By Asmo Vartiainen

Background of Direct-to-Blister Flash Smelting is discussed; especially slag chemistry relating to copper solubility, slag fluidity and impurity behavior. In December, 2000, Mini-pilot Flash Smelting test runs were carried out at Outokumpu Research Oy to produce blister copper from Chilean concentrate and white metal and from a mixture of them. Tested slag types were iron silicate slag, ferrous calcium silicate slag and calcium ferrite slag with different slag compositions and different concentrate/white metal ratios. The test runs were successful. The fluxing effect of copper oxide was clearly demonstrated and ferrous calcium silicate slags remained fluid on a very wide liquidus range. The distribution of arsenic between ferrous calcium silicate slag and blister copper is much higher than between iron silicate slag and blister copper. This successful test run with the new slag type offer new possibilities in Direct-to-Blister process design.

Jan 1, 2003

By Xie Zhang, Jiang Diao, Xin Qiu, Lu Jiang, Bing Xie, Hong-Yi Li

"Duplex converter process, in which the first converter is used for removing phosphorus from hot metal (De-P), is an important way to produce low P-content and ultra-low P-content steels. In order to improve phosphorization removal and formation of slag with high basicity at relatively low temperature during dephosphorization converter process, effects of temperature, silicon content in hot metal and varied compositions of the De-P converter slag on phosphorus distribution between the slag and hot metal were investigated with thermodynamic calculations and by laboratory scale experiments in present work. Results showed that phosphorus distribution ratio between slag and metal was varied in 10.6~26.6 when basicity of the slag was in the range of 1.5~2.1 at 1370, and the distribution ratio was increased with increasing basicity and Fe10 content in the slag.IntroductionIt is known that phosphorus exists in steel in the form of solid solution, which can significantly improve strength and hardness of steel at room temperature. However, the plasticity and toughness of steel, especially the low temperature plasticity is sharply reduced and leads to high ductile-brittle transition temperature. This phenomenon is commonly known as cold brittleness of steel [1~3]. Hence, phosphorus should be removed as much as possible in the steelmaking process, because it is generally harmful to the iron and steel products."

Jan 1, 2013

By J. Y. Hwang

The relationship between coal characterization and physical cleaning has not been well understood due to the complex nature of coal. Therefore, it is difficult to apply the results of coal characterization to predict and evaluate the performance of a physical separation (e.g. flotation). Eight U.S. bituminous coals were analyzed and studied petrographically in conjunction with washability and flotation tests. The results show that grindability correlates to ash and fixed carbon contents; liberation determined directly by petrographic techniques is close to liberation determined indirectly by washability; and an ideal separation efficiency can be determined by measuring the inertinite content and the washability separation efficiency using a heavy liquid with a density of 1.4. The ideal separation efficiency was attained for most coals by packed column flotation. The ideal separation efficiency can be used for comparing process technologies and process parameters.

Jan 1, 1988

By W. K. Connor, O&apos

Thermal Treatment Technology Division Albany Research Center, U.S. Dept. of Energy Oregon. This evaluation included a characterization study and direct smelting tests conducted in a bench-scale electric arc furnace (EAF). In contrast to other thermal treatment technologies considered for these wastes (i.e., fluidized bed combustion), direct smelting in the EAF can process 100% of the wastes without prior beneficiation, and utilizes solid oxidant additions (in this case iron ore) rather than air to oxidize the carbon. This solid oxidant addition is advantageous because it results in the production of several value-added furnace products. These products include cast iron resulting from the reduction of the iron oxides, baghouse dust containing virtually all of the zinc from the residues, and a clean (nonhazardous) slag product suitable for recycle as concrete aggregate or construction fill. Offgas from the smelting furnace also holds potential as fuel gas for cogeneration. The direct smelting tests conducted thus far were successful at producing the desired furnace products, exhibiting the potential for complete recycle of the waste pile. A cast iron product of comparable quality to conventional cast irons was produced, at nearly 80% iron recovery to the metal. The slag product was determined to be nonhazardous, based on the EPA TCLP. Lead and zinc partitioning to the dust product was greater than 99%. The material balance over the furnace indicates that for every ton of feed processed, 540 lb. of cast iron, 600 lb. of slag, and 150 lb. of dust would be produced. Energy consumption was roughly 1.10 kWxh/lb of feed material. Prior experience suggests that these figures measured in the bench-scale furnace would translate to 0040 to 0.50 kWxh/lb at the industrial-scale.

Jan 1, 2000

By Sven Reutzel

Investigations show that Co-based melts embedded by glass flux in a crucible can be under- cooled nearly as strong as samples processed containerlessly by electromagnetic levitation. This allows to measure magnetic susceptibility on undercooled melts while combining the use of a Faraday-balance and undercooling technique. The magnetic susceptibility of Co and Co-based alloys (such as Co-Pd and Co-Cu) is investigated as a function of temperature from superheated to undercooled state. This is done by measuring the change of magnetic force F, on a sample in a constant magnetic field Bo and an additional gradient field by means of a Faraday-balance. When liquid Co-based alloys are undercooled the magnetisation steeply rises if temperature approaches the Curie temperature. The magnetisation is measured for some Co-based alloys in liquid state as a function of alloy system and its concentration. The results show that the magnetic susceptibility of the liquid undercooled samples follows a Curie-Weiss behaviour, from which Curie temperature and magnetic moments for the liquid state are inferred.

Jan 1, 2002

By Thomas P. Battle

Titanium is the ninth most common element in the Earth's crust, yet only in this century has titanium come into use as an engineering material, particularly in aircraft structures, as the metal, and in pigments, as the dioxide. In this presentation, the metallurgical aspects of processing titanium-containing raw materials will be reviewed. Particular emphasis will be given to the ores and beneficiation techniques which lead to the production of titanium dioxide pigment, which accounts for over 90% of world titanium production.

Jan 1, 1993

By Taiping Lou

The effects of slag composition, additive agents, and heat treatment conditions on the perovskite (CaO ? TiO2) crystal morphology, the precipitation behavior, the crystal growth and the volume fraction (VF) in the Ti-bearing blast furnace slags were investigated. The morphology of perovskite is dispersed dendriform in molten slags. The crystal growth mechanism of the remelting of fine dendrites and the coarsening of larger grains exists throughout the solidification of molten slags. With the temperature decrease, the VF was increased and Perovskite transformed from fine dendrites to coarsening ones or equiaxed grains. The lower cooling rate can increase the VF and coarsen the grain obviously, while higher cooling rate will decrease the VF and reduce the average equivalent diameter (AED) of Perovskite. When .increasing the content of CaO and Fe20}, the VF can increase obviosly. However, high basicity will give rise to the increasing of viscosity of slag, which result in the reducing of the AED. The experimental results showed that additive CaF2 and MnO can efficiently decreased the viscosity of the slags, and obviously improved the morphology of perovskite and promote growth.

Jan 1, 2000

By R. G. Reddy

Reduction of different chromite ores with carbon was studied as a function of C/FeO ratio and temperature in the range 700 °C to 1100 °C by thermogravimetry (TGA) analysis. Powders of chromite ore(-150 mesh) and carbon(-150 mesh) were thoroughly mixed in a desired proportions and were placed in the reaction crucible. The reduction rates of reactions were determined by continuously monitoring the weight loss as a function of time at constant temperature using TGA set up. The analysis of results suggest that FeO present in the chromite ores is reduced to Fe involving gaseous intermediates CO and CO2. The overall rate of FeO reduction is controlled by the oxidation of carbon. A kinetic equation, that of random nucleation, was proposed. The activation energies for the reduction of FeO, present in Roast Movat and Transvaal ores, with carbon were determined to be 55800 and 23000 J/mole, respectively. The results of the present study are compared with the data available in literature. The low activation energy values as determined in this study suggest that the carbon oxidation reaction is catalyzed. It is concluded from the present investigation that the low grade chromite ores can be significantly upgraded to higher value added chromite that can be used as a feed source for economical smelting.

Jan 1, 1998

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of alloying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy's mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an alloy.

Jan 1, 2003

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of aJ10ying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy's mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an aJ1oy.

Jan 1, 2003

By Mehmet Bu daycı, Onuralp Yücel, Ahmet Turan, Murat Alkan

In this study, iron based alloys (Fe, Fe-Cr-Ni-Mo, etc.) were produced by using metallothermic methods starting from Mill Scales obtained continuous casting processes. During the process, the combustion was realized by ignition and the produced wave propagates throughout the reactant mixture yielding the desired product. In this work, Mill scale used as an iron source, which includes +2, +3 values iron oxides. Aluminum, Magnesium and Silicon were used as reductants. In these metallothermic experiments, different ratios of reductants were examined, and their effects on the metal recovery and alloy compositions were investigated. The samples were characterized by using chemical analysis (AAS), XRD and XRF techniques.

Jan 1, 2016

By Jun Lu, Min Chen, Wei-jian Su, Jian-zhong Luo, Yu-tao Lei

"In the case of treating phosphatizing wastewater containing zinc, zinc had an impact on the solution chemistry, especially on pH. Fe2(SO4)3 and CaCl2 were used as precipitators to remove phosphate from zincic phosphatizing wastewater and the optimum pH was investigated. Zinc ion had a significant effect on the optimum pH. The optimum pH ranges were 12.10(inlet concentration of 15.67mg/L, outlet concentration of 9.53mg/L), 3.04-5.50(inlet concentration of 11.97mg/L, outlet concentration of 0.44-0.26mg/L), and more than 10.72(inlet concentration of 12.24mg/L, outlet concentration of less than 0.47mg/L) under the conditions without precipitator, with Fe2(SO4)3 and with CaCl2 respectively.Introduction Phosphate coating is commonly used for protective coating of machine elements. Including oil removal by caustic washing, rust removal by acid washing, phosphatization and inactivation, the phosphatization process produces wastewater containing inorganic salt of high concentration, especially the phosphate, beyond the environmental standards and polluting environment seriously. What’s more, the wastewater from zincic phosphatizing technology also contains another pollutant, zinc. At present, Chemical Precipitation (CP) and Biological Nutrient Removal (BNR) are two of most common technologies of phosphate removal. BNR, such as A/O, A2/O and UCT technology, is suited for wastewater containing organ phosphorus of low concentration and CP for wastewater with phosphate of high concentration [1]. Researches on CP treating wastewater containing phosphate of high concentration, mainly focus on adding quantity of precipitators[2-5] and coagulants[2-4] and the choice of technologies[3-9]."

Jan 1, 2008

By George Oprea, Tom Troczynski, Joe A. Rigby, Waiman Lo

The refractory lining of the tuyere line in Peirce Smith converters have usually much shorter life in service than the rest of the lining, above or below it. There are already recognized chemical, thermal and mechanical factors which contribute to the wear of the lining. Our study presents the experimental results on microstructural changes occurring on these tuyere line bricks in a nickelcopper converter. The experimental bricks, after use at the tuyere line, were investigated using SEM/EDS and XRD techniques, to identify the mineralogical changes due to interactions with the nickel-copper matte or fayalite type slag at the process temperatures. The microstructural changes were correlated with physical and mechanical properties of the brick before and after use and a wear mechanism was suggested. Although the matte does not theoretically react with the mineralogical components of the brick, a partial oxidation of the Ni-Cu sulphides was identified using a line analysis by SEM/EDS in the densified layer at the hot face, which allows for mineralogical changes at the matte-refractory interfaces, with a high probability of microcrack formation due to the thermal cycling during use. These microcracks were also identified to open through inter-granular fractures parallel to the hot face, which appeared to be the main cause of lost lining during use. The reactions between the fayalite slag and refractory brick could eventually play a role in chemical dissolution of the brick only in the superficial layer at the hot face, as no slag components were identified deep into the brick.

Jan 1, 2009

By Hiroyuki Matsuura

The effects of P2OS or Na2O addition on the reaction rate of CO2 dissociation on the surface of FexO-base molten oxides was investigated at I 773K by isotope exchange method 1-6. The rate constant decreased with increasing P2Os content of molten oxides and the residual rate constant was observed at high P2OS content. On the other hand, the rate constant increased with increasing Na20 content for FexO-SiO2 melts, The rate constant was evaluated by the composition of oxides and the rate controlling step of CO2 dissociation was discussed.

Jan 1, 2003

Cospidie (3CaO*2SiO2*CaFe2) is one of the most important compounds crystallized in mold flux films during casting in the continuous casting process of steel, The primary crystallization field of cuspidine has been experimentally developed in the CaO-SiO2-CaF2-SiF4 system. The cuspidine-NaF binary and cuspidine-CaF2-NaF ternary systems have been also experimentally determined to study effects of addition of NaF on the primary field of cuspidine. In order to discuss its thermodynamic stability the standard Gibbs energy of formation of cuspidine has been deterimed by an electromotive force methods using CaF2 as solid electrolyte and a transpiration method as follows: ^fG° (cuspidine) /kjmol-1 = 5198 + 0.825T (+12) (1313<T/K<1329): EMF method ^fG° (cuspidine) /kjmol-1 = 5178 + 0.813T (+8) (1221<T/K<1469): Transpiration method The chemical potential diagram and constituent activities for the CaO-SiO2-CaF2 System have been evaluated based on the obtained thermodynamic data.

Jan 1, 2003

By Neng-Wen Yu, Shau-Jun Zhu, Ji-He Wei

The desulfurization process by powder injection and blowing in the RH refining of molten steel and its mechanism have been considered and analyzed. Based on the two-resistance mass transfer theory and the mass balance of sulfur in the system, a kinetic model for the process has been developed. The related parameters of the model, including the mass transfer coefficients and the effective amount of powder in the molten steel being treated for desulfurization, have been more reasonably determined. Modeling and predictions of the process of injecting and blowing the lime-based powder flux under assumed operating modes with the different initial contents of sulfur and amounts of powder injected and blown in a RH degasser of 300 t capacity have been carried out using the model. The relevant circulation rate of the liquid steel and the powder injection and blowing rate were taken to be 100 t/min and 150 kg/min, respectively. The initial contents of sulfur in the liquid steel to be treated and the amounts of powder injection and blowing were respectively assumed to be 0.007, 0.006, 0.005, 0.004, 0.003, 0.002 mass-% and 10, 8, 6, 5, 4, 3 kg/t-steel. The total treatment time for desulfurization under each mode was set up at 24 min, equivalent to eight circulation cycles of the liquid steel to be treated. The results indicated that the predictions made with this model are in good agreement with some data of the industrial experiments and practice. Injecting and blowing the lime-based powder flux with the composition of 85 mass-% lime (CaO) + 15 mass-% fluorspar (CaF2) of 3-5 kg/t-steel, it is possible to decrease the sulfur content in the molten steel to ultralow level below (5-10)x10·4 mass-% from (60-80)x 10·4 mass-%. The total treatment time needed will appropriately be 12-20 min. Intensifying the powder injection and blowing operation and increasing the circulation rate of the liquid steel may effectively' raise the rate of the process in RH refining. The model may be expected to offer some useful information and a reliable basis for determining the reasonable process parameters and help in optimizing the technology of desulfurization by powder injection and blowing in the RH refining of molten steel.

Jan 1, 2000

By Atul Kurnar

In the present research a two-cell polymer electrolyte membrane fuel cell stack (PEMFCS) with SS-316 bipolar plates has been tested. Different flow field designs were studied and a modified multi-parallel channel design is proposed. The stack is stable within ±3 mV even after 1000 hours of continuous operation, indicating efficient water management and effective removal of any metal ions from the stack. Also no iron is detected in membrane electrode assembly (MEA) by EDAX analysis after 1000 hours of cell operation. Results indicate that high operating pressures beyond 138 kPa didn&apos;t significantly increase the performance of cell, however added much to the pressurization cost of the system. Tests at different temperatures showed that at temperatures below 80°C, external humidification could be completely removed. The prototype stack is also tested under variable load conditions simulating highway-driving schedule. The experimental efficiency of PEMFCS is 48%, which is in good agreement with the model predicted efficiency of 53.8 %. Results show that 59% of the total losses are due to ohmic polarization in the cell. Further analysis on applications of the stack in automotive transportation system is in progress.

Jan 1, 2002

By S. J. Thiele, T. Newton, W. Magalhäes, T. Takayama, J. Welsh

Companhia Paraibuna de Metais (CPM) is presently pursuing a zinc production expansion project. Besides increasing production, the goal of the project is to address existing problems while providing a platform for a proposed twofold increase in production in 2003/2004. Therefore, the current expansion strategy was formulated to address present and future requirements. Computer simulation modeling and full scale plant testing are being used to generate data to optimize the operating conditions and to perform a sensitivity analysis. The initial phase of the project, which will boost CPM's capacity to 86,000 t/y of marketable zinc, is to be completed in September 2000.

Jan 1, 2000

Cuspidine (3CaO?2SiO2?CaF2) is one of the most important compounds crystallized in mold flux films during casting in the continuous casting process of steel. The primary crystallization field of cuspidine has been experimentally developed in the CaO-SiOrCaF2-SiF4 system. The cuspidine-NaF binary and cuspidine-CaF2-NaF ternary systems have been also experimentally determined to study effects of addition of NaF on the primary field of cuspidine. In order to discuss its thermodynamic stability the standard Gibbs energy of formation of cuspidine has been determined by an electromotive force method using CaF2 as solid electrolyte and a transpiration method as follows: The chemical potential diagram and constituent activities for the CaO-Si02-CaF2 system have been evaluated based on the obtained thermodynamic data.

Jan 1, 2003

By Sharif Jahanshahi

Calcium ferrite slags are often associated with Professor Yazawa due to his pioneering work on the thermodynamics of this type of melts. Over the past years CSIRO has invested some effort in studying physico-chemical properties of such melts to fill in some gaps in our knowledge and explore opportunities for application of the understanding developed. These investigations cover thermodynamics, transport properties of calcium ferrite based slags, as well as the kinetics of reactions of such slags with refractories. The present paper provides an overview of some of these studies and highlights some of the interesting behavior of such melts, The oxidation state of copper and arsenic in calcium ferrite based slags are predominantly Cu+ and As3+, respectively, at oxygen potentials below 10-7 atm. The concentration of CU2+ in such slags becomes significant at oxygen potentials of greater than 10-7 atm at 1300 °C. The activities of CuO0.5 and AsO1.5 in calcium ferrite slags show strong deviations from the Raoultian Law, while that of CoO is very close to ideal behaviour with respect to pure solid CoO. Addition of SiO2 to calcium ferrite slags can have significant effects on the activities of FeO and Fe2O3 and hence the stability of magnetite phase. Transfer of oxygen in calcium ferrite slags is fast with diffusivity of 2x 103 cm2/s at 1350 °C and activation energy of 16 kcal/mol. Presence of solid phases, such as magnetite, has pronounced effect on the viscosity of calcium ferrite slags. The observed dependence on solid loading and shear rate indicates deviation from Newtonian behaviour. The interfacial tension between copper mattes and calcium ferrite slags is strongly dependent on the matte grade, with the determined values being much lower than the corresponding ones for interfacial tension between similar mattes and iron silicate slags. MgO, Cr2O3 and MgCr2O4 have low solubility in calcium ferrite slags and their solubility increases with increasing copper oxide content of the slag at 1300°C. The oxidation state of the slag has strong effects on phase transformation, dissolution rate and disintegration of refractories in calcium ferrite slags. Other key factors with major impact on slag-refractory interactions include viscosity and surface tension of slags as well as the contact angle between slag and refractory material,

Jan 1, 2003