Search Documents

By Taner Kavas

In the present study the utilization of coal ashes that appear at the end of firing process of brick production in cement pastes was examined. Ashes with three different particle sizes of 75 µm, 106 µm and 150 µm were used to replace ordinary Portland cement (PC) as 5 % and 15 % by weight. Seven samples were prepared and physical, mechanical, chemical and microstructural analyses were carried out. The compressive and bending strength values of samples were determined at the ages of 2, 7 and 28 days. It was found that cementitious pastes with finer particle sizes possessed the highest compressive and bending strength values at all curing ages. Both values after 2 and 7 days cure increased with an increase in ash content, no matter what the particle sizes of ashes were. However, strength decreased after 28 days cure as a result of ash addition of 15 %, although it was still above that of the PC.

Jan 1, 2006

By Józef Czernecki

The Polish copper concentrates are characterised by low content of sulphur and iron. At KGHM Polska Miedz S.A. two copper production technologies are in use. The shaft furnace process is used at the Legnica Copper Smelter and the Glogów I Copper Smelter. A single-stage direct to blister Outokumpu flash smelting process is used at the- Glogów II Copper Smelter. Melting copper concentrates in the shaft furnaces is carried out in a reducing atmosphere and the product obtained is a matte. Instead, a result of melting copper concentrates by an oxidising flash process blister copper of a quality similar to that of converter copper is obtained. The annual copper production at KGHM Polska Miedz S.A. exceeds 450,000 tons. Another important metal is silver produced from slimes from copper electrolysis (about 1000 t/y). Moreover, such metals as Pb, Ni, Se, As, Au and other precious metals, including Pt and Pd, are recovered from various semiproducts. This paper presents technological flow sheet of the copper production in plants using the shaft furnaces and in another plant in which a single-state flash process is applied. Characteristics of products, methods of their utilisation, main parameters of particular technological operations, and advantages and shortcomings of the solution applied are presented. There are also discussed: the natural environment protection as well as directions of the KGHM Polska Miedz S.A. plants modernisation.

Jan 1, 1999

By Alexandr I. Volkhin

It is practically useful to separate copper from nickel at the fire refining stage of blister copper by transferring nickel in electrochemical inert silicides which are being concentrated further into the tank-house slimes. The treatment of copper melt by silicon-containing reagents is resulted in lowering the interfacial tension of the melt, its deoxidizing, selective siliconizing of in-melt nickel and forming a by-product with fluxing properties. Si-containing reagents have positive influence on results of fire and electrolytic refining, and further pulverizing of copper in plant conditions.

Jan 1, 2006

By G. Cifuentes

It is known that the cathode purity and the electrolyte treatment are affected by the solids present in the electrolyte. Anodic slimes properties (e.g., chemical composition, crystalline composition, sedimentation) were studied in copper electrorefining. These properties were modified through anodic composition and current density. In this investigation, we have worked with anode material from the Ventana Smelting, Hernan Videla Lira Smelting (ex - Paipote) of ENAMI (National Mining Company) and El Teniente Smelting of CODELCO-Chile (National Corporation of Copper of Chile). The characterization of the anodic slimes was done as a function of current density and anodic composition.

Jan 1, 1999

By M. Arenas

A corrosion study of a bonded NdFeB permanent magnet materials alloyed with titanium carbide additions has been undertaken. The materials were produced by rapid solidification by melt spinning. Commercial epoxy was used as a bonding medium. The corrosion results were compared with those of a near stoichometric unalloyed NdFeB. Anodic polarization and potentiostatic techniques in 0.9 M Na2SO4 solutions were used to characterize corrosion behavior. It was found that the addition of 6 a10 Tic resulted in superior corrosion resistance, as indicated by lower corrosion currents and less iron dissolution at fixed potential.

Jan 1, 1997

By T. Taniguchi

The existing Mitsubishi Process line at Naoshima Smelter and Refinery has been operating successfully since 1991, and its present production capacity is 270,000tpy of copper. Furnace relining works have been carried out every two years to coincide with the compulsory bi-yearly boiler inspection, but the next target is to extend the furnace refractory life to four years, while still undergoing the mandatory boiler inspection every two years. Although the damage of hearth bricks beneath lances in the Smelting furnace was a matter of concern, it was reduced by controlling gas velocity and evening solid distribution to each lance. The life of bath level bricks in the Converting furnace was also a concern, but four-years continuous use of the bricks was achieved in the course of the last two campaigns. Several other improvements were also carried out to the cooling systems during the shutdown in 2005 to ensure longer campaign life. This paper summarizes recent improvements implemented to enhance the advantages of the Mitsubishi Process.

Jan 1, 2006

By Jean Frenay

Bacterial leaching tests have been carried out on Portugese pyritic ores containing zinc, copper, lead and silver as valuable elements. Both indigenous and isolated strains of Thiobacillus ferrooxidans were used. During the tests the factors pH, Eh and dissolved oxygen were measured and related to the leaching activity of the bacteria. Different means to estimate or determine the real bacteria concentration were examined. The influence of nutrient media and particle size has been evaluated. The role of galvanic couples was studied by electrical linking of mineralogical samples of pyrite, sphalerite and chalcopyrite. Leach residues were examined by optical microscopy to follow the mineralogical alterations during the leaching. The results show a rather good leaching of the sphalerite. However, the dissolution of copper from chalcopyrite is much more difficult, 50 % recovery never being obtained.

Jan 1, 1985

By Romeo U. Pagador

After privatization in 1999, PASAR Corporation initiated a plant modernization program to optimize the performance of the smelter by increasing plant availability. This initiative required operational adjustments to the converting and anode furnace procedures, to support the higher throughput in the flash furnace, while continuing to meet government environmental regulations. The major shift in production direction was to eliminate the 30-35 day maintenance shutdown every two years, and replace it with a 15-day shutdown. This paper discusses the changes implemented in the converter and anode operation that have resulted in an increase of 10% in flash furnace throughput, an 18% increase in blister output, to 170 tonnes per cycle, and a converter campaign tonnage increase of 10%. Since privatization, PASAR has instituted a series of ?management of change? programs that have facilitated an industrial cultural change needed to achieve the company?s vision, mission and strategic goals.

Jan 1, 2005

By C. M. Acuña

Copper losses in slags are of great concern, specially in smelting and slag cleaning processes. It is widely accepted that the suspension of metallic copper and matte droplets is strongly affected by the viscosity of the slag. The Chuquicamata Division of Codelco- Chile produces concentrates high in zinc, an element which reports mainly to the slag phase. The ZnO may affect the viscosity and therefore the copper losses. This work aimed to investigate the effect of lime to control the viscosity of slags, and in turn to control the copper losses. By using the experimental viscosity data and the Stoke's law, the settling rate of matte prills in various slags was estimated. The results indicate the possibility of increasing the recovery of copper and/or decrease the process time.

Jan 1, 1999

By Burkhard Seeger et al.

The oxidation of copper sulfides can be highly accelerated in the presence of nitrous gases (NOx) as reaction catalysts. Sulfur and sulfate are simultaneously produced in this highly exothermic reaction. This process, carried out in sulfuric acid medium, is performed at an approximately normal pressure and at a temperature of around 110 °C, in a closed container, adding either oxygen or air. The oxidation is automatically controlled through a computer. The process covers the following steps: Catalytic oxidation, filtration and crystallisation of the hot concentrated liquid, electrowinning, mother liquor treatment through jarosite formation, recovery of dissolved copper and zinc and regeneration of industrial water, and non-soluble residue treatment with extraction of sulfur and recovery of silver and gold. No combustibles are needed. No air is contaminated, and no waste water is produced. Solid residues are in a stable, non-toxic and non-corrosive state of equilibrium. Risk of accident is low. Investment costs are small compared to those of the comparable pyrometallurgical process, and production costs are competitive.

Jan 1, 1999

By Seiji Yokoyama

As a series of fundamental study on the gas evaporation method, a levitation-melted aluminum was evaporated in the gas mixture of argon and ammonia to synthesize ultrafine particles of aluminum nitride. When the ammonia partial pressure were more than 2kPa, the formation ratio of aluminum nitride was about 95%. The particles of aluminum nitride were mainly hexagonal. The mean size of the particles of aluminum nitride was about 57 nm, and it was constant without depending on the temperature of the levitated aluminum and the partial pressure pf ammonia. The aluminum nitride was formed by the reaction between ammonia and condensed liquid aluminum particle whose size was relatively small.

Jan 1, 2006

By L. A. Kazanbayev

The Chelyabinsk Electrolytic Zinc Plant (CEZP) was commissioned in 1935. Over the elapsed years the Plant capacity has been increased from 10 thousand tons of zinc (1935) to 150 thousand tons of zinc (2005). The paper describes the Plant main achievements in production updating for the last 10 years.

Jan 1, 2006

By J. Peter, S. E. James, J. L. Watson

A survey of operating zinc smelters and refineries throughout the world has been done in conjunction with the Lead-Zinc 2000 Symposium. This survey follows the examples set by the Japanese Mining Industry Association in 1985 and 1995. Questionnaires were sent to operating zinc plants that covered feed materials, process details, energy consumption and labor requirements. The voluntary responses to the survey were tabulated. Key operating parameters including feed grade, production capacity, quality of the intermediate products and quality of the final products have been compared for both hydrometallurgical and pyrometallurgical processes.

Jan 1, 2000

By Kang-In Rhee

Nonferrous metal recycling not only provides energy saving and environmental benefits but also is a significant factor in the supply of various types of metals used in our society. Recycling plays an important role in establishing the sustainability of materials. The total amount of recycled nonferrous metals by weight accounts for less than 5% but their value is larger than 50% compared to ferrous metal recycling which consists of about half of the total metal recycling in weight. This paper describes trends and typical achievements in nonferrous metal recycling and overviews the present and future of nonferrous metal recycling technology and business in Korea.

Jan 1, 2006

By F. Tailoka

In order to decrease the voltage required for electrorefining, a recessed electrode cell has been developed in which the anode and cathode have recesses machined into their faces. The anode and cathode plates are separated by a thin refractory cloth and the cell is filled with fused salt. Bismuth containing 10 to 90 % lead with copper and silver as minor impurities has been electrorefmed at a current density of 10,000 to 20,000 Am-2. The cell voltage was between 285 and 635 millivolts and the bismuth was refined to a purity of 99.9 %. Flow patterns were observed in a room temperature model of the recessed channel cell using water and mercury to simulate molten metal and the fused salt electrolyte. The flow in the electrode recesses is characterized by discrete droplets when the liquid flow rate is low and thin streams and rivulets at higher flow rates.

Jan 1, 1995

By Giovanni Principi

The activity of the ?Hydrogen Group? of Padova University, addressed to the study of materials for solid state hydrogen storage, is illustrated. Various Mg-based materials have been considered and are being studied: a) MgH2 and 0.5% mol Nb2O5 mixture ball milled under argon atmosphere; b) Mg-Ni-Fe intermetallic compounds prepared by short time ball milling of ribbons obtained by melt spinning and by long time ball milling of a mixture of MgH2, Ni and Fe powders; c) MgH2 ball milled in argon with Mm-Ni-Al (Mm = La-rich mishmetal) and Zr-Cr-Fe catalyst alloys. All the samples have been structurally characterized by X-ray diffraction (Rietveld refinement) before and after hydrogen absorption/desorption cycling and tested with a Sievert apparatus as regarding their thermodynamic and kinetic properties.

Jan 1, 2006

By Y. Mori, K. Kawanaka

The permeability changes during the sintering of the feed for the Imperial Smelting Process (ISP) were investigated using an experimental sintering pot, as well as with a mathematical model. The results obtained were as follows. The blowing resistance in the sintering bed changes as the sintering reaction proceeds. It increases at the beginning of the reaction when the temperature of the bed is still low. Then it decreases as the reaction continues, accompanied by an increase of the bed temperature. The increase of the blowing resistance in the bed during the sintering process mainly occurred in the drying zone, and was comparatively small in the reaction and cooling zones. Based on Erugen's equation, the change of the permeability during sintering is explained by the decrease of the apparent fractional void volume in the drying zone of the bed.

Jan 1, 2000

By Xu Weihong

After being pre-treated, composite electro-deposits of semi-bright nickel/nano-SiO2 with bright nickel or with amorphous Ni-P alloy, and Composite electro-deposits of Zinc were prepared on Nd-Fe-B magnetic material. The effect of cathodic current density, nano-SiO2 concentration, stirring strength and surfactants on the corrosion resistance of electro-deposits were studied. In addition surface appearance and structure of the composite coatings were analyzed by SEM. The present investigation shows that the corrosion resistance of composite electro-deposits of semi-bright nickel/nano-SiO2 with amorphous Ni-P alloy was the best, the solution system of semi-bright nickel/nano-SiO2 with bright nickel was stable and its electro-deposits also had an excellent corrosion resistance, composite electro-deposits of Zinc not only had good corrosion resistance, but also low cost, thus making it an excellent electro-deposit for medium or low-class Nd-Fe-B magnetic material.

Jan 1, 2006

By R. E. Molnar

A number of flowsheets have been designed and operated, or are currently being considered, to extract copper from leach solutions having much more copper than the 4 g/L levels typically found in heap leach liquors. Dealing with these solutions has required that the envelope for ?normal? copper solvent extraction be pushed beyond the usually considered limits. Others have published information on flowsheets to recover copper from leach liquors containing over 25 g/L copper. Secondary solvent extraction circuits are often required to attain satisfactory overall recoveries. This paper reviews some of the issues faced in three pilot plant circuits that were operated by SGS Lakefield Research to produce cathode copper from solutions containing 8 to 20 g/L Cu. The primary objective was to maximize copper extraction using one solvent extraction circuit. The role of feed acidity and the disposition of impurities such as iron and chloride are considered. The challenges of running short SX piloting campaigns are discussed.

Jan 1, 2003

By Shaolong Chen

Feeding dry sulfide concentrate into smelting furnaces enhances process performance and reduces the energy consumption and exhaust gas flow. Direct heated rotary dryers and flash dryers have being replaced by rotary steam dryers featured by very low wear rate of the pipe heating elements and long maintenance interval. Impact of the drying processes on the environment receives more and more attention as the emission legislation tightens. In this regard, environmental factors such as SO2, CO2, dust and gas flow among rotary dryers, flash dryers and steam dryers were compared. Selection of a rotary steam dryer for copper and nickel concentrate drying would be an ideal solution to reduce the pollution of exhaust gas, as drying is achieved by indirect contact to the steam at relatively low drying temperature and as the off-gas contains almost only water vapor and air. The emissions can be significantly reduced and only small and simple off-gas handling units are needed.

Jan 1, 2006