful, for at steelmaking temperatures (1600°C.) the slags had such a low surface tension that they crept up to the refractory and slowly dissolved it. These difficulties made it impossible to maintain a constant slag composition for an unlimited period of time. However, by using the rotating

Jan 1, 1946

By R. A. Bergman, C. J. B. Fincham

THERMODYNAMIC properties of many high-temperature systems containing sulfur, such as slags, metal sulfides, and solutions of sulfur in liquid metals, have been studied by means of equilibration with known gas mixtures.'" This method presupposes a complete and accurate knowledge of the thermodynamic data for all possible components of the gas phase at high temperatures. However, a survey of the data available up to 1952 on the thermodynamics of gaseous sulfur species and compounds, by Richardson and Jeffes,' showed that there was considerable uncertainty in the values of the free energies of formation of S, SO, HS, and CS. In many cases, this uncertainty made it impossible to decide whether or not these species would form a significant proportion of the sulfur present in the gas phase in any given system. After the review by Richardson and Jeffes had been published, St. Pierre and Chipman6 measured, by an indirect method, the free energy of formation of SO. This also enabled a clear choice to be made among the three possible spectroscopic values for the dissociation energy of S2 into atoms10 thereby determining the free energy of formation of S from S2, and fixing the free energy of formation of HS more accurately" The main purpose of the present investigation was to measure the free energy of formation of CS, which was still in considerable doubt. For example, at 1600°C, it could be estimated to be +6 +25 kcal per mole,* most of the uncertainty being in the * Based on the dissociation energles of CS6 and S2,5 the heat of sublimation of graphite, and, the assumption that the entropy of formation of CS is the same as that of CO. value of the dissociation energy." A secondary purpose of the investigation was to determine more accurately the equilibrium sulfur pressures over dilute solutions of sulfur in carbon-saturated liquid iron. General Method Dilute solutions of sulfur in liquid iron, saturated with carbon, were brought to equilibrium at 1600" and 1800°C, with known gas mixtures consisting, initially, of A and CS2. After equilibrium had been reached, the melts were quenched and analyzed for sulfur. In the high temperature region of the furnace, an equilibrium was set up between the various possible sulfur species and compounds in the gas phase; namely, CS2, CS, S2, and S. (It can be calculated that the amounts of S6 and S, are negligible at these temperatures:) Morris and Bueh17 and Kitchener, Bockris, and Libermana had previously studied the corresponding

Jan 1, 1958

By R. Priestner, R. F. Krause

Solid, cylindrical crystals of a iron have been fractured at 10°K by the simultaneous application of tension and torsion stresses. Thus, a complex distribution of normal (sN) and shear (ss) stresses existed in a cleavage plane at fracture. In every crystal the clearage-plane normal was inclined to the specimen axis, so that a unique point, M*, in the operative cleavage plane was defined where the quantities sn and s2 N + s2 S) were maximized. It is shown that the maxirrzum resolved normal stress on the cleavage plane at fracture decreased as the resolved shear stress in the cleavage plane at M* increased. Thus, a normal stress la?*! for fracture was not satisfied. A fracture law which takes shear stress into account. and which predicts that (s2 N +s2S) should be constant, is to be preferred. However, the data is best represented by a linear dependence of sN on sS, sS which 110 physical significance can be attached. It is suggested that the fracture-nucleating -mechanism is a short-range one. A critical stress law has not yet been unequivocally established for the propagation of cracks in metals. Measurements of the tensile fracture stresses of variously oriented zinc single crystals1 failed to establish the normal stress law expressed by In Eq. [1], sN is the fracture stress, P, resolved normal to the fracture plane, and 0 is the angle between the fracture -plane normal and the stress axis. Similarly, a comprehensive investigation failed to verify the normal stress law for the tensile fracture of a-iron single crystals.' However, a subsequent investigation,3 using iron from the same ingot, presented fracture data which obeyed the normal stress law. It has been shown previously4,5 that the Griffith criterion for fracture6 does not predict such a normal stress law. This result is of particular significance in considering the fracture of metals, such as zinc and iron, which may fail by cleavage. In these metals fracture propagates in a well-defined "cleavage" plane, whether or not an applied stress is normal to it. When the cleavage-plane normal deviates from the direction of application of a uniaxial stress, for example, the crack propagates under the combined action of normal (sN) and shear (ss) stresses. When the presence of a resolved shear stress in the crack plane is taken into account, the Griffith criterion is expressed by4

Jan 1, 1967

By Shiro Ban-ya, John Chipman

Using the same experimental method previously described, the activity of sulfur in a number of quaternary and more complex liquid iron alloys at 1550oC is determined. A "cross-product term zj.zk is determined for each of the quaternary alloys to take account of the mutual effects of the combinalion on the indi-vidual contributions to In 5 The interactiotl coefjicienls delermined for ternary solutions and cross-pvoducl coefficierlts from the quaternary systems are used to estimate the activity coefficient of sulfur in more complex alloys. OUR recent papers 1,2 have described new determinations of the activity of sulfur in Fe-S binary and Fe-S-j ternary solutions, but the practical applications of these data require the estimation of activity of sulfur in more complex systems. Previously, Sherman and chipman3 devised an approximate method for calculating the activity of sulfur in complex systems by summing the contributions to the logarithm of the activity coefficient of each element in the alloy. This procedure is more successful, as one of us has pointed out,4 when the concentration variable is taken as zs = ns/(nFe — nS t CLJ~ nj) rather than the conventional atom fraction x~ = nS/(nF, + nS + Enj). In the former definition, which is based on analogy to interstitial solutions, the value assigned to uj is normally +1 for metallic and -1 for nonmetallic elements." In addition, however, the effects of mutual interaction between alloying elements must be considered for the accurate estimation of the activity of sulfur in more complex systems. The purpose of this investigation has been to devise a more reliable method for estimating the activity coefficient of sulfur in nmIticomponent iron alloys. The measurements were carried out on some quaternary systems Fe-S-j-k for combinations of silicon, chromium, nickel, cobalt, molybdenum, and tungsten. Manganese was not included since the experimental method has been found unsatisfactory for volatile, sulfide-forming elements. The experimental method was the same in every detail as described previously. 1,2 The concentrations of sulfur, silicon, chromium, and copper in the quenched metals were determined by chemical analysis but those of nickel, cobalt, molybdenum, and tungsten were calculated from charged amounts. Iron sulfide was included in the charges in amounts estimated to furnish approximately the final sulfur content. CALCULATION W2 have shown2 that when zs and zj are the concentration variables in a ternary Fe-S-j solution the logarithm of the activity coefficient S = a~/zg is a linear function of the variables as and aj defined as follows:

Jan 1, 1970

By Earl G. Alexander, W. R. Runyan

The nature of silicon growths which form on amorphous silicon dioxide during epitaxial deposition in unmasked areas was investigated. Octahedral silicon crystals nucleate and grow on the oxide at pinholes, adjacent to foreign matter, and probably at oxygen-deficient sites. Generation of these oxygen-deficient sites on the oxide surface is shown to be thermody-namically favorable under usual deposition conditions. The conditions which affect saturation (SiCl4 concentration, flow rate, temperature) determine the number of sites on which silicon will nucleate and grow. Reaction product HCl is likely responsible for suppressing silicon growths on the oxide near exposed areas of silicon. Evidence is given that the oxide-silicon interaction occurs in hydrogen only and involves water as a transport agent. SINCE shortly after the first epitaxial layers of silicon and germanium were grown over large areas, efforts have been underway to grow selectively on specified portions of the surface. Such selective growth should be particularly applicable to monolithic integrated circuits. Usually the approach has been to use a mask to delineate the desired area,'-7 but the VLS methoda can also be used, and direct programmed atomic beam deposition has been suggested.9 The masking techniques may embody two forms: in one the mask is a material which can later be removed along with any growths attached to it; in the other, attempts are made to prevent growth on the mask, so that over a whole slice the only deposition that will occur is in the unmasked regions. The present work is concerned with only the latter case, and specifically with silicon. Joyce and Baldrey1 suggested the use of thermally grown silicon dioxide as a mask material and showed that for the proper choice of operating conditions (total flow, SiCl4 concentration, total deposition time, and temperature) spurious growth could be minimized and that if the deposition times were not too large, and the criteria not too stringent, a usable process occurred. Later Schnable et al 4 observed that after extended deposition times, during which most of the silicon dioxide became covered with growth, there was always a band of oxide around the exposed silicon area that was quite free of spurious silicon crystallites. This latter observation is particularly intriguing since it extends the hope that with proper precautions masking can be much more versatile than it presently is. EXPERIMENTAL PROCEDURE Silicon substrates oriented to within 1.5 deg of a (111) plane were prepared by etch polishing lapped

Jan 1, 1967

By E. N. Silverman

Mixtures of' MnS, ZFeO-SiO,, ZMnO.SiO, FeO, and MnO were prepared synthetically and used to study the planes ZFeO. Si0,-ZMnO.SiO,-MnS, FeO-MnO-MnS, and Fe0-MnO.Si0,-MnS in the quaternary system. Because the oxides and silicates studied flux MnS, inclusions in this system are partly liquid during rolling. Also, oxygen can modify subsurface inclusions through the reaction MnS + FeO—FeS + MnO during the soaking of ingots and the reheating of blooms and billets. NONMETALLIC inclusions in steel have long been a subject of study and conjecture because the properties of many steels are known to be affected by the the kind and amount of inclusions present. In free-machining steels, the type of inclusion present has a direct bearing on their machinability; in other steels, cleanliness is important and metallurgists direct their efforts at reducing the amount of non-metallic inclusions. Thus, the accumulation of knowledge about the formation and behavior of inclusions during all stages of steelmaking and processing should aid in improving the quality of steels and decreasing the production costs resulting from rejections. Previous studies of inclusions have contributed greatly to our understanding. The investigators have generally examined inclusions in finished steel. Boulger, Moorehead, and Garvey1 found that in Bessemer steels, low silicon contents results in globular sulfide inclusions with attendant high machin- ability ratings. Van vlack2 also found that low silicon contents favor inclusion morphology that contributes to high machinability ratings. Boquist and Stoll* found that silicon content affected sulfide inclusions and machinability of blooms, billets and bars more than did the finishing temperature in the range between 1775° and 2075°F. Carney and Rudolphy3 studied the distribution of sulfur, manganese, silicon, and carbon in a commercial ingot of resulfur-ized steel and found that silicon was concentrated near the bottom. This helped to explain why bottom cuts had poorer machinability. Klinger and Koch4 developed techniques for extracting inclusions from steel, and the technique devised by Gurry, Chris-takos, and stricker5 for extracting carbides can also be adapted to the study of inclusions. A different approach to the study of inclusions in steel consists of synthesizing the constituents that form inclusions and determining the phase eauilibria in the system that contains the constituents. The resulting phase diagrams can then be used to determine the effect of the various constituents upon each other. In this way, it becomes possible to under-

Jan 1, 1962

By B. R. Coil, C. A. Ross

NEW demands for underground power in the Miami mine of the Miami Copper Co., Miami, Ariz. has brought about expansion of the distribution system for both ac and dc power. Progress in mining equipment and the normal changes in the mine were responsible for this increased demand. Early power requirements were for pumping and haulage. A 440 v ac power line down No. 5 shaft took care of a small pumping load and shaft station lighting, 275 v dc power was generated by motor generator sets on the surface, with a churn drill hole from surface to the 570 haulage level serving as a cableway. Electric lights were installed where power was available, and thus were confined to the haulage level and shaft stations. All industrial power in the Miami area is 25-cycle, which dates back to the hydroelectric generator installation at Roosevelt Dam in 1908-10. The Problem The main haulage level was moved to the 720 level and later, to the 1000 level, requiring a longer feeder line with the resultant voltage drop. Also, as mining progressed to the east, the churn drill hole for the power cable would have been subjected to subsidence cracks. The first extension in the use of electricity was in electric blasting. About 1935 the mine went to electric blasting, using the dc haulage current. Bringing electric current to the working levels of the mine for blasting greatly expanded the use of electric lights. Lights were used in tool rooms, powder and cap magazines, stairways, and other semi-permanent installations. Like all mines, Miami Copper began to study and experiment with mechanical mucking and transportation of ore by slushers, shakers, and belts during the late 1930's and early 1940's. At the beginning of the program, power was supplied from the haulage level 275 v dc system. Later it became necessary to run a cable, carrying 440 v ac power, down the No. 7 ventilation shaft. The increased use of power came about gradually, and many new problems were added, not the least being the introduction of switch boards and power cables into the working areas of the mine, where drifts and crosscuts take weight, and require repairs. The 25-cycle current presented special problems, in that 25-cycle transformers are twice as large and about 2V2 times as heavy as 60-cycle transformers of the same power output. The 25-cycle transformers were considered too large for installation in the mining areas. In 1947 the distribution system was revised and standards were adopted, governed by the following

Jan 1, 1952

By Herbert H. Kellogg

RECENTLY the long-chain primary amines have been used extensively for the flotation of silicate minerals. The use of amines to float sulphide minerals has been investigated by several authors1-5,18 but most of this work has been done with the short-chain (less than six carbon atoms) primary amine compounds or the more expensive secondary, tertiary and quaternary amines. Perhaps the fact that the long-chain amines are good collectors for the common gangue minerals has led investigators to omit them from consideration as collectors for the selective flotation of metallic sulphides. The work reported in this paper was designed to investigate the use of a typical long-chain amine salt, lauryl amine hydrochloride, as a collector for the flotation of galena-sphalerite ores. The results show that lauryl amine hydrochloride (LAmHCI), when used in small amounts, is a good collector for the selective flotation of sphalerite and galena from the common gangue minerals. The differential flotation of sphalerite from galena was not accomplished but the amine flotation of sphalerite after the standard xanthate flotation of galena is possible. The experimental work reported herein is not complete enough to be able to say whether amine flotation of lead-zinc ores would prove superior to xanthate flotation, or whether the method is even applicable to a more complex ore than the one used for this work. However, the apparent reagent costs for the flotation operations described in this paper seem to be less than for xanthate flotation. This fact alone should be sufficient to encourage the millman to investigate the use of these amine reagents, especially as these reagents are available on a commercial scale at a reasonable price. This paper has as its secondary purposes to illustrate how contact-angle measurements have aided in this investigation, and to bring forward some evidence concerning the mechanism of the collecting action of primary amines. CONTACT-ANGLE TESTS The contact-angle measurements were made by the method described by del Giudice6 and used in recent work by Taggart and his collaborators.7-9 The mineral specimens for the contact-angle tests were carefully chosen, to avoid cracks and inclusions of other minerals. All specimens were mounted in "transoptic" plastic mounts and the surfaces were cleaned by polishing with levigated alumina on a cloth-covered glass polishing wheel. Distilled water was used on the lap during the polishing and at all subsequent steps in the contact-angle tests. The mounted mineral specimens were handled with glass forceps and special care was exercised to prevent exposure of the dean surface to air or any other source of contamination.

Jan 1, 1945

By D. C. Hilty, W. Crafts

The solubility of oxygen in iron containing aluminum has been determined at 1550°, 1600°, and 1650°C and found to be much higher than predicted from theoretical considerations, possibly due to equilibria with an iron-aluminum spinel phase rather than pure AI,O.. The presence of manganese greatly increased the deoxidizing power of aluminum. DEOXIDATION and inclusion formation in steel have proved to be elusive phenomena that are difficult to control in spite of much effort to understand and evaluate the reactions. Study of the problem indicated that more accurate data on the solubility of oxygen in iron containing deoxidizers were essential to further progress, and an empirical determination of oxygen solubilities has been initiated at the Union Carbide and Carbon Research Laboratories, Inc. The investigation has included the effects of aluminum, silicon, manganese, and combinations of these elements at 1550°, 1600°, and 1650°C. The equipment and experimental procedure as well as the results of a study of the effects of aluminum are described below. In general, it was found that the solubility of oxygen in iron containing aluminum is much higher than predicted, possibly because of the formation of complex nonmetallic phases, and that manganese greatly increases the deoxidizing power of aluminum. The generally accepted deoxidation curves for 1600°C are summarized in fig. 1, from "Basic Open Hearth Steelmaking"'. These curves are assumed to represent the solubility of oxygen in the presence of deoxidizers and should indicate the limits of mis-cibility gaps in the phase diagrams of the systems that control the formation and character of non-metallic inclusions as described by Benedicks and Lofquist'. They were derived mainly by application of the methods of thermodynamics to the available experimental observations, and by calculations based on the thermal constants of the pure substances when experimental data were lacking. Among the more notable researches contributing to the development of knowledge of oxygen solubilities are those of Korber and Oelsen8, 4, C. H. Herty, Jr. and associates5,6, Krings and Schackmann7, Went-rup and Hieber8 Schenck and Briiggeman9, Vacher and Hamilton'" and Chipman and co-authors 1,11,12,13 Practically, the deoxidation curves are of limited value in predicting oxygen content and rationalizing deoxidation practices. The reasons for this inadequacy appear to be error from inaccurate data, oversimplifying assumptions, interacting effects of combined deoxidizers, and possibly unknown extra-equilibrium and side reactions. Although inclusion formation is a very complex reaction it must be re-

Jan 1, 1951

By W. L. Fink, M. S. Hunter, R. H. Brown

Early workers attempted to study the structure of alloys by measurement of equilibrium electrode potentials in aqueous solutions containing ions of the metals from which the alloy was made.' The method was subject to such limitations (e.g., the difficulty in attaining electrochemical equilibrium at low temperatures) that it has not been widely used by metallurgists. Recently, Seltz and co-workers have introduced a greatly improved method for studying alloys by measurement of equilibrium electrode potentials in molten salts.2"4 The mathematical treatment is the same, of course, as for equilibrium potentials of amalgams in aqueous solutions.5 This method will probably find extensive use, since it makes possible not only the determination of phase fields of equilibrium diagrams but also the determination of certain thermodynamic quantities which can be used advantageously in metallurgical calculations. However, the method presents difficulties. With many metallic and alloy electrodes, reversibility is not readily obtainable. Also, the difficulty of obtaining suitable material from which to make the cells is increased as the temperature is increased. Moreover, the necessity of carrying out measurements in a vacuum requires additional apparatus and introduces considerable difficulty, especially at the higher temperatures. Apparently, no consideration has been given heretofore to the metallurgical use of irreversible electrode potentials that exist when a specimen is immersed in a suitable aqueous solution at room temperature. The apparatus and the method required for such measurements are very simple, and if the results of such measurements could be demonstrated to be reproducible they might be very valuable in studying the structure of alloys. The method would not have the scope of that developed by Seltz and his co-workers because no thermodynamic quantities could be calculated from the data. However, the utility and the simplicity of the method might warrant extensive use for the determination of phase fields and similar applications. Theory of Irreversible Potentials A brief review of the theory of irreversible potentials will be given before showing how to interpret the potential readings in terms of alloy structure. It is known that heterogeneity of a metal surface in an electrolyte will produce points of different potentials, with the result that current flows between these points and electrochemical reactions occur. The points at which oxidation reactions are localized are known as anodes, and those at which reduction reactions are localized are known as cathodes.6, 7, 8 For the benefit of those who are not familiar with the terms anode and cathode as applied to a primary cell, the potential difference between anode and cathode of such a cell can be measured when

Jan 1, 1941

By M. S. Hunter, W. L. Fink, R. H. Brown

Early workers attempted to study the structure of alloys by measurement of equilibrium electrode potentials in aqueous solutions containing ions of the metals from which the alloy was made.' The method was subject to such limitations (e.g., the difficulty in attaining electrochemical equilibrium at low temperatures) that it has not been widely used by metallurgists. Recently, Seltz and co-workers have introduced a greatly improved method for studying alloys by measurement of equilibrium electrode potentials in molten salts.2"4 The mathematical treatment is the same, of course, as for equilibrium potentials of amalgams in aqueous solutions.5 This method will probably find extensive use, since it makes possible not only the determination of phase fields of equilibrium diagrams but also the determination of certain thermodynamic quantities which can be used advantageously in metallurgical calculations. However, the method presents difficulties. With many metallic and alloy electrodes, reversibility is not readily obtainable. Also, the difficulty of obtaining suitable material from which to make the cells is increased as the temperature is increased. Moreover, the necessity of carrying out measurements in a vacuum requires additional apparatus and introduces considerable difficulty, especially at the higher temperatures. Apparently, no consideration has been given heretofore to the metallurgical use of irreversible electrode potentials that exist when a specimen is immersed in a suitable aqueous solution at room temperature. The apparatus and the method required for such measurements are very simple, and if the results of such measurements could be demonstrated to be reproducible they might be very valuable in studying the structure of alloys. The method would not have the scope of that developed by Seltz and his co-workers because no thermodynamic quantities could be calculated from the data. However, the utility and the simplicity of the method might warrant extensive use for the determination of phase fields and similar applications. Theory of Irreversible Potentials A brief review of the theory of irreversible potentials will be given before showing how to interpret the potential readings in terms of alloy structure. It is known that heterogeneity of a metal surface in an electrolyte will produce points of different potentials, with the result that current flows between these points and electrochemical reactions occur. The points at which oxidation reactions are localized are known as anodes, and those at which reduction reactions are localized are known as cathodes.6, 7, 8 For the benefit of those who are not familiar with the terms anode and cathode as applied to a primary cell, the potential difference between anode and cathode of such a cell can be measured when

Jan 1, 1941

By Phillip B. Bucky, Fred D. Wright

The present known petroleum reserves are limited, and unless important new fields are discovered the Nation will be dependent, in the not too distant future, upon imports or upon synthetic liquid fuels to supplement domestic petroleum supplies. As a national defense measure, it would appear desirable to develop a substitute source of liquid fuels within the borders of the country if new discoveries of petroleum should Prove disappointing. Congress undoubtedly had this in mind when it passed the Synthetic Liquid Fuels Act (78th Congress, approved April 5, 1944). The act directed the Bureau of Mines to construct and operate demonstration plants for producing synthetic liquid fuels from coal and oil shale, and from forestry and agricultural products. As a part of this program, the Bureau of Mines has built a demonstration plant at Anvil Points, near Rifle, Colo., for retorting the oil shale, and has developed a mine to supply the plant with oil shale. At the beginning of mining operations, the physical qualities of the oil shale, which would have a bearing upon the selection of mining methods and practices for exploiting the deposits, were largely unknown. A comprehensive mining-research program has been set up to determine the best methods and practices to follow to obtain the lowest overall practicable mining cost for producing the oil shale on a large scale. Unusually low mining costs will be necessary for shale oil to be produced commercially. Consideration now is being given to exploiting a series of flat-lying beds 70 ft thick by a room-and-pillar method of three benches with the advance heading at the top. This report is one of a series giving the results obtained in research on mining problems, The structure and physical qualities of the oil shale indicate that the 70-ft interval of the oil-shale measure can be safely mined in open stopes; studies indicate that this method would be the most economical one to use.' As labor will be a major item of expense, the largest equipment that could be operated efficiently in the workings would be required to obtain the lowest practicable mining Cost. It Was therefore desirable to know the maximum safe span of unsupported rooms and the size of pillars necessary to support the overburden. This paper describes the work done at the Columbia School of Mines Barodynamic Laboratory in determining the maximum safe unsupported roof spans and the minimum safe pillar dimensions for the oil-shale mine at Rifle, Colo.

Jan 1, 1949

By C. Ernest Birchenall, Robert F. Mehl

Application of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion cocfficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner¹ derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smith5 on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 Activities in Brass9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by

Jan 1, 1947

By C. Ernest Birchenall, Robert F. Mehl

Application of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion cocfficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner¹ derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smith5 on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 Activities in Brass9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by

Jan 1, 1947

By John S. Brown

As a part of a symposium on the relations of structure to ore deposition, in February 1938, the writer presented some tentative opinions derived from his experience with a number of important lead-zinc replacement deposits. These ideas were set forth, as a basis for discussion and a stimulus to further inquiry, in a mimeographed leaflet that read as follows: Intimate acquaintance with a number of lead and zinc deposits in metamorphosed limestones seems to indicate the existence of certain common features from which can be established some general principles governing the localization of ore in this type of formation. It is suspected that these principles can be applied, with modifications, to mineralization in unmetamorphosed limestone. In metamorphosed formations, some observed rules are as follows: 1. Bands or masses of pure limestone are very resistant to replacement by ore solutions, and are likely either to contain no ore or to resist replacement until near the end of mineralization. The reason for this apparently is physical, not chemical, since microscopic data indicate that when ore is deposited by far the greater part of it substitutes for carbonate. The chief factor is believed to be a lack of porosity in massive limestone that has undergone flowage and recrystallization. 2. Masses of intensely siliceous or silicated rock are likewise unfavorable ore receptacles. This seems to be accounted for by two factors: (a) chemical unsuit-ability or resistance to replacement, and (b) physical resistance to small-scale brecci-ation, which might faeilitate the opening of effective channelways for solutions. Some low-grade ore may occur, however, and also sporadic fracture fillings. 3. The optimum condition for ore reception appears to be found in bands or areas containing carbonate and silicates (or quartz) intimately mingled in something like equal proportions. In this situation movement is likely to result in mixed flowage and fracture, producing a finc-textured porosity that admits solutions freely and provides access to an abundance of replaceable carbonate. Cleavage cracks in some minerals such as diopside are believed to facilitate the penetration of solutions. 4. Certain minerals or assemblages are regarded as favorable impurities in a limestone and others as unfavorable. Original quartz, and subsequently developed diopside, and perhaps garnet, are typical favorable pre-ore gangue; in general rather equidimensional, brittle minerals. Tremolite, biotite, and probably wollastonite, are typical unfavorable pre-ore gangue; in general highly elongated and somewhat flexible minerals likely to develop under strong shearing stresses. 5. Tentative opinion is that the ratio of lime and magnesia in a limestone is of little or no importance.

Jan 1, 1941

By M. Cohen, S. A. Kulin

AT a recent symposium on thermodynamics in physical metallurgy1 two opposing theories of the austenite-martensite transformation were presented. Both theories agreed that this type of reaction involves a nucleation process which requires activation and that the activated nuclei develop into the well-known martensite plates with tremendous speed. However, there were essential differences in the two points of view concerning the nature of the nucleus and the mechanism by which the nucleus propagates. According to Cohen, Machlin, and Paranjpe,' the nucleus is a strain center with sufficient elastic energy to initiate a cooperative displacement among the atoms of the parent phase when a sufficiently low temperature is reached. This displacement propagates as a wave in shear-like fashion to transform the austenite into martensite without benefit of diffusion. On the other hand, Fisher, Hollomon, and Turnbull3 regard the nucleus as a solute-poor region (in the austenite) of a size which becomes supercritical relative to coherent growth into martensite when an appropriately low temperature is reached. This growth process is taken to be an atom-by- atom transfer from the receding austenite lattice to the advancing martensite lattice through the coherent interface that exists between the two phases. The present paper is not conceded with the divergent views as to the nature of the nucleus but describes some critical experiments which differentiate between the two proposed mechanisms of propagation. Fisher' has summarized the latter issue in the following way: According to the cooperative displacement theory, the speed of formation of mar-tensite plates should not be decreased by lowering the temperature, and martensite should form with extreme rapidity at very low temperatures; whereas with the alternate growth process, the speed of the martensite transformation should be retarded at very low temperatures, decreasing to zero at the absolute zero. The atom-by-atom growth mechanism predicts a marked slowing down of the reaction rate with decreasing temperature because the rate of self-diffusion in the austenite is involved in this picture. For example, Fisher, Hollomon and Turn-bull5 estimate that the activation energy for this growth process in steel is (0.34)2(0.36)* times the activation energy for self-diffusion in y-iron. The two most recent determinations of the latter quantity are 67,900" and 74,2007 cal/mol, which may be averaged as 71,000 cal/mol. This, in turn, gives a value of 3000 cal/mol for the activation energy of the atom-by-atom process, and hence the rate of growth should vary as e 8,000/RT where R is the gas constant

Jan 1, 1951

By John S. Brown

As a part of a symposium on the relations of structure to ore deposition, in February 1938, the writer presented some tentative opinions derived from his experience with a number of important lead-zinc replacement deposits. These ideas were set forth, as a basis for discussion and a stimulus to further inquiry, in a mimeographed leaflet that read as follows: Intimate acquaintance with a number of lead and zinc deposits in metamorphosed limestones seems to indicate the existence of certain common features from which can be established some general principles governing the localization of ore in this type of formation. It is suspected that these principles can be applied, with modifications, to mineralization in unmetamorphosed limestone. In metamorphosed formations, some observed rules are as follows: 1. Bands or masses of pure limestone are very resistant to replacement by ore solutions, and are likely either to contain no ore or to resist replacement until near the end of mineralization. The reason for this apparently is physical, not chemical, since microscopic data indicate that when ore is deposited by far the greater part of it substitutes for carbonate. The chief factor is believed to be a lack of porosity in massive limestone that has undergone flowage and recrystallization. 2. Masses of intensely siliceous or silicated rock are likewise unfavorable ore receptacles. This seems to be accounted for by two factors: (a) chemical unsuit-ability or resistance to replacement, and (b) physical resistance to small-scale brecci-ation, which might faeilitate the opening of effective channelways for solutions. Some low-grade ore may occur, however, and also sporadic fracture fillings. 3. The optimum condition for ore reception appears to be found in bands or areas containing carbonate and silicates (or quartz) intimately mingled in something like equal proportions. In this situation movement is likely to result in mixed flowage and fracture, producing a finc-textured porosity that admits solutions freely and provides access to an abundance of replaceable carbonate. Cleavage cracks in some minerals such as diopside are believed to facilitate the penetration of solutions. 4. Certain minerals or assemblages are regarded as favorable impurities in a limestone and others as unfavorable. Original quartz, and subsequently developed diopside, and perhaps garnet, are typical favorable pre-ore gangue; in general rather equidimensional, brittle minerals. Tremolite, biotite, and probably wollastonite, are typical unfavorable pre-ore gangue; in general highly elongated and somewhat flexible minerals likely to develop under strong shearing stresses. 5. Tentative opinion is that the ratio of lime and magnesia in a limestone is of little or no importance.

Jan 1, 1941

By John L. Lamont, Walter Crafts

ADEQUATE hardenability has long been recognized as one of the first requirements for producing desired mechanical properties in a heat-treated steel. Since the introduction of the Jominy end-quench test1 and the development of correlative information to expand its use, industry has had an effective measure of hardenability. Prediction and control of the hardenability have been made possible by Grossmann's principle2 for calculating hardenability from chemical composition; and Field's conversion3 from depth of half-martensite hardening to Rockwell C hardness has made the relation more quantitative. These developments have facilitated the design of new steels and the control of standard grades to the extent that it has been possible to establish tentative hardenability bands for some of the more commonly used alloy steels.4 As the depth of hardening of the Jominy test specimen is usually measured by Rockwell C hardness, it was considered that it should be possible to predict the hardness by a more direct calculation. It has been found that this can be accomplished by the addition of Rockwell C units proportional to the carbon and alloy content, grain size, and position in the Jominy test specimen. The calculation has been found to be fairly accurate, and because of its additive character is relatively simple to use. In principle the method of calculation is somewhat similar to the expressions developed by Herty, McBride, and Hollenback,5 Burns, Moore, and Archer,6 and Burns and Riegel.7 The calculation is started from a base that includes the effects of carbon content and position in the Jominy test speimen. Rockwell C units are added to the base in proportion to the alloy content and grain size. This sum represents the Rockwell C hardness up to the level at which a disproportionate increase of hardness is caused by the formation of martensite, and above this level an increment for martensite hardening is added. The effects of alloys are directly proportional to the amounts present and are independent of each other, the carbon content, and the position in the specimen. Furthermore, the factors for determining the martensite increment are dependent only on carbon content and are independent of cooling rate and alloy content. It is this absence of interrelation between the different factors that makes it possible to calculate the hardness and makes the method of calculation consistent with the principle that the character of the hardening reaction is governed primarily by carbon and that alloys exert their effect chiefly through control of the critical cooling rate. The principle of the calculation, and the effects of alloys on the critical cooling rate,

Jan 1, 1945

By W. E. Rice

The ceramic industry has to do with forming or molding articles of clay, and imparting to them their characteristic properties of permanence, strength and color by subjecting them to heat treatment in kilns. This heat treatment is commonly known as "firing" or "burning." The art of firing clay ware antedates the industrial use of coal; hence wood was the fuel first used, and the earliest kilns were built to burn wood. The majority of the clay ware produced today is fired in periodic kilns that are essentially enlarged structures similar to the earliest enclosed kilns; a kiln consists of a large chamber 16 to 32 ft. dia. (or rectangular) in which the ware is charged and fired either in direct contact with flame or hot gases from the fuel, or in saggers which shield the ware from direct contact with the gases. The fuel is burned in a number of small furnaces built in the thick wall that encloses the chamber; these furnaces are from 16 to 36 in. wide and from 3 to 5 ft. long; some of them have horizontal or sloping grates, but many have no grates; the last are called "dead-bottom" furnaces. The temperature necessary to mature the charge in the kiln varies for different clays; for some it is as low as 1800°, and for others as high as 2700" F. Wood was an ideal fuel for the low temperatures that were used in early kilns; it burns freely and produces a long, clean flame, which promotes uniform distribution of the heat in the kiln; it does not coke and so restrict the passage of air through the fuel bed; the ash does not melt in the fuel bed to form clinker; and the ash that is carried into the chamber and deposited on the charge does not contain iron and sulfur to discolor the clay. The extent of the ceramic industry now precludes the general use of wood in kilns, so that today this industry is one of the large users of bituminous coal, burning more than eight million tons annually in kilns. Manufacturing plants usually are at or near the source of clay, with deposits of coal suitable for kilns occurring near the clay. The cost of coal is the largest single item of expense in the manufacture of clay ware, and, because all coals are not equally suitable for the process, the careful selection of coal is important. In this selection the desidera-

Jan 1, 1932