By Larry Southwick

In the early 1940's, the Caron ammonia ? ammonia carbonate leach process was used to produce nickel from Mayari ores at the Nicaro plant in Oriente Province, Cuba. While plant operation was generally successful, it was not broadly economical and was shut down. The plant was later restarted in the 1950's and a number of investigations initiated to resolve the more serious operational and performance issues. Processing steps studied included iron reduction (chemistry ? nickel and iron, reductant, equipment), ore variability (homogeneity and consistency of mineral concentrations, serpentine vs. laterite), leach solution strength, nickel recovery (temperature ? reduction and leaching, reoxidation) and a variety of other topics. These studies and their findings will be discussed. Caron himself obtained good results on these ores in the laboratory. They could not be duplicated in the field, the reasons for which will be reviewed. (Note: the ore looked like garden dirt; charcoal made from palm trees was one of the reductants attempted; and ammonia was the leach solution. Mixing the three, so to speak, was to yield nickel.)

Jan 1, 2006

By S. C. Grand, T. J. Auping, K. Born

Process control, environmental monitoring, budgeting and accounting are based on process data. Without appropriate tools for data analysis, the process data could remain unused and wasted. This paper demonstrates how data reconciliation can be used as a tool to develop closed mass balances. Mass balances are the initial step in plant optimisation (technical, economical or environmental). From mass balances, fundamental process models can be developed. These balances link process parameters (e.g., feed materials) to process performance (e.g., recovery of valuable elements). Some of these models could find their way into simulators useful to plant operators. Classical regression methods regularly fail when they are applied to complex non-linear problems involving a large number of variables. Alternatively, multiparametrical regression analysis can be successfully applied with the aid of neural networks based on reconciled data. Both methods have been applied to plant data originating from the hydrometallurgical zinc plant at Ruhr-Zink, which in this paper serves as a case study. Very promising and useful results were obtained from this study.

Jan 1, 2000

By Xiaorong Liu

Interfacial emulsion generated in copper solvent extraction is an inhomogeneous O/W emulsion that consists of organic phase, aqueous phase and solid particles. In order to determine what kind of components in organic phase promotes the emulsion, the organic phase separated from the interfacial crud provided by Dexing Copper Mine in Jiangxi, China was analyzed for its components by combined gas chromatography-mass spectroscopy. It was found that many kinds of emphiphiles containing such hydrophilic groups as carbonyl, carboxyl, or acylamine existed in organic phase, most of which were originated from the reagent degradation. Conclusively, Lix984N would degrade gradually during a long-term contact with the acidic aqueous feed and strip reagents. Lix84 and nonylphenol, as effective components of Lix984N, degraded almost completely after long-term recycling. As a result, the effective components of Lix984N were far lower in concentration than the dense-aromatic impurities derived from the diluent and the degradation products in total. The degradation of Lix984N would deteriorate solvent extraction, disengagement performance and result in more serious interfacial emulsion.

Jan 1, 2006

By Peter G. Smith

Tri-calcium aluminate (TCA) is a dominant alkaline component of the red mud residue from the Bayer process. A method being considered for industrial implementation partially neutralizes the residue by contacting it with gaseous CO2. This paper outlines the chemistry of CO2neutralisation of TCA under conditions relevant to the treatment of Bayer residue. CO2 neutralisation of the liquor is fast. It results in the formation of amorphous aluminium hydroxide and dawsonite that agglomerate together. Neutralisation of solid TCA is slower and leads to the formation of calcite, dawsonite and amorphous aluminium hydroxide. The dissolution of TCA in partially neutralised slurries causes pH reversion. However the carbonated solutions contain a store of bicarbonate that can supply aqueous carbon dioxide to complete the transformation. The pH at which the carbonation is carried out will affect the degree of TCA transformation during the carbonation process. In particular, if the pH of the carbonation is too low (near 7.0), calcite precipitation is inhibited and the degree of transformation is low. Controlling the carbonation pH helps to optimise the neutralisation process.

Jan 1, 2003

By Li Fangi

This paper describes the characteristics and regularities of a process to recover rare earth minerals from Baotou Ore with H-205 collector. H-205 is a kind of hydroxamic acid with amide as a polar group and poly-cycle aromatic hydrocarbon as a non-polar group, having strong ability to capture RE minerals (bastnasite, monazite). When adding a certain dosage of water glass and some other modifying agents, and maintaining pH value between 8.5 and 9.5, RE minerals can be effectively separated from calcium and barium minerals, such as fluorite and barite, etc. Under normal flotation temperature and concentration, when using H-205 to float RE minerals, it needs a bit longer conditioning time (a few minutes longer than that for the conventional collectors). It is also shown that the reagent has the property of resistance to hard water. The laboratory scale and pilot scale tests of the process have been carried out on bulk froth containing RE minerals and fluorite taken from Ore Dressing Plant of Baotou Iron and Steel Company, in both cases, high grade RE concentrates were obtained and the recovery increased remarkably. Therefore, the process has a great practical value.

Jan 1, 1989

By R. D. MacDonald

The papers presented in this chapter cover a wide range of hydrometallurgical topics and might be considered to be unrelated to each other. All of the authors, however, utilized the basic methods of process mineralogy to characterize the reactants in their experiments and the products produced. The wide range of research topics which can be pursued successfully by the use of the methods of process mineralogy is a matter of interest in itself. One might speculate that the methods could be even more widely applied if only their utility were better recognized. These methods for characterizing reactants and products include principally x-ray diffraction, optical micros-copy, wet chemical analyses, instrumental chemical analyses, high intensity magnetic separation, micro-scale gravity separation, differential thermal analysis, micro-hardness testing, and judicious use of the sledgehammer and cold chisel. It is perhaps not by coincidence that most of the papers in this chapter were prepared not by mineralogists, but by hydrometallurgists, who are recognizing the importance of thinking in terms of mineral phases, and not just assays! It appears that the gap between process mineralogy and the mineral industry is closing, and that future AIME sessions promise to become established forums where mutual discussion of such topics as metallurgical "troubleshooting" and process design may become commonplace between plant engineer and process mineralogist.

Jan 1, 1981

By Peng Fan

Nitride capacity is usually employed as the measure of slag?s ability to remove nitrogen from liquid metal, since nitrogen distribution ratio between slag and metal can be calculated from nitride capacity provided that the value of oxygen activity in liquid metal is available. However, during liquid metal refining processes, oxygen activity in liquid metal is usually unknown and thus it is impossible to get nitrogen distribution ratio from nitride capacity under this usual condition. In this paper, thermodynamic analysis indicates that the activity coefficient of nitride in slag can be used to measure slag?s ability to remove nitrogen from liquid metal, because nitrogen distribution ratio between slag and metal can be calculated from the activity coefficient of nitride in slag provided that the content of oxygen potential controlling element like Al in liquid metal is available. Review of reported nitrogen removal studies and our recent study has verified that for a given Al content in metal, the lower the AlN activity coefficient in slag is, the higher the nitrogen distribution ratio. Titanium monoxide based slag has been found to be much more effective to remove nitrogen than other slags. Since Al content in liquid metal is usually available during liquid metal refining processes, AlN seems to be a better measure of slag?s ability to remove nitrogen from liquid metal.

Jan 1, 2006

By Albert W. Spitz

Profitably recovering copper and precious metals from copper bearing scrap is a demanding and frustrating combination of art, science and economics. With fluctuating markets, varying raw materials and increasingly stringent environmental regulations requiring process revisions, practically everything is changing. The volatile copper market constantly shifts the percentage of copper in the scrap that can be economically processed. Scrap that has value one day may incur a disposal cost the following day. Also with less copper in the scrap, more residuals, slag, fume, etc. are generated which frequently present disposal problems and infrequently generate income. The ever increasing amounts of electronic scrap add value to the copper produced by virtue of the precious metals present. Printed circuit board materials create more slag and organic off gases which must be treated. Finally, the emphasis on reducing emissions of organics and other metals, especially lead, is a continuing challenge. Stack gases, fugitive emissions and ambient air quality all demand constant surveillance.

Jan 1, 1997

By C. J. Lewis

This presentation concerns calcium oxide-better known as high calcium quick lime High calcium quicklime is produced by calcining high calcium limestone, mostly in the many rotary kilns located throughout the United States and Canada. This paper presents suggestions on the handling of lime based on field experience. The subjects covered are chemical analyses, transporta¬tion, lime storage, lime slaking to form a water slurry of calcium hydroxide solids, slurry transportation, slurry viscosity, and scaling of lime slurries. It is hoped that the comments on the foregoing areas will be of use to those designing or operating lime systems.

Jan 1, 1992

By Pradeep kumar Jha, Manas Mohan Mahapatra, Sabin Kumar Mishra, Satish Kumar Ajmani, Satish C. Sharma

"Due to mechanical/ electrical failure in the C.C. line or inadequate availability of molten steel from coming ladle, sometimes one/two outlets of a multi-strand tundish in continuous casting unit is closed. Closing any of the outlets affects the flow distribution inside the tundish which in turn governs the quality of steel coming out. Hence it is important to study which of the outlets should be closed to have proper results in terms of flow behavior and inclusion removal inside the tundish. Present study aims at finding the effect of closing one or two outlets on flow behavior and inclusion removal in a multi strand tundish. It was found that closing the near outlet (outlet near to the inlet) increases the inclusion removal tendency than closing the other two outlets in a six-strand billet caster tundish (only three outlets are considered because of symmetry).IntroductionContinuous casting process transforms molten metal into solid on a continuous basis. This process is the most efficient way to solidify large volumes of metal into simple shapes for subsequent processing [1]. Molten metal is tapped into the ladle from furnaces. From the ladle, the hot metal is transferred via a refractory shroud (pipe) to a holding bath called a tundish. The tundish allows a reservoir of metal to feed the casting machine while ladles are switched, thus acting as a buffer of hot metal as well as smoothing out flow, regulating metal feed to the moulds and cleaning the metal [2]."

Jan 1, 2012

By M. Sripathy, K. V. Sharmal

"The conventional fiber reinforced plastic does not participate in the plastic deformation or enter the large plastic deformation state during collision. On the other hand, sandwich structure allows more plastic deformation, which improves the energy absorption efficiency. The objective of this study is focused on the investigation of the crushing of sandwich structure made from sisal / coir / bamboo/ glass fabrics as reinforcement and with polyester resin to form the composites skin and with polyurethane foam as the core. Experiments were conducted, showing that the underlying crushing mechanism of sandwich structures is very different from that of solid-section thin-walled structures. When a sandwich is subjected to crushing, the core deforms in the shear mode and the face bends independently. The damage is through the width zone of crushed foam core accompanied by a residual crushing in the foam. It is shown that such damage causes a significant reduction of compressive strength. Results show that glass/polyester and bamboo/polyester skin based sandwich structures have superior compressive strength. Coir /polyester based sandwich structure come next to glass/polyester sandwich structures in this aspect which is then followed by Sisal /polyester based sandwich structures.IntroductionCellular polymeric foam sandwich structures are often employed in shock mitigating applications. The cellular polymeric foam has several favorable properties, such as, low density, relatively high strength-to weight ratio and a significant degree of crushability. This high crushability is the result of the large void ratio in such materials, which also facilitates the collapse of cell walls via bending and buckling [1]. A few feasibility studies on FRP sandwich panels show that the panels efficiently provided high mechanical performance for minimum weight [2]."

Jan 1, 2012

By Ibrahim Yusufoglu, Ahmet Orkun Kalpakli, Cem Kahruman, Sedat Ilhan

"The effects of oxalic acid concentration, temperature, stirring rate and particle size on the dissolution rate of synthetically prepared calcium molybdate were investigated. Dissolution of calcium molybdate in oxalic acid solutions takes place as a series - parallel type reaction. In the first reaction step, which proceeds according to the ""Langmuir - Hinshelwood Mechanism"", calcium aqua oxalato molybdate is formed as a complex chelate intermediate product. In the second reaction step, molybdic acid is formed during the slow hydrolysis of calcium aqua oxalato molybdate, and it reacts rapidly with oxalic acid to form the polymeric hydrogen oxalate dimolybdate chelate as an end product. Activation energies were calculated as 41.4 and 49.9 kJ mol-1 for the first and zero order reactions. The fractional conversion versus time relationship can be given by the following equation.IntroductionMolybdenum is used widely in electric-electronic, metal working, aerospace and aeronautic, nuclear, glass and petrochemical industries because of its high melting temperature and resistance against chemical effects. However, the largest molybdenum consumers are the iron-steel and super alloy industries where molybdenum is used as an alloying element. Industrially important molybdenum minerals are limited to molybdenite (M0S2), powellite (CaMo04) and wulfenite (PbMo04), which are considered as primary molybdenum resources. Secondary molybdenum resources are spent catalysts and scrap [1-4].Molybdenum has been produced by pyrometallurgical processes in the past. Since it is possible to process low grade molybdenum ores and industrial wastes by hydrometallurgical processes, which are more environmentally friendly than pyrometallurgical processes, the importance of the use of hydrometallurgical processes has increased in the molybdenum production industry."

Jan 1, 2012

By Justin Karl, Ali Gordon, James DeMarco, Yongho Sohn

"Aluminum metal-matrix composites are lightweight materials that have the potential to supplant steel in many applications. The current work helps to identify the parameters that confer maximal strength and ductility. Torsion tests were performed on the as-cast aluminum metal-matrix composite A359-SiCp-30% at a variety of temperatures and twist rates. Dependence of material properties on temperature and strain rate were identified from equivalent stress-strain curves constructed from the reduced data. Examination of the microstructure was performed on the as-cast material and on fracture surfaces. A temperature-and strain rate-dependent constitutive model was applied to simulation of the mechanical response of the torsion specimen. Trends in material properties corroborate and extend trends identified previously under tensile loading with regard to temperature and strain rate dependence. Shear properties of simulated specimens agree with properties obtained through experimentation.IntroductionAluminum metal-matrix composites (A1-MMCs) have become increasingly popu1ar in recent years. While unreinforced aluminum alloys have low densities and high ductilities, they are not suitable for many applications due to their lack of strength and stiffness. To provide added strength and stiffness while maintaining favorable densities, it has become common to reinforce aluminum alloys with silicon carbide in various forms, although usually the inclusions are in the form of whiskers or particles. The result is a composite material with superior specific strength and stiffness. While whisker-reinforced composites are expensive due to the necessity of processing by nonstandard techniques and have low transverse properties when rolled, particle reinforced Al-MMCs have transverse material property values almost as high as the longitudinal properties and are not as expensive to process as whisker-reinforced Al-MMCs [1]."

Jan 1, 2012

By Jing Zhan, Chuanfu Zhang, Yonglin Yao

"The Ni/Co arbitrary ratios of fibrous precursor were investigated during coordinated coprecipitation by changing the precipitating medium. The results show that the original molar ratio ofNi2+ to Co2+ in reaction solution can be maintained in the coprecipitate at pH'.'05.0 and the coprecipitate is single phase solid solution using water and water-X precipitating medium. But the original Ni/Co ratios are no longer kept and composition of the coprecipitate is not uniform at pH>5.0 in water precipitation medium. In order to obtain the precursors with the required morphology and accuracy Ni/Co ratios, the optimum conditions of fibrous precursors were chosen as follows: ammonia used as complex agent and pH adjustor, water-X solvent as precipiting medium, oxalate as coprecipitated agent, 8.0-8.4 for pH value, 50-70°C of reaction temperature, 0.5-0.8 mol/L of initial nickel and cobalt salt concentrations and excesses of oxalic acid of 10% - 20%.IntroductionNi-Co alloy as an important transition metal alloy with high mechanical strength, good anti-deformation, corrosion resistance, thermal conductivity, thermal stability, electrical conductivity, electrical contact, and special magnetic properties indicates that it can be used as high-temperature catalyst, special magnetic material, high-temperature electrochemical devices, and so on [1-6]. An ideal composite powder should have an appropriate stoichiometric ratio, good uniformity of chemical composition, appropriate phase, low impurity content and small particle size [7]. Similarly, the composition of nickel-cobalt alloy powder has an important impact on its crystal structure, properties and applications. Guo[8] found that magnetisms of CoxNi1-x such as magnetic anisotropy, curie temperature, and the shifts of the spin steering are very sensitive to the composition of alloy powder."

Jan 1, 2013

By Xinghua He, Shujing Zhu

"In this paper, the chemical composition, the content and the leachability of heavy metals in dredged sludge are tested and analyzed. It is shown that the leachability of Pb and Cr exceeds the leaching toxicity standard, and so the dredged sludge is considered as hazardous waste and must be solidified. The effect of solidifying the dredged sludge by the hydraulic ash-slag cementitious composites is studied, and it indicates that the heavy metals can be well immobilized if the mass fraction of the dredged sludge is appropriate. The heavy metals are immobilized within the hydraulic ash-slag cementitious composites hydration products through either physical fixation, substitution, deposition or adsorption mechanisms.IntroductionDredged sludge is classified as a hazardous waste because it usually contains concentrated heavy metals and chlorinated organic compounds, as well as soluble salts, and is also composed of very fine particles. Moreover, inorganic pollutants are typically associated with soluble compounds, which are, therefore, highly leachable from dredged sludge when dredged sludge is contacted by a liquid medium[l1. Thus, dredged sludge must be stabilized in order to reduce its environmental impact on the final disposal site. The frequent means of dredged sludge disposal used include(!) Chemical stabilization (2) acidic extractionChemical stabilization is translating mobile heavy metals into low dissolution and low toxicity form through chemical reaction. The commonly chemical medicaments are sodium hydroxide, soldium sulfide, thiourea, EDTA. But Zhao et al [ZJ found sodium hydroxide is not fit for Pb stabilization, the other three are effective, but the chemical properties of sodium sulfide are not stable, thiourea and EDTA are very expensive, and so it is very difficult to apply them. Moreover, because of the complexity of heavy metal conformation and dredged sludge composition, it is very difficult to find a cheap and prevalent stabilization medicament in point[31 ."

Jan 1, 2013

By Thomas Brynjulfsen, Merete Tangstad

"Manganese ore fines, generated during mining and transportation, can not be added to the submerged arc furnace directly as they will prevent even gas flow through the burden. Low gas permeability in the burden will lower the degree of pre-reduction of ore and subsequently increase the carbon and energy consumption of the process. In order to utilize manganese ore fines in the furnace they are agglomerated into sinter, pellet or briquettes. The agglomeration process will however change the reduction properties of the ore. In this work the melting and reduction properties of sinter has been investigated.The melting temperature and melting mechanisms has been studied. The mineralogy of the raw ores and agglomerated has been found using XRD, and the composition established using EPMA(WDS). The effect of adding fluxes such as dolomite and quartz has also been investigated.IntroductionManganese metal is produced in a submerged electric arc furnace or in blast furnaces. The reduction of manganese oxide in blast furnace has in the recent years become more unusual due to the high consumption of reducing carbon material[5]. Manganese metal for alloying in steel usually contains silicon and iron, and are therefore called ferro manganese and silicomanganese.During mining, transportation and handling the manganese ore is broken up into different size fractions. The larger lump are used directly in the electric arc furnace, but the finer materials can not be added without treatment. The fine ore can disrupt the flow of CO and CO2 gas through the burden, subsequently reducing the degree of pre-reduction. The fine fractions must therefore be agglomerated into larger lumps, in order to promote gas flow. This can be achieved through a number of different processes. The agglomerate used in this work has been sintered, which means that is has been partly molten and reduced, in order to create bigger lumps."

Jan 1, 2012

By M. Rockandel

"Universal Dynamics Ltd. of Vancouver, Canada has developed, patented and commercialized the ""REMERC"" process for the treatment of mercury contaminated sludges and soils. Mercury is extracted into an acidified and oxidizing, sodium chloride brine solution. REMERC was initially developed to treat mercury contaminated EPA listed wastes (K106) generated by the chlor-alkali industry. More recent work has expanded the capability;' of REMERC to include remediation of mercury contaminated sites, equipment and building materials.In the process mercury is currently recovered from solution by cementation on iron powder in an agitated reactor. The process recovers high purity elemental mercury (99.9% purity). Cementation typically recovers about 90-95% of the mercury in 30 minutes. Higher recovery is not necessary because of the recirculation of the leach solution. When treating highly contaminated chloralkali wastes (5-13% mercury content), REMERC will reduce the mercury laden solutions from 400-1,000 mg/L mercury to 50-100 mg/L. In the treatment of less concentrated wastes «1,000 mg/kg mercury) such as those encountered in site remediation, the treated solutions will generally contain 10-20 mg/L mercury. Cementation while being simple and able to achieve the required recovery has the. undesirable properties of; requiring a solid-liquid separation and adding iron to solution which must be precipitated, ultimately increasing the weight of residue to landfill. .The potential advantages of electrolysis were recognized early in the development of REMERC. Mercury electrolysis is well known in gold and chloralkali processing. Initial testwork utilized a liquid mercury cathode and a coated titanium anode both common to chloralkali producers. The mercury cathode appeared susceptible to polarization and solution impurities significantly affected performance. Agitation of the mercury pool improved performance but it was still not possible to achieve the reduction objectives. Current efficiencies were low, near 10%, and it was apparent that a relatively large cathode pool would be required to limit the current density. A number of electrode combinations with and without a membrane were then tested in a vertical electrode' configuration but the desired performance was not obtained."

Jan 1, 1997

By Chris T. Vild

"ABSTRACT NOT AVAILABLEPRESENTATION SUMMARYIntroductionToday, light gauge aluminum scrap is melted in sidewell furnaces using natural gas reverberatory burners. The scrap is introduced into the sidewell adjacent to the combustion chamber through a submerged archway. Super-heated metal is then pumped into the sidewell where it aids in melting the scrap. From the sidewell, the flow is returned to the combustion chamber through a second submerged archway at some lower temperature. Normally, the burners are set at a designed high fire level and the scrap is introduced at a rate to attempt to mat.ch the burner input. A thermocouple in the bath is programmed to throttle back the burners to low fire if a high temperature limit is exceeded.Jn many cases the thermal efficiencies of these furnaces can be very low. With inadequate circulation, air and natural gas furnaces run at a dismal 18% thermal efficiency. If a circulation system· is added, the efficiency can jump to 28%. For a $100 million lb/yr recycling facility, and natural gas prices reaching $4.50 per million Btu, fuel cost at 18% efficiency can reach $1 million per year. A 10% increase in thermal efficiency saves $350,000 a year in fuel costs.With an increase in thermal efficiency, furnace utilization also increases. A 10% increase in thermal efficiency would result in a 20 million Btu furnace producing 12,000 lb/hr up from 8,000 lb/hr or 35 million lb more produced per year. This is a 33% increase in output.Most current furnace development has focused on burner technology using oxy-fuel, regenerative burners, etc. However, thermal efficiency is also largely effected by the molten metal circulation rate and how well the scrap is mixed into the superheated metal. Therefore, the flow dynamics should be optimized first, before installing of more thermal power.Jn an effort to understand the effect of these variables, a series of computer models were made and the critical factors studied with the goal of demonstrating an increase in thermal efficiency and production. Large-scale graphical representations of these models will be presented."

Jan 1, 2000

By Linli Wu, Guangchun Yao

"The influence of deformation on the properties of short-carbon-fiber reinforced 2024 alloy matrix composites was investigated in this study. It was found that the distribution of carbon fibers changed from the random state before deformation to the ordered state that carbon fibers arranged along the direction of rolling and extruding after deformation. Under the temperature range in control, the increase of rolling and extruding temperature would benefit to improve strength and elongation of composites, but was not conductive to improve the hardness of composites. With the increment of total deformation, all the strength and the hardness of composites became greater, nevertheless the elongation decreased. After being rolled and extruded, the strength and the hardness of composites were all bigger than those of composites before being rolled and extruded; moreover, the strength of extruded 2024 alloy matrix composites was higher than that of rolled 2024 alloy matrix composites under the same heat treatment conditions.IntroductionCarbon fibers have been reckoned as very important reinforcements due to the high specific strength, specific modulus, high thermal and electric conductivity, low expansion coefficient and good self-lubricant properties [1-4]. Light metal composites reinforced with carbon fibers, such as carbon fibers in an aluminum matrix, are widely used and studied. Some studies have concentrated on the interfacial characteristic of CF/Al composites in order to search for the way of improving the bonding between carbon fibers and the matrix alloy [5-8], and on the influence of the carbon fiber percent composition in the composites [9-11]. Some researchers began to take interest in the deforming characteristic and failure behavior of carbon fiber reinforced metal matrix composites [12-16]. However, the same with other metal materials, most of CF/AI composites were prepared by some single processes, such as powder metallurgy, extrusion casting and vacuum press infiltration, which caused that the composites products could not be manufactured directly. In order to cover the shortage of the mentioned above processes and get composites products with perfect mechanical properties and dimensional accuracy, the composites should be reworked by rolling, extruding or forging process. Compared with research about manufacturing process, the correlative investigation on the reworking of CF/Al composites was much less evidently, which restricted the application and the further development of CF/Al composites."

Jan 1, 2012

By Erich Hovestädt, Hans-Jürgen Odenthal, Christian Wuppermann, Herbert Pfeifer, Antje Rückert

"During the argon oxygen decarburization (AOD) process high-chromium steel melts are decarburized by oxygen and inert gas injection through sidewall nozzles and a top-lance. Due to the large amount of the injected processing gas, low frequency oscillations of the vessel can be observed. It is suspected that these oscillations can influence the converter's structure. The exchange of forces between fluid and the surrounding vessel is the focus of this study. An oscillation model was developed and tested, one objective being to limit the computational effort which is necessary for fully coupled and time resolved CFD and FEM simulations. Experimental results obtained from water-model studies as well as from on-sight measurements are available and were used in order to validate the numerical results. The authors' intention is a contribution towards a more in depth understanding of the factors influencing vessel vibration during the AOD process.IntroductionDuring the last four decades the AOD process has been established as a reliable and efficient refining process in stainless steel making. The injection of process gases (O2, N2, Ar) through sidewall nozzles shows advantages in mixing effectiveness compared to other injection geometries e.g. bottom blowing [1]. Stainless steel grades contain usually more than 10% chromium. With decreasing carbon content during the decarburization periods the tendency of chromium oxidation increases according to the varying chemical equilibrium which depends on the partial pressure of carbon-monoxide (CO) in the gas phase. That's why oxygen is gradually replaced by inert gases, usually argon or nitrogen, in order to lower the CO partial pressure and thus to minimize chromium oxidation. Despite the high injection velocity of approximately Ma = 1, the kinetic energy of the gas jets is consumed within a short distance from the nozzle exits due to the large density ratio between gas and melt of approximately 1:8000. With increasing distance to the nozzle exit, the initial horizontal velocity of the gas jet decreases and due to buoyancy force motion of the detached bubbles turns into a vertical direction. Subsequently a gas plume develops with its typical conical shape described by various authors [1-4]. Due to the drag force between gas bubbles and melt also the liquid phase is forced into a vertical motion. Near the free surface and the wall regions the melt flow is deflected in different directions. Subsequently, the typical flow pattern in the AOD vessel arises, as sketched in Figure 1 and described in literature [5-9]."

Jan 1, 2012